JPH08315101A - Information recording medium - Google Patents

Abstract

PURPOSE: To easily generate characteristic information and also form a magnetic pattern which has large variation in intensity by varying the distribution and orientation of magnetic particles in a binder and fixing the magnetic particles in a characteristic state in that state while bringing the binder into a solid phase state. CONSTITUTION: A microcapsule layer (1st information recording layer) 13 provided on one surface of a base material 11 has many microcapsules 20 dispersed in the binder. The microcapsules 20 are constituted by capsuling core substances consisting principally of a suspending agent made of a binder containing plural magnetic particles. This binder is in the solid-phase state at room temperature (10-35 deg.C) and is a liquid-phase state above the room temperature (40-80 deg.C). In the microcapsule layer 13, magnetic characteristic information is recorded which is specified with the orientation of the magnetic particles and can not be discriminated visibly. This information is read out as an output waveform by a magnetic head, etc., and recorded on a digital information recording part (2nd information recording part) 12 on the other surface of the base material 11.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】この発明は、定期券、入場券、プ
リペイドカード、クレジットカード、キャッシュカー
ド、各種有価証券、身分証明書等のＩＤカードなどに用
いられる情報記録媒体に係り、特に、偽造あるいは改ざ
んされた情報記録媒体の使用を防止する技術に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an information recording medium used for ID cards such as commuter tickets, entrance tickets, prepaid cards, credit cards, cash cards, various securities, and identification cards, and in particular, forgery. Or, it relates to a technique for preventing the use of a falsified information recording medium.

【０００２】[0002]

【従来の技術】近年、カード式の情報記録媒体が普及し
つつあり、このような情報記録媒体は、磁気記録等を書
き込むことができる情報記録部を有している。情報記録
部には、その利用対象に応じた様々な情報が磁気ヘッド
などの書込手段によって書き込まれ、書き込まれた情報
は磁気ヘッド等によって読み取られるようになってい
る。書き込まれる情報としては、例えば、情報記録媒体
自体のＩＤ情報、情報記録媒体の保持者の情報、あるい
は金銭に関する情報などがある。このような情報記録媒
体の使用に際しては、情報記録媒体が正当なものである
のか、さらに、その使用者が使用にあたって正当権限を
有するのかについても判別し、情報記録媒体の悪用を防
止する必要性が高まってきている。2. Description of the Related Art In recent years, a card type information recording medium has become widespread, and such an information recording medium has an information recording section in which magnetic recording or the like can be written. Various information according to the usage target is written in the information recording unit by a writing unit such as a magnetic head, and the written information is read by the magnetic head or the like. The information to be written includes, for example, the ID information of the information recording medium itself, the information of the holder of the information recording medium, or the information about money. When using such an information recording medium, it is necessary to determine whether the information recording medium is legitimate and whether the user has the right to use the information recording medium to prevent misuse of the information recording medium. Is increasing.

【０００３】そこで、悪用防止のための対策のうち、情
報記録媒体が偽造ないしは変造されたものか否かを判別
するたに、以下のような種々の技術が開発されている。
たとえば、情報記録部を高い保磁力を有する材料で構成
したり、情報記録部に磁気シールドを設けることによ
り、磁気情報を簡単に変更することができないようにし
た情報記録媒体が知られている。また、情報記録媒体に
当該情報記録媒体が正当なものであることを示す情報を
記録したマークを設け、そのマークの記録を読み取るよ
うにした技術も知られている。たとえば、マークに所定
の光を照射すると特定の波長の光を反射して真正である
ことが判るようにした情報記録媒体や、マークに真正な
情報記録媒体であることを示す磁気情報を記録する技術
が知られている。あるいは、特殊インキによって情報記
録媒体にマーキングし、特殊な装置によってマーキング
を検出するようにした技術、あるいは、所定箇所にレー
ザー光を照射すると真正品であることを示すホログラム
が発生するようにした技術などが知られている。Therefore, in order to determine whether or not the information recording medium is forged or altered, among the measures for preventing abuse, the following various techniques have been developed.
For example, there is known an information recording medium in which magnetic information cannot be easily changed by forming the information recording portion with a material having a high coercive force or providing a magnetic shield in the information recording portion. There is also known a technique in which an information recording medium is provided with a mark recording information indicating that the information recording medium is valid, and the recording of the mark is read. For example, when a mark is irradiated with a predetermined light, an information recording medium that reflects the light of a specific wavelength and is found to be authentic, or a mark is recorded with magnetic information indicating that the mark is an authentic information recording medium. The technology is known. Alternatively, a technology for marking an information recording medium with special ink and detecting the marking with a special device, or a technology for generating a hologram indicating that it is a genuine product when a predetermined portion is irradiated with laser light. Are known.

【０００４】また、情報記録媒体を使用する者が正当な
権限を有するか否かについては、使用者が暗唱番号を知
っているか否かにより、あるいは、情報記録媒体のサイ
ンパネルに記された署名と使用者のサインとを照合する
ことにより確認するようにしている。Further, whether or not the person who uses the information recording medium has the proper authority depends on whether or not the user knows the password, or the signature written on the signature panel of the information recording medium. The user's signature is checked against the user's signature.

【０００５】ところで、上記した情報記録媒体の正当性
を確認する技術をもってしても、現在では確実とはいえ
なくなってきているのが現状である。そこで、特表昭６
３ー５０１２５０号公報では、書類中にステンレス等の
金属ファイバを不均一に分布させて真偽判定情報を記録
し、この書類にマイクロ波を照射して真偽を判定する技
術が提案されている。この提案に係る技術では、金属フ
ァイバにおいて反射された応答マイクロ波束を一定のル
ールの下にデジタル信号に変換し、そのデジタル信号を
示すマークを当該書類に予め記録するようにしている。
そして、書類の真偽は、書類にマイクロ波を照射すると
ともに、反射した応答マイクロ波束を真偽判定情報とし
て受信し、この真偽判定情報をマークにして記録された
デジタル信号と照合することにより行うようにしてい
る。By the way, at present, even with the technique of confirming the validity of the information recording medium, it cannot be said to be reliable at present. Therefore, special table Sho 6
Japanese Laid-Open Patent Publication No. 3-501250 proposes a technique in which metal fibers such as stainless steel are nonuniformly distributed in a document to record authenticity determination information, and the document is irradiated with a microwave to determine authenticity. . In the technique according to this proposal, the response microwave flux reflected by the metal fiber is converted into a digital signal under a certain rule, and a mark indicating the digital signal is recorded in advance in the document.
The authenticity of the document is determined by irradiating the document with microwaves, receiving the reflected response microwave flux as authenticity determination information, and comparing the authenticity determination information with the recorded digital signal as a mark. I am trying to do it.

【０００６】しかしながら、上記提案された技術では、
金属ファイバを書類に分散しなければならないため、加
工が困難で製造コストが割高になるばかりでなく、マイ
クロ波の送受信装置も大型化、複雑化するという問題が
ある。さらに、マイクロ波がギガヘルツ帯のものである
ためその制御が困難であることに加えて、受信した応答
マイクロ波束のばらつきに起因する読取誤差が大きいた
め、応答マイクロ波束と記録されたデジタル信号との整
合性の判定が不正確となり、結局のところ、情報記録媒
体の真偽判定が不正確なために実用性に問題があった。However, in the above proposed technique,
Since the metal fibers have to be dispersed in the document, there is a problem that not only the processing is difficult and the manufacturing cost is high, but also the microwave transmitter / receiver becomes large and complicated. Furthermore, because the microwave is in the GHz band, it is difficult to control it, and since the reading error due to the variation in the received response microwave flux is large, the response microwave flux and the recorded digital signal are The determination of the consistency becomes inaccurate, and, after all, the authenticity determination of the information recording medium is inaccurate, which causes a problem in practicality.

【０００７】そこで、本発明者等は、真偽判定情報の記
録方法につき種々の検討を行った結果、マイクロ波を反
射する金属ファイバに代えて、磁性材料を情報記録媒体
中に不均一に分散させることを考えた。その方法として
具体的には以下のような構成を例示することができる。 情報記録媒体に磁性金属ファイバーを分散させること
により、マイクロ波を用いなくて済むようにする。 磁性金属ファイバーに代えて、磁性材料を充填した高
分子繊維を用いる。 磁性を有するインキを用いて不均一な磁気パターンを
情報記録媒体に印刷または転写するか、あるいはインク
ジェットや静電印刷の手法により印字する。 磁性粒子を不均一に分散させた磁性塗料を情報記録媒
体に印刷、コーティングあるいは転写等の方法により付
着させる。 上記において、磁性粒子および磁性粒子よりも大き
い平均粒径を有する非磁性粒子を塗料に分散させること
により、磁性粒子の不均一性を確保する。Therefore, as a result of various investigations on the method of recording the authenticity determination information, the present inventors have found that a magnetic material is unevenly dispersed in an information recording medium instead of a metal fiber that reflects microwaves. I thought to let you. Specifically, the following configurations can be exemplified as the method. Dispersing the magnetic metal fibers in the information recording medium eliminates the need for using microwaves. Polymer fibers filled with a magnetic material are used instead of the magnetic metal fibers. A non-uniform magnetic pattern is printed or transferred onto an information recording medium using an ink having magnetism, or is printed by a method such as inkjet or electrostatic printing. A magnetic coating material in which magnetic particles are non-uniformly dispersed is attached to an information recording medium by a method such as printing, coating or transfer. In the above, the non-uniformity of the magnetic particles is ensured by dispersing the magnetic particles and the non-magnetic particles having an average particle size larger than that of the magnetic particles in the coating material.

【０００８】[0008]

【発明が解決しようとする課題】しかしながら、上記
〜に対しては以下のような検討課題がそれぞれ存在す
る。においては、金属ファイバを使用するため、上記
提案に係る技術と同等の問題を依然として含んでいる。
すなわち、金属ファイバが高価であるとともにその切断
加工が容易ではなく、所望の長さに切断するための切断
工具の費用が割高になる。また、金属ファイバを分散さ
せた媒体を所定の大きさに加工する際に、金属ファイバ
がバリやヒゲとなって現出し、加工不良を生じ易い。However, there are the following examination subjects for the above items (1) to (3). In the above, since the metal fiber is used, the same problems as those of the above-mentioned proposed technique are still included.
That is, the metal fiber is expensive and the cutting process is not easy, and the cost of the cutting tool for cutting to a desired length is relatively high. Further, when the medium in which the metal fibers are dispersed is processed into a predetermined size, the metal fibers appear as burrs and whiskers, and processing defects are likely to occur.

【０００９】においては、磁性材料を充填した高分子
繊維を製造するには大がかりな設備を要するため、一度
に生産する量が大量になって小ロットの場合に製造コス
トが割高になる。[0009] In the above, since a large amount of equipment is required to produce the polymer fiber filled with the magnetic material, a large amount is produced at one time, and the production cost becomes high in the case of a small lot.

【００１０】においては、製造コストは比較的割安で
はあるものの、インキにより形成した磁気パターンが盛
り上がってしまうため、その磁気パターンを外部から容
易に判別できてしまう。また、印刷などによって磁気パ
ターンを設ける場合には、複数の情報記録媒の磁気パタ
ーンが互いに同一になってしまうことがある。In the above, although the manufacturing cost is relatively low, since the magnetic pattern formed by the ink rises, the magnetic pattern can be easily discriminated from the outside. Further, when the magnetic patterns are provided by printing or the like, the magnetic patterns of the plurality of information recording media may be the same.

【００１１】においては、製造コストは比較的安価で
あり、外部から磁気パターンを容易に判別することがで
きない等の利点はあるが、磁性塗料中に磁性粒子に不均
一に分散させる方法では、その不均一な状態を制御する
ことが難しい。また、単に磁性粒子を不均一に分散させ
る方法では、その不均一に基づく磁気ムラの強弱の程度
が小さいため、それから得られる磁気信号が弱くＳ／Ｎ
比が小さい。また、においても、大きな平均粒径を有
する非磁性粒子を塗料に分散させて磁性粒子を不均一に
分散させるものであるから、の場合と同様の利点と欠
点とを有している。In the above method, the manufacturing cost is relatively low and there is an advantage that the magnetic pattern cannot be easily discriminated from the outside. However, in the method in which the magnetic particles are dispersed non-uniformly in the magnetic paint, It is difficult to control the non-uniform state. Further, in the method in which the magnetic particles are simply dispersed inhomogeneously, the intensity of the magnetic unevenness due to the inhomogeneity is small, so the magnetic signal obtained therefrom is weak and the S / N ratio is small.
The ratio is small. Further, also in the above, since the non-magnetic particles having a large average particle diameter are dispersed in the coating material to disperse the magnetic particles in a non-uniform manner, it has the same advantages and disadvantages as in the above case.

【００１２】以上のように、本発明者等による改善策は
種々の課題を有している。よって、本発明は、以下の特
徴を有する情報記録媒体を提供することを目的とする。 製造コストが割安で容易に製造することができる。 真偽判定情報となる磁気パターンを外部から容易に判
別できず、偽造および変造に対する安全性が高い。 真偽判定情報を比較的簡単な装置で容易に読み取るこ
とができる。 磁気パターンの不均一状態を容易に制御することがで
きる。 磁気パターンの不均一の強弱の程度を大きくしてＳ／
Ｎ比を大きくすることができる。As described above, the improvement measures by the present inventors have various problems. Therefore, an object of the present invention is to provide an information recording medium having the following features. The manufacturing cost is low and it can be easily manufactured. The magnetic pattern serving as the authenticity determination information cannot be easily discriminated from the outside, and the security against forgery and alteration is high. The authenticity determination information can be easily read by a relatively simple device. The non-uniform state of the magnetic pattern can be easily controlled. Increase the degree of non-uniformity of the magnetic pattern to increase S /
The N ratio can be increased.

【００１３】[0013]

【課題を解決するための手段】請求項１に記載の情報記
録媒体は、磁性粒子をバインダー中に分散させ、上記磁
性粒子を上記バインダー中で固定することにより、上記
磁性粒子の分布及び配向のうち少なくともいずれか一つ
を固有情報とした第１の情報記録部と、上記固有情報に
よって得られた磁気情報を記録する第２の情報記録部と
を備え、上記バインダーを、所定条件で液相状態と固相
状態のいずれかの状態となる樹脂で構成したことを特徴
としている。The information recording medium according to claim 1, wherein the magnetic particles are dispersed in a binder, and the magnetic particles are fixed in the binder, whereby the distribution and orientation of the magnetic particles can be improved. A first information recording section having at least one of them as unique information, and a second information recording section for recording magnetic information obtained by the unique information are provided, and the binder is liquid phase under predetermined conditions. It is characterized in that it is made of a resin that is in either a solid state or a solid state.

【００１４】請求項２に記載の情報記録媒体は、請求項
１に記載の特徴に加え、前記磁性粒子の分布及び配向の
うち少なくともいずれか一つにランダムな変化を設けた
ことを特徴としている。The information recording medium according to a second aspect is characterized in that, in addition to the features according to the first aspect, at least one of distribution and orientation of the magnetic particles is provided with a random change. .

【００１５】請求項３に記載の情報記録媒体は、請求項
１または２に記載の特徴に加え、前記バインダーの融点
が３５〜１５０゜Ｃであることを特徴としている。The information recording medium described in claim 3 is characterized in that, in addition to the characteristics described in claim 1 or 2, the melting point of the binder is 35 to 150 ° C.

【００１６】請求項４に記載の情報記録媒体は、請求項
１ないし３のいずれかに記載の特徴に加え、前記バイン
ダーをマイクロカプセル内に設けるとともに、同マイク
ロカプセルを前記第１の情報記録部に分散させたことを
特徴としている。The information recording medium according to a fourth aspect of the present invention is the feature of any one of the first to third aspects of the present invention, in which the binder is provided in a microcapsule and the microcapsule has the first information recording section. It is characterized by being dispersed in.

【００１７】請求項５に記載の情報記録媒体は、請求項
４に記載の特徴に加え、前記マイクロカプセルの平均粒
径が１０〜１００μｍであることを特徴としている。The information recording medium described in claim 5 is characterized in that, in addition to the characteristics described in claim 4, the microcapsules have an average particle diameter of 10 to 100 μm.

【００１８】請求項６に記載の情報記録媒体は、請求項
１ないし５のいずれかに記載の特徴に加え、前記磁性粒
子が６０ Ｏｅ以下の保磁力を有することを特徴として
いる。An information recording medium according to a sixth aspect is characterized in that, in addition to the features according to any of the first to fifth aspects, the magnetic particles have a coercive force of 60 Oe or less.

【００１９】請求項７に記載の情報記録媒体は、請求項
１ないし６のいずれかに記載の特徴に加え、前記磁性粒
子が鱗片状をなすとともにその平均粒径が５〜８０μｍ
であることを特徴としている。An information recording medium according to a seventh aspect of the present invention has the features of any one of the first to sixth aspects, and the magnetic particles are scaly and have an average particle size of 5 to 80 μm.
It is characterized by being.

【００２０】請求項８に記載の情報記録媒体は、請求項
１ないし７のいずれかに記載の特徴に加え、前記第１の
情報記録部の表面に保護層を設けたことを特徴としてい
る。An information recording medium described in claim 8 is characterized in that, in addition to the features described in any one of claims 1 to 7, a protective layer is provided on the surface of the first information recording portion.

【００２１】[0021]

【作用】請求項１に記載の情報記録媒体においては、バ
インダーが液相状態のときに適当な処理を施してバイン
ダー内の磁性粒子の分布や配向を変化させ、その状態で
バインダーを固相状態にすることにより、磁性粒子を当
該情報記録媒体に固有の状態で固定することができる。
よって、簡単に固有情報を形成することができるととも
に、磁性粒子の分布や配向の程度を適宜設定することに
よって、強弱の大きな磁気パターンを形成することが可
能となる。また、バインダーを再び液相状態とすること
により、第１の情報記録部の固有情報情報を変更するこ
とができ、情報記録媒体として繰り返し利用することが
できる。In the information recording medium according to claim 1, when the binder is in a liquid phase state, appropriate treatment is applied to change the distribution and orientation of the magnetic particles in the binder, and in that state, the binder is in a solid phase state. By this, the magnetic particles can be fixed in a state peculiar to the information recording medium.
Therefore, the unique information can be easily formed, and by setting the distribution and orientation of the magnetic particles appropriately, it is possible to form a strong and weak magnetic pattern. Further, by bringing the binder into the liquid phase state again, the unique information information of the first information recording section can be changed and can be repeatedly used as an information recording medium.

【００２２】請求項２に記載の情報記録媒体において
は、磁性粒子により形成される磁気パターンがランダム
であるため、その磁気パターンは当該情報記録媒体に唯
一固有のものとなる。よって、磁気パターンの偽造が極
めて困難となる。また、請求項３に記載の情報記録媒体
においては、バインダーの融点が３５〜１５０゜Ｃであ
るから、通常の使用状態では固相状態が維持される。さ
らに、請求項４に記載の情報記録媒体では、磁性粒子を
分散させたバインダーをマイクロカプセル内に設けてい
るから、磁性粒子の磁気パターンを外部から容易に解読
することができない。In the information recording medium according to the second aspect, since the magnetic pattern formed by the magnetic particles is random, the magnetic pattern is unique to the information recording medium. Therefore, it is extremely difficult to forge the magnetic pattern. Further, in the information recording medium according to the third aspect, since the melting point of the binder is 35 to 150 ° C., the solid state is maintained in the normal use state. Further, in the information recording medium according to the fourth aspect, since the binder in which the magnetic particles are dispersed is provided in the microcapsule, the magnetic pattern of the magnetic particles cannot be easily read from the outside.

【００２３】[0023]

【実施例】【Example】

Ａ．第１実施例 （１）情報記録媒体の構成 以下、図１ないし図７を参照して本発明の第１実施例に
ついて説明する。図２（Ａ）は第１実施例の情報記録媒
体１０を示す側断面図、同図（Ｂ）は平面図である。図
において符号１１は基材である。基材１１は、強度のあ
る紙や合成紙、ＰＥＴ（ポリエチレンテレフタレー
ト）、ポリ塩化ビニル、ポリエステル、ポリカーボネー
ト、ポリメタクリル酸メチル、ポリスチレン、ポリ乳
酸、ポリカプロラクトン、ポリ（３ヒドロキシブチレー
ト−３ヒドロキシヴァリレート）、ポリビニルアルコー
ル等の合成樹脂類、天然樹脂類、金属、セラミックス等
を単独または組み合わせた複合体として用いることがで
きる。そして、このような基材１１の一方の面には、マ
イクロカプセル層（第１の情報記録層）１３が設けらて
いる。A. First Embodiment (1) Configuration of Information Recording Medium Hereinafter, a first embodiment of the present invention will be described with reference to FIGS. 1 to 7. FIG. 2A is a side sectional view showing the information recording medium 10 of the first embodiment, and FIG. 2B is a plan view. In the figure, reference numeral 11 is a base material. The base material 11 is made of strong paper or synthetic paper, PET (polyethylene terephthalate), polyvinyl chloride, polyester, polycarbonate, polymethylmethacrylate, polystyrene, polylactic acid, polycaprolactone, poly (3hydroxybutyrate-3hydroxyvarie). Rate), synthetic resins such as polyvinyl alcohol, natural resins, metals, ceramics, etc., or a combination of them. A microcapsule layer (first information recording layer) 13 is provided on one surface of the base material 11.

【００２４】マイクロカプセル層１３は、バインダー中
に多数のマイクロカプセル２０を分散させて構成されて
いる。なお、マイクロカプセル２０の分散状態は本実施
例では均一であるが、不均一であっても良い。また、バ
インダー中には、必要に応じて分散剤、消泡剤、重合剤
等を添加することができる。The microcapsule layer 13 is composed of a large number of microcapsules 20 dispersed in a binder. Although the dispersed state of the microcapsules 20 is uniform in this embodiment, it may be nonuniform. In addition, a dispersant, a defoaming agent, a polymerizing agent and the like can be added to the binder, if necessary.

【００２５】図１（Ａ）はマイクロカプセル２０を示す
拡大断面図であり、この図に示すように、マイクロカプ
セル２０は、複数の磁性粒子２２…を含有したバインダ
ー２３からなる懸濁剤を主成分とした芯物質を、ポリマ
ー等から構成された殻２１によってカプセル化して構成
されている。FIG. 1A is an enlarged cross-sectional view showing a microcapsule 20. As shown in this figure, the microcapsule 20 mainly contains a suspension agent composed of a binder 23 containing a plurality of magnetic particles 22. The core substance as a component is encapsulated by a shell 21 made of a polymer or the like.

【００２６】磁性粒子２２は、γ−フェライト、マグネ
タイト、Ｍｎフェライト、Ｍｎ−Ｚｎフェライト、Ｃｏ
被着γ−フェライト等の各種酸化鉄、Ｎｉ、Ｆｅ等の結
晶質単体金属、パーマロイ（Ｎｉ−Ｆｅ）等の結晶質合
金、ＦｅＮｉＢ、ＦｅＣｏ等の非結晶質合金等の何れで
も本発明に使用することができる。また、磁性粒子と有
機溶媒等との親和性を高めるために、高級エステル処
理、シランカップリング処理、チタネート系カップリン
グ処理を施しておくことが望ましい。The magnetic particles 22 are γ-ferrite, magnetite, Mn ferrite, Mn-Zn ferrite, Co.
Any of various types of iron oxide such as deposited γ-ferrite, crystalline single metals such as Ni and Fe, crystalline alloys such as permalloy (Ni-Fe), and amorphous alloys such as FeNiB and FeCo are used in the present invention. can do. Further, in order to enhance the affinity between the magnetic particles and the organic solvent, it is desirable to carry out a higher ester treatment, a silane coupling treatment, and a titanate coupling treatment.

【００２７】磁性粒子２２の保磁力は、軟質磁性材料の
範囲（６０ Ｏｅ以下）、半硬質磁性材料の範囲（６０
〜２０００ Ｏｅ）、硬質磁性材料の範囲（２０００ Ｏ
ｅ以上）に分かれるが、どのような保磁力であっても使
用可能である。ただし、磁性粒子２２の保磁力が６０
Ｏｅ以下の場合には、後述する方法で情報記録媒体１０
に記録した磁気パターンを容易に解読することができな
くなる。また、磁気パターンを形成するに際して磁性粒
子２２を着磁する必要がなく、しかも、低いバイアス磁
界でも磁気パターンに基づく磁気データを読み取ること
ができる。The coercive force of the magnetic particles 22 is in the range of the soft magnetic material (60 Oe or less) and in the range of the semi-hard magnetic material (60
~ 2000 Oe), range of hard magnetic materials (2000 Oe)
However, any coercive force can be used. However, the coercive force of the magnetic particles 22 is 60
In the case of less than Oe, the information recording medium 10
It becomes impossible to easily decipher the magnetic pattern recorded in. Further, it is not necessary to magnetize the magnetic particles 22 when forming the magnetic pattern, and magnetic data based on the magnetic pattern can be read even with a low bias magnetic field.

【００２８】磁性粒子２２の形状は、球状、片状、針状
など任意であり、また、いずれかの形状に特定されなく
てもよい。強いていえば、厚さが薄く平らな鱗片状（フ
レーク状）を使用した場合には、読み出した磁気データ
のＳ／Ｎ比が良いためにこの形状のものが好適に用いら
れる。The shape of the magnetic particles 22 is arbitrary such as spherical, flaky, needle-like, and may not be specified to any shape. If the strength is strong, when a thin and flat scale-like (flake-like) shape is used, this shape is preferably used because the S / N ratio of the read magnetic data is good.

【００２９】次に、バインダー２３としては、常温（１
０〜３５゜Ｃ）で固相状態を示し、かつ、常温以上の温
度（４０〜８０゜Ｃ）に加熱されると流動状態（液相状
態）となるものであればよく、例えば、有機化合物、パ
ラフィンワックス、カルナバワックス、ポリエチレンワ
ックス等の天然あるいは合成ワックス、天然あるいは合
成樹脂、またはカルボン酸エステル等のように上記条件
を満たす物質を単独で、あるいは混合して使用すること
ができる。Next, the binder 23 is used at room temperature (1
It should be a substance that exhibits a solid phase state at 0 to 35 ° C. and is in a fluid state (liquid state state) when heated to a temperature (40 to 80 ° C.) higher than room temperature. Natural or synthetic waxes such as paraffin wax, carnauba wax, and polyethylene wax, natural or synthetic resins, and substances satisfying the above-mentioned conditions such as carboxylic acid esters can be used alone or in combination.

【００３０】次に、殻２１の材料としては、アクリル樹
脂、メタクリル系樹脂、ポリスチレン、ポリエステル樹
脂、ポリウレタン樹脂、ポリウレア樹脂、ポリアミド樹
脂、エポキシ樹脂、天然樹脂等の一般的に用いられる樹
脂を用いることができ、それら樹脂を単独あるいは２種
類以上混合して使用することも可能である。Next, as the material of the shell 21, generally used resins such as acrylic resin, methacrylic resin, polystyrene, polyester resin, polyurethane resin, polyurea resin, polyamide resin, epoxy resin and natural resin are used. These resins can be used alone or in combination of two or more.

【００３１】マイクロカプセル２０は、ポリマー溶液に
分散させた芯物質の周囲にポリマーの濃厚相を分散させ
る相分離法、ポリマーの硬化試薬等を用いてポリマー溶
液中の芯物質の周囲のポリマーを硬化させる液中硬化被
覆法、芯物質を分散させたエマルジョンの内相または外
相のいずれか一方からモノマーや重合触媒を供給し、芯
物質の表面をポリマーで被覆する「ｉｎ−ｓｉｔｕ重合
法」、芯物質を分散させたエマルジョンの内相及び外相
の両方からモノマーや重合触媒を供給する界面重合法等
のマイクロカプセル製造方法が好適であるが、これらの
方法に限定されるものではない。The microcapsule 20 cures the polymer around the core substance in the polymer solution using a phase separation method in which a concentrated phase of the polymer is dispersed around the core substance dispersed in the polymer solution, a polymer curing reagent, or the like. In-situ polymerization method, in which a monomer or a polymerization catalyst is supplied from either the inner phase or the outer phase of an emulsion in which a core material is dispersed, and the surface of the core material is coated with a polymer. A microcapsule production method such as an interfacial polymerization method in which a monomer and a polymerization catalyst are supplied from both the inner phase and the outer phase of an emulsion in which a substance is dispersed is suitable, but the method is not limited to these methods.

【００３２】ただし、マイクロカプセル２０の粒径、殻
２１の厚さその他の物性、磁性粒子２２の性質、磁性粒
子２２の配向移動の容易さ、カプセル化の際の収率等を
考慮すると、「ｉｎ−ｓｉｔｕ重合法」または相分離法
によりカプセル化することが望ましい。この場合に用い
る重合性モノマーとしては、アクリル酸エステル、メタ
クリル酸エステル、スチレン及びその誘導体、イソシア
ネート、各種アミン、エポキシ基を有する化合物等が好
適である。However, in consideration of the particle size of the microcapsule 20, the thickness of the shell 21 and other physical properties, the property of the magnetic particle 22, the ease of orientation movement of the magnetic particle 22, the yield at the time of encapsulation, etc. Encapsulation by "in-situ polymerization method" or phase separation method is desirable. As the polymerizable monomer used in this case, acrylic acid ester, methacrylic acid ester, styrene and its derivatives, isocyanate, various amines, compounds having an epoxy group and the like are preferable.

【００３３】次に、マイクロカプセル２０を分散させる
バインダーとしては、水系バインダー、エマルジョン系
バインダー、溶剤系バインダー等を適宜用いることがで
きる。そして、このようなバインダーにマイクロカプセ
ル２０を分散させたマイクロカプセル層１３は、転写箔
やシールのような形態に加工した後に基材１１の全面あ
るいはその一部に貼着するか、または塗料にして基材１
１の全面またはその一部に直接コーティングしたり、印
刷あるいはインジェクションなどの種々の方法で形成す
ることができる。Next, as the binder in which the microcapsules 20 are dispersed, an aqueous binder, an emulsion binder, a solvent binder or the like can be appropriately used. Then, the microcapsule layer 13 in which the microcapsules 20 are dispersed in such a binder is applied to the entire surface of the base material 11 or a part thereof after being processed into a form such as a transfer foil or a seal, or a paint. Base material 1
It can be formed by directly coating the entire surface of 1 or a part thereof, or by various methods such as printing or injection.

【００３４】次に、図２に示すように、マイクロカプセ
ル層１３の表面には、隠蔽層１４が設けられている。隠
蔽層１４は、磁性粒子２２の配向パターンを目視できな
いようにするためのものである。また、隠蔽層１４を設
ける代わりに、マイクロカプセル２０のバインダー２３
中に、非磁性金属粉末や非磁性でかつ隠蔽性を有する顔
料を含有させることもできる。ここで、非磁性金属粉末
を用いる場合には、非磁性金属単体あるいは非磁性金属
合金等を用いることができる。また、非磁性でかつ隠蔽
性を有する顔料としては、例えば、不溶性アゾ染料、銅
フタロシアンニン系顔料などの一般的な非磁性有機顔料
や、クロム酸塩、硫酸塩、酸化物、珪酸塩、炭酸塩、燐
酸塩などの非磁性無機顔料を用いることができる。Next, as shown in FIG. 2, a masking layer 14 is provided on the surface of the microcapsule layer 13. The hiding layer 14 is for making the orientation pattern of the magnetic particles 22 invisible. Further, instead of providing the hiding layer 14, the binder 23 of the microcapsule 20
A non-magnetic metal powder or a non-magnetic and hiding pigment may be contained therein. Here, when the non-magnetic metal powder is used, a non-magnetic metal simple substance or a non-magnetic metal alloy can be used. Examples of the non-magnetic and opaque pigments include, for example, insoluble azo dyes, general non-magnetic organic pigments such as copper phthalocyanine pigments, chromates, sulfates, oxides, silicates, Non-magnetic inorganic pigments such as carbonates and phosphates can be used.

【００３５】また、隠蔽層１４は、例えば非磁性金属薄
膜をマイクロカプセル層１３の表面に貼着したり、非磁
性金属粉末を合成樹脂等に分散させた塗料、あるいは非
磁性でかつ隠蔽性を有する顔料を合成樹脂等に分散させ
た塗料等をマイクロカプセル層１３の表面に塗布するこ
とにより形成することができる。また、隠蔽層１４に代
えて、マイクロカプセル層１３を保護するための保護層
１５（図３参照）を設けることもできる。保護層１５
は、マイクロカプセル層１３の磁性粒子２２，…への磁
気パターンの書込および読取りに支障のないように形成
される。保護層１５の材料としては、ポリエステル、Ｐ
ＥＴ、ポリ塩化ビニル、ポリ酢酸ビニル、エポキシ樹
脂、ポリメタクリル酸メチル、ポリスチレン、アクリル
樹脂、ポリカーボネート等の合成樹脂、天然樹脂等を使
用することができる。また、必要に応じて非磁性金属粉
末、非磁性顔料や染料を加えることができる。The hiding layer 14 is, for example, a non-magnetic metal thin film adhered to the surface of the microcapsule layer 13, a coating in which a non-magnetic metal powder is dispersed in a synthetic resin, or a non-magnetic and hiding property. It can be formed by coating the surface of the microcapsule layer 13 with a coating material or the like in which the pigment contained therein is dispersed in a synthetic resin or the like. Further, instead of the hiding layer 14, a protective layer 15 (see FIG. 3) for protecting the microcapsule layer 13 can be provided. Protective layer 15
Are formed so as not to interfere with writing and reading of a magnetic pattern on the magnetic particles 22, ... Of the microcapsule layer 13. As the material of the protective layer 15, polyester, P
ET, polyvinyl chloride, polyvinyl acetate, epoxy resin, polymethylmethacrylate, polystyrene, acrylic resin, synthetic resin such as polycarbonate, natural resin and the like can be used. In addition, non-magnetic metal powder, non-magnetic pigment or dye can be added if necessary.

【００３６】上記構成のマイクロカプセル層１３には、
目視では判別不可能な磁気の固有情報が記録される。す
なわち、磁気の固有情報は当該情報記録媒体１０固有の
ものであって、磁性粒子２２，…の配向によって特定さ
れる。磁性粒子２２，…の配向は、磁気ヘッド等の適当
な手段によってマイクロカプセル層１３からの出力波形
として読み出される。一方、基材１１の他方の面の全域
あるいは一部には、デジタル情報記録部（第２の情報記
録部）１２が形成されている。そして、読み出された出
力波形は、Ａ／Ｄ変換がなされた後にデジタル情報記録
部１２に記録されるようになっている。デジタル情報記
録部１２としては、例えば、磁気ストライプ、バーコー
ド、ＯＣＲ、ＭＩＣＲ、ＩＣメモリや光メモリなどの情
報記録媒体１０を使用することができる。In the microcapsule layer 13 having the above-mentioned structure,
Magnetic unique information that cannot be visually identified is recorded. That is, the unique magnetic information is unique to the information recording medium 10 and is specified by the orientation of the magnetic particles 22 ,. The orientation of the magnetic particles 22, ... Is read as an output waveform from the microcapsule layer 13 by an appropriate means such as a magnetic head. On the other hand, a digital information recording section (second information recording section) 12 is formed on the whole or part of the other surface of the base material 11. Then, the read output waveform is recorded in the digital information recording unit 12 after A / D conversion. As the digital information recording unit 12, for example, an information recording medium 10 such as a magnetic stripe, a bar code, an OCR, a MICR, an IC memory or an optical memory can be used.

【００３７】（２）情報記録媒体の使用方法 固有情報の形成 固有情報の記録は、マイクロカプセル層１３に熱と磁界
を加えて行う。マイクロカプセル層１３に熱を加えるこ
とにより、そのマイクロカプセル２０中のバインダー２
３が流動状態となる。そして、この状態で磁界を印加す
ると、磁性粒子２２，…が磁界の方向に応じて配向し、
次いでマイクロカプセル層１３を冷却するとバインダー
２３が固化する。これにより、磁性粒子２２，…が配向
したままバインダー２３中に固定される。よって、その
後に環境中に存在する種々の磁界がマイクロカプセル層
１３に印加されても磁性粒子２２，…の配向状態は変化
しない。(2) Method of using information recording medium Formation of unique information Recording of unique information is performed by applying heat and magnetic field to the microcapsule layer 13. By applying heat to the microcapsule layer 13, the binder 2 in the microcapsule 20 is heated.
3 becomes a fluid state. When a magnetic field is applied in this state, the magnetic particles 22, ... Orient according to the direction of the magnetic field,
Then, when the microcapsule layer 13 is cooled, the binder 23 is solidified. As a result, the magnetic particles 22, ... Are fixed in the binder 23 while being oriented. Therefore, even if various magnetic fields existing in the environment are thereafter applied to the microcapsule layer 13, the orientation state of the magnetic particles 22, ... Does not change.

【００３８】磁性粒子２２，…を配向させるには、例え
ば図１（Ｂ）に示すように、輻射加熱、対流加熱あるい
は接触加熱等の適当な加熱手段により情報記録媒体１０
を加熱し、マイクロカプセル２０中のバインダー２３を
液状にする。その状態で、ペン状あるいはリング状等の
形状を有する磁気ヘッドを用いて、マイクロカプセル層
１３にランダムに磁界を印加する。この場合の磁界は、
マイクロカプセル層１３のランダムな位置に印加する。
これにより、磁界が印加された部分に存在する磁性粒子
２２，…が所定方向に配向し、その配向は規則性のない
ランダムなパターンを形成する。そして、次に磁気ヘッ
ドで読み取ったときに、マイクロカプセル層１３の位置
に応じて磁性粒子２２，…の配向が変化し、その変化に
応じた出力波形が得られる。In order to orient the magnetic particles 22, ..., For example, as shown in FIG. 1 (B), the information recording medium 10 is heated by an appropriate heating means such as radiation heating, convection heating or contact heating.
Is heated to liquefy the binder 23 in the microcapsule 20. In this state, a magnetic field having a pen-like shape or a ring-like shape is used to randomly apply a magnetic field to the microcapsule layer 13. The magnetic field in this case is
The voltage is applied to random positions of the microcapsule layer 13.
As a result, the magnetic particles 22, ... Present in the portion to which the magnetic field is applied are oriented in a predetermined direction, and the orientation forms a random pattern having no regularity. Then, when read by the magnetic head next time, the orientations of the magnetic particles 22, ... Change according to the position of the microcapsule layer 13, and an output waveform corresponding to the change is obtained.

【００３９】また、図１（Ｃ）に示すように、永久磁石
あるいは電磁石などによって情報記録媒体１０全体に磁
界を印加し、この状態で、サーマイクロカプセル２０ヘ
ッドや半導体レーザ等の適当な加熱手段によりマイクロ
カプセル層１３を部分的に加熱する。これにより、加熱
された部分のマイクロカプセル２０のバインダー２３が
液状となり、当該マイクロカプセル２０内の磁性粒子２
２，…が所定方向に配向する。さらに、上記のような部
分加熱および磁界の部分的な印加を１つのヘッドによっ
て行うこともできる。たとえば、磁気ヘッドと半導体レ
ーザまたはサーマイクロカプセル２０ヘッドを複合した
ヘッドを用いることもできる。Further, as shown in FIG. 1C, a magnetic field is applied to the entire information recording medium 10 by a permanent magnet or an electromagnet, and in this state, a suitable heating means such as a thermo-capsule 20 head or a semiconductor laser is applied. The microcapsule layer 13 is partially heated by. As a result, the binder 23 of the heated microcapsules 20 becomes liquid, and the magnetic particles 2 in the microcapsules 20 are heated.
2, ... Orient in a predetermined direction. Further, the partial heating and the partial application of the magnetic field as described above can be performed by one head. For example, a head in which a magnetic head and a semiconductor laser or thermo-capsule 20 head are combined can be used.

【００４０】固有情報のデジタル記録 上記のようにして固有情報がマイクロカプセル層１３に
形成されると、次に、磁気ヘッドや磁気抵抗センサなど
の公知の磁気センサを用いて磁性粒子２２，…の配向の
変化を読み取る。たとえば、磁性粒子２２，…が硬質磁
性材料で構成されている場合には、磁性粒子２２，…の
残留磁界の変化を検出する。あるいは、磁性粒子２２，
…が半硬質磁性材料または軟質磁性材料で構成されてい
る場合には、情報記録媒体１０にバイアス磁界を印加し
た状態でマイクロカプセル層１３における磁界の変化を
検出する。マイクロカプセル層１３における磁界の変化
は磁気センサの出力波形として現出され、この出力波形
をＡ／Ｄ変換して例えば８バイトのデジタル情報に変換
する。そして、こうして得たデジタル情報を前述のデジ
タル情報記録部１２に登録する。Digital recording of unique information When the unique information is formed on the microcapsule layer 13 as described above, the magnetic particles 22, ... Are then formed using a known magnetic sensor such as a magnetic head or a magnetoresistive sensor. Read the change in orientation. For example, when the magnetic particles 22, ... Are made of a hard magnetic material, the change in the residual magnetic field of the magnetic particles 22 ,. Alternatively, the magnetic particles 22,
When .. is composed of a semi-hard magnetic material or a soft magnetic material, a change in the magnetic field in the microcapsule layer 13 is detected with a bias magnetic field applied to the information recording medium 10. The change of the magnetic field in the microcapsule layer 13 appears as an output waveform of the magnetic sensor, and this output waveform is A / D converted to be converted into, for example, 8-byte digital information. Then, the digital information thus obtained is registered in the digital information recording unit 12 described above.

【００４１】情報記録媒体の真偽判定 本発明をキャッシュカードに適用した場合について図５
ないし図７を参照して説明する。情報記録媒体１０をキ
ャッシュカードを使用するに際しては、まず、マイクロ
カプセル層１３から出力波形を読み取り、例えば８バイ
トのデジタル情報に変換する。次に、変換されたデジタ
ル情報とデジタル情報記録部１２に予め登録されたデジ
タル情報との相関性を比較演算する。図６は２つのデジ
タル情報の相関係数が所定の閾値以上である場合を示
し、この場合には、当該情報記録媒体１０は真正と判定
され、使用者が所望する取引を行うことができる。Determination of Authenticity of Information Recording Medium FIG. 5 shows a case where the present invention is applied to a cash card.
It will be described with reference to FIGS. When using a cash card as the information recording medium 10, first, the output waveform is read from the microcapsule layer 13 and converted into, for example, 8-byte digital information. Next, the correlation between the converted digital information and the digital information registered in advance in the digital information recording unit 12 is compared and calculated. FIG. 6 shows a case where the correlation coefficient of two pieces of digital information is greater than or equal to a predetermined threshold value. In this case, the information recording medium 10 is determined to be authentic, and the transaction desired by the user can be performed.

【００４２】次に、情報記録媒体１０が改ざんまたは偽
造された場合を考える。図５（Ａ）は真正な情報記録媒
体１０を示し、この情報記録媒体１０のデジタル情報記
録部１２のデジタル情報を改ざんしたものを同図（Ｂ）
に、デジタル情報記録部１２のデジタル情報を他の情報
記録媒体１０にそのままコピーして偽造したものを同図
（Ｃ）に示す。これら改ざんまたは偽造された情報記録
媒体１０では、図５に示すように、マイクロカプセル層
１３から読み出された出力波形は、登録時の出力波形と
大きく異なる。このため、読み出された出力波形を８バ
イトのデジタル情報に変換して予め登録されたデジタル
情報との相関係数を演算すると、所定の閾値を下回る結
果となる。その結果、当該情報記録媒体１０は偽物と判
定して取引を禁止する。Next, consider a case where the information recording medium 10 has been tampered with or forged. FIG. 5A shows a genuine information recording medium 10, in which the digital information in the digital information recording section 12 of the information recording medium 10 is falsified.
FIG. 3C shows a copy of the digital information recorded in the digital information recording unit 12 as it is on the other information recording medium 10 and is forged. In these falsified or forged information recording medium 10, as shown in FIG. 5, the output waveform read from the microcapsule layer 13 is significantly different from the output waveform at the time of registration. Therefore, when the read output waveform is converted into 8-byte digital information and the correlation coefficient with digital information registered in advance is calculated, the result is below a predetermined threshold value. As a result, the information recording medium 10 is determined to be fake and the transaction is prohibited.

【００４３】このように、上記構成の情報記録媒体１０
においては、デジタル情報記録部１２のデジタル情報を
改ざんあるいはコピーしても、マイクロカプセル層１３
に形成した固有情報に基づいて変換されたデジタル情報
を照合することによって容易に真偽判定を行うことがで
きる。また、製造コストが割安で容易に製造することが
できるとともに、固有情報を比較的簡単な装置で容易に
読み取ることができる。さらに、マイクロカプセル２０
内のバインダー２３を再び加熱溶融することにより、磁
性粒子の配向を変化させて固有情報を変更することがで
きるから、情報記録媒体として繰り返し利用することが
できる。As described above, the information recording medium 10 having the above structure
In the above, even if the digital information in the digital information recording section 12 is falsified or copied, the microcapsule layer 13
The authenticity can be easily determined by collating the digital information converted based on the unique information formed in (1). Further, the manufacturing cost is low and the manufacturing is easy, and the unique information can be easily read by a relatively simple device. Furthermore, microcapsules 20
By reheating and melting the binder 23 therein, the orientation of the magnetic particles can be changed and the unique information can be changed, so that the binder 23 can be repeatedly used as an information recording medium.

【００４４】特に、上記実施例では、磁界を印加するこ
とにより磁性粒子２２，…に磁化パターンを形成するか
ら、磁気パターンの不均一状態を容易に制御することが
できるとともに、磁気パターンの不均一の強弱の程度を
大きくしてＳ／Ｎ比を大きくすることができる。さら
に、上記実施例では、磁性粒子２２をマイクロカプセル
２０内に封入しているから、磁性粒子２２，…の配向パ
ターンを解読するのは極めて困難である。よって、マイ
クロカプセル層１３を似せて造って情報記録媒体１０を
偽造することは殆ど不可能である。一方、マイクロカプ
セル層１３から出力される信号の波形からマイクロカプ
セル層１３を製造することも考えられる。しかしなが
ら、上記情報記録媒体１０では、磁性粒子２２，…の配
向パターンがランダムに形成されているから、それに基
づいて出力される信号の波形も何ら規則性のないものと
なる。よって、そのような出力信号から磁性粒子２２，
…の配向パターンを導き出すことは極めて困難である。
すなわち、磁性粒子２２，…の配向パターンは、指紋と
同様に当該情報記録媒体１０について唯一のものであ
り、これを複製することは殆ど不可能である。よって、
上記情報記録媒体１０においては、改ざんや偽造等の悪
用をほぼ完全に防止することができる。In particular, in the above embodiment, since the magnetic patterns are formed on the magnetic particles 22, ... By applying the magnetic field, the nonuniform state of the magnetic pattern can be easily controlled and the nonuniform magnetic pattern can be controlled. It is possible to increase the S / N ratio by increasing the degree of strength of. Furthermore, in the above embodiment, since the magnetic particles 22 are enclosed in the microcapsules 20, it is extremely difficult to decipher the orientation pattern of the magnetic particles 22, .... Therefore, it is almost impossible to forge the information recording medium 10 by making the microcapsule layer 13 similar. On the other hand, it is possible to manufacture the microcapsule layer 13 from the waveform of the signal output from the microcapsule layer 13. However, in the information recording medium 10, since the orientation patterns of the magnetic particles 22, ... Are randomly formed, the waveform of the signal output based on the orientation pattern has no regularity. Therefore, from such an output signal, the magnetic particles 22,
It is extremely difficult to derive the orientation pattern of ...
That is, the orientation pattern of the magnetic particles 22, ... Is the same for the information recording medium 10 as the fingerprint, and it is almost impossible to duplicate the same. Therefore,
In the information recording medium 10, it is possible to almost completely prevent misuse such as falsification and forgery.

【００４５】Ｂ．製造例 次に、図２ないし図４に示す情報記録媒体を実際に製造
した例について説明する。 ［製造例１］図２に示す情報記録媒体をＰＥＴ製カード
として製造した。 マイクロカプセル２０の製造 シランカップリング処理を施したフレーク状のニッケル
粒子２２を、６０℃に加熱して融解したパラフィンワッ
クスに均一に分散した。この分散液を６０℃に加熱した
１０％ゼラチン水溶液中に分散させた。この分散に際し
ては、ホモジナイザーを回転数２０００ｒｐｍにして使
用し、平均粒径が８０ｍとなるように約５分間分散させ
た。得られた分散液に１０％アラビアゴム水溶液を混合
するとともに水を添加した。そして、４０℃に保って１
０％酢酸水溶液を滴下し、ｐＨを４に調節した。その
後、液温を５℃まで冷却して３０％ホルマリン水溶液を
加え、１０％水酸化ナトリウム水溶液を滴下してｐＨを
９に調節した。これにより、ゼラチンーアラビアゴムを
殻２１とするマイクロカプセル２０を製造した。B. Manufacturing Example Next, an example of actually manufacturing the information recording medium shown in FIGS. 2 to 4 will be described. [Manufacturing Example 1] The information recording medium shown in FIG. 2 was manufactured as a PET card. Production of Microcapsules 20 Flake-shaped nickel particles 22 subjected to silane coupling treatment were uniformly dispersed in paraffin wax melted by heating at 60 ° C. This dispersion was dispersed in a 10% gelatin aqueous solution heated to 60 ° C. At the time of this dispersion, a homogenizer was used at a rotation speed of 2000 rpm, and the dispersion was carried out for about 5 minutes so that the average particle diameter was 80 m. A 10% aqueous solution of gum arabic was mixed with the obtained dispersion, and water was added. And keep it at 40 ℃ 1
A 0% aqueous acetic acid solution was added dropwise to adjust the pH to 4. Then, the liquid temperature was cooled to 5 ° C., a 30% formalin aqueous solution was added, and a 10% sodium hydroxide aqueous solution was added dropwise to adjust the pH to 9. As a result, the microcapsules 20 having gelatin-arabic gum as the shell 21 were manufactured.

【００４６】情報記録媒体の製造 縦５．４ｃｍ、横８．６ｃｍ、厚さ約０．２５ｍｍの白
色のＰＥＴ製板を基材１１として用いた。この基材１１
の一方の面に下記組成からなるデジタル情報記録部１２
を形成した。デジタル情報記録部１２は、当該情報記録
媒体１０の固有情報と、ＩＤ情報や取引情報をデジタル
情報として記録するように構成され、塗布量が４０ｇ／
ｍ ²となるようにグラビアコータにより塗布した。Production of Information Recording Medium A white PET plate having a length of 5.4 cm, a width of 8.6 cm and a thickness of about 0.25 mm was used as the substrate 11. This base material 11
Digital information recording part 12 having the following composition on one surface
Was formed. The digital information recording unit 12 is configured to record the unique information of the information recording medium 10 and the ID information and the transaction information as digital information, and the coating amount is 40 g /
It was applied by a gravure coater so as to be m ² .

【００４７】基材１１の他方の面に、マイクロカプセル
層１３を層厚１００μｍとなるようにグラビアコータに
て塗布した。マイクロカプセル層１３における磁性粒子
２２とバインダーの配合割合を下記に示す。さらに、マ
イクロカプセル層１３の固有情報を隠蔽する隠蔽層１４
を塗布量２ｇ／ｍ²となるようにグラビアコータにより
塗布した。なお、隠蔽層１４の組成も下記に示す。The microcapsule layer 13 was applied to the other surface of the base material 11 by a gravure coater so as to have a layer thickness of 100 μm. The mixing ratio of the magnetic particles 22 and the binder in the microcapsule layer 13 is shown below. Further, the concealing layer 14 that conceals the unique information of the microcapsule layer 13
Was coated with a gravure coater so that the coating amount was 2 g / m ² . The composition of the hiding layer 14 is also shown below.

【００４８】固有情報の形成 このように製造した情報記録媒体１０を熱風で加熱し、
コンピューターの演算によるランダムデータに基付き、
単極磁気ヘッドによる垂直磁界を印加して磁性粒子２
０，…を配向回転した。その後、情報記録媒体１０を冷
却して配向パターンを固定し、磁性粒子２２，…の配向
の変化を情報記録媒体の固有情報とした。Formation of Unique Information The information recording medium 10 thus manufactured is heated with hot air,
Based on random data calculated by computer,
Applying a vertical magnetic field with a unipolar magnetic head, magnetic particles 2
The orientation of 0, ... Was rotated. After that, the information recording medium 10 was cooled to fix the orientation pattern, and the change in the orientation of the magnetic particles 22, ... Was used as the unique information of the information recording medium.

【００４９】 ○マイクロカプセル組成 磁性粒子 ：Ｎｉフレーク（保磁力４５ Ｏｅ） ６０部 バインダー ：パラフインワックス ８０部 殻物質 ：１０％ゼラチン水溶液 ２００部 ：１０％アラビアゴム水溶液 ２００部 ：３０％ホルマリン水溶液 １０部 溶媒 ：水 １０００部 ｐＨ調整剤 ：１０％酢酸水溶液 ：１０％水酸化ナトリウムMicrocapsule composition Magnetic particles: Ni flakes (coercive force 45 Oe) 60 parts Binder: Paraffin wax 80 parts Shell material: 10% gelatin aqueous solution 200 parts: 10% arabic gum aqueous solution 200 parts: 30% formalin aqueous solution 10 parts Solvent: Water 1000 parts pH adjuster: 10% acetic acid aqueous solution: 10% sodium hydroxide

【００５０】 ○デジタル情報記録部組成 磁性材 ：バリウムフェライト １０部 バインダー ：塩化ビニル／酢酸ビニル ４部Composition of digital information recording part Magnetic material: barium ferrite 10 parts Binder: vinyl chloride / vinyl acetate 4 parts

【００５１】 ○マイクロカプセル層組成 磁性マイクロカプセル： １０部 バインダー ：アクリルエマルジョン ５部Microcapsule layer composition Magnetic microcapsules: 10 parts Binder: Acrylic emulsion 5 parts

【００５２】 ○隠蔽層組成 顔料 ：鱗片状アルミ粒子 １０部 バインダー ：ポリエステル樹脂 ３部○ Hiding layer composition Pigment: Scale-like aluminum particles 10 parts Binder: Polyester resin 3 parts

【００５３】［製造例２］図３に示す情報記録媒体をＰ
ＥＴ製カードとして製造した。 マイクロカプセルの製造 オレフィン酸処理を施したフレーク状ニッケル・鉄合金
２２（パーマロイ）５０重量部と鱗片状アルミ粒子１０
重量部を、５０℃に加熱し溶解したパラフィンワックス
とフタル酸ジブチルの混合溶媒８０重量部に均一に分散
し、この分散液を５０℃に加熱した５％ポリビニルアル
コール２００重量部中に分散した。この分散に際して
は、ホモジナイザーを回転数２０００ｒｐｍで使用し、
平均粒径７５０μｍとなるように約５分間分散させた。
得られた分散液にメラミン−ホルマリンプレポリマー水
溶液１００重量部を加え、２０％酢酸水溶液を滴下して
ｐＨを６に調節した。その後、液温を６５℃に昇温して
３０分間重合反応を行い、メラミン−ホルマリンからな
る殻２１を有するマイクロカプセル２０を製造した。[Manufacturing Example 2] The information recording medium shown in FIG.
It was manufactured as an ET card. Manufacture of microcapsules 50 parts by weight of flaky nickel-iron alloy 22 (permalloy) treated with olefinic acid and scale-like aluminum particles 10
Part by weight was uniformly dispersed in 80 parts by weight of a mixed solvent of paraffin wax and dibutyl phthalate which had been heated to 50 ° C., and this dispersion was dispersed in 200 parts by weight of 5% polyvinyl alcohol heated to 50 ° C. At the time of this dispersion, a homogenizer was used at a rotation speed of 2000 rpm,
The particles were dispersed for about 5 minutes so that the average particle diameter was 750 μm.
100 parts by weight of a melamine-formalin prepolymer aqueous solution was added to the obtained dispersion, and a 20% acetic acid aqueous solution was added dropwise to adjust the pH to 6. Then, the liquid temperature was raised to 65 ° C. and a polymerization reaction was carried out for 30 minutes to produce microcapsules 20 having a shell 21 made of melamine-formalin.

【００５４】情報記録媒体の製造 縦５．４ｃｍ、横８．６ｃｍ、厚さ約０．８ｍｍの白色
塩化ビニル板を基材１１として用いた。この基材１１の
一方の面に、幅６．５ｍｍ、長さ８．６ｍｍの磁気スト
ライプ転写テープを、基材１１の横方向に延在するよう
にして熱転写した。こうして、当該情報記録媒体１０の
固有情報と携帯者のＩＤ情報や金銭情報、取引情報等を
デジタル情報として記録するデジタル情報記録部１２を
形成した。Production of Information Recording Medium A white vinyl chloride plate having a length of 5.4 cm, a width of 8.6 cm and a thickness of about 0.8 mm was used as the substrate 11. A magnetic stripe transfer tape having a width of 6.5 mm and a length of 8.6 mm was thermally transferred onto one surface of the base material 11 so as to extend in the lateral direction of the base material 11. In this way, the digital information recording section 12 for recording the unique information of the information recording medium 10 and the ID information, financial information, transaction information, etc. of the carrier as digital information was formed.

【００５５】基材１１の他方の面に、幅１０ｍｍ、長さ
５０ｍｍ、層厚８０μｍのマイクロカプセル層１３をス
クリーン印刷により形成した。マイクロカプセル層１３
における磁性粒子２２とバインダーの配合割合を下記に
示す。さらに、マイクロカプセル層１３の表面に、下記
の組成からなるアクリル樹脂を塗布量４ｇ／ｍ²となる
ようにグラビア印刷により塗布し、これによってマイク
ロカプセル層１３を保護する保護層１５を形成した。On the other surface of the base material 11, a microcapsule layer 13 having a width of 10 mm, a length of 50 mm and a layer thickness of 80 μm was formed by screen printing. Microcapsule layer 13
The mixing ratio of the magnetic particles 22 and the binder in the above is shown below. Further, an acrylic resin having the following composition was applied to the surface of the microcapsule layer 13 by gravure printing so that the coating amount was 4 g / m ² , thereby forming a protective layer 15 for protecting the microcapsule layer 13.

【００５６】固有情報の形成 コンピューターの演算によるランダムデータに基づき、
半導体レーザを内蔵する熱磁気ヘッドによってマイクロ
カプセル層１３を加熱すると同時に磁界を印加した。こ
れにより、マイクロカプセル２０，…中の磁性粒子２２
を配向回転させ、磁性粒子２２，…の配向の変化を情報
記録媒体１０の固有情報とした。Formation of unique information Based on random data calculated by a computer,
The microcapsule layer 13 was heated by a thermomagnetic head containing a semiconductor laser, and at the same time a magnetic field was applied. As a result, the magnetic particles 22 in the microcapsules 20, ...
Was rotated for orientation, and the change in the orientation of the magnetic particles 22, ... Was used as the unique information of the information recording medium 10.

【００５７】 ○マイクロカプセル組成 磁性粒子 ：Ｎｉ・Ｆｅ合金（保磁力２５ Ｏｅ） ５０部 隠蔽顔料 ：鱗片状アルミ粒子 １０部 バインダー ：パラフィンワックスとフタル酸ジブチルの混合液 ８０部 殻物質 ：５％ポリビニルアルコール ２００部 ：メラミン−ホルマリンプレポリマー １００部 ｐＨ調整剤 ：２０％酢酸水溶液 Microcapsule composition Magnetic particles: Ni / Fe alloy (coercive force 25 Oe) 50 parts Concealing pigment: Scale-like aluminum particles 10 parts Binder: Mixture of paraffin wax and dibutyl phthalate 80 parts Shell material: 5% polyvinyl Alcohol 200 parts: Melamine-formalin prepolymer 100 parts pH adjuster: 20% acetic acid aqueous solution

【００５８】 ○マイクロカプセル層組成 磁性マイクロカプセル：ポリビニルアルコール １０部 バインダー ： ５部Microcapsule Layer Composition Magnetic Microcapsules: Polyvinyl alcohol 10 parts Binder: 5 parts

【００５９】 ○保護層組成 バインダー ：アクリル樹脂 １０部 溶剤 ：ＭＥＫ／トルエンの混合液 ３０部 添加剤 ：ポリエチレンワックス ２部Protective layer composition Binder: Acrylic resin 10 parts Solvent: MEK / toluene mixed solution 30 parts Additive: Polyethylene wax 2 parts

【００６０】［製造例３］図４に示す情報記録媒体１０
を製造した。 マイクロカプセルの製造 シランカップリング処理を施したフレーク状のコバルト
・アルミニウム合金６０重量部を、６０℃に加熱して融
解したパラフィンワックス２３に均一に分散した。この
分散液を６０℃に加熱した１０％ゼラチン水溶液中に分
散させた。この分散に際しては、ホモジナイザーを回転
数２０００ｒｐｍにして使用し、平均粒子径が８０μｍ
となるように約５分間分散させた。得られた分散液に１
０％アラビアゴム水溶液を混合するとともに水を添加し
た。そして、４０℃に保って１０％酢酸水溶液を滴下
し、ｐＨを４に調節した。その後、液温を５℃まで冷却
して３０％ホルマリン水溶液を加え、１０％水酸化ナト
リウム水溶液を滴下してｐＨを９に調節しゼラチン−ア
ラビアゴムを殻２１とするマイクロカプセル２０を製造
した。[Manufacturing Example 3] Information recording medium 10 shown in FIG.
Was manufactured. Production of Microcapsules 60 parts by weight of flaky cobalt-aluminum alloy subjected to silane coupling treatment was uniformly dispersed in paraffin wax 23 melted by heating at 60 ° C. This dispersion was dispersed in a 10% gelatin aqueous solution heated to 60 ° C. At the time of this dispersion, a homogenizer was used at a rotation speed of 2000 rpm and an average particle diameter of 80 μm.
Was dispersed for about 5 minutes. 1 in the resulting dispersion
Water was added while mixing 0% aqueous gum arabic solution. Then, the temperature was maintained at 40 ° C. and a 10% aqueous acetic acid solution was added dropwise to adjust the pH to 4. Then, the liquid temperature was cooled to 5 ° C., 30% formalin aqueous solution was added, and 10% sodium hydroxide aqueous solution was added dropwise to adjust the pH to 9 to produce microcapsules 20 having gelatin-arabic gum as shell 21.

【００６１】縦５．４ｃｍ、横８．６ｃｍ、厚さ約０．
７ｍｍの白色塩化ビニル板を基材１１として用いた。基
材１１の一方の面に、幅６．５ｍｍの磁気ストライプ転
写テープを基材の横方向に長さ約８．６ｍｍ熱転写し
た。こうして、当該情報記録媒体１０の固有情報と携帯
者のＩＤ情報や金銭情報、取引情報等をデジタル情報と
して記録するデジタル情報記録部１２を形成した。Height 5.4 cm, width 8.6 cm, thickness about 0.
A 7 mm white vinyl chloride plate was used as the substrate 11. A magnetic stripe transfer tape having a width of 6.5 mm was thermally transferred to one surface of the base material 11 in the lateral direction of the base material by a length of about 8.6 mm. In this way, the digital information recording section 12 for recording the unique information of the information recording medium 10 and the ID information, financial information, transaction information, etc. of the carrier as digital information was formed.

【００６２】基材１１の他方の面全体に、下記組成から
なるマイクロカプセル層１３を層厚８０μｍとなるよう
にグラビアコータで塗布した。さらに、マイクロカプセ
ル層１３の表面に、下記の組成からなる樹脂を塗布量５
ｇ／ｍ²となるようにグラビアコータにより塗布し、こ
れによってマイクロカプセル層１３を保護する保護層１
５を形成した。A microcapsule layer 13 having the following composition was applied to the entire other surface of the base material 11 by a gravure coater so as to have a layer thickness of 80 μm. Further, a resin having the following composition is applied on the surface of the microcapsule layer 5
Protective layer 1 applied by a gravure coater so as to be g / m ^2, and thereby protecting the microcapsule layer 13.
5 was formed.

【００６３】このように得られた情報記録媒体１０に永
久磁石により垂直磁界を印加しながら、コンピューター
演算によるランダムな箇所をサーマルヘッドによって加
熱した。これにより、加熱されたマイクロカプセル２
０，…中の磁性粒子２２が配向回転し、磁性粒子２２，
…の配向の変化を情報記録媒体１０の固有情報とした。While applying a vertical magnetic field to the information recording medium 10 thus obtained with a permanent magnet, a random portion calculated by computer was heated by a thermal head. Thereby, the heated microcapsules 2
The magnetic particles 22 in 0, ...
The change in the orientation of ... Is taken as the unique information of the information recording medium 10.

【００６４】 ○マイクロカプセル組成 磁性粒子 ：コバルト・アルミニウム合金 ６０部 分散媒 ：パラフィンワックス ８０部 壁物質 ：１０％ゼラチン水溶液 ２００部 ：１０％アラビアゴム水溶液 ２００部 ：３０％ホルマリン水溶液 １０部 溶媒 ：水 １０００部 ｐＨ調整剤 ：１０％酢酸水溶液 ：１０％水酸化ナトリウムMicrocapsule composition Magnetic particles: Cobalt-aluminum alloy 60 parts Dispersion medium: Paraffin wax 80 parts Wall material: 10% gelatin aqueous solution 200 parts: 10% arabic gum aqueous solution 200 parts: 30% formalin aqueous solution 10 parts Solvent: water 1000 parts pH adjuster: 10% acetic acid aqueous solution: 10% sodium hydroxide

【００６５】 ○マイクロカプセル層組成 磁性マイクロカプセル： １０部 鱗片状アルミ粒子 ： ３部 バインダー ：アクリルエマルジョン ５部Microcapsule layer composition Magnetic microcapsule: 10 parts Scale-like aluminum particles: 3 parts Binder: Acrylic emulsion 5 parts

【００６６】 ○保護層組成 バインダー ：エポキシ樹脂 １０部 添加剤 ：カルナバワックス １部Protective layer composition Binder: Epoxy resin 10 parts Additive: Carnauba wax 1 part

【００６７】［使用例］製造例１ないし３で製造した情
報記録媒体１０各々の固有情報である磁性粒子２２，…
の配向からなるアナログ信号をＭＲセンサで読み取り、
読み取ったアナログ信号をＡＤ変してデジタル情報化
し、このデジタル情報をデジタル記録部１２に記録し
た。その後、同様に再生したマイクロカプセル層１３の
磁気情報とデジタル記録部１２に記録された固有情報と
の照合を行ったところ、何れの製造例の情報記録媒体１
０についても良好な結果が得られた。[Example of Use] Magnetic particles 22, ... Which are the unique information of each of the information recording media 10 produced in Production Examples 1 to 3.
The analog signal consisting of the orientation of
The read analog signal was AD converted to digital information, and this digital information was recorded in the digital recording unit 12. After that, when the magnetic information of the microcapsule layer 13 reproduced in the same manner and the unique information recorded in the digital recording unit 12 are collated, the information recording medium 1 of any production example is obtained.
Good results were also obtained for 0.

【００６８】Ｃ．変更例 本発明は上記実施例に限定されるものではなく、以下の
ように種々の変更が可能である。 上記実施例では磁性粒子２２をマイクロカプセル２０
中のバインダー２３に分散させているが、磁性粒子を熱
可塑性を有する合成樹脂に分散させ、この合成樹脂を溶
融して基材１１に塗布することによって、固有情報記録
層を形成することもできる。また、この場合において、
樹脂が溶融状態にあるときに磁界を印加して、磁性粒子
２２，…にランダムな配向パターンを形成することもで
きる。あるいは、塗布した溶融樹脂の上から磁性粒子２
２，…を撒いてランダムに分布させることもできる。さ
らに、磁性粒子２２，…の分布を不均一にすることもで
きる。 磁性粒子２２，…の配向パターンは必ずしもランダム
にする必要はなく、一定の規則性をもって変化させるこ
ともできる。 温度の変化によってバインダーの液相状態と固相状態
とを変化させるものに限らず、適当な添加剤を加えて液
相状態から固相状態にするように構成することもでき
る。C. Modifications The present invention is not limited to the above embodiments, and various modifications can be made as follows. In the above embodiment, the magnetic particles 22 are used as the microcapsules 20.
Although it is dispersed in the binder 23, the magnetic recording particles are dispersed in a synthetic resin having thermoplasticity, and the synthetic resin is melted and applied to the base material 11, so that the unique information recording layer can be formed. . Also, in this case,
A magnetic field may be applied when the resin is in a molten state to form a random orientation pattern on the magnetic particles 22, .... Alternatively, the magnetic particles 2 are applied from above the applied molten resin.
It is also possible to scatter 2, ... And randomly distribute. Further, the distribution of the magnetic particles 22, ... Can be made non-uniform. The orientation pattern of the magnetic particles 22, ... Does not necessarily need to be random, and can be changed with a certain regularity. The binder is not limited to the one in which the liquid phase state and the solid phase state of the binder are changed by changing the temperature, and it is also possible to add an appropriate additive to change the liquid phase state to the solid state.

【００６９】[0069]

【発明の効果】以上説明したように本発明によれば、バ
インダー内の磁性粒子の分布や配向を変化させ、その状
態でバインダーを固相状態にすることにより、磁性粒子
を当該情報記録媒体に固有の状態で固定することができ
る。よって、簡単に固有情報を形成することができると
ともに、磁性粒子の分布や配向の程度を適宜設定するこ
とによって、強弱の大きな磁気パターンを形成すること
が可能となる。また、バインダーを再び液相状態とする
ことにより、第１の情報記録部の固有情報情報を変更す
ることができ、情報記録媒体として繰り返し利用するこ
とができる。As described above, according to the present invention, the distribution and orientation of the magnetic particles in the binder are changed, and the binder is brought into the solid phase state in that state so that the magnetic particles can be used as the information recording medium. It can be fixed in a unique state. Therefore, the unique information can be easily formed, and by setting the distribution and orientation of the magnetic particles appropriately, it is possible to form a strong and weak magnetic pattern. Further, by bringing the binder into the liquid phase state again, the unique information information of the first information recording section can be changed and can be repeatedly used as an information recording medium.

【図面の簡単な説明】[Brief description of drawings]

【図１】実施例の情報記録媒体におけるマイクロカプセ
ルを示す断面図である。FIG. 1 is a cross-sectional view showing a microcapsule in an information recording medium of an example.

【図２】（Ａ）は実施例の情報記録媒体を示す側断面
図、（Ｂ）はその平面図である。2A is a side sectional view showing an information recording medium of an embodiment, and FIG. 2B is a plan view thereof.

【図３】（Ａ）は製造例の情報記録媒体を示す側断面
図、（Ｂ）はその平面図である。3A is a side sectional view showing an information recording medium of a manufacturing example, and FIG. 3B is a plan view thereof.

【図４】（Ａ）は他の製造例の情報記録媒体を示す側断
面図、（Ｂ）はその平面図である。FIG. 4A is a side sectional view showing an information recording medium of another manufacturing example, and FIG. 4B is a plan view thereof.

【図５】実施例の情報記録媒体の使用態様を説明するた
めの図である。FIG. 5 is a diagram for explaining a usage mode of the information recording medium of the embodiment.

【図６】真正な情報記録媒体を照合したときのデータの
処理を示す図である。FIG. 6 is a diagram showing processing of data when a genuine information recording medium is collated.

【図７】変造または偽造された情報記録媒体を照合した
ときのデータの処理を示す図である。FIG. 7 is a diagram showing processing of data when collating an altered or forged information recording medium.

【符号の説明】[Explanation of symbols]

１１ 基材 １２ デジタル情報記録部（第２の情報記録部） １３ マイクロカプセル層（第１の情報記録部） １４ 隠蔽層 １５ 保護層 11 Base Material 12 Digital Information Recording Section (Second Information Recording Section) 13 Microcapsule Layer (First Information Recording Section) 14 Hiding Layer 15 Protective Layer

───────────────────────────────────────────────────── フロントページの続き (72)発明者 松本 美子 東京都台東区台東一丁目５番１号 凸版印 刷株式会社内 (72)発明者 松本 陽美 東京都台東区台東一丁目５番１号 凸版印 刷株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Miko Matsumoto 1-5-1 Taito, Taito-ku, Tokyo Within Toppan Printing Co., Ltd. (72) Inventor Yoshimi Matsumoto 1-5-1 Taito, Taito-ku, Tokyo Toppan Printing Co., Ltd.

Claims (8)

【特許請求の範囲】[Claims] 【請求項１】 磁性粒子をバインダー中に分散させ、上
記磁性粒子を上記バインダー中で固定することにより、
上記磁性粒子の分布及び配向のうち少なくともいずれか
一つを固有情報とした第１の情報記録部と、 上記固有情報によって得られた磁気情報を記録する第２
の情報記録部とを備え、 上記バインダーを、所定条件で液相状態と固相状態のい
ずれかの状態となる樹脂で構成したことを特徴とする情
報記録媒体。1. Dispersing magnetic particles in a binder and fixing the magnetic particles in the binder,
A first information recording section having at least one of distribution and orientation of the magnetic particles as unique information, and a second information recording section for recording magnetic information obtained from the unique information.
And an information recording part of the above, wherein the binder is made of a resin that is in either a liquid phase state or a solid phase state under a predetermined condition. 【請求項２】 前記磁性粒子の分布及び配向のうち少な
くともいずれか一つにランダムな変化を設けたことを特
徴とする請求項１に記載の情報記録媒体。2. The information recording medium according to claim 1, wherein at least one of distribution and orientation of the magnetic particles is randomly changed. 【請求項３】 前記バインダーの融点は３５〜１５０゜
Ｃであることを特徴とする請求項１または２に記載の情
報記録媒体。3. The information recording medium according to claim 1, wherein the melting point of the binder is 35 to 150 ° C. 【請求項４】 前記バインダーをマイクロカプセル内に
設けるとともに、同マイクロカプセルを前記第１の情報
記録部に分散させたことを特徴とする請求項１ないし３
のいずれかに記載の情報記録媒体。4. The binder is provided in a microcapsule, and the microcapsule is dispersed in the first information recording section.
An information recording medium according to any one of 1. 【請求項５】 前記マイクロカプセルは、平均粒径が１
０〜１００μｍであることを特徴とする請求項４に記載
の情報記録媒体。5. The microcapsules have an average particle size of 1
The information recording medium according to claim 4, wherein the information recording medium has a thickness of 0 to 100 μm. 【請求項６】 前記磁性粒子は、６０ Ｏｅ以下の保磁
力を有することを特徴とする請求項１ないし５のいずれ
かに記載の情報記録媒体。6. The information recording medium according to claim 1, wherein the magnetic particles have a coercive force of 60 Oe or less. 【請求項７】 前記磁性粒子は鱗片状をなすとともにそ
の平均粒径が５〜８０μｍであることを特徴とする請求
項１ないし６のいずれかに記載の情報記録媒体。7. The information recording medium according to claim 1, wherein the magnetic particles have a scaly shape and have an average particle size of 5 to 80 μm. 【請求項８】 前記第１の情報記録部の表面に保護層を
設けたことを特徴とする請求項１ないし７のいずれかに
記載の情報記録媒体。8. The information recording medium according to claim 1, wherein a protective layer is provided on the surface of the first information recording section.