JPH08150610A - Producing device for green board - Google Patents
Producing device for green boardInfo
- Publication number
- JPH08150610A JPH08150610A JP29761694A JP29761694A JPH08150610A JP H08150610 A JPH08150610 A JP H08150610A JP 29761694 A JP29761694 A JP 29761694A JP 29761694 A JP29761694 A JP 29761694A JP H08150610 A JPH08150610 A JP H08150610A
- Authority
- JP
- Japan
- Prior art keywords
- steel belt
- sheet
- seal member
- dehydration
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、生板製造装置に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a raw plate manufacturing apparatus.
【０００２】[0002]
【従来の技術】従来、例えば外壁材や屋根瓦等の板状材
を製造する方法としてフローオン方式と呼ばれるものが
ある。この方式は、固定分濃度２０〜４５％という比較
的高濃度のスラリーを循環走行可能なエンドレスの透水
性シート上に単層で且つ所望厚さで供給し、このスラリ
ーに含まれる水分をシートを介してその下方へ吸引除去
することで、シート上に生板を残置形成させるというも
のであり、このようにして得られた生板は所定寸法に切
断された後、養生される（特開平４−１５３００４号公
報参照）。2. Description of the Related Art Conventionally, there is a method called a flow-on method as a method for manufacturing a plate-shaped material such as an outer wall material or a roof tile. In this method, a relatively high concentration slurry having a fixed concentration of 20 to 45% is supplied in a single layer on an endless water-permeable sheet which can be circulated and traveled in a desired thickness, and the moisture contained in this slurry is transferred to the sheet. The raw plate is left to be formed on the sheet by sucking and removing the raw plate through the lower side of the sheet. The raw plate thus obtained is cut into a predetermined size and then cured (Japanese Patent Laid-Open No. Hei 4). -153004).
【０００３】なお、シート上のスラリーから水分を除去
するには、エンドレスチェーンの外周側に箱状をした複
数の減圧脱水部（サクションボックス）を連接状に結合
して、この連接体をシートのエンドレス内側で同期的に
循環走行させ、またシートエンドレス中における所定領
域でシート下面へ幾つかの減圧脱水部を沿接させるよう
にして水分の吸引除去を行っている。In order to remove water from the slurry on the sheet, a plurality of box-shaped vacuum dewatering units (suction boxes) are connected to the outer peripheral side of the endless chain in a concatenated manner, and the concatenated body is connected to the sheet. Moisture is sucked and removed by synchronously circulating running inside the endless and by arranging some depressurized dewatering portions along the lower surface of the seat in a predetermined region in the seat endless.
【０００４】一方、これとは別の水分除去方法として、
減圧脱水部を固定しておき、この上部とシート下面との
間に、エンドレスの金網帯をシートと同期進行的に通過
させるようにするものも知られている。On the other hand, as another water removing method,
It is also known that the depressurized dehydration unit is fixed, and an endless wire mesh band is allowed to pass in synchronization with the sheet between the upper portion and the lower surface of the sheet.
【０００５】[0005]
【発明が解決しようとする課題】減圧脱水部の連接体を
循環走行させる方法では、その連接体の走行がチェーン
駆動によるものであるから、チェーンがスプロケットに
噛合する際のガタがそのまま減圧脱水部及びシートに伝
わり、これらが振動する結果、供給されたスラリーの堆
積厚、即ち生板の形成厚に不均一部分が発生し易くなっ
ていた。また、減圧脱水部の相互間では水分除去ができ
ないため、このことも生板の形成圧を不均一化させる原
因となっていた。In the method of circulating traveling of the connecting body of the decompression / dehydration unit, since the traveling of the connection unit is driven by the chain, the play when the chain meshes with the sprocket is directly maintained in the decompression / dehydration unit. Moreover, as a result of being transmitted to the sheet and vibrating, the deposited thickness of the supplied slurry, that is, the non-uniform portion of the formed thickness of the green plate is likely to occur. Further, since water cannot be removed between the reduced pressure dehydration units, this also causes the forming pressure of the green plate to be non-uniform.
【０００６】そのうえ、複数の減圧脱水部を走行させる
うえで大型の駆動装置が必要となり、ランニングコスト
が高騰化するわりに、生産性に劣る（減圧脱水部の連接
体を高速走行できない）という問題もあった。一方、金
網帯を循環走行せせる方法では、金網帯が目詰まりし易
く、頻繁に清掃しなければならない欠点があった。また
構造的に緻密であるため破損の頻度も高く、金網帯全体
を比較的早期のうちに交換しなければならないので、極
めて不経済であった。In addition, a large drive unit is required to run a plurality of decompression / dehydration units, and the running cost rises, but the productivity is inferior (the connecting body of the decompression / dehydration units cannot run at high speed). there were. On the other hand, the method of circulating the wire mesh band has a drawback that the wire mesh band is easily clogged and must be cleaned frequently. Moreover, since it is structurally dense, it is frequently damaged and the entire wire mesh band must be replaced in a relatively early period, which is extremely uneconomical.
【０００７】本発明は、上記事情に鑑みてなされたもの
であって、厚さが均一な生板を製造することができると
共に、ランニングコストの低廉化を図ることができるよ
うにした生板製造装置を提供することを目的とする。The present invention has been made in view of the above circumstances, and it is possible to manufacture a raw plate having a uniform thickness, and at the same time, to reduce the running cost. The purpose is to provide a device.
【０００８】[0008]
【課題を解決するための手段】本発明では、上記目的を
達成するために、次の技術的手段を講じた。即ち、本発
明では、循環走行可能とされたエンドレスの透水性シー
トと、該シートのエンドレス内側を所定領域においてシ
ートと面状に沿接しつつ同期走行するようになされたエ
ンドレスの透水性スチールベルトと、シートにおける上
流側適所の上部に設けられたスラリー供給部と、シート
とスチールベルトとが沿接走行する領域内であってスチ
ールベルトの下部に設けられた減圧脱水部とを具備し、
スチールベルトはその両側縁部が自由端状に張り出した
状態を保持して走行できるように当該両側縁部よりも内
側の上面部がシール部材により押圧されていることを特
徴としている。In order to achieve the above object, the present invention takes the following technical means. That is, in the present invention, an endless water-permeable sheet that is capable of circulating travel, and an endless water-permeable steel belt that is configured to travel in parallel with the sheet in a predetermined region inside the endless inner surface of the sheet. A slurry supply unit provided in an upper portion of an upstream proper position in the sheet, and a reduced pressure dehydration unit provided in a lower portion of the steel belt in a region where the sheet and the steel belt travel alongside,
The steel belt is characterized in that the upper surface portion inside the both side edge portions is pressed by the seal member so that the both side edge portions of the steel belt can run while maintaining the state of being bulged in a free end shape.
【０００９】前記シール部材は、スチールベルトへの押
圧部より更に内側でシートの両側縁部をも押圧するよう
にしてもよい。前記シール部材は、少なくとも減圧脱水
部に対応する領域に設けておくのがよい。The seal member may press both side edges of the sheet further inside the pressing portion against the steel belt. The seal member is preferably provided at least in a region corresponding to the reduced pressure dehydration unit.
【００１０】[0010]
【作用】シートをスチールベルトによって面状に沿接支
持しつつ循環走行させ、減圧脱水部はスチールベルトの
下部へ固定した構成とすることで、従来技術の欠点を略
解消するに至ったが、このようにスチールベルトを用い
ることにより、その側縁部からスラリーがこぼれ落ちる
のを防止し、且つ、スチールベルトの両側縁部が反りを
生じることがないようにする必要がある。そこで、スチ
ールベルトにおける両側縁部の上面部をシール部材で押
圧するようにしてある。The sheet is circulated while being supported laterally by a steel belt, and the depressurization / dehydration section is fixed to the lower part of the steel belt, thereby substantially eliminating the drawbacks of the prior art. By using the steel belt in this manner, it is necessary to prevent the slurry from spilling from the side edge portion thereof and to prevent the both side edge portions of the steel belt from warping. Therefore, the seal members press the upper surfaces of both side edges of the steel belt.
【００１１】そして、この場合において、スチールベル
トの両側縁部がシール部材との摩擦により損傷や磨耗を
起こすのを防止するうえで、シール部材による押圧位置
を、スチールベルトの両側縁部より内側としてある。Further, in this case, in order to prevent the both side edges of the steel belt from being damaged or worn by friction with the seal member, the pressing position by the seal member is set to be inside the both side edges of the steel belt. is there.
【００１２】[0012]
【実施例】以下、本発明の実施例を図面に基づいて説明
する。図１は本発明に係る生板製造装置１を示したもの
で、この生板製造装置１では、少なくとも一方を原動側
とする一対の駆動ローラ２と複数の誘導ローラ（テンシ
ョンローラを含む）３とにより循環走行可能に架設保持
されたエンドレスの透水性シート５に対し、そのエンド
レス内側に、少なくとも一方を原動側とする一対の駆動
ローラ７によってエンドレスのスチールベルト８が循環
走行可能に架設保持されて成る。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 shows a raw plate manufacturing apparatus 1 according to the present invention. In the raw plate manufacturing apparatus 1, a pair of drive rollers 2 and a plurality of guide rollers (including tension rollers) 3 at least one of which is a driving side. With respect to the endless water-permeable sheet 5 which is erected and circulated so as to be able to circulate, an endless steel belt 8 is erected and circulated so as to be circulated by a pair of drive rollers 7, at least one of which is the driving side, inside the endless permeable sheet 5. Consists of
【００１３】スチールベルト８は、駆動ローラ７の相互
間を架設される張り側の部分（以下、「上部ライン」と
言う）が、シート５における駆動ローラ２の相互間部分
（同様に以下、「上部ライン」と言う）に対してその下
から面状に沿接して、これを支持するようになってい
る。スチールベルト８の走行はシート５と同期して（同
速・同方向で）行われ、上記した両者の沿接部分におい
て相対的滑りは生じないものとされている。The steel belt 8 has a portion on the tension side (hereinafter referred to as "upper line") which is installed between the drive rollers 7, and a portion between the drive rollers 2 on the sheet 5 (hereinafter, similarly, " The upper line is referred to as "the upper line", and a planar surface is formed from below to support it. The traveling of the steel belt 8 is performed in synchronization with the seat 5 (at the same speed and in the same direction), and the relative slippage does not occur at the above-mentioned contact portions of the both.
【００１４】シート５における上部ラインの上流部（図
１左側）上方にはスラリー供給部１２が設けられ、この
スラリー供給部１２に対応したシート５の下部には初段
減圧脱水部１３が設けられている。また、スチールベル
ト８における上部ラインの下方側には減圧脱水部１８が
設けられている。A slurry supply unit 12 is provided above the upstream portion of the upper line of the sheet 5 (on the left side in FIG. 1), and a first stage depressurization dehydration unit 13 is provided below the sheet 5 corresponding to the slurry supply unit 12. There is. A decompression dehydration unit 18 is provided below the upper line of the steel belt 8.
【００１５】そして、この減圧脱水部１８に対応するよ
うにシート５の上部には、スラリー上面にフィルムを押
し付けて脱水効果を促進させる脱水促進装置１９及び脱
水の補完を行うプレスローラ装置２０が設けられてい
る。２１はスチールベルト８の洗浄装置、２２はスチー
ルベルト８の異物除去装置、２３はシート５の洗浄装
置、２４はシート５の脱水乾燥装置である。Corresponding to the depressurized dewatering section 18, a dehydration accelerating device 19 for pressing the film against the upper surface of the slurry to accelerate the dewatering effect and a press roller device 20 for complementing the dewatering are provided above the sheet 5. Has been. Reference numeral 21 is a cleaning device for the steel belt 8, 22 is a foreign material removing device for the steel belt 8, 23 is a cleaning device for the sheet 5, and 24 is a dehydrating and drying device for the sheet 5.
【００１６】スチールベルト８はステンレス等の耐蝕性
金属板によって形成されたものであって、図２に示すよ
うにその幅方向一杯にわたり、また長手方向全長にわた
って多数の貫通孔２５が均等配置状に穿設されており、
これによって透水性を呈するようになっている。このス
チールベルト８は、金属板より形成されたものであるた
め、金網帯の場合とは異なり溶接による接合が可能であ
る。そのため、装置装着前の段階ではエンドレスとはし
ない帯状状態（巻回しておけばよい）にしておき、交換
時等の使用に際して溶接によりエンドレスとするような
ことも可能である。このようにすれば、交換作業が容易
且つ迅速に行える利点がある。The steel belt 8 is formed of a corrosion-resistant metal plate such as stainless steel. As shown in FIG. 2, a large number of through holes 25 are evenly arranged over the entire width in the width direction and the entire length in the length direction. Has been drilled,
This allows it to exhibit water permeability. Since the steel belt 8 is made of a metal plate, it can be joined by welding unlike the case of the wire mesh band. Therefore, it is possible to set the belt-like state (which may be wound) that is not endless before mounting the apparatus, and to endlessly weld it at the time of replacement and the like. This has the advantage that replacement work can be performed easily and quickly.
【００１７】スチールベルト８として、表面や裏面の平
滑性が高いものを用いればシート５の沿接支持を平面的
に行え（即ち、シート５の表面性状を平滑にできる）、
また減圧脱水部１８での走行振動を小さくできるので、
生板としての表面平滑度を高めるうえで有益である。ま
た、スチールベルト８の表面や裏面を粗面とした場合に
は、シート５や駆動ローラ７との滑りを防止するうえで
有益となる。これらは、生板（製品）として要請される
形体や、この生板製造装置１における使用現場の状況等
において適宜選択すればよい。If the steel belt 8 having a high smoothness on the front surface and the back surface is used, the sheet 5 can be supported laterally in a planar manner (that is, the surface texture of the sheet 5 can be smoothed).
Moreover, since the traveling vibration in the reduced pressure dehydration unit 18 can be reduced,
It is useful for improving the surface smoothness of the green plate. Further, when the front surface or the back surface of the steel belt 8 is roughened, it is useful for preventing slippage with the sheet 5 or the drive roller 7. These may be appropriately selected depending on the shape required as a raw plate (product), the situation of the use site in the raw plate manufacturing apparatus 1, and the like.
【００１８】シート５はフエルト又は織布等により形成
されており、その素材自体において透水性を有したもの
である。このシート５は、図３に示すようにスチールベ
ルト８よりも幅狭に形成されており、シート５を通じて
下部へ浸透するスラリーは全て、スチールベルト８の幅
方向における貫通孔２５の形成領域（Ｌ寸法参照）内に
収まるようになっている。The sheet 5 is made of felt, woven fabric or the like, and the material itself has water permeability. As shown in FIG. 3, the sheet 5 is formed to be narrower than the steel belt 8, and all the slurry that permeates to the lower portion through the sheet 5 has a through hole 25 forming region (L (See dimensions).
【００１９】初段減圧脱水部１３は、主サクションボッ
クス２７と補助サクションボックス２８とを有して成
る。いずれも、内部が適宜吸引装置（図示略）によって
減圧される中空箱体であって、その上面部はシート５を
面状に支持する摺動支持面となされ、この摺動支持面に
は多数の初段脱水孔（図示略）が形成されている。従っ
て、スラリー供給部１２からシート５上へ供給されたス
ラリーは、この供給時点で直ぐに初段減圧脱水部１３に
より大方の水分除去が行われ、その流動性が抑えられる
と共に、強度の向上が図られるものである。そのため、
それ以降にシート５により搬送される過程において、ス
ラリーが堆積厚に差を生じるような変形を起こしたり、
また亀裂やカケを発生させたりすることが防止される。The first stage reduced pressure dehydration section 13 comprises a main suction box 27 and an auxiliary suction box 28. Each of them is a hollow box body whose inside is appropriately decompressed by a suction device (not shown), and the upper surface part thereof is a sliding support surface for supporting the sheet 5 in a planar manner, and a large number of sliding support surfaces are provided on this sliding support surface. Has a first-stage dehydration hole (not shown). Therefore, most of the water supplied to the sheet 5 from the slurry supply unit 12 is immediately removed by the first stage depressurization dehydration unit 13 at the time of this supply, the fluidity thereof is suppressed, and the strength is improved. It is a thing. for that reason,
After that, in the process of being conveyed by the sheet 5, the slurry may be deformed to cause a difference in deposition thickness,
In addition, cracks and chips are prevented from occurring.
【００２０】減圧脱水部１８は、複数のサクションボッ
クス３１がスチールベルト８の進行方向に沿って並設さ
れて成る。これらサクションボックス３１についても、
内部が適宜吸引装置（図示略）によって減圧される中空
箱体となされたものであり、図２に示すようにその上面
部はスチールベルト８を面状に支持する摺動支持面３１
ａとなっている。The reduced-pressure dehydration section 18 comprises a plurality of suction boxes 31 arranged in parallel along the traveling direction of the steel belt 8. As for these suction boxes 31,
The inside is a hollow box body whose pressure is appropriately decompressed by a suction device (not shown), and the upper surface portion thereof has a sliding support surface 31 for planarly supporting the steel belt 8 as shown in FIG.
It is a.
【００２１】この摺動支持面３１ａには多数の脱水孔３
３が形成されている。これら脱水孔３３は、スチールベ
ルト８の進行方向と直交する方向に長い長孔状をしてい
る。なお、脱水孔３３の中には寸法調整のため丸孔とな
ったものも含まれている。そして、各脱水孔３３の長手
方向開口端（サンクションボックス３１における幅方向
最外側のものを除く）は、スチールベルト８の進行方向
に沿って整列することのない、即ち、不揃い状となるよ
うに配されている。A large number of dehydration holes 3 are formed on the sliding support surface 31a.
3 are formed. These dehydration holes 33 are long holes long in the direction orthogonal to the traveling direction of the steel belt 8. It should be noted that the dehydration hole 33 includes a hole which is a round hole for size adjustment. Then, the longitudinal opening ends of the dehydration holes 33 (except for the outermost one in the width direction of the suction box 31) are not aligned along the traveling direction of the steel belt 8, that is, have an irregular shape. It is distributed.
【００２２】そのため、仮にスチールベルト８が蛇行す
るようなことがあっても、その貫通孔２５と脱水孔３３
とが合致しなくなる確率を可及的に抑えることができ、
全体としての吸引作用を均一化させると共に、吸引圧を
所定以上に確保できる利点がある。また、脱水孔３３が
各貫通孔２５に対して直線的な擦過を行うため、貫通孔
２５の水切りをよくするうえでも有益となっている。Therefore, even if the steel belt 8 meanders, its through hole 25 and dehydration hole 33 are formed.
The probability that and will not match can be suppressed as much as possible,
There is an advantage that the suction action as a whole can be made uniform and the suction pressure can be secured above a predetermined level. Further, since the dehydration holes 33 rub the respective through holes 25 linearly, it is also useful for improving the drainage of the through holes 25.
【００２３】なお、脱水孔３３は、スチールベルト８の
進行方向に対して直交することが限定されるものではな
く、傾斜して交差するものでもよく、またこれらが直線
的又は曲線的に行われるものであってもよい。本実施例
では、スチールベルト８における貫通孔２５の開口率を
３０％、各サクションボックス３１における脱水孔３３
の開口率を２０〜３０％とし、スチールベルト８の走行
時における有効開口率が６〜９％を維持できる状態とし
た。なお、サクションボックス３１には、全脱水孔３３
の開口面積を一挙に変更できるようにしたスライドシャ
ッター式の開口調節機構（図示略）を設けておくのが好
ましい。The dewatering holes 33 are not limited to being orthogonal to the traveling direction of the steel belt 8 and may be inclined and intersecting with each other, and these are performed linearly or curvedly. It may be one. In this embodiment, the opening ratio of the through hole 25 in the steel belt 8 is 30%, and the dehydration hole 33 in each suction box 31.
The opening ratio was set to 20 to 30%, and the effective opening ratio during running of the steel belt 8 was kept to 6 to 9%. In addition, the suction box 31 has a total dehydration hole 33.
It is preferable to provide a slide shutter-type opening adjusting mechanism (not shown) capable of changing the opening area of the above.
【００２４】各サクションボックス３１は、スチールベ
ルト８の進行方向上流側から順に、吸引圧が段階的に高
くなるように制御しておくのが好ましい。このようにす
ることで、スラリーの堆積形状に変形又は亀裂やカケが
生じるのを防止しつつ、脱水が効率的に行えるようにな
る。なお、各サクションボックス３１を一連に連結させ
た一つの長箱状のものとしておき、その内部を複数の室
に仕切って、各室の吸引圧を制御するようにしてもよ
い。It is preferable to control each suction box 31 so that the suction pressure gradually increases in order from the upstream side in the traveling direction of the steel belt 8. By doing so, it becomes possible to efficiently perform dehydration while preventing deformation or cracking or chipping of the slurry deposit shape. Alternatively, the suction boxes 31 may be in the form of a single long box that is connected in series, and the inside thereof may be partitioned into a plurality of chambers to control the suction pressure in each chamber.
【００２５】この減圧脱水部１８において、摺動支持面
３１ａの幅寸法は図３に示すようにスチールベルト８の
幅寸法よりも狭く（但し、シート５の幅寸法よりは広
く）形成されており、従ってスチールベルト８の両側縁
部が摺動支持面３１ａよりも幅方向両外方へ突出するよ
うになっている。そして、摺動支持面３１ａの上部に
は、その幅方向両端部に対応する真上位置で、スチール
ベルト８の両側縁部より内側となる上面部を摺動支持面
３１ａへ押圧するシール部材３５が設けられている。３
６はシール部材３５を保持するブラケットであり、３７
はシール部材３５と減圧脱水部１８との位置関係を一定
に保つためのスペーサである。In the reduced pressure dehydration section 18, the width dimension of the sliding support surface 31a is formed to be narrower than the width dimension of the steel belt 8 (but wider than the width dimension of the sheet 5) as shown in FIG. Therefore, both side edges of the steel belt 8 project outward in the width direction from the sliding support surface 31a. Then, on the upper portion of the sliding support surface 31a, at a position directly above the both ends in the width direction, a seal member 35 for pressing the upper surface portion inside the both side edges of the steel belt 8 to the sliding support surface 31a. Is provided. Three
6 is a bracket for holding the seal member 35, and 37
Is a spacer for keeping the positional relationship between the seal member 35 and the reduced pressure dehydration unit 18 constant.
【００２６】また、このシール部材３５には、スチール
ベルト８に対する押圧部３５ａから内方へ向けて薄肉に
突出する張出部３５ｂが設けられており、この張出部３
５ｂにより、シート５の両側縁部上面をも摺動支持面３
１ａへ押圧するようになっている。このシール部材３５
には、水密性、耐磨耗性に優れ且つ摩擦係数の小さな樹
脂材等が用いられており、シート５上へ供給されたスラ
リーＳがその側縁部乃至スチールベルト８の側縁部から
こぼれ落ちるのを防止するのは勿論、シート５及びスチ
ールベルト８の両側縁部が反るのを防止するうえでも重
要な作用を奏している。Further, the seal member 35 is provided with an overhanging portion 35b which projects inward from the pressing portion 35a against the steel belt 8 in a thin manner.
5b allows the sliding support surface 3 to cover the upper surfaces of both side edges of the seat 5.
It is designed to push to 1a. This seal member 35
A resin material or the like having excellent water-tightness and abrasion resistance and a small friction coefficient is used for this, and the slurry S supplied onto the sheet 5 spills from its side edge portion or the side edge portion of the steel belt 8. Not only does it prevent the sheet 5 and the steel belt 8 from warping, but it also has an important effect in preventing the side edges of the sheet 5 and the steel belt 8 from warping.
【００２７】このシール部材３５は、スチールベルト８
に対する押圧位置（押圧部３５ａ）がその両側縁部より
も内側となっているので、当該スチールベルト８はその
両側縁部が上下両面及び端縁を何ら干渉されることのな
い自由端として走行する状態を保持される。そのため、
スチールベルト８が摩擦により損傷したり磨耗したりす
るのを可及的に防止でき、その長寿命化が図れる。The seal member 35 is a steel belt 8
Since the pressing position (pressing portion 35a) with respect to is on the inner side of the both side edge portions, the steel belt 8 runs with both side edge portions as the upper and lower surfaces and the end edge as free ends without any interference. The state is retained. for that reason,
It is possible to prevent the steel belt 8 from being damaged or worn by friction as much as possible, and the life of the steel belt 8 can be extended.
【００２８】このシール部材３５は、少なくとも減圧脱
水部１８の全長に対応するように設けるのがよく、好ま
しくはスラリー供給部１２から減圧脱水部１８に至るま
での間をも含め、シート５の上部ライン全長にわたって
設けることも可能である。ところで、本実施例では、ス
チールベルト８を循環走行させる駆動ローラ７のうち、
一方のものに、スチールベルト８の蛇行防止装置４０を
設けてある。この蛇行防止装置４０は、駆動ローラ７の
回転軸７ａにおける一端部又は両端部に設けた油圧シリ
ンダ４１の伸縮により、その傾きを変更可能なようにし
たもので、スチールベルト８の走行を監視して蛇行を検
出する適宜監視手段（図示略）と組み合わされてフィー
ドバック制御される。The seal member 35 is preferably provided so as to correspond to at least the entire length of the reduced pressure dehydration unit 18, and preferably, the upper portion of the sheet 5 including the portion from the slurry supply unit 12 to the reduced pressure dehydration unit 18. It is also possible to provide over the entire length of the line. By the way, in the present embodiment, among the drive rollers 7 for circulating the steel belt 8,
A meandering prevention device 40 for the steel belt 8 is provided on one side. The meandering prevention device 40 is configured so that the inclination of the hydraulic cylinder 41 can be changed by expanding and contracting a hydraulic cylinder 41 provided at one end or both ends of the rotary shaft 7a of the drive roller 7, and monitors the traveling of the steel belt 8. Feedback control is performed in combination with an appropriate monitoring means (not shown) for detecting the meandering.
【００２９】また、この蛇行防止装置４０を利用して、
スチールベルト８のテンション調節（スリップ防止制
御）も可能としてある。このようにして成る生板製造装
置１では、シート５及びスチールベルト８を同期走行さ
せつつ、セメント、骨材、水等を適宜配合割合で混練し
て成るスラリーをスラリー供給部１２からシート５上へ
一定供給すると、まずこの供給時点で初段減圧脱水部１
３により初期脱水が行われ、スラリーは所定の保形性及
び強度を有した状況で減圧脱水部１８へと送られる。Further, by utilizing this meandering prevention device 40,
It is also possible to adjust the tension of the steel belt 8 (slip prevention control). In the green board manufacturing apparatus 1 configured as described above, while the sheet 5 and the steel belt 8 are synchronously run, a slurry formed by kneading cement, aggregate, water, etc. at an appropriate mixing ratio is supplied from the slurry supply unit 12 onto the sheet 5. First, the first stage depressurization dehydration unit 1
Initial dehydration is carried out by No. 3, and the slurry is sent to the reduced pressure dehydration unit 18 in a state having a predetermined shape retention property and strength.
【００３０】この減圧脱水部１８では、脱水促進装置１
９の援助作用を受けてスラリー中の水分が高効率で除去
され、またプレスローラ装置２０によって脱水作用の補
完がなされてシート５上に生板が残置形成されるように
なる。この生板は、図示しない次工程において所定長さ
に切断され、オートクレーブ等の養生を経て、外壁材や
屋根瓦等の板状材として製品化される。In the reduced pressure dehydration unit 18, the dehydration acceleration device 1
The moisture in the slurry is removed with high efficiency by the assisting action of the sheet 9, and the dehydration action is complemented by the press roller device 20, so that the green plate is left on the sheet 5. This green board is cut into a predetermined length in the next step (not shown), and after being cured by an autoclave or the like, it is commercialized as a plate-shaped material such as an outer wall material or a roof tile.
【００３１】この生板製造装置１では、スチールベルト
８を用いていることに伴い、高テンションをかけること
ができ、これによってその走行速度の高速化が可能とな
っている。本実施例では２０ｍ／ｍｉｎとした。因み
に、従来、減圧脱水部の連接体をチェーン駆動により循
環走行させるものにあっては、８ｍ／ｍｉｎ程度にする
のが限度であり、また金網帯を用いたものでも、せいぜ
い１５ｍ／ｍｉｎであった。In this raw plate manufacturing apparatus 1, since the steel belt 8 is used, a high tension can be applied, which allows the traveling speed to be increased. In this embodiment, the speed is 20 m / min. By the way, conventionally, in the case where the connecting body of the vacuum dewatering section is circulated by the chain drive, the limit is about 8 m / min, and even the one using the wire netting band is at most 15 m / min. It was
【００３２】また、この場合の出力を比較すると、上記
実施例ではスチールベルト８の走行に用いるモータが７
４ｋｗのもので十分であったのに対し、減圧脱水部の連
接体をチェーン駆動するのに用いるモータでは１８０ｋ
ｗのものが必要であり、金網帯を走行させるのに用いる
モータでも８５ｋｗのものが必要であった。Further, comparing the outputs in this case, in the above embodiment, the motor used for traveling the steel belt 8 is 7
The motor used to drive the chain of the reduced pressure dehydration unit is 180k, while the 4kW one was sufficient.
The motor used for running the wire mesh belt also needed the motor of 85 kW.
【００３３】[0033]
【発明の効果】本発明は、上述の構成を具備するもので
あって、シートをスチールベルトによって面状に沿接支
持しつつ循環走行させ、減圧脱水部はスチールベルトの
下部へ固定した構成とすることで従来技術の欠点を略解
消すると共に、スチールベルトの両側縁部より内側をシ
ール部材で押圧するようにしているので、その側縁部か
らスラリーがこぼれ落ちることがなく、しかもスチール
ベルトの両側縁部に反りが生じることもない。そのた
め、スラリーに無駄が生じず、生板の形成厚に不均一が
生じることも可及的に防止できる。The present invention has the above-mentioned structure, in which the sheet is circulated while being supported laterally by a steel belt, and the reduced pressure dehydration section is fixed to the lower part of the steel belt. By substantially eliminating the drawbacks of the prior art by doing so, the inside of both side edges of the steel belt is pressed by the seal members, so that the slurry does not spill from the side edges, and the steel belt No warpage occurs on both side edges. Therefore, the slurry is not wasted, and unevenness in the thickness of the green plate can be prevented as much as possible.
【００３４】また、スチールベルトの両側縁部がシール
部材と接触することがないので、摩擦による損傷や磨耗
がなく、その長寿命化が図れる。従って、ランニングコ
ストの低廉化が図れる。Further, since both side edges of the steel belt do not come into contact with the seal member, there is no damage or abrasion due to friction, and the life of the steel belt can be extended. Therefore, the running cost can be reduced.
【図１】本発明に係る生板製造装置を模式的に示す側面
図である。FIG. 1 is a side view schematically showing a raw plate manufacturing apparatus according to the present invention.
【図２】減圧脱水部とスチールベルトとを示す平面図で
ある。FIG. 2 is a plan view showing a vacuum dewatering unit and a steel belt.
【図３】図１のＡ−Ａ線断面図である。FIG. 3 is a sectional view taken along line AA of FIG. 1;
１ 生板製造装置 ５ シート ８ スチールベルト １２ スラリー供給部 １３ 初段減圧脱水部 １８ 減圧脱水部 ３１ａ 摺動支持面 ３３ 脱水孔 ３５ シール部材 1 Raw Plate Manufacturing Device 5 Sheet 8 Steel Belt 12 Slurry Supply Section 13 First Stage Decompression / Dehydration Section 18 Decompression / Dehydration Section 31a Sliding Support Surface 33 Dehydration Hole 35 Sealing Member
Claims (3)
性シート（５）と、該シート（５）のエンドレス内側を
所定領域においてシート（５）と面状に沿接しつつ同期
走行するようになされたエンドレスの透水性スチールベ
ルト（８）と、シート（５）における上流側適所の上部
に設けられたスラリー供給部（１２）と、シート（５）
とスチールベルト（８）とが沿接走行する領域内であっ
てスチールベルト（８）の下部に設けられた減圧脱水部
（１８）とを具備し、スチールベルト（８）はその両側
縁部が自由端状に張り出した状態を保持して走行できる
ように当該両側縁部よりも内側の上面部がシール部材
（３５）により押圧されていることを特徴とする生板製
造装置。1. An endless water-permeable sheet (5) which can be circulated, and an endless inner side of the sheet (5), which runs synchronously while being in planar contact with the sheet (5) in a predetermined region. And an endless water-permeable steel belt (8), a slurry supply section (12) provided at an upper portion of the seat (5) at an upstream proper position, and a seat (5)
And a depressurized dehydration section (18) provided below the steel belt (8) in a region where the steel belt (8) travels alongside the steel belt (8). An apparatus for producing a raw plate, characterized in that an upper surface portion inside the both side edge portions is pressed by a seal member (35) so that the vehicle can travel while maintaining a state of being projected in a free end shape.
ルト（８）への押圧部より更に内側でシート（５）の両
側縁部をも押圧するようになっていることを特徴とする
請求項１記載の生板製造装置。2. The seal member (35) is adapted to press both side edges of the sheet (5) further inside the pressing portion against the steel belt (8). 1. The raw plate manufacturing apparatus according to 1.
減圧脱水部（１８）に対応する領域に設けられているこ
とを特徴とする請求項１又は請求項２記載の生板製造装
置。3. The raw plate manufacturing apparatus according to claim 1 or 2, wherein the seal member (35) is provided at least in a region corresponding to the reduced pressure dehydration section (18).