JPH08323286A - Aluminum alloy plate having good lubrication property - Google Patents
Aluminum alloy plate having good lubrication propertyInfo
- Publication number
- JPH08323286A JPH08323286A JP13549395A JP13549395A JPH08323286A JP H08323286 A JPH08323286 A JP H08323286A JP 13549395 A JP13549395 A JP 13549395A JP 13549395 A JP13549395 A JP 13549395A JP H08323286 A JPH08323286 A JP H08323286A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- film
- alloy plate
- polyethylene oxide
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、その表面に潤滑性を有
する皮膜が形成されたアルミニウム合金板に関し、特に
プレス成形等の成形加工が施される家電製品又はシャー
シ等の自動車部品等の製造に好適の潤滑性が優れたアル
ミニウム合金板に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an aluminum alloy plate having a film having lubricity formed on the surface thereof, and in particular to the production of home electric appliances or automobile parts such as chassis which are subjected to molding such as press molding. The present invention relates to an aluminum alloy plate having excellent lubricity suitable for.
【０００２】[0002]
【従来の技術】アルミニウム合金板（以下、アルミニウ
ム板も含む）は、耐食性及び美的外観（意匠性）が優れ
ていると共に軽量であるため、家庭用電化製品、シャー
シ等の自動車部品又は各種容器類等に広く使用されてい
る。2. Description of the Related Art Aluminum alloy sheets (hereinafter also referred to as aluminum sheets) are excellent in corrosion resistance and aesthetic appearance (design) and are lightweight, so that they are household electric appliances, automobile parts such as chassis, and various containers. Widely used for etc.
【０００３】しかし、アルミニウム合金板は、冷延鋼板
又は表面処理鋼板に比べて成形性が劣り、プレス成形等
によって素材の表層が剥離し易い。このため、成形加工
時に剥離片が金型に付着して金型の寸法が変わる所謂ビ
ルドアップ現象が発生してしまうという欠点がある。ま
た、アルミニウム合金板は、鋼等に比べて硬度が低いた
め、鋼と同一の条件で成形加工すると、その表面に疵が
付いてしまう。However, the aluminum alloy sheet is inferior in formability to the cold-rolled steel sheet or the surface-treated steel sheet, and the surface layer of the material is easily peeled off by press forming or the like. For this reason, there is a drawback that a peeling piece adheres to the mold during the molding process, which causes a so-called build-up phenomenon in which the size of the mold changes. Further, since the aluminum alloy plate has a lower hardness than steel or the like, if the aluminum alloy plate is formed and processed under the same conditions as steel, its surface will be flawed.
【０００４】このため、従来、アルミニウム合金板を成
形加工する場合には、その表面に潤滑油を塗布して、ア
ルミニウム合金板を保護することにより、その成形性を
向上させている。そして、成形加工後に有機溶剤を使用
してアルミニウム合金板を脱脂洗浄し、表面に残留した
潤滑油を除去している。For this reason, conventionally, when forming an aluminum alloy plate, the surface of the aluminum alloy plate is coated with lubricating oil to protect the aluminum alloy plate, thereby improving its formability. After the forming process, the aluminum alloy plate is degreased and washed using an organic solvent to remove the lubricating oil remaining on the surface.
【０００５】ところで、近年、環境保護の観点から、有
機溶剤の使用が規制されるようになったため、アルミニ
ウム合金板を成形加工する場合には、従来使用している
潤滑油に替えて低粘度の揮発性潤滑油を使用し、有機溶
剤による脱脂洗浄の工程を省略する傾向にある。また、
潤滑油を使用せずにアルミニウム合金板を成形加工する
方法も提案されている。By the way, in recent years, from the viewpoint of environmental protection, the use of organic solvents has come to be regulated. Therefore, when forming an aluminum alloy sheet, a lubricating oil having a low viscosity is used instead of the conventionally used lubricating oil. Volatile lubricating oil is used, and the process of degreasing and cleaning with an organic solvent tends to be omitted. Also,
A method of forming an aluminum alloy plate without using a lubricating oil has also been proposed.
【０００６】しかし、潤滑油を使用しない場合は勿論の
こと、揮発性潤滑油を使用する場合であっても、アルミ
ニウム合金板の成形性を十分に向上させることは困難で
ある。このため、アルミニウム合金板の成形加工時にお
いて割れ、しわ又は焼付きが発生したり、表面に疵が付
きやすくなってしまう。However, it is difficult to sufficiently improve the formability of the aluminum alloy sheet not only when the lubricating oil is not used but also when the volatile lubricating oil is used. For this reason, cracks, wrinkles, or seizures may occur during the forming process of the aluminum alloy plate, or the surface may be easily scratched.
【０００７】そこで、アルミニウム合金板の表面に予め
潤滑性を有する皮膜として、例えばポリオレフィンワッ
クス、パーフロロカーボン樹脂ワックス、フッ素系樹脂
粉末、グラファイト又は窒化ホウ素等の潤滑剤を混合し
たウレタン系又はエポキシ系等の樹脂膜を形成して、成
形性を向上させたアルミニウム合金板が提案されている
（特開平１−１２２４３２号、特開平４−２６８０３８
号、特開平５−３０９３１１号、特開平５−３１１４５
４及び特開平５−３２０９３４号）。Therefore, as a film having a lubricating property in advance on the surface of the aluminum alloy plate, for example, a polyolefin-based wax, a perfluorocarbon resin wax, a fluorine-based resin powder, a urethane-based or epoxy-based material mixed with a lubricant such as graphite or boron nitride, etc. There is proposed an aluminum alloy plate having a resin film formed by improving the formability thereof (JP-A-1-122432, JP-A-4-268038).
JP-A-5-309311 and JP-A-5-31145.
4 and JP-A-5-320934).
【０００８】[0008]
【発明が解決しようとする課題】しかしながら、上述し
た皮膜をアルミニウム合金板の表面に形成する場合であ
っても、前記皮膜の強度が十分ではないため、成形加工
時においてその皮膜の焼付きが発生してしまう。それ
に、アルミニウム合金板の表面は疵が付きやすく、耐疵
付き性も十分ではない。However, even when the above-mentioned coating is formed on the surface of an aluminum alloy plate, the strength of the coating is not sufficient, so that seizure of the coating occurs during molding. Resulting in. In addition, the surface of the aluminum alloy plate is easily scratched and the scratch resistance is not sufficient.
【０００９】また、皮膜における潤滑剤の添加量が少な
いと、十分な潤滑性を得ることができず、逆に潤滑剤の
添加量を多くすると、潤滑剤が皮膜の表面に滲み出して
しまう。このため、アルミニウム合金板の成形加工後に
塗装を施す場合には、皮膜と塗料との密着性が低下する
ため、アルミニウム合金板の表面に良好な塗装による皮
膜（以下、「塗装皮膜」という）を形成することができ
ない。If the amount of the lubricant added to the film is small, sufficient lubricity cannot be obtained. Conversely, if the amount of the lubricant added is too large, the lubricant oozes out on the surface of the film. For this reason, when applying a coating after the aluminum alloy sheet has been formed, the adhesion between the coating and the coating will decrease, so a good coating on the surface of the aluminum alloy sheet (hereinafter referred to as the "coating") Cannot be formed.
【００１０】更に、上述の潤滑剤及び樹脂を使用して皮
膜を形成する場合には、この他に架橋剤等を添加する必
要があるため、皮膜形成用の塗料を作製する場合に、そ
の作業性が低下してしまう。更にまた、上述の潤滑剤及
び樹脂は高価であるため、前記塗料の製作コストが高く
なってしまう。Further, when a film is formed using the above-mentioned lubricant and resin, it is necessary to add a cross-linking agent or the like in addition to the above. Sex is reduced. Furthermore, since the above-mentioned lubricant and resin are expensive, the manufacturing cost of the paint is increased.
【００１１】本発明はかかる問題点に鑑みてなされたも
のであって、皮膜の焼付きを防止することができ、高い
耐疵付き性を有し、成形加工後の塗装性が良好である潤
滑性が優れたアルミニウム合金板を提供することを目的
とする。The present invention has been made in view of the above problems, and it is possible to prevent seizure of a film, have high scratch resistance, and have good paintability after molding. An object is to provide an aluminum alloy plate having excellent properties.
【００１２】[0012]
【課題を解決するための手段】本発明に係る潤滑性が優
れたアルミニウム合金板は、その表面に平均分子量が５
万乃至５００万であるポリエチレンオキシドの皮膜を有
することを特徴とする。また、前記表面はクロメート処
理が施されていることが好ましい。The aluminum alloy sheet having excellent lubricity according to the present invention has an average molecular weight of 5 on its surface.
It is characterized by having a polyethylene oxide film of 10 to 5 million. Moreover, it is preferable that the surface is subjected to a chromate treatment.
【００１３】なお、ポリエチレンオキシドの化学組成は
下記化１に示すものであり、Ｒ1及びＲ2はアルキル基、
またｎは１０００乃至１０００００である。The chemical composition of polyethylene oxide is shown in the following chemical formula 1, wherein R 1 and R 2 are alkyl groups,
Further, n is 1000 to 100000.
【００１４】[0014]
【化１】 Embedded image
【００１５】[0015]
【作用】本願発明者等は皮膜の焼付きを防止することが
でき、高い耐疵付き性を有し、成形加工後の塗装性が良
好である潤滑性が優れたアルミニウム合金板を開発すべ
く、種々の実験研究を行った。その結果、アルミニウム
合金板の表面に所定のポリマーを皮膜として形成するこ
とにより、本発明の目的を達成し得ることを見い出し
た。The present inventors intend to develop an aluminum alloy plate which can prevent seizure of the coating, has high scratch resistance, and has good paintability after forming and excellent lubricity. , Various experimental studies were conducted. As a result, they have found that the object of the present invention can be achieved by forming a predetermined polymer as a film on the surface of an aluminum alloy plate.
【００１６】このポリマーには、以下のような特性を有
するポリエチレンオキシドを使用する。即ち、ポリエチ
レンオキシドは柔軟性を有すると共に、高密度ポリエチ
レンと略同程度の高強度を有する。このため、ポリエチ
レンオキシドの皮膜は、優れた強度を有すると共に延伸
性が優れたものとなる。Polyethylene oxide having the following characteristics is used for this polymer. That is, polyethylene oxide has flexibility and high strength that is substantially the same as high-density polyethylene. Therefore, the polyethylene oxide film has excellent strength and excellent stretchability.
【００１７】また、ポリエチレンオキシドは直鎖状の規
則正しい螺旋構造をしており、また優れた摩擦抵抗減少
効果も有する。このため、ポリエチレンオキシドの皮膜
は、優れた潤滑性を有するものとなる。Polyethylene oxide has a linear regular helix structure and also has an excellent effect of reducing frictional resistance. Therefore, the polyethylene oxide film has excellent lubricity.
【００１８】更に、ポリエチレンオキシドは吸湿性が低
く、また化学的活性基を有しない。このため、ポリエチ
レンオキシドの皮膜は化学反応性が小さく、高温等の過
酷な環境下においても安定性を有する。Furthermore, polyethylene oxide has low hygroscopicity and has no chemically active group. Therefore, the polyethylene oxide film has low chemical reactivity and is stable even in a severe environment such as high temperature.
【００１９】これらの特性を有するポリエチレンオキシ
ドの皮膜をアルミニウム合金板の表面に形成することに
より、優れた潤滑性を有するアルミニウム合金板を得る
ことができ、成形加工時におけるアルミニウム合金板の
金型への滑り込みが良好となるため、成形性を大幅に向
上させることができる。By forming a film of polyethylene oxide having these characteristics on the surface of the aluminum alloy plate, an aluminum alloy plate having excellent lubricity can be obtained, and the aluminum alloy plate mold can be formed during molding. Since the slippage is good, the moldability can be greatly improved.
【００２０】また、前記皮膜は高強度であるため、成形
加工時における皮膜の焼付きを防止することができ、ア
ルミニウム合金板の耐疵付き性を向上させることができ
る。更に、前記皮膜を形成したアルミニウム合金板を成
形加工した後に塗装する場合において、前記皮膜には塗
装皮膜との密着性を阻害する潤滑剤が添加されていない
ため、前記皮膜と塗装皮膜との密着性を向上させること
ができ、良好な塗装皮膜を形成することができる。更に
また、前記皮膜は吸湿性が低く、化学反応性も低いた
め、アルミニウム合金板が酸又はアルカリ等の過酷な条
件下で使用されても、優れた耐食性の効果を発揮するこ
とができる。Further, since the film has a high strength, it is possible to prevent the film from seizing during the molding process and improve the scratch resistance of the aluminum alloy plate. Furthermore, in the case of coating after forming and processing the aluminum alloy plate on which the film has been formed, the film does not contain a lubricant that inhibits the adhesion to the film, so that the film adheres to the film. The property can be improved and a good coating film can be formed. Furthermore, since the film has low hygroscopicity and low chemical reactivity, even if the aluminum alloy plate is used under harsh conditions such as acid or alkali, excellent corrosion resistance can be exerted.
【００２１】次に、ポリエチレンオキシドの皮膜をアル
ミニウム合金板の表面に形成する方法について説明す
る。先ず、ポリエチレンオキシドを所定の濃度となるよ
うに水に溶解した処理浴を、ロールコーティング法等に
よりアルミニウム合金板の表面上に塗布して、所定の厚
さの水膜を形成する。その後、１００〜２００℃の温度
で数秒間焼き付けることにより、水分を蒸発させてポリ
エチレンオキシドの皮膜を形成する。Next, a method for forming a polyethylene oxide film on the surface of the aluminum alloy plate will be described. First, a treatment bath in which polyethylene oxide is dissolved in water so as to have a predetermined concentration is applied on the surface of an aluminum alloy plate by a roll coating method or the like to form a water film having a predetermined thickness. Then, by baking at a temperature of 100 to 200 ° C. for several seconds, the water is evaporated to form a polyethylene oxide film.
【００２２】次に、アルミニウム合金板の表面にクロメ
ート処理を施す場合について説明する。クロメート処理
には、リン酸クロメート処理と塗布型クロメート処理と
がある。リン酸クロメート処理では、リン酸、クロム酸
又はフッ酸等の化合物を所定の濃度となるように水に溶
解したリン酸クロメート処理浴を、所定の温度に調整
し、その処理浴にアルミニウム合金板を所定時間浸漬し
て行う。また、前記処理浴にアルミニウム合金板を浸漬
させずに、前記処理浴をスプレー等によりアルミニウム
合金板の表面に吹き付け、そのアルミニウム合金板を水
洗した後乾燥させることによってクロメート処理を行っ
てもよい。Next, the case where the surface of the aluminum alloy plate is chromated will be described. The chromate treatment includes a phosphoric acid chromate treatment and a coating type chromate treatment. In the phosphoric acid chromate treatment, a phosphoric acid chromate treatment bath in which a compound such as phosphoric acid, chromic acid or hydrofluoric acid is dissolved in water so as to have a predetermined concentration is adjusted to a predetermined temperature, and an aluminum alloy plate is added to the treatment bath. For a predetermined time. Alternatively, the chromate treatment may be performed by spraying the treatment bath onto the surface of the aluminum alloy plate by spraying or the like without immersing the aluminum alloy plate in the treatment bath, washing the aluminum alloy plate with water, and then drying it.
【００２３】一方、塗布型クロメート処理では、先ずリ
ン酸、クロム酸、フッ酸又はポリアクリル酸等を所定の
濃度となるように水に溶解した塗布型クロメート処理浴
を、ロールコーティング法等によりアルミニウム合金板
の表面上に塗布して、所定の厚さの水膜を形成する。そ
の後、１００〜２００℃の温度で数秒間焼き付けること
により、水分を蒸発させて皮膜を形成してクロメート処
理を行う。On the other hand, in the coating type chromate treatment, first, a coating type chromate treatment bath in which phosphoric acid, chromic acid, hydrofluoric acid, polyacrylic acid or the like is dissolved in water so as to have a predetermined concentration is subjected to aluminum coating by a roll coating method or the like. It is applied on the surface of the alloy plate to form a water film having a predetermined thickness. Then, by baking at a temperature of 100 to 200 ° C. for several seconds, moisture is evaporated to form a film and chromate treatment is performed.
【００２４】このように、ポリエチレンオキシドの皮膜
を形成する前の下地処理として、アルミニウム合金板に
クロメート処理を施すことにより、アルミニウム合金板
と皮膜との界面の密着性をより一層向上させることがで
きるため、アルミニウム合金板の成形加工時における焼
付きの防止及び耐食性をより一層向上させることができ
る。As described above, by performing chromate treatment on the aluminum alloy plate as the base treatment before forming the polyethylene oxide film, the adhesion at the interface between the aluminum alloy plate and the film can be further improved. Therefore, it is possible to further prevent seizure and corrosion resistance during the forming process of the aluminum alloy plate.
【００２５】次に、ポリエチレンオキシドの分子量の限
定理由について説明する。Next, the reason for limiting the molecular weight of polyethylene oxide will be explained.
【００２６】分子量：５万乃至５００万 一般に、エチレンオキシドの重合体は、分子量が２万程
度までであるポリエチレングリコールと、数万以上であ
るポリエチレンオキシドとに分類される。分子量が５万
未満であるエチレンオキシド、即ちポリエチレングリコ
ール又は分子量の小さいポリエチレンオキシドを皮膜と
して使用する場合には、分子量が小さいため、十分な皮
膜を形成することができず、またその皮膜は強度が低く
脆いものとなってしまう。このため、このような皮膜が
形成されたアルミニウム合金板では、成形加工時に焼付
きが発生し易くなり、耐疵付き性も十分とはいえない。
また、吸湿性が高くなるため、皮膜の安定性は低下し、
耐食性も低下してしまう。 Molecular weight: 50,000 to 5,000,000 Generally, polymers of ethylene oxide are classified into polyethylene glycol having a molecular weight of up to about 20,000 and polyethylene oxide having a molecular weight of tens of thousands or more. When ethylene oxide having a molecular weight of less than 50,000, that is, polyethylene glycol or polyethylene oxide having a small molecular weight is used as a film, a sufficient film cannot be formed because the molecular weight is small, and the film has low strength. It becomes fragile. For this reason, an aluminum alloy sheet having such a coating is apt to cause seizure during the forming process, and the scratch resistance is not sufficient.
Also, since the hygroscopicity is high, the stability of the film is reduced,
Corrosion resistance is also reduced.
【００２７】一方、分子量が５００万を超えると、皮膜
を形成するための処理浴が低濃度であっても、溶液粘度
が高くなってしまう。このため、アルミニウム合金板の
表面に均一に皮膜を形成することが困難となり、また作
業性が低下してしまう。従って、ポリエチレンオキシド
の分子量は５万乃至５００万とする。On the other hand, when the molecular weight exceeds 5,000,000, the solution viscosity becomes high even if the treatment bath for forming the film has a low concentration. Therefore, it becomes difficult to form a uniform film on the surface of the aluminum alloy plate, and the workability is deteriorated. Therefore, the molecular weight of polyethylene oxide is 50,000 to 5,000,000.
【００２８】なお、皮膜の厚さは、０．１乃至１０μｍ
であることが好ましい。これは、厚さが０．１μｍ未満
であると、潤滑性、耐疵付き性及び耐食性の効果を十分
に得ることができず、また厚さが１０μｍを超えてもこ
れらの効果を更に向上させることはできず、製造コスト
を上昇させてしまうだけだからである。The thickness of the film is 0.1 to 10 μm.
It is preferred that This is because if the thickness is less than 0.1 μm, the effects of lubricity, scratch resistance and corrosion resistance cannot be sufficiently obtained, and if the thickness exceeds 10 μm, these effects are further improved. It is not possible to do so, it only increases the manufacturing cost.
【００２９】[0029]
【実施例】以下、本発明の実施例について、本発明の特
許請求の範囲から外れる比較例と比較して説明する。先
ず、材質が５０００系のＯ材で厚さが１ｍｍのアルミニ
ウム合金板を酸洗、脱脂及び水洗し十分に乾燥させた
後、下記表１に示す組成を有する皮膜を前記アルミニウ
ム合金板の表面に形成した。また、皮膜形成前にクロメ
ート処理を施した場合は下記表１の下地処理の欄に「有
り」と、クロメート処理を施さなかった場合は「なし」
と記載する。なお、比較例Ｎｏ２〜７の皮膜組成の欄で
記載したワックス及び樹脂の値の単位は重量％である。EXAMPLES Examples of the present invention will be described below in comparison with comparative examples that depart from the claims of the present invention. First, an aluminum alloy plate made of a 5000 series O material and having a thickness of 1 mm is pickled, degreased, washed with water and sufficiently dried, and then a coating having the composition shown in Table 1 below is formed on the surface of the aluminum alloy plate. Formed. In addition, if chromate treatment was applied before film formation, "Yes" in the column of base treatment in Table 1 below, "No" if chromate treatment was not applied
Enter. In addition, the unit of the value of the wax and the resin described in the column of the film composition of Comparative Examples Nos. 2 to 7 is% by weight.
【００３０】[0030]
【表１】 [Table 1]
【００３１】上記表１に示す表面処理が施された各アル
ミニウム合金板について、平板摺動試験、深絞り試験、
塗装性試験、耐食性試験並びに耐酸性及び耐アルカリ性
試験を、以下のような条件で行った。For each aluminum alloy plate subjected to the surface treatment shown in Table 1 above, a flat plate sliding test, a deep drawing test,
A paintability test, a corrosion resistance test, and an acid resistance and an alkali resistance test were conducted under the following conditions.
【００３２】平板摺動試験 図１は、平板摺動試験に使用する試験機の一部を示す模
式的断面図である。この図１に示すように、試験片の押
さえ部のダイス２ａ及び２ｂを接近させて、その間にア
ルミニウム合金板１を挟んだ。このとき、アルミニウム
合金板１にダイス２ａ及び２ｂで加圧力Ｐを印加しつ
つ、アルミニウム合金板１を白抜矢印の方向へ引き抜い
た。この場合の条件を下記表２に示す。 Flat Plate Sliding Test FIG. 1 is a schematic sectional view showing a part of a testing machine used for the flat plate sliding test. As shown in FIG. 1, the dies 2a and 2b of the pressing portion of the test piece were brought close to each other, and the aluminum alloy plate 1 was sandwiched therebetween. At this time, the aluminum alloy plate 1 was pulled out in the direction of the white arrow while applying the pressing force P to the aluminum alloy plate 1 with the dies 2a and 2b. The conditions in this case are shown in Table 2 below.
【００３３】[0033]
【表２】 [Table 2]
【００３４】そして、上記表２の条件でアルミニウム合
金板１を引き抜くときの引き抜き荷重Ｆを測定し、下記
数１により動摩擦係数μを算出して、この値により各ア
ルミニウム合金板の潤滑性を評価した。Then, the pulling load F when pulling out the aluminum alloy sheet 1 under the conditions of the above Table 2 is measured, the dynamic friction coefficient μ is calculated by the following equation 1, and the lubricity of each aluminum alloy sheet is evaluated by this value. did.
【００３５】[0035]
【数１】 動摩擦係数μ＝Ｆ（引き抜き荷重）／２Ｐ（加圧力）[Equation 1] Dynamic friction coefficient μ = F (drawing load) / 2P (pressing force)
【００３６】また、引き抜き後のアルミニウム合金板の
外観を目視観察して、焼付き状況及び耐疵付き性を調査
した。この場合、焼付きが発生しなかった場合、若干焼
付きが発生した場合及び著しい焼付きが発生した場合を
夫々「○」、「△」及び「×」とし、また疵が発生しな
かった場合、小さな疵が発生した場合及び大きな疵が発
生した場合を夫々「○」、「△」及び「×」として、下
記表４の焼付き状況及び耐疵付き性の欄に夫々示す。Further, the appearance of the aluminum alloy sheet after drawing was visually observed to examine the seizure state and the scratch resistance. In this case, when seizure did not occur, when slight seizure occurred or when significant seizure occurred, it was designated as "○", "△" and "x", respectively, and when no flaw occurred. The cases of small flaws and large flaws are shown as "○", "△" and "x" respectively in the column of seizure and flaw resistance in Table 4 below.
【００３７】深絞り試験 深絞り試験では、下記表３に示す条件で円筒深絞り試験
を行い、アルミニウム合金板の成形性を評価し、その結
果を下記表４に示す。なお、下記表４の円筒絞り高さに
示す値は、絞り試験で割れ又はしわ等の不具合が発生せ
ずに成形することができた最大の高さである。 Deep Drawing Test In the deep drawing test, a cylindrical deep drawing test was conducted under the conditions shown in Table 3 below to evaluate the formability of the aluminum alloy sheet, and the results are shown in Table 4 below. The value indicated by the cylindrical drawing height in Table 4 below is the maximum height that could be molded without causing defects such as cracks or wrinkles in the drawing test.
【００３８】[0038]
【表３】 [Table 3]
【００３９】塗装性試験 塗装性試験では、アルミニウム合金板に上塗り用塗料
（熱硬化型アミノアルキッド樹脂系塗料アミラック１０
００（白）：関西ペイント（株）製）を、塗装皮膜の厚
さが３０μｍとなるように塗装した。そして、碁盤目テ
ープ剥離試験にて上塗りした塗装性を評価した。この場
合、剥離がない場合を「○」、剥離部が１／１００〜１
０／１００の場合を「△」、剥離部が１０／１００より
多い場合には「×」として、その結果を下記表４に示
す。Paintability Test In the paintability test, an aluminum alloy plate was coated with a top coating (thermosetting amino alkyd resin-based coating, Amylak 10).
00 (white): Kansai Paint Co., Ltd. was applied so that the thickness of the coating film was 30 μm. Then, the coatability of the top coat was evaluated by a cross-cut tape peeling test. In this case, "○" means that there is no peeling, and the peeled portion is 1/100 to 1
The result is shown in Table 4 below, where 0/100 is “Δ”, and when the number of peeled parts is more than 10/100, “x”.
【００４０】耐食性試験 耐食性試験では、塩水噴霧試験方法（ＪＩＳ Ｚ２３７
１）を使用して、アルミニウム合金板に対して、１００
０時間の連続噴霧を行った。このときの腐食状況により
耐食性を評価し、その結果を下記表４にレイティングＮ
ｏで示す。Corrosion Resistance Test In the corrosion resistance test, a salt spray test method (JIS Z237) is used.
Using 1), 100 for aluminum alloy plate
A continuous spray of 0 hours was performed. Corrosion resistance was evaluated based on the corrosion state at this time, and the results are shown in Table 4 below.
Denote by o.
【００４１】耐酸性及び耐アルカリ性試験 耐酸性試験では、アルミニウム合金板を５％濃度のＨ2
ＳＯ4水溶液（室温）に２４時間浸漬し、一方耐アルカ
リ性試験では、０．５１％濃度のＮａＯＨ水溶液（室
温）に２４時間浸漬して、耐酸性及び耐アルカリ性を評
価した。この場合、アルミニウム合金板に変化がない場
合を「◎」、表面が若干白化し、素材に腐食がない場合
を「○」、表面が白化し、素材が若干腐食した場合を
「△」、素材の全面が腐食した場合を「×」として、下
記表４の耐酸化性及び耐アルカリ性の欄にその結果を示
す。 Acid Resistance and Alkali Resistance Test In the acid resistance test, an aluminum alloy plate was treated with H 2 at a concentration of 5%.
In the alkali resistance test, the sample was immersed in a SO 4 aqueous solution (room temperature) for 24 hours, while in a 0.51% NaOH aqueous solution (room temperature) for 24 hours, the acid resistance and the alkali resistance were evaluated. In this case, when there is no change in the aluminum alloy plate, it is "◎", when the surface is slightly whitened and the material is not corroded, it is "○", when the surface is whitened and the material is slightly corroded, "△" is the material The case where the entire surface is corroded is indicated by "x", and the results are shown in the column of oxidation resistance and alkali resistance in Table 4 below.
【００４２】[0042]
【表４】 [Table 4]
【００４３】上記表４に示すように、本発明の特許請求
の範囲内である実施例Ｎｏ１〜７については、動摩擦係
数はいずれも０．１以下と低く、潤滑性が優れており、
また円筒絞り高さはいずれも２４ｍｍ以上となり、成形
性が優れていることがわかる。また、高強度の皮膜が形
成されているため、焼付き及び疵は発生せず、形成され
た皮膜には塗装皮膜との密着性を阻害する潤滑剤が添加
されていないため、いずれの実施例も上塗り塗装性は良
好なものとなった。更に、耐食性の評価を示すレイティ
ングＮｏはいずれも９．８以上と、高い耐食性を有し、
耐酸性及び耐アルカリ性についても良好以上の結果とな
った。特に、皮膜を形成する前に下地処理としてクロメ
ート処理を施した実施例Ｎｏ２、３、５、６及び７の耐
酸性及び耐アルカリ性については、いずれも優れた結果
となった。As shown in Table 4 above, in Examples Nos. 1 to 7 within the scope of the claims of the present invention, the coefficient of dynamic friction is as low as 0.1 or less, and the lubricity is excellent.
Further, the height of the cylindrical drawing is 24 mm or more, which shows that the moldability is excellent. In addition, since a high-strength film is formed, seizure and flaws do not occur, and the formed film does not contain a lubricant that inhibits adhesion with the coating film. However, the top coatability was good. Furthermore, each of the rating numbers showing the evaluation of corrosion resistance is 9.8 or higher, and has high corrosion resistance.
The acid resistance and alkali resistance were also good or better. In particular, with respect to the acid resistance and alkali resistance of Examples Nos. 2, 3, 5, 6 and 7 in which chromate treatment was performed as the base treatment before forming the film, excellent results were obtained.
【００４４】次に、比較例について説明する。比較例Ｎ
ｏ１については、形成された皮膜がポリエチレングリコ
ールからなる皮膜であるため、十分な皮膜を形成するこ
とができず、また形成された皮膜は強度が低く脆いもの
であった。このため、潤滑性を向上させることができ
ず、成形性を十分に向上させることはできなかった。ま
た、皮膜の強度が低いため、焼付き及び疵が発生し、特
にアルミニウム合金板の表面に大きな疵が発生した。更
に、実施例と比べて耐食性、耐酸性及び耐アルカリ性に
ついていずれも劣ったものとなった。Next, a comparative example will be described. Comparative Example N
Regarding o1, since the formed film was a film made of polyethylene glycol, a sufficient film could not be formed, and the formed film had low strength and was brittle. Therefore, the lubricity cannot be improved, and the moldability cannot be sufficiently improved. In addition, since the strength of the film was low, seizure and flaws occurred, and particularly large flaws occurred on the surface of the aluminum alloy plate. Further, the corrosion resistance, acid resistance and alkali resistance were all inferior to those of the examples.
【００４５】比較例Ｎｏ２及び４については、形成され
た皮膜の潤滑剤の添加量が少ないため、潤滑性を向上さ
せることができず、成形性を十分に向上させることがで
きなかった。また、形成された皮膜は強度が不十分であ
ったため、焼付き及び疵が発生した。更に、皮膜の大部
分の成分であるウレタン樹脂は、酸に対する安定性が低
いため、特に耐酸性について実施例と比べて劣ったもの
となった。In Comparative Examples Nos. 2 and 4, since the amount of the lubricant added to the formed film was small, the lubricity could not be improved and the formability could not be sufficiently improved. In addition, since the formed film had insufficient strength, seizure and flaws occurred. Furthermore, since the urethane resin, which is a major component of the film, has low acid stability, it was inferior in acid resistance to the examples.
【００４６】比較例Ｎｏ３及び５については、形成され
た皮膜に潤滑剤が多く添加されていたため、潤滑性を向
上させることができ、成形性を向上させることはできた
が、皮膜の強度が不十分であったため、焼付き及び疵が
発生した。また、潤滑剤の添加量が多いため、上塗りし
た塗装皮膜との密着性が低下してしまった。更に、上述
した比較例Ｎｏ２又は４と同様に、耐酸性について実施
例と比べて劣ったものとなった。In Comparative Examples Nos. 3 and 5, since a large amount of lubricant was added to the formed film, the lubricity could be improved and the formability could be improved, but the film strength was not good. Since it was sufficient, seizure and flaws occurred. Also, since the amount of lubricant added was large, the adhesion with the top-coated coating film deteriorated. Further, similarly to Comparative Example No. 2 or 4, the acid resistance was inferior to that of the example.
【００４７】比較例Ｎｏ６及び７については、形成され
た皮膜に潤滑剤が多く添加されていたため、潤滑性を向
上させることができ、成形性を向上させることはできた
が、皮膜の強度が不十分であったため、焼付き及び疵が
発生した。また、潤滑剤の添加量が多いため、上塗りし
た塗装皮膜との密着性が低下してしまった。更に、皮膜
の大部分の成分であるエポキシ樹脂は、酸及びアルカリ
に対する安定性が低いため、耐酸性及び耐アルカリ性に
ついて実施例と比べて劣ったものとなった。In Comparative Examples Nos. 6 and 7, since a large amount of lubricant was added to the formed film, the lubricity could be improved and the formability could be improved, but the film strength was not good. Since it was sufficient, seizure and flaws occurred. Also, since the amount of lubricant added was large, the adhesion with the top-coated coating film deteriorated. Further, since the epoxy resin, which is a major component of the film, has low stability to acids and alkalis, the acid resistance and alkali resistance were inferior to those of the examples.
【００４８】比較例Ｎｏ８については、皮膜を形成せず
に低粘度油を塗油したため、潤滑性を向上させることが
できず、成形性を十分に向上させることができなかっ
た。また、焼付き及び疵が発生し、特にアルミニウム合
金板の表面に大きな疵が発生した。更に、油層の上から
塗装したため、その塗装性は極めて劣化し、また耐食
性、耐酸性及び耐アルカリ性についても実施例と比べて
極めて劣化したものとなった。In Comparative Example No. 8, since the low-viscosity oil was applied without forming a film, the lubricity could not be improved and the moldability could not be sufficiently improved. In addition, seizure and flaws were generated, and particularly large flaws were generated on the surface of the aluminum alloy plate. Further, since the oil layer was coated from above, the coating property was extremely deteriorated, and the corrosion resistance, acid resistance and alkali resistance were also extremely deteriorated as compared with the examples.
【００４９】比較例Ｎｏ９については、皮膜形成等の表
面処理を施していないため、潤滑性が極めて劣化し、成
形性も極めて劣化したものとなった。また、焼付き及び
疵が極めて大量に発生し、更に塗装性、耐食性、耐酸性
及び耐アルカリ性はいずれも実施例と比べて極めて劣っ
たものとなった。Since Comparative Example No. 9 was not subjected to surface treatment such as film formation, the lubricity was extremely deteriorated and the moldability was also extremely deteriorated. In addition, an extremely large amount of seizure and flaws were generated, and the paintability, corrosion resistance, acid resistance and alkali resistance were all inferior to those of the examples.
【００５０】[0050]
【発明の効果】以上説明したように、本発明によれば、
アルミニウム合金板の表面に所定量の平均分子量を有す
るポリエチレンオキシドの皮膜を形成することにより、
成形性が良好な潤滑性が優れたアルミニウム合金板を製
造することができる。また、前記皮膜は高強度であるた
め、焼付き及び疵が発生することを防止することがで
き、耐食性、耐酸性及び耐アルカリ性を向上させること
ができる。更に、前記皮膜には塗装皮膜との密着性を阻
害する潤滑剤が添加されていないため、上塗り塗装性を
向上させることができる。As described above, according to the present invention,
By forming a film of polyethylene oxide having a predetermined amount of average molecular weight on the surface of the aluminum alloy plate,
It is possible to manufacture an aluminum alloy plate having good formability and excellent lubricity. Further, since the film has high strength, it is possible to prevent the occurrence of seizure and flaws, and improve the corrosion resistance, the acid resistance and the alkali resistance. Furthermore, since a lubricant that inhibits the adhesion to the coating film is not added to the film, top coatability can be improved.
【００５１】また、前記皮膜を形成する前に下地処理と
して、アルミニウム合金板の表面にクロメート処理を施
すことにより、成形加工時における焼付きの発生をより
一層防止することができ、また耐食性もより一層向上さ
せることができる。By subjecting the surface of the aluminum alloy plate to a chromate treatment as a base treatment before forming the above-mentioned coating, it is possible to further prevent the occurrence of seizure during the forming process and also to improve the corrosion resistance. It can be further improved.
【図１】平板摺動試験に使用する試験機の一部を示す模
式的断面図である。FIG. 1 is a schematic cross-sectional view showing a part of a testing machine used for a flat plate sliding test.
１；アルミニウム合金板 ２ａ，２ｂ；ダイス 1; Aluminum alloy plate 2a, 2b; Die
Claims (2)
万であるポリエチレンオキシドの皮膜を有することを特
徴とする潤滑性が優れたアルミニウム合金板。1. The surface has an average molecular weight of 50,000 to 500.
An aluminum alloy plate with excellent lubricity characterized by having a polyethylene oxide film.
ることを特徴とする請求項１に記載の潤滑性が優れたア
ルミニウム合金板。2. The aluminum alloy plate with excellent lubricity according to claim 1, wherein the surface is subjected to chromate treatment.