JPH0813297A - Elastic warp knitted fabric - Google Patents

Abstract

PURPOSE:To obtain an elastic warp knitted fabric texture having high mechanical strength while retaining its high elasticity and excellent in burst strength even in the case of light-gage specification, by using a warp knitting machine equipped with a weft-inserting device. CONSTITUTION:Elastic yarns are inserted as wefts 2 extending in the horizontal row direction into a warp knitted fabric texture with inelastic yarns as warps 1, making loops 2a along stitches 1a and being held by the warps 1, thus obtaining the objective warp knitted fabric. In this case, the ground weave comprising the warps 1 represents a two needle stitch texture. Specifically, warps with 20-50 denier in single fiber fineness are subjected to the two needle stitch in full set to doubly make the stitches of mutually adjacent warps in each wale and the basis weight of the cloth is set at 100-300g/m<2>.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、経緯両方向に略均等な
伸縮性を有する比較的薄地でかつ破裂強度や生地強度に
優れる弾性経編地に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an elastic warp knitted fabric which has relatively uniform stretchability in both warp and weft directions and which is relatively thin and has excellent burst strength and fabric strength.

【０００２】[0002]

【従来の技術と発明が解決しようとする課題】経編地
は、織物地とは異なり縦横両方向に伸縮性を有するもの
であるが、さらに高い弾性および伸長回復性を付与する
場合、スパンデックス等の弾性糸（エラスチック糸）を
経糸に用いて編成している。BACKGROUND OF THE INVENTION A warp knitted fabric, unlike a woven fabric, has stretchability in both longitudinal and transverse directions, but in the case of imparting higher elasticity and elongation recovery, a warp knitted fabric, etc. Knitting using elastic yarns (elastic yarns) as warp yarns.

【０００３】例えば、弾性糸と非弾性糸とを交編して製
造した弾性経編地、特に弾性糸を経糸の一部または全部
に用いて編目を形成した生地は、弾性糸の特性から縦横
両方向に高い伸縮性を有するもので、通常２ウエイ地と
して知られており、水着やファンデーション等に好適に
用いられている。For example, an elastic warp knitted fabric produced by interlacing an elastic yarn and an inelastic yarn, in particular, a fabric in which a stitch is formed by using the elastic yarn as a part or all of the warp yarn, is characterized by the characteristics of the elastic yarn. It has high elasticity in both directions and is generally known as 2-way fabric, and is suitably used for swimwear, foundations and the like.

【０００４】中でも、薄地の水着やファンデーション等
に多く利用されている編組織は、編機のバック側筬に弾
性糸を配して１×１トリコット編し、フロント側筬に非
弾性糸を配して１×２トリコット編した編組織による所
謂ロックロニット組織で編成されている。Among the knitting structures that are often used for thin swimwear and foundations, elastic yarns are arranged on the back side of the knitting machine to make 1 × 1 tricot knitting, and non-elastic yarns are arranged on the front side reed. Then, it is knitted by a so-called rock-ronit structure, which is a knitting structure formed by 1 × 2 tricot knitting.

【０００５】しかし、前記のように経糸の一部または全
部に弾性糸を用いた弾性経編地は、 経緯両方向の弾性力の働きや伸度バランスが悪くな
る。例えば、経方向の伸びに対する緯方向の伸びが悪く
なったり、あるいはその逆になることがある。 生地伸長後の復元性（伸長回復性）が劣り、元の状
態に戻り難い。 生地伸長状態での生地緊締力（伸長した生地が復元
しようとする時の張力、復元力）が劣る。 等といった問題があった。However, as described above, the elastic warp knitted fabric using the elastic yarns as a part or all of the warp yarns has poor balance of elasticity and elongation balance in both warp and weft directions. For example, elongation in the weft direction with respect to elongation in the warp direction may become worse, or vice versa. It is difficult to return to the original state because the restorability after stretching the fabric (stretch recovery) is poor. The dough tightening force in the stretched condition (tensile force when restoring the stretched dough and restoring force) is poor. There was a problem such as.

【０００６】そのため、近年、緯糸挿入装置付きの経編
機（トリコット機）による編成において、緯方向に挿入
される緯糸としてスパンデックス糸等の弾性糸を用い、
この緯糸を針のタック位置または横糸挿入位置にある針
先の下に導いてループを形成し、次に該ループを経糸に
よる地組織に編み込んで経糸により保持させるように編
成してなる経緯両方向に弾性力が略均等に働く、両方向
弾性経編地が提案されている（例えば特公平１−３０９
３８号公報）。図９はその編組織を拡大して示し、（１
１）は非弾性糸による経糸、（１２）は弾性糸による緯
糸を示す。Therefore, in recent years, in knitting by a warp knitting machine (tricot machine) equipped with a weft insertion device, an elastic yarn such as a spandex yarn is used as a weft yarn to be inserted in the weft direction,
The weft is guided under the needle tip at the tack position or the weft insertion position of the needle to form a loop, and then the loop is knitted in the ground structure of the warp and knitted so as to be held by the warp in both the warp and weft directions. A bidirectional elastic warp knitted fabric in which elastic forces work substantially uniformly has been proposed (for example, Japanese Patent Publication No. 1-309.
No. 38). FIG. 9 is an enlarged view of the knitting structure, showing (1
1) shows a warp made of non-elastic yarn, and (12) shows a weft made of elastic yarn.

【０００７】ところで、水着やファンデーシヨン等の用
途において、要求される特性の一つに、生地の厚みをで
きるだけ薄くすることがある。By the way, one of the required characteristics in applications such as swimwear and foundation is to make the fabric as thin as possible.

【０００８】しかし前記提案の弾性経編地による場合、
地組織を構成する非弾性糸の経糸（１１）が１×１トリ
コット編（デンビ）の編組織よりなるもので、薄地にす
ればするほど、引裂き強度や破裂強度に問題があって、
安心して着用できないものであり、満足できるものでは
ない。すなわち、経緯両方向の弾性経編地で薄地のもの
としては、充分満足できるものは未だ出現していないの
が実情である。However, in the case of the elastic warp knitted fabric proposed above,
The warp yarn (11) of the non-elastic yarn constituting the ground structure is composed of a knit structure of 1 × 1 tricot knitting (Denbi), and the thinner the fabric, the more the tear strength and the burst strength are problematic.
They are not comfortable to wear and not satisfactory. That is, as the elastic warp knitted fabric in both the warp and weft directions, a sufficiently satisfactory one has not yet appeared.

【０００９】また、前記の編組織に綿糸等の天然繊維の
紡績糸を編目を形成せずに経方向に挿入して交編した場
合には、ピリングが発生する等の問題もある。Further, when spun yarn of natural fiber such as cotton yarn is inserted into the knitting structure in the warp direction without forming stitches and interwoven, there is a problem such as pilling.

【００１０】本発明は、上記に鑑みてなしたものであ
り、緯糸挿入装置付の経編機を使用して編成した弾性経
編地として、経緯両方向に高弾性を保ちつつ、しかも薄
地であっても破裂強度に優れる編組織の弾性経編地を提
供することを目的とする。The present invention has been made in view of the above, and is an elastic warp knitted fabric knitted by using a warp knitting machine equipped with a weft insertion device, while maintaining high elasticity in both warp and weft directions and being thin. The object is to provide an elastic warp knitted fabric having a knit structure excellent in burst strength.

【００１１】[0011]

【課題を解決するための手段】上記の課題を解決する本
発明の弾性経編地は、緯糸挿入装置付きの経編機により
編成され、非弾性糸を経糸とする経編地組織に、弾性糸
がコース方向に延在する緯糸として挿入されて編目に沿
うループを形成して経糸に保持されてなる経編地であっ
て、前記非弾性糸の経糸による地組織が二目編組織より
なることを特徴とする。The elastic warp knitted fabric of the present invention for solving the above problems is knitted by a warp knitting machine equipped with a weft insertion device, and has an elastic property in a warp knitted fabric structure in which a non-elastic yarn is used as a warp. A warp knitted fabric in which a yarn is inserted as a weft yarn extending in the course direction and forms a loop along a stitch and is held by a warp yarn, and the ground structure of the warp of the non-elastic yarn is a two-piece knitting structure. It is characterized by

【００１２】前記において、非弾性糸よりなる経糸は、
２０〜５０デニールの糸であって、フルセットで二目編
されて、各ウエールにおいて隣接する経糸の編目が２重
に形成され、他方、弾性糸よりなる緯糸は、２０〜７０
デニールの糸であって、各コース毎に挿入されて経糸に
保持されており、生地目付が１００〜３００ｇ／ｍ²で
あるものが特に好適である。In the above, the warp made of inelastic yarn is
A yarn of 20 to 50 denier, which is double-knitted in a full set to form double stitches of adjacent warp yarns in each wale, while a weft yarn made of elastic yarn is 20 to 70
A denier yarn, which is inserted into each course and held by the warp, and has a fabric weight of 100 to 300 g / m ² , is particularly preferable.

【００１３】また、前記の弾性経編地において、天然繊
維の紡績糸等よりなる第３糸を同一ウエールにおいてジ
グザグ状に経方向に挿入して編込んでおくこともでき
る。In the elastic warp knitted fabric, a third yarn made of spun yarn of natural fiber or the like may be inserted in the zigzag shape in the same wale and knitted in the warp direction.

【００１４】前記の非弾性糸としては、ナイロン糸の合
成繊維フィラメント糸が好適に用いられるが、このほか
天然繊維の糸を用いることもできる。また弾性糸として
は、スパンデックス糸のほか、裸のエラスチックフィラ
メント糸が好適に用いられ、中でも２５０％以上の伸長
度を有するポリウレタン等のエラスチックフィラメント
糸が好ましく用いられる。As the non-elastic yarn, a synthetic fiber filament yarn of nylon yarn is preferably used, but a yarn of natural fiber can also be used. As the elastic yarn, in addition to spandex yarn, bare elastic filament yarn is preferably used, and among them, elastic filament yarn such as polyurethane having an elongation of 250% or more is preferably used.

【００１５】[0015]

【作用】上記の本発明の弾性経編地によれば、縦横両方
向に略均等な高い伸縮性が得られ、しかも伸長時回復時
の張力（生地緊締力）が伸長時の張力と略等しく、弾性
力が有効に作用する。しかも地組織を構成する非弾性糸
よりなる経糸が二目編組織で編成されているために、引
裂き強度および破裂強度等が向上し、水着やファンデー
ション等に使用される比較的薄地のものにおいて、生地
強度を従来品よりも高めることができる。According to the elastic warp knitted fabric of the present invention described above, substantially uniform high stretchability can be obtained in both longitudinal and transverse directions, and the tension at the time of recovery during stretching (fabric tightening force) is substantially equal to the tension at stretching. Elastic force works effectively. Moreover, since the warp yarns made of the non-elastic yarns that form the base structure are knitted in the double stitch structure, the tear strength and the burst strength are improved, and in the relatively thin cloth used for swimwear, foundations, etc., The fabric strength can be increased compared to conventional products.

【００１６】殊に請求項２のように、経糸をフルセット
で二目編組織にて編成し、各ウエールにおいて隣接する
経糸の編目が重なって２重に形成しておくことにより、
生地目付が１００〜３００ｇ／ｍ² の比較的薄地の経編
地であっても、充分な引裂き強度や破裂強度を得ること
ができ、またこれによって薄地要求にも対応できること
になる。In particular, as in claim 2, by fully knitting the warp in a two-knit design and forming adjacent double stitches in each wale,
Even with a relatively thin warp knitted fabric having a basis weight of 100 to 300 g / m ² , it is possible to obtain sufficient tear strength and burst strength, and thereby it is possible to meet the demand for thin cloth.

【００１７】また、請求項３のように、綿糸その他の天
然繊維の紡績糸等よりなる第３糸を経方向に挿入した場
合、この紡績糸交編によるピリングの発生を抑制できる
上、この紡績糸等により薄地であっても風合が良好なも
のとなり、かつ適度に吸湿性も保有することになる。When a third yarn made of spun yarn such as cotton yarn or other natural fiber is inserted in the warp direction as described in claim 3, the occurrence of pilling due to the interlaced spun yarn can be suppressed and the spinning can be performed. Even if the fabric is thin, it will have a good texture and will also have appropriate hygroscopicity.

【００１８】なお、上記の経糸に使用する非弾性糸の繊
度が、５０デニールより大きくなると、厚みが大きくな
って薄地要求に対応できないことになり、２０デニール
より小さくなると、編立てがやや困難になる上、期待す
る引裂き強度が得られないことになる。また、緯糸に使
用する弾性糸の繊度が、２０デニールより小さくなる
と、編立てがやや困難になる上に弾性力も小さくなり、
７０デニールより大きくなると、弾性力が強くなりすぎ
て着心地が悪くなる。When the fineness of the non-elastic yarn used for the above warp is more than 50 denier, the thickness becomes too large to meet the demand for thin fabric, and when it is less than 20 denier, knitting is rather difficult. In addition, the expected tear strength cannot be obtained. Further, when the fineness of the elastic yarn used for the weft is less than 20 denier, knitting becomes slightly difficult and the elastic force also becomes small,
When it is larger than 70 denier, the elastic force becomes too strong and the wearing becomes uncomfortable.

【００１９】したがって、上記したように繊度を設定
し、薄地要求に応えるように生地目付を１００〜３００
ｇ／ｍ² 、好ましくは前記範囲の中でも２６０ｇ／ｍ²
以下に設定するのがよい。Therefore, the fineness is set as described above, and the fabric weight is 100 to 300 so as to meet the demand for thin fabric.
g / m ² , preferably 260 g / m ² within the above range
The following should be set.

【００２０】生地目付を前記範囲にするためには、仕上
りコース密度を８０〜１１０コース／インチ、また仕上
りウエール密度を５０〜６５ウエール／インチに設定す
る必要がある。このコース密度およびウエール密度が、
前記より大きくなると、生地目付が前記より大きくな
り、目的とする薄地の弾性経編地が得られなくなる。In order to set the fabric weight to the above range, it is necessary to set the finished course density to 80 to 110 courses / inch and the finished wale density to 50 to 65 wale / inch. This course density and wale density
When it is larger than the above range, the fabric weight becomes larger than the above range, and it becomes impossible to obtain an intended elastic warp knitted fabric.

【００２１】[0021]

【実施例】図１は本発明に係る弾性経編地の１例の編組
織の拡大図を示し、図２はその編組織の各糸のラッピン
グ状態を分解して示している。また図３および図４は他
の実施例の編組織の拡大図と各糸のラッピング図を示
す。EXAMPLE FIG. 1 is an enlarged view of a knitting structure of an example of an elastic warp knitted fabric according to the present invention, and FIG. 2 is an exploded view showing a wrapping state of each yarn of the knitting structure. 3 and 4 show an enlarged view of the knitting structure of another embodiment and a wrapping view of each yarn.

【００２２】図において、（１）は殆ど全くあるいは僅
かしか伸縮性を有さない非弾性糸よりなる経糸であり、
例えばナイロン糸等の合成繊維フィラメント糸よりな
る。（２）はポリウレタン等のエラスチックフィラメン
ト糸、合成繊維で被覆したスパンデックス糸等の弾性糸
よりなる緯糸である。In the figure, (1) is a warp made of an inelastic yarn having almost no elasticity or only a little elasticity,
For example, it is made of synthetic fiber filament yarn such as nylon yarn. (2) is a weft made of elastic filament yarn such as polyurethane or elastic yarn such as spandex yarn covered with synthetic fiber.

【００２３】前記の非弾性糸による経糸（１）は、緯糸
挿入装置付きの経編機のフロント側筬にフルセットで配
されて１針間以上のアンダーラッピングを行なう経編組
織、特に２針間にオーバーラップする二目編組織にて編
成され、地組織を構成している。The warp (1) made of the non-elastic yarn is arranged in a full set on the front side reed of a warp knitting machine equipped with a weft insertion device, and warp knitting structure for performing underlapping for one or more stitches, particularly two stitches. It is knitted with a double stitch structure that overlaps between them to form a ground structure.

【００２４】この編組織による場合、フルセットで配さ
れた糸が二目編されるために、隣接する経糸の編目（１
ａ）（１ａ）が各ウエールにおいて２重に重なって形成
されることになる。In the case of this knitting structure, since yarns arranged in a full set are knitted in two stitches, stitches (1
a) (1a) is formed in each wale so as to be doubled.

【００２５】図１の実施例の場合は、非弾性糸の経糸
（１）を各コース毎に１針間のアンダーラッピングを行
なってシンカーループが隣接するウエールに移行する開
き目の二目編による編組織、すなわち図２のように０２
／３１／／の組織（チェーン組）で編成されている。ま
た図３の実施例の場合は、図４のように２０／１３／／
の組織（チェーン組）で編成されて閉じ目になってい
る。In the case of the embodiment shown in FIG. 1, the non-elastic warp (1) is underlapped by one stitch for each course, and the sinker loop is transferred to the adjacent wales by the second stitch. Knitting structure, that is, 02 as shown in FIG.
It is organized by the organization (chain group) of / 31 //. Further, in the case of the embodiment shown in FIG. 3, as shown in FIG.
It is organized by the organization (chain group) and is a closed eye.

【００２６】また弾性糸よりなる緯糸（２）は、前記の
経糸（１）の地組織に対し、公知の緯糸挿入装置により
各コース毎にコース方向に延在するように挿入されて、
かつ各ウエールの編目（１ａ）に沿うループ（２ａ）を
形成して前記の経糸（１）に保持されるように編込まれ
ている。A weft (2) made of an elastic yarn is inserted into the ground structure of the warp (1) by a known weft insertion device so as to extend in the course direction for each course,
Moreover, the loops (2a) are formed along the stitches (1a) of each wale to be held by the warp (1).

【００２７】すなわち、前記のように緯糸（２）を挿入
した経編地は、経糸（１）による経編編成における編目
形成工程中に、弾性糸の緯糸（２）を針のタック位置ま
たは緯糸挿入位置にある針先の下に導き、編目脱出工程
中に、針のフックとノッキングオーバー及びホールディ
ングダウンシンカーによってループを形成し、次に該ル
ープを経糸（１）による経編地組織の編目（１ａ）に沿
うように編込んで経糸（１）により保持させるように編
成する。That is, in the warp knitted fabric in which the weft yarn (2) is inserted as described above, the weft yarn (2), which is an elastic yarn, is set at the needle tack position or the weft yarn during the stitch forming step in the warp knitting by the warp yarn (1). A loop is formed under the needle tip at the insertion position and formed by the hook of the needle and the knocking over and holding down sinker during the stitch escape process, and then the loop is formed by the warp (1) stitches of the warp knitted fabric structure ( 1a) is knitted and knitted so as to be held by the warp (1).

【００２８】これにより、前記の緯糸（２）は、経編生
地の両面において前記経糸（１）により覆われて、かつ
経糸（１）の編目（１ａ）とともにループ（２ａ）を形
成して該経糸（１）に保持されることになる。As a result, the weft yarn (2) is covered with the warp yarn (1) on both sides of the warp knitted fabric and forms a loop (2a) together with the stitch (1a) of the warp yarn (1). It will be held by the warp (1).

【００２９】前記の非弾性糸の経糸（１）による経編地
組織としては、上記した実施例のほか、種々の二目編組
織による実施が可能である。As the warp knitted fabric design by the warp yarn (1) of the above-mentioned inelastic yarn, various second stitch design can be carried out in addition to the above-mentioned embodiment.

【００３０】例えば、図５の（ａ）および（ｂ）の開き
目および閉じ目の鎖編の二目編組織や、同図の（ｃ）
（ｄ）（ｅ）のような二目編組織で編成することができ
る。いずれの場合も、この非弾性糸の経糸（１）はフル
セットで配して編成することにより、各ウエールで隣接
する経糸の編目（１ａ）（１ａ）が重なって２重に形成
されるように編成する。For example, the second stitch structure of the chain stitches of the open and closed stitches in FIGS. 5A and 5B, and FIG. 5C.
(D) It is possible to knit with a double stitch structure such as (e). In any case, by arranging and knitting the non-elastic warp yarns (1) in a full set, the stitches (1a) (1a) of the adjacent warp yarns in each wale are overlapped to form a double layer. To organize.

【００３１】中でも、図１（図２）の二目編組織と、図
３（図４）の二目編組織とは、経緯両方向の弾力や伸度
に殆ど差はなく、いずれも経緯の伸縮性つまり経緯の伸
度バランスが図５に例示する二目編組織に比して良好も
のとなる。Among them, there is almost no difference in elasticity and elongation in both directions of the warp and weft from the two-knitted structure of FIG. 1 (FIG. 2) and the two-knitted structure of FIG. The property, that is, the elongation balance of the background, becomes better than that of the double stitch structure illustrated in FIG.

【００３２】また図５の（ａ）および（ｂ）の場合、図
１（図２）の二目編組織に比して、弾力は経緯両方向と
もに向上もしくはやや向上し、伸度は経緯両方向ともに
やや減少ぎみになるが、それほど大きな差はなく、経緯
の伸度バランスには大きな影響はない。In the case of FIGS. 5 (a) and 5 (b), the elasticity is improved or slightly improved in both the longitudinal and lateral directions, and the elongation is increased in both the longitudinal and lateral directions, as compared with the double stitch structure of FIG. 1 (FIG. 2). Although it is only slightly decreasing, there is no big difference and it does not affect the elongation balance of the history.

【００３３】図６の実施例は、図１の編組織に、天然繊
維の紡績糸等よりなる第３糸（３）を編目を形成せずに
経方向に挿入して編込んだ場合を示している。この第３
糸（３）は、バック側筬にフルセットで配されて各ウエ
ールにおいて１コース毎にジグザグ状をなすように挿入
されて編込まれる。この第３糸（３）としては、綿糸等
の天然繊維の紡績糸のほか、綿糸等の紡績糸を芯糸にし
てフィラメント糸をカバリングしたカバリング加工糸を
用いることができる。図３の編組織においても、同様に
第３糸を縦方向に挿入して編込んでおくことができる。The embodiment of FIG. 6 shows a case where the knitting structure of FIG. 1 is knitted by inserting a third yarn (3) made of spun yarn of natural fiber or the like in the warp direction without forming stitches. ing. This third
The yarn (3) is arranged in a full set on the back side reed and is inserted and knitted in a zigzag shape for each course in each wale. As the third yarn (3), a spun yarn of natural fiber such as cotton yarn, or a covered yarn obtained by covering a filament yarn with a spun yarn such as cotton yarn as a core yarn can be used. Also in the knitting structure of FIG. 3, the third yarn can be similarly inserted and knitted in the longitudinal direction.

【００３４】前記のように第３糸（３）として綿糸等を
用いることにより、薄地であってしかも風合の良好な弾
性経編地を得ることができ、また適度に吸湿性を有する
ものとなる。As described above, by using a cotton yarn or the like as the third yarn (3), it is possible to obtain an elastic warp knitted fabric which is thin and has a good feeling, and has an appropriate hygroscopicity. Become.

【００３５】上記したいずれの編組織の場合において
も、仕上り生地目付を１００〜３００ｇ／ｍ² にするた
めに、前記の経糸（１）となる非弾性糸は２０〜５０デ
ニールの繊度の糸が、また緯糸（２）となる弾性糸は２
０〜７０デニールの糸が用いられて、仕上りコース密度
は８０〜１１０コース／インチ、また仕上りウエール密
度は５０〜６５ウエール／インチとなるように編成され
る。第３糸（３）が挿入される場合は、経糸には比較的
細い糸を用いる。また第３糸（３）としては、通常、１
５０〜５０番手（綿番手）程度の繊度の糸が用いられ
る。In any of the above knitting structures, in order to obtain a finished fabric weight of 100 to 300 g / m ² , the non-elastic yarn as the warp (1) has a fineness of 20 to 50 denier. , And the elastic yarn to be the weft (2) is 2
A yarn having a denier of 0 to 70 is used and knitted to have a finished course density of 80 to 110 courses / inch and a finished wale density of 50 to 65 wale / inch. When the third yarn (3) is inserted, a relatively thin yarn is used as the warp yarn. The third yarn (3) is usually 1
A yarn having a fineness of about 50 to 50 count (cotton count) is used.

【００３６】なお、次の表１は、図１（図２）の編組織
の経編生地において、経糸（非弾性糸）と緯糸（非弾性
糸）の繊度と、仕上りコース、仕上りウエールおよび生
地目付との関係を示し、いずれも生地目付を１００〜３
００ｇ／ｍ2 の範囲にした場合を示している。The following Table 1 shows the fineness of the warp (inelastic yarn) and the weft (inelastic yarn) in the warp knitting fabric having the knitting structure shown in FIG. 1 (FIG. 2), finish course, finish wale and fabric. Shows the relationship with the basis weight, and the basis weight is 100 to 3 for both.
It shows the case where the range is 00 g / m 2.

【００３７】[0037]

【表１】 [Table 1]

【００３８】また次の表２は、図６の第３糸（３）を挿
入した編組織の経編生地において、経糸（非弾性糸）お
よび緯糸（弾性糸）の繊度と、仕上りコース、仕上りウ
エールおよび生地目付との関係の１例を示している。こ
の例では、第３糸とし、８０番手綿糸を１５デニールの
フィラメント糸でカバリングしたカバリング加工糸を用
いた。Further, the following Table 2 shows the fineness of the warp (inelastic yarn) and the weft (elastic yarn), the finish course, and the finish in the warp knitting fabric having the knitting structure in which the third yarn (3) of FIG. 6 is inserted. An example of the relationship between wale and fabric weight is shown. In this example, as the third yarn, a covering processed yarn obtained by covering an 80th count cotton yarn with a 15 denier filament yarn was used.

【００３９】[0039]

【表２】 [Table 2]

【００４０】このようにして編成した弾性経編地は、縦
横両方向に略均等な高い伸縮性が得られ、しかも伸長時
回復時の張力（生地緊締力）が伸長時の張力と略等し
く、弾性力が有効に作用する。しかも地組織を構成する
経糸である非弾性糸が二目編されているために、隣接す
る経糸の編目が各ウエールにおいて２重に重なって形成
されることになって、引裂き強度および破裂強度等が向
上し、水着やファンデーションにに使用される比較的薄
地のものにおいて、その生地強度を従来品よりも高める
ことができる。The elastic warp knitted fabric knitted in this manner has high elasticity which is substantially uniform in both longitudinal and transverse directions, and the tension at the time of recovery during stretching (fabric tightening force) is substantially equal to the tension at stretching, so that elasticity Power works effectively. Moreover, since the non-elastic yarn which is the warp that constitutes the ground structure is double-knitted, the stitches of the adjacent warp yarns are doubled in each wale, so that the tear strength and the burst strength, etc. In a relatively thin material used for a swimsuit or a foundation, the fabric strength thereof can be increased more than that of a conventional product.

【００４１】（実施例）図１（図２）の編組織の経編地
を、非弾性糸の経糸（１）として、２０デニール、６フ
ィラメントのナイロンフィラメントヤーンを、弾性糸の
緯糸（２）として、７０デニールのエラスチックヤーン
（１フィラメント）を用い、表１のＮｏ−３の編立て条
件で編成した。この経編地の破裂強度、伸長後の回復率
および伸長率についてテストを行なった。その結果を下
記の表３に示す。(Example) Using the warp knitted fabric of the knitting structure of FIG. 1 (FIG. 2) as a warp yarn (1) of a non-elastic yarn, a nylon filament yarn of 20 denier and 6 filaments, and a weft yarn (2) of an elastic yarn. As the material, 70 denier elastic yarn (1 filament) was used and knitted under the knitting conditions of No. 3 in Table 1. The warp knitted fabric was tested for burst strength, recovery rate after elongation, and elongation rate. The results are shown in Table 3 below.

【００４２】なお、表３中の比較例は、実施例と同じ糸
使い、同じ仕上げ加工条件で編成した図８の編組織の経
編地の場合を示している。The comparative example in Table 3 shows the case of the warp knitted fabric having the knitting structure shown in FIG. 8 which is knitted under the same finishing conditions using the same yarns as those used in the examples.

【００４３】[0043]

【表３】 [Table 3]

【００４４】また、上記のようにして得られた経編地の
経方向の伸長時の張力（伸長力）と伸長回復時の張力
（緊締力）とを測定したところ、実施例の編地は図７の
ようになり、また比較例の編地は図８のようになった。When the tension (extension force) when the warp knitted fabric was stretched in the warp direction and the tension (tension force) when stretch-recovered were measured, the knitted fabrics of Examples were 7 and the knitted fabric of the comparative example is as shown in FIG.

【００４５】なお測定法は、カットストリップ法 ＪＩ
Ｓ Ｌ １０１３（定速伸長型）で行なった。The measuring method is the cut strip method JI.
S L 1013 (constant speed extension type) was used.

【００４６】上記の表３のテスト結果から明らかなよう
に、実施例の編地は、比較例に比して伸長率にそれほど
大きな差はなく、また伸長後の回復率についても殆ど差
はないが、生地自体の破裂強度については比較例の編地
に比して向上している。As is clear from the test results of Table 3 above, the knitted fabrics of the examples do not show much difference in the elongation rate as compared with the comparative example, and there is almost no difference in the recovery rate after the elongation. However, the burst strength of the fabric itself is improved as compared with the knitted fabric of the comparative example.

【００４７】また比較例の編地は、大きな力を加えて伸
長させた場合ほど、経方向と緯方向の身長率の差が大き
くなり、経緯両方向の伸長率に不均一が生じるが、実施
例の編地は、大きな力を加えて伸長させた場合にも、経
緯両方向の伸長率に大きな差がなく、伸度バランスが略
均等に保持できるものとなっている。In the knitted fabric of the comparative example, the difference in height ratio between the warp direction and the weft direction becomes larger as it is stretched by applying a large force, and the stretch ratios in both the warp and weft directions become uneven. Even when the knitted fabric is stretched by applying a large force, there is no large difference in the stretching rate in both the warp and weft directions, and the stretch balance can be maintained substantially even.

【００４８】さらに、図７および図８に示すように、生
地緊締力（伸長した生地が元に戻ろうとするときの張
力）が、比較例の編地に比して大きくなっている。Further, as shown in FIGS. 7 and 8, the cloth tightening force (the tension when the stretched cloth tries to return to its original state) is larger than that of the knitted fabric of the comparative example.

【００４９】[0049]

【発明の効果】上記したように本発明のの弾性経編地に
よれば、経緯両方向に略均等な伸縮性を有し、特に経緯
両方向の伸度パランスおよび伸長回復性を良好に維持し
ながら比較的薄地のものであっても、破裂強度、引裂き
強度を大幅に向上できるものであり、薄地であることが
要求される水着やファンデーションとして好適に使用で
きるものとなる。As described above, according to the elastic warp knitted fabric of the present invention, the elastic warp knitted fabric has substantially uniform stretchability in both warp and weft directions, and particularly, while maintaining good elongation balance and elongation recovery in both warp and weft directions. Even if it is a relatively thin material, the burst strength and the tear strength can be greatly improved, and it can be suitably used as a swimsuit or a foundation required to be thin.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の１実施例に係る弾性経編地の編組織の
拡大図である。FIG. 1 is an enlarged view of a knitting structure of an elastic warp knitted fabric according to an embodiment of the present invention.

【図２】同上の各糸の分解したラッピング図である。FIG. 2 is an exploded wrapping diagram of each yarn of the above.

【図３】本発明の他の実施例に係る弾性経編地の編組織
の拡大図である。FIG. 3 is an enlarged view of a knitting structure of an elastic warp knitted fabric according to another embodiment of the present invention.

【図４】同上の各糸の分解したラッピング図である。FIG. 4 is an exploded wrapping diagram of each yarn of the above.

【図５】非弾性糸の上記以外の編組織を例示する組織図
である。FIG. 5 is a structure diagram illustrating a knitting structure other than the above for the non-elastic yarn.

【図６】第３糸を経方向に挿入した弾性経編地の編組織
の拡大図である。FIG. 6 is an enlarged view of a knitting structure of an elastic warp knitted fabric in which a third yarn is inserted in the warp direction.

【図７】図１の経編生地の伸長力（伸長時張力）と緊締
力（伸長回復時の張力）とを測定したグラフである。FIG. 7 is a graph in which the stretching force (tensile force during stretching) and the tightening force (tensile force during stretching recovery) of the warp knit fabric of FIG. 1 are measured.

【図８】図９の弾性経編地の伸長力と緊締力とを測定し
たグラフである。8 is a graph in which the stretching force and the tightening force of the elastic warp knitted fabric of FIG. 9 are measured.

【図９】従来の弾性経編地の編組織の拡大図である。FIG. 9 is an enlarged view of a knitting structure of a conventional elastic warp knitted fabric.

【符号の説明】[Explanation of symbols]

（１） 非弾性糸による経糸 （１ａ） 編目 （２） 弾性糸による緯糸 （２ａ） ループ （３） 第３糸 (1) Warp made of non-elastic yarn (1a) Stitch (2) Weft made of elastic yarn (2a) Loop (3) Third yarn

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】緯糸挿入装置付きの経編機により編成さ
れ、非弾性糸を経糸とする経編地組織に、弾性糸がコー
ス方向に延在する緯糸として挿入されて編目に沿うルー
プを形成して経糸に保持されてなる経編地であって、前
記非弾性糸の経糸による地組織が二目編組織よりなるこ
とを特徴とする弾性経編地1. A warp knitting machine equipped with a weft insertion device, wherein elastic yarns are inserted as weft yarns extending in the course direction into a warp knitted fabric structure having inelastic yarns as warp yarns to form loops along the stitches. An elastic warp knitted fabric that is retained by the warp yarns, characterized in that the ground structure of the warp of the non-elastic yarn is a second stitch structure. 【請求項２】非弾性糸よりなる経糸は、２０〜５０デニ
ールの糸であって、フルセットで二目編されて、各ウエ
ールにおいて隣接する経糸の編目が２重に形成され、他
方、弾性糸よりなる緯糸は、２０〜７０デニールの糸で
あって、各コース毎に挿入されて経糸に保持されてお
り、生地目付が１００〜３００ｇ／ｍ² である請求項１
に記載の弾性経編地。2. A warp made of an inelastic yarn is a yarn having a denier of 20 to 50 and is fully knitted in two stitches to form a double stitch of adjacent warp yarns in each wale. The weft composed of a yarn is a yarn having a denier of 20 to 70, inserted into each course and held by a warp, and the basis weight of the fabric is 100 to 300 g / m ^2.
The elastic warp knitted fabric according to. 【請求項３】天然繊維の紡績糸等よりなる第３糸が同一
ウエールにおいてジグザグ状をなして経方向に挿入され
て編込まれてなる請求項１または２に記載の弾性経編
地。3. The elastic warp knitted fabric according to claim 1, wherein a third yarn made of spun yarn of natural fiber or the like is formed in a zigzag shape in the same wale and is inserted in the warp direction and knitted.