JPH09251706A - Turntable - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a turntable which has a high coefft. of friction and and is improved in the deflection accuracy of a disk contact part by forming the turntable by injection molding of a resin compsn. consisting of a thermoplastic resin and a thermoplastic elastomer at a specific mixing ratio. SOLUTION: The turntable 11 has a shape symmetrical with a shaft 13 at a center and comes into contact with a disk with the surface 12 exists at its top end. This turntable 11 is formed by injection molding of the resin compsn. contg. the thermoplastic resin and the thermoplastic elastomer. The mixing ratio of the resin compsn. is preferably 40 to 80 pts.wt., more preferably 60 to 80 pts.wt. thermoplastic resin per 100 pts.wt. resin compsn. The content of the thermoplastic elastomer is preferably 60 to 20 pts.wt., more hydrophilic 40 to 20 pts.wt. Inorg. or org. fibrous fillers and power fillers are added to the thermoplastic resin and the thermoplastic elastomer in order to prevent the occurrence of creep. As a result, the turntable having the high friction coefft. is obtd. and the deflection accuracy of the disk contact part is improved.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】この発明は、ディスク状記録
媒体の情報記録再生装置用のターンテーブルに関し、特
に、ＣＤ−ＲＯＭ、ＤＶＤ用のターンテーブルに関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a turntable for an information recording / reproducing apparatus for a disc-shaped recording medium, and more particularly to a turntable for CD-ROM and DVD.

【０００２】[0002]

【従来の技術】ディスク状の記録媒体を回転させて情報
の記録又は再生を行う情報記録装置、例えば、ＣＤ−Ｒ
ＯＭ、ＤＶＤには、上記装置のスピンドルモータの回転
を正確にディスク状の記録媒体（以下、ディスクと称す
る。）に伝達するため、上記ディスクと上記装置のター
ンテーブルとの間の摩擦係数を大きくしている。2. Description of the Related Art An information recording apparatus, such as a CD-R, for recording or reproducing information by rotating a disk-shaped recording medium.
In the OM and DVD, since the rotation of the spindle motor of the device is accurately transmitted to a disc-shaped recording medium (hereinafter referred to as a disc), the friction coefficient between the disc and the turntable of the device is increased. are doing.

【０００３】この上記ディスクと上記ターンテーブルと
の間の摩擦係数を大きくする方法として、図４に示すよ
うな方法が用いられている。すなわち、図４（ａ）に示
すように、ターンテーブル１の上記ディスクと接触する
面にゴム材からなるシート２を接着する方法や、図４
（ｂ）に示すように、ターンテーブル１の上記ディスク
と接触する面にゴムコーティング３を行う方法が行われ
ている。As a method of increasing the friction coefficient between the disc and the turntable, a method as shown in FIG. 4 is used. That is, as shown in FIG. 4A, a method of adhering the sheet 2 made of a rubber material to the surface of the turntable 1 that contacts the disc,
As shown in (b), a method in which a rubber coating 3 is applied to the surface of the turntable 1 that contacts the disk is used.

【０００４】[0004]

【発明が解決しようとする課題】しかしながら、上記の
方法は、ターンテーブル１を射出成形後、ゴム材シート
２の接着工程、またはゴムコーティング３を行う後工程
が必要となる。また、これらの後工程を行うと、スピン
ドルモータの軸４を中心としたターンテーブル１のバラ
ンスが悪くなり、上記軸４に対するターンテーブル１の
ディスク接触部の振れ精度が悪くなる問題点を生じる。However, the above method requires a step of bonding the rubber material sheet 2 after the injection molding of the turntable 1 or a post-step of performing the rubber coating 3. Further, if these post-processes are carried out, the balance of the turntable 1 around the shaft 4 of the spindle motor is deteriorated, and the runout accuracy of the disk contact portion of the turntable 1 with respect to the shaft 4 deteriorates.

【０００５】そこで、この発明の課題は、ターンテーブ
ル材に高摩擦係数を有する樹脂を用いることにより、後
工程を省略し、ターンテーブルのディスク接触部の振れ
精度を高めることである。SUMMARY OF THE INVENTION Therefore, an object of the present invention is to use a resin having a high friction coefficient for a turntable material, thereby omitting a post-process and improving the runout accuracy of a disk contact portion of the turntable.

【０００６】[0006]

【課題を解決するための手段】上記の課題を解決するた
め、この発明においては、熱可塑性樹脂及び熱可塑性エ
ラストマーを含有する樹脂組成物を射出成形したのであ
る。また、樹脂組成物１００重量部に対し、上記熱可塑
性樹脂を４０〜８０重量部、上記熱可塑性エラストマー
を６０〜２０重量部含有させることができる。さらに、
上記熱可塑性樹脂としてポリカーボネートを用いること
ができ、また、上記熱可塑性エラストマーとしてポリエ
ステル系熱可塑性エラストマーを用いることができる。
さらにまた、上記樹脂組成物に繊維状充填剤又は粉末状
充填剤を含有させることができる。In order to solve the above problems, in the present invention, a resin composition containing a thermoplastic resin and a thermoplastic elastomer is injection molded. Also, 40 to 80 parts by weight of the thermoplastic resin and 60 to 20 parts by weight of the thermoplastic elastomer may be contained with respect to 100 parts by weight of the resin composition. further,
Polycarbonate can be used as the thermoplastic resin, and polyester-based thermoplastic elastomer can be used as the thermoplastic elastomer.
Furthermore, the resin composition may contain a fibrous filler or a powdered filler.

【０００７】ターンテーブル材に高摩擦係数を有する、
熱可塑性樹脂及び熱可塑性エラストマーを含有する樹脂
組成物を用いたので、後工程を省略しても充分な摩擦力
が得られる。また、ゴムの接着工程又はコーティング工
程がないので、このゴムの接着又はコーティングのため
生じていた、ターンテーブルの振れ精度の悪化が防止さ
れるので、スピンドルモータの軸を中心とするターンテ
ーブルのバランスが保持され、ターンテーブルのディス
ク接触部の振れ精度を高めることができる。The turntable material has a high coefficient of friction,
Since the resin composition containing the thermoplastic resin and the thermoplastic elastomer is used, sufficient frictional force can be obtained even if the subsequent steps are omitted. In addition, since there is no rubber bonding or coating process, the deterioration of the turntable run-out accuracy that occurs due to this rubber bonding or coating is prevented, so the balance of the turntable centered on the spindle motor shaft is prevented. Is held, and the swing accuracy of the disk contact portion of the turntable can be improved.

【０００８】[0008]

【発明の実施の形態】以下、この発明の実施形態を図面
を参照して説明する。Embodiments of the present invention will be described below with reference to the drawings.

【０００９】この発明に用いられるターンテーブル１１
は、図１に示すように、軸１３を中心に対称形を有して
おり、その上端にある面１２でディスクと接触する。こ
のターンテーブルに用いられる材料としては、熱可塑性
樹脂及び熱可塑性エラストマーを含有する樹脂組成物が
あげられる。Turntable 11 used in the present invention
Has a symmetry about an axis 13, as shown in FIG. 1, and is in contact with the disc at a surface 12 at its upper end. Examples of the material used for this turntable include a resin composition containing a thermoplastic resin and a thermoplastic elastomer.

【００１０】上記熱可塑性樹脂は、混合される上記熱可
塑性エラストマーが熱分解を起こさない範囲の温度で射
出成形が可能であれば特に限定されないが、ターンテー
ブル１１のディスク接触面１２の摩擦係数をより大きく
するものが好ましい。摩擦係数をより高めるためには、
凝着の点から、互いに接触する材料自体が同種の材料で
あることが好ましい。よって、ディスクに用いられる材
料と同種の材料を用いることが望ましく、現在、ディス
ク材料として広く使用されているポリカーボネートを用
いることが最も望ましい。The thermoplastic resin is not particularly limited as long as it can be injection-molded at a temperature in a range where the thermoplastic elastomer to be mixed does not cause thermal decomposition, but the friction coefficient of the disk contact surface 12 of the turntable 11 is not limited. The larger one is preferable. To increase the friction coefficient,
From the viewpoint of adhesion, it is preferable that the materials that are in contact with each other are the same kind of material. Therefore, it is desirable to use the same material as the material used for the disc, and it is most desirable to use polycarbonate which is widely used as the disc material at present.

【００１１】また、上記熱可塑性エラストマーは、その
使用温度において軟化しないものであれば特に限定され
るものではない。例として、ポリスチレン−ポリブタジ
エン−ポリスチレンブロックコポリマー等のポリスチレ
ン系熱可塑性エラストマー、エチレン−プロピレンゴム
等のポリオレフィン系熱可塑性エラストマー、ポリウレ
タン系熱可塑性エラストマー、ポリエステル系熱可塑性
エラストマー、ポリアミド系熱可塑性エラストマーをあ
げることができる。これらの中でも、耐熱性、耐クリー
プ性、耐油性に優れているポリエステル系熱可塑性エラ
ストマーを用いると、耐熱性、耐クリープ性、耐油性の
効果も得られて好ましい。The thermoplastic elastomer is not particularly limited as long as it does not soften at the temperature of use. Examples include polystyrene-based thermoplastic elastomers such as polystyrene-polybutadiene-polystyrene block copolymers, polyolefin-based thermoplastic elastomers such as ethylene-propylene rubber, polyurethane-based thermoplastic elastomers, polyester-based thermoplastic elastomers, and polyamide-based thermoplastic elastomers. You can Among these, it is preferable to use a polyester-based thermoplastic elastomer having excellent heat resistance, creep resistance and oil resistance because the effects of heat resistance, creep resistance and oil resistance can be obtained.

【００１２】さらに、上記樹脂組成物には、上記熱可塑
性組成物や上記熱可塑性エラストマーに加えて、クリー
プが生じるのを防止するため、繊維状充填材や粉末状充
填材を用いることもできる。この繊維状充填材は、無機
物又は有機物からなるものであり、例として、ガラス繊
維又はアラミド繊維等があげられる。また、粉末状充填
材とは、無機物又は有機物からなるものであり、例とし
て、炭酸カルシウム粉末又はポリイミド樹脂粉末等があ
げられる。Further, in addition to the thermoplastic composition and the thermoplastic elastomer, a fibrous filler or a powder filler may be used in the resin composition in order to prevent the occurrence of creep. This fibrous filler is made of an inorganic material or an organic material, and examples thereof include glass fiber or aramid fiber. The powdery filler is made of an inorganic material or an organic material, and examples thereof include calcium carbonate powder or polyimide resin powder.

【００１３】これらの混合比率としては、上記樹脂組成
物１００重量部に対し、上記熱可塑性樹脂４０〜８０重
量部がよく、６０〜８０重量部が好ましい。また、上記
熱可塑性エラストマー６０〜２０重量部がよく、４０〜
２０重量部が好ましい。上記熱可塑性樹脂が８０重量部
より多いと、射出成形で得られるターンテーブルの摩擦
係数が小さくなり好ましくない。さらに、４０重量部よ
り少ないと、射出成形で得られるターンテーブルの曲げ
弾性率が小さくなり、応力緩和やクリープ現象が大きく
なり、上記樹脂組成物を精度高く成形することが難しく
なる場合が生じ、バランスのよい成形品が得にくくな
る。The mixing ratio of these is preferably 40 to 80 parts by weight of the thermoplastic resin, and more preferably 60 to 80 parts by weight with respect to 100 parts by weight of the resin composition. Further, the thermoplastic elastomer is preferably 60 to 20 parts by weight, and 40 to
20 parts by weight are preferred. When the amount of the thermoplastic resin is more than 80 parts by weight, the friction coefficient of the turntable obtained by injection molding becomes small, which is not preferable. Further, if the amount is less than 40 parts by weight, the bending elastic modulus of the turntable obtained by injection molding becomes small, stress relaxation and creep phenomenon become large, and it may be difficult to mold the resin composition with high accuracy. It becomes difficult to obtain a well-balanced molded product.

【００１４】また、上記熱可塑性エラストマーが２０重
量部より少ないと、射出成形で得られるターンテーブル
の摩擦係数が小さくなり好ましくない。さらに、６０重
量部より多いと、射出成形で得られるターンテーブルの
曲げ弾性率が小さくなり、応力緩和やクリープ現象が大
きくなり、上記樹脂組成物を精度高く成形することが難
しくなる場合が生じ、バランスのよい成形品が得にくく
なる。When the amount of the thermoplastic elastomer is less than 20 parts by weight, the friction coefficient of the turntable obtained by injection molding becomes small, which is not preferable. Further, if it is more than 60 parts by weight, the bending elastic modulus of the turntable obtained by injection molding becomes small, stress relaxation and creep phenomenon become large, and it may be difficult to mold the resin composition with high accuracy. It becomes difficult to obtain a well-balanced molded product.

【００１５】さらに、繊維状充填材や粉末状充填材を添
加する場合、それらの添加量は特に限定されるものでは
ないが、上記樹脂組成物の成形性を損なわない範囲、例
えば、上記熱可塑性組成物及び上記熱可塑性エラストマ
ーの合計量に対して３０重量％以下の量を添加すること
ができる。Further, when the fibrous filler or the powdered filler is added, the addition amount thereof is not particularly limited, but is within a range not impairing the moldability of the resin composition, for example, the above-mentioned thermoplasticity. An amount of 30% by weight or less based on the total amount of the composition and the thermoplastic elastomer can be added.

【００１６】上記樹脂組成物を射出成形することによ
り、この発明のターンテーブルが得られるが、その方法
としては、通常の射出成形機を用いて成形すればよい。
例えば、上記熱可塑性樹脂組成物としてポリカーボネー
トを用い、上記熱可塑性エラストマーとしてポリエステ
ル系熱可塑性エラストマーを用いたときは、射出成形温
度２８０〜３００℃で、所定の金型を用いて射出成形す
ることにより、ターンテーブルを得ることができる。The turntable of the present invention can be obtained by injection molding the above resin composition. As a method therefor, a usual injection molding machine may be used for molding.
For example, when polycarbonate is used as the thermoplastic resin composition and polyester-based thermoplastic elastomer is used as the thermoplastic elastomer, injection molding is performed at a temperature of 280 to 300 ° C. using a predetermined mold. , You can get a turntable.

【００１７】[0017]

【実施例】以下に、この発明の実施例を説明する。 （実施例１、比較例１〜４）表１に示す割合でポリカー
ボネート及び熱可塑性エラストマーを配合して樹脂組成
物とし、表１に記載の温度条件で、射出成形を行った。
このとき、射出成形品の摩擦の度合いを調べるため、図
１に示すターンテーブル１１ではなく、図２に示すよう
な円筒体１４を成形した。この円筒体１４を用いて、下
記の方法により、回転トルクを測定し、摩擦の度合いを
調べた。その結果を表１に示す。Embodiments of the present invention will be described below. (Example 1, Comparative Examples 1 to 4) Polycarbonate and a thermoplastic elastomer were blended at a ratio shown in Table 1 to obtain a resin composition, and injection molding was performed under the temperature conditions shown in Table 1.
At this time, in order to examine the degree of friction of the injection-molded product, the cylindrical body 14 as shown in FIG. 2 was molded instead of the turntable 11 shown in FIG. Using this cylindrical body 14, the rotational torque was measured and the degree of friction was examined by the following method. Table 1 shows the results.

【００１８】なお、用いたポリカーボネート及び熱可塑
性エラストマーは次の通りである。 １．ポリカーボネート： 帝人化成（株）社製 パンラ
イトＬ−１２５０ ２．熱可塑性エラストマー１：東洋紡績（株）社製
ペルブレンＰ−４５０Ｂ（ポリエステル系） 熱可塑性エラストマー２：東洋紡績（株）社製 ペル
ブレンＰ−２８０Ｂ（ポリエステル系） 熱可塑性エラストマー３：東洋紡績（株）社製 ペル
ブレンＰ−１５０Ｂ（ポリエステル系）。The polycarbonate and thermoplastic elastomer used are as follows. 1. Polycarbonate: Panlite L-1250 manufactured by Teijin Chemicals Ltd. 2. Thermoplastic elastomer 1: manufactured by Toyobo Co., Ltd.
Perbrene P-450B (polyester type) thermoplastic elastomer 2: manufactured by Toyobo Co., Ltd. Perbrene P-280B (polyester type) Thermoplastic elastomer 3: manufactured by Toyobo Co., Ltd. Perbrene P-150B (polyester type).

【００１９】（回転トルク測定法）図３に示す試験装置
を用いて回転トルクを測定した。上記の方法で成形され
た円筒体１４の上端部を静圧空気軸受２２によって支持
された固定ハウジング２１で固定し、軸１３及びプーリ
１７を介してモータ１６と接続されている円板２０に所
定の力で押しつけた。円筒体１４には、図２に示すよう
に穴１５が設けられており、ロードセル１８から出され
る糸１９の先端は固定ハウジング２１の外周面に固定さ
れている。円筒体１４をセットした後、モータ１６を駆
動させて円板２０を回転させる。このとき、円筒体１４
は、当初は円板２０に従って回転するが、次第に円板２
０上を滑るようになる。この滑りが生じるまでの円筒体
１４の回転は、ロードセル１８によって測定される。こ
れらから、円筒体１４の回転トルクを測定した。(Method of Measuring Rotational Torque) Rotational torque was measured using the test apparatus shown in FIG. The upper end of the cylindrical body 14 molded by the above method is fixed by the fixed housing 21 supported by the static pressure air bearing 22, and is fixed to the disc 20 connected to the motor 16 via the shaft 13 and the pulley 17. I pressed it with the power of. The cylindrical body 14 is provided with a hole 15 as shown in FIG. 2, and the tip of the thread 19 discharged from the load cell 18 is fixed to the outer peripheral surface of the fixed housing 21. After setting the cylindrical body 14, the motor 16 is driven to rotate the disc 20. At this time, the cylindrical body 14
Initially rotates according to the disk 20, but gradually the disk 2
You will be able to slide over 0. The rotation of the cylinder 14 until the slip occurs is measured by the load cell 18. From these, the rotational torque of the cylindrical body 14 was measured.

【００２０】（比較例５）ポリカーボネート樹脂（帝人
化成（株）社製：パンライトＬ−１２５０）を用いて、
図２に示す円筒体１４を成形し、その一端に日本合成ゴ
ム（株）社製のＮＢＲゴムＮ２３０Ｓを接着した。この
ゴムを接着した一端を図３の試験機の円板２０にセット
して回転トルクを測定した。その結果を表１に示す。(Comparative Example 5) Polycarbonate resin (manufactured by Teijin Chemicals Ltd .: Panlite L-1250) was used.
The cylindrical body 14 shown in FIG. 2 was molded, and NBR rubber N230S manufactured by Nippon Synthetic Rubber Co., Ltd. was bonded to one end thereof. One end of this rubber adhered was set on the disk 20 of the tester in FIG. 3 to measure the rotational torque. Table 1 shows the results.

【００２１】[0021]

【表１】 [Table 1]

【００２２】（結果）表１より、従来品である比較例５
と比べ、実施例は、若干回転トルクが低いが、ターンテ
ーブル材として充分使用可能であることが明らかとなっ
た。また、比較例１は回転トルクが低かった。このた
め、必要な回転トルクを得るためには、熱可塑性エラス
トマーが必要であることが明らかとなった。さらに、比
較例２〜４は、回転トルクは充分得られたものの、熱可
塑性エラストマーのみで成形されている為、製品形状の
曲げ弾性率、圧縮永久歪や引張強度が低く、部品として
要求される強度、精度の機能を満足することができなか
ったため、ターンテーブル材としては適さないと推測さ
れた。(Results) From Table 1, Comparative Example 5 which is a conventional product
In comparison with Example, it was revealed that the embodiment can be sufficiently used as a turntable material, although the rotational torque is slightly low. Further, Comparative Example 1 had a low rotation torque. Therefore, it has become clear that a thermoplastic elastomer is necessary to obtain the required rotation torque. Further, in Comparative Examples 2 to 4, although the rotational torque was sufficiently obtained, since they were molded only from the thermoplastic elastomer, the bending elastic modulus, compression set and tensile strength of the product shape were low, and they were required as parts. Since it could not satisfy the functions of strength and precision, it was presumed that it was not suitable as a turntable material.

【００２３】[0023]

【発明の効果】この発明によれば、ターンテーブル材に
高摩擦係数を有する、ポリカーボネート及び熱可塑性エ
ラストマーを含有する樹脂組成物を用いたので、後工程
を省略しても充分な摩擦力が得られる。また、ゴムの接
着工程又はコーティング工程がないので、このゴムの接
着又はコーティングのため生じていた、ターンテーブル
の振れ精度の悪化が防止されるので、スピンドルモータ
の軸を中心とするターンテーブルのバランスが保持さ
れ、ターンテーブルのディスク接触部の振れ精度を高め
ることができる。According to the present invention, since a resin composition containing a polycarbonate and a thermoplastic elastomer having a high coefficient of friction is used as a turntable material, a sufficient frictional force can be obtained even if the subsequent steps are omitted. To be In addition, since there is no rubber bonding or coating process, the deterioration of the turntable run-out accuracy that occurs due to this rubber bonding or coating is prevented, so the balance of the turntable centered on the spindle motor shaft is prevented. Is held, and the swing accuracy of the disk contact portion of the turntable can be improved.

【図面の簡単な説明】[Brief description of drawings]

【図１】この発明にかかるターンテーブルの一例を示す
断面図FIG. 1 is a sectional view showing an example of a turntable according to the present invention.

【図２】回転トルク測定に用いられる円筒体の断面図FIG. 2 is a cross-sectional view of a cylindrical body used for measuring rotational torque.

【図３】回転トルクの測定装置FIG. 3 Measuring device for rotational torque

【図４】（ａ）従来のターンテーブルの一例を示す断面
図 （ｂ）従来のターンテーブルの他の一例を示す断面図4A is a sectional view showing an example of a conventional turntable. FIG. 4B is a sectional view showing another example of a conventional turntable.

【符号の説明】[Explanation of symbols]

１ ターンテーブル ２ ゴム材シート ３ ゴムコーティング ４ 軸 １１ ターンテーブル １２ ディスク接触面 １３ 軸 １４ 円筒体 １５ 穴 １６ モータ １７ プーリ １８ ロードセル １９ 糸 ２０ 円板 ２１ 固定ハウジング ２２ 静圧空気軸受 1 Turntable 2 Rubber Material Sheet 3 Rubber Coating 4 Shaft 11 Turntable 12 Disk Contact Surface 13 Shaft 14 Cylindrical Body 15 Hole 16 Motor 17 Pulley 18 Load Cell 19 Thread 20 Disk 21 Fixed Housing 22 Hydrostatic Air Bearing

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 熱可塑性樹脂及び熱可塑性エラストマー
を含有する樹脂組成物を射出成形してなるディスク状記
録媒体の情報記録再生装置用のターンテーブル。1. A turntable for an information recording / reproducing apparatus for a disc-shaped recording medium, which is obtained by injection-molding a resin composition containing a thermoplastic resin and a thermoplastic elastomer. 【請求項２】 上記樹脂組成物１００重量部に対し、上
記熱可塑性樹脂を４０〜８０重量部、上記熱可塑性エラ
ストマーを６０〜２０重量部含有する請求項１に記載の
ターンテーブル。2. The turntable according to claim 1, which contains 40 to 80 parts by weight of the thermoplastic resin and 60 to 20 parts by weight of the thermoplastic elastomer with respect to 100 parts by weight of the resin composition. 【請求項３】 上記熱可塑性樹脂がポリカーボネートで
ある請求項１又は２に記載のターンテーブル。3. The turntable according to claim 1, wherein the thermoplastic resin is polycarbonate. 【請求項４】 上記熱可塑性エラストマーがポリエステ
ル系熱可塑性エラストマーである請求項１〜３のいずれ
かに記載のターンテーブル。4. The turntable according to claim 1, wherein the thermoplastic elastomer is a polyester-based thermoplastic elastomer. 【請求項５】 上記樹脂組成物に繊維状充填剤又は粉末
状充填剤を含有する請求項１〜４のいずれかに記載のタ
ーンテーブル。5. The turntable according to claim 1, wherein the resin composition contains a fibrous filler or a powdered filler.