JPH09226825A - Packaging plastic film or sheet - Google Patents
Packaging plastic film or sheetInfo
- Publication number
- JPH09226825A JPH09226825A JP3658196A JP3658196A JPH09226825A JP H09226825 A JPH09226825 A JP H09226825A JP 3658196 A JP3658196 A JP 3658196A JP 3658196 A JP3658196 A JP 3658196A JP H09226825 A JPH09226825 A JP H09226825A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum
- plastic film
- film
- sheet
- aluminum pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は各種包装材の分野の
中でも特に、電子レンジによるマイクロ波の照射を受け
た時に、内容物の温度が上昇するのを避ける必要がある
食品包装用プラスチックフィルムに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plastic film for food packaging, in which it is necessary to prevent the temperature of the contents from rising when irradiated with microwaves from a microwave oven, in particular in the field of various packaging materials. It is a thing.
【０００２】[0002]
【従来の技術】近年コンビニエンスストアーなどで弁当
類を利用する際、電子レンジで加温するのが一般的にな
っている。この時弁当の中には醤油／ソース等の調味料
類が小さいプラスチックフィルムの袋に入って同封され
ている事が多い。これらは内容物が加温されるのを避け
る必要があるが、弁当の加温時にはこれをわざわざ取り
除く手間が嫌われる事が多く、調味料の包装材がマイク
ロ波を透過するプラスチックフィルムである場合、内容
物を加温してしまい、ひどい場合には内容物の沸騰によ
り袋が破裂して内容物が弁当容器内に飛散してしまうこ
とがある。また弁当に刺身、漬け物、サラダ、果物のよ
うな生ものが含まれている場合これらが加温されると風
味が著しく低下するため、これらを加温から保護するよ
うな包装材が求められている。2. Description of the Related Art In recent years, when using lunch boxes in convenience stores and the like, it has become common to heat them in a microwave oven. At this time, the seasoning such as soy sauce / sauce is often enclosed in a small plastic film bag inside the bento box. It is necessary to avoid heating the contents of these, but it is often the case that the time and effort to remove them when heating the bento is disliked, and when the packaging material for the seasoning is a microwave-permeable plastic film. The contents are heated, and in severe cases, boiling of the contents may cause the bag to burst and the contents to be scattered in the lunch box container. Also, if the bento contains raw fish such as sashimi, pickles, salads, and fruits, the flavor will significantly decrease when heated, so packaging materials that protect these from heating are required. There is.
【０００３】このため例えばアルミニウム箔は電子レン
ジによるマイクロ波を透過しないために、プラスチック
のフィルムやシート上にアルミニウム箔膜による層を形
成させたものがこのための包装材として使用されてい
る。しかしアルミニウム箔表面は導電性の層を形成して
いるために、ここにマイクロ波が照射されると帯電した
電荷によりスパークが発生し、包装材が収縮や溶解を起
こしたり、ひどい場合には電子レンジを破損する事もあ
り問題となっていた。For this reason, for example, since aluminum foil does not transmit microwaves from a microwave oven, a plastic film or sheet on which a layer of an aluminum foil film is formed is used as a packaging material for this purpose. However, since the surface of the aluminum foil forms a conductive layer, when microwaves are applied to it, sparks are generated due to the charged electric charge, causing the packaging material to shrink or dissolve, and in the worst case, electronic It was a problem because it could damage the range.
【０００４】このため例えば実開平５−３６３９５号公
報においては金属箔膜を絶縁素材で挟み込む事により金
属部分同士の接触を避け、スパークの発生を防ぐ方法が
提案されている。しかしこの場合には袋のヒートシール
部の外縁端部分には金属箔膜が露出するためにスパーク
の発生を完全に防止することはできなかった。For this reason, for example, Japanese Utility Model Laid-Open No. 5-36395 proposes a method of preventing the occurrence of sparks by sandwiching a metal foil film with an insulating material to avoid contact between metal parts. However, in this case, the metal foil film was exposed at the outer edge portion of the heat-sealed portion of the bag, so that the generation of sparks could not be completely prevented.
【０００５】また実開平６−６５２７８号公報において
はアルミニウム箔や金属蒸着などの金属箔膜が袋の周縁
部に露出しないようにし、かつ金属箔鋭角部をなくすこ
とによってスパークの発生を防止する袋を提案してい
る。しかしこの方法においては導電体である金属箔層が
袋のヒートシール部の外縁端部分に存在しないようにす
るため、袋にした場合シール部の外縁端部分になる箇所
のアルミニウム箔や蒸着膜を、エッチングなどの処理に
より部分的に除去する必要があり、工程が複雑になりコ
ストアップになる欠点があった。又別の問題として金属
箔層がある部分と、エッチング処理により無い部分でフ
ィルムの厚み差が生じ、それが段差となってヒートシー
ル時のヒート不良トラブルとなることがあった。Further, in Japanese Utility Model Laid-Open No. 6-65278, a bag is formed so that a metal foil film such as an aluminum foil or a metal vapor deposition is not exposed at the peripheral portion of the bag, and a sharp edge portion of the metal foil is eliminated to prevent the occurrence of sparks. Is proposed. However, in this method, in order to prevent the metal foil layer, which is a conductor, from being present at the outer edge portion of the heat-sealing portion of the bag, the aluminum foil or the vapor-deposited film at the portion which becomes the outer edge portion of the sealing portion when formed into a bag is used. However, it is necessary to partially remove it by a treatment such as etching, which has a drawback that the process is complicated and the cost is increased. Another problem is that there is a difference in film thickness between the portion where the metal foil layer is present and the portion where it is not subjected to the etching treatment, which causes a step difference, which may cause a heat failure problem during heat sealing.
【０００６】また特開昭６３−１５７８５８号公報にお
いてはスズ系の合金を用いて、金属蒸着層を連続箔膜で
はなく特定の島状構造にする事によって、マイクロ波の
透過性及び絶縁性を高め、スパークの発生を防ぐ方法を
提案している。しかしこの方法では、マイクロ波の一部
が金属蒸着層を透過するため、内容物の加温を完全に防
止する事は困難であった。Further, in Japanese Patent Laid-Open No. 63-157858, a tin-based alloy is used to form a metal vapor deposition layer into a specific island-like structure instead of a continuous foil film, thereby improving microwave transmission and insulation properties. It proposes a method to raise and prevent the occurrence of sparks. However, in this method, it is difficult to completely prevent the heating of the contents, because part of the microwaves penetrates the metal vapor deposition layer.
【０００７】[0007]
【発明が解決しようとする課題】本発明は電子レンジに
よる加温の際に、マイクロ波の遮断効果が高いために内
容物の温度が上昇することがなく、なおかつ包装材を劣
化させるスパークの発生を防止する事が可能な包装用プ
ラスチックフィルム又はシートを提供することを目的と
するものである。DISCLOSURE OF THE INVENTION According to the present invention, the temperature of the contents does not rise due to the high microwave blocking effect during heating by a microwave oven, and the sparks that deteriorate the packaging material are generated. An object of the present invention is to provide a plastic film or sheet for packaging capable of preventing the above.
【０００８】[0008]
【課題を解決するための手段】本発明は、プラスチック
フィルム又はシート上に、アルミニウム顔料を含むイン
キを用いた印刷によるコーティング層を形成させた、電
子レンジによる加熱調理に適した包装用プラスチックフ
ィルム及びプラスチックシートに関わるものである。DISCLOSURE OF THE INVENTION The present invention relates to a plastic film for packaging, which is suitable for cooking by microwave oven, in which a coating layer formed by printing with an ink containing an aluminum pigment is formed on a plastic film or sheet, and a plastic film for packaging. It is related to plastic sheets.
【０００９】本発明における必須の条件としては印刷に
用いられるインキの顔料としてアルミニウム顔料を使用
する事があげられる。プラスチックフィルム上に印刷に
より形成されたコーティング層は通常膜厚が０．５〜２
ミクロン程度の層であり、インキのバインダー樹脂中に
細かい鱗片状のアルミニウムフレークが幾重にも層をな
して分散した構造になっている。通常印刷においてアル
ミニウム顔料を使用すると、このアルミニウムフレーク
層部分によって電磁波である可視光や赤外線を遮断する
効果が得られる。発明者らはこの点に着目し鋭意検討の
結果、顔料としてアルミニウムを用いたインキによって
プラスチックフィルム表面に印刷によるコーティングを
行い、このフィルムを食品包装材として使用することに
よって、電子レンジにおけるマイクロ波を高度に遮断す
る事が可能である事をつきとめ、本発明に至った。An essential condition in the present invention is to use an aluminum pigment as the pigment of the ink used for printing. The coating layer formed by printing on a plastic film usually has a thickness of 0.5 to 2
It is a layer of about a micron, and has a structure in which fine flaky aluminum flakes are dispersed in layers in the binder resin of the ink. When an aluminum pigment is used in normal printing, this aluminum flake layer portion has the effect of blocking visible light and infrared rays, which are electromagnetic waves. The inventors of the present invention have paid attention to this point, and as a result of earnest studies, as a result, a plastic film surface is coated by printing with an ink using aluminum as a pigment, and by using this film as a food packaging material, microwaves in a microwave oven are prevented. The inventors have found that it is possible to shut off at a high degree, and have reached the present invention.
【００１０】加えて本発明で重要な事は電子レンジにお
けるマイクロ波の照射時にスパークが全く発生しないこ
とである。この理由としては、本発明の印刷コーティン
グ層においては、顔料である個々の微細なアルミニウム
フレーク粒子がバインダー樹脂により覆われているため
絶縁性が付与されている事が考えられる。In addition, what is important in the present invention is that no spark occurs at the time of microwave irradiation in a microwave oven. It is considered that the reason for this is that in the print coating layer of the present invention, since individual fine aluminum flake particles which are pigments are covered with the binder resin, the insulating property is imparted.
【００１１】またアルミニウムフレーク粒子に到達する
マイクロ波があっても、アルミニウムフレークは平均粒
子径が５〜４０ミクロン、厚みが０．５ミクロン以下の
微細な粒子で、さらに丸みを帯びているために、スパー
クを起こすような帯電や放電が起き難いと考えられる。Even if there are microwaves reaching the aluminum flake particles, the aluminum flakes are fine particles having an average particle size of 5 to 40 μm and a thickness of 0.5 μm or less, and are rounded. It is considered that charging and discharging that cause sparks are unlikely to occur.
【００１２】またマイクロ波遮断層としてアルミニウム
フレークを含む印刷コーティング層を用いることによっ
て、コーティング工程における生産性やコストを著しく
向上させることが出来る。例えば実開平６−６５２７８
においては、プラスチックフィルム上にマイクロ波遮断
層としてアルミニウム箔層を設けているが、ここでは金
属蒸着をしたりアルミニウム箔を張り合わせた後に、ス
パークの原因となるヒートシール部のアルミニウム箔を
エッチング処理により一部カットしており、その分工程
やコストが増えることになるが、本発明においてはヒー
トシール部の一部カット加工が不要なため、グラビア印
刷後を行うだけで直ぐに包装用ラミネート基材として使
用が可能である。By using a printed coating layer containing aluminum flakes as the microwave blocking layer, the productivity and cost in the coating process can be significantly improved. For example, actual Kaihei 6-65278
In, the aluminum foil layer is provided as a microwave blocking layer on the plastic film, but here, after the metal vapor deposition or the aluminum foil is laminated, the aluminum foil in the heat-sealing part that causes sparks is etched. Although it is partially cut, the process and cost will increase by that amount, but in the present invention it is not necessary to partially cut the heat seal part, so it can be immediately used as a packaging laminate base material after performing gravure printing. It can be used.
【００１３】次にコーティング層が十分なマイクロ波の
遮断性を得て、なおかつスパークが発生しないために
は、アルミニウム粒子層によってコーティング層に高い
隠蔽性を与えた上で、アルミニウム粒子がバインダー樹
脂でしっかりと被覆保護されている事が必要になる。こ
のためにはアルミニウム顔料の比表面積ＳＳＡを２〜２
０ｍ2／ｇ、好ましくは５〜１８ｍ2／ｇにし、かつイン
キ塗膜層におけるバインダー樹脂に対するアルミニウム
顔料の固形分重量比を好ましくは１５〜６０％、より好
ましくは２０〜５０％にする。アルミニウム顔料の比表
面積ＳＳＡが２ｍ2／ｇ未満であるとマイクロ波の遮断
が不十分になり内容物を加温してしまうことになり、２
０ｍ2／ｇより大きいとアルミニウム粒子の平均粒子径
が細かくなりすぎるため、金属アルミニウム特有の輝度
感が著しく低下するという意匠性上の問題が発生する。
またアルミニウム顔料のバインダー樹脂に対する固形分
重量比が１５ｐｈｒ未満であるとやはりマイクロ波の遮
断性が不十分になり、また６０ｐｈｒ以上になるとコー
ティング層においてバインダー樹脂に対するアルミニウ
ム顔料の比率が高くなりすぎて、バインダー樹脂が不連
続になり、部分的に金属の露出が起きるためにスパーク
の原因となる。Next, in order for the coating layer to have a sufficient microwave blocking property and to prevent sparks from being generated, the aluminum particle layer provides the coating layer with a high hiding property, and the aluminum particles serve as a binder resin. It is necessary that it is covered and protected firmly. To this end, the specific surface area SSA of the aluminum pigment is 2 to 2
0 m 2 / g, preferably in 5~18m 2 / g, and preferably 15 to 60% by solid weight ratio of aluminum pigment to binder resin in the ink coating film layer, more preferably 20 to 50%. If the specific surface area SSA of the aluminum pigment is less than 2 m 2 / g, the microwaves will not be sufficiently shielded and the contents will be heated.
If it is larger than 0 m 2 / g, the average particle diameter of the aluminum particles becomes too fine, so that there is a problem in terms of design that the brightness feeling peculiar to metallic aluminum is remarkably reduced.
If the solid content weight ratio of the aluminum pigment to the binder resin is less than 15 phr, the microwave blocking property is also insufficient, and if it is 60 phr or more, the ratio of the aluminum pigment to the binder resin in the coating layer becomes too high. The binder resin becomes discontinuous and partially exposed to the metal, which causes sparks.
【００１４】なお印刷によるコーティング層の膜厚につ
いては１μｍ以上あることが好ましく、２μｍ以上あれ
ばより好ましい。The thickness of the coating layer formed by printing is preferably 1 μm or more, more preferably 2 μm or more.
【００１５】次に本発明の包装用プラスチックフィルム
及びプラスチックシートの製造方法であるが、用いられ
るプラスチックフィルムとしては通常食品包装用に用い
られるポリエステル、ナイロン、ポリエチレン、セロハ
ンなどの延伸又は無延伸のフィルムや、ポリビニールア
ルコール、ポリ塩化ビニール、ポリ塩化ビニリデンなど
のフィルムがある。これらのフィルムは単層フィルムで
あっても、又は共押し出しフィルムであってもよく、又
ガスバリアー性が必要な場合は塩化ビニリデンがコーテ
ィングされたいわゆるＫコートフィルムや、アルミナ、
シリカ蒸着の様な非導電性の箔膜を蒸着したフィルムな
どであっても良い。又用いられるプラスチックシートは
圧空、真空又はその組み合わせによって型でトレーなど
の形状に賦型形成されるもので、一般的には厚み１５０
μｍ以上のポリエステル、ポリスチレン、ポリプロピレ
ン、ポリエチレン、ポリ塩化ビニール、ポリカーボネー
トなどが用いられる。Next is a method for producing a plastic film for packaging and a plastic sheet of the present invention. The plastic film used is a stretched or non-stretched film of polyester, nylon, polyethylene, cellophane or the like which is usually used for food packaging. There are also films such as polyvinyl alcohol, polyvinyl chloride, and polyvinylidene chloride. These films may be single-layer films or co-extruded films, and when gas barrier properties are required, so-called K-coated films coated with vinylidene chloride, alumina,
It may be a film obtained by vapor deposition of a non-conductive foil film such as silica vapor deposition. The plastic sheet used is formed into a shape such as a tray with a mold by compressed air, vacuum or a combination thereof, and generally has a thickness of 150.
Polyester, polystyrene, polypropylene, polyethylene, polyvinyl chloride, polycarbonate or the like having a size of μm or more is used.
【００１６】アルミニウム顔料を含むインキとしては従
来から使用されている溶剤型と、また近年使用が増加し
ている水性型があるが、いずれのタイプも使用可能であ
りインキ溶剤やインキ用バインダー樹脂に対する制限は
ない。As the ink containing an aluminum pigment, there are a solvent type which has been conventionally used and an aqueous type which has been increasingly used in recent years, but any type can be used and it can be used for an ink solvent or a binder resin for ink. There is no limit.
【００１７】次に本発明で使用するアルミニウム顔料の
形態としては、溶剤を含むペーストタイプと粉末タイプ
があるが、いずれのタイプも使用可能である。Next, as the form of the aluminum pigment used in the present invention, there are a paste type containing a solvent and a powder type, and either type can be used.
【００１８】またアルミニウム顔料は印刷後のコーティ
ング層におけるアルミニウム粒子の配列の仕方から、塗
膜表面に集中的にアルミニウムフレーク粒子が配列する
リーフィングタイプと、塗膜全体に分散配列するノンリ
ーフィングタイプの２つに分けられるが、いずれのタイ
プも使用可能である。しかしリーフィングタイプはラミ
ネートした場合、塗膜表面で層間剥離を起こしやすいた
めノンリーフィングタイプの方が好ましい。The aluminum pigment is classified into a leafing type in which aluminum flake particles are arranged in a concentrated manner on the surface of the coating film and a non-leafing type in which aluminum particles are dispersed and arranged in the entire coating film, depending on the arrangement of the aluminum particles in the coating layer after printing. There are two types, but either type can be used. However, the non-leafing type is preferable because the leafing type tends to cause delamination on the coating film surface when laminated.
【００１９】次に印刷の方式としては、グラビア、フレ
キソ、スクリーン印刷などがあり、方式の制限はないが
印刷コーティング層厚みのコントロール、印刷の簡便性
などから特にグラビア印刷方式が好ましい。印刷方式に
は上記のいわゆる印刷の他にコーティングマシンによる
コーティングも含まれる。又印刷によるコーティングは
フィルム、シートの全面に施しても良いし、本発明の効
果を妨げない限り、その一部に施しても良い。本発明の
包装用プラスチックフィルムとしては、例えば密封袋と
して使用する場合は、アルミニウム顔料を含むインキを
用いた印刷コーティングがヒートシール性を有するフィ
ルムに施されている場合は単独で用いても良いし、他の
基材フィルムや中間層フィルムと組み合わせてラミネー
トして用いても良い。又印刷コーティングがヒートシー
ル性を有さないフィルムに施されている場合にはヒート
シール性を有するフィルム又は樹脂をラミネートして用
いられる。又袋形態での利用を要さない用途、例えば刺
身、漬け物、果物などの非液体のものを含む場合はフィ
ルムにヒートシール性は特に要求されないので印刷コー
ティングされた単独フィルム、又は必要があれば他のフ
ィルムとラミネートして用いられる。Next, the printing method includes gravure, flexo, screen printing and the like, and there is no limitation on the method, but the gravure printing method is particularly preferable from the viewpoint of controlling the thickness of the printing coating layer, easiness of printing and the like. The printing method includes coating by a coating machine in addition to the so-called printing described above. The coating by printing may be applied to the entire surface of the film or sheet, or may be applied to a part of the film or sheet as long as the effect of the present invention is not impaired. As the packaging plastic film of the present invention, for example, when it is used as a sealed bag, it may be used alone when a print coating using an ink containing an aluminum pigment is applied to a film having heat sealability. Alternatively, it may be laminated and used in combination with another substrate film or an intermediate layer film. When the print coating is applied to a film having no heat-sealing property, it is used by laminating a film having heat-sealing property or a resin. In addition, applications that do not require use in bag form, such as sashimi, pickles, and fruits that include non-liquid ones, do not require heat-sealability in the film, so a print-coated single film, or if necessary It is used by laminating with other films.
【００２０】又、本発明のプラスチックシートは圧空、
真空形成法などにより、各種サイズ、形状のトレー形態
に賦型して電子レンジ用のマイクロ波の遮断効果の高い
容器として用いることができる。又本発明のプラスチッ
クフィルム、シートには本発明の印刷コーティングの他
にデザインなどのための別の印刷が施されても良い。Further, the plastic sheet of the present invention is compressed air,
By a vacuum forming method or the like, it can be shaped into trays of various sizes and shapes to be used as a container having a high microwave blocking effect for a microwave oven. In addition to the print coating of the present invention, the plastic film or sheet of the present invention may be subjected to other printing for design or the like.
【００２１】以上のように本発明によって電子レンジに
よる加温時に、その高いマイクロ波遮断性によって内容
物を加温しないという特性と、帯電が無いためにスパー
クを起こさないという特性を兼ね備えた包装用材料を提
供する事ができる。尚本発明においてはプラスチックフ
ィルムの代わりにプラスチックシートを使用しても全く
同様の効果が得られる。As described above, according to the present invention, the packaging material has the characteristics that the contents are not heated due to its high microwave blocking property when it is heated by the microwave oven, and that it does not cause sparks due to no charging. Material can be provided. In the present invention, even if a plastic sheet is used instead of the plastic film, the same effect can be obtained.
【００２２】[0022]
【発明の実施の形態】以下、実施例により本発明につい
てさらに具体的な説明をおこなう。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail below with reference to Examples.
【００２３】実施例１ 厚み１２μｍのポリエステルフィルム上に下記の配合に
よるインキを使用して、乾燥後のコーティング膜厚が２
μｍになるようにフィルム全面にグラビア印刷をおこな
った。Example 1 An ink having the following composition was used on a polyester film having a thickness of 12 μm, and the coating film thickness after drying was 2
Gravure printing was performed on the entire surface of the film so that the thickness became μm.
【００２４】このインキ配合ではバインダー樹脂に対す
るアルミニウム顔料の固形分重量比（ｐｈｒ）は次の計
算式で求められる。In this ink formulation, the solid content weight ratio (phr) of the aluminum pigment to the binder resin is determined by the following formula.
【００２５】[0025]
【数１】 [Equation 1]
【００２６】この時アルミニウム顔料の比表面積を比表
面積計（フローソーブ ２３００型、島津製作所製）を
用いて測定したところ２０ｍ2／ｇであった。At this time, the specific surface area of the aluminum pigment was measured using a specific surface area meter (Flowsorb 2300 type, manufactured by Shimadzu Corp.) and found to be 20 m 2 / g.
【００２７】 （配合） ・アルミニウムペースト １０重量部 （１５Ｔ、リーフィングタイプ、固形分６５％、旭化成工業（株）製） ・ウレタン樹脂 ４５重量部 （サンプレンＩＢ−１７００、固形分４０％、三洋化成工業製） ・溶剤（トルエン／ＩＰＡ／ＭＥＫ＝４／３／３） ４５重量部 このグラビア印刷をおこなったポリエステルフィルムの
印刷コーティング層側に２液性ウレタン樹脂を接着剤と
して用いて厚さ４０μｍの直鎖状低密度ポリエチレンフ
ィルムをラミネートした。(Compounding) -Aluminum paste 10 parts by weight (15T, leafing type, solid content 65%, manufactured by Asahi Chemical Industry Co., Ltd.)-Urethane resin 45 parts by weight (Samprene IB-1700, solid content 40%, Sanyo Chemical Industries) Solvent (toluene / IPA / MEK = 4/3/3) 45 parts by weight Using a two-component urethane resin as an adhesive on the printing coating layer side of this gravure-printed polyester film, a 40 μm-thick direct coating is used. A chain low density polyethylene film was laminated.
【００２８】このフィルムを用いてヒートシール部の幅
が５ｍｍで縦横１０ｃｍ四方の水１５ｃｃを充填した４
方袋を作成した。この試験袋に対して電子レンジ（日立
熱器具株式会社製ＭＲＯ−Ｍ５６２型、定格高周波出力
５００Ｗ）を用いて２分間加熱し、下記評価項目につい
て適性を確認した。 (1)耐加温性 加温前後の袋の表面の温度を接触型の温度計で測定し加
熱による昇温の程度を調べる。Using this film, a heat-sealed portion having a width of 5 mm and a length of 10 cm was filled with 15 cc of water 4
I made a bag. The test bag was heated for 2 minutes by using a microwave oven (MRO-M562 type manufactured by Hitachi Thermal Equipment Co., Ltd., rated high-frequency output of 500 W), and the suitability of the following evaluation items was confirmed. (1) Resistance to heating Measure the temperature of the bag surface before and after heating with a contact-type thermometer to check the temperature rise due to heating.
【００２９】評価基準 ◎：５℃未満 ○：５℃以上１０℃未満 ×：１０℃以上 (２) 耐スパーク性 加温時のスパーク発生の有無を確認する。 評価基準 ◎：全く発生しない ○：実用上問題ないが、わずかに発生する ×：実用上問題となる程発生する 実施例２ アルミニウム顔料として旭化成工業（株）製のアルミニ
ウムペースト／ＳＡ−８０００Ｔ（ノンリーフィングタ
イプ、比表面積８．０ｍ2／ｇ）用いる以外は実施例１
と同様の方法で試験をおこなった。Evaluation Criteria ⊚: Less than 5 ° C. ∘: 5 ° C. or more and less than 10 ° C. ×: 10 ° C. or more Evaluation Criteria ⊚: No occurrence at all ∘: There is no problem in practical use, but a slight occurrence occurs ×: It occurs so as to cause a problem in practical use Example 2 As an aluminum pigment, aluminum paste / SA-8000T (Non-paste) Leafing type, specific surface area 8.0 m 2 / g) Example 1 except using
The test was conducted in the same manner as in.
【００３０】比較例１ 厚み１２μｍのポリエステルフィルム上にグラビア印刷
をおこなう代わりに、７μｍ厚のアルミニウム箔を張り
合わせた以外は、実施例１と同様の方法で試験をおこな
った。Comparative Example 1 A test was conducted in the same manner as in Example 1 except that an aluminum foil having a thickness of 7 μm was laminated on the polyester film having a thickness of 12 μm, instead of performing gravure printing.
【００３１】実施例３ アルミニウム顔料として旭化成工業（株）製のアルミニ
ウムペースト／ＭＦ−２０（ノンリーフィングタイプ、
比表面積１．５ｍ2／ｇ）を用いる以外は実施例１と同
様の方法で試験をおこなった。Example 3 As an aluminum pigment, Asahi Kasei Kogyo KK aluminum paste / MF-20 (non-leafing type,
A test was conducted in the same manner as in Example 1 except that a specific surface area of 1.5 m 2 / g) was used.
【００３２】実施例４ アルミニウム顔料のバインダー樹脂に対する比率を１０
ｐｈｒにする以外は実施例１と同様の方法で試験をおこ
なった。Example 4 The ratio of aluminum pigment to binder resin was 10
A test was conducted in the same manner as in Example 1 except that the phr was used.
【００３３】実施例５ アルミニウム顔料のバインダー樹脂に対する比率を７０
ｐｈｒにする以外は実施例１と同様の方法で試験をおこ
なった。Example 5 The ratio of aluminum pigment to binder resin was 70.
A test was conducted in the same manner as in Example 1 except that the phr was used.
【００３４】[0034]
【表１】 [Table 1]
【００３５】実施例６ 厚み１５μｍのナイロン６フィルム上に実施例１と同じ
インキ処方でコーティング膜厚が３μｍになるようにフ
ィルム全面にグラビア印刷コーティングをおこなった。Example 6 A nylon 6 film having a thickness of 15 μm was subjected to gravure printing coating on the entire surface of the film with the same ink formulation as in Example 1 so that the coating film thickness was 3 μm.
【００３６】このフィルムで刺身１５ｇをフィルム一重
で包み、実施例１で用いたのと同じ電子レンジで２分間
加熱し、加熱前後で刺身内部の温度上昇を測定したとこ
ろ４度で、加熱前後で同じ食感が得られた。15 g of sashimi was wrapped in a single layer with this film, heated in the same microwave oven as used in Example 1 for 2 minutes, and the temperature rise inside the sashimi was measured before and after heating. The same texture was obtained.
【００３７】実施例７ 厚み２００μｍのポリスチレンシート上に実施例１と同
様にしてコーティング膜厚が３μｍになるようにシート
全面にグラビア印刷コーティングをおこなった。Example 7 A gravure printing coating was performed on a polystyrene sheet having a thickness of 200 μm in the same manner as in Example 1 so that the coating film thickness was 3 μm.
【００３８】このシートを圧空成型法により縦横５ｃｍ
四方、高さ３ｃｍの箱形のトレーを成形した。This sheet is 5 cm in length and width by a pressure molding method.
A box-shaped tray having a height of 3 cm on each side was formed.
【００３９】このトレーにポテトサラダ２５ｇを入れ、
同じサイズの別のトレーをかぶせて蓋をし実施例１と同
じ電子レンジで２分間加熱した。加熱後のサラダの内温
上昇は３℃であり、加熱前と同じ食感が得られた。Put 25 g of potato salad in this tray,
It was covered with another tray of the same size, covered, and heated in the same microwave oven as in Example 1 for 2 minutes. The rise in internal temperature of the salad after heating was 3 ° C, and the same texture as before heating was obtained.
【００４０】この試験結果から本発明によるプラスチッ
ク包装材は電子レンジにかけられることを前提とした食
品包装材として優れた性能を有していることが確認され
た。From the results of this test, it was confirmed that the plastic packaging material according to the present invention has excellent performance as a food packaging material that is supposed to be put into a microwave oven.
【００４１】[0041]
【発明の効果】以上説明したように、本発明によればマ
イクロ波照射下においてそのマイクロ波遮断効果が高
く、かつスパークの発生を防止することができる。した
がって、本発明のフィルム又はシートは、とくに電子レ
ンジ用食品包装材として好適である。As described above, according to the present invention, the microwave blocking effect is high under the irradiation of microwaves and the generation of sparks can be prevented. Therefore, the film or sheet of the present invention is particularly suitable as a food packaging material for microwave oven.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 奥田 泰正 茨城県西茨城郡友部町大古山499 旭化成 メタルズ株式会社内 (72)発明者 石井 文男 東京都台東区松が谷２−31−１ ─────────────────────────────────────────────────── ─── Continued Front Page (72) Inventor Yasumasa Okuda 499 Okoyama, Tomobe-cho, Nishi-Ibaraki-gun, Ibaraki Prefecture Asahi Kasei Metals Co., Ltd. (72) Inventor Fumio Ishii 2-31-1 Matsugaya, Taito-ku, Tokyo
Claims (2)
シート上に、アルミニウム顔料を含むインキによるコー
ティング層を形成させた事を特徴とする、電子レンジ加
熱調理に適した包装用プラスチックフィルム又はシー
ト。1. A plastic film or sheet for packaging suitable for microwave cooking, comprising a plastic film or plastic sheet on which a coating layer of an ink containing an aluminum pigment is formed.
２．０〜２０ｍ2／ｇであり、かつ印刷コーティング層
におけるバインダー樹脂に対するアルミニウム顔料の固
形分重量比が１５〜６０ｐｈｒであることを特徴とする
請求項１に記載の包装用プラスチックフィルム及びプラ
スチックシート。2. The aluminum pigment has a specific surface area SSA of 2.0 to 20 m 2 / g, and the solid weight ratio of the aluminum pigment to the binder resin in the print coating layer is 15 to 60 phr. Item 2. A plastic film for packaging and a plastic sheet according to Item 1.