JPH0853106A - Packing method for cementitious plate material, and package made up therewith - Google Patents

Abstract

PURPOSE:To simply materialize automatization of packing work with penetration of water prevented by a method wherein the packing work is composed of three processes of wrapping round with films, wrapping round with sheets and wrapping round with films. CONSTITUTION:The packing work is composed of a first process wherein the lateral 12b and the end on the upper side 12a of a piled-up body 12 are wrapped with films 7, a second process wherein the upper side 12a and the lateral 12b of the piled-up body 12 wrapped round in the first process are wrapped with sheets 8, and a third process wherein the lateral 12b and the upper side 12a of the piled-up body 12 wrapped round in the second process are wrapped with films 9.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、平瓦のようなセメント
系板材の梱包方法及びその梱包体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of packing a cement board material such as a flat roof tile and a packing body for the same.

【０００２】[0002]

【従来の技術】従来、平瓦のようなセメント系板材の梱
包方法としては、本発明者は、特願平６−４２６号明細
書に記載のように、無機成形体を小単位に梱包した積重
ね体を傾斜したパレット上に垂直に積載し、この積重ね
体が積載されたパレット全体をフィルムで包装する無機
成形体の梱包方法を発明している。2. Description of the Related Art Conventionally, as a method of packing a cement board material such as a flat roof tile, the present inventor packed an inorganic molded body into small units as described in Japanese Patent Application No. 6-426. The inventor has invented a method for packing an inorganic molded body in which a stack is vertically stacked on an inclined pallet and the entire pallet on which the stack is stacked is wrapped with a film.

【０００３】又、複数枚の平板瓦の凹凸を揃えて梱包し
て瓦積重ね体とし、パレット上に上記瓦積重ね体の凹凸
を噛み合わせるように上下方向に積載し、上段の瓦積重
ね体の裏表を反転させて積載する瓦積重ね体のパレット
への積載方法が、特開平４−２２３９３２号公報に記載
されている。一方、セメント瓦においては、袋掛けによ
る梱包を実施している例もある。Further, a plurality of flat roof tiles are aligned and packed to form a roof tile stack, and the roof tiles are stacked vertically on the pallet so that the recesses and protrusions of the roof tile stack are engaged with each other. JP-A-4-223932 describes a method of loading a tile stack on a pallet by inverting and stacking. On the other hand, in some cases, cement tiles are packed by bags.

【０００４】[0004]

【発明が解決しようとする課題】しかしながら、上記の
特願平６−４２６号明細書に記載されているパレット全
体をフィルムで包装する梱包方法においては、荷崩れに
対しては配慮されているが、防水に対しては考慮された
梱包ではなく、又、後者の特開平４−２２３９３２号公
報に記載されている積載方法においては、防水に関して
全く無防備であり、風雨に曝される積重ね体の上面から
は積重ね体内に水が侵入し、セメント瓦ではエフロレッ
センスの発生により瓦の表面が白濁するといった問題が
ある。However, in the packing method for packing the entire pallet with a film described in the above-mentioned Japanese Patent Application No. 6-426, the collapse of the load is taken into consideration. However, the packing is not considered for waterproofing, and in the latter loading method described in Japanese Patent Laid-Open No. 4-223932, there is no protection against waterproofing and the upper surface of the stack exposed to wind and rain. There is a problem that water invades into the stack and the cement roof tile becomes turbid due to the occurrence of efflorescence.

【０００５】又、袋掛けの場合には、水の侵入は防止で
きるが、梱包工程の自動化が困難であり工数が多く掛か
って人手を要し、生産性が悪いといった問題が残されて
いる。Further, in the case of bagging, invasion of water can be prevented, but automation of the packaging process is difficult, a lot of man-hours are required, manpower is required, and productivity is low.

【０００６】本発明は、上記のこのような問題点に着眼
してなされたものであり、その目的とするところは、こ
れらの問題点を解消し、水の侵入が防止され、梱包工程
の自動化が簡単に行えるセメント系板材の梱包方法とそ
の梱包体を提供するものてある。The present invention has been made in view of the above problems, and an object thereof is to solve these problems, prevent water from entering, and automate the packaging process. The present invention provides a method of packing a cement board and a packing body that can easily perform the above.

【０００７】[0007]

【課題を解決するための手段】請求項１記載の本発明の
セメント系板材の梱包方法においては、パレット上に積
載されたセメント系板材の積重ね体の梱包方法であっ
て、積載された積重ね体の側面と上面端部をフィルムに
より巻回されて梱包する第一工程と、この第一工程で梱
包された積重ね体の上面と側面上端部をシート掛けによ
り梱包する第二工程と、更に第二工程で梱包された積重
ね体の側面と上面端部をフィルムにより巻回されて梱包
する第三工程よりなることを特徴とする。A packing method for cement-based board materials according to the present invention is a packing method for stacking cement-based board materials stacked on a pallet, wherein the stacked stacks are stacked. The first step of packing the side surface and the upper end of the sheet by winding with a film, the second step of packing the upper surface and the upper end of the side surface of the stacked body packaged in the first step with a sheet, and the second step. It is characterized in that it comprises a third step of winding and packing the side surface and the upper end portion of the stacked body packed in the step by a film.

【０００８】又、請求項２記載の本発明の梱包体におい
ては、パレット上にセメント系板材の積重ねられ、セメ
ント系板材積重ね体の側面と上面端部とがフィルムによ
り巻回され、更に積重ね体の上面と側面上端部とがシー
ト掛けされ、更に積重ね体の側面と上面端部とがフィル
ムにより巻回されていることを特徴とする。Further, in the package of the present invention as set forth in claim 2, the cement-based plate materials are stacked on the pallet, the side surface and the upper end of the cement-based plate material stack are wound with a film, and the stacked body is further formed. The upper surface and the upper end of the side surface of the stack are covered with a sheet, and the side surface and the upper end of the stack are wound with a film.

【０００９】上記本発明の梱包方法においては、防水性
能を高めるために、第一工程のフィルムによる梱包は、
積重ね体の上面端部、即ち上面を上方角部より内側に向
かって５ｃｍ以上入った位置まで側面と一体に覆うこと
が好ましい。In the packing method of the present invention, in order to enhance the waterproof performance, the packing with the film in the first step is
It is preferable that the upper surface end portion of the stack, that is, the upper surface is integrally covered with the side surface up to a position 5 cm or more inward from the upper corner portion.

【００１０】第二工程のシート掛けによる梱包は、側面
上端部、即ち上方角部より側面下方に向かって５ｃｍ以
上の位置まで上面と一体に覆うことが好ましく、更に第
三工程のフィルムによる梱包は、積重ね体の上面端部、
即ち上面を上方角部より内側に向かって５ｃｍ以上入っ
た位置まで側面と一体に覆うことが好ましい。In the second step, the sheet-wrapping package is preferably integrally covered with the upper surface at the upper end of the side surface, that is, at a position 5 cm or more downward from the upper corner portion toward the lower side surface. , The top edge of the stack,
That is, it is preferable to integrally cover the upper surface with the side surface up to a position 5 cm or more inward from the upper corner.

【００１１】積重ね体の梱包に用いられるフィルムは、
熱可塑性樹脂製であり、延伸性と粘着性を有し、重量物
の梱包に適するストレッチフィルムが好適に用いられ
る。又、シートは、防水性を有するポリ塩化ビニル製シ
ートやエアクッションシートが好適に用いられる。The film used for packaging the stack is
A stretch film, which is made of a thermoplastic resin, has stretchability and adhesiveness, and is suitable for packing heavy goods, is preferably used. As the seat, a waterproof polyvinyl chloride seat or an air cushion seat is preferably used.

【００１２】[0012]

【作用】上記本発明のセメント系板材の梱包方法及びそ
の梱包体においては、積載された積重ね体の側面と上面
端部がフィルムにより梱包され、次いで上面と側面上端
部がシート掛けにより梱包され、更に側面と上面端部が
フィルムにより梱包されることにより、防水性能が高く
なり、積重ね体内への水の侵入がなく、エフロレッセン
スの発生により瓦の表面が白濁するといった汚れが防止
される。又、梱包方法がフィルムの巻付けによる梱包
と、シート掛けによる梱包であるから、梱包工程の自動
化が容易に実施でき生産性が向上する。In the method of packing a cement board according to the present invention and the packed body thereof, the side surface and the upper end of the stacked stack are packed with a film, and then the upper surface and the upper end of the side surface are packed with a sheet, Further, by packing the side surface and the upper end portion with a film, the waterproof performance is improved, water does not enter the stack, and the roof surface of the roof tile is prevented from becoming clouded due to the occurrence of efflorescence. Further, since the packing method is the packing by winding the film and the packing by the sheet hanging, automation of the packing process can be easily carried out and the productivity is improved.

【００１３】[0013]

【実施例】以下、本発明の実施例を図面を参照して説明
する。図１は、本発明のセメント系板材の梱包方法の一
例を示すフロー図である。図１において、１は成形、塗
装を終えて完成品となったセメント系板材よりなる瓦で
あり、この瓦１は載置台２より内結束工程１０の段積み
装置３に移動され、ここで４枚が一組となって段積みさ
れ、隣接する次の結束機４に移されて、図２の瓦の結束
体の斜視図において示すように、ＰＰバンド１ａにより
結束された瓦の結束体１１となされる。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a flow chart showing an example of a method for packing a cement board material according to the present invention. In FIG. 1, reference numeral 1 is a roof tile made of a cement-based board material that has been molded and painted to be a finished product. The roof tile 1 is moved from a mounting table 2 to a stacking device 3 in an inner bundling step 10, where 4 The sheets are stacked in a set and transferred to the next binding machine 4 adjacent thereto, and as shown in the perspective view of the roof tile binding body of FIG. 2, the roof tile binding body 11 bound by the PP band 1a. Is made.

【００１４】続いて、図３の瓦の積重ね体の斜視図にお
いて示すように、瓦の結束体１１は９組が並列に並べら
れて梱包の単位となされ、ＰＰバンド１ｂにより結束さ
れて瓦の積重ね体１２となされる。Next, as shown in the perspective view of the stack of roof tiles in FIG. 3, nine sets of roof tile bundles 11 are arranged in parallel to form a packing unit, which is bundled by the PP band 1b. The stack 12 is formed.

【００１５】この瓦の積重ね体１２は、隣接するパレッ
ト積みロボット５により、図１の矢視で示すように次の
工程である積載工程２０に移されてパレット６上に積載
される。続いて、次のフィルム包装工程３０において、
以下に詳述するようにフィルム、及びシートによる梱包
が実施される。The stack 12 of the roof tiles is transferred by the adjacent pallet stacking robot 5 to the next stacking step 20 as shown by the arrow in FIG. Then, in the next film packaging step 30,
As described in detail below, film and sheet packaging is performed.

【００１６】図４は、本発明のセメント系板材の梱包体
の一例を示す部分断面図である。図４において、先ずス
トレッチフィルム７（３００パーセント延伸タイプ）を
用いて、瓦の積重ね体１２の側面１２ｂのパレット６を
含む四方全面と、上面端部、即ち上面１２ａの角よりほ
ぼ１０ｃｍ内側に入った位置までを覆うようにして１０
回転の自動巻き付けを行って梱包した。FIG. 4 is a partial cross-sectional view showing an example of the package of the cement board material of the present invention. In FIG. 4, first, a stretch film 7 (300% stretch type) is used to enter the entire four sides including the pallet 6 on the side surface 12b of the stack 12 of roof tiles and the upper end, that is, approximately 10 cm inside from the corner of the upper surface 12a. 10 to cover up to
It was packaged by automatic rotation.

【００１７】続いて、上記ストレッチフィルム７による
梱包の上より、シート掛けによる梱包として４ｍｍ厚さ
のエアクッションシート８を用い、瓦の積重ね体１２の
側面上端部、即ち側面１２ｂの上端より下方にほぼ１０
ｃｍ垂下がるようにして、上面１２ａ全面と側面１２ｂ
の上部をシート掛けによる梱包を行った。Next, an air cushion sheet 8 having a thickness of 4 mm is used for packing by stretching the sheet by using the stretch film 7 above the side of the stack 12 of roof tiles, that is, below the upper end of the side 12b. Almost 10
cm so that the entire upper surface 12a and side surfaces 12b
The upper part of the was packed with a sheet.

【００１８】更に、上記エアクッションシート８による
シート掛け梱包の上より、ストレッチフィルム９（３０
０パーセント延伸タイプ）を用いて、瓦の積重ね体１２
の側面１２ｂのパレット６を含む四方全面と、上面端
部、即ち上面１２ａの角よりほぼ１０ｃｍ内側に入った
位置までを覆うようにして１０回転の自動巻き付けを行
って梱包を行った。以上により瓦の積重ね体１２の梱包
が完成され梱包体を得ることができる。Further, the stretch film 9 (30
Stack of tiles 12 using 0% stretch type)
The entire side surface 12b including the pallet 6 and all of the four sides including the pallet 6 and the end portion of the upper surface, that is, a position approximately 10 cm inside the corner of the upper surface 12a are covered by automatic winding of 10 rotations for packaging. As described above, the stacking of the stack 12 of roof tiles is completed and the packed body can be obtained.

【００１９】上記のストレッチフィルム７、９には、厚
さ２５μｍ、幅５００ｍｍを用い、エアクッション８
は、長さ９２０ｍｍ、幅７２０ｍｍで厚さ４ｍｍのもの
を用いた。尚、本実施例に用いられた瓦１は、セメント
系の平瓦であり、寸法縦６４０×横４２０×厚さ２０ｍ
ｍ、重量５ｋｇである。As the stretch films 7 and 9 described above, a thickness of 25 μm and a width of 500 mm are used, and the air cushion 8 is used.
Used a product having a length of 920 mm, a width of 720 mm and a thickness of 4 mm. The roof tile 1 used in this example is a cement-based flat roof tile, and has dimensions of 640 vertical × 420 horizontal × 20 m thick.
m, weight 5 kg.

【００２０】〔比較例〕上記実施例と全く同様の積重ね
体１２を用い、パレット６上に積載した上、フィルム包
装工程３０において、以下に詳述するようにフィルム、
及びシートによる梱包を行った。[Comparative Example] A stack 12 exactly the same as that in the above-mentioned example was used, and the stack 12 was stacked on the pallet 6 and, in the film packaging step 30, a film as described in detail below,
And the packaging by the sheet was done.

【００２１】図５は、従来のセメント系板材の梱包体を
示す部分断面図であり、図５において、エアクッション
シート８ａを用い、瓦の積重ね体１２の側面上端部、即
ち側面１２ｂの上端より下方にほぼ１０ｃｍ垂下がるよ
うにして、上面１２ａ全面と側面１２ｂの上部をシート
掛けによる梱包を行い、この梱包の上よりストレッチフ
ィルム９（３００パーセント延伸タイプ）を用いて、瓦
の積重ね体１２の側面１２ｂのパレット６を含む四方全
面と、上面端部、即ち上面１２ａの角よりほぼ１０ｃｍ
内側に入った位置までを覆うようにして２０回転の自動
巻き付けを行って梱包を行った。FIG. 5 is a partial cross-sectional view showing a conventional cement-based board material packaging body. In FIG. 5, an air cushion sheet 8a is used, and the side surface upper end portion of the roof tile stack 12, that is, the upper side surface 12b. The entire upper surface 12a and the upper portions of the side surfaces 12b are wrapped by sheets so that they hang downward by about 10 cm, and a stretch film 9 (300% stretch type) is used on the packaging to stack the roof tiles 12 together. About 10 cm from the four sides of the side surface 12b including the pallet 6 and the edge of the upper surface, that is, the corner of the upper surface 12a
The product was packaged by automatically winding it 20 times so as to cover the inside position.

【００２２】尚、上記比較例において用いたエアクッシ
ョンシート８ａ、及びストレッチフィルム９ａは、上記
実施例と全く同様のものを用いた。又、用いた瓦１も実
施例と同様のものとした。The air cushion sheet 8a and the stretch film 9a used in the above comparative example were the same as those in the above example. The roof tile 1 used was also the same as that used in the example.

【００２３】以上の実施例と比較例の梱包の屋外暴露の
テスト結果は、表１に示す通りとなり、実施例の梱包に
おいては、瓦１の表面汚れの発生がなかったが、比較例
の梱包においては、瓦１の表面汚れの発生がみられた。The outdoor exposure test results of the packaging of the above-mentioned Examples and Comparative Examples are as shown in Table 1. In the packaging of the Examples, the surface contamination of the roof tile 1 did not occur, but the packaging of the Comparative Examples. In, the occurrence of stains on the surface of the roof tile 1 was observed.

【００２４】[0024]

【表１】 [Table 1]

【００２５】本発明のセメント系板材の梱包方法におい
て、実施例ではセメント系の瓦が用いられたが、その他
セメント系板材、例えば壁材等の建材であっても好適に
用いられるものであり、実施例に限定されるものではな
い。In the method for packing cement-based board materials of the present invention, cement-based roof tiles were used in the examples, but other cement-based board materials, such as building materials such as wall materials, are also preferably used. It is not limited to the examples.

【００２６】[0026]

【発明の効果】上記本発明のセメント系板材の梱包方
法、或いはその梱包体においては、積載された積重ね体
の側面と上面端部がフィルムにより梱包され、次いで上
面と側面上端部がシート掛けにより梱包され、更に側面
と上面端部がフィルムにより梱包されることにより、防
水性能が高くなり、積重ね体内への水の侵入がなく、エ
フロレッセンスの発生により瓦の表面が白濁するといっ
た汚れが防止される。又、梱包方法がフィルムの巻付け
による梱包と、シート掛けによる梱包であるから、梱包
工程の自動化が容易に実施でき生産性が向上する。従っ
て、セメント系板材の梱包方法及びその梱包体として好
適に用いられる。According to the method of packing a cement-based plate material of the present invention or the packing body thereof, the side surface and the upper end of the stacked stack are packed with a film, and then the upper surface and the upper end of the side surface are covered with a sheet. By packing and further packing the side and top edges with a film, the waterproof performance is improved, there is no water in the stack, and efflorescence causes the surface of the roof tile to become cloudy and prevent dirt. It Further, since the packing method is the packing by winding the film and the packing by the sheet hanging, automation of the packing process can be easily carried out and the productivity is improved. Therefore, it can be suitably used as a method for packing cement-based board materials and a packing body for the same.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明のセメント系板材の梱包方法の一例を示
すフロー図。FIG. 1 is a flow chart showing an example of a method for packing a cement board material according to the present invention.

【図２】瓦の結束体の斜視図。FIG. 2 is a perspective view of a bundle of roof tiles.

【図３】瓦の積重ね体の斜視図。FIG. 3 is a perspective view of a stack of roof tiles.

【図４】本発明のセメント系板材の梱包体の一例を示す
部分断面図。FIG. 4 is a partial cross-sectional view showing an example of a package of the cement board material of the present invention.

【図５】従来のセメント系板材の梱包体を示す部分断面
図。FIG. 5 is a partial cross-sectional view showing a conventional cemented board material package.

【符号の説明】[Explanation of symbols]

１ 瓦 １ａ、１ｂ ＰＰバンド ２ 載置台 ３ 段積み装置 ４ 結束機 ５ パレット積みロボット ６ パレット ７、９、９ａ フィルム ８、８ａ エアクッションシート １０ 内結束工程 １１ 瓦の結束体 １２ 瓦の積重ね体 １２ａ 上面 １２ｂ 側面 ２０ 積載工程 ３０ フィルム包装工程 DESCRIPTION OF SYMBOLS 1 roof tile 1a, 1b PP band 2 mounting table 3 stacking device 4 bundling machine 5 pallet loading robot 6 pallet 7, 9, 9a film 8, 8a air cushion sheet 10 inner bundling process 11 roof tile bundling body 12 roof tile stacking body 12a Upper surface 12b Side surface 20 Loading process 30 Film packaging process

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 パレット上に積載されたセメント系板材
の積重ね体の梱包方法であって、積載された積重ね体の
側面と上面端部をフィルムにより巻回されて梱包する第
一工程と、この第一工程で梱包された積重ね体の上面と
側面上端部をシート掛けにより梱包する第二工程と、更
に第二工程で梱包された積重ね体の側面と上面端部をフ
ィルムにより巻回されて梱包する第三工程よりなること
を特徴とするセメント系板材の梱包方法。1. A method of packing a stack of cement-based board materials stacked on a pallet, comprising a first step of winding a side surface and an upper end portion of the stacked stack by a film and packing the same. The second step of packing the top and side upper ends of the stack packed in the first step by sheeting, and the side and top edges of the stack packed in the second step are wrapped with a film and packed. A method for packing a cement board material, comprising the third step of: 【請求項２】 パレット上にセメント系板材の積重ねら
れ、セメント系板材積重ね体の側面と上面端部とがフィ
ルムにより巻回され、更に積重ね体の上面と側面上端部
とがシート掛けされ、更に積重ね体の側面と上面端部と
がフィルムにより巻回されていることを特徴とする梱包
体。2. A cement-based board material is stacked on a pallet, a side surface and an upper end portion of the cement-based board material stack are wound with a film, and a top surface and an upper end portion of a side surface of the stack body are covered with a sheet. A package in which a side surface and an upper end portion of the stack are wound with a film.