JPH08143720A - Heat sealant layer and cover material - Google Patents
Heat sealant layer and cover materialInfo
- Publication number
- JPH08143720A JPH08143720A JP30947294A JP30947294A JPH08143720A JP H08143720 A JPH08143720 A JP H08143720A JP 30947294 A JP30947294 A JP 30947294A JP 30947294 A JP30947294 A JP 30947294A JP H08143720 A JPH08143720 A JP H08143720A
- Authority
- JP
- Japan
- Prior art keywords
- sealant layer
- ethylene
- heat sealant
- heat
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、主としてポリプロピレ
ン系樹脂製の容器の開放口部を閉塞する蓋材に利用され
るヒートシーラント層に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat sealant layer mainly used as a lid material for closing an opening of a polypropylene resin container.
【０００２】[0002]
【従来の技術】プリン、ゼリー、アイスクリーム、調味
料、ジュース、酒精飲料等の食品を封入する容器に、ポ
リプロピレン系樹脂による合成樹脂の容器が汎用されて
おり、その蓋材として高度の密封性と易剥離性を兼ね備
えた熱融着材が必要であり、ポリエチレンとポリプロピ
レンとの混合樹脂、あるいは、エチレン−酢酸ビニル共
重合体を主成分として、これに粘着付与剤やエチレン−
α・オレフィン共重合体を配合したものなどが知られて
いる。BACKGROUND ART Synthetic resin containers made of polypropylene resin are widely used as containers for foods such as pudding, jelly, ice cream, seasonings, juices, alcoholic beverages, etc. And a heat-sealant having both easy peelability is required, and a mixed resin of polyethylene and polypropylene, or an ethylene-vinyl acetate copolymer as a main component, to which a tackifier or ethylene-
Known are those containing an α-olefin copolymer.
【０００３】[0003]
【発明が解決しようとする課題】しかし、従来のこの種
の熱融着材は熱接着強度が不安定であり、確実な熱融着
がなされていない場合があったり、開封時にその熱融着
部でスムースに剥離せず、熱融着材が破断してしまい、
易開封性に欠ける等の問題があった。そこで、本発明の
目的としては、ポリプロピレン樹脂製の容器に対し、確
実な熱融着が可能であって、消費者が飲用あるいは食用
する際には、易開封性を示す蓋となるような特性を有
し、加工および包装の工程においても問題のないヒート
シーラント層を提供することである。However, the heat-bonding strength of this type of conventional heat-bonding material is unstable, and there is a case where reliable heat-bonding is not performed, or the heat-bonding at the time of opening. Part does not peel off smoothly, the heat-sealing material breaks,
There was a problem such as lack of easy opening. Therefore, as an object of the present invention, a container made of polypropylene resin can be reliably heat-sealed, and when the consumer drinks or eats, it has a property such that the container has an easily openable property. And to provide a heat sealant layer having no problems in the processing and packaging steps.
【０００４】[0004]
【課題を解決するための手段】種々検討の結果、本発明
者はポリプロピレン製の容器に対する蓋材として、本発
明の目的にあった特性を示すような樹脂組成物により製
膜されたヒートシーラント層を得ることができた。本発
明によるヒートシーラント層は次のようなものである。
すなわち、エチレン−α・オレフィン共重合体、ポリプ
ロピレン系樹脂、ポリエチレン、エチレン−酢酸ビニル
共重合体とによる混合樹脂によるヒートシーラント層と
する、または、必要に応じて前記混合樹脂とポリエチレ
ン、あるいは、エチレン−α・オレフィン共重合体とを
共押出し法により製膜してヒートシーラント層とするも
のである。As a result of various studies, the present inventor has found that a heat sealant layer formed by a resin composition as a cover material for a container made of polypropylene, the resin composition having the characteristics suitable for the purpose of the present invention. I was able to get The heat sealant layer according to the present invention is as follows.
That is, a heat sealant layer is formed by a mixed resin of ethylene-α / olefin copolymer, polypropylene resin, polyethylene, and ethylene-vinyl acetate copolymer, or if necessary, the mixed resin and polyethylene, or ethylene. A film is formed by a co-extrusion method with an α-olefin copolymer to form a heat sealant layer.
【０００５】本発明についてさらに詳細に説明する。図
１は本発明によるヒートシーラント層がラミネートされ
た蓋材の構成例を示しており、（Ａ）は単層のヒートシ
ーラント層を接着剤で蓋の基材、例えばアルミ箔と貼り
合わせた例である。（Ｂ）は複層のヒートシーラント層
を同じように蓋基材と貼り合わせた例である。これらの
例においては、アルミ箔基材を例示したが、各種のプラ
スチックフィルムや、紙等を基材とした場合も、ヒート
シーラント層としての機能に変わりは無く、基材がアル
ミ箔に限定されるものではない。更に、フィルム、紙、
箔等のラミネートされた複層基材も使用することができ
る。本発明のヒートシーラント層が利用されるのは、例
えば図２に示すような形状を有するポリプロピレン製の
容器の蓋Ｌであつて、前記ポリプロピレン製の容器Ｐ
（以下、容器という）は、インジェクション成形、ある
いは、シートからのサーモフォーミングによる方法等に
より得られる。容器の口縁部には、ヒートシールのため
のフランジ６が設けられている。通常、このフランジは
巾が狭く、安定した密封性と、易開封性とを要求される
商品の場合には、密封用の蓋材の材質の選定が極めて重
要である。また、蓋Ｌには開封する際に便利な摘まみ口
７が設けられている。次に、容器に蓋材をヒートシール
する装置、一般的には内容物の充填機能と連結された装
置（以下、包装機械という）であるが、前記蓋材が巻き
取り状態で容器の上に供給される包装機械と、容器の開
口部よりやや大きめに打ち抜かれた状態で供給される包
装機械があるが、後者のタイプを使用する場合には、打
ち抜かれた蓋材の平坦性が特に重要である。すなわち、
図２に示すような打ち抜かれた蓋材Ｌがカールしている
と、包装機械上でのトラブルを引き起こして作業性を悪
くし、また所定位置でのヒートシールができなかった
り、極端な場合は折れ曲がったままのヒートシールとな
る場合もある。The present invention will be described in more detail. FIG. 1 shows a constitutional example of a lid material laminated with a heat sealant layer according to the present invention. (A) shows an example in which a single layer heat sealant layer is bonded with an adhesive to a lid base material, for example, an aluminum foil. Is. (B) is an example in which a multi-layer heat sealant layer is similarly attached to a lid base material. In these examples, the aluminum foil base material is exemplified, but even when various plastic films, paper, etc. are used as the base material, the function as the heat sealant layer does not change, and the base material is limited to the aluminum foil. Not something. In addition, film, paper,
Laminated multilayer substrates such as foils can also be used. The heat sealant layer of the present invention is used for, for example, a polypropylene container lid L having a shape as shown in FIG.
(Hereinafter, referred to as a container) can be obtained by injection molding, thermoforming from a sheet, or the like. A flange 6 for heat sealing is provided at the edge of the container. Usually, this flange has a narrow width, and in the case of a product that requires stable sealing property and easy opening property, selection of the material of the sealing lid material is extremely important. Further, the lid L is provided with a grip opening 7 which is convenient when opening the lid. Next, there is a device for heat-sealing the lid material in the container, generally a device connected to the function of filling the contents (hereinafter referred to as a packaging machine). There are wrapping machines that are supplied and wrapping machines that are punched out slightly larger than the opening of the container, but when using the latter type, the flatness of the punched lid material is particularly important. Is. That is,
If the punched lid material L as shown in FIG. 2 is curled, it causes troubles on the packaging machine and deteriorates workability, and heat sealing cannot be performed at a predetermined position. In some cases, the heat seal remains bent.
【０００６】前述のヒートシールの際の、容器フランジ
と蓋材のヒートシーラント用の樹脂組成物との関係にお
いて、本発明におけるヒートシーラント層を構成する樹
脂組成物の各素材の機能について述べる。これらの樹脂
組成物は、蓋材として用いられるが、蓋とするための前
工程があり、前記樹脂組成物を各種の方法により製膜す
るが、その際の製膜性のよいこと、加えて次工程の蓋の
基材フィルムとの貼り合わせにおいても作業上での支障
のないことが重要である。本発明におけるヒートシーラ
ント層を構成する樹脂組成物の主成分のひとつであるエ
チレン−α・オレフィン共重合体は20〜70重量％の範囲
で用いる。エチレン−α・オレフィン共重合体は、ポリ
プロピレン系樹脂製容器との間に熱接着強度を備えさせ
るものであり、エチレンと、ブテン、ペンテン、ヘキセ
ン、ヘプテン、オクテン、4-メチル-1- ペンテン等との
共重合体であり、その密度が0.915未満のものになると
製膜製が悪くなるばかりでなく、耐ブロッキング性も悪
化する。また、密度が0.940 を超えるようになっても製
膜性が悪化する。エチレン−α・オレフィン共重合体
は、前述のとおり、20〜70重量％の範囲で用いるが、本
発明において用いる他の混合樹脂であるポリプロピレン
系樹脂とともに、ポリプロピレン製容器との接着成分と
なるものであり、その混合割合が20％未満の場合は、接
着性が低下し、また、その混合割合が70％を超えると接
着強度が強すぎて、初期の目的である易開封性が失われ
る。後述のように他の混合樹脂との相関においてその配
合割合は微調整する。The function of each material of the resin composition forming the heat sealant layer in the present invention will be described in relation to the container flange and the resin composition for the heat sealant of the lid material in the above heat sealing. These resin compositions are used as a lid material, but there is a pre-process for forming a lid, and the resin composition is formed into a film by various methods. In that case, the film forming property is good. It is important that there is no hindrance in the work even when the lid is attached to the base material film in the next step. The ethylene-α-olefin copolymer, which is one of the main components of the resin composition constituting the heat sealant layer in the present invention, is used in the range of 20 to 70% by weight. The ethylene-α / olefin copolymer is provided with thermal adhesive strength between the polypropylene resin container and ethylene, butene, pentene, hexene, heptene, octene, 4-methyl-1-pentene, etc. When the density of the copolymer is less than 0.915, not only the film-forming property deteriorates, but also the blocking resistance deteriorates. Further, even if the density exceeds 0.940, the film formability deteriorates. As described above, the ethylene-α / olefin copolymer is used in the range of 20 to 70% by weight, but it becomes an adhesive component with the polypropylene container together with the polypropylene resin which is another mixed resin used in the present invention. If the mixing ratio is less than 20%, the adhesiveness is lowered, and if the mixing ratio exceeds 70%, the adhesive strength is too strong and the easy opening property which is the initial purpose is lost. As will be described later, the blending ratio is finely adjusted in correlation with other mixed resins.
【０００７】本発明のヒートシーラント層を構成する他
の樹脂組成物であるポリプロピレン系樹脂は、エチレン
−α・オレフィン共重合体とともにポリプロピレン系樹
脂容器との間に、熱接着強度を備えさせるものであり、
プロピレンのホモポリマー、プロピレンとエチレンとの
共重合体のいずれでも良い。ポリプロピレン系樹脂が25
重量％を超えるようになるとヒートシール強度が過大に
なり、易剥離性に欠ける。エチレン−α・オレフィン共
重合体とポリプロピレン系樹脂の総量が20〜70重量％の
範囲で用いることが望ましい。その総量が20重量％未満
になると、得られる熱融着部の接着強度が弱くなり、消
費者に対して信頼感を与えるような接着強度が得られな
くなるとともに、密封性を保持するに十分な熱融着部が
得られなくなる恐れが生じ、また、その総量が、70重量
％を超えるようになると、ヒートシーラント層を利用し
て形成された熱融着部の接着強度が強くなり、易開封性
の熱融着部が得られなくなる。更には、ポリプロピレン
系樹脂は、エチレン−α・オレフィン共重合体より少な
い重量％の範囲で用いることが望ましい。The polypropylene resin, which is another resin composition constituting the heat sealant layer of the present invention, has a thermal adhesive strength between the ethylene-α / olefin copolymer and the polypropylene resin container. Yes,
Either a propylene homopolymer or a propylene / ethylene copolymer may be used. 25 polypropylene resin
If it exceeds 5% by weight, the heat-sealing strength becomes excessive and the easy peeling property is lacking. It is desirable to use the total amount of the ethylene-α / olefin copolymer and the polypropylene resin in the range of 20 to 70% by weight. If the total amount is less than 20% by weight, the adhesive strength of the resulting heat-sealed portion will be weak, and the adhesive strength that will give the consumer a sense of reliability will not be obtained, and it will be sufficient to maintain the hermeticity. There is a risk that the heat-sealed part will not be obtained, and if the total amount exceeds 70% by weight, the adhesive strength of the heat-sealed part formed by using the heat sealant layer will be strong and easy opening will occur. It becomes impossible to obtain a heat-sealed portion having good properties. Furthermore, it is desirable to use the polypropylene-based resin in the range of less than the weight% of the ethylene-α-olefin copolymer.
【０００８】本発明のヒートシーラント層を構成する他
の樹脂組成物であるポリエチレンは、ポリプロピレン系
樹脂性容器に対して、離型性能を備えさせるものであ
り、低密度ポリエチレン、中密度ポリエチレン、高密度
ポリエチレンのいずれでも良い。ポリエチレンが10重量
％未満になると、ヒートシール強度が過大になり、易剥
離性の熱融着部が得られなくなる。また、ポリエチレン
が70重量％を超えるとヒートシール強度が弱くなり、消
費者に対して信頼感を与えるような接着強度が得られな
くなるとともに、密封性を保持するに十分な熱融着部が
得られなくなる恐れが生じる。[0008] Polyethylene, which is another resin composition constituting the heat sealant layer of the present invention, provides a polypropylene resin container with a releasing property, such as low density polyethylene, medium density polyethylene and high density polyethylene. Any of density polyethylene may be used. If the polyethylene content is less than 10% by weight, the heat-sealing strength becomes excessively large and an easily peelable heat-sealed portion cannot be obtained. Further, when the polyethylene content exceeds 70% by weight, the heat-sealing strength becomes weak and the adhesive strength that gives the consumer a sense of reliability cannot be obtained, and a heat-sealing part sufficient to maintain the sealing property is obtained. There is a fear of being unable to be controlled.
【０００９】本発明のヒートシーラント層を構成する別
の樹脂組成物であるエチレン−酢酸ビニル共重合体は、
エチレンと酢酸ビニルの共重合体（酢酸ビニルが5 〜20
重量％) との共重合体であり、ポリエチレン系樹脂製容
器との熱接着強度を弱くして、易剥離性を備えさせ、剥
離感を向上させるために添加するものである。混合樹脂
において、エチレン−酢酸ビニル共重合体が5 重量％未
満では添加した効果が無く、25重量％を超えると剥離の
際に糸引き現象が認められ、熱融着強度がかえって増大
し、剥離感が低下する。Another resin composition which constitutes the heat sealant layer of the present invention is ethylene-vinyl acetate copolymer,
Copolymer of ethylene and vinyl acetate (vinyl acetate 5-20
% By weight), and is added for the purpose of weakening the thermal adhesive strength with the polyethylene resin container, providing easy peeling property, and improving the peeling feeling. In the mixed resin, if the ethylene-vinyl acetate copolymer is less than 5% by weight, there is no effect, and if it exceeds 25% by weight, a stringing phenomenon is observed at the time of peeling, and the heat fusion strength rather increases, resulting in peeling. Feeling deteriorates.
【００１０】本発明のヒートシーラント層を構成する樹
脂組成物は、該組成物中の樹脂成分が前記の構成からな
るものであって、さらに、顔料、酸化防止剤、滑剤、紫
外線防止剤等の添加成分が必要に応じて添加されている
ものである。なお、前記本発明のヒートシーラント層用
樹脂組成物によるヒートシーラント層は、各樹脂のペレ
ットをヘンシェルミキサー等の混合装置によって混合し
た樹脂組成物、あるいは、混合樹脂を溶融、混練し、こ
れをペレツト化した樹脂組成物を、通常の方法、例え
ば、Ｔダイ法やインフレーション法等によって、厚さ5
〜100 μｍ、好ましくは、20〜50μｍ程度のヒートシー
ラント層として製膜されることが望ましい。In the resin composition constituting the heat sealant layer of the present invention, the resin component in the composition has the above-mentioned constitution, and further, a pigment, an antioxidant, a lubricant, an ultraviolet protective agent, etc. The additive components are added as needed. The heat sealant layer for the heat sealant layer resin composition of the present invention is a resin composition in which pellets of each resin are mixed by a mixing device such as a Henschel mixer, or the mixed resin is melted and kneaded, and then pelletized. The resin composition thus converted into a resin composition having a thickness of 5 by a conventional method such as a T-die method or an inflation method.
It is desirable to form a heat sealant layer having a thickness of about 100 to 100 μm, preferably about 20 to 50 μm.
【００１１】本発明のヒートシーラント層は、単層で用
いても良いが、共押出加工により、ポリエチレンあるい
はエチレン−α・オレフィン共重合体体との多層として
も良い。ポリエチレンあるいはエチレン−α・オレフィ
ン共重合体は、加工がし易く本発明のヒートシーラント
層用混合樹脂をより安定して製膜可能となる。また、前
記ポリエチレンあるいはエチレン−α・オレフィン共重
合体と蓋基材との接着強度( ラミ強度) が安定する。単
層で用いる場合とおなじ厚みの多層フィルムとすれば、
混合樹脂の単価は、単体樹脂の単価よりも高価なのて、
多層ヒートシーラント層としては安価である。また、ポ
リエチレン等の樹脂を用いて、溶融サンドイッチラミを
行う際、基材へのアンカーコートはおこなうが、多層ヒ
ートシーラント層の、前記ポリエチレンやエチレン−α
・オレフィン共重合体の層にはアンカーコート無しでも
強い接着が得られる。The heat sealant layer of the present invention may be used as a single layer, but may be formed as a multilayer with polyethylene or an ethylene-α-olefin copolymer by coextrusion processing. Polyethylene or ethylene-α-olefin copolymer is easy to process, and the mixed resin for heat sealant layer of the present invention can be more stably formed into a film. In addition, the adhesive strength (laminar strength) between the polyethylene or the ethylene-α-olefin copolymer and the lid substrate is stable. If you use a multilayer film with the same thickness as when using a single layer,
Since the unit price of the mixed resin is more expensive than the unit price of the single resin,
It is inexpensive as a multilayer heat sealant layer. Also, when performing melt sandwich laminating using a resin such as polyethylene, anchor coating is performed on the substrate, but the polyethylene or ethylene-α of the multilayer heat sealant layer is used.
-Strong adhesion can be obtained without an anchor coat on the olefin copolymer layer.
【００１２】[0012]
【作用】本発明のヒートシーラント層用樹脂組成物は、
エチレン−α・オレフィン共重合体とポリプロピレン系
樹脂、ポリエチレン系樹脂及びエチレン−酢酸ビニル共
重合体による混合樹脂であり、密度0.915 〜0.940 のエ
チレン−α・オレフィン共重合体及びポリプロピレン系
樹脂とがポリプロピレン製の容器に対し熱融着性能を、
ポリエチレン系樹脂及びエチレン−酢酸ビニル共重合体
とが離型性能を発現するものである。ポリプロピレン系
樹脂製の容器に対する蓋材におけるヒートシーラント層
として利用され、該組成物によるヒートシーラント層を
具備する蓋材は、これを剥離する際のピール感が良好で
あり、蓋材を製造する工程において、製膜性が良好で、
ブロッキング現象等の発生がなく、各種基材との接着性
が良好であるヒートシーラント層を形成し得るものであ
る。The resin composition for heat sealant layer of the present invention comprises
It is a mixed resin of ethylene-α / olefin copolymer and polypropylene resin, polyethylene resin and ethylene-vinyl acetate copolymer, and ethylene-α / olefin copolymer and polypropylene resin of density 0.915 to 0.940 are polypropylene. Heat fusion performance for containers made of
The polyethylene resin and the ethylene-vinyl acetate copolymer exhibit the releasing performance. A lid material that is used as a heat sealant layer in a lid material for a polypropylene resin container and has a heat sealant layer of the composition has a good peel feeling when peeled off, and a step of manufacturing the lid material. In, the film forming property is good,
It is possible to form a heat sealant layer which does not cause a blocking phenomenon or the like and has good adhesiveness to various base materials.
【００１３】[0013]
（１）本発明による樹脂組成物の実施例と比較例につい
て説明する。第１表は前記実施例及び比較例の樹脂組成
割合を重量％で示したものである。それぞれの混合樹脂
を溶融、ペレット化し、２層共押出インフレーション製
膜機を用い、エチレン−α・オレフィン共重合体20μｍ
と、第 1表の各組成のヒートシーラント層10μｍ( 全体
の厚さ30μｍ) のヒートシーラント層用フィルムを得た
後、得られたフィルムのエチレン−α・オレフィン共重
合体の層表面にコロナ処理を施し、厚さ40μｍのアルミ
箔に対して、2 液硬化型ウレタン系接着剤を利用したド
ライラミネート法によって積層し、蓋材用の積層シート
を得た。 （以下余白） 使用した樹脂は下記の通りである。 LLDPE:エチレン−α・オレフィン共重合体 三井石油化学工業株式会社製 ウルトゼックス 2022
L PP:ポリプロピレン 昭和電工株式会社製 KS-063P PE:ポリエチレン 三井石油化学工業株式会社製 ミラソン 16P EVA:エチレン−酢酸ビニル共重合体 住友化学工業株式会社製 エバテート D3022(1) Examples and comparative examples of the resin composition according to the present invention will be described. Table 1 shows the resin composition ratios of the above Examples and Comparative Examples in% by weight. Each mixed resin is melted and pelletized, and a two-layer coextrusion inflation film forming machine is used, and ethylene-α / olefin copolymer 20 μm
After obtaining a film for heat sealant layer of 10 μm (total thickness 30 μm) of heat sealant layer of each composition in Table 1, corona treatment was applied to the surface of ethylene-α / olefin copolymer layer of the obtained film. Then, the aluminum foil having a thickness of 40 μm was laminated by a dry lamination method using a two-component curing type urethane adhesive to obtain a laminated sheet for a lid material. (Below margin) The resins used are as follows. LLDPE: Ethylene-α / olefin copolymer Mitsui Petrochemical Co., Ltd. Ultzex 2022
L PP: Polypropylene Showa Denko KS-063P PE: Polyethylene Mitsui Petrochemical Co., Ltd. Mirason 16P EVA: Ethylene-vinyl acetate copolymer Sumitomo Chemical Co., Ltd. Ebate D3022
【００１４】（２）次いで、前記蓋材用の積層シート
を、直径70mmの円盤状に打ち抜き加工することによって
得られた蓋材を、ポリプロピレン樹脂からなる内径60mm
φ、フランジ部の巾 5mmのカップ状の射出成形容器の開
放口部に接当し、さらに、前記蓋材におけるヒートシー
ラント層とカップ状容器のフランジ部６とを、 200℃で
熱融着することによって、密封容器を得た。前記得られ
た密封容器における熱融着強度の測定結果と評価とを第
２表にまとめて示す。 (2) Then, the lid material obtained by punching the laminated sheet for the lid material into a disk shape having a diameter of 70 mm is used, and the lid material made of polypropylene resin has an inner diameter of 60 mm.
φ, the width of the flange portion is 5 mm, and the cup-shaped injection-molded container is in contact with the open mouth portion, and the heat sealant layer of the lid and the flange portion 6 of the cup-shaped container are heat-sealed at 200 ° C. Thereby, a sealed container was obtained. Table 2 shows the measurement results and evaluation of the heat fusion strength of the obtained sealed container.
【００１５】[0015]
【発明の効果】本発明のヒートシーラント層用樹脂組成
物は、密度0.915 〜0.940 のエチレン−α・オレフィン
共重合体20〜70重量％、ポリプロピレン系樹脂 0〜25重
量％、ポリエチレン70〜10重量％及びエチレン−酢酸ビ
ニル共重合体 5〜25重量％による混合樹脂であり、密度
0.915 〜0.940 のエチレン−α・オレフィン共重合体及
びポリプロピレン系樹脂とによる熱融着性能と、ポリエ
チレン及びエチレン−酢酸ビニル共重合体とによる離型
性能とが、バランスして奏されるものであり、ポリプロ
ピレン系樹脂製の容器に対する蓋材におけるヒートシー
ラント層として利用され、該組成物によるヒートシーラ
ント層を具備する蓋材は、これを剥離する際のピール感
が良好であり、しかも、前記蓋材を得る際の製膜性が良
好で、ブロッキング現象等の発生がなく、かつ、アルミ
箔、紙、ポリエステル、ナイロン、ポリエチレン、ポリ
カーボネート、エチレン−ビニルアルコール共重合体等
のプラスチックなどの単層または複層からなる基材との
接着性が良好であるヒートシーラント層を形成し得るも
のである。The resin composition for the heat sealant layer of the present invention comprises 20 to 70% by weight of ethylene-α / olefin copolymer having a density of 0.915 to 0.940, 0 to 25% by weight of polypropylene resin, and 70 to 10% by weight of polyethylene. % And ethylene-vinyl acetate copolymer 5 to 25% by weight is a mixed resin and has a density
0.915 to 0.940 of ethylene-α / olefin copolymer and polypropylene-based resin have good heat fusion performance and polyethylene and ethylene-vinyl acetate copolymer have good release performance. A lid material that is used as a heat sealant layer in a lid material for a polypropylene resin container and has a heat sealant layer of the composition has a good peeling feeling when peeling it off, and moreover, the lid material It has good film-forming properties when obtained, does not cause a blocking phenomenon, etc., and has a single layer or multiple layers of plastic such as aluminum foil, paper, polyester, nylon, polyethylene, polycarbonate, ethylene-vinyl alcohol copolymer, etc. It is possible to form a heat sealant layer having good adhesion to a base material composed of layers.
【図１】本発明によるヒートシーラント層と基材との材
質構成例FIG. 1 is a material configuration example of a heat sealant layer and a base material according to the present invention.
【図２】本発明のヒートシーラント層の利用法の説明図FIG. 2 is an explanatory diagram of a method of using the heat sealant layer of the present invention.
Ｌ 蓋 Ｐ 容器 １ 蓋材の基材 ２ 印刷層 ３ 接着剤層 ４ ヒートシーラント層 ５ ヒートシーラント層と共押出された層 ６ 容器のフランジ ７ 蓋に設けた摘まみ片 L Lid P Container 1 Base material of lid material 2 Printing layer 3 Adhesive layer 4 Heat sealant layer 5 Layer co-extruded with heat sealant layer 6 Flange of container 7 Knob piece provided on lid
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｌ 23/08 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display area C08L 23/08
Claims (3)
レフィン共重合体20〜70重量％、ポリプロピレン系樹脂
0〜25重量％、ポリエチレン70〜10重量％、およびエチ
レン- 酢酸ビニル共重合体 5〜25重量％とによる混合樹
脂から形成されることを特徴とするヒートシーラント
層。1. An ethylene-α-olefin copolymer having a density of 0.915 to 0.940, 20 to 70% by weight, and a polypropylene resin.
A heat sealant layer formed from a mixed resin comprising 0 to 25% by weight, polyethylene 70 to 10% by weight, and ethylene-vinyl acetate copolymer 5 to 25% by weight.
−オレフィン共重合体と共押出し法により製膜されたこ
とを特徴とする請求項１記載のヒートシーラント層。2. Polyethylene or ethylene-α
-The heat sealant layer according to claim 1, wherein the heat sealant layer is formed by coextrusion with an olefin copolymer.
って、該蓋材のシーラント層が請求項１、又は、請求項
２で構成されていることを特徴とする易開封性蓋材。3. A lid material for a polypropylene resin container, wherein the sealant layer of the lid material is constituted by claim 1 or claim 2.