JPH09209266A - Fiber structure and production of the same - Google Patents
Fiber structure and production of the sameInfo
- Publication number
- JPH09209266A JPH09209266A JP8314729A JP31472996A JPH09209266A JP H09209266 A JPH09209266 A JP H09209266A JP 8314729 A JP8314729 A JP 8314729A JP 31472996 A JP31472996 A JP 31472996A JP H09209266 A JPH09209266 A JP H09209266A
- Authority
- JP
- Japan
- Prior art keywords
- fiber structure
- hydrophilic vinyl
- structure according
- monomer
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、快適な着用感を奏
するドレスシャツ、肌着、スポーツウエア等の繊維構造
物およびその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a textile structure such as a dress shirt, underwear, sportswear, etc., which provides a comfortable wearing feeling, and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】ドレスシャツ、肌着、スポーツウェアと
いった人体に直接触れたり、運動時に使用する衣料に
は、着用時の快適性が要求されるが、中でも吸湿性は快
適性を左右する重要な機能の一つである。2. Description of the Related Art Clothing such as dress shirts, underwear, and sportswear that are directly touched by the human body and used during exercise require comfort when worn, and hygroscopicity is an important function that affects comfort. one of.
【０００３】木綿や麻といったセルロース繊維１００％
からなるドレスシャツ、肌着、スポーツウェアは吸湿性
に優れているが、快適性に対する要求は高まっており、
従来のセルロース繊維からなるドレスシャツなどではそ
うした要求に十分対応できなくなってきている。100% cellulose fibers such as cotton and hemp
The dress shirts, underwear, and sportswear made of are excellent in moisture absorption, but the demand for comfort is increasing,
Conventional dress shirts made of cellulose fibers are no longer able to meet such demands.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、セルロース
繊維を用いてなる繊維構造物において、快適な着用感を
奏するドレスシャツ、肌着、スポーツウエア等の繊維構
造物およびその製造方法を提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention provides a fiber structure made of cellulosic fibers, such as a dress shirt, underwear, sportswear, etc., which gives a comfortable wearing feeling, and a method for producing the same. With the goal.
【０００５】[0005]
【課題を解決するための手段】この目的を達成するた
め、本発明の繊維構造物は、次の構成を有する。In order to achieve this object, the fiber structure of the present invention has the following constitution.
【０００６】すなわち、セルロース繊維を用いてなる繊
維構造物において、該セルロース繊維に親水性ビニル系
モノマが重合されていることを特徴とする繊維構造物で
ある。That is, a fiber structure comprising a cellulose fiber, wherein a hydrophilic vinyl monomer is polymerized in the cellulose fiber.
【０００７】また、本発明の繊維構造物の製造方法は次
の構成を有する。The method for producing a fiber structure of the present invention has the following constitution.
【０００８】すなわち、セルロース繊維からなる繊維構
造物を、親水性ビニル系モノマと重合開始剤を含有する
水溶液の含浸処理を施した後、熱処理を施し、次いで洗
浄することを特徴とする繊維構造物の製造方法である。That is, a fibrous structure comprising a cellulose fiber, which is obtained by impregnating an aqueous solution containing a hydrophilic vinyl monomer and a polymerization initiator, then heat-treating, and then washing. Is a manufacturing method.
【０００９】[0009]
【発明の実施の形態】以下、本発明について詳細に説明
する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below.
【００１０】本発明において、セルロース繊維には、木
綿、麻、レーヨン等のセルロースを骨格としてなる繊維
が用いられる。In the present invention, fibers having a skeleton of cellulose such as cotton, hemp and rayon are used as the cellulose fibers.
【００１１】本発明の繊維構造物は、セルロース繊維か
らなる糸を織物、編物、または不織布等に織成、編成な
どしたものであるが、セルロース繊維に親水性ビニル系
モノマが重合されてなる繊維構造物である。セルロース
繊維以外の繊維が含まれていてもよいが、セルロース繊
維の吸湿性、保温性等の特性を十分に活かすために実質
的にセルロース繊維からなることが好ましい。The fiber structure of the present invention is a woven fabric, a knitted fabric, a non-woven fabric, or the like in which yarns made of cellulose fibers are woven or knitted. Fibers obtained by polymerizing hydrophilic vinyl monomers in the cellulose fibers. It is a structure. Although fibers other than the cellulose fibers may be contained, it is preferable that the fibers substantially consist of the cellulose fibers in order to fully utilize the properties of the cellulose fibers such as hygroscopicity and heat retention.
【００１２】本発明において、親水性ビニル系モノマと
は、分子構造内に重合性のビニル基を有し、かつカルボ
ン酸、スルホン酸等の酸性基および／またはその塩、水
酸基、アミド基等の親水性基を有するモノマをいう。In the present invention, the hydrophilic vinyl-based monomer has a polymerizable vinyl group in its molecular structure, and has an acidic group such as carboxylic acid or sulfonic acid and / or its salt, hydroxyl group, amide group and the like. A monomer having a hydrophilic group.
【００１３】具体的には、アクリル酸、アクリル酸ナト
リウム、アクリル酸アルミニウム、アクリル酸亜鉛、ア
クリル酸カルシウム、アクリル酸マグネシウム等のアク
リル酸塩類モノマー、２−アクリルアミド−２−メチル
プロパンスルホン酸、メタクリル酸、アリルアルコー
ル、アリルスルホン酸ナトリウム、アクリルアミド、ビ
ニルスルホン酸ナトリウム、メタリルスルホン酸ナトリ
ウム、スチレンスルホン酸ナトリウム等を用いることが
できる。これらは、１種単独で用いてもよく、または２
種以上を併用してもよい。Specifically, acrylic acid monomers such as acrylic acid, sodium acrylate, aluminum acrylate, zinc acrylate, calcium acrylate, and magnesium acrylate, 2-acrylamido-2-methylpropanesulfonic acid, and methacrylic acid. , Allyl alcohol, sodium allyl sulfonate, acrylamide, sodium vinyl sulfonate, sodium methallyl sulfonate, sodium styrene sulfonate and the like can be used. These may be used alone, or 2
More than one species may be used in combination.
【００１４】これらの中でも、２−アクリルアミド−２
−メチルプロパンスルホン酸および／またはそのナトリ
ウム塩、アリルスルホン酸ナトリウム等の分子構造内に
スルホン酸および／またはその塩を含有するモノマが、
反応性に優れる点で好ましい。Among these, 2-acrylamide-2
-A monomer containing sulfonic acid and / or its salt in the molecular structure of methyl propane sulfonic acid and / or its sodium salt, sodium allyl sulfonate, etc.,
It is preferable in terms of excellent reactivity.
【００１５】本発明の繊維構造物は、セルロース繊維に
上記の親水性ビニルモノマが重合されているものからな
るため、吸湿性が特に優れたものとなる。Since the fibrous structure of the present invention is composed of cellulose fibers polymerized with the above-mentioned hydrophilic vinyl monomer, the hygroscopicity thereof is particularly excellent.
【００１６】ここで「セルロース繊維に親水性ビニル系
モノマが重合されている」とは、セルロース繊維に親水
性ビニル系モノマがグラフト重合していること、セルロ
ース繊維の空隙内（中空部など）で親水性ビニル系モノ
マがラジカル重合していること、またはセルロース単繊
維内部で親水性ビニル系モノマがラジカル重合している
ことをいう。なお、親水性ビニル系モノマがセルロース
繊維の空隙内やセルロース単繊維内部にグラフト重合や
ラジカル重合していることは、吸湿性の耐久性を格別な
ものとし、かつ織編物の風合いを阻害しないので好まし
い。セルロース繊維に親水性ビニル系モノマが重合して
いることは、例えば切片染色法により確認できる。切片
染色法は次のように行う。パラフィンで包埋した繊維束
を繊維軸に垂直方向に切断し、切片を作製する。この切
片を有機溶媒等で脱包埋した後、適切な染料（例えば塩
基性染料）を用いて染色し、水洗する。これを光学顕微
鏡で観察することにより親水性ビニル重合体の存在を確
認できる。Here, "the hydrophilic vinyl-based monomer is polymerized on the cellulose fiber" means that the hydrophilic vinyl-based monomer is graft-polymerized on the cellulose fiber, and that the cellulose fiber is in the voids (hollow part, etc.). It means that the hydrophilic vinyl-based monomer is radically polymerized or that the hydrophilic vinyl-based monomer is radically polymerized inside the cellulose single fiber. Incidentally, the fact that the hydrophilic vinyl-based monomer is graft-polymerized or radical-polymerized in the voids of the cellulose fibers or inside the cellulose single fibers makes the hygroscopic durability exceptional and does not hinder the texture of the woven or knitted fabric. preferable. The fact that the hydrophilic vinyl-based monomer is polymerized on the cellulose fiber can be confirmed by, for example, a section staining method. The section staining method is performed as follows. A paraffin-embedded fiber bundle is cut in the direction perpendicular to the fiber axis to prepare a section. This section is deembedded with an organic solvent or the like, then stained with an appropriate dye (for example, a basic dye), and washed with water. The presence of the hydrophilic vinyl polymer can be confirmed by observing this with an optical microscope.
【００１７】親水性ビニル系モノマの繊維構造物に対す
る反応率は、繊維構造物の風合いを良好に保持しつつ優
れた吸湿性を得る観点から、１重量％以上２０重量％以
下であることが好ましい。３重量％以上１７重量％以下
であることはより好ましく、６重量％以上１５重量％以
下であることはさらに好ましい。なお、ここでいう反応
率とは、繊維構造物が親水性ビニル系モノマの重合によ
って増加した重量の割合（重量％）のことをいい、１０
０×［（親水性ビニル系モノマの重合をした後の繊維構
造物の絶乾重量）−（親水性ビニル系モノマの重合をす
る前の繊維構造物の絶乾重量）］／（親水性ビニル系モ
ノマの重合をする前の絶乾重量）から算出される。The reaction rate of the hydrophilic vinyl-based monomer with respect to the fiber structure is preferably 1% by weight or more and 20% by weight or less from the viewpoint of obtaining excellent hygroscopicity while maintaining good texture of the fiber structure. . It is more preferably 3% by weight or more and 17% by weight or less, and further preferably 6% by weight or more and 15% by weight or less. The reaction rate as used herein means the proportion (% by weight) of the weight of the fiber structure increased by the polymerization of the hydrophilic vinyl-based monomer.
0 × [(absolute dry weight of fiber structure after polymerization of hydrophilic vinyl monomer)-(absolute dry weight of fiber structure before polymerization of hydrophilic vinyl monomer)] / (hydrophilic vinyl It is calculated from the absolute dry weight before the polymerization of the system monomer).
【００１８】また、本発明の繊維構造物は、温度３０
℃、湿度９０％における繊維構造物の吸湿率ＭＲ２
（％）から温度２０℃、湿度６５％における繊維構造物
の吸湿率ＭＲ１（％）を差し引いた値で表されるΔＭＲ
が、下記式を満足することが好ましい。The fiber structure of the present invention has a temperature of 30.
Moisture absorption rate MR2 of fiber structure at ℃ and humidity of 90%
ΔMR represented by the value obtained by subtracting the moisture absorption rate MR1 (%) of the fiber structure at a temperature of 20 ° C. and a humidity of 65% from (%)
However, it is preferable that the following formula is satisfied.
【００１９】４＜ΔＭＲ≦１４ なお、温度２０℃、湿度６５％における繊維構造物の吸
湿率ＭＲ１（％）は、標準的な環境下での衣服のもつ吸
湿性と考えることができるものであり、温度３０℃、湿
度９０％における繊維構造物の吸湿率ＭＲ２（％）は、
軽く運動した後の衣服のもつ吸湿性と考えることができ
るものである。4 <ΔMR ≦ 14 The moisture absorption rate MR1 (%) of the fibrous structure at a temperature of 20 ° C. and a humidity of 65% can be considered as the hygroscopicity of the clothes under a standard environment. The moisture absorption rate MR2 (%) of the fiber structure at a temperature of 30 ° C. and a humidity of 90% is
It can be considered as the hygroscopicity of clothes after light exercise.
【００２０】親水性ビニル系モノマを重合していないセ
ルロース繊維から実質的になる繊維構造物のΔＭＲは
３．６〜４である。The ΔMR of the fiber structure which is substantially composed of cellulose fibers in which the hydrophilic vinyl monomer is not polymerized is 3.6 to 4.
【００２１】本発明の繊維構造物は、吸湿性に特に優れ
るため、ドレスシャツ、肌着、スポーツウェアなどの人
体に直接触れたり、発汗量が多いときに着用するような
衣服として好ましく用いられる。Since the fibrous structure of the present invention is particularly excellent in hygroscopicity, it is preferably used as clothes such as dress shirts, underwear, and sportswear which are directly contacted with the human body or worn when the amount of sweat is large.
【００２２】ここでいうドレスシャツとは、ワイシャ
ツ、セミシャツ、カッターシャツ、スクールシャツ、一
般作業シャツ、サービスシャツ、シャツブラウス、オー
バーブラウス、Ｔシャツ、ニットシャツ、開衿シャツ、
アロハシャツ、ポロシャツ等を含む。The dress shirt referred to here is a shirt, a semi-shirt, a cutter shirt, a school shirt, a general work shirt, a service shirt, a shirt blouse, an overblouse, a T-shirt, a knit shirt, an open collar shirt,
Includes Aloha shirts, polo shirts, etc.
【００２３】また、肌着とは、パンツ、アンダーシャ
ツ、ショーツ、ロングパンツ、ステテコ、ブリーフ、サ
ニタリショーツ、スキャンティ、ランニングシャツ、ズ
ボン下、スリップ、シュミーズ、ペチコート、キャミソ
ール、パニエ、ブラジャー、ガードル、ウェストニッパ
ー、ガーターベルト、レオタード、オーバーオール、ロ
ンパス、オムツカバー用織編物の他、スラックス等直接
肌に触れるものも含む。Underwear means pants, undershirts, shorts, long pants, steteco, briefs, sanitary shorts, scanties, running shirts, under pants, slips, chemise, petticoats, camisole, pannier, brassiere, girdle, waist nippers, In addition to garter belts, leotards, overalls, rompass, woven and knitted fabrics for diaper covers, slacks and other items that come into direct contact with the skin are also included.
【００２４】また、スポーツウェアとは、トレパン、ト
レシャツ、アスレチックウェア、ジョギングウェア、ウ
ォームアップ、ランニングパンツ、テニスウェア、ベー
スボールウェア、ソフトボールウェア、バレーボールウ
ェア、バスケットボールウェア、ゴルフジャンパー、ゴ
ルフブルゾン、アノラック、スノーウェア、マウンテン
ウェア、ウインドブレーカー、ポンチョ、スキーアウタ
ー、スキーパンツ、スキーズボン、スキーピステル、競
泳水着用織編物、スクール水着用織編物、遊泳水着用織
編物、ビーチウェア用織編物、マリンウェア用織編物、
ウェットスーツ用織編物、フィッシングウェア用織編
物、ライダーウェア用織編物等を含む。The sportswear includes trepanes, training shirts, athletic wear, jogging wear, warm-up, running pants, tennis wear, baseball wear, softball wear, volleyball wear, basketball wear, golf jumpers, golf blouson, anorak. , Snow wear, mountain wear, windbreaker, poncho, ski outerwear, ski pants, ski trousers, ski pistels, swimsuit woven / knitted fabric, school swimsuit woven / knitted fabric, swimsuit woven / knitted fabric, beachwear woven / knitted fabric, marine wear Woven knit,
It includes woven and knitted fabrics for wet suits, woven and knitted fabrics for fishing wear, woven and knitted fabrics for rider wear, and the like.
【００２５】次に、本発明の繊維構造物の製造方法につ
いて説明する。Next, the method for producing the fiber structure of the present invention will be described.
【００２６】セルロース繊維からなる糸を用いて織物、
編物、または不織布等に織成、編成などして得られる繊
維構造物を、親水性ビニル系モノマと重合開始剤を含有
する水溶液の含浸処理を施した後、熱処理し、次いで洗
浄することにより本発明の繊維構造物を得ることができ
る。Fabrics using yarns composed of cellulose fibers,
A fibrous structure obtained by weaving or knitting a knitted fabric or a non-woven fabric is impregnated with an aqueous solution containing a hydrophilic vinyl monomer and a polymerization initiator, followed by heat treatment and then washing. The fiber structure of the invention can be obtained.
【００２７】セルロース繊維からなる繊維構造物に親水
性ビニル系モノマと重合開始剤を含有する水溶液の含浸
処理を施す方法としては、例えば、一定時間浸漬する方
法やパディングする方法を採用できる。含浸温度は、特
に制限はなく、常温で行うことができる。As a method of impregnating a fiber structure composed of cellulose fibers with an aqueous solution containing a hydrophilic vinyl monomer and a polymerization initiator, for example, a method of dipping for a certain period of time or a method of padding can be adopted. The impregnation temperature is not particularly limited and may be room temperature.
【００２８】本発明において、重合開始剤にはラジカル
重合で一般に用いられる重合開始剤が好ましく用いられ
る。具体的には、過硫酸アンモニウム、過酸化ベンゾイ
ル等の過酸化物、アゾ系触媒、セリウム触媒等が好まし
く用いられる。In the present invention, a polymerization initiator generally used in radical polymerization is preferably used as the polymerization initiator. Specifically, peroxides such as ammonium persulfate and benzoyl peroxide, azo catalysts and cerium catalysts are preferably used.
【００２９】親水性ビニル系モノマと重合開始剤を含有
する水溶液中における親水性ビニル系モノマの濃度は、
特に制限はないが、反応を効率的に行う観点から１０重
量％以上３０重量％以下の濃度が好ましい。１３重量％
以上２７重量％以下であることがより好ましく、１５重
量％以上２５重量％以下であることがさらに好ましい。The concentration of the hydrophilic vinyl-based monomer in the aqueous solution containing the hydrophilic vinyl-based monomer and the polymerization initiator is
Although not particularly limited, a concentration of 10% by weight or more and 30% by weight or less is preferable from the viewpoint of efficiently carrying out the reaction. 13% by weight
It is more preferably at least 27% by weight, and even more preferably at least 15% by weight and at most 25% by weight.
【００３０】親水性ビニル系モノマと重合開始剤を含有
する水溶液中における重合開始剤の濃度は、特に制限は
ないが、反応を効率的に行うため観点から、親水性ビニ
ル系モノマに対して１重量％以上５重量％以下であるこ
とが好ましく、２重量％以上４重量％以下であることが
より好ましい。The concentration of the polymerization initiator in the aqueous solution containing the hydrophilic vinyl-based monomer and the polymerization initiator is not particularly limited, but from the viewpoint of efficiently carrying out the reaction, it is 1 relative to the hydrophilic vinyl-based monomer. The content is preferably 5% by weight or more and 5% by weight or less, more preferably 2% by weight or more and 4% by weight or less.
【００３１】また、セルロース繊維からなる繊維構造物
の強度物性低下を抑制し、また反応を効率的に行う観点
から、親水性ビニル系モノマと重合開始剤を含有する水
溶液のｐＨは６以上１２以下であることが好ましく、ｐ
Ｈが７以上１１以下であることがより好ましい。From the viewpoint of suppressing the deterioration of strength and physical properties of the fiber structure composed of cellulose fibers and efficiently carrying out the reaction, the pH of the aqueous solution containing the hydrophilic vinyl monomer and the polymerization initiator is 6 or more and 12 or less. Is preferred, p
It is more preferable that H is 7 or more and 11 or less.
【００３２】本発明の繊維構造物の製造方法では、含浸
処理後、熱処理を行うが、熱処理は重合反応を行うため
に必須である。熱処理は、乾熱処理、湿熱処理など特に
限定されず採用できる。In the method for producing a fiber structure of the present invention, a heat treatment is carried out after the impregnation treatment, but the heat treatment is essential for carrying out the polymerization reaction. The heat treatment may be dry heat treatment, wet heat treatment or the like without particular limitation.
【００３３】熱処理温度は、特に制限はないが、重合反
応を効率的に行う観点から、８０℃以上２００℃以下の
温度で行うことが好ましい。１段階または２段階以上で
熱処理を行う。熱処理時間は、目的とする反応率との関
係から熱処理温度を勘案して定められるが、２０秒以上
５分以下であることがこのましい。The heat treatment temperature is not particularly limited, but from the viewpoint of efficiently carrying out the polymerization reaction, it is preferably carried out at a temperature of 80 ° C. or higher and 200 ° C. or lower. Heat treatment is performed in one step or in two or more steps. The heat treatment time is determined in consideration of the heat treatment temperature from the relationship with the target reaction rate, but it is preferably 20 seconds or more and 5 minutes or less.
【００３４】さらに、本発明の繊維構造物の製造方法に
おいては、熱処理を行った後、繊維構造物に付着してい
る未反応モノマなどを除去するために洗浄を行うことが
必要である。洗浄する方法としては、水洗、湯洗など特
に限定されずに行えるが、洗浄効率などの観点から湯洗
が好ましく採用できる。Further, in the method for producing a fiber structure of the present invention, it is necessary to carry out a heat treatment and then a washing for removing unreacted monomers and the like adhering to the fiber structure. The washing method is not particularly limited and may be washing with water or washing with hot water, but washing with hot water can be preferably used from the viewpoint of washing efficiency.
【００３５】このようにして得られた繊維構造物は、従
来のセルロース繊維からなる繊維構造物より高い吸湿性
を有する。The fiber structure thus obtained has a higher hygroscopicity than the conventional fiber structure made of cellulose fibers.
【００３６】[0036]
【実施例】以下、本発明を実施例を挙げてより具体的に
説明する。なお、実施例中の各特性値は次の方法によっ
て求めた。EXAMPLES The present invention will be described more specifically below with reference to examples. Each characteristic value in the examples was determined by the following method.
【００３７】（１）吸湿性 吸湿率は、繊維構造物の絶乾重量と、温度２０℃、湿度
６５％あるいは温度３０℃、湿度９０％の雰囲気下、恒
温恒湿器中に２４時間放置した後の繊維構造物の重量と
の重量変化から、次式により求めた。(1) Hygroscopicity The hygroscopicity was determined by allowing the fiber structure to stand in a thermo-hygrostat for 24 hours in an atmosphere of absolutely dry weight and a temperature of 20 ° C. and a humidity of 65% or a temperature of 30 ° C. and a humidity of 90%. From the weight change with the weight of the subsequent fiber structure, it was determined by the following formula.
【００３８】吸湿率（％）＝１００×［（一定温度、湿
度下に放置後の繊維構造物の重量）−（繊維構造物の絶
乾重量）］／（繊維構造物の絶乾重量） 上記した式により求めた、温度２０℃、湿度６５％の条
件下での吸湿率ＭＲ１と、温度３０℃、湿度９０％の条
件下での吸湿率ＭＲ２から、次式によりΔＭＲを算出し
た。Moisture absorption rate (%) = 100 × [(weight of fiber structure after standing at constant temperature and humidity)-(absolute dry weight of fiber structure)] / (absolute dry weight of fiber structure) From the moisture absorption rate MR1 under the conditions of temperature 20 ° C. and humidity 65% and the moisture absorption rate MR2 under the conditions of temperature 30 ° C. and humidity 90%, ΔMR was calculated by the following equation.
【００３９】ΔＭＲ ＝ ＭＲ２ − ＭＲ１ （２）反応率 反応率は、親水性ビニル系モノマの重合を行う前の繊維
構造物の絶乾重量と、親水性ビニル系モノマの重合を行
った後の繊維構造物の絶乾重量から、次式により算出し
た。ΔMR = MR2-MR1 (2) Reaction rate The reaction rate is the absolute dry weight of the fiber structure before the polymerization of the hydrophilic vinyl monomer and the fiber after the polymerization of the hydrophilic vinyl monomer. It was calculated from the absolute dry weight of the structure by the following formula.
【００４０】反応率（％）＝１００×［（親水性ビニル
系モノマの重合をした後の繊維構造物の絶乾重量）−
（親水性ビニル系モノマの重合をする前の繊維構造物の
絶乾重量）］／（親水性ビニル系モノマの重合をする前
の絶乾重量） （３）快適性 直接肌に触れるようにワイシャツを着用し、官能テスト
を行った。Reaction rate (%) = 100 × [(absolute dry weight of fiber structure after polymerization of hydrophilic vinyl monomer)-
(Absolute dry weight of the fiber structure before polymerizing the hydrophilic vinyl monomer)] / (Absolute dry weight before polymerizing the hydrophilic vinyl monomer) (3) Comfort Shirt that touches the skin directly Was worn and a sensory test was conducted.
【００４１】実施例１ 綿１００％の４５番手の紡績糸を経糸および緯糸に用い
て平織物（経密度１１５本／inch、緯密度７６本／inc
h）に製織した。Example 1 A plain woven fabric (warp density of 115 yarns / inch, weft density of 76 yarns / inc) was prepared by using 45-count spun yarn of 100% cotton as warp yarns and weft yarns.
h) was woven.
【００４２】この織物１００ｇを、２００ｇの２−アク
リルアミド−２−メチルプロパンスルホン酸と６ｇの過
硫酸アンモニウムを含有する水溶液１０００ｇ（ｐＨ８
に調整）に含浸処理した後、１６０℃で３分間熱処理を
行った。熱処理後６０℃の湯で洗浄を行った。織物に対
する、モノマの反応率は１５％であった。この織物を用
いて縫製を行いワイシャツを得た。得られたワイシャツ
はΔＭＲが１４％であった。このワイシャツは着用した
ときに優れた快適性を有するものであった。100 g of this woven fabric was added to 1000 g of an aqueous solution (pH 8) containing 200 g of 2-acrylamido-2-methylpropanesulfonic acid and 6 g of ammonium persulfate.
After the impregnation, the heat treatment was performed at 160 ° C. for 3 minutes. After the heat treatment, it was washed with hot water at 60 ° C. The reaction rate of the monomer with respect to the woven fabric was 15%. Sewing was performed using this woven fabric to obtain a shirt. The obtained shirt had a ΔMR of 14%. This shirt had excellent comfort when worn.
【００４３】比較例１ ２−アクリルアミド−２−メチルプロパンスルホン酸の
代わりにメタクリル酸メチルを用いたこと以外は実施例
１と同様に行った。得られたワイシャツは、ΔＭＲが
３．２％であった。このワイシャツは着用したときに汗
がムレる感じがするものであった。Comparative Example 1 Example 1 was repeated except that methyl methacrylate was used instead of 2-acrylamido-2-methylpropanesulfonic acid. The obtained shirt had a ΔMR of 3.2%. This shirt felt sweaty when worn.
【００４４】比較例２ ２−アクリルアミド−２−メチルプロパンスルホン酸及
び過硫酸アンモニウムを用いなかったこと以外は実施例
１と同様に行った。得られたワイシャツは、ΔＭＲが
３．６％であった。このワイシャツは着用したときに、
実施例１に比べて快適性に劣るものであった。Comparative Example 2 The procedure of Example 1 was repeated except that 2-acrylamido-2-methylpropanesulfonic acid and ammonium persulfate were not used. The obtained shirt had a ΔMR of 3.6%. When I wear this shirt,
The comfort was inferior to that of Example 1.
【００４５】比較例３ ポリエステル短繊維（単繊維繊度０．１７テックス、カ
ット長４０ｍｍ）１００％の４５番手の紡績糸を用いて
平織物とした以外は実施例１と同様に行った。得られた
ワイシャツはΔＭＲが０％であった。このワイシャツは
着用したときに汗がムレる感じがするものであった。Comparative Example 3 The same procedure as in Example 1 was carried out except that a plain woven fabric was formed using 100% polyester spun yarn (single fiber fineness 0.17 tex, cut length 40 mm) of 45%. The obtained shirt had a ΔMR of 0%. This shirt felt sweaty when worn.
【００４６】[0046]
【発明の効果】本発明によれば、着用した時に優れた快
適性を奏する繊維構造物を提供できる。According to the present invention, it is possible to provide a fiber structure which exhibits excellent comfort when worn.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０６Ｍ 14/04 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location D06M 14/04
Claims (15)
おいて、該セルロース繊維に親水性ビニル系モノマが重
合されていることを特徴とする繊維構造物。1. A fiber structure comprising cellulose fibers, wherein the cellulose fibers are polymerized with a hydrophilic vinyl monomer.
物の吸湿率ＭＲ２（％）から温度２０℃、湿度６５％に
おける繊維構造物の吸湿率ＭＲ１（％）を差し引いた値
で表されるΔＭＲが、下記式を満足することを特徴とす
る請求項１記載の繊維構造物。 ４＜ΔＭＲ≦１４2. A value obtained by subtracting the moisture absorption rate MR1 (%) of the fiber structure at a temperature of 20 ° C. and a humidity of 65% from the moisture absorption rate MR2 (%) of the fiber structure at a temperature of 30 ° C. and a humidity of 90%. The fibrous structure according to claim 1, wherein ΔMR satisfies the following formula. 4 <ΔMR ≦ 14
対する反応率が１重量％以上２０重量％以下であること
を特徴とする請求項１記載の繊維構造物。3. The fiber structure according to claim 1, wherein the reaction rate of the hydrophilic vinyl-based monomer with respect to the fiber structure is 1% by weight or more and 20% by weight or less.
および／またはスルホン酸塩を含有するビニル系モノマ
であることを特徴とする請求項１記載の繊維構造物。4. The fiber structure according to claim 1, wherein the hydrophilic vinyl-based monomer is a vinyl-based monomer containing sulfonic acid and / or sulfonate.
を特徴とする請求項１記載の繊維構造物。5. The fibrous structure according to claim 1, wherein the fibrous structure is a dress shirt.
する請求項１記載の繊維構造物。6. The fiber structure according to claim 1, wherein the fiber structure is underwear.
とを特徴とする請求項１記載の繊維構造物。7. The fiber structure according to claim 1, wherein the fiber structure is sportswear.
からなることを特徴とする請求項１記載の繊維構造物。8. The fibrous structure according to claim 1, wherein the fibrous structure consists essentially of cellulose fibers.
を、親水性ビニル系モノマと重合開始剤を含有する水溶
液の含浸処理を施した後、熱処理を施し、次いで洗浄す
ることを特徴とする繊維構造物の製造方法。9. A fiber characterized in that a fibrous structure using cellulose fibers is impregnated with an aqueous solution containing a hydrophilic vinyl monomer and a polymerization initiator, then heat-treated, and then washed. Structure manufacturing method.
酸および／またはスルホン酸塩を含有するビニル系モノ
マであることを特徴とする請求項９記載の繊維構造物の
製造方法。10. The method for producing a fiber structure according to claim 9, wherein the hydrophilic vinyl-based monomer is a vinyl-based monomer containing sulfonic acid and / or sulfonate.
ることを特徴とする請求項９記載の繊維構造物の製造方
法。11. The method for producing a fiber structure according to claim 9, wherein the pH of the aqueous solution is 6 or more and 12 or less.
系モノマの濃度が１０重量％以上３０重量％以下である
ことを特徴とする請求項９記載の繊維構造物の製造方
法。12. The method for producing a fiber structure according to claim 9, wherein the concentration of the hydrophilic vinyl-based monomer in the aqueous solution is 10% by weight or more and 30% by weight or less.
ノマに対して１重量％以上５重量％以下含有しているこ
とを特徴とする請求項９記載の繊維構造物の製造方法。13. The method for producing a fiber structure according to claim 9, wherein the polymerization initiator is contained in an amount of 1% by weight or more and 5% by weight or less with respect to the hydrophilic vinyl monomer.
下であることを特徴とする請求項９記載の繊維構造物の
製造方法。14. The method for producing a fiber structure according to claim 9, wherein the heat treatment temperature is 80 ° C. or higher and 200 ° C. or lower.
維からなることを特徴とする請求項９記載の繊維構造物
の製造方法。15. The method for producing a fiber structure according to claim 9, wherein the fiber structure is substantially composed of cellulose fibers.