JPH08322701A - Hanger - Google Patents

Abstract

PURPOSE: To permit effective use of resources and to make refuse disposal at an office safe and easy by using recycled paper made from paper, especially waste paper, for the main body of a hanger and covering the surface thereof by a hardening coating film. CONSTITUTION: A hanger body A is formed into a hanger with a thickness of 0.5 to 50mm by stamping paperboard made from mainly waste paper. Both sides 1, 2 are flat, and a continuous front outer part 3 and a rear outer part 4 are chamfered and rounded. Paperboard such as white paperboard and yellow paperboard or paperboard made by impregnating waste paper with starch, a synthetic adhesive and a melanin resin and pressing and heat-laminating a stack of the impregnated waste paper, is used for the hanger body A. To make the hanger body A deodorant, hard, water-resistant, and heat-resistant and to smoothen the surface thereof, a hardening resin coat is applied evenly. Furthermore, it is made recyclable by using a low solvent resistant hardening resin.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、主として衣料品等物流
段階において合成樹脂製ハンガーの代替品として使用さ
れるハンガーに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hanger mainly used as a substitute for a synthetic resin hanger in the distribution stage such as clothing.

【０００２】[0002]

【従来の技術】従来、衣料品卸メーカーの商品納品にお
いては、合成樹脂製ハンガーによる納品が行われたり、
ダンボールを打抜き使用されているものが知られてい
る。素材が合成樹脂の場合、射出成形、圧縮成形などの
方法によって製造されている。2. Description of the Related Art Conventionally, in the delivery of goods by a clothing wholesale manufacturer, a synthetic resin hanger is used for delivery.
It is known that punching out cardboard is used. When the material is synthetic resin, it is manufactured by a method such as injection molding or compression molding.

【０００３】[0003]

【発明が解決しようとする課題】従来の技術で述べたも
ののうち前者の合成樹脂で作られたハンガーにおいて
は、ある程度の量になると事業所でのゴミ処理が難し
い。そしてゴミとして回収後、行政等が合成樹脂製ハン
ガーを廃棄処分する場合、土中に埋めても腐らないし、
燃やすと有毒ガスを発生する危険が有ったり、高熱を発
してゴミ焼却炉を傷めるなど廃棄が難しく、コストの面
においてリサイクルの要請に応えることが、現段階にお
いては困難という問題点を有している。また、後者のダ
ンボールを人体の形に打抜いただけのハンガーにおいて
は、合成樹脂性のハンガーと違い、吊すことができない
為、ハンガーとしての機能を持たず、ただ納品の際、芯
として使用されているだけで商品物流には適さないとい
う問題点を有している。In the former hanger made of synthetic resin among those described in the prior art, it is difficult to dispose of dust at a business site when the amount is a certain amount. When the government disposes of the synthetic resin hanger after collecting it as garbage, it will not rot even if buried in the soil.
There is a problem that it is difficult at present to meet the recycling requirement in terms of cost because it is difficult to dispose of it, such as the risk of producing toxic gas when burned or the high temperature that damages the garbage incinerator. ing. Also, in the latter hanger that only punches the corrugated cardboard into the shape of a human body, unlike a synthetic resin hanger, it can not be hung, so it does not have the function as a hanger, but it is used as a core at the time of delivery. However, there is a problem in that it is not suitable for merchandise distribution just by being present.

【０００４】本発明は、このような従来の技術の有する
問題に鑑みてなされたものであり、その目的とするとこ
ろは、合成樹脂製ハンガーの商品物流に於ける特性生か
しつつ、本体に故紙を用いることにより資源の有効利用
が可能であり、事業所でのゴミ処理が簡単で、行政等が
廃棄処分する場合、安全かつ容易処理ができ、資源のリ
サイクルの要請に応えることができるハンガーを提供し
ようとするものである。The present invention has been made in view of the problems of the prior art as described above, and an object of the present invention is to use a waste paper in the main body while making the most of the characteristics in the product distribution of the synthetic resin hanger. Providing hangers that enable effective use of resources by using them, simple disposal of waste at business sites, safe and easy disposal when the government disposes of waste, and response to requests for resource recycling Is what you are trying to do.

【０００５】[0005]

【課題を解決するための手段】上記目的を達成するため
に、本発明におけるハンガーは、ハンガー本体に、紙、
特に故紙を原料とした再生紙を用いるもので、再生紙特
有の臭いを防ぎ、表面の滑らかさ、硬度、耐水性、酎熱
性を得るために硬化性樹脂を用い構成されている。In order to achieve the above object, a hanger according to the present invention comprises a hanger body, a paper,
In particular, recycled paper made from waste paper is used, and is composed of a curable resin in order to prevent odor peculiar to recycled paper and to obtain surface smoothness, hardness, water resistance, and shochu heat resistance.

【０００６】[0006]

【作用】本発明のハンガーは、合成樹脂を本体に一切使
用せず、本体に紙、特に故紙を原料とした再生紙を用い
ることにより故紙の有効利用が可能になる。また、事業
所でのゴミ処理が簡単で、行政等が廃棄処分する場合、
安全かつ容易に処理ができる。さらに再度のリサイクル
の要請に応えることができる。The hanger of the present invention does not use any synthetic resin in the main body, but can effectively use the waste paper by using paper, particularly recycled paper made from the waste paper, in the main body. In addition, if disposal of garbage at business sites is easy and the government disposes of it,
Safe and easy to process. Furthermore, it is possible to meet the request for recycling again.

【０００７】そして、硬化性樹脂被膜をハンガー全体に
均等に形成することにより、再生紙特有の臭いを防ぎ、
硬度、耐水性、耐熱性を得ることができる。また、紙の
繊維が表面に出てきにくく、表面の滑らかさを得ること
ができ外見的にも優れている構成が可能である。By forming the curable resin film evenly on the entire hanger, the odor peculiar to recycled paper is prevented,
Hardness, water resistance, and heat resistance can be obtained. In addition, the fibers of the paper are less likely to come out on the surface, and the smoothness of the surface can be obtained, so that a configuration excellent in appearance is possible.

【０００８】[0008]

【実施例】実施例について図面を参照して説明する。図
１〜図２において、ハンガー本体Ａは、故紙を主な原料
として作られた板紙を用い、その板紙を打抜き加工によ
り、厚み０．５〜５０ｍｍ程度の肉厚を有するハンガー
の形状に形成される。さらに詳しくは、両側面部１、２
は、板状であり、また連続している前面外側部３、後面
外側部４は、角を削り丸み帯びた形状を有している。ハ
ンガー本体Ａには、白板紙、黄板紙、チップボール、色
板紙等の市販の板紙を用いるか、または故紙に澱分、合
成接着剤及びメラミン樹脂等を含浸させ、重ねてプレス
し加熱積層した板紙を用いる。ハンガー本体Ａに、防臭
効果、硬度及び耐水性、耐熱性、表面を滑らかにする目
的で、硬化性樹脂被膜５を均等に被覆する。EXAMPLES Examples will be described with reference to the drawings. 1 to 2, the hanger body A is made of paperboard made mainly from waste paper, and is formed into a hanger shape having a wall thickness of about 0.5 to 50 mm by punching the paperboard. It More specifically, the side surface portions 1 and 2
Is a plate shape, and the front outer side portion 3 and the rear outer side portion 4 which are continuous have a shape with rounded corners. For the hanger body A, commercially available paperboard such as white paperboard, yellow paperboard, chip ball, and colored paperboard is used, or the waste paper is impregnated with starch, synthetic adhesive, melamine resin, etc., pressed and laminated by heating. Use paperboard. The hanger body A is evenly coated with a curable resin coating 5 for the purpose of deodorizing effect, hardness and water resistance, heat resistance, and smoothing the surface.

【０００９】図３において、ハンガー本体Ｂは、故紙に
澱分、合成接着剤またはメラミン樹脂等を含浸させた故
紙を、現在一般的に使用されているスーツハンガーと同
型の金型を用い、加熱圧縮成形しハンガーの形状に形成
される。ハンガー本体Ｂの上部６には、ハンガー本体Ｂ
の略中央の位置で上方に向けて突設した金属製フック７
で構成される。さらに詳しくは、ハンガー本体Ｂは、厚
み０．５〜１．５ｍｍ程度肉厚を有する。図４におい
て、右側面部８左側面部９は幅が最大４０〜８０ｍｍ
で、金属製フック７を中心に前方へ人体の肩のように湾
曲している。In FIG. 3, a hanger body B is made by heating a waste paper obtained by impregnating waste paper with a starch, a synthetic adhesive, a melamine resin or the like, using a mold of the same type as a suit hanger that is generally used at present. It is compression molded and formed into a hanger shape. On the upper part 6 of the hanger body B, the hanger body B
Metal hook 7 protruding upward at a position approximately in the center of
Composed of. More specifically, the hanger body B has a wall thickness of about 0.5 to 1.5 mm. In FIG. 4, the right side surface portion 8 and the left side surface portion 9 have a maximum width of 40 to 80 mm.
Then, it is curved forward around the metal hook 7 like a shoulder of a human body.

【００１０】また、図５において、ハンガー本体Ｂへの
金属製フック７を軸支固定を確実にする目的で、上部６
は１０〜４０ｍｍ程度厚みを形成されれている。またハ
ンガー本体Ｂに、防臭効果、硬度及び耐水性、耐熱性、
耐熱性、表面を滑らかにする目的で、硬化性樹脂被膜５
を均等に被覆する。Further, in FIG. 5, a metal hook 7 on the hanger body B is fixed to the upper portion 6 for the purpose of securely fixing the shaft support.
Has a thickness of about 10 to 40 mm. In addition, the hanger body B has a deodorant effect, hardness, water resistance, heat resistance,
Curable resin coating 5 for the purpose of heat resistance and smoothing the surface
Evenly.

【００１１】硬化性樹脂塗料の具体例としては、ポリウ
レタン樹脂系では、１液性のドリームクリヤー（カシュ
ー社商品名）に対して５〜５０重量％の範囲でドリーム
シンナー（カシュー社商品名）を加える。また同じ１液
性のウルトラック（大阪塗料株式会社商品名）に５〜５
５重量％の範囲でウルトラックシンナー（大阪塗料株式
会社商品名）を加える。ポリウレタン樹脂系では２液性
のストロンフレッシュＡ液、ストロンフレッシ９９Ｂ液
（いずれもカシュー社商品名）を２：１の比率で混合
し、５〜５０重量％の範囲で専用シンナーを加える。ま
た同じく２液性のストロンエースＡ液とストロン２４Ｂ
液（いずれもカシュー社商品名）を１：１の比率で混合
し、５〜５０重量％の範囲で専用シンナーを加える。エ
ポキシ樹脂系では、２液性のキコートトップクリアＡ液
とＢ液（古川塗料株式会社商品名）を１：１の比率で混
合し、溶剤としてメタノール１０〜４５重量％を用い
る。As a concrete example of the curable resin coating material, in the case of a polyurethane resin type, a dream thinner (trade name of cashew company) is used in a range of 5 to 50% by weight with respect to a one-liquid dream clear (trade name of cashew company). Add. In addition, 5-5 for the same one-pack ULTRAC (trade name of Osaka Paint Co., Ltd.)
Add ULTRACK thinner (trade name of Osaka Paint Co., Ltd.) in the range of 5% by weight. In the case of the polyurethane resin system, two-liquid Stron Fresh A liquid and Stron Fresh 99B liquid (both are trade names of Cashew Co., Ltd.) are mixed at a ratio of 2: 1, and a dedicated thinner is added in the range of 5 to 50% by weight. Also, two-component Stron Ace liquid A and Stron 24B
The liquids (both trade names of cashew company) are mixed at a ratio of 1: 1 and a dedicated thinner is added in the range of 5 to 50% by weight. In the epoxy resin system, two-component Kicoat Top Clear liquid A and liquid B (trade name of Furukawa Paint Co., Ltd.) are mixed at a ratio of 1: 1 and 10 to 45% by weight of methanol is used as a solvent.

【００１２】上記の方法によって混合して得られた硬化
性樹脂塗料は、原液のままでも使用できるが、ハンガー
本体の素材の浸透性の程度やハンガー本体に塗布する方
法、例えば刷毛塗り、浸漬法、スプレー法などに応じ
て、それぞれの硬化性樹脂に合ったシンナーやメタノー
ル等の溶剤を前記の範囲で加えて調合し、ハンガー本体
の上に硬化性樹脂塗料を上記の方法で塗り、それぞれの
硬化性樹脂の特性や調合の仕方で異なるが、１〜８時間
程度、自然乾燥させ、硬化性樹脂被膜５を形成する。な
お、以上にあげた硬化性樹脂塗料は一例であり、再利用
のために耐溶剤性が弱く、しかも剛性、耐水性、耐熱
性、無毒性の硬化性樹脂を使用できることは勿論ある。The curable resin paint obtained by mixing by the above method can be used as it is as a stock solution, but the penetrability of the material of the hanger body and the method of applying to the hanger body, for example, brush coating and dipping method. Depending on the spray method, etc., a solvent such as thinner or methanol suitable for each curable resin is added and mixed in the above range, and the curable resin paint is applied on the hanger body by the above method, Although it depends on the characteristics of the curable resin and the method of preparation, it is naturally dried for about 1 to 8 hours to form the curable resin film 5. The above-mentioned curable resin coating materials are merely examples, and needless to say, a curable resin having weak solvent resistance for reuse and having rigidity, water resistance, heat resistance and non-toxicity can be used.

【００１３】[0013]

【発明の効果】本発明は、上述のとうり構成されている
ので、次に記載する効果を奏する。Since the present invention is constructed as described above, it has the following effects.

【００１４】請求項１のハンガーにおいては、原料に紙
を使用しているので事業所内でのゴミ処理が簡単で、行
政等の廃棄処分も安全かつ容易に行え、資源のリサイク
ルの要請に応えることができる。According to the hanger of claim 1, since paper is used as a raw material, it is easy to dispose of the waste in the business site, and the disposal by the government can be safely and easily performed, and the request for resource recycling can be met. You can

【００１５】請求項２のハンガーにおいては、故紙を原
料とした再生紙を用いるので資源の有効利用が可能であ
る。In the hanger of the second aspect, since recycled paper made from waste paper is used, resources can be effectively used.

【００１６】請求項３のハンガーにおいて、ハンガー本
体の表面を硬化性樹脂被膜で被覆させたことにより、再
生紙特有の臭いを防ぎ、硬度、耐水性、耐熱性、紙の繊
維が表面に出て来にくく、表面の滑らかさを得ることが
でき外見的にも優れている。さらに、耐溶剤性が弱い硬
化性樹脂を選択することでリサイクルが可能である。In the hanger of claim 3, by covering the surface of the hanger body with a curable resin film, the odor peculiar to recycled paper is prevented, and hardness, water resistance, heat resistance, and paper fibers are exposed on the surface. It is hard to come by, and the smoothness of the surface can be obtained, and it is also excellent in appearance. Furthermore, recycling is possible by selecting a curable resin having weak solvent resistance.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明に係るハンガーＡの全体斜視図である。FIG. 1 is an overall perspective view of a hanger A according to the present invention.

【図２】本発明に係るハンガーＡ図１のＣからＣの矢視
断面図である。FIG. 2 is a cross-sectional view taken along the line C to C in FIG.

【図３】本発明に係るハンガーＢの全体斜視図である。FIG. 3 is an overall perspective view of a hanger B according to the present invention.

【図４】本発明に係るハンガーＢを上から見た状態を示
す斜視図である。FIG. 4 is a perspective view showing a state in which the hanger B according to the present invention is viewed from above.

【図５】本発明に係るハンガーＢ図３上部のＤからＤの
矢視断面図である。5 is a cross-sectional view of the hanger B according to the present invention taken along the line D to D in the upper portion of FIG.

【符号の説明】[Explanation of symbols]

Ａ ハンガー本体 Ｂ ハンガー本体 １ 側面部 ２ 側面部 ３ 前面外側部 ４ 後面外側部 ５ 硬化性樹脂被膜 ６ 上部 ７ フック ８ 右側面部 ９ 左側面部 A Hanger main body B Hanger main body 1 Side part 2 Side part 3 Front outside part 4 Rear outside part 5 Curable resin coating 6 Upper part 7 Hook 8 Right side part 9 Left side part

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 ハンガー本体の材料が紙であって、澱粉
及び合成接着剤で硬化させてなるハンガー。1. A hanger in which the material of the hanger body is paper, which is cured with starch and a synthetic adhesive. 【請求項２】 ハンガー本体の材料が故紙である請求項
１記載のハンガー。2. The hanger according to claim 1, wherein the material of the hanger body is waste paper. 【請求項３】 ハンガー本体の表面を硬化性樹脂被膜で
被覆させてなる請求項１記載のハンガー。3. The hanger according to claim 1, wherein the surface of the hanger body is covered with a curable resin film.