JPH08158217A - Production of warp knit fabric - Google Patents

Abstract

PURPOSE: To obtain warp knit fabric, excellent in see-through preventing properties, maintaining the high stretchability and useful for swimming wears, etc., by specifying fiber yarns fed to a front, a middle and a rear reeds and arranging underlaps of the front and the rear reeds in the same direction and the underlap in the rear reed in the opposite direction. CONSTITUTION: Synthetic fiber yarn having <=0.1wt.% content of a delustering agent is fed to a front reed of a warp knitting machine and synthetic fiber yarn having >=2.0wt.% content of the delustering agent is fed to a middle reed. Elastic yarn having >=400% breaking elongation is fed to a rear reed. The knitting is carried out in a design arranging underlaps of the front and middle reeds in the same direction and an underlap of the rear reed in the opposite direction. Thereby, stretchable knit fabric retaining the glossiness and fitness is obtained.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は，スポーツウェアー，特
に水着に使用される透け防止に優れた伸縮性編地の製造
方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a stretchable knitted fabric which is used for sportswear, particularly swimwear and which is excellent in preventing sheer.

【０００２】[0002]

【従来の技術】従来より，ポリエステル系繊維やポリア
ミド系繊維等の合成繊維は，優れた発色性と光沢性を有
しており，ファッション性の高いスポーツウェアー用途
に広く使用されている。特に婦人水着用途には，ポリエ
ーテルエステル系弾性糸やポリウレタン系弾性糸等とト
リコット編機にて交編した，薄くて体にフィットし，フ
ァッション性を満たす経編地が「２ｗａｙトリコット」
と称され，大量に生産されている。2. Description of the Related Art Conventionally, synthetic fibers such as polyester fibers and polyamide fibers have excellent coloring and gloss properties and are widely used for sportswear having high fashionability. Especially for women's swimwear applications, "2 way tricot" is a warp knitted fabric that is knitted with polyetherester elastic yarn or polyurethane elastic yarn on a tricot knitting machine, fits thinly, and fits the body.
And is produced in large quantities.

【０００３】しかしながら，合成繊維は，天然繊維や再
生繊維に比べ透明感が高く，淡色布帛が透けやすい欠点
を有している。特に，白色布帛が水に濡れたときに著し
く透明性が高くなるため，透け防止の改善が要望されて
いた。However, synthetic fibers are more transparent than natural fibers and regenerated fibers, and have the drawback that light-colored fabrics are easily transparent. In particular, when the white cloth gets wet with water, the transparency is remarkably increased. Therefore, improvement of the sheer prevention has been demanded.

【０００４】この欠点の改善のために，合成繊維に酸化
チタン等の艶消剤の含有量を増加し，不透明化を図る方
法や，合成繊維の表面を高濃度アルカリ溶液等で処理
し，粗面化し，不透明化する方法や，編地を厚地化し，
透けを防止する方法等が提案されている。しかしなが
ら，これらの方法は，「透け防止」対策を考慮するあま
りに，元来有していたフィット感，光沢感等を低下さ
せ，商品価値感を乏しくさせている。In order to improve this drawback, a method of increasing the content of a matting agent such as titanium oxide in the synthetic fiber to make it opaque, or treating the surface of the synthetic fiber with a high-concentration alkaline solution, etc. A method of making the surface flat and opaque, making the knitted fabric thicker,
Methods for preventing see-through have been proposed. However, these methods reduce the fit and gloss originally possessed by taking into consideration the "prevention of see-through" measures and make the product value poor.

【０００５】[0005]

【発明が解決しようとする課題】本発明は，このような
現状に鑑みて行われたもので，透け防止に優れ，かつ光
沢性，フィット感を阻害しない経編地を得ることを目的
とするものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and an object of the present invention is to obtain a warp knitted fabric which is excellent in preventing sheer and does not impair glossiness and fit. It is a thing.

【０００６】[0006]

【課題を解決するための手段】本発明は，上記目的を達
成するもので，次の構成よりなるものである。すなわ
ち，本発明は，経編機の前筬に艶消剤の含有量が０．１
％以下である合成繊維を，中筬に艶消剤の含有量が２．
０％以上である合成繊維を，後筬に切断伸度が４００％
以上である弾性糸を使用し，前筬と中筬のアンダーラッ
プが同方向で，かつ後筬のアンダーラップが逆方向の組
織で編成することを特徴とする経編地の製造方法を要旨
とするものである。SUMMARY OF THE INVENTION The present invention achieves the above object and has the following configuration. That is, according to the present invention, the content of the matting agent is 0.1 in the front reed of the warp knitting machine.
% Of synthetic fiber, the content of the matting agent in the middle reed is 2.
Synthetic fiber of 0% or more has a cutting elongation of 400% in the rear reed.
A method for manufacturing a warp knitted fabric is characterized in that the elastic yarns described above are knitted in a structure in which the underlaps of the front reed and the middle reed are in the same direction and the underlaps of the rear reed are in the opposite direction. To do.

【０００７】以下，本発明を詳細に説明する。本発明に
使用する経編機は，筬を３枚以上有するトリコット編機
あるいはラッセル編機であり，編機のゲージは，２４〜
３２Ｇ／インチで，一般的には２８Ｇ／インチを多く使
用する。筬枚数は３枚を必要とする。編機幅は，編地の
仕上幅との関係で決定すればよいが，１８０インチ幅の
編機を多く使用する。The present invention will be described in detail below. The warp knitting machine used in the present invention is a tricot knitting machine or a Russell knitting machine having three or more reeds, and the gauge of the knitting machine is 24 to
32 G / inch, and generally 28 G / inch is often used. Three reeds are required. The width of the knitting machine may be determined in relation to the finished width of the knitted fabric, but a 180-inch wide knitting machine is often used.

【０００８】本発明において，前筬と中筬に使用する合
成繊維は，ポリエステル系繊維やポリアミド系繊維であ
る。繊度は，用途からみて３０〜５０デニールが適して
いるが，編地の厚み，伸縮性から判断して３０〜４０デ
ニールであるのが望ましい。In the present invention, the synthetic fibers used for the front reed and the middle reed are polyester fibers and polyamide fibers. A fineness of 30 to 50 denier is suitable from the viewpoint of use, but it is desirable to be 30 to 40 denier as judged from the thickness and stretchability of the knitted fabric.

【０００９】単糸デニールは，１〜２デニール／フィラ
メントであるのが編地風合から適している。The single yarn denier is preferably 1 to 2 denier / filament in view of the texture of the knitted fabric.

【００１０】上記合成繊維は，艶消剤を含有しており，
その含有量は，前筬に使用する合成繊維が０．１％以下
の微量であり，中筬に使用する合成繊維が２．０％以上
である。艶消剤としては，酸化チタンが一般的に使用さ
れており，本発明においても酸化チタンの微粒子を使用
すると好適である。なお，その合成繊維の艶消剤の含有
量は，ラスタータイプ別に，ブライトタイプが０．０５
％以下，セミダルタイプが０．５％程度，フルダルタイ
プが２％程度であるのが一般的であり，艶消剤含有量が
少ないほど光沢感があり，多いほど透け感はなくなるこ
とは周知のとおりであり，本発明は，艶消剤含有量の異
なる２種類の合成繊維を使用し，目的を達成するもので
ある。The above synthetic fiber contains a matting agent,
The content of the synthetic fiber used for the front reed is 0.1% or less, and the content of the synthetic fiber used for the medium reed is 2.0% or more. Titanium oxide is generally used as a matting agent, and it is preferable to use fine particles of titanium oxide in the present invention. The content of the matting agent in the synthetic fiber is 0.05 for bright type, depending on the raster type.
%, Semi-dull type is about 0.5%, full-dull type is about 2%, and it is well known that the smaller the content of the matting agent, the more glossy, and the greater the content, the less transparent. The present invention achieves the object by using two kinds of synthetic fibers having different matting agent contents.

【００１１】次に，後筬に使用する弾性糸としては，ポ
リウレタン系弾性糸やポリエーテルエステル系弾性糸が
挙げられ，切断伸度が４００％以上のものである。ポリ
ウレタン系弾性糸は，ジオールとジイソシアネートの重
付加により生成するポリウレタンを紡糸して得られる弾
性糸（スパンデックス）であり，一方ポリエーテルエス
テル系弾性糸は，ハードセグメントをポリエステルと
し，ポリブチレンテレフタレートを主とするポリエステ
ルを用い，分子量５００〜５０００の直鎖状ポリアルキ
レングリコールをソフトセグメントとするポリエーテル
エステルブロック共重合体を通常の溶融紡糸装置を用
い，紡糸，延伸することによって得られる弾性糸であっ
て，耐熱性が高いので，ポリエステル繊維の染色仕上げ
時の染色温度１３０℃でも劣化が少ない弾性糸である。Next, examples of elastic yarns used for the rear reed include polyurethane type elastic yarns and polyether ester type elastic yarns, which have a breaking elongation of 400% or more. Polyurethane elastic yarn is an elastic yarn (spandex) obtained by spinning polyurethane produced by polyaddition of diol and diisocyanate, while polyetherester elastic yarn uses polyester as a hard segment and mainly polybutylene terephthalate. An elastic yarn obtained by spinning and drawing a polyester ester block copolymer having a molecular weight of 500 to 5000 and a linear polyalkylene glycol having a soft segment as a soft segment using an ordinary melt spinning device. Since it has high heat resistance, it is an elastic yarn that is less deteriorated even at a dyeing temperature of 130 ° C during dyeing and finishing of polyester fiber.

【００１２】これらの弾性糸の繊度は，用途からみて２
０〜７０デニールが適しているが，４０デニールが一般
的であり，これを積極送り出し装置を有する専用整経機
にてドラフト２００％程度で整経し，使用する。The fineness of these elastic yarns is 2 from the viewpoint of use.
Although 0 to 70 denier is suitable, 40 denier is generally used, and this is warped with a dedicated warper having a positive feeding device at a draft of about 200% and used.

【００１３】次に，本発明においては，前筬と中筬のア
ンダーラップが同方向で，かつ後筬のアンダーラップが
これらと逆方向である組織で編成する。使用組織は，図
１にトリコットのモデル図を示したが，ニードルによっ
て形成されたループがアンダーラップ部によって接続さ
れながら編地を編成していき，編地表裏の関係は，一方
にループ面，他方にアンダーラップ面となるが，光沢感
を必要とする本発明の場合には，アンダーラップ面を使
用表面とする。また，アンダーラップ糸は，特殊な組織
を除き，一般的にはアンダーラップ面から見て前筬→中
筬→後筬の順に後に配列し，前筬に使用した繊維が常に
表面に露出している。また，アンダーラップの方向性と
は，図２に本発明の組織の一例を示したが，図中矢印部
がアンダーラップであるが，前筬の矢印部と中筬のそれ
とは「右上がり」に同方向であり，後筬は「左上がり」
に逆方向である。本発明におけるアンダーラップの方向
性とはこの意味である。Next, in the present invention, knitting is performed with a structure in which the underlaps of the front and the reeds are in the same direction and the underlaps of the rear reed are in the opposite direction. The tissue used is a tricot model diagram shown in Fig. 1. The knitted fabric is knitted while the loops formed by the needles are connected by the underlap portion. On the other hand, the underlap surface is used, but in the case of the present invention that requires a glossy feeling, the underlap surface is used. Except for a special design, the underlap yarns are generally arranged rearward in the order of front reed → middle reed → rear reed when viewed from the underlap surface, and the fibers used for the front reed are always exposed on the surface. There is. As for the direction of underlap, an example of the structure of the present invention is shown in FIG. 2. The arrow part in the figure is underlap, but the arrow part of the front reed and that of the middle reed are “upward to the right”. It is in the same direction, and the rear reed is “up to the left”
In the opposite direction. The directionality of the underlap in the present invention has this meaning.

【００１４】[0014]

【作用】編地表面部を編成する前筬に艶消剤含有量の少
ない合成繊維を使用し，その前筬のアンダーラップより
内側に存し，表面には露出することのない中筬に艶消剤
含有量の多い合成繊維を使用すると，必ず前筬のアンダ
ーラップ部は中筬のアンダーラップ部より表面を編成す
るため，表面部の光沢感は含有量の少ないブライト感と
なり，その内側に存する含有量の多い中筬糸が「透け防
止」となり，光沢感があり，かつ透けない編地が編成さ
れる。[Function] Synthetic fibers with a low matting agent content are used in the front reed for knitting the surface of the knitted fabric, and the inner reed is exposed inside the underlap of the front reed and is not exposed on the surface. When a synthetic fiber with a high content of an eraser is used, the underlap portion of the front reed is always knitted on the surface more than the underlap portion of the middle reed, so the glossiness of the surface becomes a bright feeling with a small content, and The existing middle reed yarn, which has a large content, serves as a “prevention of see-through”, and a knitted fabric having a glossy feeling and not see-through is knitted.

【００１５】また，前筬と中筬はアンダーラップが同方
向，後筬は逆方向の組織を組み合わせることにより，伸
縮性に富み，かつ寸法安定性のある編地を編成すること
ができる。By combining the structures of the front reed and the middle reed with the underlaps in the same direction and the rear reeds in the opposite direction, a knitted fabric having excellent stretchability and dimensional stability can be knitted.

【００１６】[0016]

【実施例】次に，本発明を実施例によって具体的に説明
するが，実施例における布帛の性能の測定，評価は，下
記の方法で行った。EXAMPLES Next, the present invention will be described in detail with reference to Examples. Measurement and evaluation of the performance of the cloths in Examples were carried out by the following methods.

【００１７】（１）透け防止性 標準状態に２４時間放置した試料及び水に浸漬後マング
ルで絞り含水率１００％とした試料について，日立Ｕ−
３４００自記分光光度計にて，測定波長４００〜８００
ｎｍの可視光線の透過率を測定した。(1) Anti-transparency Hitachi U-for a sample left in a standard state for 24 hours and a sample dipped in water and squeezed with a mangle to have a water content of 100%
Measurement wavelength 400-800 with 3400 self-recording spectrophotometer
The transmittance of visible light of nm was measured.

【００１８】（２）編地の伸縮性 ＪＩＳ Ｌ−１０１８定速伸長法に準じ，１．５kg荷重
時の編地の伸長回復率を測定した。(2) Stretchability of the knitted fabric The stretch recovery rate of the knitted fabric under a load of 1.5 kg was measured according to JIS L-1018 constant velocity stretching method.

【００１９】実施例１ ナイロン６チップに艶消剤として粒径０．２５μｍの酸
化チタンを０．０５重量％添加したポリマーを紡糸，延
伸した４０デニール１２フィラメントのナイロン糸Ａを
カールマイヤー社製トリコット編機ＫＳ−３，２８Ｇの
前筬に，同ナイロン６チップに同酸化チタンを４．０重
量％添加したポリマーを紡糸，延伸した４０デニール１
２フィラメントのナイロン糸Ｂを中筬に配し，積極送り
出し装置を有するリバー社製弾性糸専用整経機で整経し
たポリウレタン系弾性糸４０デニール／６フィラメント
を後筬に配し，図１に示した前筬１−０／３−４，中筬
１−０／２−３，後筬１−２／１−０の組織で，編立コ
ース６０コース／インチ，編立幅１７９インチの本発明
生機を編成した。Example 1 A 40 denier 12-filament nylon yarn A having 40 denier and 12 filaments spun and stretched with a polymer obtained by adding 0.05% by weight of titanium oxide having a particle size of 0.25 μm to a nylon 6 chip as a matting agent was made by Karl Mayer Tricot. 40 denier 1 obtained by spinning and stretching a polymer in which 4.0% by weight of titanium oxide was added to the nylon 6 tip of the nylon 6 tip in the front reed of the knitting machine KS-3, 28G.
A 2-filament nylon yarn B is placed in the middle reed, and 40 denier / 6 filaments of polyurethane elastic yarn warped by a warper for elastic yarn manufactured by River Co., which has a positive feeding device, is placed in the rear reed. Book with a knitting course of 60 courses / inch and a knitting width of 179 inches, with the organization of the front reed 1-0 / 3-4, the middle reed 1-0 / 2-3, and the rear reed 1-2 / 1-0 shown The invention machine was organized.

【００２０】次に，この生機にリラックス，精練，仕上
げセットを行い，密度１００コース／インチ，６０ウェ
ール／インチの本発明の水着用白色編地を得た。Next, this greige was subjected to relaxation, scouring, and finishing setting to obtain a white knitted fabric of the present invention having a density of 100 courses / inch and 60 wales / inch.

【００２１】比較例１ 実施例１において，前筬，中筬共にナイロン糸Ａを配し
て編成すること以外は実施例１と同条件にて白色編地を
得て，比較例１とした。Comparative Example 1 A white knitted fabric was obtained under the same conditions as in Example 1 except that nylon yarn A was arranged for both the front reed and the middle reed, and a white knitted fabric was obtained.

【００２２】得られた実施例１と比較例１の透け防止性
および伸縮性能の評価結果を表１に示した。Table 1 shows the evaluation results of the see-through preventive property and the stretchability of the obtained Example 1 and Comparative Example 1.

【００２３】[0023]

【表１】 [Table 1]

【００２４】表１の結果で明らかなごとく，実施例１
は，透け防止性に優れ，また，伸縮性能も十分な編地で
あった。これに対し酸化チタンの含有量の少ないナイロ
ンのみを前筬と中筬に用いた比較例１は，光線の透過を
遮る物質の量が少なく，標準状態及び含水率１００％時
の可視光線の透過率が大きく，透け防止性の劣るもので
あった。As is clear from the results of Table 1, Example 1
Was a knitted fabric with excellent see-through prevention and sufficient stretchability. On the other hand, Comparative Example 1 in which only nylon having a low content of titanium oxide was used in the front reed and the middle reed, the amount of the substance that blocks the transmission of light is small, and the visible light transmission at the standard state and the water content of 100% is small. The rate was high and the anti-see-through property was poor.

【００２５】実施例２ ポリエステルチップに艶消剤として粒径０．１５μｍの
酸化チタンを０．０２重量％添加したポリマーを紡糸，
延伸した４０デニール２４フィラメントのポリエステル
糸Ａをカールマイヤー社製トリコット編機ＫＳ−３，２
８Ｇの前筬に，，同ポリエステルチップに同酸化チタン
を５．０重量％添加したポリマーを紡糸，延伸した３０
デニール１２フィラメントのポリエステル糸Ｂを中筬に
配し，，積極送り出し装置を有するリバー社製弾性糸専
用整経機で整経したポリウレタン系弾性糸４０デニール
／６フィラメントを後筬に配し，図１に示した前筬１−
０／３−４，中筬１−０／２−３，後筬１−２／１−０
の組織で，編立コース５０コース／インチ，編幅１３０
インチおよび編立ランナーも前筬２１５cm／ラック，中
筬１８５cm／ラック，後筬９５cm／ラックと同条件にて
編立て，生機を編成後，リラックス，精練，熱処理を行
い，仕上げ密度９０コース／インチ，５６ウェール／イ
ンチ編立コース６０コース／インチ，編立幅１７９イン
チの本発明の水着用白色編地を得た。Example 2 A polymer prepared by adding 0.02% by weight of titanium oxide having a particle diameter of 0.15 μm to a polyester chip as a matting agent is spun,
A 40-denier, 24-filament polyester filament A, which has been drawn, is used as a tricot knitting machine KS-3,2 manufactured by KARL MAYER.
A polymer prepared by adding 5.0% by weight of titanium oxide to the same polyester chip was spun and stretched on an 8G front reed 30
Polyester thread B of denier 12 filaments is placed in the middle reed, and 40 denier / 6 filaments of polyurethane elastic thread warped by the warp machine for elastic threads made by River Co. having an active feeding device is placed in the rear reed. Front reed 1 shown in 1-
0 / 3-4, medium reed 1-0 / 2-3, rear reed 1-2 / 1-0
Organization, knitting course 50 courses / inch, knitting width 130
Inch and knitting runners are knitted under the same conditions as the front reed 215 cm / rack, middle reed 185 cm / rack, and rear reed 95 cm / rack. After knitting the raw material, relaxing, scouring and heat treatment are performed, and finish density is 90 courses / inch. , 56 wales / inch knitting course 60 courses / inch, and a white knitted fabric for water use of the present invention having a knitting width of 179 inches.

【００２６】比較例２ 実施例２において，中筬の組織を１−０／２−３から２
−３／１−０に変えてアンダーラップの方向を実施例１
と逆方向にしたこと以外は実施例１と同様にして水着用
白色編地を得て，比較例２とした。Comparative Example 2 In Example 2, the structure of the medium reed was changed from 1-0 / 2-3 to 2
-3 / 1-0, the direction of underlap is changed to the first embodiment.
A white knitted fabric for water wearing was obtained in the same manner as in Example 1 except that the direction was reversed to that of Comparative Example 2.

【００２７】比較例３ ポリエステルチップに同酸化チタンを０．０２重量％添
加したポリマーを紡糸，延伸した７０デニール３６フィ
ラメントのポリエステル糸Ｃをカールマイヤー社製トリ
コット編機ＫＳ−３，２８Ｇの前筬に，積極送り出し装
置を有するリバー社製弾性糸専用整経機で整経したポリ
ウレタン系弾性糸４０デニール／６フィラメントを後筬
に配し，前筬１−０／２−３，後筬１−２／１−０の組
織で，編立コース５０コース／インチ，編幅１３０イン
チおよび編立ランナーも前筬２１５cm／ラック，中筬１
８５cm／ラック，後筬９５cm／ラックと同条件にて編立
て，生機を編成後，リラックス，精練，熱処理を行い，
仕上げ密度９０コース／インチ，５６ウェール／インチ
編立コース６０コース／インチ，編立幅１７９インチの
水着用白色編地を得て，比較例３とした。Comparative Example 3 A polyester yarn C of 70 denier 36 filaments obtained by spinning and drawing a polymer in which 0.02% by weight of the same titanium oxide was added to a polyester chip was used in a reed knitting machine KS-3, 28G manufactured by Karl Mayer. In addition, 40 denier / 6 filaments of polyurethane elastic yarn warped by a warp machine exclusively for elastic yarn manufactured by River Co., which has a positive feeding device, is arranged in the rear reed, and the front reed 1-0 / 2-3 and the rear reed 1- Organization of 2 / 1-0, knitting course 50 courses / inch, knitting width 130 inches, and knitting runner also front reed 215 cm / rack, middle reed 1
85cm / rack and rear reed 95cm / rack are knitted under the same conditions, after knitting the raw machine, relax, scouring, heat treatment,
Comparative Example 3 was obtained by obtaining a white knitted fabric with a finishing density of 90 courses / inch, 56 wales / inch knitting course of 60 courses / inch, and a knitting width of 179 inches.

【００２８】得られた実施例２及び比較例２〜３の透け
防止性及び伸縮性能の評価結果を表２に示した。Table 2 shows the evaluation results of the anti-transparency and the stretchability of the obtained Example 2 and Comparative Examples 2 to 3.

【００２９】[0029]

【表２】 [Table 2]

【００３０】表２の結果で明らかなごとく，実施例２
は，透け防止性に優れ，また，伸縮性能は，前筬と中筬
のアンダーラップを同方向にすることにより低下せず，
フィット性に優れた編地を得ることができた。これに対
しアンダーラップの方向を逆方向にした比較例２は，透
け防止性は良好であるが，アンダーラップが左右に組織
し、外力に対し変形しにくい組織となっているため、経
緯方向共に伸縮性が劣り、水着用途には適さないもので
あった。また，酸化チタンの含有量の少ないポリエステ
ルのみを用いた比較例２は，伸縮性は良好であるが，標
準状態及び含水率１００％時の可視光線の透過率が大き
く，透け防止性の劣るものであった。As is clear from the results in Table 2, Example 2
Is excellent in see-through prevention, and the stretching performance does not decrease by making the underlaps of the front and middle reeds in the same direction,
It was possible to obtain a knitted fabric with excellent fit. On the other hand, in Comparative Example 2 in which the direction of the underlap is reversed, the anti-seepage property is good, but the underlap has a structure on the left and right and is a structure that is not easily deformed by an external force. The stretchability was poor and it was not suitable for swimwear. Further, Comparative Example 2 using only the polyester having a low content of titanium oxide has a good stretchability, but has a large visible light transmittance at the standard state and a water content of 100%, and is inferior in the transparency prevention property. Met.

【００３１】[0031]

【発明の効果】本発明の白色布帛は，透け防止性に優れ
ており，また，高伸縮性能も有しているので，従来より
着用中に肌が透けてしまう欠点があるため商品拡大でき
なかった衣料分野，特に水着において，商品拡大が可能
となる。EFFECTS OF THE INVENTION The white fabric of the present invention is excellent in anti-sheer property and also has a high stretchability, so that it has a drawback that the skin becomes transparent during wearing, so that the product cannot be expanded. It is possible to expand products in the clothing field, especially in swimwear.

【図面の簡単な説明】[Brief description of drawings]

【図１】トリコットのループモデル図である。FIG. 1 is a tricot loop model diagram.

【図２】本発明の編成組織図の一例である。FIG. 2 is an example of a knitting organization chart of the present invention.

【符号の説明】[Explanation of symbols]

１ アンダーラップ ２ ループ 1 underlap 2 loop

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 経編機の前筬に艶消剤の含有量が０．１
％以下である合成繊維を，中筬に艶消剤の含有量が２．
０％以上である合成繊維を，後筬に切断伸度が４００％
以上である弾性糸を使用し，前筬と中筬のアンダーラッ
プが同方向で，かつ後筬のアンダーラップが逆方向の組
織で編成することを特徴とする経編地の製造方法。1. The content of the matting agent in the front reed of the warp knitting machine is 0.1.
% Of synthetic fiber, the content of the matting agent in the middle reed is 2.
Synthetic fiber of 0% or more has a cutting elongation of 400% in the rear reed.
A method for manufacturing a warp knitted fabric, which comprises using the elastic yarn as described above, and knitting a structure in which the underlaps of the front reed and the middle reed are in the same direction and the underlaps of the rear reed are in the opposite direction.