JPH08323911A - Forgery preventing laminate - Google Patents
Forgery preventing laminateInfo
- Publication number
- JPH08323911A JPH08323911A JP7247490A JP24749095A JPH08323911A JP H08323911 A JPH08323911 A JP H08323911A JP 7247490 A JP7247490 A JP 7247490A JP 24749095 A JP24749095 A JP 24749095A JP H08323911 A JPH08323911 A JP H08323911A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- refractive index
- optical
- forgery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、偽造防止等に使用
する、視角の変化により色の変化する、光学的多層膜を
持つ積層体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a laminate having an optical multi-layered film, which is used for prevention of forgery and the like, and whose color changes according to a change in viewing angle.
【０００２】[0002]
【従来の技術】従来、偽造を防止する手段は、物品その
ものを真似することが困難なもので、しかも偽造・改竄
などの不正行為の形跡の発見が容易であって、本物と偽
物を確実に識別できるようにするものがある。例えば紙
幣など有価証券のように、そのもの自体に微細な加工を
施するか、真似しにくい色調の彩色を施したり、また素
材を特殊なものとして、模造または印刷技術の不正行
為、或いは複写機による不法な複写による偽造などを困
難にすることで、防止できるようにしている。さらに印
刷複製技術の進歩、または複写機などデジタル技術の進
歩により、上記したような微細な加工を施したり、色彩
を真似しにくくしても容易に再現することが可能とな
り、このような技術に対応して、加工技術を高微細化
し、より複製・偽造を困難とするような方向にある。2. Description of the Related Art Conventionally, it is difficult to imitate an article itself as a means for preventing counterfeiting, and it is easy to find a trace of fraudulent activity such as counterfeiting or falsification, so that a genuine article and a fake article can be reliably assured. There is something that can be identified. For example, like securities such as banknotes, they are subjected to fine processing or colored in a color that is difficult to imitate, or as a special material, imitation of imitation or printing technology, or by copying machine This makes it possible to prevent forgery by making illegal copying difficult. Furthermore, due to advances in printing and duplication technology, and advances in digital technology such as copying machines, it becomes possible to easily reproduce even the fine processing described above and even when it is difficult to imitate colors. Correspondingly, the technology is becoming finer, making it more difficult to copy and forge.
【０００３】また複製又は偽造が困難なものであるとと
もに、機械による読み取りが可能な識別体がある。特定
の情報を表す回折格子からなるバーコードパターンをカ
ードの表面に形成し、これをレーザー照射光の反射光の
検出によって、その情報を読み取るものがある。またレ
リーフ型ホログラム・体積位相型ホログラムなどをレー
ザー光・白色光の照射により、その反射画像又は透過画
像を読み取る方法があり、実用化されている。Further, there is an identification body which is difficult to copy or forge and which can be read by a machine. There is a method in which a bar code pattern composed of a diffraction grating representing specific information is formed on the surface of a card, and the information is read by detecting reflected light of laser irradiation light. Further, there is a method of reading a reflection image or a transmission image of a relief type hologram, a volume phase type hologram, or the like by irradiating the relief type hologram or volume phase type hologram with laser light or white light, which has been put into practical use.
【０００４】これらは、識別しようとする媒体・物体に
直接形成される場合や、ベースとなる基材上にホログラ
ム画像を設けたシール、または被転写面に剥離可能にホ
ログラム画像を設けた転写箔を介して識別する媒体・物
体にホログラム画像を形成する場合がある。このように
して光学的に読み取り可能な情報を被識別体に設け、簡
単にその識別情報を読み取ることができる。These are used when they are directly formed on a medium or object to be identified, on a sticker provided with a hologram image on a base material, or on a transfer foil provided with a peelable hologram image on a surface to be transferred. A hologram image may be formed on a medium / object to be identified via the. In this way, the optically readable information is provided on the identification object, and the identification information can be easily read.
【０００５】さらに、これらは見る角度（すなわち、支
持している角度）に応じて固有のカラーシフト（反射光
の色変化）が起こす多層干渉層を形成してなるもので、
観察する位置により、見える色が異なることから、その
有無を確認すれば、本物であるか否かを判定できるもの
である。Further, these are formed by forming a multi-layer interference layer which causes a specific color shift (color change of reflected light) depending on the viewing angle (that is, the supporting angle).
Since the visible color differs depending on the position to be observed, it is possible to determine whether the product is genuine by checking the presence or absence of the color.
【０００６】しかしながら、印刷物の高度な微細化によ
る真偽の判別は、微細な箇所を拡大して見るか、あるい
は本物と比較するなど余程注意して見なければ見逃して
しまうため、またその場所の明るさや確認時間を十分に
とらなければならないなど、現状に合致しなくなってき
ている。また素材を特殊としても、全く特異な素材とす
ることはできず、またコスト的にも高くなり現実的では
ない。However, since the true / false discrimination due to the high degree of miniaturization of the printed matter is overlooked if the minute portion is magnified or compared with the genuine article, it is overlooked. It is becoming inconsistent with the current situation, such as having to take sufficient brightness and confirmation time. Moreover, even if the material is special, it cannot be made to be a peculiar material, and the cost becomes high, which is not realistic.
【０００７】[0007]
【発明が解決しようとする課題】本発明はこのような問
題点を解決するためになされたものであり、その課題と
するところは、真偽の判別の容易な偽造判定効果を有し
極めて高い偽造防止効果を発揮する光学的性質の異なる
膜を交互に積層した光学機能層を用いてなる偽造防止用
積層体を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in order to solve such a problem, and its problem is that it has a forgery judgment effect in which it is easy to judge whether it is true or false and is extremely high. An object of the present invention is to provide a forgery preventive laminate using an optical functional layer in which films having different optical properties that exert an anti-counterfeit effect are alternately laminated.
【０００８】[0008]
【課題を解決するための手段】本発明はこの課題を解決
するため、光学的性質の異なる膜が交互に積層してなる
光学機能層を有する偽造防止用積層体において、前記光
学機能層が、金属膜／低屈折率層と高屈折率層を交互に
積層してなるセラミック多層膜又は低屈折率か高屈折率
のセラミック単層膜／金属膜、あるいは低屈折率層と高
屈折率層を交互に積層してなるセラミック多層膜又は低
屈折率か高屈折率のセラミック単層膜／金属膜、からな
ることを特徴とする偽造防止用積層体を提供する。In order to solve this problem, the present invention provides a forgery prevention laminate having an optical functional layer formed by alternately laminating films having different optical properties, wherein the optical functional layer comprises: A metal multilayer film / ceramic multilayer film in which low refractive index layers and high refractive index layers are alternately laminated, or a ceramic single layer film / metal film having a low refractive index or a high refractive index, or a low refractive index layer and a high refractive index layer. There is provided a forgery prevention laminate comprising a ceramic multilayer film or a ceramic single layer film / metal film having a low refractive index or a high refractive index, which are alternately laminated.
【０００９】また、その構成として、基材上に、場合に
よっては剥離層を有し、光学機能層、接着層が順次積層
されてなり、光学機能層に接した上層又は下層に印刷層
を、または基材と光学機能層の間、または剥離層と光学
機能層との間にホログラム形成層を設けてなることを特
徴とする偽造防止用積層体を提供する。As its constitution, it has a release layer on the base material in some cases, and an optical functional layer and an adhesive layer are laminated in this order, and a printing layer is formed on the upper or lower layer in contact with the optical functional layer. Alternatively, there is provided a forgery-preventing laminate comprising a hologram forming layer provided between the substrate and the optical functional layer or between the peeling layer and the optical functional layer.
【００１０】また、その材料として、前記金属膜が、ク
ロム、アルミニウムのいずれかあるいは両方からなり、
前記低屈折率セラミックス膜が、二酸化珪素、フッ化マ
グネシウム、フッ化カルシウム、フッ化アルミニウムの
いずれかからなり、前記高屈折率セラミックス膜が、硫
化亜鉛、二酸化チタン、２酸化ジルコニウム、酸化イン
ジウム、酸化錫、酸化タンタル、酸化セリウム、酸化亜
鉛のいずれかからなることを特徴とする偽造防止用積層
体を提供する。As the material thereof, the metal film is made of chromium, aluminum, or both,
The low refractive index ceramic film is made of silicon dioxide, magnesium fluoride, calcium fluoride, or aluminum fluoride, and the high refractive index ceramic film is zinc sulfide, titanium dioxide, zirconium dioxide, indium oxide, or oxide. There is provided a forgery prevention laminate, which is made of any one of tin, tantalum oxide, cerium oxide, and zinc oxide.
【００１１】以上に示したように、本発明の偽造防止用
積層体においては、光学機能層を、金属膜／低屈折率層
と高屈折率層を交互に積層してなるセラミック多層膜又
は低屈折率か高屈折率のセラミック単層膜／金属膜、あ
るいは低屈折率層と高屈折率層を交互に積層してなるセ
ラミック多層膜又は低屈折率か高屈折率のセラミック単
層膜／金属膜、からなるものとしたことで、金属膜を使
用していることにより、吸収が大きく透明性は悪いが、
反射率が大きく、視角による色の変化の判別が容易とな
る。As described above, in the forgery prevention laminate of the present invention, the optical functional layer is a ceramic multilayer film or a low-refractive index layer in which a metal film / low refractive index layer and high refractive index layer are alternately laminated. Ceramic single layer film / metal film with high or high refractive index, or ceramic multilayer film with low refractive index layer and high refractive index layer alternately laminated, or ceramic single layer film / metal with low or high refractive index Since it is made of a film, since it uses a metal film, it has large absorption and poor transparency,
Since the reflectance is large, it is easy to determine the color change depending on the viewing angle.
【００１２】さらに光学機能層の上あるいは下に印刷層
を設けるまたは多層干渉膜と基材との間にホログラム形
成層を設けることにより、印刷画像またはホログラム画
像による情報と、印刷画像の間に露出する光学機能層に
よる真偽判別作用がより効果的になる。Further, by providing a printing layer above or below the optical functional layer or by providing a hologram forming layer between the multilayer interference film and the substrate, it is possible to expose between the printed image or information by the hologram image and the printed image. The optical discriminating function of the optical functional layer is effective.
【００１３】また、光学機能層の間に印刷層を設た場合
には、印刷のある部分では本来の光学機能層としての光
学的性能が阻害され、印刷画像による情報と印刷画像の
間に露出する光学機能層による真偽判別作用がより効果
的になる。Further, when the printing layer is provided between the optical functional layers, the optical performance as the original optical functional layer is impaired in a portion where printing is performed, and the information between the printed images is exposed. The optical discriminating function of the optical functional layer is effective.
【００１４】[0014]
【発明の実施形態】以下、本発明を図面を用いて詳細に
説明する。図１〜３に本発明の偽造防止用積層体の断面
の構成の一例を示す。DETAILED DESCRIPTION OF THE INVENTION The present invention will be described in detail below with reference to the drawings. 1 to 3 show an example of the cross-sectional structure of the forgery preventing laminate of the present invention.
【００１５】基材１は、ある程度の剛性および表面の平
滑性を有していればよく、とくに限定されるものではな
く、例えばポリエステルフィルム、ポリオレフィンフィ
ルム等の高分子フィルムが挙げられる。The base material 1 is not particularly limited as long as it has a certain degree of rigidity and surface smoothness, and examples thereof include polymer films such as polyester films and polyolefin films.
【００１６】剥離層２は、転写箔等として基材を剥離す
る場合に加えられる。剥離層に使用するものとしては、
加工の工程上安定性を有するものであれば、いかなるも
のであってもよい。有機材料であっても、無機材料であ
っても構わない。例えば、熱可塑性アクリル樹脂、塩化
ゴム系樹脂、塩化ビニル−酢酸ビニル共重合体樹脂、セ
ルロース系樹脂、塩素化ポリプロピレン、あるいはこれ
らにオイルシリコーン、脂肪酸アミド、ステアリン酸亜
鉛を添加したものが挙げられる。光学機能層の表面を保
護する目的を考えれば、光学機能層に影響が少ないこと
が好ましいが、特に限定されるものではない。The peeling layer 2 is added when peeling the substrate as a transfer foil or the like. For the release layer,
Any material may be used as long as it has stability in the processing step. It may be an organic material or an inorganic material. For example, a thermoplastic acrylic resin, a chlorinated rubber resin, a vinyl chloride-vinyl acetate copolymer resin, a cellulose resin, a chlorinated polypropylene, or those obtained by adding an oil silicone, a fatty acid amide, or zinc stearate may be mentioned. Considering the purpose of protecting the surface of the optical functional layer, it is preferable that the optical functional layer is less affected, but it is not particularly limited.
【００１７】光学機能層３の金属膜３ａに用いる金属と
しては、アルミニウム、クロム等が使用可能であるが、
これらと同等の屈折率と反射率を有するものであれば他
の鉄、チタン、銀等も用いることができる。この金属膜
３ａを設ける方法としては、通常の真空蒸着法、スパッ
タリング等の物理的気相析出法やＣＶＤ法のような化学
的気相析出法を用いることができ、金属膜３ａを構成す
る材料に応じて任意に選択することができる。As the metal used for the metal film 3a of the optical function layer 3, aluminum, chromium or the like can be used.
Other iron, titanium, silver, etc. can be used as long as they have the same refractive index and reflectance. As a method of providing the metal film 3a, a normal vapor deposition method, a physical vapor deposition method such as sputtering, or a chemical vapor deposition method such as a CVD method can be used. It can be arbitrarily selected according to.
【００１８】光学機能層３の低屈折率セラミックス膜３
ｂに用いるセラミックとしては、二酸化珪素、フッ化マ
グネシウム、フッ化カルシウム、フッ化アルミニウム等
が使用可能であるが、これらと同等の耐候性、耐薬品性
に優れてるものであれば他の、フッ化セリウム、酸化ア
ルミニウム、酸化マグネシウムも使用できる。Low refractive index ceramic film 3 of optical function layer 3
Silicon dioxide, magnesium fluoride, calcium fluoride, aluminum fluoride or the like can be used as the ceramic used in b. However, other ceramics can be used as long as they have excellent weather resistance and chemical resistance equivalent to these. Cerium chloride, aluminum oxide and magnesium oxide can also be used.
【００１９】この低屈折率セラミックス膜３ｂを設ける
方法としては、膜厚の制御が可能であれば、いかなる成
膜方法も用いることが可能である。なかでも薄膜の生成
には乾式法が優れており、これには通常の真空蒸着法、
スパッタリング等の物理的気相析出法やＣＶＤ法のよう
な化学的気相析出法を用いることができる。As a method of providing the low refractive index ceramic film 3b, any film forming method can be used as long as the film thickness can be controlled. Among them, the dry method is excellent for producing a thin film.
A physical vapor deposition method such as sputtering or a chemical vapor deposition method such as a CVD method can be used.
【００２０】光学機能層３の高屈折率セラミックス膜３
ｃに用いるセラミックとしては、硫化亜鉛、二酸化チタ
ン、二酸化ジルコニウム、酸化インジウム、酸化錫、酸
化タンタル、酸化セリウム、酸化亜鉛等が使用可能であ
るが、これらと同等の耐候性、耐薬品性に優れてるもの
であれば他のものも使用できる。この高屈折率セラミッ
クス膜３ｃを設ける方法は前記低屈折率セラミックス膜
３ｂと同様である。High refractive index ceramic film 3 of optical function layer 3
As the ceramic used for c, zinc sulfide, titanium dioxide, zirconium dioxide, indium oxide, tin oxide, tantalum oxide, cerium oxide, zinc oxide, etc. can be used, but they have excellent weather resistance and chemical resistance equivalent to these. Others can be used as long as they are available. The method for providing the high-refractive index ceramic film 3c is the same as that for the low-refractive index ceramic film 3b.
【００２１】接着層４は、転写目的で光学機能層を他の
基材に接着する際に使用する。使用する接着剤は後述す
る印刷層あるいはホログラム形成層の性能を侵すもので
なければ、いかなるものであっても構わない。例えば、
塩化ビニル−酢酸ビニル共重合体、アクリル系接着剤、
ポリエステル系ポリアミド等があるが、これらに限定さ
れるものではない。The adhesive layer 4 is used when the optical functional layer is adhered to another substrate for the purpose of transfer. Any adhesive may be used as long as it does not impair the performance of the printing layer or hologram forming layer described later. For example,
Vinyl chloride-vinyl acetate copolymer, acrylic adhesive,
Examples include polyester-based polyamides, but are not limited to these.
【００２２】印刷層５は、形成するパターン等の柄模様
は任意に決定することができ、図３の構成１において
は、少なくとも光学機能層３の一部が上面から見えるよ
うに構成すればよい。すなわち印刷層５を光学機能層３
上に部分的に形成するか、もしくは実質的にそのような
状態となるように形成されればよい。印刷層５の形成に
は、グラビア印刷など従来公知の印刷方法や塗布方法を
用いることができる。The pattern of the printing layer 5 such as a pattern to be formed can be arbitrarily determined, and in the configuration 1 of FIG. 3, at least a part of the optical functional layer 3 may be seen from the upper surface. . That is, the printing layer 5 is replaced with the optical function layer 3
It may be formed partially on the top, or may be formed so as to be substantially in such a state. A conventionally known printing method such as gravure printing or a coating method can be used for forming the printing layer 5.
【００２３】さらに印刷層５の色を単色で構成する場合
に、この薄膜を上方向から見たときの色あるいは極めて
それに近い色としてもよい。光学機能層３と印刷層５
が、上方向から見たときの色あるいは極めてそれに近い
色とすることで、一見同色に見えるようにすることによ
り、同一の層であると判断され、印刷層を隠し文字のよ
うに秘匿性を持たせ、より偽造防止効果を上げることも
可能である。また印刷層５の下層に透明なアンカー層を
形成してもよい。Further, when the printing layer 5 is composed of a single color, the color of the thin film may be a color viewed from above or a color very close to the color. Optical function layer 3 and printing layer 5
However, by setting the color as viewed from above or a color very close to it, it is judged that they are the same layer by making them seem to be the same color, and the printing layer is kept secret like hidden characters. It is also possible to increase the anti-counterfeiting effect by having it. Further, a transparent anchor layer may be formed below the printing layer 5.
【００２４】特に機能層３中に印刷層５が含まれる場合
は、上方向から見たときの色あるいは極めてそれに近い
色とすることで、一見同色に見えるようにすることによ
り、同一の層であると判断され、印刷層を隠し文字のよ
うに秘匿性を持たせ、より偽造効果を上げることも可能
である。さらに機能層３の従来の機能を阻害することで
より一層偽造防止効果を示すものである。In particular, when the functional layer 3 includes the printing layer 5, the color when viewed from above or a color very close to it is made to appear the same color so that the same layer is formed. If it is determined that the print layer is present, it is possible to make the print layer confidential like a hidden character to further enhance the forgery effect. Further, by inhibiting the conventional function of the functional layer 3, the anti-counterfeiting effect is further exhibited.
【００２５】この印刷層は上記したような文字以外に、
文字や数字、模様などデザインのように任意のパターン
を形成することができる。In addition to the characters described above, this printed layer is
Arbitrary patterns can be formed like designs such as letters, numbers and patterns.
【００２６】ホログラム形成層６は、形成するパターン
は任意に決定することができ、レリーフ型のホログラム
で、例えばウレタン系の樹脂層にスタンパーでエンボス
形成したものが挙げられる。The hologram forming layer 6 can be formed in any pattern, and may be a relief type hologram, for example, a urethane resin layer formed by embossing with a stamper.
【００２７】[0027]
＜実施例１＞基材１として厚さ２５μｍの透明ポリエス
テルフィルムを使用し、シリコン樹脂系の剥離層２を塗
布し、３ａ膜としてスパッタリング法によりクロムを膜
厚２３００Å、３ｂ膜として真空蒸着法により二酸化珪
素を膜厚３５Å、さらに３ａ膜としてスパッタリング法
によりクロムを膜厚３５Å積層し、光学機能層３を形成
した。さらに接着層４を形成し、転写箔とした。転写性
は良好であった。光学機能層３の透過スペクトルは図４
に示すスペクトルと同じであった。反射光は基材に対し
て垂直に見た場合には緑色であり、４５度斜めより見た
場合には青色であった。<Example 1> A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a silicone resin-based release layer 2 was applied, and chromium was deposited as a 3a film by a sputtering method to 2300Å and a 3b film was deposited by a vacuum deposition method. An optical functional layer 3 was formed by depositing silicon dioxide with a film thickness of 35Å and further depositing chromium with a film thickness of 35Å by a sputtering method as a 3a film. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good. The transmission spectrum of the optical functional layer 3 is shown in FIG.
It was the same as the spectrum shown in. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees.
【００２８】なお、作成した光学機能層の可視スペクト
ルを視外・可視分光光度計により測定した結果を図４に
示す。FIG. 4 shows the results of measuring the visible spectrum of the produced optical functional layer with an extra-visible / visible spectrophotometer.
【００２９】＜実施例２＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを使用し、シリコン樹脂系の
剥離層２を塗布し、３ａ膜としてスパッタリング法によ
りアルミニウムを膜厚３５Å、３ｂ膜として真空蒸着法
により二酸化珪素を膜厚２３００Å、さらに３ａ膜とし
てスパッタリング法によりアルミニウムを膜厚３５Å積
層し、光学機能層３を形成した。さらに接着層４を形成
し、転写箔とした。転写性波良好であった。Example 2 A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a silicone resin-based release layer 2 was applied, and a 3a film was formed of aluminum by a sputtering method with a film thickness of 35Å and a 3b film was formed into a vacuum. The optical function layer 3 was formed by depositing silicon dioxide with a film thickness of 2300 Å by a vapor deposition method and further laminating aluminum with a film thickness of 35 Å as a 3a film by a sputtering method. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００３０】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には緑色であり、４５度斜めより見た場合
には青色であった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees.
【００３１】＜実施例３＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを使用し、シリコン樹脂系の
剥離層２を塗布し、３ａ膜としてスパッタリング法によ
りクロムを膜厚３５Å、３ｂ膜として真空蒸着法により
フッ化マグネシウムを膜厚２３００Å、さらに３ａ膜と
してスパッタリング法によりクロムを膜厚３５Å積層
し、光学機能層３を形成した。さらに接着層４を形成
し、転写箔とした。転写性は良好であった。Example 3 A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a silicone resin-based release layer 2 was applied, and chromium was formed as a 3a film by a sputtering method with a film thickness of 35Å and a 3b film was formed into a vacuum. An optical function layer 3 was formed by depositing magnesium fluoride with a film thickness of 2300 Å by a vapor deposition method and further depositing chromium with a film thickness of 35 Å by a sputtering method as a 3a film. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００３２】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には緑色であり、４５度斜めより見た場合
には青色であった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees.
【００３３】＜実施例４＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを使用し、シリコン樹脂系の
剥離層２を塗布し、３ａ膜としてスパッタリング法によ
りアルミニウムを膜厚３５Å、３ｂ膜として真空蒸着法
によりフッ化マグネシウムを膜厚２３００Å、さらに３
ａ膜としてスパッタリング法によりアルミニウムを膜厚
３５Å積層し、光学機能層３を形成した。さらに接着層
４を形成し、転写箔とした。転写性は良好であった。Example 4 A transparent polyester film having a thickness of 25 μm was used as a base material 1, a silicone resin-based release layer 2 was applied, and aluminum was formed as a 3a film by a sputtering method with a film thickness of 35Å and a 3b film was formed into a vacuum. Magnesium fluoride film thickness of 2300Å by evaporation method, and further 3
As the film a, aluminum having a film thickness of 35 Å was laminated by a sputtering method to form the optical function layer 3. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００３４】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には緑色であり、４５度斜めより見た場合
には青色であった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees.
【００３５】＜実施例５＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを使用し、シリコン樹脂系の
剥離層２を塗布し、３ａ膜としてスパッタリング法によ
りクロムを膜厚３５Å、３ｂ膜として真空蒸着法により
二酸化珪素を膜厚２３００Å、さらに３ａ膜としてスパ
ッタリング法によりクロムを膜厚３５Å積層し、光学機
能層３を形成した。Example 5 A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a silicone resin-based release layer 2 was applied, and chromium was formed as a 3a film by a sputtering method with a film thickness of 35Å and 3b film. An optical function layer 3 was formed by depositing silicon dioxide with a film thickness of 2300 Å by a vapor deposition method and further depositing chromium with a film thickness of 35 Å by a sputtering method as a 3a film.
【００３６】次に「ＴＯＰ」の文字を黒色のインキで印
刷した。さらに接着層４を形成し、転写箔とした。転写
性は良好であった。Next, the letters "TOP" were printed with black ink. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００３７】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には緑色であり、４５度斜めより見た場合
には青色となった。「ＴＯＰ」の文字はいずれの角度か
らも認識できた。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. The letters "TOP" could be recognized from any angle.
【００３８】＜実施例６＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを使用し、シリコン樹脂系の
剥離層２を塗布し、「ＴＯＰ」の文字を青色のインキで
印刷した。３ａ膜としてスパッタリング法によりクロム
を膜厚３５Å、３ｂ膜として真空蒸着法により二酸化珪
素を膜厚２３００Å、さらに３ａ膜としてスパッタリン
グ法によりクロムを膜厚３５Å積層し、光学機能層３を
形成した。さらに接着層４を形成し、転写箔とした。転
写性は良好であった。Example 6 A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a release layer 2 made of a silicone resin was applied, and the letters “TOP” were printed with a blue ink. As the 3a film, a chromium film having a thickness of 35 Å was formed as a 3b film, and a silicon dioxide film having a film thickness of 2300 Å was formed as a 3b film by a vacuum deposition method, and further, a chromium film having a film thickness of 35 Å was laminated as a 3a film by a sputtering method to form an optical function layer 3. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００３９】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には緑色であり、「ＴＯＰ」の文字が認識
できたが、４５度斜めより見た場合には青色となり、
「ＴＯＰ」の文字の認識は困難となった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was green when viewed perpendicularly to the substrate, and the letters "TOP" could be recognized, but when viewed obliquely from 45 degrees, it became blue,
It became difficult to recognize the letters "TOP".
【００４０】＜実施例７＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを用い、これにシリコン樹脂
系の剥離層２を塗布し、さらにホログラム層６としてウ
レタン系の樹脂層にエンボス形成したものを用い、積層
した。Example 7 A transparent polyester film having a thickness of 25 μm was used as a base material 1, a silicone resin type release layer 2 was applied thereto, and a hologram layer 6 was embossed on a urethane type resin layer. Was used for lamination.
【００４１】これに真空蒸着法により、３ａ膜として硫
化亜鉛（光学膜厚２２５０Å）、３ｂ膜としてフッ化マ
グネシウム（光学膜厚４５００Å）、３ｃ膜として硫化
亜鉛（光学膜厚２２５０Å）の順で積層し、更に３ａ膜
としてクロム（膜厚７００Å）を形成した。さらに接着
層４を形成し、転写箔とした。転写性は良好であった。
多層干渉膜３の反射スペストルは図５に示すようになっ
た。反射光は、基材に対して垂直に見た場合は黄金色に
近く、４５度斜めより見た場合には緑色であった。Then, by vacuum deposition, zinc sulfide (optical film thickness 2250Å) as 3a film, magnesium fluoride (optical film thickness 4500Å) as 3b film, and zinc sulfide (optical film thickness 2250Å) as 3c film were laminated in this order. Then, chromium (film thickness 700Å) was further formed as a 3a film. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
The reflection spectrum of the multilayer interference film 3 is as shown in FIG. The reflected light was close to golden when viewed perpendicularly to the substrate and green when viewed obliquely at 45 degrees.
【００４２】＜実施例８＞３ｂ膜としてアルミニウム
（膜厚２００Å）を使用した以外は実施例７と同様にし
て転写箔とした。転写性は良好であった。多層干渉膜３
の反射スペストルは図６に示すようになった。反射光
は、基材に対して垂直に見た場合には、黄金色に近く、
さらにアルミニウムの金属光沢を有して、４５度斜めよ
り見た場合には緑色であった。<Example 8> A transfer foil was prepared in the same manner as in Example 7 except that aluminum (film thickness 200Å) was used as the 3b film. The transferability was good. Multilayer interference film 3
The reflection spectrum of the above became as shown in FIG. The reflected light is close to golden when viewed perpendicular to the substrate,
Further, it had a metallic luster of aluminum, and was green when viewed obliquely at 45 degrees.
【００４３】＜実施例９＞基材１として厚さ２５μｍの
透明ポリエステルフィルムを用い、これにシリコン樹脂
系の剥離層２を塗布し、さらにホログラム層６としてウ
レタン系の樹脂層にエンボス形成したものを用い、積層
した。Example 9 A transparent polyester film having a thickness of 25 μm was used as a substrate 1, a silicone resin-based release layer 2 was applied to this, and a hologram layer 6 was embossed on a urethane-based resin layer. Was used for lamination.
【００４４】これに真空蒸着法により、３ｃ膜として二
酸化チタン（光学膜厚２０００Å）、３ｂ膜として二酸
化珪素（光学膜厚４０００Å）、３ｃ膜として二酸化チ
タン（光学膜厚２０００Å）の順で積層し、更に３ａ膜
としてクロム（膜厚５００Å）を形成した。さらに接着
層４を形成し、転写箔とした。転写性は良好であった。
多層干渉膜３の反射スペクトルは図７に示すようになっ
た。反射光は、基材に対して垂直に見た場合には黄色〜
黄金色に近く、４５度斜めより見た場合には緑色であっ
た。Then, a 3c film made of titanium dioxide (optical film thickness 2000Å), a 3b film made of silicon dioxide (optical film thickness 4000Å), and a 3c film made of titanium dioxide (optical film thickness 2000Å) were laminated in this order by vacuum deposition. Further, chromium (thickness 500Å) was formed as a 3a film. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
The reflection spectrum of the multilayer interference film 3 is as shown in FIG. The reflected light is yellow ~ when viewed perpendicular to the substrate.
It was close to golden color and was green when viewed at an angle of 45 degrees.
【００４５】＜実施例１０＞３ｂ膜としてクロム（膜厚
５００Å）を用いた以外は実施例７と同様にして積層
し、さらに印刷層５として「ＴＯＰ」の文字を黒色のイ
ンキで印刷し、さらに接着層５を形成、転写箔とした。
転写性は良好であった。多層干渉膜３の反射スペクトル
は図８に示すようになった。反射光は、基材に対して垂
直に見た場合には緑色であり、４５度斜めより見た場合
には青色となった。クロムの膜厚が薄いため、光が透過
し、「ＴＯＰ」の文字はいずれの角度からも確認でき
た。<Example 10> Laminates were formed in the same manner as in Example 7 except that chromium (film thickness 500Å) was used as the 3b film, and the letters "TOP" were printed as the printing layer 5 with black ink. Further, an adhesive layer 5 was formed to obtain a transfer foil.
The transferability was good. The reflection spectrum of the multilayer interference film 3 is as shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. Since the chrome film thickness was thin, light was transmitted, and the letters "TOP" could be confirmed from any angle.
【００４６】＜実施例１１＞「ＴＯＰ」の文字を青色の
インキで設けた以外は実施例１０と同様にして転写箔を
得た。多層干渉膜３の反射スペクトルは図８に示すよう
になった。反射光は、基材に対して垂直に見た場合には
緑色であり、４５度斜めより見た場合には青色となっ
た。クロムの膜厚が薄いため、光が透過し、垂直に見た
場合に、「ＴＯＰ」の文字は確認できたが、４５度斜め
より見た場合には青色となり、「ＴＯＰ」の文字の確認
は困難となった。<Example 11> A transfer foil was obtained in the same manner as in Example 10 except that the letters "TOP" were formed with blue ink. The reflection spectrum of the multilayer interference film 3 is as shown in FIG. The reflected light was green when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. Since the chrome film thickness is thin, light can be transmitted, and the letters "TOP" can be seen when viewed vertically, but when viewed from 45 degrees diagonally, it becomes blue, and the letters "TOP" can be confirmed. Became difficult.
【００４７】＜実施例１２＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、シリコン樹脂系
の剥離層２を塗布し、３ａ膜としてスパッタリング法に
よりクロムを膜厚１０ｎｍ、３ｂ層として真空蒸着法に
より二酸化珪素を光学膜厚で５４０ｎｍ積層させ、その
後、スクリーン印刷法で「ＴＯＰ」の文字を白色のイン
キで印刷した。さらに３ａ層としてスパッタリング法に
よりクロムを膜厚で１００ｎｍ積層し、光学機能層３を
形成した。さらに接着層５を形成し、転写箔とした。転
写性は良好であった。光学機能層３の透過スペクトルは
図４に示すスペクトルと同じであった。反射光は基材に
対して垂直に見た場合には金色であり、４５度斜めより
見た場合には青色であった。白色で印刷した部分の色は
印刷部分に比べて金色は薄く、色の変化も小さかった。<Embodiment 12> The substrate 1 has a thickness of 12 μm.
Of the transparent polyester film, a release layer 2 made of a silicone resin is applied, a chromium film having a thickness of 10 nm is formed as a 3a film by a sputtering method, and a silicon dioxide film having an optical film thickness of 540 nm is formed as a 3b layer by a vacuum vapor deposition method. The character "TOP" was printed with white ink by the screen printing method. Further, as the 3a layer, chromium was laminated in a thickness of 100 nm by a sputtering method to form the optical function layer 3. Further, an adhesive layer 5 was formed to obtain a transfer foil. The transferability was good. The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００４８】なお、作成した光学機能層の可視スペクト
ルを視外・可視分光光度計により測定した結果を図４に
示す。FIG. 4 shows the result of measurement of the visible spectrum of the produced optical functional layer with an extra-visible / visible spectrophotometer.
【００４９】＜実施例１３＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、シリコン樹脂系
の剥離層２を塗布し、３ａ層としてスパッタリング法に
よりアルミニウムを膜厚１０ｎｍ、３ｂ層として真空蒸
着法により二酸化珪素を膜厚５４０ｎｍ積層させ、その
後、スクリーン印刷法で「ＴＯＰ」の文字を白色のイン
キで印刷した。さらに、３ａ層としてスパッタリング法
によりアルミニウムを膜厚１００ｎｍ積層し、光学機能
層３を形成した。さらに接着層４を形成し、転写箔とし
た。転写性波良好であった。<Embodiment 13> The substrate 1 has a thickness of 12 μm.
Of the transparent polyester film, a release layer 2 made of a silicon resin is applied, a layer 3a is formed by sputtering with a thickness of 10 nm of aluminum, and a layer 3b is formed by stacking silicon dioxide with a thickness of 540 nm by a vacuum deposition method, and then a screen is formed. The letters "TOP" were printed with white ink by the printing method. Further, as the 3a layer, aluminum was laminated to a film thickness of 100 nm by a sputtering method to form the optical function layer 3. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００５０】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には金色であり、４５度斜めより見た場合
には青色であった。白色で印刷した部分の色は印刷部分
に比べて金色は薄く、色の変化も小さかった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００５１】＜実施例１４＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、シリコン樹脂系
の剥離層２を塗布し、３ａ膜としてスパッタリング法に
よりクロムを膜厚１０ｎｍ、３ｂ膜として真空蒸着法に
よりフッ化マグネシウムを膜厚６００ｎｍ積層させ、そ
の後、スクリーン印刷法で「ＴＯＰ」の文字を白色のイ
ンキで印刷した。さらに、３ａ膜としてスパッタリング
法によりクロムを膜厚１００ｎｍ積層し、光学機能層３
を形成した。さらに接着層４を形成し、転写箔とした。
転写性は良好であった。<Example 14> A substrate 1 having a thickness of 12 μm
Of the transparent resin film, a silicone resin-based release layer 2 is applied, a chromium film having a thickness of 10 nm is formed as a 3a film by a sputtering method, and a magnesium fluoride film having a film thickness of 600 nm is formed as a 3b film by a vacuum evaporation method. The letters "TOP" were printed with white ink by screen printing. Further, as the 3a film, a chromium film having a film thickness of 100 nm is laminated by a sputtering method to obtain an optical function layer 3
Was formed. Further, an adhesive layer 4 was formed to obtain a transfer foil.
The transferability was good.
【００５２】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には金色であり、４５度斜めより見た場合
には青色であった。白色で印刷した部分の色は印刷部分
に比べて金色は薄く、色の変化も小さかった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００５３】＜実施例１５＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、シリコン樹脂系
の剥離層２を塗布し、３ａ膜としてスパッタリング法に
よりアルミニウムを光学膜厚で１０ｎｍ、３ｂ膜として
真空蒸着法によりフッ化マグネシウムを光学膜厚で６０
０ｎｍ積層させ、その後、スクリーン印刷法で「ＴＯ
Ｐ」の文字を白色のインキで印刷した。さらに、３ａ膜
としてスパッタリング法によりアルミニウムを光学膜厚
で１００ｎｍ積層し、光学機能層３を形成した。さらに
接着層４を形成し、転写箔とした。転写性は良好であっ
た。<Example 15> 12 μm thick as the base material 1
Of the transparent polyester film, a silicon resin-based release layer 2 is applied, and as a 3a film, aluminum is formed to an optical film thickness of 10 nm by a sputtering method, and as a 3b film, magnesium fluoride is formed to an optical film thickness of 60 nm by a vacuum deposition method.
After stacking it to 0 nm, the screen printing method "TO
The letter "P" was printed with white ink. Further, as the 3a film, aluminum was laminated to have an optical film thickness of 100 nm by a sputtering method to form an optical function layer 3. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００５４】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には金色であり、４５度斜めより見た場合
には青色であった。白色で印刷した部分の色は印刷部分
に比べて金色は薄く、色の変化も小さかった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００５５】＜実施例１６＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、シリコン樹脂系
の剥離層２を塗布し、３ａ膜としてスパッタリング法に
よりクロムを膜厚１０ｎｍ、３ｂ膜として真空蒸着法に
より二酸化珪素を膜厚５４０ｎｍ積層させ、その後、ス
クリーン印刷法で「ＴＯＰ」の文字を白色のインキで印
刷した。さらに、３ａ膜としてスパッタリング法により
クロムを光学膜厚で１００ｎｍ積層し、光学機能層３を
形成した。さらに接着層４を形成し、転写箔とした。転
写性は良好であった。<Example 16> A substrate 1 having a thickness of 12 μm
Of the transparent polyester film, a release layer 2 made of a silicon resin is applied, a chromium film having a thickness of 10 nm is formed as a 3a film by a sputtering method, and a silicon dioxide film having a film thickness of 540 nm is formed as a 3b film by a vacuum deposition method, and then a screen is formed. The letters "TOP" were printed with white ink by the printing method. Further, as the 3a film, chromium was laminated in an optical film thickness of 100 nm by a sputtering method to form the optical function layer 3. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good.
【００５６】光学機能層３の透過スペクトルは図４に示
すスペクトルと同じであった。反射光は基材に対して垂
直に見た場合には金色であり、４５度斜めより見た場合
には青色であった。白色で印刷した部分の色は印刷部分
に比べて金色は薄く、色の変化も小さかった。The transmission spectrum of the optical functional layer 3 was the same as the spectrum shown in FIG. The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００５７】＜実施例１７＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを使用し、３ａ膜としてス
パッタリング法によりアルミニウムを１０ｎｍ膜厚、３
ｂ膜として真空蒸着法により二酸化珪素を膜厚５４０ｎ
ｍ積層させ、その後、スクリーン印刷法で「ＴＯＰ」の
文字を白色のインキで印刷した。さらに、３ａ膜として
スパッタリング法によりアルミニウムを１００ｎｍ膜厚
積層し、光学機能層３を形成した。さらに接着層４を形
成し、シールとした。<Example 17> A substrate 1 having a thickness of 12 μm
Using a transparent polyester film of No. 3, aluminum is formed to a thickness of 10 nm by a sputtering method as a 3a film,
As the film b, a silicon dioxide film having a thickness of 540 n is formed by a vacuum deposition method.
Then, the letters “TOP” were printed with white ink by a screen printing method. Further, as the 3a film, aluminum was laminated in a thickness of 100 nm by a sputtering method to form the optical function layer 3. Further, an adhesive layer 4 was formed to make a seal.
【００５８】反射光は基材に対して垂直に見た場合には
金色であり、４５度斜めより見た場合には青色であっ
た。白色で印刷した部分の色は印刷部分に比べて金色は
薄く、色の変化も小さかった。The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００５９】＜実施例１８＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを用い、３ａ膜としてスパ
ッタリング法によりクロムを１０ｎｍ膜厚、３ｂ膜とし
て真空蒸着法により二酸化珪素を膜厚６００ｎｍ積層さ
せ、その後、スクリーン印刷法で「ＴＯＰ」の文字を白
色のインキで印刷した。さらに、３ａ膜としてスパッタ
リング法によりクロムを１００ｎｍ膜厚積層し、光学機
能層３を形成した。さらに接着層４を形成し、シールと
した。<Embodiment 18> The substrate 1 has a thickness of 12 μm.
Using the transparent polyester film of 3), chromium is deposited to a thickness of 10 nm as a film 3a and silicon dioxide is deposited to a thickness of 600 nm as a film 3b by a vacuum vapor deposition method, and then the letters "TOP" are printed in white ink by a screen printing method. Printed in. Further, as the 3a film, chromium was laminated in a thickness of 100 nm by a sputtering method to form the optical function layer 3. Further, an adhesive layer 4 was formed to make a seal.
【００６０】反射光は基材に対して垂直に見た場合には
金色であり、４５度斜めより見た場合には青色であっ
た。白色で印刷した部分の色は印刷部分に比べて金色は
薄く、色の変化も小さかった。The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００６１】＜実施例１９＞基材１として厚さ１２μｍ
の透明ポリエステルフィルムを用い、３ａ膜としてスパ
ッタリング法によりアルミニウムを１０ｎｍ膜厚、３ｂ
膜として真空蒸着法によりフッ化マグネシウムを膜厚６
００ｎｍ積層させ、その後、スクリーン印刷法で「ＴＯ
Ｐ」の文字を白色のインキで印刷した。さらに、３ａ膜
としてスパッタリング法によりアルミニウムを１００ｎ
ｍ膜厚積層し、光学機能層３を形成した。さらに接着層
４を形成し、シールとした。<Example 19> 12 μm thick as the base material 1
Using a transparent polyester film of No. 3, aluminum is formed as a film 3a by a sputtering method to a film thickness of 10 nm, 3b
As a film, magnesium fluoride having a film thickness of 6 is formed by a vacuum deposition method.
Layered to a thickness of 00 nm, and then screen printed using "TO
The letter "P" was printed with white ink. Further, as a 3a film, 100n of aluminum is formed by a sputtering method.
The optical functional layer 3 was formed by laminating m layers. Further, an adhesive layer 4 was formed to make a seal.
【００６２】反射光は基材に対して垂直に見た場合には
金色であり、４５度斜めより見た場合には青色であっ
た。白色で印刷した部分の色は印刷部分に比べて金色は
薄く、色の変化も小さかった。The reflected light was gold when viewed perpendicularly to the substrate and blue when viewed obliquely at 45 degrees. As for the color of the part printed in white, the gold color was lighter and the change in color was smaller than that of the printed part.
【００６３】＜比較例＞基材として厚さ２５μｍの透明
ポリエステルフィルムに、シリコン樹脂系の剥離層３を
塗布し、更にホログラム層を形成して基材とした。セラ
ミック膜を形成せずにクロム（膜厚５００Å）のみを真
空蒸着法により形成した。さらに接着層４を形成し転写
箔とした。転写性は良好であった。反射光は、基材に対
して垂直に見た場合は黒のメタリック色となり、４５度
斜めより見ても色に変化はなかった。<Comparative Example> A transparent polyester film having a thickness of 25 μm was coated with a silicone resin-based release layer 3 and a hologram layer was further formed as a substrate. Only chromium (film thickness 500Å) was formed by vacuum deposition without forming a ceramic film. Further, an adhesive layer 4 was formed to obtain a transfer foil. The transferability was good. The reflected light had a black metallic color when viewed perpendicularly to the substrate, and there was no change in color when viewed at an angle of 45 degrees.
【００６４】[0064]
【発明の効果】本発明の偽造防止用積層体は以上のよう
な光学機能層の構成をとることにより、その反射光が視
角により変わることで真偽の判別の容易な偽造判定効果
を有するようにしたものである。これにより従来の回折
格子を利用したホログラムのようなものより、簡素な構
造であり、かつ真偽判定を容易に行なうことができ、極
めて高い偽造防止効果を発揮するものである。The anti-counterfeit laminate of the present invention has the above-mentioned optical functional layer structure, so that the reflected light changes depending on the viewing angle so that the anti-counterfeit judgment can be easily made. It is the one. As a result, the structure is simpler than that of a hologram using a conventional diffraction grating, the authenticity determination can be easily performed, and an extremely high forgery prevention effect is exhibited.
【００６５】[0065]
【図１】本発明の偽造防止用積層体の断面の構成の一例
を示す説明図である。FIG. 1 is an explanatory view showing an example of a cross-sectional structure of a forgery preventing laminate of the present invention.
【図２】本発明の偽造防止用積層体の断面の構成の一例
を示す説明図である。FIG. 2 is an explanatory diagram showing an example of a cross-sectional structure of a forgery preventing laminate of the present invention.
【図３】本発明の偽造防止用積層体の断面の構成の一例
を示す説明図である。FIG. 3 is an explanatory diagram showing an example of a cross-sectional structure of a forgery preventing laminate of the present invention.
【図４】本発明の偽造防止用積層体による光学機能層の
透過スペクトルを表す図である。FIG. 4 is a diagram showing a transmission spectrum of an optical functional layer formed by the forgery preventing laminate of the present invention.
【図５】本発明の偽造防止用積層体による光学機能層の
透過スペクトルを表す図である。FIG. 5 is a diagram showing a transmission spectrum of an optical function layer of the forgery preventing laminate of the present invention.
【図６】本発明の偽造防止用積層体による光学機能層の
透過スペクトルを表す図である。FIG. 6 is a diagram showing a transmission spectrum of an optical function layer of the forgery preventing laminate of the present invention.
【図７】本発明の偽造防止用積層体による光学機能層の
透過スペクトルを表す図である。FIG. 7 is a diagram showing a transmission spectrum of an optical function layer of the forgery preventing laminate of the present invention.
【図８】本発明の偽造防止用積層体による光学機能層の
透過スペクトルを表す図である。FIG. 8 is a diagram showing a transmission spectrum of an optical function layer of the forgery preventing laminate of the present invention.
１…基材 ２…剥離層 ３…光学機能層 ３ａ…金属膜 ３ｂ…低屈折率セラミックス膜 ３ｃ…高屈折率セラミ
ックス膜 ４…接着層 ５…印刷層 ６…ホログラム形成層DESCRIPTION OF SYMBOLS 1 ... Substrate 2 ... Release layer 3 ... Optical functional layer 3a ... Metal film 3b ... Low refractive index ceramics film 3c ... High refractive index ceramics film 4 ... Adhesive layer 5 ... Printing layer 6 ... Hologram forming layer
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 18/00 Ｂ３２Ｂ 18/00 Ｂ Ｇ０３Ｈ 1/18 Ｇ０３Ｈ 1/18 (72)発明者 牛腸 智 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内 (72)発明者 清川 和利 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内 (72)発明者 北村 智史 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内Continuation of the front page (51) Int.Cl. 6 Identification number Reference number within the agency FI Technical display location B32B 18/00 B32B 18/00 B G03H 1/18 G03H 1/18 (72) Inventor Satoshi Usuen Taito-ku, Tokyo 1-5-1 Taito Toppan Printing Co., Ltd. (72) Inventor Kazutoyo Kiyokawa 1-5-1 Taito Taito-ku, Tokyo Inside Toppan Printing Co., Ltd. (72) Satoshi Kitamura Taito-ku Taito-ku, Tokyo 1-5-1 Toppan Printing Co., Ltd.
Claims (10)
る光学機能層を有する偽造防止用積層体において、前記
光学機能層が、金属膜／低屈折率層と高屈折率層を交互
に積層してなるセラミック多層膜又は低屈折率か高屈折
率のセラミック単層膜／金属膜、あるいは低屈折率層と
高屈折率層を交互に積層してなるセラミック多層膜又は
低屈折率か高屈折率のセラミック単層膜／金属膜、から
なることを特徴とする偽造防止用積層体。1. A forgery-preventing laminate having an optical functional layer formed by alternately laminating films having different optical properties, wherein the optical functional layer alternates a metal film / low refractive index layer and high refractive index layer. Ceramic multilayer film or low refractive index or high refractive index ceramic single layer film / metal film, or ceramic multilayer film or low refractive index layer alternately laminated with low refractive index layer and high refractive index layer An anti-counterfeit laminate comprising a high refractive index ceramic single layer film / metal film.
着層が順次積層されてなることを特徴とする請求項１記
載の偽造防止用積層体。2. The anti-counterfeit laminate according to claim 1, wherein the optical function layer according to claim 1 and the adhesive layer are sequentially laminated on a base material.
てなることを特徴とする請求項２記載の偽造防止用積層
体。3. The anti-counterfeit laminate according to claim 2, further comprising a release layer provided between the base material and the optical functional layer.
刷層を設けてなることを特徴とする請求項２または３の
いずれか記載の偽造防止用積層体。4. The anti-counterfeit laminate according to claim 2, wherein a print layer is provided as an upper layer or a lower layer in contact with the optical function layer.
と光学機能層との間にホログラム形成層を設けてなるこ
とを特徴とする請求項２または３のいずれか記載の偽造
防止用積層体。5. The forgery prevention according to claim 2, wherein a hologram forming layer is provided between the substrate and the optical functional layer or between the peeling layer and the optical functional layer. Laminate.
ずれかあるいは両方からなることを特徴とする請求項１
〜５のいずれか記載の偽造防止用積層体。6. The metal film is made of one or both of chromium and aluminum.
A laminated body for preventing forgery according to any one of to 5.
素、フッ化マグネシウム、フッ化カルシウム、フッ化ア
ルミニウムのいずれかからなることを特徴とする請求項
１〜６のいずれか記載の偽造防止用積層体。7. The forgery prevention according to claim 1, wherein the low refractive index ceramic film is made of any one of silicon dioxide, magnesium fluoride, calcium fluoride and aluminum fluoride. Laminate.
鉛、二酸化チタン、２酸化ジルコニウム、酸化インジウ
ム、酸化錫、酸化タンタル、酸化セリウム、酸化亜鉛の
いずれかからなることを特徴とする請求項１〜７のいず
れか記載の偽造防止用積層体。8. The high refractive index ceramic film is made of any one of zinc sulfide, titanium dioxide, zirconium dioxide, indium oxide, tin oxide, tantalum oxide, cerium oxide, and zinc oxide. A laminated body for preventing forgery according to any one of to 7.
ることを特徴とする請求項２または３、及び請求項５〜
８のいずれか記載の偽造防止用積層体。9. A print layer is provided between the optical functional layers, and the print layer is provided between the optical function layer and the optical function layer.
8. The forgery preventing laminate according to any one of 8 above.
特徴とする請求項４または９のいずれか記載の偽造防止
用積層体。10. The anti-counterfeit laminate according to claim 4, wherein the printed layer is patterned.