JPH08322409A - Member for culturing algae - Google Patents
Member for culturing algaeInfo
- Publication number
- JPH08322409A JPH08322409A JP15222395A JP15222395A JPH08322409A JP H08322409 A JPH08322409 A JP H08322409A JP 15222395 A JP15222395 A JP 15222395A JP 15222395 A JP15222395 A JP 15222395A JP H08322409 A JPH08322409 A JP H08322409A
- Authority
- JP
- Japan
- Prior art keywords
- gel
- rope
- algae culture
- algae
- culture member
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ワカメなどの藻類を養
殖するために用いられる藻類養殖用部材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an algae culture member used for culturing algae such as seaweed.
【０００２】[0002]
【従来の技術】藻類の胞子を付着させる種糸は、直径3m
m ，長さ20〜50mm程度のタコ糸である。この種糸は、始
めは100m程度の長さであり、多数の胞子を含む海水に浸
すことにより胞子を付着させた後、短く切断したもので
ある。このようにして得られた種糸を直径10〜20mm程度
の太いロープに挟んで、海中に設置することにより、藻
類の養殖が行われている。このロープ等は、現在では一
般的な合成樹脂から形成されている。2. Description of the Related Art Seed threads for attaching algae spores have a diameter of 3 m.
It is an octopus thread with m and a length of 20 to 50 mm. This seed thread has a length of about 100 m at the beginning, and is soaked in seawater containing many spores to attach the spores and then cut into short pieces. Algae are cultivated by sandwiching the thus obtained seed yarn between thick ropes with a diameter of about 10 to 20 mm and installing it in the sea. These ropes and the like are currently made of general synthetic resins.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来技
術では、ロープ等の回収の手間が煩雑であるとともに、
ロープ等が流失すると海洋汚染が生ずるという問題があ
った。However, in the prior art, it is troublesome to collect ropes and the like, and
There was a problem that marine pollution would occur if ropes were washed away.
【０００４】[0004]
【発明の目的】そこで、本発明の目的は、回収の手間を
省けるとともに、海洋汚染も防げる藻類養殖用部材を提
供することにある。SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a member for algae cultivation which can save the trouble of recovery and prevent marine pollution.
【０００５】[0005]
【課題を解決するための手段】本発明に係る藻類養殖用
部材は、分解性樹脂からなるロープと、このロープに被
装されるとともに膨潤性及び分解性を呈するゲルとを備
えたものである。ここでいう「ロープ」には、種糸や、
網を構成するロープ等も含まれる。また、前記ゲルは例
えば光架橋型ポリビニルアルコールであり、前記ゲルに
吸水性高分子の粒子を分散させてもよい。A member for algae culture according to the present invention comprises a rope made of a degradable resin and a gel which is covered with the rope and exhibits swelling and degrading properties. . The "rope" referred to here includes seed yarn,
It also includes ropes that make up the net. Further, the gel is, for example, photocrosslinking polyvinyl alcohol, and particles of a water-absorbing polymer may be dispersed in the gel.
【０００６】ここでいう「藻類」には、ワカメ，コン
ブ，ホンダワラ等の隠花植物の他に、アマモ，コアマモ
等の顕花植物も含むものとする。顕花植物の場合は、
「胞子」を「種子」と言い換えるものとする。また、こ
こでいう「分解性樹脂」とは、自然環境の中で分解・消
滅する樹脂をいい、具体的には生分解性，水溶性等を呈
する樹脂をいう。生分解性樹脂としては、ポリ（ヒド
ロキシブチレート／ヒドロキシバリレート）コポリマー
等の微生物生産型、ポリエチレンサクシネート，ポリ
ブチレンサクシネート，ポリカプロラクトン等の石油合
成型、ポリ−Ｌ乳酸等の植物合成型、澱粉＋ポリビ
ニルアルコール等の天然高分子型、等がある。水溶性樹
脂としては、ポリビニルアルコール，セルロース系ポリ
マー，紙，粘土等がある。[0006] The term "algae" as used herein includes flowering plants such as eelgrass and koala, as well as hidden flowering plants such as wakame, kelp, and straw. For flowering plants,
“Spores” is to be reworded as “seed”. The term "degradable resin" as used herein refers to a resin that decomposes and disappears in a natural environment, and specifically refers to a resin that exhibits biodegradability, water solubility, and the like. Biodegradable resins include microbial production type such as poly (hydroxybutyrate / hydroxyvalerate) copolymer, petroleum synthetic type such as polyethylene succinate, polybutylene succinate and polycaprolactone, plant synthetic type such as poly-L lactic acid. , Starch + polyvinyl alcohol and other natural polymer types, and the like. Examples of the water-soluble resin include polyvinyl alcohol, cellulosic polymers, paper, and clay.
【０００７】[0007]
【作用】請求項１記載の藻類養殖用部材の作用は、次の
とおりである。まず、この藻類養殖用部材を船から海中
に設置する。このときは、ロープに被装されたゲルがま
だ膨潤していない。そのため、藻類養殖用部材が軽くか
つ嵩張らないので、設置作業は容易である。海中に設置
されると、ゲルが膨潤することにより、ゲルの部分の体
積が増大する。しばらくして、ゲル等に付着している胞
子が成長を続けて、仮根がゲルに付着する。このとき、
ゲルの表面積は十分に大きくなっているので、仮根はゲ
ルに強固に付着する。一般に、仮根の付着力は、付着面
積が大きい程、大きいからである。これにより、ロープ
は、仮根を付着させる必要がなくなるので、十分に細く
できる。その後、藻類養殖用部材は、その分解性に起因
して崩壊又は消滅する。The operation of the member for algae culture according to claim 1 is as follows. First, this algae culture member is installed in the sea from a ship. At this time, the gel coated on the rope has not swollen yet. Therefore, since the algae culture member is light and not bulky, the installation work is easy. When placed in the sea, the volume of the gel part increases due to the swelling of the gel. After a while, the spores attached to the gel and the like continue to grow and the roots attach to the gel. At this time,
The surface area of the gel is large enough that the roots adhere firmly to the gel. This is because, in general, the adhesion force of the temporary root increases as the adhesion area increases. As a result, the rope can be made sufficiently thin because it is not necessary to attach a temporary root. After that, the algae culture member collapses or disappears due to its degradability.
【０００８】請求項２記載の藻類養殖用部材の作用は、
次のとおりである。光架橋型ポリビニルアルコールは、
透光性を有する。したがって、藻類養殖用部材のゲルが
光架橋型ポリビニルアルコールであれば、藻類の成長に
必要な日光がゲルによって遮られない。The action of the algae culture member according to claim 2 is as follows:
It is as follows. The photocrosslinkable polyvinyl alcohol is
Has translucency. Therefore, if the gel of the algae culture member is a photocrosslinking type polyvinyl alcohol, the sunlight necessary for the growth of algae is not blocked by the gel.
【０００９】請求項３記載の藻類養殖用部材の作用は、
次のとおりである。藻類養殖用部材のゲルに吸水性高分
子の粒子が分散しているので、膨潤した吸水性高分子の
粒子が、膨潤したゲルの表面に凹凸を形成する。したが
って、仮根の付着するゲルの表面積が増大するととも
に、仮根がゲルの表面の凹凸に絡み付く。The action of the algae culture member according to claim 3 is:
It is as follows. Since the water-absorbent polymer particles are dispersed in the gel of the algae culture member, the swollen water-absorbent polymer particles form irregularities on the surface of the swollen gel. Therefore, the surface area of the gel to which the temporary root adheres increases, and the temporary root becomes entangled with the irregularities on the surface of the gel.
【００１０】[0010]
【実施例】図１及び図２は本発明に係る藻類養殖用部材
の第一実施例を示し、図１が斜視図、図２が図１におけ
るII−II線縦断面図である。以下、これらの図面に基づ
き説明する。1 and 2 show a first embodiment of a member for algae culture according to the present invention. FIG. 1 is a perspective view and FIG. 2 is a vertical sectional view taken along line II-II in FIG. Hereinafter, description will be given with reference to these drawings.
【００１１】藻類養殖用部材１０は、分解性樹脂からな
るロープ１２と、ロープ１２に被装されるとともに膨潤
性及び分解性を呈するゲル１４とを備えたものである。
また、ゲル１４は、光架橋型ポリビニルアルコールであ
り、円筒状に膨潤した状態を図示している。ロープ１２
は、単線でも撚り線でもよい。藻類養殖用部材１０は、
短く切って網，他のロープ等の任意の位置に取付ける
か、又はそのまま使用する。The algae culture member 10 comprises a rope 12 made of a degradable resin, and a gel 14 which is covered with the rope 12 and exhibits swelling and degrading properties.
Further, the gel 14 is a photocrosslinking type polyvinyl alcohol, and shows a state in which it swells in a cylindrical shape. Rope 12
May be a single wire or a stranded wire. The algae culture member 10 is
Cut it short and attach it to any position such as a net or other rope, or use it as it is.
【００１２】図３乃至図５は光架橋型ポリビニルアルコ
ールの構造・性質を示し、図３は分子構造及び光架橋反
応を示す説明図、図４は膨潤の状態を示す説明図、図５
は架橋率と膨潤度との関係を示すグラフである。以下、
これらの図面に基づき説明する。3 to 5 show the structure / property of the photocrosslinking polyvinyl alcohol, FIG. 3 is an explanatory view showing the molecular structure and the photocrosslinking reaction, and FIG. 4 is an explanatory view showing the swelling state.
Is a graph showing the relationship between the crosslinking rate and the swelling degree. Less than,
A description will be given based on these drawings.
【００１３】光架橋型ポリビニルアルコールは、水溶性
のポリビニルアルコール（ＰＶＡ）に、光感応基のスチ
リルピリジニウム（ＳｂＱ）を導入したもの（以下「Ｐ
ＶＡ−ＳｂＱ」という。）であり、270 〜450nm の波長
の光を照射すると、二量化してゲルとなる。このゲル
は、網目構造になっており、水を吸収して体積が増加す
るという膨潤性を呈する。膨潤度は、架橋率が増加する
に従って減少する性質があり、最大で200 倍程度であ
る。The photocrosslinkable polyvinyl alcohol is a water-soluble polyvinyl alcohol (PVA) into which a photosensitive group styrylpyridinium (SbQ) is introduced (hereinafter referred to as “P”).
VA-SbQ ". When irradiated with light having a wavelength of 270 to 450 nm, it dimerizes into a gel. This gel has a network structure and exhibits swelling property by absorbing water and increasing in volume. The degree of swelling has the property of decreasing as the crosslinking rate increases, and is up to about 200 times.
【００１４】次に、図１乃至図５に基づき、藻類養殖用
部材１０の製造方法を説明する。Next, a method for manufacturing the algae culture member 10 will be described with reference to FIGS. 1 to 5.
【００１５】ロープ１２の材質となる分解性樹脂として
は、水流に対して十分な強度を有する、ポリカプロラク
トン（商品名「トーン」：日本ユニカー株式会社），脂
肪族ポリエステル（商品名「ビオノーレ」：昭和高分子
株式会社），ポリ−Ｌ乳酸（商品名「ラクティ」：島津
製作所株式会社）等が好ましい。これらの分解性樹脂か
らロープ１２を製造する方法は、一般の合成樹脂からロ
ープを製造する方法と同様であるので、説明を省略す
る。As the degradable resin used as the material of the rope 12, polycaprolactone (trade name "Tone": Nippon Unicar Co., Ltd.) and aliphatic polyester (trade name "Bionore": having sufficient strength against water flow): Showa High Polymer Co., Ltd.), poly-L-lactic acid (trade name "Lacty": Shimadzu Corporation) and the like are preferable. The method for manufacturing the rope 12 from these degradable resins is the same as the method for manufacturing the rope from general synthetic resins, and thus the description thereof is omitted.
【００１６】ロープ１２の直径φ１は、一年程度で分解
・消滅させるためには、分解性樹脂の種類にもよるが、
3mm 程度とすることが好ましい。また、直径φ１は、次
の観点からできるだけ細いことが好ましい。重量及び
専有体積を減少させて、作業性を向上させる。分解性
樹脂は一般の合成樹脂に比べて単価が高いことから、で
きるだけ低価格にする。The diameter φ1 of the rope 12 depends on the type of degradable resin in order to disintegrate and eliminate it in about one year.
It is preferably about 3 mm. Further, the diameter φ1 is preferably as thin as possible from the following viewpoint. Improve workability by reducing weight and occupied volume. Since the decomposable resin has a higher unit price than general synthetic resins, the price should be kept as low as possible.
【００１７】ゲル１４をロープ１２に被装する方法につ
いて述べる。まず、ロープ１２に、未架橋状態にある10
％重量濃度のＰＶＡ−ＳｂＱ水溶液（光感応基導入量1.
31mol ％，ケン化率88％）を、塗布する。塗布方法は、
例えば浸漬，刷毛塗り，ローラ塗り等である。続いて、
ＰＶＡ−ＳｂＱ水溶液を塗布したロープ１２に、にキセ
ノンアークランプの光を照射し、ＰＶＡ−ＳｂＱ水溶液
をゲル化する。また、この光照射の前又は後に、乾燥工
程が設けられる。こうして、藻類養殖用部材１０が完成
する。A method for covering the rope 12 with the gel 14 will be described. First, the rope 12 has 10
% Weight concentration of PVA-SbQ aqueous solution (amount of photosensitive group introduced 1.
31 mol%, saponification rate 88%). The application method is
For example, dipping, brush coating, roller coating and the like. continue,
The rope 12 coated with the PVA-SbQ aqueous solution is irradiated with light from a xenon arc lamp to gelate the PVA-SbQ aqueous solution. A drying step is provided before or after this light irradiation. Thus, the algae culture member 10 is completed.
【００１８】また、ゲル１４は、ロープ１２の全体に被
装してもよいが、藻類の過密を避けるために、本実施例
のようにロープ１２の一部に一定間隔で被装することが
望ましい。この一定間隔は、藻類の成長に最も適した密
度にするためのものであって、藻類の種類によって異な
る。例えばワカメの場合は、好ましくは30〜200cm 、よ
り好ましくは50〜90cmである。さらに、ゲル１４の外径
φ２は、藻類の仮根が水流によって剥がされないように
するために、従来のロープの直径と同じように少なくと
も10mm程度が必要となる。The gel 14 may be applied to the entire rope 12, but in order to avoid overcrowding of algae, a part of the rope 12 may be applied at regular intervals as in this embodiment. desirable. This fixed interval is for achieving the density most suitable for the growth of algae, and varies depending on the type of algae. For example, in the case of wakame seaweed, the length is preferably 30 to 200 cm, more preferably 50 to 90 cm. Further, the outer diameter φ2 of the gel 14 needs to be at least about 10 mm, which is the same as the diameter of a conventional rope, in order to prevent the algal roots from being peeled off by the water flow.
【００１９】次に、図１に基づき、藻類養殖用部材１０
の作用を説明する。Next, based on FIG. 1, the member 10 for algae culture.
The operation of will be described.
【００２０】まず、人工採苗の場合は、多数の胞子を含
む海水に藻類養殖用部材１０を浸すことにより、藻類養
殖用部材１０に胞子を付着させる。なお、当然ながら、
天然採苗の場合は、このような処理は不要である。続い
て、作業者が、藻類養殖用部材１０を船で沖合まで運
び、藻類養殖用部材１０を海中に設置する。このとき
は、ロープ１２に被装されたゲル１４がまだ膨潤してい
ない。そのため、藻類養殖用部材１０が軽くかつ嵩張ら
ないので、設置作業は容易である。海中に設置される
と、長くても一日でゲル１４が膨潤する。しばらくし
て、ゲル１４等に付着している胞子（図示せず）が成長
を続けて、仮根（図示せず）がゲル１４に付着する。こ
のとき、ゲル１４の表面積は十分に大きくなっているの
で、仮根はゲル１４に強固に付着する。一般に、仮根の
付着力は、付着面積が大きい程、大きいからである。こ
れにより、ロープ１２は、仮根を付着させる必要がなく
なるので、十分に細くできる。また、ロープ１２が細く
なることにより、ロープ１２に繁殖する雑藻類も低減で
きる。その後、藻類養殖用部材１０は、その分解性に起
因して崩壊又は消滅するので、回収の手間が不要であ
り、しかも自然環境を汚染することもない。First, in the case of artificial seedling, spores are attached to the algae culture member 10 by immersing the algae culture member 10 in seawater containing many spores. Of course,
In the case of natural seedling, such treatment is unnecessary. Subsequently, the worker carries the algae culture member 10 by ship to the offshore and installs the algae culture member 10 in the sea. At this time, the gel 14 coated on the rope 12 has not swollen yet. Therefore, since the algae culture member 10 is light and not bulky, the installation work is easy. When installed in the sea, the gel 14 swells in one day at the longest. After a while, spores (not shown) attached to the gel 14 and the like continue to grow, and temporary roots (not shown) attach to the gel 14. At this time, since the surface area of the gel 14 is sufficiently large, the temporary root firmly adheres to the gel 14. This is because, in general, the adhesion force of the temporary root increases as the adhesion area increases. As a result, the rope 12 can be made sufficiently thin because it is not necessary to attach a temporary root. Further, by making the rope 12 thin, it is possible to reduce the algae that propagate on the rope 12. After that, the algae culture member 10 disintegrates or disappears due to its degradability, so that the trouble of recovery is unnecessary and the natural environment is not polluted.
【００２１】また、ゲル１４は、光架橋型ポリビニルア
ルコールからなるので、透光性を有する。したがって、
ゲル１４が藻類の成長に必要な日光を遮らないので、藻
類の成長が促進される。また、光架橋型ポリビニルアル
コールは、完全な水溶液であるので、生体に有害な有機
溶媒等を含まない。そのため、ゲル１４は胞子の付着を
阻害しない。しかも、ゲル１４は、膨潤した網目に仮根
がよく絡まるので、従来のロープ等に比べて、はるかに
仮根の付着性がよい。Since the gel 14 is made of photocrosslinking polyvinyl alcohol, it has translucency. Therefore,
Algae growth is promoted because the gel 14 does not block the sunlight needed for algae growth. Moreover, since the photocrosslinking polyvinyl alcohol is a complete aqueous solution, it does not contain an organic solvent or the like which is harmful to the living body. Therefore, the gel 14 does not inhibit the attachment of spores. Moreover, in the gel 14, since the tentative roots are well entangled in the swollen mesh, the adhesiveness of the tentative roots is far better than that of a conventional rope or the like.
【００２２】図６乃至図８は本発明に係る藻類養殖用部
材の第二実施例を示し、図６が斜視図、図７が胞子の成
長した段階における斜視図、図８が図７におけるVIII−
VIII線縦断面図である。以下、これらの図面に基づき説
明する。ただし、図１と同一部分は同一符号を付すこと
により重複説明を省略する。FIGS. 6 to 8 show a second embodiment of the algae culture member according to the present invention. FIG. 6 is a perspective view, FIG. 7 is a perspective view at the stage when spores have grown, and FIG. 8 is VIII in FIG. −
FIG. 8 is a vertical sectional view taken along line VIII. Hereinafter, description will be given with reference to these drawings. However, the same parts as those in FIG.
【００２３】藻類養殖用部材２０は、分解性樹脂からな
るロープ１２と、ロープ１２に被装されるとともに膨潤
性及び分解性を呈するゲル１４と、ゲル１４に分散した
吸水性高分子の粒子２２とを備えたものである。ゲル１
４及び粒子２２は、膨潤後の状態を図示している。The algae culture member 20 includes a rope 12 made of a degradable resin, a gel 14 that is covered with the rope 12 and exhibits swelling and degrading properties, and particles 22 of a water-absorbing polymer dispersed in the gel 14. It is equipped with and. Gel 1
4 and particles 22 show the state after swelling.
【００２４】粒子２２を構成する吸水性高分子は、例え
ば、ポリアクリル酸ナトリウム，ポリアクリル酸でんぷ
ん等である。藻類養殖用部材２０の製造方法は、膨潤し
ていない粒子２２を前述のＰＶＡ−ＳｂＱ水溶液に混合
して，ロープ１２に塗布する点を除き、藻類養殖用部材
１０と同じである。The water-absorbing polymer forming the particles 22 is, for example, sodium polyacrylate, polyacrylic acid starch or the like. The method for manufacturing the algae culture member 20 is the same as the algae culture member 10 except that the unswelled particles 22 are mixed with the above-described PVA-SbQ aqueous solution and applied to the rope 12.
【００２５】次に、藻類養殖用部材２０の作用を説明す
る。ゲル１４に吸水性高分子の粒子２２が分散している
ので、膨潤した粒子２２が、膨潤したゲル１４の表面に
凹凸を形成する。これにより、仮根Ｒの付着するゲル１
４の表面積が増大するとともに、仮根Ｒがゲル１４の表
面の凹凸に絡み付くので、仮根Ｒの付着性を向上でき
る。Next, the operation of the algae culture member 20 will be described. Since the water-absorbent polymer particles 22 are dispersed in the gel 14, the swollen particles 22 form irregularities on the surface of the swollen gel 14. As a result, the gel 1 to which the temporary root R adheres
As the surface area of No. 4 is increased and the temporary root R is entangled with the irregularities on the surface of the gel 14, the adhesion of the temporary root R can be improved.
【００２６】図９は、本発明に係る藻類養殖用部材の第
三実施例を示す斜視図である。以下、この図面に基づき
説明する。FIG. 9 is a perspective view showing a third embodiment of the algae culture member according to the present invention. Hereinafter, description will be given with reference to this drawing.
【００２７】藻類養殖用部材３０は、分解性樹脂からな
る長いロープ（図示せず）の全体に、膨潤性及び分解性
を呈するゲル３２を被装し、短く切断したものである。
また、藻類養殖用部材３０は、網を構成するロープ部３
４等に結んだり（図９〔イ〕）、ロープ部３４等にクリ
ップ３６で固定したり（図９〔ロ〕）して使用する。藻
類養殖用部材３０よれば、ロープの全体をＰＶＡ−Ｓｂ
Ｑ水溶液に浸漬する等の簡単な方法により、製造を容易
化できる。The algae culture member 30 is a long rope (not shown) made of a degradable resin, which is covered with a gel 32 exhibiting swelling and degrading properties and cut into short pieces.
Further, the algae culture member 30 is a rope portion 3 that constitutes a net.
It is used by tying it to 4 or the like (FIG. 9 [a]) or fixing it to the rope portion 34 or the like with a clip 36 (FIG. 9 [b]). According to the algae culture member 30, the entire rope is PVA-Sb.
Manufacturing can be facilitated by a simple method such as immersing in a Q aqueous solution.
【００２８】図１０は、本発明に係る藻類養殖用部材の
第四実施例を示す斜視図である。以下、この図面に基づ
き説明する。FIG. 10 is a perspective view showing a fourth embodiment of the algae culture member according to the present invention. Hereinafter, description will be given with reference to this drawing.
【００２９】藻類養殖用部材４０は、分解性樹脂からな
る短いロープ４２の両端に、膨潤性及び分解性を呈する
ゲル４４を被装したものである。また、藻類養殖用部材
４０は、網を構成するロープ部３４等に結んで使用す
る。藻類養殖用部材４０によれば、ゲル４４が膨潤して
ロープ４２のゆるみ止めとして作用するので、網等から
の脱落を防止できる。The algae culture member 40 comprises a short rope 42 made of a degradable resin, and both ends of which are covered with a gel 44 exhibiting swelling and degrading properties. Further, the algae culture member 40 is used by being tied to the rope portion 34 or the like forming the net. According to the algae culture member 40, the gel 44 swells and acts as a loosening stopper for the rope 42, so that the rope 44 can be prevented from falling off from the net or the like.
【００３０】図１１は本発明に係る藻類養殖用部材の第
五実施例を示す斜視図であり、図１１〔イ〕はゲルの外
観、図１１〔ロ〕は膨潤前、図１１〔ハ〕は膨潤後をそ
れぞれ示している。以下、これらの図面に基づき説明す
る。FIG. 11 is a perspective view showing a fifth embodiment of the algae culture member according to the present invention. FIG. 11 (a) shows the appearance of the gel, FIG. 11 (b) shows before swelling, and FIG. 11 (c). Indicates after swelling. Hereinafter, description will be given with reference to these drawings.
【００３１】藻類養殖用部材５０は、分解性樹脂からな
るロープ５２に、膨潤性及び分解性を呈する板状のゲル
５４を被装したものである。また、藻類養殖用部材５０
は、ロープ５２にゲル５４を巻いて、これらを網を構成
するロープ部３４等にクリップ３６で固定して使用す
る。藻類養殖用部材５０によれば、ロープ５２にＰＶＡ
−ＳｂＱ水溶液を塗布する工程が不要となるので、製造
を容易化できる。The algae culture member 50 comprises a rope 52 made of a degradable resin and a plate-like gel 54 having a swelling property and a degrading property. Also, the algae culture member 50
Is used by winding the gel 54 around the rope 52 and fixing them with the clip 36 to the rope portion 34 or the like forming the net. According to the algae culture member 50, the PVA is attached to the rope 52.
Since the step of applying the -SbQ aqueous solution is unnecessary, the manufacturing can be facilitated.
【００３２】なお、本発明は、いうまでもないが、上記
第一乃至第五実施例に限定されるものではない。例え
ば、ゲルは、光架橋型ポリビニルアルコールにポリアク
リル酸ナトリウム，ポリアクリル酸でんぷん等を混合し
たものとしてもよい。この場合は、光架橋型ポリビニル
アルコールのみの場合と比べて、膨潤度が増加するが、
強度が若干低下する。具体例をあげれば、膨潤度が５〜
50倍程度の光架橋型ポリビニルアルコールに、ポリアク
リル酸ナトリウム又はポリアクリル酸でんぷんを0.1 〜
50重量％添加すると、膨潤度が10〜1000倍程度に増加す
る。Needless to say, the present invention is not limited to the above first to fifth embodiments. For example, the gel may be a mixture of photocrosslinking polyvinyl alcohol with sodium polyacrylate, polyacrylic starch, or the like. In this case, the swelling degree is increased as compared with the case of only the photocrosslinking polyvinyl alcohol,
The strength is slightly reduced. For example, the degree of swelling is 5
About 50 times as much photocrosslinkable polyvinyl alcohol, sodium polyacrylate or polyacrylic starch
When 50% by weight is added, the degree of swelling increases 10 to 1000 times.
【００３３】[0033]
【発明の効果】請求項１記載の藻類養殖用部材によれ
ば、分解性樹脂からなるロープと、このロープに被装さ
れるとともに膨潤性及び分解性を呈するゲルとを備えた
ので、時間とともに崩壊又は消滅することにより、回収
の手間を不要にできるとともに、自然環境の汚染を防止
できる。しかも、藻類養殖用部材を海中に設置する際に
は、ゲルがまだ膨潤していないことから、膨潤後のゲル
の外径と同じ太さの従来のロープ等に比べて、軽くかつ
嵩張らないので、作業性を向上できる。さらに、海中に
設置されるとゲルが膨潤することにより、仮根の付着す
る面積が十分に大きくなるので、仮根はゲルに強固に付
着する。これにより、ロープに仮根を付着させる必要が
なくなるので、ロープを十分に細くできる。したがっ
て、より作業性を向上できるとともに、低価格化を図る
ことかできる。EFFECTS OF THE INVENTION According to the algae culture member of the first aspect, since the rope made of a degradable resin and the gel which is covered with the rope and exhibits swelling and degrading properties are provided, By disintegrating or disappearing, it is possible to eliminate the trouble of collection and prevent pollution of the natural environment. Moreover, since the gel is not swollen when the algae culture member is installed in the sea, it is lighter and less bulky than conventional ropes having the same thickness as the outer diameter of the swollen gel. The workability can be improved. Furthermore, when the gel is swelled in the sea, the gel swells, so that the area on which the root attaches becomes sufficiently large, so that the root firmly attaches to the gel. This eliminates the need to attach a temporary root to the rope, so that the rope can be made sufficiently thin. Therefore, the workability can be further improved and the price can be reduced.
【００３４】請求項２記載の藻類養殖用部材によれば、
ゲルを光架橋型ポリビニルアルコールとしたので、藻類
の成長に必要な日光がゲルによって遮られないことによ
り、藻類の成長をより促進できる。According to the algae culture member of claim 2,
Since the gel is photocrosslinkable polyvinyl alcohol, the algae can be further promoted because the sunlight necessary for the algae growth is not blocked by the gel.
【００３５】請求項３記載の藻類養殖用部材によれば、
ゲルに吸水性高分子の粒子が分散しているので、膨潤し
た吸水性高分子の粒子が、膨潤したゲルの表面に凹凸を
形成する。したがって、仮根の付着するゲルの表面積が
増大するとともに、仮根がゲルの表面の凹凸に絡み付く
ので、仮根の付着性をより向上できる。According to the member for algae culture of claim 3,
Since the water-absorbent polymer particles are dispersed in the gel, the swollen water-absorbent polymer particles form irregularities on the surface of the swollen gel. Therefore, the surface area of the gel to which the root adheres is increased, and the root is entangled with the irregularities on the surface of the gel, so that the adhesion of the root can be further improved.
【図１】本発明に係る藻類養殖用部材の第一実施例を示
す斜視図である。FIG. 1 is a perspective view showing a first embodiment of a member for algae culture according to the present invention.
【図２】図１におけるII−II線縦断面図である。FIG. 2 is a vertical sectional view taken along line II-II in FIG.
【図３】光架橋型ポリビニルアルコールの分子構造及び
光架橋反応を示す説明図である。FIG. 3 is an explanatory view showing a molecular structure of photocrosslinking-type polyvinyl alcohol and a photocrosslinking reaction.
【図４】光架橋型ポリビニルアルコールの膨潤の状態を
示す説明図である。FIG. 4 is an explanatory diagram showing a swelling state of photocrosslinking polyvinyl alcohol.
【図５】光架橋型ポリビニルアルコールの架橋率と膨潤
度との関係を示すグラフである。FIG. 5 is a graph showing the relationship between the degree of crosslinking and the degree of swelling of photocrosslinkable polyvinyl alcohol.
【図６】本発明に係る藻類養殖用部材の第二実施例を示
す斜視図である。FIG. 6 is a perspective view showing a second embodiment of the algae culture member according to the present invention.
【図７】図６の藻類養殖用部材における胞子の成長した
段階を示す斜視図である。7 is a perspective view showing a stage where spores have grown in the algae culture member of FIG.
【図８】図７におけるVIII−VIII線縦断面図である。8 is a vertical cross-sectional view taken along the line VIII-VIII in FIG.
【図９】本発明に係る藻類養殖用部材の第三実施例を示
し、図９〔イ〕が網を構成するロープ部等に結んだ状
態、図９〔ロ〕が網を構成するロープ部等にクリップで
固定した状態である。FIG. 9 shows a third embodiment of the algae culture member according to the present invention, in which FIG. 9 (a) is in a state of being tied to a rope portion constituting a net, and FIG. 9 (b) is a rope portion constituting a net. It is in a state of being fixed to the etc. with a clip.
【図１０】本発明に係る藻類養殖用部材の第四実施例を
示す斜視図である。FIG. 10 is a perspective view showing a fourth embodiment of the algae culture member according to the present invention.
【図１１】本発明に係る藻類養殖用部材の第五実施例を
示す斜視図であり、図１１〔イ〕はゲルの外観、図１１
〔ロ〕は膨潤前、図１１〔ハ〕は膨潤後をそれぞれ示し
ている。FIG. 11 is a perspective view showing a fifth embodiment of a member for algae culture according to the present invention, FIG.
[B] shows before swelling, and FIG. 11C shows after swelling.
１０，２０，３０，４０，５０ 藻類養殖用部材 １２，４２，５２ ロープ １４，３２，４４，５４ ゲル 10, 20, 30, 40, 50 Algae culture member 12, 42, 52 Rope 14, 32, 44, 54 Gel
Claims (3)
プに被装されるとともに膨潤性及び分解性を呈するゲル
とを備えた藻類養殖用部材。1. An algae culture member comprising a rope made of a degradable resin and a gel which is covered with the rope and exhibits swelling and degrading properties.
ルであることを特徴とする請求項１記載の藻類養殖用部
材。2. The algae culture member according to claim 1, wherein the gel is photocrosslinking polyvinyl alcohol.
せたことを特徴とする請求項１記載の藻類養殖用部材。3. The algae culture member according to claim 1, wherein particles of a water-absorbent polymer are dispersed in the gel.