JPH09241589A - Cushioning, pressure-sensitive adhesive sheet and cushioning structure - Google Patents
Cushioning, pressure-sensitive adhesive sheet and cushioning structureInfo
- Publication number
- JPH09241589A JPH09241589A JP8056023A JP5602396A JPH09241589A JP H09241589 A JPH09241589 A JP H09241589A JP 8056023 A JP8056023 A JP 8056023A JP 5602396 A JP5602396 A JP 5602396A JP H09241589 A JPH09241589 A JP H09241589A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- adhesive sheet
- shock
- adherend
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、粘着シートに関
し、特に衝撃緩和性粘着シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure sensitive adhesive sheet, and more particularly to a shock absorbing pressure sensitive adhesive sheet.
【０００２】[0002]
(１)(規則的な)凹凸パターン付き粘着層を備える粘着シ
ート 実開平６−２００４３号公報には、図５に示すような、
表面シート(１０１)と、独立した複数の小凸部(１０２)
とを含む粘着層を備えた粘着シート(１００)が開示され
ている。小凸部(１０２)の高さは３〜５０μｍ程度と比
較的微小であり、また、図５からも分かる様に、被着体
に貼り付けられた状態では、被着体と粘着層との間に気
密空間を形成せず、また、この様な気密空間を維持する
ことを意図していない。これは、空気を被着体と粘着層
との間に貼り込むことなく容易に貼り付け、貼り付け完
了後は小凸部(１０２)は流動して平坦化され、接着面積
を増加させて接着力を高めることを企図しているからで
ある。(1) Adhesive sheet provided with (regular) adhesive layer with concave-convex pattern As disclosed in Japanese Utility Model Publication No. 6-200443, as shown in FIG.
Top sheet (101) and multiple independent small protrusions (102)
An adhesive sheet (100) provided with an adhesive layer including and is disclosed. The height of the small convex portion (102) is relatively small, about 3 to 50 μm, and, as can be seen from FIG. 5, when it is attached to the adherend, the adherend and the adhesive layer are separated from each other. It does not form an airtight space between them, nor is it intended to maintain such an airtight space. This is because it is easy to attach air without adhering it between the adherend and the adhesive layer, and after the attachment is completed, the small convex portion (102) flows and is flattened, increasing the adhesion area and adhering. This is because they intend to increase their power.
【０００３】特開平３−１８１１５７８(米国特許５,１
４１,７９０号に対応)には、図６に示すような、粘着層
(２０１)に、複数の粒子集団(２０２)を先端部に含む複
数の突部(２０３)を備える位置調整性接着テープ(２０
０)が開示されている。この接着テープでは、突部(２０
３)間の間隔を０.１〜０.５ｍｍとすることにより、突
部間の凹部分の接着面(２０４)が被着体と接触すること
なく、良好な位置調整性が得られることが示唆されてい
る。しかしながら、上記粘着シートと同様に、位置調整
完了後は突部(２０３)は流動して平坦化されことを意図
しており、したがって、被着体と粘着層との間に気密空
間を形成し、接着テープを被着体に貼り付けた状態で使
用する間に気密空間を維持することはできない。Japanese Unexamined Patent Publication No. 3-181578 (US Pat.
(Corresponding to No. 41,790), an adhesive layer as shown in FIG.
(201) A position-adjustable adhesive tape (20) comprising a plurality of protrusions (203) including a plurality of particle groups (202) at the tip.
0) is disclosed. With this adhesive tape, the protrusion (20
By setting the interval between 3) to be 0.1 to 0.5 mm, it is possible to obtain good position adjustability without the adhesive surface (204) of the concave portion between the protrusions coming into contact with the adherend. Has been suggested. However, like the above-mentioned pressure-sensitive adhesive sheet, the projection (203) is intended to flow and be flattened after the position adjustment is completed, and therefore, an airtight space is formed between the adherend and the pressure-sensitive adhesive layer. , The airtight space cannot be maintained while the adhesive tape is used while being attached to the adherend.
【０００４】実開平１−７０８４８号公報では、支持体
と粘着剤層とからなる粘着テープにおいて、壁紙等の平
らでない被着体表面への接着面積を高める目的で、粘着
剤層に網目模様等の規則的形状を有する凹凸を設けるこ
とが提案されている。しかしながら、この公報には、そ
の網目模様の凹凸による気密空間の形成については言及
されていない。In Japanese Utility Model Laid-Open No. 1-70848, in a pressure-sensitive adhesive tape comprising a support and a pressure-sensitive adhesive layer, a mesh pattern or the like is formed on the pressure-sensitive adhesive layer for the purpose of increasing the adhesion area to an uneven surface of an adherend such as wallpaper. It has been proposed to provide irregularities having a regular shape. However, this publication does not mention the formation of the airtight space due to the unevenness of the mesh pattern.
【０００５】特開平７−１２６５８２には、支持体と、
支持体上に設けられた、表面に１ｍｍピッチ以下の、規
則的な形状と配置の凹凸を有する粘着剤層とを備えてな
る粘着テープが開示されている。この凹凸は、２０μｍ
以下の高さの凸部と、深さが凸部の高さの１０〜９０％
である凹部からなる非常に微細な構造を有し、粘着剤
は、ｎ−ブチルアクリレート−アクリル酸共重合体と、
共重合体１００ｇに対して１ｇの割合のポリイソシアネ
ート化合物とからなる。この粘着テープの粘着剤層の凹
凸は、被着体に接着後も実質的に変形しないので、支持
体を通して文字、数字、図形、記号等として視認するこ
とができる。しかしながら、この様な凹凸では、非常に
小さな気密空間しか形成できず、衝撃緩和能はない。Japanese Patent Application Laid-Open No. 7-126582 discloses a support and
Disclosed is a pressure-sensitive adhesive tape comprising a pressure-sensitive adhesive layer provided on a support and having a regular shape and arrangement of irregularities having a pitch of 1 mm or less on the surface. This unevenness is 20 μm
10 to 90% of the height of the convex part with the following height and the depth of the convex part
It has a very fine structure consisting of concave portions, and the adhesive is n-butyl acrylate-acrylic acid copolymer,
It is composed of a polyisocyanate compound in a ratio of 1 g per 100 g of the copolymer. Since the unevenness of the pressure-sensitive adhesive layer of this pressure-sensitive adhesive tape is not substantially deformed even after being adhered to the adherend, it can be visually recognized as characters, numbers, figures, symbols, etc. through the support. However, with such unevenness, only a very small airtight space can be formed, and there is no impact relaxation capability.
【０００６】国際特許公開ＷＯ９５／１１９４５号公報
には、約１×１０-3ｍｍ3の容積の空間を被着体との間
に形成可能なミクロ構造(microstructured)表面を持つ
粘着層を有する物品が開示されている。この粘着層は、
９０部のイソオクチルアクリレートと、１０部のアクリ
ル酸と、比較的少量の架橋剤(０.１部の１,６−ヘキサ
ンジオールジアクリレート)とを原料モノマーとしてＵ
Ｖ重合により形成される。また、国際特許公開ＷＯ９５
／１１６５５号公報には、上記と同様なミクロ構造表面
を持つ粘着層を有するテープが開示されている。International Patent Publication No. WO95 / 11945 discloses an article having an adhesive layer having a microstructured surface capable of forming a space having a volume of about 1 × 10 −3 mm 3 with an adherend. Is disclosed. This adhesive layer is
90 parts of isooctyl acrylate, 10 parts of acrylic acid, and a relatively small amount of a cross-linking agent (0.1 part of 1,6-hexanediol diacrylate) were used as raw material monomers.
It is formed by V polymerization. Also, International Patent Publication WO95
/ 11655 discloses a tape having an adhesive layer having a microstructured surface similar to that described above.
【０００７】これらミクロ構造表面を有する粘着製品
も、非常に小さな気密空間しか形成できないので衝撃緩
和能はない。Adhesive products having these microstructured surfaces are also not shock-absorbing because they can form only very small airtight spaces.
【０００８】(２)衝撃緩和シート等 一方、複数の(すなわち多数の)、比較的大きな容積の気
密空間や凹凸部を略全面に備える様にポリマー材料から
形成され、衝撃、振動(音を含む)、熱等の外的作用を吸
収、減衰または緩和することができるシート材料が広く
知られている。これらは、衝撃緩和材(クッション材、
緩衝材を含む)の他、防振材(制振材)、防音材(吸音材、
遮音材)、または保温材(断熱材)として利用される材料
である。また、通常、これらの機能のいずれか１つ、若
しくはこれら２以上の機能を複合的に有することができ
る。(2) Impact-Relieving Sheet, etc. On the other hand, it is formed of a polymer material so as to have a plurality of (that is, a large number of) air-tight spaces of relatively large volume and uneven portions on almost the entire surface, and shocks, vibrations (including sound) ), Sheet materials capable of absorbing, attenuating or mitigating external effects such as heat are widely known. These are shock absorbing materials (cushion materials,
In addition to cushioning materials), vibration damping materials (vibration damping materials), sound damping materials (sound absorbing materials,
It is a material used as a sound insulating material) or a heat insulating material (heat insulating material). Further, usually, it is possible to have any one of these functions or a composite of two or more of these functions.
【０００９】(２−１)気密空間をシート等が内包してい
るもの 特開昭６３−５３０２４号公報には、複数の独立した小
室を内包した緩衝性素材からなる断熱体層と、その少な
くとも一面に備え付けられた自己接着性プラスチックフ
ィルム層とからなる、ガラス貼着用断熱シートが開示さ
れている。このシートでは、断熱体層は凹凸状の第１の
フィルムと平坦な第２のフィルムを貼り合わせて、凹部
に対応するシート内に密閉された小室が形成されてお
り、窓ガラス等の物体に自己接着性フィルムを介して貼
り付けられる。(2-1) Sheet or the like enclosing an airtight space Japanese Patent Laid-Open No. 63-53024 discloses a heat insulating layer made of a cushioning material containing a plurality of independent small chambers, and at least the heat insulating layer. A heat insulating sheet for glass sticking is disclosed, which comprises a self-adhesive plastic film layer provided on one surface. In this sheet, the heat insulation layer is formed by bonding a concave-convex first film and a flat second film to each other to form a sealed small chamber in the sheet corresponding to the concave portion. It is attached via a self-adhesive film.
【００１０】特開平３−４３２４１号公報の防音シート
は、防音性に富んだ材料によって製造され、表面の全面
に凹凸を形成した第１の板状素材の表面に、防音性に富
んだ第２の板状素材を貼り合わせて、両素材間に中空部
を形成することにより、それを通過する音のエネルギー
を減衰し、防音性能を向上させ得ることを教示してい
る。The soundproof sheet disclosed in JP-A-3-43241 is manufactured from a material having a high soundproof property, and a second soundproof sheet is formed on the surface of a first plate-shaped material having irregularities formed on the entire surface thereof. It teaches that the plate-shaped materials of (1) and (2) are bonded to each other to form a hollow portion between the two materials, whereby the energy of sound passing therethrough can be attenuated and the soundproof performance can be improved.
【００１１】実開昭５６−１７６８３０号公報の保温シ
ートは、一方のエンボスフィルムに複数の独立した突起
室がほとんど隙間無く形成され、この突起室の開口部を
密閉する様に他の平坦なフィルムが積層接着され、全面
にわたって独立の、それぞれが約１４〜７,０００ｍｍ3
の容積を有する複数の中空室が形成され、これにより、
すぐれた断熱効果を発揮する。In the heat insulating sheet of Japanese Utility Model Laid-Open No. 56-176830, a plurality of independent projection chambers are formed on one embossed film with almost no gap, and another flat film is formed so as to seal the opening of the projection chamber. Are laminated and adhered, and they are independent over the entire surface, each about 14-7,000 mm 3
A plurality of hollow chambers having a volume of
Exhibits excellent heat insulation effect.
【００１２】実開昭６０−８８７３１号公報には、ガラ
ス等に粘着剤を介して貼り付けられ、立体模様が視認さ
れる立体模様化粧シートが開示されている。この化粧シ
ートは、シートが完全に密着し、下の着色シートの絵柄
が鮮明に見える状態の圧着部と、シートが密着しておら
ず、空隙を形成している非圧着部からなる表面部と、前
記圧着部が圧着される平滑な裏面部をと備え、外圧によ
って容易に凹凸が消えない様に密封された空間をシート
内に有する。[0012] Japanese Utility Model Laid-Open No. 60-88731 discloses a three-dimensional pattern decorative sheet which is attached to glass or the like via an adhesive to make a three-dimensional pattern visible. This decorative sheet includes a pressure-bonded portion in which the sheet is completely adhered and the pattern of the colored sheet below can be clearly seen, and a surface portion which is a non-pressure-bonded portion in which the sheet is not adhered and forms voids. The sheet includes a smooth back surface portion to which the crimp portion is crimped, and has a sealed space in the sheet so that the unevenness is not easily erased by external pressure.
【００１３】これらの断熱シート等の物品は、被着体と
の間に有効な寸法の気密空間を形成するためのものでは
なく、また、被着体との接着には別途接着手段を必要と
する。These articles such as a heat insulating sheet are not for forming an airtight space having an effective size with the adherend, and require an adhering means for adhering to the adherend. To do.
【００１４】(２−２)被着体に接する凹凸部を有するも
の 特開平３−２１３３３４号公報の吸音断熱インシュレー
タは、多孔質材としてグラスウールと、熱可塑性合成フ
ィルムとしてエチレン−酢酸ビニル共重合体を添加した
ポリエチレン樹脂(ＥＶＡＰＧ)を片面に施したフィルム
と軟質ポリウレタンフォームからなる表皮材を積層して
なり、ダッシュパネルの様な複雑な凹凸形状の製品にプ
レス加工が容易で、クッション性も高い。(2-2) Having uneven portions in contact with the adherend The sound absorbing and heat insulating insulator disclosed in Japanese Patent Laid-Open No. 213334/1993 is glass wool as a porous material and an ethylene-vinyl acetate copolymer as a thermoplastic synthetic film. Polyethylene resin with added (EVAPG) on one side is laminated with a skin material made of flexible polyurethane foam, which makes it easy to press on products with complicated irregular shapes such as dash panels and has high cushioning properties. .
【００１５】特開平４−３５１５３８号公報の緩衝材及
びそれを用いてなる防音床材は、発泡倍率の高い発泡ポ
リウレタン樹脂シートの裏面に凹凸合成樹脂シートを積
層接着して緩衝材とし、これを適宜不織布を介して床基
板に接着して、防音効果を向上させる。この床材は、被
着床面に凸部が接する様に配置して使用される。The cushioning material and the soundproofing flooring material using the cushioning material disclosed in JP-A-4-351538 are formed by laminating and bonding a concavo-convex synthetic resin sheet on the back surface of a foamed polyurethane resin sheet having a high expansion ratio to form a cushioning material. The soundproofing effect is improved by appropriately adhering to the floor substrate through a nonwoven fabric. This floor material is used by arranging it so that the convex portion is in contact with the adherend floor surface.
【００１６】実開平４−７９１０５号公報の衝撃緩和シ
ートは、基材接着用突起と、物体上にシート自体を支持
するための突起とをそれぞれ複数備えてなる。このシー
トでは、基材接着用突起の接着面が平坦であるので、基
材と強固に接着させることができ、また、その平坦面
と、シート支持用突起の先端部とが、衝撃緩和シートの
厚さ方向断面で見て、同じ領域に存在しないように配置
されているので、基材に加わった衝撃力が直線的に物体
に伝わらない。ここで、支持用突起は物体表面には接着
させず、物体とシートとの間に気密空間を形成しない様
にして使用される。The impact absorbing sheet disclosed in Japanese Utility Model Laid-Open No. 4-79105 comprises a plurality of base material bonding projections and a plurality of projections for supporting the sheet itself on an object. In this sheet, since the bonding surface of the base material bonding projection is flat, it can be firmly bonded to the base material, and the flat surface and the tip end portion of the sheet supporting projection are the same as those of the shock absorbing sheet. The impact force applied to the base material is not linearly transmitted to the object because they are arranged so that they do not exist in the same region when viewed in the thickness direction cross section. Here, the supporting projections are not adhered to the surface of the object and are used so as not to form an airtight space between the object and the sheet.
【００１７】これらのインシュレータ等の物品の吸音・
断熱等の作用は、もっぱら構成材料または／および突起
の形状に由来し、気密空間を利用したものではない。Sound absorption of these insulators and other articles
The action of heat insulation or the like originates exclusively from the shape of the constituent material and / or the protrusion, and does not utilize the airtight space.
【００１８】(２−３)被着体に自己接着が可能なもの 実開平４−４０７４１号公報には、発泡ポリエチレン等
の弾力性支持材の一方の主要面を凹凸にし、その凹凸面
上に感圧性接着剤を塗布してなる、粘着体が開示されて
いる。この粘着体は、別途接着手段を必要とすることな
く、物体表面に、１００〜５００ｇ／ｃｍ2の粘着力で
接着し固定することができ、物体の保護カバーに適す
る。(2-3) One capable of self-adhesion to an adherend In Japanese Utility Model Laid-Open No. 4-40741, one main surface of an elastic support material such as foamed polyethylene is made uneven, and the uneven surface is provided. A pressure-sensitive adhesive body formed by applying a pressure-sensitive adhesive is disclosed. This adhesive body can be adhered and fixed to the surface of an object with an adhesive force of 100 to 500 g / cm 2 without the need for a separate adhesion means, and is suitable as a protective cover for the object.
【００１９】実開平４−１２６３６９号公報の磁気光学
ディスク内に備え付けられた防振層は、ＵＶ架橋された
イソオクチルアクリレート−アクリル酸共重合体からな
り、少なくとも約２５.４μｍの厚さの接着剤層と、少
なくとも約１０２μｍのポリエステルフィルムとからな
る。この防振層は、少なくとも８５０Ｈｚの振動数での
ディスクの振動を抑制する。The antivibration layer provided in the magneto-optical disk of Japanese Utility Model Laid-Open No. 4-126369 is made of UV-crosslinked isooctyl acrylate-acrylic acid copolymer and has an adhesive thickness of at least about 25.4 μm. It comprises an agent layer and a polyester film having a thickness of at least about 102 μm. The anti-vibration layer suppresses vibration of the disc at a frequency of at least 850 Hz.
【００２０】これらの粘着体および防振層は、粘着性の
ポリマー材料からなり、自己接着性を有するが、貼り付
けられた被着体との間に気密空間を形成するためのもの
ではない。These adhesives and vibration-proof layers are made of an adhesive polymer material and have a self-adhesive property, but they are not for forming an airtight space between the adherend and the adherend.
【００２１】(２−４)被着体との間に気密空間を形成可
能なもの 実開平４−６２５２０号公報には、両面粘着フィルムを
介して２枚の記録媒体を貼り合わせる光情報記録媒体に
おいて、両面粘着フィルムの少なくとも一方の粘着剤層
に凹凸を設け、熱的作用を外界より与えられても、粘着
剤の緩衝効果が媒体の反りによる変形を有効に解消する
ことができることを開示する。しかしながら、粘着剤層
の厚さは１０〜５０μｍ程度が適当とされ、粘着剤層に
より形成される気密空間の容積は比較的小さく、衝撃緩
和能は低い。(2-4) A device capable of forming an airtight space with an adherend Japanese Utility Model Publication No. 4-62520 discloses an optical information recording medium in which two recording media are bonded together via a double-sided adhesive film. In this, it is disclosed that at least one pressure-sensitive adhesive layer of the double-sided pressure-sensitive adhesive film is provided with irregularities, and even if a thermal action is given from the outside, the buffering effect of the pressure-sensitive adhesive can effectively eliminate deformation due to warpage of the medium. . However, it is appropriate that the thickness of the pressure-sensitive adhesive layer is about 10 to 50 μm, the volume of the airtight space formed by the pressure-sensitive adhesive layer is relatively small, and the impact relaxation ability is low.
【００２２】実開平５−７０９３３号公報の空気封入緩
衝材では、図７に示される様に、粘着性フィルム(３０
２)と非粘着性フィルム(３０７)と積層してなり、粘着
性フィルム側に複数の凹部を有する第１の合成樹脂フィ
ルム(３０１)に、その凹部(３０３)の開口部を覆うよう
にして平坦な第２の合成樹脂フィルム(３０４)を粘着性
フィルム(３０５)を介して貼着して独立空気室(３０６)
が形成される。In the air-filled cushioning material of Japanese Utility Model Laid-Open No. 5-70933, as shown in FIG. 7, an adhesive film (30
2) and a non-adhesive film (307) are laminated, and a first synthetic resin film (301) having a plurality of recesses on the adhesive film side is formed so as to cover the opening of the recess (303). Separate flat air chamber (306) by sticking flat second synthetic resin film (304) through adhesive film (305)
Is formed.
【００２３】したがって、合成樹脂フィルムの貼り合わ
せに加熱を必要とせずに、緩衝材を使用する現場で簡単
に完成させることができ、保管や輸送時に嵩張らない。
この粘着性フィルムは、ポリアクリル等の熱可塑性樹脂
に粘着剤を混入して作製する。しかしながら、粘着性フ
ィルムの凹凸に追従した非粘着フィルム(３０７)を用い
ずに、気密空間(空気室)の容積や形状を経時で安定に維
持する有効な手段(たとえば、粘着フィルムの架橋の有
無、その弾性率など)は開示されていない。Therefore, it is possible to easily complete the work at the site where the cushioning material is used, without the need for heating for attaching the synthetic resin film, and it is not bulky during storage and transportation.
This adhesive film is manufactured by mixing an adhesive agent into a thermoplastic resin such as polyacrylic. However, without using the non-adhesive film (307) that follows the unevenness of the adhesive film, an effective means for maintaining the volume and shape of the airtight space (air chamber) stably over time (for example, the presence or absence of crosslinking of the adhesive film) , Its elastic modulus, etc.) is not disclosed.
【００２４】以上をまとめると、従来の粘着シート等の
粘着剤を含む物品では、衝撃緩和、断熱等の効果を発揮
可能な、比較的大きな容積の気密空間の形成は意図され
ていない。In summary, conventional articles containing an adhesive, such as an adhesive sheet, do not intend to form an airtight space having a relatively large volume capable of exerting effects such as impact relaxation and heat insulation.
【００２５】また、比較的大きな容積の気密空間を有す
る、従来の衝撃緩和シート等の物品では、被着体に貼り
付ける前にすでに物品が気密空間を内包しているか、ま
たは／および、被着体に貼り付ける際に別途接着手段を
必要とする。物品自体が気密空間を内包している場合
は、使用前の運搬または貯蔵の際に気密空間から空気が
抜けたり、または気密空間が破損して、衝撃緩和性等の
性能が低下することがある。また、貼り付けの際に別途
接着手段が必要であると、使用の際の作業工程数が増え
て取り扱いが不便である。Further, in the case of a conventional article such as a shock absorbing sheet having a relatively large volume of airtight space, the article already contains the airtight space before being attached to an adherend, and / or A separate adhesive means is required when it is attached to the body. If the article itself contains an airtight space, air may escape from the airtight space during transportation or storage before use, or the airtight space may be damaged, and performance such as shock absorbing properties may deteriorate. . In addition, if a separate bonding means is required for sticking, the number of working steps in use increases, which makes the handling inconvenient.
【００２６】一方、上記実開平５−７０９３３号公報の
緩衝材の様に、貼り付けられた被着体(この場合、平坦
な第２の合成樹脂フィルム(３０４)がそれに相当す
る。)との間に、比較的大きな寸法の気密空間を形成可
能なものもあるが、気密空間を経時で安定に維持するに
は、その空間形状(凹凸)に追従する様に加工された非粘
着フィルムが必要である。On the other hand, like the cushioning material of Japanese Utility Model Laid-Open No. 5-70933, it is attached to an adherend (in this case, the flat second synthetic resin film (304) corresponds thereto). Some of them can form a relatively large size airtight space, but in order to keep the airtight space stable over time, a non-adhesive film processed to follow the space shape (unevenness) is required. Is.
【００２７】ところが、比較的腰の強い非粘着フィルム
と比較的腰の弱い粘着性フィルムとを密着性良く積層
し、凹凸形状を有する様に加工することは容易ではな
く、気密空間の寸法等の設計の自由度が小さくなる。However, it is not easy to laminate a relatively strong non-adhesive film and a relatively weak adhesive film so as to have an uneven shape, and it is not easy to process them so that the size of the airtight space, etc. The degree of freedom in design is reduced.
【００２８】[0028]
【発明が解決しようとする課題】本発明は上記従来の問
題を解決するものであり、その目的とするところは、比
較的大きな容積の気密空間を被着体に貼り付けてその場
で形成し、その気密空間を経時で安定に維持すること
で、衝撃緩和性が経時で低下するおそれがない、衝撃緩
和性粘着シートを提供することにある。SUMMARY OF THE INVENTION The present invention is intended to solve the above-mentioned conventional problems, and an object of the present invention is to form an airtight space having a relatively large volume on an adherend and form it on the spot. The purpose of the present invention is to provide an impact-reducing pressure-sensitive adhesive sheet that maintains its airtight space stably over time so that the impact-reducing property does not decrease over time.
【００２９】[0029]
【課題を解決するための手段】本発明は、(ｉ)基部(１
０)と；(ii)基部(１０)の少なくとも１方の主要面(２)
に、架橋された粘着性ポリマーを含んで成り、複数の幾
何学的形状の凹部(４)を囲む様に立設され、接着面(１
２)を有する凸部(１１)とを；備えた粘着シート(１)に
おいて、上記凹部(４)の容積が０.８〜６００ｍｍ3であ
り、１ｒａｄ／秒の周波数、シェアモードにて動的粘弾
性測定法により測定された該凸部(１１)の弾性率Ｇが２
５℃において５×１０5 〜４×１０6ｄｙｎｅ／ｃｍ2
の範囲であり、２５℃〜１２５℃の範囲でのｌｏｇ10Ｇ
の低下が１.０未満である衝撃緩和性粘着シートを提供
するものであり、そのことにより上記目的が達成され
る。The present invention provides (i) a base (1)
0) and; (ii) at least one major surface (2) of the base (10)
A cross-linking adhesive polymer, which is erected so as to surround the recesses (4) having a plurality of geometric shapes, and the adhesive surface (1
In the pressure-sensitive adhesive sheet (1) provided with the convex portion (11) having the second portion (2), the concave portion (4) has a volume of 0.8 to 600 mm 3 , and is dynamically operated in a share mode at a frequency of 1 rad / sec. The elastic modulus G of the convex portion (11) measured by viscoelasticity measurement method is 2
5 × 10 5 to 4 × 10 6 dyne / cm 2 at 5 ° C.
And the log 10 G in the range of 25 ° C to 125 ° C.
To provide an impact-damping pressure-sensitive adhesive sheet having a decrease of less than 1.0, thereby achieving the above object.
【００３０】上記衝撃緩和性粘着シート(１)を被着物
(３)の表面に接着させることにより、被着物表面と凹部
の内面とから形成される気密空間(４１)を有する衝撃緩
和構造体が提供される。The shock-absorbing pressure-sensitive adhesive sheet (1) is adhered to
By adhering to the surface of (3), an impact absorbing structure having an airtight space (41) formed by the surface of the adherend and the inner surface of the recess is provided.
【００３１】[0031]
【発明の実施の形態】以下、図１及び図２を参照しなが
ら説明する。図１(ａ)は本発明の衝撃緩和性粘着シート
の一例を示す斜視図であり、図１(ｂ)はそのＩ−Ｉ’断
面図である。図２(ａ)及び(ｂ)は、それぞれ本発明の衝
撃緩和構造体の一例を示す断面図である。DETAILED DESCRIPTION OF THE INVENTION A description will be given below with reference to FIGS. FIG. 1 (a) is a perspective view showing an example of the shock-absorbing pressure-sensitive adhesive sheet of the present invention, and FIG. 1 (b) is a sectional view taken along the line II '. 2A and 2B are cross-sectional views showing an example of the shock absorbing structure of the present invention.
【００３２】基部(１０） 基部（１０)は、架橋された粘着性ポリマーを含む凸部
(１１)と同一材料からなり、凸部(１１)と一体に形成さ
れてなる場合、凸部(１１)とは異なり、架橋された粘着
性ポリマーを含む凸部(１１)を固着可能な材料(例、プ
ラスチックフィルム、金属箔等)からなり、いわば、凸
部(１１)の支持体としても機能する場合、の両方の形態
が可能である。しかしながら、衝撃緩和性粘着シートの
製造が容易であり、凸部(１１)と基部(１０)との界面で
の固着力を高め、比較的強い衝撃力の緩和が可能である
点からは、上記の凸部(１１)と基部(１０)とが一体に形
成されているのが好適である。Base (10) The base (10) is a convex portion containing a crosslinked adhesive polymer.
When it is made of the same material as (11) and is formed integrally with the convex portion (11), unlike the convex portion (11), a material capable of fixing the convex portion (11) containing a crosslinked adhesive polymer. (Eg, plastic film, metal foil, etc.), so to speak, both forms are possible when it also functions as a support for the convex portion (11). However, from the viewpoint that the shock-absorbing pressure-sensitive adhesive sheet can be easily manufactured, the fixing force at the interface between the convex portion (11) and the base portion (10) can be increased, and the relatively strong impact force can be relaxed, It is preferable that the convex portion (11) and the base portion (10) are integrally formed.
【００３３】基部(１０)の厚さは、通常０.０５〜３ｍ
ｍ、好適には０.１〜１ｍｍ、特に好適には０.２〜０.
７ｍｍである。基部の厚さが０.０５ｍｍを下回ると気
密空間(４１)の維持性能が低下するおそれがあり、３ｍ
ｍを上回ると衝撃緩和性粘着シートが嵩高になり、取扱
いやすさや貼り付けられた際の外観が損なわれる。本発
明の衝撃緩和性粘着シートは、気密空間(４１)の気密性
が高く、凸部(１１)が所定の弾性率を有するので、比較
的薄いシート状でも衝撃緩和性にすぐれる。The thickness of the base (10) is usually 0.05 to 3 m.
m, preferably 0.1 to 1 mm, particularly preferably 0.2 to 0.2 mm.
7 mm. If the thickness of the base part is less than 0.05 mm, the maintenance performance of the airtight space (41) may be deteriorated, and it may be 3 m.
If it exceeds m, the shock-absorbing pressure-sensitive adhesive sheet becomes bulky, and the easiness of handling and the appearance when attached are impaired. The shock-absorbing pressure-sensitive adhesive sheet of the present invention has a high air-tightness in the airtight space (41) and the convex portion (11) has a predetermined elastic modulus.
【００３４】また、基部(１０)の凸部が設けられていな
い平坦な主要面(５)が粘着性を持たない方が良い場合
は、凸部が設けられていない平坦な主要面(５)上に非粘
着性の可撓性支持体(６)を積層することができる。When it is better that the flat main surface (5) of the base portion (10) on which the convex portion is not provided has no tackiness, the flat main surface (5) on which the convex portion is not provided is formed. A non-sticky flexible support (6) can be laminated on top.
【００３５】凸部(１１) 凸部(１１)の形状は、気密空間(４１)の維持性能を損な
わない限り、あらゆる形状を採用することができる。好
適には、断面形状が略正方形、略矩形、および略台形で
あり、凹部(４)を囲む様な壁状である。これらは、充分
な面積の接着面(１２)を有しつつ、かつ加工性が良好で
ある。The shape of the convex portion (11) projecting portions (11), as long as they do not impair the maintenance performance of the airtight space (41), can be adopted any shape. Preferably, the cross-sectional shape is a substantially square shape, a substantially rectangular shape, and a substantially trapezoidal shape, and is a wall shape surrounding the recess (4). These have good workability while having an adhesive surface (12) with a sufficient area.
【００３６】好ましくは、凸部(１１)は断面形状が幅
０.１〜５ｍｍ、特に０.５〜３ｍｍの矩形である。又は
凸部(１１)は上辺０.１〜５ｍｍ、特に０.２〜３ｍｍ、
底辺０.２〜１０ｍｍ、特に０.５〜７ｍｍの台形であ
る。Preferably, the convex portion (11) has a rectangular cross section with a width of 0.1 to 5 mm, especially 0.5 to 3 mm. Alternatively, the convex portion (11) has an upper side of 0.1 to 5 mm, particularly 0.2 to 3 mm,
The trapezoid has a base of 0.2 to 10 mm, especially 0.5 to 7 mm.
【００３７】凸部(１１)は、図１に示す様に、基部(１
０)の端縁に設け、被着物に貼り付けた時に全面に気密
空間を形成できるようにすることもできるが、基部(１
０)の端縁に凸部を形成せず、剥離を容易にするための
手掛りを残してもよい。As shown in FIG. 1, the convex portion (11) has a base portion (1).
It is also possible to provide it on the edge of (0) so that an airtight space can be formed on the entire surface when it is attached to an adherend.
No protrusion may be formed on the edge of (0), and a clue for facilitating peeling may be left.
【００３８】凸部(１１)の弾性率 １ｒａｄ／秒の周波数、シェアモードにて、動的粘弾性
測定法により測定された凸部(１１)の弾性率Ｇは、２５
℃において５×１０5〜４×１０6ｄｙｎｅ／ｃｍ2、好
ましくは６×１０5〜２×１０6ｄｙｎｅ／ｃｍ2、更に
好ましくは６.１×１０5〜１.５×１０6ｄｙｎｅ／ｃｍ
2である。また、２５℃〜１２５℃の範囲でのｌｏｇ10
Ｇの低下が１.０未満、好ましくは０.５未満、更に好ま
しくは０.４未満である。これにより、衝撃緩和性粘着
シート(１)を被着体表面(３１)に接着して、夫々が所定
容積を有する複数の独立した気密空間(４１)を形成し、
外力を加えない状態にて放置した場合に、その気密空間
(４１)の容積および形状の経時での安定な維持が可能と
なる。 Elastic modulus of the convex portion (11) The elastic modulus G of the convex portion (11) measured by the dynamic viscoelasticity measuring method in the shear mode at a frequency of 1 rad / sec is 25.
5 × 10 5 to 4 × 10 6 dyne / cm 2 , preferably 6 × 10 5 to 2 × 10 6 dyne / cm 2 , and more preferably 6.1 × 10 5 to 1.5 × 10 6 dyne / cm
2 Also, log 10 in the range of 25 ° C to 125 ° C
The decrease in G is less than 1.0, preferably less than 0.5, and more preferably less than 0.4. Thereby, the shock-absorbing pressure-sensitive adhesive sheet (1) is adhered to the adherend surface (31) to form a plurality of independent airtight spaces (41) each having a predetermined volume,
Airtight space when left without applying external force
The volume and shape of (41) can be stably maintained over time.
【００３９】弾性率Ｇが５×１０5ｄｙｎｅ／ｃｍ2未満
では、衝撃緩和性粘着シートを被着体表面(３１)に接着
した後、凸部(１１)が経時で塑性流動し、気密空間(４
１)の形成が不可能となり、反対に、弾性率Ｇが４×１
０6ｄｙｎｅ／ｃｍ2を超えると凸部(１１)の接着性が低
下し、衝撃緩和性粘着シート(１)と被着体表面(３１)と
の界面における気密性が得られない。When the elastic modulus G is less than 5 × 10 5 dyne / cm 2 , after the impact-relieving pressure-sensitive adhesive sheet is adhered to the adherend surface (31), the protrusions (11) plastically flow over time, resulting in an airtight space. (4
1) cannot be formed, on the contrary, the elastic modulus G is 4 × 1.
When it exceeds 0 6 dyne / cm 2 , the adhesiveness of the convex portions (11) is deteriorated, and the airtightness at the interface between the shock-absorbing pressure-sensitive adhesive sheet (1) and the adherend surface (31) cannot be obtained.
【００４０】また、衝撃緩和性粘着シート(１)が衝撃緩
和構造を構成する場合は、好適には凸部(１１)の２５℃
における弾性率Ｇは、６×１０5〜２×１０6ｄｙｎｅ／
ｃｍ2の範囲である。この範囲から外れた場合、衝撃緩
和性能の顕著な向上が期待できないからである。When the shock-absorbing pressure-sensitive adhesive sheet (1) constitutes a shock-absorbing structure, it is preferable that the convex portion (11) is at 25 ° C.
The elastic modulus G at 6 × 10 5 to 2 × 10 6 dyne /
cm 2 . This is because if it deviates from this range, a remarkable improvement in impact relaxation performance cannot be expected.
【００４１】一方、凸部(１１)の２５℃〜１２５℃の範
囲でのｌｏｇ10Ｇの低下が１.０より大きいと、すなわ
ち、ｌｏｇ10Ｇのこの温度範囲での変動が−１.０を下
回ると、接着された衝撃緩和性粘着シートにおいて凸部
(１１)が経時で塑性流動し、気密空間(４１)の維持が不
可能となる。ｌｏｇ10Ｇがまったく低下しないか、若し
くは上昇する場合はこの様な塑性流動は生じない。しか
しながら、凸部(１１)の弾性率(すなわち、ｌｏｇ10Ｇ)
が上昇する場合は、衝撃緩和性粘着シートの形成時に粘
着性ポリマーの架橋が不十分であり、経時で架橋が進む
ことが考えられ、架橋の進行は経時での接着力の低下を
招く。したがって、ｌｏｇ10Ｇの上昇は好適には＋１.
０以下である。On the other hand, when the decrease of log 10 G in the range of 25 ° C. to 125 ° C. of the convex portion (11) is larger than 1.0, that is, the variation of log 10 G in this temperature range is -1.0. If it falls below the range of
(11) plastically flows over time, and it becomes impossible to maintain the airtight space (41). If log 10 G does not decrease at all or rises, such plastic flow does not occur. However, the elastic modulus of the convex portion (11) (that is, log 10 G)
In the case where the impact-reducing pressure-sensitive adhesive sheet is formed, the adhesive polymer is insufficiently crosslinked, and it is considered that the crosslinking progresses over time, and the progress of crosslinking causes a decrease in adhesive strength over time. Therefore, a log 10 G rise is preferably +1.
0 or less.
【００４２】凹部(４) 凹部(４)は基部の表面及び凸部の側面で囲まれた空間を
形成する。凹部は、夫々が０.８〜６００ｍｍ3、好まし
くは０.９〜１５０ｍｍ3、更に好ましくは１.０〜１０
ｍｍ3の範囲の容積を有する。凹部の容積が１ｍｍ3を下
回ると、衝撃緩和性粘着シートの衝撃緩和能(衝撃力を
緩和する能力)が低下する。反対に、６００ｍｍ3を超え
る場合は、経時で凹部(４)が塑性変形し、また、衝撃緩
和作用も低下する。Recess (4) The recess (4) forms a space surrounded by the surface of the base and the side surface of the protrusion. The recesses each have a thickness of 0.8 to 600 mm 3 , preferably 0.9 to 150 mm 3 , and more preferably 1.0 to 10.
It has a volume in the range of mm 3 . When the volume of the concave portion is less than 1 mm 3 , the impact relaxation ability (ability to absorb impact force) of the impact relaxation adhesive sheet decreases. On the other hand, when it exceeds 600 mm 3 , the concave portion (4) is plastically deformed with time, and the impact relaxation action is also reduced.
【００４３】凹部(４)の配置個数等 凹部(４)は、好適には、基部(１０)の主要面(２)のほぼ
全面にわたり均一に配置される。これにより、凹部(４)
の気密空間維持性能が効果的に高められる。凹部(４)の
配置は、たとえば、格子模様状及び千鳥状(市松模様状)
に規則的に配置することができる。単位面積当たりの凹
部(４)の個数は、通常１〜５０個／ｃｍ2、好適には２
〜２５個／ｃｍ2である。凹部(４)の個数が２個／ｃｍ2
を下回ると衝撃緩和能が低下するおそれがあり、反対に
２５個／ｃｍ2を上回ると凹部(４)の容積が小さくなる
ので衝撃緩和能が低下するおそれがある。The number of recesses (4) arranged, etc. The recesses (4) are preferably arranged uniformly over substantially the entire main surface (2) of the base (10). This allows the recess (4)
The airtight space maintenance performance of is effectively enhanced. The arrangement of the recesses (4) is, for example, a lattice pattern or a staggered pattern (checkered pattern).
Can be arranged regularly. The number of recesses (4) per unit area is usually 1 to 50 / cm 2 , preferably 2
~ 25 / cm 2 . The number of recesses (4) is 2 / cm 2
If it is less than 25, the impact relaxation ability may be lowered, and on the other hand, if it is more than 25 / cm 2 , the volume of the concave portions (4) may be reduced, so that the impact relaxation ability may be reduced.
【００４４】凹部(４)の深さ、すなわち、凸部(１１)の
高さは、通常０.５〜１０ｍｍ、好適には０.７〜２ｍｍ
である。この深さが０.５ｍｍを下回ると有効な衝撃緩
和作用が得られないおそれがあり、１０ｍｍを上回ると
気密空間維持性能が低下するおそれがある。The depth of the concave portion (4), that is, the height of the convex portion (11) is usually 0.5 to 10 mm, preferably 0.7 to 2 mm.
It is. If the depth is less than 0.5 mm, an effective shock absorbing action may not be obtained, and if it exceeds 10 mm, the airtight space maintaining performance may be deteriorated.
【００４５】凹部(４)には、種々の形状を採用すること
ができる。たとえば、円柱、角柱、角錐、円錐、角錐
台、円錐台、亜球体、亜楕円体等の幾何学的立体であ
る。凹部(４)は、これらの形状からなる群から選ばれた
１種、または２種以上からなる複合形状を採用すること
ができる。Various shapes can be adopted for the recess (4). For example, it is a geometric solid such as a cylinder, a prism, a pyramid, a cone, a truncated pyramid, a truncated cone, a subsphere, or a subellipsoid. The recessed part (4) can adopt a single shape selected from the group consisting of these shapes or a composite shape composed of two or more kinds.
【００４６】また、透明な被着体に貼り付けられた場
合、若しくは透明な基部を備える衝撃緩和性粘着シート
である場合、複数の凹部(４)を含んでなる空間群は１種
の立体模様として看者の視覚を通じて認識される。した
がって、本発明の効果を損なわない範囲において、上記
空間群は、意匠性を備える様に、幾何学配列模様、文
字、数字、図形、記号の表示等の形態をとることができ
る。Further, in the case of being attached to a transparent adherend, or in the case of a shock-absorbing pressure-sensitive adhesive sheet having a transparent base, the space group including a plurality of recesses (4) is one kind of three-dimensional pattern. Is perceived through the eyes of the viewer. Therefore, as long as the effect of the present invention is not impaired, the space group can have a form such as a geometric arrangement pattern, display of letters, numbers, figures, and symbols so as to have designability.
【００４７】粘着性ポリマー 架橋された粘着性ポリマーを含んで成る凸部(１１)は、
被着体表面(３１)と確実に接着し、所定容積の空気を内
部に密封し、気密空間(４１)を維持する。気密空間(４
１)内部の空気の漏出には、(ｉ)凸部(１１)と被着体表
面(３１)との接着界面に隙間が有り、そこから漏れ出る
場合と、(ii)凸部(１１)を透過して外へ抜け出る場合と
がある。 Adhesive Polymer The protrusions (11) comprising a crosslinked adhesive polymer are
The surface of the adherend (31) is securely adhered, a predetermined volume of air is sealed inside, and the airtight space (41) is maintained. Airtight space (4
1) When air leaks inside, (i) there is a gap at the adhesive interface between the convex portion (11) and the surface of the adherend (31), and there is leakage from that, and (ii) the convex portion (11) In some cases, it may pass through and escape to the outside.
【００４８】架橋された粘着性ポリマーは、接着性にす
ぐれ、凸部(１１)の形状維持性能を高め、かつ空気の遮
蔽性(非透過性)を向上させ、すなわち気密性を高める。
また、所定範囲に制御された貯蔵弾性率とその低下割合
は、凸部(１１)に適度な凝集力を付与し、空気の遮蔽性
を高める。The crosslinked tacky polymer has excellent adhesiveness, enhances the shape maintaining ability of the convex portion (11), and improves the air shielding property (impermeable property), that is, the airtightness is enhanced.
In addition, the storage elastic modulus controlled within a predetermined range and the rate of decrease thereof impart an appropriate cohesive force to the convex portion (11) and enhance the air shielding property.
【００４９】好適な実施形態において、架橋された粘着
性ポリマーは、アルキル(メタ)アクリレートと、エチレ
ン性不飽和酸と、２以上の(メタ)アクリル基を分子内に
有する架橋剤モノマーとから実質的になるモノマー成分
の重合により生成した、架橋アクリル系ポリマーであ
る。架橋アクリル系ポリマーは、気密性に特にすぐれ
る。この様な気密性は、上記架橋剤モノマーの含有量
が、モノマー成分全体に対して０.５〜５重量％の範囲
である場合に特に高められる。０.５重量％未満では空
気遮蔽性と形状維持性が低下する傾向があり、反対に５
重量％を超えると接着性が低下する傾向がある。この様
な観点から、特に好適な架橋剤モノマーの範囲は、０.
７〜２重量％である。In a preferred embodiment, the crosslinked tacky polymer consists essentially of an alkyl (meth) acrylate, an ethylenically unsaturated acid and a crosslinker monomer having two or more (meth) acrylic groups in the molecule. It is a crosslinked acrylic polymer produced by the polymerization of a monomer component that becomes The crosslinked acrylic polymer is particularly excellent in hermeticity. Such airtightness is particularly enhanced when the content of the crosslinking agent monomer is in the range of 0.5 to 5% by weight based on the whole monomer components. If it is less than 0.5% by weight, the air-shielding property and the shape-retaining property tend to be deteriorated.
If it exceeds the weight%, the adhesiveness tends to decrease. From this point of view, a particularly preferable range of the crosslinking agent monomer is 0.1.
It is 7 to 2% by weight.
【００５０】アルキル(メタ)アクリレートとしては、イ
ソオクチルアクリレートが好適である。イソオクチルア
クリレートは、凸部(１１)の接着面(１２)に効果的に粘
着性を付与し、衝撃緩和性粘着シートの貼り付け操作を
容易にするからである。この他のアルキル(メタ)アクリ
レートとして、アルキル基が、メチル、エチル、イソプ
ロピル、ブチル、イソブチル、イソオクチル、２−メチ
ルブチル、２−エチルヘキシル、ラウリル、ステアリ
ル、シクロヘキシル、イソボルニル、２−ヒドロキシエ
チル、２−ヒドロキシプロピル、３−クロロ−２−ヒド
ロキシプロピル、ヒドロキシエトキシエチル、メトキシ
エチル、エトキシエチル、ジメチルアミノエチル、ジエ
チルアミノエチル、グリシジル、のうちのいずれか１つ
であるアルキルアクリレートまたはアルキルメタクリレ
ートの１種またはこれらから選ばれた２種以上の混合物
が使用できる。Isooctyl acrylate is preferred as the alkyl (meth) acrylate. This is because isooctyl acrylate effectively gives tackiness to the adhesive surface (12) of the convex portion (11) and facilitates the sticking operation of the shock-absorbing pressure-sensitive adhesive sheet. As the other alkyl (meth) acrylate, an alkyl group is methyl, ethyl, isopropyl, butyl, isobutyl, isooctyl, 2-methylbutyl, 2-ethylhexyl, lauryl, stearyl, cyclohexyl, isobornyl, 2-hydroxyethyl, 2-hydroxy. Propyl, 3-chloro-2-hydroxypropyl, hydroxyethoxyethyl, methoxyethyl, ethoxyethyl, dimethylaminoethyl, diethylaminoethyl, glycidyl, any one of alkyl acrylate or alkyl methacrylate, or from these. Mixtures of two or more selected can be used.
【００５１】エチレン性不飽和酸は、(メタ)アクリル酸
が好適である。(メタ)アクリル酸は、粘着性ポリマーの
凝集力を効果的に高めて、凸部(１１)の形状維持性を向
上させ、気密空間の気密性を効果的に高めるからであ
る。この他のエチレン性不飽和酸として、β−ヒドロキ
シエチルカルボン酸、イタコン酸、マレイン酸、フマー
ル酸、の１種またはこれらから選ばれた２種以上の混合
物が使用できる。The ethylenically unsaturated acid is preferably (meth) acrylic acid. This is because (meth) acrylic acid effectively enhances the cohesive force of the adhesive polymer, improves the shape retention of the protrusions (11), and effectively enhances the airtightness of the airtight space. As the other ethylenically unsaturated acid, one of β-hydroxyethylcarboxylic acid, itaconic acid, maleic acid and fumaric acid, or a mixture of two or more selected from them can be used.
【００５２】アルキル(メタ)アクリレート(Ａ)とエチレ
ン性不飽和酸(Ｅ)との配合割合は、凸部(１１)の弾性率
が所定の範囲になる様に選択されるが、好適にはＡ：Ｅ
＝８０：２０〜９９：１の範囲である。The mixing ratio of the alkyl (meth) acrylate (A) and the ethylenically unsaturated acid (E) is selected so that the elastic modulus of the convex portion (11) falls within a predetermined range, but it is preferable. A: E
= 80: 20 to 99: 1.
【００５３】また、２以上の(メタ)アクリル基を分子内
に有する架橋剤モノマーは、１,６−ヘキサンジオール
ジアクリレートが好適である。１,６−ヘキサンジオー
ルジアクリレートは、粘着性ポリマーの架橋密度を効果
的に高めて、接着性、空気遮蔽性および形状維持性をバ
ランス良く向上させることができる。The cross-linking agent monomer having two or more (meth) acrylic groups in the molecule is preferably 1,6-hexanediol diacrylate. 1,6-Hexanediol diacrylate can effectively increase the crosslink density of the adhesive polymer, and improve the adhesion, air-shielding property and shape retention in a well-balanced manner.
【００５４】架橋された粘着性ポリマーは、上記各成分
を含有するモノマー成分を出発原料として、熱により、
または紫外線、電子線等の放射線により重合させて得る
ことができる。たとえば、後述する様に、所定の幾何学
構造を有する型にモノマー成分を接触させながら、型上
で重合および架橋を完了させて衝撃緩和性粘着シート
(１)を形成する。この場合、架橋剤モノマーを含まない
モノマー成分を含有する予備成分を予め部分的に重合さ
せ、粘度調節された部分重合シロップを用意し、このシ
ロップと架橋剤モノマーとの混合物を型と接触させなが
ら、その重合および架橋を完了させることができる。こ
の場合、シロップの粘度は、通常１００〜１００,００
０ｃｐｓである。The crosslinked tacky polymer is prepared by heating a monomer component containing each of the above components as a starting material,
Alternatively, it can be obtained by polymerization with radiation such as ultraviolet rays and electron beams. For example, as will be described later, while the monomer component is brought into contact with a mold having a predetermined geometric structure, polymerization and cross-linking are completed on the mold to give an impact-damping pressure-sensitive adhesive sheet.
Form (1). In this case, preliminarily partially polymerizing a preliminary component containing a monomer component containing no crosslinking agent monomer, to prepare a viscosity-controlled partially polymerized syrup, while the mixture of this syrup and the crosslinking agent monomer is brought into contact with the mold. , Its polymerization and crosslinking can be completed. In this case, the viscosity of the syrup is usually 100-100,00.
0 cps.
【００５５】上記のアクリル系ポリマーの他、粘着性ポ
リマーとして、ポリイソプレン(天然ゴム)、スチレン−
ブタジエンゴム、ブチルゴム、ニトリルゴム、シリコー
ンゴム、ネオプレン、ポリイソブチレン、ポリビニルブ
チルエーテル等のポリビニルエーテル、ポリウレタン、
ポリ酢酸ビニル、エチレン−酢酸ビニル共重合体、ポリ
アルファオレフィン等が使用できる。また、上記粘着性
ポリマーは、１種又は２種以上を混合して用いることが
できる。In addition to the above-mentioned acrylic polymer, polyisoprene (natural rubber), styrene-
Butadiene rubber, butyl rubber, nitrile rubber, silicone rubber, neoprene, polyisobutylene, polyvinyl ether such as polyvinyl butyl ether, polyurethane,
Polyvinyl acetate, ethylene-vinyl acetate copolymer, polyalphaolefin, etc. can be used. Moreover, the said adhesive polymer can be used 1 type or in mixture of 2 or more types.
【００５６】また、アクリル系ポリマーの架橋剤には、
イソシアネート化合物、エポキシ化合物、メラミン化合
物等も使用できる。Further, the acrylic polymer crosslinking agent includes
Isocyanate compounds, epoxy compounds, melamine compounds and the like can also be used.
【００５７】さらに、本発明の別の実施形態では、粘着
性ポリマーと未反応の架橋剤とを含んで成る凸部を有す
る粘着性シートを、被着体に貼り付けた後に架橋反応を
完了させることもできる。Further, in another embodiment of the present invention, the crosslinking reaction is completed after the pressure-sensitive adhesive sheet having the convex portion containing the pressure-sensitive adhesive polymer and the unreacted crosslinking agent is attached to the adherend. You can also
【００５８】また、本発明の効果を損なわない範囲にお
いて、粘着性ポリマーと硬化性樹脂とを併用することが
できる。Further, an adhesive polymer and a curable resin may be used in combination within a range that does not impair the effects of the present invention.
【００５９】さらに、本発明の効果を損なわない範囲に
おいて、粘着性ポリマーと常温で非粘着性の熱可塑性樹
脂とを併用することができる。このような場合、粘着性
ポリマーと熱可塑性樹脂とを含んで成る凸部が、加熱前
には充分な粘着性を有しない場合でも、加熱して粘着性
を増大させて被着体に貼り付けることができる。Further, an adhesive polymer and a non-adhesive thermoplastic resin at room temperature can be used together within a range not impairing the effects of the present invention. In such a case, even if the convex portion containing the tacky polymer and the thermoplastic resin does not have sufficient tackiness before heating, the tackiness is increased by heating and the sticking is performed on the adherend. be able to.
【００６０】衝撃緩和性粘着シート(１)の剥離強度 衝撃緩和性粘着シート(１)を被着体表面(３１)から剥離
する時の２５℃における剥離強度は、２０〜２,５００
ｇ／２５ｍｍの範囲、特に３５０〜２,０００ｇ／２５
ｍｍの範囲であるのが好ましい。２０ｇ／２５ｍｍ未満
であると、被着物の垂直面に貼り付けられたときに空間
(４)の気密性が経時で低下するおそれがある。反対に、
２,５００ｇ／２５ｍｍを超える場合は、貼り付けた直
後の衝撃緩和性粘着シート(１)を剥がすことが困難にな
り、貼り付け位置合わせが困難になる等に起因し操作性
が低下する。 Peel Strength of Impact-Relieving Adhesive Sheet (1) The peel strength at 25 ° C. when peeling the impact-relieving adhesive sheet (1) from the adherend surface (31) is 20 to 2,500.
g / 25 mm range, especially 350-2,000 g / 25
It is preferably in the range of mm. When it is less than 20 g / 25 mm, it has a space when attached to the vertical surface of the adherend.
The airtightness of (4) may decrease with time. Conversely,
If it exceeds 2,500 g / 25 mm, it becomes difficult to peel off the shock-absorbing pressure-sensitive adhesive sheet (1) immediately after sticking, and it becomes difficult to align the sticking position, which lowers the operability.
【００６１】また、一度使用した衝撃緩和性粘着シート
を被着体から剥がして、別の被着体に貼り付けて再度使
用することができれば有利である。すなわち、接着面
(１２)が再剥離性を備え、繰り返し再使用可能な衝撃緩
和材は、省資源の観点から有用である。この様な観点か
ら、特に好適な剥離強度は、５０〜１,０００ｇ／２５
ｍｍである。Further, it is advantageous if the impact-relieving pressure-sensitive adhesive sheet used once can be peeled off from an adherend, adhered to another adherend and reused. That is, the adhesive surface
The impact absorbing material (12) having removability and being reusable repeatedly is useful from the viewpoint of resource saving. From such a viewpoint, a particularly preferable peel strength is 50 to 1,000 g / 25.
mm.
【００６２】作用 基部(１０)と、その基部(１０)の主要面(２)に複数の凹
部(４)を囲む様に立設され架橋された粘着性ポリマーを
含む複数の凸部(１１)とを備えること、凸部の粘着性ポ
リマーのポリマーが架橋されていること、および、この
凸部が所定の弾性率を有することは、別途接着手段を必
要とすることなく、被着体に貼り付けるだけで、気密空
間を使用場所で形成することを可能とし、また、凸部の
塑性変形(自然流動)及び外力による気密空間の変形およ
び消滅を防止し、気密空間の容積および形状を安定に維
持する。The working base (10) and a plurality of protrusions (11) containing an adhesive polymer which is erected so as to surround the plurality of recesses (4) on the main surface (2) of the base (10) and which contains a crosslinked adhesive polymer. That the polymer of the adhesive polymer of the convex portion is crosslinked, and that this convex portion has a predetermined elastic modulus, it is possible to apply the adhesive to an adherend without requiring a separate bonding means. Just by attaching it, it is possible to form an airtight space at the place of use, prevent plastic deformation (natural flow) of the convex part and deformation and disappearance of the airtight space due to external force, and stabilize the volume and shape of the airtight space. maintain.
【００６３】被着体表面(３１)に接着された状態で、凹
部(４)と被着体表面(３１)とで密閉された所定容積の気
密空間が形成される様に凹部(４)が設計されていること
は、基部(１０)の凸部が設けられていない平坦な主要面
(５)側から加えられた衝撃力を、被着体(３)に伝わる前
に緩和する、衝撃緩和作用を発揮する。While being adhered to the adherend surface (31), the recess (4) is formed so as to form an airtight space of a predetermined volume that is sealed by the recess (4) and the adherend surface (31). It is designed to have a flat main surface with no protrusions on the base (10).
It exerts a shock absorbing effect of relaxing the impact force applied from the (5) side before being transmitted to the adherend (3).
【００６４】衝撃緩和性粘着シート 本発明の衝撃緩和性粘着シート(１)は次の様にして使用
される。 Impact-Reducing Adhesive Sheet The impact-reducing adhesive sheet (1) of the present invention is used as follows.
【００６５】凸部(１１)の接着面(１２)と、被着体表面
(３１)とが接する様に衝撃緩和性粘着シート(１)を配置
し、基部(１０)の凸部が設けられていない平坦な主要面
(５)側から手、圧着用ローラなどで軽く圧着させて、接
着面(１２)を被着体表面(３１)に接着させる。凸部(１
１)は粘着性ポリマーを含むので、通常の感圧性接着シ
ートの場合の様な軽い圧着操作により、衝撃緩和性粘着
シート(１)の被着体表面に接着することができる。接着
された衝撃緩和性粘着シート(１)は、凹部(４)と被着体
表面(３１)とに密閉された複数の独立した気密空間(４
１)を形成する。Adhesive surface (12) of convex portion (11) and surface of adherend
The impact-reducing pressure-sensitive adhesive sheet (1) is arranged so as to be in contact with (31), and a flat main surface on which the convex portion of the base (10) is not provided
The side (5) is lightly pressure-bonded with a hand or a pressure roller to bond the adhesive surface (12) to the adherend surface (31). Convex part (1
Since 1) contains an adhesive polymer, it can be adhered to the adherend surface of the shock-absorbing adhesive sheet (1) by a light pressure-bonding operation as in the case of a normal pressure-sensitive adhesive sheet. The bonded shock-absorbing pressure-sensitive adhesive sheet (1) has a plurality of independent airtight spaces (4) which are sealed in the recess (4) and the surface of the adherend (31).
1) is formed.
【００６６】２５℃における凸部(１１)の弾性率(測定
値Ｇ)が５×１０5ｄｙｎｅ／ｃｍ2以上であり、２５℃
〜１２５℃の範囲でのｌｏｇ10Ｇの低下が１.０未満で
あることと、気密空間(４１)が一定の空気圧にて潰れな
い様に支えられていることとが共同して、気密空間(４
１)の形状および容積を維持する。圧着操作は、貼り付
け操作のみで気密空間(４１)が潰れない程度の圧力、た
とえば、１０ｋＰａ未満の範囲で行うことができる。The elastic modulus (measured value G) of the convex portion (11) at 25 ° C. is 5 × 10 5 dyne / cm 2 or more,
The decrease of log 10 G in the range of up to 125 ° C is less than 1.0, and the fact that the airtight space (41) is supported so as not to be crushed by a constant air pressure cooperates with each other. (4
Maintain the shape and volume of 1). The pressure bonding operation can be performed at a pressure such that the airtight space (41) is not crushed only by the bonding operation, for example, within a range of less than 10 kPa.
【００６７】衝撃緩和性粘着シート(１)は、基部(１０)
の凸部が設けられていない平坦な主要面(５)に固着され
た可撓性支持体(６)を有してもよい。衝撃緩和性粘着シ
ート(１)が被着体表面(３１)に接着された形態は、基部
(１０)の凸部が設けられていない平坦な主要面(５)側か
ら加えられた衝撃力を、被着体(３)に伝わる前に緩和す
る衝撃緩和構造として有用である。The shock-absorbing pressure-sensitive adhesive sheet (1) has a base (10).
It may have a flexible support (6) fixed to a flat main surface (5) having no convex portion. The form in which the shock-absorbing pressure-sensitive adhesive sheet (1) is adhered to the adherend surface (31) has a base portion.
It is useful as a shock absorbing structure for relaxing the impact force applied from the side of the flat main surface (5) on which the convex portion (10) is not provided, before being transmitted to the adherend (3).
【００６８】換言すれば、本発明は、衝撃緩和性粘着シ
ート(１)の被着体表面(３１)に接着されて使用される自
己接着性の衝撃緩和材としての利用形態を提供する。こ
の様な場合、可撓性支持体(６)は、衝撃緩和性粘着シー
ト(１)が比較的柔軟性が高く、また、凸部が設けられて
いない平坦な主要面(５)が粘着性を有する場合に、衝撃
緩和性粘着シート(１)の取り扱いを容易にするのに有利
である。In other words, the present invention provides a form of use as a self-adhesive shock absorbing material which is used by being adhered to the adherend surface (31) of the shock absorbing adhesive sheet (1). In such a case, in the flexible support (6), the shock-absorbing pressure-sensitive adhesive sheet (1) has relatively high flexibility, and the flat main surface (5) having no convex portion is adhesive. When it has, it is advantageous for facilitating the handling of the shock-absorbing pressure-sensitive adhesive sheet (1).
【００６９】可撓性支持体(６)には、ポリエステルフィ
ルム、ポリ塩化ビニル(及びその共重合体)フィルム、ポ
リカーボネートフィルム、ポリアミドフィルム、ポリオ
レフィン(及びその共重合体)フィルム、アクリル系共重
合体フィルムなどが使用できる。可撓性支持体(６)の厚
さは、通常１０〜２００μｍの範囲である。また、基部
(１０)の凸部が設けられていない平坦な主要面(５)と可
撓性支持体(６)との界面において、コロナ処理、プライ
マー処理等の易接着処理を行うことができる。The flexible support (6) includes a polyester film, a polyvinyl chloride (and its copolymer) film, a polycarbonate film, a polyamide film, a polyolefin (and its copolymer) film, and an acrylic copolymer. Film etc. can be used. The thickness of the flexible support (6) is usually in the range of 10 to 200 μm. Also the base
At the interface between the flat main surface (5) having no convex portion (10) and the flexible support (6), easy adhesion treatment such as corona treatment or primer treatment can be performed.
【００７０】また、図３(ａ)に示す様に、２つの衝撃緩
和性粘着シートを重ねて貼り合わせて重層構造の衝撃緩
和材とすることもできる。この場合、気密空間(４１)の
他に、緩和材内部の気密室(４４)を有する。この場合、
衝撃緩和効果を高めるために、図３(ｂ)の透過上面図に
示すように、気密室(４４)の周囲を囲む立設壁(１３)
は、気密空間(４１)の略中心に相当する位置にて、下側
衝撃緩和性粘着シートの基部(１０)と接着されるのが好
適である。Further, as shown in FIG. 3 (a), two shock-absorbing pressure-sensitive adhesive sheets may be laminated and bonded together to form a shock-absorbing material having a multilayer structure. In this case, in addition to the airtight space (41), there is an airtight chamber (44) inside the relaxation material. in this case,
In order to enhance the shock absorbing effect, as shown in the transparent top view of FIG. 3 (b), the standing wall (13) surrounding the airtight chamber (44).
Is preferably adhered to the base portion (10) of the lower shock-absorbing pressure-sensitive adhesive sheet at a position corresponding to approximately the center of the airtight space (41).
【００７１】衝撃緩和性粘着シートが貼り付けられて使
用される被着物には、この粘着シートが貼り付けられた
時に有効な気密空間を形成できるような平滑かつ空孔を
含まない表面を有する物を使用する。その材料には、例
えば、ガラス、瀬戸物、プラスチック、金属等が挙げら
れる。The adherend to which the impact-relieving pressure-sensitive adhesive sheet is attached and used has a smooth and void-free surface that can form an effective airtight space when the pressure-sensitive adhesive sheet is attached. To use. Examples of the material include glass, pottery, plastic, metal and the like.
【００７２】本発明の衝撃緩和性粘着シートは、その優
れた衝撃緩和性を有効に利用する実施形態として、被着
物が運搬中に破損することを防止するための梱包材又は
被着物表面の損傷を防止する表面保護材として有用であ
る。特に、窓、机の天板、レンズ、皿、コップ及び花瓶
等の保護用途に適する。本発明の衝撃緩和性粘着シート
はガラス及び瀬戸物に対する接着性に優れ、気密空間の
形成及び保持が特に容易だからである。The shock-absorbing pressure-sensitive adhesive sheet of the present invention, as an embodiment in which its excellent shock-damping property is effectively utilized, damages the packaging material or the surface of the adherend to prevent the adherend from being damaged during transportation. It is useful as a surface protective material for preventing In particular, it is suitable for protecting windows, desk top plates, lenses, plates, cups, vases, etc. This is because the shock-absorbing pressure-sensitive adhesive sheet of the present invention has excellent adhesion to glass and crockery, and it is particularly easy to form and maintain an airtight space.
【００７３】本発明の衝撃緩和性粘着シートは被着物か
らの剥離強度がほとんど無い場合(すなわち、１８０度
剥離強度がゼロ)でも、保持力が所定の範囲であれば使
用できる。例えば、複数のガラス板を重ねて梱包する場
合、２枚のガラス板の間に衝撃緩和性粘着シートを挟
み、ガラス板同士の接触による破損を防止できる。ま
た、水平に配置されたガラス板からなる天板の表面保護
材として使用する場合も、必ずしも高い剥離強度を必要
としない。The impact-damping pressure-sensitive adhesive sheet of the present invention can be used as long as the holding force is within a predetermined range, even when the peel strength from the adherend is almost zero (that is, the 180-degree peel strength is zero). For example, when a plurality of glass plates are stacked and packed, an impact absorbing adhesive sheet can be sandwiched between two glass plates to prevent damage due to contact between the glass plates. Further, even when it is used as a surface protective material for a top plate composed of glass plates arranged horizontally, high peel strength is not always required.
【００７４】このような場合の保持力は、以下の様にし
て測定される。まず、温度２５℃及び湿度６０％ＲＨの
環境中において垂直に立てた生板ガラスの表面に、２５
ｍｍ×５０ｍｍの衝撃緩和性粘着シート(１)を乗せ、全
ての接着面(１２)を接着させる。この衝撃緩和性粘着シ
ート(１)が自重により、接着面(１２)のいずれかに剥離
が生ずるまでの時間を測定する。本発明の衝撃緩和性粘
着シートに好ましい保持力は１０分以上、特に６００分
以上である。The holding force in such a case is measured as follows. First, on the surface of a raw glass plate which was vertically set up in an environment of a temperature of 25 ° C. and a humidity of 60% RH,
A shock-absorbing pressure-sensitive adhesive sheet (1) having a size of mm × 50 mm is placed and all the bonding surfaces (12) are bonded. The time required for peeling of any one of the adhesive surfaces (12) due to its own weight is measured. A preferable holding force for the impact-damping pressure-sensitive adhesive sheet of the present invention is 10 minutes or longer, and particularly 600 minutes or longer.
【００７５】衝撃緩和性粘着シートの製造方法 本発明の好適な実施形態において、衝撃緩和性粘着シー
ト(１)は次の様にして製造する。 Method for Producing Impact-Reducing Adhesive Sheet In the preferred embodiment of the present invention, the impact-reducing adhesive sheet (1) is produced as follows.
【００７６】イソオクチルアクリルレートとアクリル酸
とを所定の割合で含有するモノマー成分と、光開始剤と
からなる予備成分を攪拌装置に内に入れ、攪拌を行いな
がら紫外線重合を行う。この段階では部分的な重合に止
め、その粘度が１００〜１００,０００ｃｐｓの範囲に
なる様にし、部分重合シロップを調製する。このシロッ
プに、所定量の架橋剤モノマー、１,６−ヘキサンジオ
ールジアクリレートと、追加の光開始剤とを添加し、そ
れらが均一になる様に混合し、衝撃緩和性粘着シートの
前駆体組成物を調製する。攪拌装置内は、光重合の際に
は通常窒素ガス等の不活性ガスにてパージされる。ま
た、この様な重合反応は、通常加熱操作を含まない。A preliminary component consisting of a monomer component containing isooctyl acrylate and acrylic acid in a predetermined ratio and a photoinitiator is placed in a stirrer, and UV polymerization is carried out while stirring. At this stage, partial polymerization is stopped and the viscosity is adjusted to 100 to 100,000 cps to prepare a partially polymerized syrup. To this syrup, a predetermined amount of a crosslinking agent monomer, 1,6-hexanediol diacrylate, and an additional photoinitiator are added and mixed so that they become uniform, and a precursor composition for an impact-reducing pressure-sensitive adhesive sheet is prepared. Prepare things. The inside of the stirrer is usually purged with an inert gas such as nitrogen gas during photopolymerization. Further, such a polymerization reaction usually does not include a heating operation.
【００７７】一方、所定の幾何学構造を有する衝撃緩和
性粘着シート成形用の型を次の様にして準備する。On the other hand, a mold for molding a shock-absorbing pressure-sensitive adhesive sheet having a predetermined geometric structure is prepared as follows.
【００７８】図４(ａ)に模式的に示す様に、所定の幾何
学構造を有する比較的硬質なプラスチックからなるポジ
型(８０)を用意する。プラスチックとしては、アクリ
ル、ポリカーボネート等が使用できる。このポジ型に、
剥離性樹脂を接触させ、剥離性樹脂を常温で硬化させた
ものをポジ型(８０)から剥離してネガ型(８１)とする。
この様なポジ型の具体例には、アクリサンデー(株)社製
の「(品名)アクリサンデー板」シリーズを挙げることが
でき、剥離性樹脂の具体例には、東レダウコーニング
(株)社製の型どりシリコンＳＥ９５５５を挙げることが
できる。As schematically shown in FIG. 4 (a), a positive mold (80) made of a relatively hard plastic having a predetermined geometric structure is prepared. As the plastic, acrylic, polycarbonate, etc. can be used. In this positive type,
A peelable resin is brought into contact with the peelable resin and cured at room temperature to release the positive mold (80) from the negative mold (81).
Specific examples of such a positive type include “(Product Name) Acrysanday Board” series manufactured by Acrysanday Co., Ltd., and specific examples of the peelable resin include Toray Dow Corning.
An example is Molded Silicon SE 9555 manufactured by Co., Ltd.
【００７９】ついで、図４(ｂ)に模式的に示すように、
ネガ型(８１)に上記衝撃緩和性粘着シートの前駆体組成
物(８２)を接触させ、組成物(８２)の上から透明なフィ
ルム(８３)で覆う。この時、組成物(８２)を重合および
架橋反応(すなわち、硬化反応)させた時に、衝撃緩和性
粘着シートの基部となる部分(８２２)と凸部となる部分
(８２１)とが形成される様に、ネガ型(８１)とフィルム
(８３)とを所定間隔で離して配置する。この状態で、フ
ィルム(８３)の上から紫外線を照射して硬化反応を完了
させ、ネガ型(８１)とフィルム(８３)とを取り除いた
後、組成物(８２)の硬化物からなる衝撃緩和性粘着シー
トを得る。Then, as schematically shown in FIG.
The precursor composition (82) for the impact-damping pressure-sensitive adhesive sheet is brought into contact with the negative mold (81), and the composition (82) is covered with a transparent film (83). At this time, when the composition (82) is polymerized and cross-linked (that is, cured), the base portion (822) and the convex portion of the shock-absorbing pressure-sensitive adhesive sheet are formed.
Negative mold (81) and film so that (821) is formed
(83) and are separated from each other by a predetermined distance. In this state, ultraviolet rays are radiated from above the film (83) to complete the curing reaction, the negative mold (81) and the film (83) are removed, and then the impact relaxation consisting of the cured product of the composition (82) is carried out. Obtain an adhesive sheet.
【００８０】透明なフィルム(８３)は、酸素を遮断する
ためと、衝撃緩和性粘着シートの基部(１０)の凸部が設
けられていない平坦な主要面(５)を平坦に成形するため
の両方の目的から使用される。また、この様な透明なフ
ィルム(８３)は、上記の様に、基部(１０)に固着された
可撓性支持体(６)として使用することもできる。通常、
フィルム(８３)には、ポリエステル(ＰＥＴ)等の可撓性
プラスチックフィルムを使用する。また、基部の厚さを
決定するためには、次の様な方法を採用することができ
る。The transparent film (83) is used for blocking oxygen and for flatly molding the flat main surface (5) of the shock-absorbing pressure-sensitive adhesive sheet on which the convex portion of the base (10) is not provided. Used for both purposes. Such a transparent film (83) can also be used as the flexible support (6) fixed to the base (10) as described above. Normal,
A flexible plastic film such as polyester (PET) is used for the film (83). Further, in order to determine the thickness of the base portion, the following method can be adopted.
【００８１】すなわち、過剰量の前駆体組成物(８２)を
ネガ型(８１)上に流し込み、フィルム(８３)でその上を
覆い、前駆体含有積層体(８)を形成した後、所定距離に
固定されたギャップを有するナイフコーターの、そのギ
ャップの中を積層体(８)を通過させて、縁部から前駆体
組成物(８２)の過剰分を排出させて、基部となる部分
(８２２)の厚さと平坦度を調節する。That is, an excessive amount of the precursor composition (82) is poured onto the negative mold (81), and the film is covered with a film (83) to form a precursor-containing laminate (8), and then a predetermined distance is obtained. The portion of the knife coater having a gap fixed to the base, which serves as the base by passing the laminate (8) through the gap and discharging the excess amount of the precursor composition (82) from the edge.
Adjust the thickness and flatness of (822).
【００８２】上記の様に紫外線を重合エネルギーとして
用いる場合、通常、紫外線の波長は３００〜４００ｎｍ
であり、照射強度は１００〜１,０００Ｊ／ｃｍ2の範囲
である。When ultraviolet rays are used as the polymerization energy as described above, the wavelength of the ultraviolet rays is usually 300 to 400 nm.
And the irradiation intensity is in the range of 100 to 1,000 J / cm 2 .
【００８３】また、上記ポジ型は、充分な厚さのガラス
板をサンディング・メソッドを用いた彫刻によっても形
成できる。さらに、ネガ型として、金属製の金型の成形
面をテフロン等のフッ素樹脂加工を施したものを使用す
ることができる。The positive mold can also be formed by engraving a glass plate having a sufficient thickness using a sanding method. Further, as the negative mold, it is possible to use one in which the molding surface of a metal mold is treated with a fluororesin such as Teflon.
【００８４】その他の添加剤 衝撃緩和性粘着シート(１)は、本発明の効果を損なわな
い限り、常用の感圧性接着剤において使用される、各種
添加剤を含んでも良い。添加剤とは、たとえば、粘着付
与剤、可塑剤、紫外線吸収材、酸化防止剤、重合開始剤
(光開始剤など粘着性ポリマー製造時に添加されるも
の。)、着色材、フィラー等である。これらの添加剤
は、粘着性ポリマーとともに、凸部、及び／又は凸部と
一体化した基部に含有される。 Other Additives The impact-absorbing pressure-sensitive adhesive sheet (1) may contain various additives used in a conventional pressure-sensitive adhesive as long as the effects of the present invention are not impaired. Examples of additives include tackifiers, plasticizers, ultraviolet absorbers, antioxidants, polymerization initiators.
(Those added at the time of production of the adhesive polymer such as a photoinitiator.), Colorants, fillers and the like. These additives are contained in the convex portion and / or the base portion integrated with the convex portion together with the adhesive polymer.
【００８５】その他の用途 本発明による衝撃緩和性粘着シートは、気密空間を被着
体との間に形成し、その気密空間を貼り付け完了後も維
持するので、衝撃緩和性の他に、たとえば、防振性、防
音性、または断熱性のいずれか１つ、あるいはこれらの
機能を複合的に有する接着構造の形成材料としても利用
できる。また、気密空間が装飾性の立体模様を形成する
場合、装飾シートの形成材料としても利用できる。 Other Uses The shock-absorbing pressure-sensitive adhesive sheet according to the present invention forms an airtight space between the adherend and the adherend, and maintains the airtight space even after completion of sticking. Also, it can be used as a material for forming an adhesive structure having any one of vibration-proof property, sound-proof property, and heat-insulating property, or a combination of these functions. Further, when the airtight space forms a decorative three-dimensional pattern, it can be used as a material for forming a decorative sheet.
【００８６】また、凸部(１１)側を可撓性フィルムで覆
い、接着面(１２)において接着し、気密空間を気胞室と
して初めから内包してなるシートとしても利用できる。
この場合、衝撃緩和性粘着シートの凸部と可撓性フィル
ムとの接着界面が気密にシールされること、および、凸
部が架橋され、かつ適度な凝集力(所定範囲に制御され
た貯蔵弾性率とその低下割合)を有することから、気胞
室から空気が外へ抜け出ることを効果的に防止できる。
したがって、本発明による衝撃緩和性粘着シートから形
成された気胞室内包シートは、長期に渡りその効果を維
持することが可能である。Further, it can also be used as a sheet in which the convex portion (11) side is covered with a flexible film and adhered on the adhesive surface (12) to enclose the airtight space as an alveolar chamber from the beginning.
In this case, the adhesive interface between the convex portion of the shock-absorbing pressure-sensitive adhesive sheet and the flexible film is hermetically sealed, and the convex portion is crosslinked, and an appropriate cohesive force (storage elasticity controlled to a predetermined range). Rate and its reduction rate), it is possible to effectively prevent air from escaping from the alveolar chamber to the outside.
Therefore, the alveolar chamber-containing sheet formed from the shock-absorbing pressure-sensitive adhesive sheet according to the present invention can maintain its effect for a long period of time.
【００８７】また、本発明による衝撃緩和性粘着シート
を梱包材料として使用する場合は、次の様にする。たと
えば、被梱包体(被着体)が、フロッピーディスク容器等
の薄い直方体の場合、その水平面の面積より大きな面積
の衝撃緩和性粘着シートを２枚用意し、容器をその間に
挟む様にして、粘着シートの凸部の接着面を容器の水平
面に接着させる。この時、粘着シートの外周近傍の余白
部分は、容器の水平面には接着されずに水平方向にはみ
出す様に延在させておく。When the shock-absorbing pressure-sensitive adhesive sheet according to the present invention is used as a packing material, it is carried out as follows. For example, when the object to be packed (adherent) is a thin rectangular parallelepiped such as a floppy disk container, prepare two shock-absorbing pressure-sensitive adhesive sheets having an area larger than the area of the horizontal plane, and sandwich the container between them. The adhesive surface of the convex portion of the adhesive sheet is adhered to the horizontal surface of the container. At this time, the marginal portion in the vicinity of the outer periphery of the pressure-sensitive adhesive sheet is not adhered to the horizontal surface of the container and is extended so as to protrude in the horizontal direction.
【００８８】次に、２枚の粘着シートの余白部分どうし
を貼り合わせて、２枚の粘着シートにより容器を密封す
る。この様にすると、梱包の際に別途接着手段を必要と
しない点で好適である。また、この様な場合、余白部分
の凹凸形状を任意に変形して接着力を制御することもで
きる。Next, the margins of the two adhesive sheets are attached to each other, and the container is sealed with the two adhesive sheets. In this way, it is preferable in that no additional adhesive means is required for packaging. Further, in such a case, the adhesive force can be controlled by arbitrarily deforming the uneven shape of the blank portion.
【００８９】解梱は、余白部分どうしをその界面で剥離
するか、余白部分を切り取って除くことによって行うこ
とができる。The unpacking can be carried out by peeling the margins from each other at their interfaces or by cutting off the margins.
【００９０】紙のようなパルプ材料を、支持体として本
発明の粘着シートの平坦な表面上に提供することができ
る。被梱包体が紙支持体を有する粘着シートを用いて梱
包された場合は、切手及び住所等をその上に乗せること
ができ、被梱包体は直接小包等として使用できる。A pulp material such as paper can be provided as a support on the flat surface of the pressure-sensitive adhesive sheet of the present invention. When the packaged object is packaged using an adhesive sheet having a paper support, a stamp, an address, etc. can be placed on the packaged object, and the packaged object can be directly used as a parcel or the like.
【００９１】[0091]
【実施例】物理的測定値および評価 凸部の弾性率 以下の実施例において、凸部(１１)の弾性率Ｇは、レオ
メトリックス社製ダイナミック・アナライザー「型番：
ＲＤＡII」を用い、上記条件にて測定した貯蔵弾性率で
ある。なお、測定に用いられた試料維持具は、直径７.
９ｍｍの平行プレートであった。EXAMPLES Physically Measured Values and Evaluation Elastic Modulus of Convex Section In the following examples, the elastic modulus G of the convex section (11) is determined by a dynamic analyzer “Model No .: manufactured by Rheometrics”.
RDAII ”is a storage elastic modulus measured under the above conditions. The sample holder used for the measurement had a diameter of 7.
It was a 9 mm parallel plate.
【００９２】凸部のｌｏｇ10Ｇの低下 ｌｏｇ10Ｇの変化(低下)は、２５℃〜１２５℃の範囲で
得られた粘弾性スペクトルから読取られた２５℃におけ
るＧを基準とした変動値から計算された値である。[0092] change in the drop log 10 G of log 10 G of the projections (decrease) from variation value based on the G at 25 ° C. read viscoelastic spectrum obtained in the range of 25 ° C. to 125 ° C. This is the calculated value.
【００９３】形状付与性 被着体(スライドガラス)に貼り付けた時に、衝撃緩和性
粘着シートの凹部に対応する気密空間が形成できない場
合をＮＧ、気密空間が形成できる場合をＯＫとした。Shape-Providing Property When adhered to an adherend (slide glass), the case where the airtight space corresponding to the concave portion of the shock-absorbing pressure-sensitive adhesive sheet cannot be formed is NG, and the case where the airtight space can be formed is OK.
【００９４】形状維持性 被着体(スライドガラス)に貼り付け直後の気密空間と、
貼り付け後５か月後の気密空間とを比較して、ほとんど
変化がない場合をＯＫ、明らかな変化が見られる場合を
ＮＧとした。この比較は、直後および５か月後の、それ
ぞれの２０倍の拡大写真(スライドガラスを通して撮影)
を用いて行った。Shape maintaining property An airtight space immediately after being attached to an adherend (slide glass),
A comparison was made with the airtight space 5 months after the attachment, and when there was almost no change, it was OK, and when there was a clear change, it was NG. This comparison is a 20x magnified photograph (taken through a slide glass) immediately after and after 5 months.
This was performed using
【００９５】気密空間の容積 被着体に貼り付けられる前の衝撃緩和性粘着シート(１)
の凹部(４)の容積から計算された値である。たとえば、
凹部(４)が、角錐台、直方体等の幾何学的立体の１つの
底面(または側面)を欠く形状でる場合は、その幾何学的
寸法から算出できる。Volume of airtight space Impact-absorbing pressure-sensitive adhesive sheet (1) before being attached to an adherend
It is a value calculated from the volume of the concave portion (4). For example,
When the concave portion (4) has a shape lacking one bottom surface (or side surface) of a geometric solid such as a truncated pyramid or a rectangular parallelepiped, it can be calculated from the geometric dimension.
【００９６】衝撃緩和性 衝撃緩和性粘着シートを破壊可能試験体(スライドグラ
ス)の１方の表面のほぼ全体を覆う様に貼り付けるたも
のをサンプルとした。この時、貼り付ける圧力が一定に
なる様にする。圧力を一定にするために２ｋｇの圧着用
ローラを使用し、試験体に載置した衝撃緩和性粘着シー
トの上を１往復転がして圧着させた。スライドグラス
は、マツナミガラス工業(株)社製の「(商品名)ＭＩＣＲ
Ｏ ＳＬＩＤＥ ＧＬＡＳＳ 白緑磨 Ｎｏ.１」で、
長さ７６ｍｍ×幅２６ｍｍ×厚さ１ｍｍの寸法を有して
いた。Impact-Reducing Property A sample was prepared by attaching an impact-reducing pressure-sensitive adhesive sheet so as to cover almost the entire surface of one side of a destructible test piece (slide glass). At this time, the sticking pressure should be constant. A pressure roller of 2 kg was used to keep the pressure constant, and the pressure-reducing pressure-sensitive adhesive sheet placed on the test body was rolled back and forth once for pressure bonding. The slide glass is "(trade name) MICR" manufactured by Matsunami Glass Industry Co., Ltd.
O SLIDE GLASS No.1 ”
It had dimensions of length 76 mm × width 26 mm × thickness 1 mm.
【００９７】上記の様にして作成したサンプルを、衝撃
緩和性粘着シートの貼り付け面が上向きになる様に、紙
タオル(大洋紙業(株)社製の商品名「ＦＵＪＩ ＰＡＰ
Ｉ」を介して鉄板の上に載置し、所定の高さから所定重
量の鉄球を落下させた。直径１５ｍｍ、質量３０ｇの鉄
球を用い、高さ３０ｃｍから試験を開始した。３０ｃｍ
の高さからの落球で破壊可能試験体の破損がなかった場
合、４０ｃｍの高さに変えて、同様にして落球衝撃テス
トを行い、それ以降、試験体が破損するまで１０ｃｍづ
つ高さを変えて行き、破損の生じた高さの１つ前の高さ
を、落球衝撃テストの評価値(単位はｃｍ)とした(テス
ト環境は、温度２５℃、相対湿度６０％ＲＨ)。The sample prepared as described above was placed on a paper towel (trade name "FUJI PAP manufactured by Taiyo Paper Industries Co., Ltd."
I "was placed on the iron plate, and an iron ball having a predetermined weight was dropped from a predetermined height. The test was started from a height of 30 cm using an iron ball having a diameter of 15 mm and a mass of 30 g. 30cm
If there is no breakage of the test body that can be destroyed by falling balls from the height of, drop ball impact test is performed in the same manner by changing the height to 40 cm, and thereafter, change the height by 10 cm until the test body is broken. The height immediately before the height at which damage occurred was taken as the evaluation value (unit: cm) of the falling ball impact test (test environment: temperature 25 ° C., relative humidity 60% RH).
【００９８】剥離強度 引張り試験機を用い、スライドガラスに貼り付けた衝撃
緩和性粘着シートを、１８０度方向に、３００ｍｍ／分
の引張り速度にて剥離した際の剥離抵抗を、環境温度２
５℃、相対湿度６０％ＲＨの条件にて測定した値であ
る。ただし、本発明による衝撃緩和性粘着シートは、凸
部の接着面のみで接着しているので、測定された剥離抵
抗は最大値と最小値とを示す。したがって、測定結果に
は、最大値、最小値、およびそれらの和の１／２である
平均値を示す。Peel strength Using a tensile tester, the peel resistance when the impact-relieving pressure-sensitive adhesive sheet stuck to a slide glass was peeled in a 180 degree direction at a pulling speed of 300 mm / min was measured at an ambient temperature of 2
It is a value measured under the conditions of 5 ° C. and relative humidity of 60% RH. However, since the shock-absorbing pressure-sensitive adhesive sheet according to the present invention is bonded only by the bonding surface of the convex portion, the measured peel resistance shows the maximum value and the minimum value. Therefore, the measurement result shows the maximum value, the minimum value, and the average value that is 1/2 of the sum thereof.
【００９９】実施例１ イソオクチルアクリルレート９０重量部とアクリル酸１
０重量部とからなるモノマー成分と、光開始剤としてア
ゾビスイソブチロニトリル(ＡＩＢＮ)０.１重量部とか
らなる予備成分から、紫外線重合による部分重合シロッ
プを調製した。このシロップに、架橋剤モノマーとして
１,６−ヘキサンジオールジアクリレート１重量部と、
追加の光開始剤としてＡＩＢＮ０.２重量部とを添加
し、それらが均一になる様に混合し、衝撃緩和性粘着シ
ートの前駆体組成物を調製した。 Example 1 90 parts by weight of isooctyl acrylate and acrylic acid 1
A partially polymerized syrup by UV polymerization was prepared from a preliminary component consisting of 0 part by weight of a monomer component and 0.1 part by weight of azobisisobutyronitrile (AIBN) as a photoinitiator. To this syrup, 1 part by weight of 1,6-hexanediol diacrylate as a crosslinking agent monomer,
AIBN 0.2 part by weight was added as an additional photoinitiator, and they were mixed so as to be uniform to prepare a precursor composition for an impact-damping pressure-sensitive adhesive sheet.
【０１００】ポジ型として、アクリサンデー(株)社製の
「(品名)アクリサンデー板(品番ダイヤ)」を、剥離性樹
脂として、東レダウコーニング(株)社製の「(品名)型ど
りシリコン、(品番)ＳＥ９５５５」とを用いて、図４に
示す方法により、紫外線硬化により衝撃緩和性粘着シー
トを作製した。透明フィルムには、東レ(株)社製のＰＥ
Ｔフィルム「ルミラー５０Ｔ(厚さ５０μｍ)」を用い、
衝撃緩和性粘着シート形成後は基部に固着され、可撓性
支持体として利用した。As a positive mold, "(product name) Acrysanday board (product number diamond)" manufactured by Acrysanday Co., Ltd., and as a release resin, "(product name) type silicon, (product number) manufactured by Toray Dow Corning Co., Ltd. ) SE9555 "was used to prepare an impact-damping pressure-sensitive adhesive sheet by ultraviolet curing according to the method shown in FIG. For transparent film, PE made by Toray Industries, Inc.
Using T film "Lumirror 50T (thickness 50 μm)",
After forming the shock-absorbing pressure-sensitive adhesive sheet, it was fixed to the base and used as a flexible support.
【０１０１】衝撃緩和性粘着シートの凹部形状は正四角
錐台(接着面側が幅広)であり、その容積は６ｍｍ3であ
った。また、凸部の接着面側の幅は１ｍｍ、長さは３ｍ
ｍであり、基部の厚さは０.５ｍｍであった。さらに、
凹部は９個／ｃｍ2(水平面内、格子模様状)の割合で配
置された。The concave shape of the shock-absorbing pressure-sensitive adhesive sheet was a regular square pyramid (adhesive surface side was wide), and its volume was 6 mm 3 . The width of the convex surface on the adhesive surface side is 1 mm and the length is 3 m.
m, and the thickness of the base was 0.5 mm. further,
The recesses were arranged at a rate of 9 / cm 2 (in a horizontal plane, in a lattice pattern).
【０１０２】得られた衝撃緩和性粘着シートの弾性率、
２５℃〜１２５℃の範囲でのｌｏｇ10Ｇの低下、形状付
与性、形状維持性、衝撃力緩和性及び剥離強度を評価し
た。結果を表１に示す。Elastic modulus of the obtained shock-absorbing pressure-sensitive adhesive sheet,
The decrease of log 10 G in the range of 25 ° C. to 125 ° C., shape imparting property, shape maintaining property, impact force relaxing property and peel strength were evaluated. The results are shown in Table 1.
【０１０３】実施例２〜６ 架橋剤モノマーである１,６−ヘキサンジオールジアク
リレートの含有量を表１に示すよう変化させること以外
は実施例１と同様にして衝撃緩和性粘着シートを得、評
価した。結果を表１及び２に示す。 Examples 2 to 6 Impact-damping pressure-sensitive adhesive sheets were obtained in the same manner as in Example 1 except that the content of the crosslinking agent monomer 1,6-hexanediol diacrylate was changed as shown in Table 1. evaluated. The results are shown in Tables 1 and 2.
【０１０４】実施例５および６では、１８０度剥離強度
はほとんどゼロであったが、気密空間を維持できる程度
にタックは有していた。したがって、貼り付け後にサン
プルを持ち運んでもスライドガラス接着位置から衝撃緩
和性粘着シートがずれることはなかった。In Examples 5 and 6, the 180-degree peel strength was almost zero, but the tack was sufficient to maintain the airtight space. Therefore, even if the sample was carried after attachment, the shock-absorbing pressure-sensitive adhesive sheet was not displaced from the slide glass bonding position.
【０１０５】また、実施例５及び実施例６の保持力を前
述の方法で測定したところ、それぞれ１０分及び１２時
間であった。尚、実施例１及び実施例４の保持力は４８
時間以上(４８時間で測定中止)であった。When the holding powers of Examples 5 and 6 were measured by the above-mentioned method, they were 10 minutes and 12 hours, respectively. In addition, the holding force of Example 1 and Example 4 is 48
It was over the time (measurement was stopped at 48 hours).
【０１０６】比較例１ モノマー成分としてイソオクチルアクリレートのみを用
い、架橋剤を使用しないこと以外は実施例１と同様にし
て衝撃緩和性粘着シートを得、評価した。結果を表２に
示す。 Comparative Example 1 An impact mitigating pressure-sensitive adhesive sheet was obtained and evaluated in the same manner as in Example 1 except that only isooctyl acrylate was used as the monomer component and no crosslinking agent was used. Table 2 shows the results.
【０１０７】比較例２ 架橋剤を使用しないこと以外は実施例１と同様にして衝
撃緩和性粘着シートを得、評価した。結果を表２に示
す。 Comparative Example 2 An impact cushioning pressure-sensitive adhesive sheet was obtained and evaluated in the same manner as in Example 1 except that the crosslinking agent was not used. Table 2 shows the results.
【０１０８】実施例７〜１２ ポジ型として、厚さ約５ｍｍのガラス板にサンディング
・メソッドにより彫刻して、それから作製される衝撃緩
和性粘着シートの凹部が所定の寸法を有する直方体とな
る様に、凹凸を形成したものを用いたこと以外は、実施
例１と同様にして衝撃緩和性粘着シートを得、評価し
た。結果を表２及び３に示す。 Examples 7 to 12 As a positive type, a glass plate having a thickness of about 5 mm was engraved by a sanding method so that the recesses of the shock-absorbing pressure-sensitive adhesive sheet produced therefrom were rectangular parallelepipeds having predetermined dimensions. A shock-absorbing pressure-sensitive adhesive sheet was obtained and evaluated in the same manner as in Example 1 except that the one having unevenness was used. The results are shown in Tables 2 and 3.
【０１０９】ただし、各例の凹部空間(直方体)の寸法は
次の通りとした。 実施例 ７：頂面(底面)は１辺が１ｍｍの正方形／高さ
１ｍｍ。 実施例 ８：頂面(底面)は１辺が２ｍｍの正方形／高さ
１ｍｍ。 実施例 ９：頂面(底面)は１辺が３ｍｍの正方形／高さ
１ｍｍ。 実施例１０：頂面(底面)は１辺が５ｍｍの正方形／高さ
１ｍｍ。 実施例１１：頂面(底面)は１辺が１０ｍｍの正方形／高
さ０.８ｍｍ。 実施例１２：頂面(底面)は１辺が１０ｍｍの正方形／高
さ１.５ｍｍ。 凸部の幅は１ｍｍ、基部の厚さは０.２ｍｍでそれぞれ
統一した。However, the dimensions of the concave space (rectangular parallelepiped) in each example are as follows. Example 7: The top surface (bottom surface) is a square with one side of 1 mm / height of 1 mm. Example 8: The top surface (bottom surface) is a square having a side of 2 mm and a height of 1 mm. Example 9: The top surface (bottom surface) is a square having a side of 3 mm and a height of 1 mm. Example 10: The top surface (bottom surface) is a square having a side of 5 mm and a height of 1 mm. Example 11: The top surface (bottom surface) is a square with one side of 10 mm / height 0.8 mm. Example 12: The top surface (bottom surface) is a square having a side of 10 mm / height of 1.5 mm. The width of the protrusion is 1 mm and the thickness of the base is 0.2 mm.
【０１１０】実施例１３ 実施例１と実質的に同様にして、頂面(底面)は１辺が３
ｍｍの正方形／高さ０.５ｍｍの凹部と、０.５ｍｍの厚
さの基部とを有する衝撃緩和性粘着シート(可撓性支持
体無し)と、同じ衝撃緩和性粘着シートの基部にＰＥＴ
フィルム(可撓性支持体)を固着したものをそれぞれ別に
用意し、自己の粘着力にて貼り合わせた。得られた衝撃
緩和性粘着シート複合体を実施例１と同様にして評価し
た。結果を表３に示す。 Example 13 Substantially the same as Example 1, the top surface (bottom surface) has three sides.
mm square / 0.5 mm high recess and 0.5 mm thick base, shock-absorbing PSA sheet (no flexible support), PET on the base of the same shock-absorbing PSA sheet
Separately prepared films (flexible supports) were prepared and attached by their own adhesive force. The shock-absorbing pressure-sensitive adhesive sheet composite thus obtained was evaluated in the same manner as in Example 1. The results are shown in Table 3.
【０１１１】比較例３ 厚さが１.２ｍｍの平らなシート状(凹凸部なし)に成形
したこと以外は実施例１と同様にして粘着シートを得、
評価した。衝撃緩和性［ｃｍ］は３０ｃｍであり、１８
０度剥離強度は１１５０ｇ／２５ｍｍであった。 Comparative Example 3 An adhesive sheet was obtained in the same manner as in Example 1 except that it was formed into a flat sheet having a thickness of 1.2 mm (without irregularities).
evaluated. Impact relaxation [cm] is 30 cm, 18
The 0 degree peel strength was 1150 g / 25 mm.
【０１１２】比較例４ ポジ型に３Ｍ(株)社製のプリズムフィルム「(品名)ＳＯ
ＬＦ」を用いたこと以外は、実施例１と同様にして衝撃
緩和性粘着シートを得、評価した。 Comparative Example 4 Positive type prism film "(product name) SO manufactured by 3M Co., Ltd.
An impact-damping pressure-sensitive adhesive sheet was obtained and evaluated in the same manner as in Example 1 except that "LF" was used.
【０１１３】「ＳＯＬＦ」は、高さ約０.１８ｍｍ、底
辺が約０.３６ｍｍの２等辺三角形を底面とする三角柱
の多数を平行に横置きにした多数のプリズム突起を備え
る構造。隣接するプリズム間の凹部空間は上記と同じ三
角柱からなり、したがって、衝撃緩和性粘着シートは三
角柱の底面側に開口を有する空間しか形成できない(気
密性がない)。The "SOLF" is a structure provided with a large number of prism protrusions in which a plurality of triangular prisms each having an isosceles triangle having a height of about 0.18 mm and a base of about 0.36 mm as a base are placed horizontally in parallel. The recessed space between adjacent prisms is formed of the same triangular prism as described above, and therefore the impact-damping adhesive sheet can only form a space having an opening on the bottom surface side of the triangular prism (no airtightness).
【０１１４】衝撃緩和性［ｃｍ］は３０ｃｍであり、１
８０度剥離強度は５０ｇ／２５ｍｍであった。The impact relaxation property [cm] is 30 cm, and 1
The 80 degree peel strength was 50 g / 25 mm.
【０１１５】実施例１４ 実施例１の衝撃緩和性粘着シートを８ｃｍ×１０ｃｍの
面積になる様に形成し、上記ＰＥＴフィルム、東レ(株)
社製「ルミラー５０Ｔ」の上に、凸部側を向けて貼り付
けて、気胞室内包シートを作製した。これを平坦な実験
台の上に載置し、その上から静荷重４ｋｇ／８ｃｍ×１
０ｃｍをかけた状態で、環境温度２５℃、相対湿度６０
％ＲＨの条件にて７日間放置し、静荷重に対する気胞室
の維持性能を評価した。 Example 14 The impact-reducing pressure-sensitive adhesive sheet of Example 1 was formed into an area of 8 cm × 10 cm, and the PET film, Toray Industries, Inc.
The product was attached to "Lumirror 50T" manufactured by the company with the convex side facing, to produce an alveolar chamber-containing sheet. Place this on a flat laboratory table, and apply a static load of 4 kg / 8 cm x 1 from above.
With 0 cm applied, environmental temperature 25 ℃, relative humidity 60
It was allowed to stand for 7 days under the condition of% RH to evaluate the maintenance performance of the alveolar chamber against a static load.
【０１１６】上記の形状維持性の場合と同じ手法で評価
した結果、気胞室はほとんど変形しなかった。As a result of evaluation by the same method as in the case of the shape retention, the alveolar chamber was hardly deformed.
【０１１７】対象サンプルとして、川上産業(株)社製の
「(品名)エアバッグ、(品番)＃３７」を用いて、同様の
試験を行った。このエアバッグは、非粘着性の熱可塑性
フィルム(ポリオレフィン系フィルムと思われる)から成
形され、各々が約３ｍｍの高さと約２３０ｍｍ3の容積
を有する多数の気胞室を内包するクッションシートであ
る。The same test was carried out using "(product name) airbag, (product number) # 37" manufactured by Kawakami Sangyo Co., Ltd. as a target sample. This airbag is a cushion sheet formed from a non-adhesive thermoplastic film (probably a polyolefin-based film) and containing a large number of vacuole chambers each having a height of about 3 mm and a volume of about 230 mm 3 .
【０１１８】７日後には、ほとんど空気胞から空気が漏
れ出てしまっていた。After 7 days, most of the air bubbles had leaked out.
【０１１９】また、このエアバッグについて、上記と同
様の衝撃緩和性を評価したところ、４０ｃｍであり、こ
のエアバッグを、４枚重ねてスライドガラス上に配置し
た時に、やっと８０ｃｍの評価値を得た。When the same impact relaxation property as the above was evaluated for this airbag, it was 40 cm, and when 4 sheets of this airbag were placed on a slide glass, an evaluation value of 80 cm was finally obtained. It was
【０１２０】[0120]
【表１】 実施例１ 実施例２ 実施例３ 実施例４ 実施例５ 架橋剤(重量部) 1.00 0.25 0.50 2.00 5.00 弾性率G 6.7 6.0 6.1 1.1 2.0 (dyne/cm2) ×105 ×105 ×105 ×106 ×106 Δlog10G 0 -0.4 -0.2 +0.1 +0.2 気密空間容積(mm3) 6 6 6 6 6 形状付与性 OK OK OK OK OK 形状維持性 OK OK OK OK OK 衝撃緩和性(cm) 80 60 70 70 60 剥離強度 Max. 450 1600 1000 65 (g/25mm) Av. 350 1000 675 50 〜0 Min. 250 400 350 35 Table 1 Example 1 Example 2 Example 3 Example 4 Example 5 Cross-linking agent (parts by weight) 1.00 0.25 0.50 2.00 5.00 Modulus of elasticity G 6.7 6.0 6.1 1.1 2.0 (dyne / cm 2 ) × 10 5 × 10 5 × 10 5 × 10 6 × 10 6 Δlog 10 G 0 -0.4 -0.2 +0.1 +0.2 Airtight space volume (mm 3 ) 6 6 6 6 6 Formability OK OK OK OK OK Shape maintainability OK OK OK OK OK Impact Relaxability (cm) 80 60 70 70 60 Peel strength Max. 450 1600 1000 65 (g / 25mm) Av. 350 1000 675 50 〜 0 Min. 250 400 350 35
【０１２１】[0121]
【表２】 実施例６ 比較例１ 比較例２ 実施例７ 実施例８ 架橋剤 (重量部) 10.00 0 0 1.00 1.00 弾性率G 4.0 3.8 5.8 6.7 6.7 (dyne/cm2) ×106 ×105 ×105 ×105 ×105 Δlog10G +0.2 -2 -2 0 0 気密空間容積(mm3) 6 6 6 1 4 形状付与性 OK NG OK OK OK 形状維持性 OK NG NG OK OK 衝撃緩和性(cm) 60 - - 90 80 剥離強度 Max. 1400 1350 (g/25mm) Av. 〜0 - - 1100 875 Min. 800 400 [Table 2] Example 6 Comparative Example 1 Comparative Example 2 Example 7 Example 8 Cross-linking agent (parts by weight) 10.00 0 0 1.00 1.00 Modulus of elasticity G 4.0 3.8 5.8 6.7 6.7 (dyne / cm 2 ) × 10 6 × 10 5 × 10 5 × 10 5 × 10 5 Δlog 10 G +0.2 -2 -2 0 0 Airtight space volume (mm 3 ) 6 6 6 1 4 Shape impartability OK NG OK OK OK Shape retention OK NG NG OK OK Shock mitigation Peel strength (cm) 60--90 80 Peel strength Max. 1400 1350 (g / 25mm) Av. ~ 0--1100 875 Min. 800 400
【０１２２】[0122]
【表３】 実施例９ 実施例10 実施例11 実施例12 実施例13 架橋剤 (重量部) 1.00 1.00 1.00 1.00 １．００ 弾性率Ｇ 6.7 6.7 6.7 6.7 6.7 (dyne/cm2) ×105 ×105 ×105 ×105 ×105 Δlog10G 0 0 0 0 0 気密空間容積(mm3) 9 25 80 150 4.5×2 形状付与性 OK OK OK OK OK 形状維持性 OK OK OK OK OK 衝撃緩和性(cm) 90 50 50 50 110 剥離強度 Max. 1000 880 650 650 1000 (g/25mm) Av. 650 490 280 275 650 Min. 300 100 90 80 300 [Table 3] Example 9 Example 10 Example 11 Example 12 Example 13 Crosslinking agent (parts by weight) 1.00 1.00 1.00 1.00 1.00 1.00 Modulus of elasticity G 6.7 6.7 6.7 6.7 6.7 (dyne / cm 2 ) × 10 5 × 10 5 × 10 5 × 10 5 × 10 5 Δlog 10 G 0 0 0 0 0 Airtight space volume (mm 3 ) 9 25 80 150 4.5 × 2 Shape impartability OK OK OK OK OK Shape maintainability OK OK OK OK OK Impact Relaxability (cm) 90 50 50 50 110 Peel strength Max. 1000 880 650 650 1000 (g / 25mm) Av. 650 490 280 275 650 Min. 300 100 90 80 300
【０１２３】実施例１５〜１７ 可撓性支持体(ＰＥＴフィルム)を設けず、凹部の体積を
表４に示すように変更したこと以外は実施例９と同様に
して衝撃緩和性粘着シートを作成した。この衝撃緩和性
粘着シートの防振性を、ヒューレッド・パッカード(株)
社の振動解析装置「3562Ａ Ｄynamic Ｓignal Ａnalyze
r」を用いて評価した。その評価方法を次に説明する。 Examples 15 to 17 An impact absorbing pressure-sensitive adhesive sheet was prepared in the same manner as in Example 9 except that the flexible support (PET film) was not provided and the volume of the recess was changed as shown in Table 4. did. The vibration-proof properties of this shock-absorbing pressure-sensitive adhesive sheet are
Vibration Analysis Device "3562A Dynamic Signal Analyze"
r ”was used for evaluation. The evaluation method will be described below.
【０１２４】まず、粘着シートの凸部の接着面を、25mm
(幅)×100mm(長さ)×２mm(厚み)の第１の金属板(アルミ
ニウム板)の表面のほぼ全面に貼り付け、気密空間を形
成した。第１金属板の裏面ほぼ中央には、ディテクター
としてＰＣＢ(PIEZOTRONICS)(株)社製の「(品名)加速度
ピックアップ」を取り付けた。さらに、粘着シートの基
部の凸部が設けられていない側の表面にも、上記同じ金
属板を第２金属板として基部の粘着性を利用して貼り付
けてサンプルを作成した。First, the adhesive surface of the convex portion of the pressure-sensitive adhesive sheet is set to 25 mm.
The first metal plate (aluminum plate) of (width) × 100 mm (length) × 2 mm (thickness) was attached to almost the entire surface to form an airtight space. A "(product name) accelerometer" manufactured by PCB (PIEZOTRONICS) Co., Ltd. was installed as a detector on the back surface of the first metal plate at approximately the center. Further, a sample was prepared by sticking the same metal plate as a second metal plate to the surface of the pressure-sensitive adhesive sheet on the side where the convex portion of the base is not provided, by utilizing the adhesiveness of the base.
【０１２５】このサンプルの第２金属板の表面を直系3.
5mm金属棒を用いて１回弾き、第２金属板を振動させ、
ディテクターに検出される第１金属板の振動の解析から
減衰定数(ｈ)を求めた。１つのサンプルに付き３回の測
定を行い、３回の平均値を防振性の評価値とした。な
お、減衰定数(ｈ)は次の式(１)で定義される。 ｈ＝Ｘ1／Ｘ2 ［式中、Ｘ1は第１振幅であり、Ｘ2は第２振幅であ
る。］ すなわち、減衰定数が１より大きく、より大きな値を示
すほど、防振性が良いことを示す。結果を表４に示す。The surface of the second metal plate of this sample was directly connected to 3.
Play once with a 5mm metal rod to vibrate the second metal plate,
The damping constant (h) was obtained from the analysis of the vibration of the first metal plate detected by the detector. The measurement was performed three times for one sample, and the average value of the three times was used as the evaluation value of the vibration damping property. The damping constant (h) is defined by the following equation (1). h = X 1 / X 2 [where X 1 is the first amplitude and X 2 is the second amplitude. That is, the larger the damping constant is, and the larger the damping constant is, the better the vibration damping property is. The results are shown in Table 4.
【０１２６】比較例５ 凸部のない全面が平坦な粘着面を有する以外は実施例15
と同様にして作成した粘着シートを用い、実施例15同様
にして減衰定数(ｈ)を求めた。結果を表４に示す。 Comparative Example 5 Example 15 except that the whole surface having no protrusion has a flat adhesive surface.
Using the pressure-sensitive adhesive sheet prepared in the same manner as in Example 15, the attenuation constant (h) was obtained in the same manner as in Example 15. The results are shown in Table 4.
【０１２７】[0127]
【表４】 凹部体積(mm3) 減衰定数(ｈ) 実施例15 ３×３×１＝ ９ ２.０ 実施例16 ５×５×１＝ 25 ２.１ 実施例17 10×10×１＝100 ２.３比較例５ ０ １.７ [Table 4] Recess volume (mm 3 ) Attenuation constant (h) Example 15 3 × 3 × 1 = 9 2.0 Example 16 5 × 5 × 1 = 25 2.1 Example 17 10 × 10 × 1 = 100 2.3 Comparative Example 5 0 1.7
【０１２８】比較例５の様なアクリル系粘着性ポリマー
からなるシートはすぐれた防振性を有することが知られ
ている(たとえば、前記実開平４−126369号明細書に開
示。)が、実施例15〜17の粘着シートでは、比較例５を
上回る減衰定数を示す。It is known that the sheet made of an acrylic adhesive polymer as in Comparative Example 5 has excellent vibration damping properties (for example, disclosed in the above-mentioned Japanese Utility Model Publication No. 4-126369). The pressure-sensitive adhesive sheets of Examples 15 to 17 show a damping constant higher than that of Comparative Example 5.
【０１２９】[0129]
【発明の効果】本発明は、複数の独立した、比較的大き
な容積の気密空間を、貼り付け完了後も経時で安定に維
持できる衝撃緩和性粘着シートを提供することができ
る。この様な衝撃緩和性粘着シートを被着体に貼り付け
ることにより、被着体に伝わる衝撃力を緩和する効果に
すぐれた接着構造を形成できる。INDUSTRIAL APPLICABILITY The present invention can provide an impact-damping pressure-sensitive adhesive sheet that can maintain a plurality of independent air-tight spaces having a relatively large volume and stable over time even after the completion of sticking. By sticking such a shock-absorbing pressure-sensitive adhesive sheet to an adherend, an adhesive structure having an excellent effect of relaxing the impact force transmitted to the adherend can be formed.
【図１】 (ａ)は本発明の衝撃緩和性粘着シートの一例
を示す斜視図であり、(ｂ)はそのＩ−Ｉ'断面図であ
る。FIG. 1 (a) is a perspective view showing an example of an impact-absorbing pressure-sensitive adhesive sheet of the present invention, and FIG. 1 (b) is a sectional view taken along the line II ′.
【図２】 (ａ)及び(ｂ)は、それぞれ本発明の衝撃緩和
構造体の一例を示す断面図である。2 (a) and 2 (b) are cross-sectional views showing an example of a shock absorbing structure of the present invention.
【図３】 (ａ)は本発明の衝撃緩和構造体の一例を示す
断面図であり、(ｂ)はその透過上面図である。FIG. 3A is a cross-sectional view showing an example of the shock absorbing structure of the present invention, and FIG. 3B is a transparent top view thereof.
【図４】 本発明の衝撃緩和性粘着シートの製造方法を
模式的に示す断面工程図である。FIG. 4 is a cross-sectional process diagram that schematically shows the method for producing an impact-absorbing pressure-sensitive adhesive sheet of the present invention.
【図５】 従来の接着シートの一例を示す斜視図であ
る。FIG. 5 is a perspective view showing an example of a conventional adhesive sheet.
【図６】 従来の接着シートの一例を示す断面図であ
る。FIG. 6 is a cross-sectional view showing an example of a conventional adhesive sheet.
【図７】 従来の衝撃緩和シートの一例を示す断面図で
ある。FIG. 7 is a cross-sectional view showing an example of a conventional shock absorbing sheet.
１…粘着シート、 ２…主要面、 ３…被着物、 ４…凹部、 １０…基部、 １１…凸部、 １２…接着面、 ３１…被着物表面、 ４１…気密空間。 DESCRIPTION OF SYMBOLS 1 ... Adhesive sheet, 2 ... Main surface, 3 ... Adhesion object, 4 ... Recessed part, 10 ... Base part, 11 ... Convex part, 12 ... Adhesive surface, 31 ... Adhesion object surface, 41 ... Airtight space.
Claims (6)
なくとも１方の主要面(２)に、架橋された粘着性ポリマ
ーを含んで成り、複数の幾何学的形状の凹部(４)を囲む
様に立設され、接着面(１２)を有する凸部(１１)とを；
備えた粘着シート(１)において、 該凹部(４)の容積が０.８〜６００ｍｍ3であり、１ｒａ
ｄ／秒の周波数、シェアモードにて動的粘弾性測定法に
より測定された該凸部(１１)の弾性率Ｇが２５℃におい
て５×１０5〜４×１０6ｄｙｎｅ／ｃｍ2の範囲であ
り、２５℃〜１２５℃の範囲でのｌｏｇ10Ｇの低下が
１.０未満である衝撃緩和性粘着シート。1. A plurality of geometric shapes comprising: (i) a base (10); and (ii) at least one major surface (2) of the base (10) comprising a crosslinked tacky polymer. And a convex portion (11) which is erected so as to surround the concave portion (4) and has an adhesive surface (12);
In the provided pressure-sensitive adhesive sheet (1), the volume of the concave portion (4) is 0.8 to 600 mm 3 ,
The elastic modulus G of the convex portion (11) measured by the dynamic viscoelasticity measuring method in a shear mode at a frequency of d / sec is in the range of 5 × 10 5 to 4 × 10 6 dyne / cm 2 at 25 ° C. The impact-reducing pressure-sensitive adhesive sheet, which has a log 10 G decrease of less than 1.0 in the range of 25 ° C. to 125 ° C.
含んで成り凸部と一体化された構造である請求項１記載
の衝撃緩和性粘着シート。2. The shock-absorbing pressure-sensitive adhesive sheet according to claim 1, wherein the base portion has a structure including a cross-linked pressure-sensitive adhesive polymer and is integrated with a convex portion.
な主要面(５)上に可撓性支持体の層を更に有する請求項
１記載の衝撃緩和性粘着シート。3. The shock-absorbing pressure-sensitive adhesive sheet according to claim 1, further comprising a layer of a flexible support on the flat main surface (5) on which the convex portion of the base is not erected.
キル(メタ)アクリレートとエチレン性不飽和酸と２以上
の(メタ)アクリル基を分子内に有する架橋剤モノマー
０.５〜５重量％とを含むモノマー成分の重合により調
製されたポリマーである、請求項１の衝撃緩和性粘着シ
ート。4. The crosslinked adhesive polymer comprises an alkyl (meth) acrylate, an ethylenically unsaturated acid, and 0.5 to 5% by weight of a crosslinking agent monomer having two or more (meth) acrylic groups in the molecule. The shock-absorbing pressure-sensitive adhesive sheet according to claim 1, which is a polymer prepared by polymerizing a monomer component containing a.
れた請求項１記載の衝撃緩和性粘着シート(１)とを有す
る衝撃緩和構造体であって、該被着物表面と凹部の内面
とから形成される気密空間(４１)を有する衝撃緩和構造
体。5. A shock absorbing structure comprising an adherend (3) and the shock absorbing pressure-sensitive adhesive sheet (1) according to claim 1, which is adhered to the surface (31) of the adherend. A shock absorbing structure having an airtight space (41) formed from the inner surface of the recess.
剥離する時の２５℃における剥離強度が２０〜２,５０
０ｇ／２５ｍｍの範囲である請求項５記載の衝撃緩和構
造体。6. The peel strength at 25 ° C. when peeling the shock-absorbing pressure-sensitive adhesive sheet from the surface of an adherend is 20 to 2,500.
The shock absorbing structure according to claim 5, which has a range of 0 g / 25 mm.