JPH09108328A - First-aid adhesive plaster - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a first-aid adhesive plaster which is not curled when its peeling paper is peeled off, can be easily put on a part of human skin by winding, and can be taken out of its wrapper without removing the peeling paper. SOLUTION: This first-aid adhesive plaster consists of a substrate made of polyolefin resin film, an adhesive layer put on the substrate, and a peeling paper layered on the adhesive layer to cover a gauze on the adhesive layer. The peeling paper is layered on the adhesive layer with such a peeling force that the ratio of the peeling force when the peeling paper is peeled off is A/B<=0.7, and 25<=B<=250 [A is the peeling force (gf/19mm) when the peeling paper is peeled at 180 deg. at the pulling speed of 20m/min., and B is the peeling force (gf/19mm) when the peeling paper is peeled at 180 deg. at the pulling speed of 0.5m/min].

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、基材としてポリオ
レフィン系樹脂フィルムからなるものを用いた救急絆創
膏に関し、より詳細には、剥離紙引剥し時のカールの発
生を防止した救急絆創膏に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a first-aid bandage using a polyolefin resin film as a base material, and more particularly to a first-aid bandage which prevents curling when peeling release paper.

【０００２】[0002]

【従来の技術】一般に、救急絆創膏は、軟質フィルムか
らなる基材の表面に粘着剤を塗布し、得られた粘着剤層
の上にガーゼを配してこれを覆うように剥離紙を積層
し、この層状物を所定寸法に打ち抜いてさらに表裏面に
個別包装紙を重ねると共に所定寸法に切断して作製され
る（後述の実施例１において添付図１に基づいて詳しく
説明する）。2. Description of the Related Art In general, a first-aid bandage is made by applying a pressure-sensitive adhesive to the surface of a base material made of a soft film, laying gauze on the obtained pressure-sensitive adhesive layer, and laminating release paper so as to cover it. The layered product is punched out to a predetermined size, and further, individual wrapping paper is stacked on the front and back surfaces and cut to a predetermined size (this will be described in detail in Example 1 described later with reference to FIG. 1 attached).

【０００３】従来、救急絆創膏の基材用の軟質フィルム
としては、柔軟性、伸縮性、風合いの点から、カレンダ
ー法やゾルキャスト法により作製された可塑化ポリ塩化
ビニル（以下、可塑化ＰＶＣという）を主成分とするも
のがよく使用されてきた。Conventionally, as a soft film for a base material of a first aid bandage, plasticized polyvinyl chloride (hereinafter referred to as plasticized PVC) produced by a calendering method or a sol-casting method from the viewpoints of flexibility, stretchability and texture. ) Is mainly used.

【０００４】しかしながら、上記可塑化ＰＶＣフィルム
は大量の可塑剤を含むために、可塑剤がＰＶＣフィルム
表面へブリードアウトしてフィルム基材と粘着剤層との
密着不良を引き起こしたり、フィルム基材から粘着剤層
へ可塑剤が移行し、これにより粘着剤層の粘着力が低下
したりフィルムと粘着剤層の間の接着力が低下し、絆創
膏が剥がれ易くなる。さらに、近年は環境問題も重要と
なり、ＰＶＣ廃棄物は燃焼時に塩化水素を発生させるた
め、ＰＶＣはあらゆる分野で使用を中止することが望ま
れている。However, since the plasticized PVC film contains a large amount of plasticizer, the plasticizer bleeds out to the surface of the PVC film to cause poor adhesion between the film base material and the pressure-sensitive adhesive layer, or from the film base material. The plasticizer migrates to the pressure-sensitive adhesive layer, whereby the pressure-sensitive adhesive force of the pressure-sensitive adhesive layer is reduced, the adhesive force between the film and the pressure-sensitive adhesive layer is reduced, and the adhesive bandage is easily peeled off. Further, in recent years, environmental problems have become important, and PVC wastes generate hydrogen chloride during combustion, so it is desired to stop the use of PVC in all fields.

【０００５】このため、近年、絆創膏基材用フィルムと
して軟質ＰＶＣフィルムに代わって、柔軟性、伸縮性を
有し、感温度性に優れるポリオレフィン系樹脂フィルム
を用いる研究が積極的に進められている。For this reason, in recent years, as a film for a plaster base material, a study has been actively conducted using a polyolefin-based resin film having flexibility, stretchability and excellent temperature sensitivity, instead of a soft PVC film. .

【０００６】しかし、図２に示すように、基材1 として
ポリオレフィン系樹脂フィルムを用いた絆創膏では、剥
離紙の引剥しに伴って絆創膏3 がガーゼ4 を外側にして
カール状に湾曲するという実使用上許容できない問題が
発生した。このような問題は、基材として可塑化ＰＶＣ
フィルムを用いた時には起きなかったことである。However, as shown in FIG. 2, in a bandage using a polyolefin resin film as the base material 1, the bandage 3 is curled with the gauze 4 outside as the release paper is peeled off. A problem was encountered that was unacceptable for use. Such problems are caused by plasticized PVC as a base material.
It didn't happen when I used the film.

【０００７】この点を改良するものとして、エンボス加
工を施したポリオレフィン系樹脂フィルムを基材として
用いた救急絆創膏が提案されている（実公平３−２２８
７号公報参照）。しかし、ポリオレフィン系樹脂フィル
ム基材の場合、実際にはまだ十分な湾曲防止効果が発揮
されていない。In order to improve this point, a first-aid bandage using a polyolefin-based resin film that has been embossed as a base material has been proposed (Jikkou 3-228).
No. 7). However, in the case of a polyolefin-based resin film base material, a sufficient curving prevention effect has not yet been actually exhibited.

【０００８】そこで、本発明者は、先に、上記剥離紙を
粘着剤層に、引張り速度５００ｍｍ／分での１８０度ピ
ールによる剥離力が２５ｇ／１９ｍｍ以下となるよう
に、積層してなる救急絆創膏を提案した（特願平７−１
０５９７７）。しかし、この剥離紙では、これを引剥す
時のカールは小さくなるが、剥離紙を予め少しだけめく
っておいて絆創膏を指などの貼付部位に巻付けながら貼
る場合に、剥離紙が小さな力で剥離してしまって絆創膏
が貼りにくい難点がある。また、絆創膏をラッパーから
取出すときに剥離紙が剥がれ落ちることがある等の問題
もある。Therefore, the inventor of the present invention firstly laminated the above-mentioned release paper on the adhesive layer so that the release force by 180 degree peeling at a pulling speed of 500 mm / min would be 25 g / 19 mm or less. Proposed a bandage (Japanese Patent Application 7-1
05977). However, with this release paper, the curl when peeling it off will be small, but when peeling the release paper a little beforehand and applying the adhesive bandage while winding it around the application site such as fingers, the release paper will use a small force. There is a problem that it is difficult to attach the bandage because it peels off. There is also a problem that the release paper may peel off when the adhesive bandage is taken out from the wrapper.

【０００９】[0009]

【発明が解決しようとする課題】本発明の目的は、上記
のような実情から、ポリオレフィン系樹脂フィルムから
なる基材を用いても、ＰＶＣフィルム基材使用の場合と
同様に、剥離紙引剥し時のカール発生を防止することが
できるとともに、所要貼付部位に巻付けながら容易に貼
付けることができ、ラッパーから取出すとき剥離紙が剥
がれ落ちる恐れのない救急絆創膏を提供することにあ
る。SUMMARY OF THE INVENTION In view of the above circumstances, the object of the present invention is to peel off a release paper even if a substrate made of a polyolefin resin film is used, as in the case of using a PVC film substrate. It is intended to provide a first-aid bandage that can prevent curling at the time, can be easily applied while being wound around a required application site, and that the release paper does not peel off when taken out from the wrapper.

【００１０】[0010]

【課題を解決するための手段】本発明は上記目的を達成
すべく工夫されたもので、使用する粘着剤と剥離紙の剥
離剤との組合せによって発生する剥離力を最適な範囲に
コントロールする技術に基くものである。The present invention has been devised to achieve the above object, and is a technique for controlling the peeling force generated by the combination of the pressure-sensitive adhesive used and the release agent of the release paper within an optimum range. It is based on.

【００１１】すなわち、本発明による救急絆創膏は、ポ
リオレフィン系樹脂フィルムからなる基材と、基材上に
塗工された粘着剤層と、粘着剤層の上に配されたガーゼ
を覆うように粘着剤層に積層された剥離紙とからなる救
急絆創膏において、上記剥離紙が粘着剤層に、剥離紙引
剥し時の剥離力の比Ａ／Ｂ≦０．７、かつ、２５≦Ｂ≦
２５０［ここで、Ａは引張り速度２０ｍ／分での１８０
度ピールによる剥離力（ｇｆ／１９ｍｍ）、Ｂは引張り
速度０．５ｍ／分での１８０度ピールによる剥離力（ｇ
ｆ／１９ｍｍ）である］で、積層されていることを特徴
とするものである。That is, the first-aid bandage according to the present invention comprises a base material made of a polyolefin resin film, a pressure-sensitive adhesive layer coated on the base material, and a gauze layer disposed on the pressure-sensitive adhesive layer so as to cover the base material. A first-aid adhesive bandage comprising a release paper laminated on an agent layer, wherein the release paper is used as an adhesive layer, and the release force ratio when peeling the release paper is A / B ≦ 0.7 and 25 ≦ B ≦
250 [where A is 180 at a pulling speed of 20 m / min]
Detachment force by degree peeling (gf / 19mm), B is the peeling force by 180 degree peeling at a pulling speed of 0.5m / min (g
f / 19 mm)], they are laminated.

【００１２】なお、Ａの引張速度として２０ｍ／分を採
用したのは、通常絆創膏使用の際に剥離紙を剥がす速度
が１０〜３０ｍ／分だからである。The reason why the pulling speed of A is 20 m / min is that the peeling speed of the release paper is usually 10 to 30 m / min when the adhesive plaster is used.

【００１３】[0013]

【発明の実施の形態】本発明において、上記剥離力比Ａ
／Ｂが０．７を越えるか、または、上記剥離力Ｂが２５
０ｇｆ／１９ｍｍを越えると、絆創膏使用時に粘着剤層
から剥離紙を剥がすのに大きな力を要し、これが絆創膏
のカール状の湾曲化を引き起こす恐れがある。また、上
記剥離力Ｂが２５ｇｆ／１９ｍｍ未満であると、絆創膏
を指などの貼付部位に巻付けながら貼る場合、剥離紙が
小さな力で剥離してしまって絆創膏が貼りにくく、ま
た、絆創膏をラッパーから取出すときに剥離紙が剥がれ
落ちる場合がある。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, the peeling force ratio A
/ B exceeds 0.7, or the peeling force B is 25
When it exceeds 0 gf / 19 mm, a large force is required to peel off the release paper from the pressure-sensitive adhesive layer when using the adhesive plaster, which may cause curling of the adhesive plaster. Further, when the peeling force B is less than 25 gf / 19 mm, when the adhesive bandage is applied while being wrapped around the application site such as a finger, the release paper is peeled off with a small force and the adhesive bandage is hard to be attached, and the adhesive bandage is used as a wrapper. The release paper may peel off when it is taken out from.

【００１４】特に好ましい範囲はＡ／Ｂ≦０．５で、か
つ、１００≦Ｂ≦２００（ｇｆ／１９ｍｍ）である。A particularly preferred range is A / B ≦ 0.5 and 100 ≦ B ≦ 200 (gf / 19 mm).

【００１５】本発明による救急絆創膏に用いられる剥離
紙の材質は、クラフト紙、半晒しクラフト紙，上質紙な
どの天然の繊維質シートにポリエチレン、ポリプロピレ
ンなどのポリオレフィンをコートしたもの、これにさら
にシリコーンなどの剥離剤を塗工したもの、ポリエチレ
ン、ポリプロピレンなどのポリオレフィン系樹脂シート
またはポリエチレンテレフタレート樹脂シート、もしく
はこれらにエンボス加工を施したもの、またはシリコー
ンなどの剥離剤を塗工したものなどである。The material of the release paper used in the first-aid plaster according to the present invention is a natural fiber sheet such as kraft paper, semi-bleached kraft paper or high-quality paper coated with polyolefin such as polyethylene or polypropylene, and further silicone. And the like, a polyolefin resin sheet such as polyethylene or polypropylene, or a polyethylene terephthalate resin sheet, or an embossed product of these, or a release agent such as silicone.

【００１６】上記剥離剤としては、炭素数１８以上の
長鎖アルキル基を含有するポリマー、シリコーン系ポ
リマー、パーフロロ系ポリマーなどが使用される。ア
ルキル基含有ポリマーは使い易さ、適度な剥離性、廉
価、印刷容易性などの特徴をもっており、ポリエチレン
イミンの長鎖アルキルポリマー誘導体、ポリビニルアル
コールの長鎖アルキルポリマー誘導体、長鎖アルキルア
クリレート共重合体、長鎖アルキルビニルエステル共重
合体、長鎖アルキルビニルエーテル共重合体、長鎖アル
キルアクリルアマイド共重合体などが例示される。シリ
コーン系ポリマーはテープ用途での軽剥離性に優れて
おり、フェニルメチルシロキサンとジメチルシロキサン
の共重合体などがよく使用される。特に、ガラス転移温
度（Ｔｇ）の高いものが好ましい。パーフロロ系ポリマ
ーとしては、撥水剤や耐油紙などの用途に使用されて
いるものを用いることができる。As the release agent, a polymer containing a long-chain alkyl group having 18 or more carbon atoms, a silicone-based polymer, a perfluoro-based polymer and the like are used. The alkyl group-containing polymer has features such as ease of use, moderate peelability, low cost, and easy printing. Long-chain alkyl polymer derivative of polyethyleneimine, long-chain alkyl polymer derivative of polyvinyl alcohol, long-chain alkyl acrylate copolymer , Long-chain alkyl vinyl ester copolymers, long-chain alkyl vinyl ether copolymers, long-chain alkyl acrylic amide copolymers, and the like. Silicone-based polymers have excellent light-peeling properties for tape applications, and copolymers of phenylmethylsiloxane and dimethylsiloxane are often used. Particularly, those having a high glass transition temperature (Tg) are preferable. As the perfluoro-based polymer, those used for applications such as water repellents and oil resistant papers can be used.

【００１７】剥離紙シートに剥離剤を塗工するには、グ
ラビアコーター、ナイフコーター、メイヤーバーなどを
用いる公知の方法が適用できる。A known method using a gravure coater, a knife coater, a Mayer bar or the like can be applied to apply the release agent to the release paper sheet.

【００１８】剥離力は、粘着剤種と、剥離剤種および剥
離剤量との組合せを適宜選択することによって設定され
る。The peeling force is set by appropriately selecting the combination of the pressure-sensitive adhesive type, the type of the releasing agent and the amount of the releasing agent.

【００１９】剥離紙の厚みは１００μｍ以下、好ましく
は５〜５０μｍである。The thickness of the release paper is 100 μm or less, preferably 5 to 50 μm.

【００２０】本発明による救急絆創膏において、基材フ
ィルムの材料であるポリオレフィン系樹脂は特に限定さ
れないが、エチレン、プロピレン、１−ブテン、１−ペ
ンテン、１−ヘキセン、４−メチル−１ペンテン、１−
オクテンなどのα−オレフィンの単独重合体；エチレン
−プロピレン共重合体などの上記α−オレフィン同士の
共重合体；エチレン−アクリル酸共重合体、エチレン−
アクリル酸メチル共重合体、エチレン−アクリル酸エチ
ル共重合体、エチレン−メタクリル酸共重合体、エチレ
ン−メタクリル酸メチル共重合体、エチレン−メタクリ
ル酸エチル共重合体、エチレン−プロピレン−ジエン三
元共重合体など上記α−オレフィンと他のオレフィンと
の共重合体；一つのポリオレフィン系樹脂に他のポリオ
レフィン系樹脂をブロック、ランダムブロック、ランダ
ム共重合したもの；ポリプロピレンにエチレンをアロイ
化したリアクターＴＰＯなどが例示される。In the first-aid bandage according to the present invention, the polyolefin resin as the material of the base film is not particularly limited, but ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1pentene, 1 −
Homopolymer of α-olefin such as octene; Copolymer of the above α-olefins such as ethylene-propylene copolymer; Ethylene-acrylic acid copolymer, ethylene-
Methyl acrylate copolymer, ethylene-ethyl acrylate copolymer, ethylene-methacrylic acid copolymer, ethylene-methyl methacrylate copolymer, ethylene-ethyl methacrylate copolymer, ethylene-propylene-diene ternary copolymer Copolymers of the above α-olefins and other olefins such as polymers; one polyolefin resin with another polyolefin resin blocked, random block, or random copolymer; polypropylene T-alloy reactor TPO, etc. Is exemplified.

【００２１】救急絆創膏の基材フィルムは、上記の樹脂
をＴダイ法、インフレーション法などにより所定の厚み
に押出または共押出することによって得られる。また、
各単層を押出、熱ラミネートにより積層させてもよい。The base film of the first-aid bandage can be obtained by extruding or co-extruding the above resin to a predetermined thickness by the T-die method, the inflation method or the like. Also,
Each single layer may be laminated by extrusion or heat lamination.

【００２２】救急絆創膏基材フィルムの厚みは、好まし
くは１５〜３００μｍである。１５μｍ未満の厚みで
は、絆創膏使用時の強度が不足し、３００μｍを越えた
厚みでは救急絆創膏としては柔軟性に欠け、その風合い
が好ましくない。特に実用的な厚みは５０〜８０μｍで
ある。また、このフィルムは、無色透明であっても、あ
るいは着色された透明、着色されて透明性の無いものな
どいずれでもよい。また、フィルム表面にサンドブラス
ト、絹目などのエンボス加工を施し高級感を得ることも
できる。The thickness of the first-aid bandage base film is preferably 15 to 300 μm. If the thickness is less than 15 μm, the strength at the time of using the bandage will be insufficient, and if the thickness exceeds 300 μm, the first-aid bandage will lack flexibility and its texture is not preferable. A particularly practical thickness is 50 to 80 μm. The film may be colorless and transparent, or may be colored and transparent, or colored and non-transparent. In addition, embossing such as sand blasting and silk can be applied to the film surface to obtain a high-class feeling.

【００２３】本発明に用いられる粘着剤は特に限定され
ないが、皮膚に対して粘着力を有し刺激の少ないタイプ
がよく、アクリル系粘着剤、ゴム系粘着剤、シリコーン
系粘着剤などが例示される。The pressure-sensitive adhesive used in the present invention is not particularly limited, but it is preferable that the pressure-sensitive adhesive is a type that has an adhesive force to the skin and has little irritation, and examples thereof include an acrylic pressure-sensitive adhesive, a rubber pressure-sensitive adhesive, and a silicone-based pressure-sensitive adhesive. It

【００２４】アクリル系粘着剤としては、特に、アルキ
ル基の炭素数２〜１８の（メタ）アクリル酸アルキルエ
ステルの単独重合体または共重合体、あるいは上記（メ
タ）アクリル酸アルキルエステルとその他の官能性モノ
マーとの共重合体が好適に用いられる。As the acrylic pressure-sensitive adhesive, in particular, a homopolymer or copolymer of a (meth) acrylic acid alkyl ester having an alkyl group having 2 to 18 carbon atoms, or the above-mentioned (meth) acrylic acid alkyl ester and other functional groups. A copolymer with a polymerizable monomer is preferably used.

【００２５】アクリル系粘着剤には、必要に応じてロジ
ン系樹脂、ポリテルペン樹脂などの粘着性付与剤を添加
したり、また、凝集力確保のために、必要に応じて架橋
剤を配合する。A tackifier such as a rosin resin or a polyterpene resin is added to the acrylic pressure-sensitive adhesive as necessary, and a cross-linking agent is added as necessary to secure cohesive force.

【００２６】ゴム系粘着剤としては、天然ゴム、スチレ
ン−イソプレン系ブロック共重合体、スチレン−ブタジ
エン系ブロック共重合体、ポリイソプレン、ポリブテ
ン、ポリイソブチレン、エチレン−酢酸ビニル共重合体
などのゴム弾性体１００重量部に対し、たとえばロジン
系樹脂、ポリテルペン系樹脂などの粘着性付与剤を２０
〜２００重量部、および必要に応じて、液状ポリブテ
ン、鉱油、ラノリン、液状ポリイソプレン、液状ポリア
クリレートなどの軟化剤：酸化チタンなどの充填剤：ブ
チルヒドロキシトルエンなどの老化防止剤などを適量添
加してなるものが使用される。As the rubber-based adhesive, rubber elasticity such as natural rubber, styrene-isoprene block copolymer, styrene-butadiene block copolymer, polyisoprene, polybutene, polyisobutylene, ethylene-vinyl acetate copolymer, etc. 20 parts of tackifier such as rosin resin or polyterpene resin is added to 100 parts by weight of the body.
~ 200 parts by weight, and if necessary, liquid polybutene, mineral oil, lanolin, liquid polyisoprene, liquid polyacrylate and other softening agents: titanium oxide and other fillers: butylhydroxytoluene and other anti-aging agents, etc. Is used.

【００２７】スチレン−イソプレン系ブロック共重合体
およびスチレン−ブタジエン系ブロック共重合体として
は、スチレン−イソプレン・ブロック共重合体、スチレ
ン−イソプレン−スチレン・ブロック共重合体、スチレ
ン−ブタジエン・ブロック共重合体、スチレン−ブタジ
エン−スチレン・ブロック共重合体、スチレン−エチレ
ン−ブチレン−スチレン・ブロック共重合体などのスチ
レン系熱可塑性エラストマーが例示される。The styrene-isoprene block copolymer and the styrene-butadiene block copolymer include styrene-isoprene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene block copolymer. Examples thereof include styrene-based thermoplastic elastomers such as polymer, styrene-butadiene-styrene / block copolymer, and styrene-ethylene-butylene-styrene / block copolymer.

【００２８】粘着性付与剤の添加量がゴム弾性体１００
重量部に対し２０重量部未満であると、粘着剤の内部凝
縮力が大きく粘着力が不足し、逆に２００重量部を越え
ると、粘着剤の内部凝縮力が小さく粘着剤が凝集破壊を
起こす。The amount of the tackifier added is 100% rubber elastic body.
When the amount is less than 20 parts by weight, the internal condensation force of the adhesive is large and the adhesive force is insufficient, and when it exceeds 200 parts by weight, the internal condensation force of the adhesive is small and the adhesive causes cohesive failure. .

【００２９】シリコーン系粘着剤としては、ポリジメチ
ルシロキサンなどを主成分とするものが使用される。As the silicone-based pressure-sensitive adhesive, one having polydimethylsiloxane as a main component is used.

【００３０】上記各粘着剤中には、可塑剤；充填剤；老
化防止剤などの配合剤が必要に応じて添加される。Compounding agents such as a plasticizer, a filler, and an antioxidant are added to each of the above-mentioned pressure-sensitive adhesives, if necessary.

【００３１】粘着剤層の上にはガーゼを貼着してこれを
覆う剥離紙を積層し、使用時までその粘着剤層表面を保
護する。Gauze is adhered on the pressure-sensitive adhesive layer, and a release paper covering it is laminated to protect the surface of the pressure-sensitive adhesive layer until use.

【００３２】つぎに、救急絆創膏の製造方法を説明す
る。救急絆創膏基材フィルムにおいて、粘着剤を塗布す
べき面に粘着剤塗工時の表面濡れ性が３８ｄｙｎ／ｃｍ
以上になるような条件で、コロナ放電処理を施すかまた
はアンカーコート処理を施す。その後、粘着剤の溶液な
いしは懸濁液を剥離紙に塗布して乾燥させ、得られた粘
着剤層付き剥離紙の粘着剤層に上記フィルム処理面を重
ね合わせ状に密着させる。または、上記フィルム処理面
に粘着剤層を直接形成し、その上に剥離紙を積層する。Next, a method for manufacturing the first aid bandage will be described. In the first-aid bandage base film, the surface to which the adhesive is applied has a surface wettability of 38 dyn / cm when the adhesive is applied.
Under the conditions as described above, the corona discharge treatment or the anchor coat treatment is performed. Then, the solution or suspension of the pressure-sensitive adhesive is applied to the release paper and dried, and the above-mentioned film-treated surface is superposedly adhered to the pressure-sensitive adhesive layer of the release paper with the pressure-sensitive adhesive layer obtained. Alternatively, a pressure-sensitive adhesive layer is directly formed on the film-treated surface, and release paper is laminated thereon.

【００３３】こうして得られた絆創膏用原反に使用サイ
ズにスリットを入れた後、絆創膏製造機により熱ピン穿
孔加工し、粘着剤層の上にガーゼ、剥離紙を配し、上記
原反を所定寸法に打抜き、表裏面に個別包装紙を重ね
て、製品としての救急絆創膏を得る。After slitting the used size in the bandage for plasters thus obtained, punching with hot pins by a plaster making machine, placing gauze and release paper on the adhesive layer, and predetermining the above-mentioned rolls. It is punched to the size, and individual wrapping paper is placed on the front and back sides to obtain a first-aid bandage as a product.

【００３４】本発明によれば、剥離紙は所定剥離力で粘
着剤層に積層されているので、ポリオレフィン系樹脂フ
ィルムからなる基材を用いても、ＰＶＣフィルム基材使
用の場合と同様に、剥離紙引剥し時のカールの発生防止
することができるとともに、絆創膏を指などの所要貼付
部位に巻付けながら容易に貼付けることができ、加えて
絆創膏をラッパーから取出すとき剥離紙が剥がれ落ちる
恐れがない。According to the present invention, since the release paper is laminated on the pressure-sensitive adhesive layer with a predetermined release force, even if a base material made of a polyolefin resin film is used, as in the case of using a PVC film base material, Curling can be prevented when peeling off the release paper, and the adhesive bandage can be easily applied while wrapping it around the required application site such as fingers. In addition, the release paper may peel off when removing the adhesive bandage from the wrapper. There is no.

【００３５】また、実用温度域での力学物性の変化が小
さく、低温でも柔軟性を有する救急絆創膏が得られる。Further, the first-aid adhesive bandage having a small change in mechanical properties in a practical temperature range and having flexibility even at a low temperature can be obtained.

【００３６】さらに、基材はポリオレフィン系樹脂フィ
ルムからなるので、絆創膏を焼却しても塩化水素などの
有毒ガスが発生する恐れがない。Furthermore, since the base material is made of a polyolefin resin film, there is no fear that toxic gas such as hydrogen chloride will be generated even if the bandage is incinerated.

【００３７】[0037]

【実施例】以下、本発明を実施例によりさらに具体的に
説明する。EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples.

【００３８】実施例１ Ｔダイ押出成膜により、エチレン・１−ブテン共重合体
（住友化学社製「エクセレンＶＬ８００』、密度０．９
０５ｇ／ｃｍ³ ）から、厚み６５μｍのフィルムを形成
し、これを絆創膏用基材フィルムとした。ついで、粘着
剤を塗布すべき面に粘着剤塗工時の表面濡れ性が３８ｄ
ｙｎ／ｃｍ以上になるような条件で、コロナ放電処理を
施した。Example 1 An ethylene / 1-butene copolymer (“Excellen VL800” manufactured by Sumitomo Chemical Co., Ltd., density 0.9) was obtained by T-die extrusion film formation.
A film having a thickness of 65 μm was formed from 05 g / cm ³ ) and used as a base film for adhesive plasters. Then, the surface wettability at the time of coating the adhesive on the surface to be coated with the adhesive is 38d.
The corona discharge treatment was performed under the condition of yn / cm or more.

【００３９】アクリル系粘着剤（綜研化学社製「ＳＫダ
イン１７２０」）にイソシアネート系硬化剤を固形分重
量比１００：１．２で混合し、この混合物を乾燥厚みが
４０μｍになるように上記基材フィルムの上記処理面に
塗工し、塗工層を乾燥して粘着剤層を形成した。An acrylic adhesive (“SKDyne 1720” manufactured by Soken Chemical Industry Co., Ltd.) was mixed with an isocyanate curing agent at a solid content weight ratio of 100: 1.2, and the mixture was mixed so that the dry thickness was 40 μm. The pressure-sensitive adhesive layer was formed by coating the above treated surface of the material film and drying the coating layer.

【００４０】こうして得られた絆創膏用原反から救急絆
創膏を製造する際に、上記粘着剤層の上に剥離紙を積層
した。剥離紙としては、厚さ１００μｍの半晒しクラフ
ト紙にポリエチレンを１５μｍ厚でコートし、その上に
剥離剤ａを固形分０．５ｇ／ｍ² で塗工した。剥離剤ａ
としては、ポリエチレンイミンの１級、２級アミノ基の
活性水素に長鎖アルキルイソシアネートを付加反応させ
て得られたものであって、炭素数１８以上の長鎖アルキ
ル基を含有するポリマー（日本触媒化学社製ＲＰ−２
０）を用いた。When producing a first-aid bandage from the thus obtained raw material bandage, a release paper was laminated on the pressure-sensitive adhesive layer. As the release paper, polyethylene having a thickness of 15 μm was coated on a semi-bleached kraft paper having a thickness of 100 μm, and the release agent a was coated thereon at a solid content of 0.5 g / m ² . Release agent a
Is a polymer obtained by addition-reacting a long-chain alkyl isocyanate with the active hydrogen of the primary or secondary amino group of polyethyleneimine and containing a long-chain alkyl group having 18 or more carbon atoms (Nippon Catalyst Chemical company RP-2
0) was used.

【００４１】こうして得られた救急絆創膏の構成を図１
に示す。図１中、1 はポリオレフィン系樹脂フィルムか
らなる基材、2 は剥離紙、3 は粘着剤層、4 はガーゼで
ある。FIG. 1 shows the structure of the first-aid bandage thus obtained.
Shown in In FIG. 1, 1 is a base material made of a polyolefin resin film, 2 is release paper, 3 is an adhesive layer, and 4 is gauze.

【００４２】実施例２ 剥離紙として、上質紙にポリエチレンをコートしたもの
を用い、剥離剤ｂとして、ポリビニルアルコールのヒド
ロキシル基の活性水素に長鎖アルキルイソシアネートを
付加反応させて得られたものであって、炭素数１８以上
の長鎖アルキル基を含有するポリマー（一方社油脂社製
ピーロール１０１０Ｓ）を用いた点以外は実施例１と同
様に操作を行い、救急絆創膏を作製した。Example 2 As release paper, high-quality paper coated with polyethylene was used, and as release agent b, it was obtained by addition-reacting a long-chain alkyl isocyanate with active hydrogen of the hydroxyl group of polyvinyl alcohol. Then, the same procedure as in Example 1 was performed except that a polymer containing a long-chain alkyl group having 18 or more carbon atoms (Peelol 1010S manufactured by Yushisha Co., Ltd.) was used to prepare a first-aid bandage.

【００４３】比較例１ 剥離紙として、クラフト紙にポリエチレンをコートした
ものを用い、剥離剤ｃとして、シリコーン系ポリマー
（信越化学社製ＫＳ−７７２Ｆ）を用い、これを剥離紙
に固形分０．９ｇ／ｍ² で塗工した点以外は実施例１と
同様に操作を行い、救急絆創膏を作製した。Comparative Example 1 Kraft paper coated with polyethylene was used as the release paper, and a silicone polymer (KS-772F manufactured by Shin-Etsu Chemical Co., Ltd.) was used as the release agent c. The same operation as in Example 1 was carried out except that the coating was performed at 9 g / m ² , to prepare an emergency bandage.

【００４４】比較例２ 剥離紙として、クラフト紙にポリエチレンをコートした
ものを用い、剥離剤ｄとして、シリコーン系ポリマー
（信越化学社製ＫＳ−７０５Ｆ）を用い、これを剥離紙
に固形分０．８ｇ／ｍ² で塗工した点以外は実施例１と
同様に操作を行い、救急絆創膏を作製した。Comparative Example 2 Kraft paper coated with polyethylene was used as the release paper, and a silicone polymer (KS-705F manufactured by Shin-Etsu Chemical Co., Ltd.) was used as the release agent d. A first-aid bandage was prepared in the same manner as in Example 1 except that the coating was carried out at 8 g / m ² .

【００４５】（剥離力測定方法）ステンレス板の片面に
両面テープを貼り、絆創膏用原反を１９ｍｍ幅に裁断し
て得られた試験片の剥離紙側を両面テープ面の上面に貼
る。試験片の基材を引張ることができるように基材端部
を少しめくり上げておく。(Peeling force measuring method) A double-sided tape was attached to one surface of a stainless steel plate, and a test piece obtained by cutting the adhesive plaster raw material into a width of 19 mm was attached to the upper surface of the double-sided tape surface. The base material edge is slightly turned up so that the base material of the test piece can be pulled.

【００４６】この試験片の基材を、オリエンテック社製
の試験機「テンシロンＵＣＴ−５００」を用いて、引張
速度０．５ｍ／分で１８０度ピールした。The base material of this test piece was peeled 180 degrees at a pulling speed of 0.5 m / min using a tester "Tensilon UCT-500" manufactured by Orientec.

【００４７】また、試験機としてテスター産業社製の高
速軽量剥離試験機を用いて、引張速度２０ｍ／分で、上
記と同様にこの試験片の基材を１８０度ピールした。A high-speed lightweight peeling tester manufactured by Tester Sangyo Co., Ltd. was used as a tester, and the base material of this test piece was peeled by 180 degrees at a tensile speed of 20 m / min in the same manner as above.

【００４８】（評価１）実施例および比較例で得られた
救急絆創膏をラッパーに入れて包装形態にしたあと、絆
創膏をラッパーから取出すときに剥離紙が粘着剤層から
剥がれ易いものを△、剥がれないものを○とする。(Evaluation 1) After the first-aid bandages obtained in Examples and Comparative Examples were put in a wrapper to form a packaging form, when the adhesive bandage was taken out from the wrapper, the release paper was easily peeled from the adhesive layer. Those that do not exist are marked with a circle.

【００４９】（評価２）実施例および比較例で得られた
救急絆創膏について、剥離紙を予め少しだけめくってお
いて絆創膏を指に巻き付けながら貼付ける場合に、剥離
に要する力が小さすぎて剥離紙が剥がれてしまい絆創膏
が貼り難いものを△、貼り易いものを○とした。(Evaluation 2) The first-aid bandages obtained in Examples and Comparative Examples were peeled off because the force required for peeling was too small when the release paper was slightly flipped over in advance and the bandages were wrapped around the fingers and attached. The case where the paper was peeled off and the adhesive bandage was difficult to be applied was indicated by Δ, and the case where it was easily adhered was indicated by ○.

【００５０】（評価３）実施例および比較例で得られた
救急絆創膏について、剥離紙を指で引剥し、表２に示す
評価基準に従ってカールの程度を評価した。(Evaluation 3) With respect to the first-aid bandages obtained in Examples and Comparative Examples, the release paper was peeled off with a finger, and the degree of curling was evaluated according to the evaluation criteria shown in Table 2.

【００５１】この結果を表１にまとめて示す。The results are summarized in Table 1.

【００５２】[0052]

【表１】 [Table 1]

【表２】 表１から明らかなように、実施例の救急絆創膏は全ての
評価項目において良好な結果を示した。[Table 2] As is clear from Table 1, the first-aid bandages of Examples showed good results in all evaluation items.

【００５３】[0053]

【発明の効果】本発明により、ポリオレフィン系樹脂フ
ィルムからなる基材を用いても、ＰＶＣフィルム基材使
用の場合と同様に、剥離紙引剥し時のカールの発生防止
することができるとともに、絆創膏を指などの所要貼付
部位に巻付けながら容易に貼付けることができ、加えて
絆創膏をラッパーから取出すとき剥離紙が剥がれ落ちる
恐れのない救急絆創膏を得ることができる。EFFECTS OF THE INVENTION According to the present invention, even when a substrate made of a polyolefin resin film is used, curling can be prevented at the time of peeling off the release paper, as in the case of using a PVC film substrate, and a bandage can be used. It can be easily applied while being wrapped around a required application site such as a finger, and in addition, it is possible to obtain an emergency adhesive bandage in which the release paper does not peel off when the adhesive bandage is taken out from the wrapper.

【００５４】また、実用温度域での力学物性の変化が小
さく、低温でも柔軟性を有する救急絆創膏が得られる。Further, the first-aid bandage has a small change in mechanical properties in a practical temperature range and is flexible even at a low temperature.

【００５５】さらに、基材はポリオレフィン系樹脂フィ
ルムからなるので、救急絆創膏を焼却しても塩化水素な
どの有毒ガスが発生する恐れがない。Furthermore, since the base material is made of a polyolefin resin film, there is no fear that toxic gas such as hydrogen chloride will be generated even if the first aid plaster is incinerated.

【図面の簡単な説明】[Brief description of the drawings]

【図１】 実施例１による救急絆創膏の構成を示す垂直
縦断面図である。FIG. 1 is a vertical longitudinal sectional view showing a configuration of an emergency bandage according to Example 1.

【図２】 従来の救急絆創膏のカール発生状態を示す垂
直縦断面図である。FIG. 2 is a vertical vertical cross-sectional view showing a curl occurrence state of a conventional first-aid bandage.

【符号の説明】[Explanation of symbols]

1 …基材 2 …剥離紙 3 …粘着剤層 4 …ガーゼ 1 ... Substrate 2 ... Release paper 3 ... Adhesive layer 4 ... Gauze

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 ポリオレフィン系樹脂フィルムからなる
基材と、基材上に塗工された粘着剤層と、粘着剤層の上
に配されたガーゼを覆うように粘着剤層に積層された剥
離紙とからなる救急絆創膏において、上記剥離紙が粘着
剤層に、剥離紙引剥し時の剥離力の比Ａ／Ｂ≦０．７、
かつ、２５≦Ｂ≦２５０［ここで、Ａは引張り速度２０
ｍ／分での１８０度ピールによる剥離力（ｇｆ／１９ｍ
ｍ）、Ｂは引張り速度０．５ｍ／分での１８０度ピール
による剥離力（ｇｆ／１９ｍｍ）である］で、積層され
ていることを特徴とする救急絆創膏。1. A peeling laminated on a pressure-sensitive adhesive layer so as to cover a base material made of a polyolefin resin film, a pressure-sensitive adhesive layer coated on the base material, and gauze arranged on the pressure-sensitive adhesive layer. In a first-aid bandage consisting of paper, the release paper is used as an adhesive layer, and the peel force ratio A / B ≦ 0.7 when the release paper is peeled off,
And 25 ≦ B ≦ 250 [where A is the pulling speed of 20
Peel force by 180 degree peeling at m / min (gf / 19m
m) and B are peeling forces (gf / 19 mm) by 180 degree peeling at a pulling speed of 0.5 m / min], and the first-aid bandage is characterized by being laminated.