JPH09253598A - Treating agent for solidifying waste product incineration collected ash and treating method therefor - Google Patents

Abstract

PROBLEM TO BE SOLVED: To treat collected ash at a low cost by very efficiently suppressing an elution quantity of harmful heavy metal such as lead with a small quantity of addition of the treating agent to the collected ash. SOLUTION: This treating method has characterized treating agent. The treating agent is used for solidifying waste product incineration collected ash containing harmful metal and contains slaked lime of <=15% C1<-> contents, and further the treating agent contains at least blast furnace granulated slag.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、都市ゴミ焼却場等
より排出される、特に鉛やカドミウムなどの有害重金属
を含有し、且つＣｌ^- の含有量が１５％以下の消石灰を
含有した廃棄物焼却集塵灰を固化処理する処理剤及びそ
の処理方法の改良に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to waste discharged from municipal waste incinerators and the like, which contains slaked lime having a Cl ⁻ content of 15% or less and containing harmful heavy metals such as lead and cadmium. The present invention relates to an improvement in a treatment agent for solidifying incinerated dust ash and a treatment method therefor.

【０００２】[0002]

【従来の技術】都市ゴミ焼却場等より排出される廃棄物
焼却集塵灰は、廃棄物処理法により特別管理一般廃棄物
に指定されているので、そのまま埋め立て処分すること
はできず、含有されている鉛やカドミウム，水銀，クロ
ムなどの有害重金属の溶出量が所定の基準値内に納まる
ように中間処理が義務付けられている。2. Description of the Related Art Waste incineration dust collected from municipal waste incinerators, etc., is specified as specially controlled general waste by the Waste Management Law, so it cannot be directly landfilled and is contained. Intermediate treatment is obligatory so that the amount of toxic heavy metals such as lead, cadmium, mercury, and chromium that are present may fall within the prescribed standard values.

【０００３】前記焼却集塵灰の中に存在する鉛，カドミ
ウム，水銀，クロムなどの有害な重金属の処理処分に関
しては、普通セメント、或いは普通セメントに水可溶性
酸性塩類などの薬剤を添加したものを用いて固化し、前
記重金属を不溶化、安定化する方法が低コスト、且つ簡
便であるため、採用されてきた。Regarding the treatment and disposal of harmful heavy metals such as lead, cadmium, mercury and chromium present in the incinerated dust ash, ordinary cement or ordinary cement to which a chemical such as water-soluble acid salt is added is used. The method of solidifying by using to insolubilize and stabilize the heavy metal has been adopted because it is low cost and simple.

【０００４】ところが、最近では、焼却炉で発生するＨ
Ｃｌ、ＮＯ_X 、ＳＯ_X などの有害ガスを捕捉するために
消石灰、生石灰などを吹き込む処理がなされている。However, recently, H generated in an incinerator
Cl, NO _X, slaked lime to capture harmful gases such as SO _X, the process of blowing and quicklime have been made.

【０００５】しかしながら、前記吹き込み処理では、消
石灰などが未反応のまま焼却集塵灰中に残留することが
多いため、該集塵灰のｐＨが１２以上と強アルカリ性に
なり、鉛などの両性金属は亜鉛酸塩などとなって再溶解
してしまう。However, in the above-mentioned blowing treatment, slaked lime and the like often remain unreacted in the incinerated dust ash, so that the pH of the dust ash becomes 12 or more and it becomes strongly alkaline, and amphoteric metals such as lead. Becomes zincate and redissolves.

【０００６】従って、単に普通セメントを添加しただけ
では鉛の溶出は抑えられず、また上述のように水可溶性
酸性塩類などの薬剤を添加することによって鉛などの重
金属が溶出しにくい領域までｐＨを低下させようとして
も塩類を多量に添加しなければならず、集塵灰の減容
化、処理コスト低減につながらない。Therefore, the leaching of lead cannot be suppressed by simply adding ordinary cement, and as described above, the addition of chemicals such as water-soluble acidic salts raises the pH to a region in which heavy metals such as lead are difficult to elute. Even if an attempt is made to reduce the amount, a large amount of salts must be added, which does not lead to volume reduction of dust ash and reduction of treatment cost.

【０００７】それで、最近ではその有効な処理法として
溶融ガラス固化法やキレート剤の添加による処理法が提
案されている。Therefore, recently, a molten glass solidification method and a treatment method by adding a chelating agent have been proposed as effective treatment methods.

【０００８】しかしながら、前記溶融ガラス固化法は設
備投資が大きくエネルギー消費が非常に大きいため、必
ずしも適当な方法とは言えなかったし、また、前記キレ
ート剤の添加による処理法においても、該キレート剤そ
のものがかなり高価なものであるためコスト高の問題も
ある上、該キレート剤は有機化合物であるため、廃棄後
に紫外線や微生物によって分解され、一度固化処理され
た前記重金属が長期的には溶出してくる恐れがあると共
に、既存のセメント固化施設では設備の改造が必要とな
ってしまうのが現状である。[0008] However, the molten glass solidification method cannot be said to be an appropriate method because it requires a large amount of capital investment and consumes a large amount of energy, and the method of adding the chelating agent is not always suitable. Since it itself is quite expensive, there is a problem of high cost, and since the chelating agent is an organic compound, it is decomposed by ultraviolet rays and microorganisms after disposal, and the heavy metal once solidified is eluted for a long term. The current situation is that the existing cement solidification facilities will need to be modified.

【０００９】また、溶出基準値の改正により鉛の溶出量
が３ｐｐｍから０．３ｐｐｍ以下に強化されたため、前
記従来の処理では、該基準値達成がますます厳しい状況
におかれている。Further, since the lead elution amount is strengthened from 3 ppm to 0.3 ppm or less by the revision of the elution standard value, it is becoming more and more difficult to achieve the standard value in the above conventional treatment.

【００１０】そこで、本願出願人は、アルミナセメント
を主体とし、これに硫酸アルミニウム、塩化アルミニウ
ムなどの酸性無機塩類を添加してなる固化処理剤がｐＨ
１２以上の強アルカリ性を有する集塵灰に対して鉛の溶
出量低減に効果的であることを既に見出し、特願平７−
１６６４４１号にて主張している。Therefore, the applicant of the present application has found that the solidifying agent composed mainly of alumina cement, to which an acidic inorganic salt such as aluminum sulfate or aluminum chloride is added, has a pH of
It has already been found that it is effective in reducing the elution amount of lead with respect to dust collecting ash having a strong alkalinity of 12 or more, and Japanese Patent Application No. 7-
Claimed in No. 166441.

【００１１】[0011]

【発明が解決しようとする課題】前記発明は、鉛などの
有害重金属の溶出量低減において非常に有効な方法であ
るが、如何せん、前記発明の固化処理剤はアルミナセメ
ントを主体としているため、キレート剤等に比べれば安
価ではあるが、まだまだ処理コストが高価と成らざるを
得なかった。The above invention is a very effective method for reducing the elution amount of harmful heavy metals such as lead. However, since the solidifying agent of the above invention is mainly composed of alumina cement, Although it is cheaper than the agents and the like, the processing cost is still high.

【００１２】そこで、本発明においては、有害重金属を
含有し、且つＣｌ^- の含有量が１５％以下の消石灰が含
まれている焼却集塵灰と限られてはいるが、該集塵灰に
対しては、小量の添加量にて非常に効果的に鉛などの有
害重金属の溶出量を抑制できることで、低コスト実現化
が図れる廃棄物焼却集塵灰固化用処理剤及び処理方法を
提供することを目的とする。Therefore, in the present invention, the incinerated dust ash containing harmful heavy metals and containing slaked lime having a Cl ⁻ content of 15% or less is not limited to the incinerated dust ash. On the other hand, a small amount of additive can provide a treatment agent and a treatment method for waste incineration dust collection ash solidification that can reduce the amount of harmful heavy metals such as lead that can be very effectively suppressed and realize low cost. The purpose is to do.

【００１３】[0013]

【課題を解決するための手段】本発明は上記目的を達成
するために、次の技術的手段を講じる。The present invention employs the following technical means in order to achieve the above object.

【００１４】即ち、その第一の技術的手段は、処理剤に
特徴があり、有害重金属を含有し、且つＣｌ^- の含有量
が１５％以下の消石灰を含有した廃棄物焼却集塵灰を固
化する処理剤において、高炉水滓スラグを含有してなる
ことである。[0014] That is, the first technical means is characterized by the treating agent, contain harmful heavy metals, and Cl ^- content is solidified waste incineration collection Chirihai containing slaked lime of 15% or less The treatment agent is a blast furnace slag slag.

【００１５】また、その第二の技術的手段も、処理剤に
特徴があり、有害重金属を含有し、且つＣｌ^- の含有量
が１５％以下の消石灰を含有した廃棄物焼却集塵灰を固
化する処理剤において、高炉水滓スラグと水可溶性酸性
塩類とを含有してなることである。[0015] Also, the second technical means is characterized in treatment agent, containing toxic heavy metals, and Cl ^- content is solidified waste incineration collection Chirihai containing slaked lime of 15% or less In the treatment agent, the blast furnace slag slag and the water-soluble acid salts are contained.

【００１６】更に、その第三の技術的手段も、処理剤に
特徴があり、有害重金属を含有し、且つＣｌ^- の含有量
が１５％以下の消石灰を含有した廃棄物焼却集塵灰を固
化する処理剤において、高炉水滓スラグと水可溶性酸性
塩類に、白土、ゼオライト、炭酸ナトリウム、珪酸ナト
リウムからなる群より選択された少なくとも１種類を含
有してなることである。Furthermore, also the third technical means is characterized in treatment agent, containing toxic heavy metals, and Cl ^- content is solidified waste incineration collection Chirihai containing slaked lime of 15% or less In the treatment agent, at least one selected from the group consisting of clay, zeolite, sodium carbonate, and sodium silicate is contained in the blast furnace slag slag and the water-soluble acid salts.

【００１７】また、その第四の技術的手段は、処理方法
に特徴があり、有害重金属を含有し、且つＣｌ^- の含有
量が１５％以下の消石灰を含有した廃棄物焼却集塵灰を
固化処理する方法において、所定容器内に前記廃棄物焼
却集塵灰と、前記請求項１〜３の何れかに記載の処理剤
を混合し、その中に適量の水を加えて混練し、固化処理
することにある。Further, the fourth technical means is characterized by processing method, it contains harmful heavy metals, and Cl ^- content is solidified waste incineration collection Chirihai containing slaked lime of 15% or less In the method for treating, the waste incineration dust ash and a treating agent according to any one of claims 1 to 3 are mixed in a predetermined container, and an appropriate amount of water is added to the mixture to knead the mixture to solidify it. To do.

【００１８】本発明の係る高炉水滓スラグは、鉄の製造
過程で多量に排出されるガラス質の廃棄物であるが、該
高炉水滓スラグは消石灰などのようなアルカリ性塩類の
作用によってセメントのように水和及び硬化する性質を
有しているため、セメント等に添加されて多量に消費さ
れている。The blast-furnace slag slag according to the present invention is a glassy waste discharged in a large amount in the process of iron production. The blast-furnace slag slag is produced by the action of alkaline salts such as slaked lime. Since it has the property of hydrating and hardening, it is added to cement and consumed in large quantities.

【００１９】前記高炉水滓スラグの性質を利用し、本発
明における廃棄物焼却集塵灰固化用処理剤として高炉水
滓スラグを用いると、廃棄物焼却集塵灰に含有される消
石灰と反応して、該集塵灰を硬化させ、更にそのｐＨを
低下させることが可能となる。Utilizing the properties of the blast furnace slag slag and using the blast furnace slag slag as a treating agent for solidifying the waste incineration dust ash in the present invention, it reacts with slaked lime contained in the waste incineration dust ash. As a result, the dust ash can be cured and the pH thereof can be lowered.

【００２０】従って、該高炉水滓スラグは前記有害な重
金属の溶出を抑制し、またこの際に生成する非常に微細
で高い比表面積をもった水和物に前記重金属がイオン交
換，又は物理的に取り込まれる。Therefore, the slag slag of the blast furnace suppresses the elution of the harmful heavy metals, and the hydrates produced at this time have very fine and high specific surface areas, and the heavy metals are ion-exchanged or physically hydrated. Is taken into.

【００２１】前記重金属の取り込みによって、高炉水滓
スラグは重金属の溶出を抑制する働きを有することとな
る。By taking in the heavy metal, the blast furnace slag slag has a function of suppressing the elution of heavy metal.

【００２２】また、前記高炉水滓スラグはセメントのよ
うに反応に伴って逆に消石灰を放出することもないの
で、消石灰を多量に含有した強アルカリ性を有する廃棄
物焼却集塵灰の固化処理に非常に有効である。The blast furnace slag slag does not release slaked lime conversely with the reaction unlike cement, so that it is suitable for solidifying waste incineration dust ash containing a large amount of slaked lime. It is very effective.

【００２３】更に、その際、前記高炉水滓スラグは手軽
に入手することが可能であるので、非常に低コストにて
廃棄物焼却集塵灰固化の実現化が図れる。Further, at this time, since the blast furnace slag slag can be easily obtained, the solidification of waste incineration dust ash can be realized at a very low cost.

【００２４】[0024]

【発明の実施の形態】本発明は、都市ゴミ焼却場等より
排出される廃棄物焼却集塵灰のうち、特に該集塵灰中の
消石灰の含有量が多量であっても、Ｃｌ^- の含有量が１
５％以下の集塵灰の処理処分における有効な処理剤及び
処理方法であり、該集塵灰の中に存在する鉛，カドミウ
ム，水銀，クロムなどの有害な重金属の好適な処理法を
見いだしたものである。以下、本発明の実施の形態につ
いて、いくつかの実験例を挙げ、詳述に説明する。DETAILED DESCRIPTION OF THE INVENTION The present invention, among the waste incineration collection Chirihai discharged from municipal waste incineration, etc., even a large amount especially content of slaked lime in the said population Chirihai, Cl ^- of Content is 1
The present inventors have found an effective treatment agent and treatment method for the treatment and disposal of dust ash of 5% or less, and found a suitable treatment method for harmful heavy metals such as lead, cadmium, mercury, and chromium present in the dust ash. It is a thing. Hereinafter, embodiments of the present invention will be described in detail with reference to some experimental examples.

【００２５】本発明の焼却灰固化用処理剤は、高炉水滓
スラグを主体としたものであり、一定の割合で混合し、
更に水を添加して混練し、養生固化を行うことによって
前記有害な重金属が安定化、不溶化され、これら重金属
の溶出量が埋め立ての際の基準値達成に至るまで低減さ
れるのである。The treatment agent for solidifying incinerated ash of the present invention is mainly composed of blast furnace slag slag, which is mixed at a constant ratio,
By further adding water and kneading and curing and solidifying, the harmful heavy metals are stabilized and insolubilized, and the elution amount of these heavy metals is reduced until the standard value at the time of landfill is reached.

【００２６】本発明の前記処理剤の添加量及び該処理剤
の各成分の配合割合は対象となる集塵灰により適宜調整
されるが、高炉水滓スラグ単独，又は高炉水滓スラグ５
０〜９０％に対して、水可溶性酸性塩類、白土、ゼオラ
イト、炭酸ナトリウム、珪酸ナトリウムからなる群より
選択された少なくとも１種類を１０〜５０％混合したも
のや、或いは、前記高炉水滓スラグ５０〜８０％に対し
て、水可溶性酸性塩類を１０〜２０％、及び白土、ゼオ
ライト、炭酸ナトリウム、珪酸ナトリウムからなる群よ
り選択された少なくとも１種類を１０〜３０％混合した
ものを用いる。The addition amount of the treating agent of the present invention and the mixing ratio of each component of the treating agent are appropriately adjusted depending on the target dust collecting ash. The blast furnace slag slag alone or the blast furnace slag slag 5
A mixture of 0 to 90% with 10 to 50% of at least one selected from the group consisting of water-soluble acidic salts, clay, zeolite, sodium carbonate and sodium silicate, or the blast furnace water slag 50 A mixture of 10 to 20% of water-soluble acidic salt and 10 to 30% of at least one selected from the group consisting of clay, zeolite, sodium carbonate, and sodium silicate is used to -80%.

【００２７】前記水可溶性酸性塩類は、消石灰を多量に
含有して強アルカリ性となった集塵灰のｐＨを低下さ
せ、前記鉛などの有害な両性重金属を溶出しにくくさせ
ると共に、前記集塵灰に含まれるカルシウムや重金属と
反応して水に難溶性の塩を生成するものである。The water-soluble acid salts contain a large amount of slaked lime to lower the pH of the dust-collecting ash that has become strongly alkaline, make it difficult to elute harmful amphoteric heavy metals such as lead, and collect the dust-collecting ash. Reacts with calcium and heavy metals contained in to form a salt that is sparingly soluble in water.

【００２８】具体的には、硫酸アルミニウムや硫酸第一
鉄，硫酸第二鉄などの硫酸塩、塩化アルミニウム，塩化
第一鉄，塩化第二鉄などの塩化物、第一リン酸アルミニ
ウムやリン酸一水素ナトリウム，リン酸二水素ナトリウ
ム，リン酸一水素カリウム，リン酸二水素カリウムなど
のリン酸塩等が挙げられる。Specifically, sulfates such as aluminum sulfate, ferrous sulfate and ferric sulfate, chlorides such as aluminum chloride, ferrous chloride and ferric chloride, aluminum monophosphate and phosphoric acid. Examples thereof include phosphates such as sodium monohydrogen, sodium dihydrogen phosphate, potassium monohydrogen phosphate, and potassium dihydrogen phosphate.

【００２９】前記白土及びゼオライトは、その表面及び
内部に重金属を吸収することによって溶出を抑制する作
用があるので、その混合は好ましい。The clay and the zeolite have a function of suppressing elution by absorbing heavy metals on the surface and inside thereof, and therefore their mixing is preferable.

【００３０】また、前記炭酸ナトリウム及び珪酸ナトリ
ウムは、集塵灰に含まれるカルシウムと、セメント水和
物様の難溶性の塩を生成し、固化させる作用があり、ま
た重金属とも難溶性の塩を生成して安定化させる作用が
あり、その混合は非常の望ましい。The above-mentioned sodium carbonate and sodium silicate have a function of forming and solidifying a hardly soluble salt like cement hydrate with calcium contained in the dust ash, and also a salt which is hardly soluble with heavy metals. It has the effect of forming and stabilizing, and its mixing is highly desirable.

【００３１】[0031]

【実施例】ここで、本発明の処理剤と従来の処理剤等と
の比較をして、その効果を検討して見る。尚、従来例と
しては、従来から使用されている普通セメントからなる
処理剤と、アルミナセメントからなる処理剤（特願平７
−１６６４４１号にて詳細）とを使用する。EXAMPLES Here, the treatment agent of the present invention is compared with the conventional treatment agent and the effect thereof is examined and examined. Incidentally, as a conventional example, a treating agent made of conventional cement and a treating agent made of alumina cement (Japanese Patent Application No.
(Details in No. 166441) are used.

【００３２】＜第一実験例＞先ず、 本発明に係る高炉
水滓スラグ単独からなる処理剤（実施例１及び２と比較
例１及び２）と、前記普通セメントからなる処理剤（従
来例１）及びアルミナセメントからなる処理剤（従来例
２）との比較実験を行った。<First Experimental Example> First, a treating agent comprising blast furnace slag slag alone according to the present invention (Examples 1 and 2 and Comparative Examples 1 and 2), and a treating agent comprising the ordinary cement (conventional example 1). ) And a treating agent composed of alumina cement (conventional example 2).

【００３３】サンプル体を作製するにあたっては、廃棄
物焼却集塵灰として、一つはカルシウム含有量３０．４
％及びＣｌ^- 含有量１３．１％を有するもの（以下、集
塵灰Ａと言う）、もう一つはカルシウム含有量１７．５
％及びＣｌ^- 含有量２４．３％を有するもの（以下、集
塵灰Ｂと言う）の２種類を用意する。In preparing the sample body, one of the waste incineration dust ash was a calcium content of 30.4.
% And Cl ^- content 13.1% (hereinafter referred to as dust collecting ash A), the other has a calcium content of 17.5
% And Cl ⁻ content 24.3% (hereinafter referred to as dust ash B).

【００３４】前記焼却集塵灰１００部に対して、高炉水
滓スラグ１５部、或いは高炉水滓スラグ２０部を混合し
た処理剤に、更に、水を該焼却集塵灰に対して３５部添
加したものを充分に混練し、径５cm、高さ１０cmの型枠
に詰めて養生を行った。To 100 parts of the incinerated dust ash, 15 parts of blast furnace slag slag or 20 parts of blast furnace slag slag were mixed, and 35 parts of water was added to the incinerated dust ash. The thus obtained mixture was sufficiently kneaded and packed in a mold having a diameter of 5 cm and a height of 10 cm for curing.

【００３５】養生７日目に鉛の溶出量を測定した。該鉛
の溶出量の測定は、前記各サンプル体を粉砕し、目開き
０．５mmと５mmのフルイの間に残ったものを５０ｇ採取
し、これに蒸留水５００ｇを加えて６時間振盪を行った
後、濾過したものを試験液として測定した。The amount of lead elution was measured on the 7th day of curing. The amount of lead elution was measured by crushing each of the sample bodies, collecting 50 g of what remained between the sieves having openings of 0.5 mm and 5 mm, adding 500 g of distilled water thereto, and shaking for 6 hours. Then, the filtered product was measured as a test liquid.

【００３６】その結果を下記表１にて示す。尚、対照と
して、前記集塵灰Ａ及び集塵灰Ｂに処理剤を全く入れず
に測定した。The results are shown in Table 1 below. As a control, the dust collection ash A and the dust collection ash B were measured without any treating agent.

【００３７】[0037]

【表１】 [Table 1]

【００３８】前記実験結果からわかるように、集塵灰Ｂ
に対してはその効果が殆ど見られなかった（比較例１及
び２）ものの、集塵灰Ａに関しては、従来例１での処理
剤が鉛溶出基準値達成に至らないと言う結果であったの
に対し、本発明の実施例１及び実施例２での処理剤は共
に、アルミナセメントからなる従来例２での処理剤同
様、基準値０．３ｐｐｍ以下を達成し、非常に効果が見
られる。As can be seen from the above experimental results, dust ash B
Although the effect was hardly seen for (Comparative Examples 1 and 2), the result was that for the dust collecting ash A, the treatment agent in Conventional Example 1 did not reach the lead elution standard value. On the other hand, both the treating agents in Example 1 and Example 2 of the present invention achieved the reference value of 0.3 ppm or less, which is very effective, like the treating agent in Conventional Example 2 made of alumina cement. .

【００３９】＜第二実験例＞次に、前記１００部の集塵
灰Ａを使用し、本発明に係る高炉水滓スラグ１５部に、
各種水可溶性酸性塩類を５部添加したものを固化処理剤
として、前記第一実験例同様にサンプル体を作製して同
様の処理を行い、上記同様の試験を行った（実施例３〜
７）。<Second Experimental Example> Next, using 100 parts of the dust collecting ash A, 15 parts of the blast furnace water slag according to the present invention,
Using 5 parts of various water-soluble acidic salts as a solidifying agent, a sample body was prepared in the same manner as the first experimental example, the same treatment was carried out, and the same test as described above was conducted (Examples 3 to 3).
7).

【００４０】その結果を下記表２にて示す。The results are shown in Table 2 below.

【００４１】[0041]

【表２】 [Table 2]

【００４２】前記実験結果からわかるように、前記水可
溶性酸性塩類を添加すると何れも鉛の溶出量は低減し、
特に第一リン酸アルミニウムやリン酸一水素ナトリウム
等リン酸塩の添加は非常に効果的であった。As can be seen from the experimental results, the addition of the water-soluble acid salts reduces the lead elution amount in all cases.
In particular, addition of phosphates such as monoaluminum phosphate and sodium monohydrogen phosphate was very effective.

【００４３】＜第三実験例＞前記第一実験例及び第二実
験例から、集塵灰中の消石灰の含有量が多量であって
も、Ｃｌ^- の含有量が１５％以下の集塵灰であれば、本
発明の高炉水滓スラグの混合は鉛の溶出量を低下させる
上で非常に有効であることが、また、該高炉水滓スラグ
に水可溶性酸性塩類を添加することで更にその効果が現
れることが明確化されたが、これに、白土、ゼオライ
ト、炭酸ナトリウム、珪酸ナトリウムを夫々添加させ、
その効果を検討してみた。<Third Experimental Example> From the first experimental example and the second experimental example, even if the content of slaked lime in the collected ash is large, the content of Cl ⁻ is 15% or less. If so, that the mixing of the blast furnace slag slag of the present invention is very effective in reducing the elution amount of lead, and further by adding water-soluble acid salts to the blast furnace slag slag It was clarified that the effect appears, but by adding clay, zeolite, sodium carbonate, sodium silicate to each,
I examined its effect.

【００４４】尚、該第三実験例においては、集塵灰Ａを
使用し、該焼却集塵灰１００部に対して、高炉水滓スラ
グ１６部（実施例８），或いは高炉水滓スラグ１２部
と、水可溶性酸性塩類として硫酸アルミニウムが４部と
に、夫々白土（実施例９）、ゼオライト（実施例１
０）、炭酸ナトリウム（実施例１１）、珪酸ナトリウム
（実施例１２）からなる群より選択された１種類を４部
混合した処理剤に、更に、水を該焼却集塵灰に対して３
５部添加したものを充分に混練して、前記第一及び第二
実験例同様にサンプル体を作製し、同様の処理を行い、
上記同様の試験を行った。In the third experimental example, the dust ash A was used, and 16 parts of the blast furnace water slag slag (Example 8) or the blast furnace water slag 12 was used for 100 parts of the incinerated dust ash. Parts and 4 parts of aluminum sulfate as a water-soluble acidic salt, clay (Example 9) and zeolite (Example 1), respectively.
0), sodium carbonate (Example 11), and sodium silicate (Example 12), 4 parts of one kind selected from the group consisting of 4 parts is further added, and water is further added to the incinerated dust ash in an amount of 3 parts.
Thoroughly kneading 5 parts added to prepare a sample body in the same manner as the first and second experimental examples, and perform the same treatment,
The same test as above was performed.

【００４５】その結果を下記表３にて示す。The results are shown in Table 3 below.

【００４６】[0046]

【表３】 [Table 3]

【００４７】前記実験結果からわかるように、本発明に
係る高炉水滓スラグに水可溶性酸性塩類と、更に白土、
ゼオライト、炭酸ナトリウム、珪酸ナトリウムからなる
群より選択された１種類とを加えても充分に、鉛溶出量
の基準値０．３ｐｐｍ以下を達成し得ると言える。ま
た、特に、前記白土、ゼオライトの添加においてはその
効果が顕著であることがわかる。As can be seen from the above experimental results, the blast furnace slag slag according to the present invention contains water-soluble acid salts, and further clay.
It can be said that even if one kind selected from the group consisting of zeolite, sodium carbonate and sodium silicate is added, the standard value of lead elution amount of 0.3 ppm or less can be sufficiently achieved. Further, it can be seen that the effect is particularly remarkable when the above-mentioned clay and zeolite are added.

【００４８】[0048]

【発明の効果】本発明における廃棄物焼却集塵灰固化用
処理剤、即ち、少なくとも高炉水滓スラグを含有する処
理剤を使った処理方法であれば、該集塵灰が有害重金属
を含有し、且つＣｌ^- の含有量が１５％以下の消石灰を
含有したものに限定されはするが、該集塵灰に対して
は、小量の添加量にて非常に効果的に鉛などの有害重金
属の溶出量を抑制でき、改正された溶出基準値の範囲内
にて問題なく廃棄物焼却集塵灰固化が可能となる。EFFECT OF THE INVENTION In the treatment method using the treatment agent for solidifying waste incinerated dust ash according to the present invention, that is, the treatment agent containing at least blast furnace slag slag, the dust ash contains harmful heavy metals. and Cl ^- of the content is limited to those containing the following slaked lime 15% to, for the dust collecting ash, toxic heavy metals such as very effectively lead at small amounts of added amount It is possible to suppress the elution amount of the waste, and it becomes possible to solidify the waste incineration dust ash within the range of the revised elution standard value without any problems.

【００４９】特に前記効果は、水可溶性酸性塩類を添加
したり、更に、白土、ゼオライト、炭酸ナトリウム、珪
酸ナトリウムからなる群より選択された少なくとも１種
類を添加することで顕著になる。In particular, the above effect becomes remarkable by adding a water-soluble acidic salt and further adding at least one selected from the group consisting of clay, zeolite, sodium carbonate and sodium silicate.

【００５０】また、その際、前記高炉水滓スラグは手軽
に入手することが可能であるので、非常に低コストにて
廃棄物焼却集塵灰固化の実現化が充分に図れる。At this time, since the blast furnace slag slag can be easily obtained, solidification of waste incineration dust ash can be sufficiently realized at a very low cost.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 小出 貴夫 大阪市大正区南恩加島７−１−55 住友大 阪セメント株式会社中央研究所セメント・ コンクリート研究所内 (72)発明者 木虎 智子 大阪市大正区南恩加島７−１−55 住友大 阪セメント株式会社中央研究所セメント・ コンクリート研究所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Takao Koide Inventor Takao Koide 7-1-55 Minamienkajima, Taisho-ku, Osaka City Sumitomo Osaka Co., Ltd. Central Research Institute, Cement and Concrete Research Center (72) Inventor Tomoko Kitora Osaka 7-1-55, Minami Enkajima, Taisho-ku, Shizuoka Sumitomo Osaka Cement Central Research Institute Cement and Concrete Research Center

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 有害重金属を含有し、且つＣｌ^- の含有
量が１５％以下の消石灰を含有した廃棄物焼却集塵灰を
固化する処理剤において、高炉水滓スラグを含有するこ
とを特徴とする廃棄物焼却集塵灰固化用処理剤。1. A treatment agent for solidifying waste incineration dust ash containing harmful heavy metals and containing slaked lime with a Cl ⁻ content of 15% or less, characterized by containing blast furnace water slag slag. A treatment agent for solidifying waste incineration dust ash. 【請求項２】 有害重金属を含有し、且つＣｌ^- の含有
量が１５％以下の消石灰を含有した廃棄物焼却集塵灰を
固化する処理剤において、高炉水滓スラグと水可溶性酸
性塩類とを含有することを特徴とする廃棄物焼却集塵灰
固化用処理剤。2. A treatment agent for solidifying waste incineration dust ash containing harmful heavy metals and containing slaked lime having a Cl ⁻ content of 15% or less, wherein blast furnace slag slag and water-soluble acidic salts are used. A treatment agent for solidification of waste incineration dust ash characterized by containing. 【請求項３】 有害重金属を含有し、且つＣｌ^- の含有
量が１５％以下の消石灰を含有した廃棄物焼却集塵灰を
固化する処理剤において、高炉水滓スラグと水可溶性酸
性塩類に、白土、ゼオライト、炭酸ナトリウム、珪酸ナ
トリウムからなる群より選択された少なくとも１種類を
含有することを特徴とする廃棄物焼却集塵灰固化用処理
剤。3. A treatment agent for solidifying waste incineration dust ash containing harmful heavy metals and containing slaked lime having a Cl ⁻ content of 15% or less, wherein blast furnace slag slag and water-soluble acidic salts are added. A treatment agent for solidification of waste incineration dust ash characterized by containing at least one selected from the group consisting of clay, zeolite, sodium carbonate, and sodium silicate. 【請求項４】 有害重金属を含有し、且つＣｌ^- の含有
量が１５％以下の消石灰を含有した廃棄物焼却集塵灰を
固化処理する方法において、所定容器内に前記廃棄物焼
却集塵灰と、前記請求項１〜３の何れかに記載の処理剤
を混合し、その中に適量の水を加えて混練し、固化処理
することを特徴とする廃棄物焼却集塵灰固化処理方法。4. A method for solidifying waste incineration dust ash containing harmful heavy metals and containing slaked lime having a Cl ⁻ content of 15% or less, wherein the waste incineration dust ash is contained in a predetermined container. And a treatment agent according to any one of claims 1 to 3, and an appropriate amount of water is added to the mixture to knead the mixture to solidify the waste incineration dust ash solidification treatment method.