JPH08100500A - Metallic rain gutter - Google Patents

Abstract

PURPOSE: To reduce the cost by coating a coupled seam joint portion with an adhesive seal material hardened quickly at the ordinary temperature in a metallic rain gutter coupled with the end edge of a molded metal thin plate via a seam joint. CONSTITUTION: The end section of an elbow 1 molded with a metal thin plate into a bent angular tube is coupled via a seam joint 11, the seam joint 11 is coated with an adhesive seal material 2 hardened quickly at the ordinary temperature over the whole length, and a metallic rain gutter is assembled. Since the adhesive seal material 2 hardened quickly at the ordinary temperature is used, the washing work and the subsequent drying work are not required after the soldering work unlike the conventional method, the work time is sharply shortened, and the cost can be reduced.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、銅板あるいはステンレ
ス鋼板などを成形してなる金属製雨といに係るものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rain gutter made of metal, such as a copper plate or a stainless steel plate.

【０００２】[0002]

【従来の技術】従来より雨といとして塩ビなどの樹脂製
のものが知られているが、高級なものとしては銅板製あ
るいはステンレス製のものなどが知られている。銅製の
雨といは、従来より耐候性に優れている上に、外観の自
然発色による美しさ等から古くより社寺や高級住宅の雨
といとして定評があり、更に一度施工するとメンテナン
スも掛からず、半永久的に使用できるものとして知られ
ている。またステンレス製の雨といは耐候性にも優れ、
さらに近年の洋風住宅などに素材のもつ質感がマッチす
るため高級感を呈するものとして好まれている。2. Description of the Related Art Conventionally, as rain gutters, those made of resin such as vinyl chloride have been known. Copper rain gutters are more weather-resistant than before, and have long been well-known as rain gutters for shrines and high-class homes due to the beauty of their natural appearance, and once installed, they do not require maintenance and are semi-permanent. It is known to be used in general. The rain gutter made of stainless steel also has excellent weather resistance,
Furthermore, because the texture of the material matches that of Western-style houses in recent years, it is preferred as one that has a high-class feel.

【０００３】このような金属製雨といを製造するには、
成形した金属部品の端部どうしをハゼ組などにより組合
せ、このハゼ組部分を半田付けなどにより固定してお
り、この時半田がハゼの隙間に浸透して固着するため、
強固な接続方法であった。この係合部分はハゼ組の他に
も、爪掛け方式やあるいはこれらの組合せなど、種々の
構造が知られている。しかしこの半田付けによる接合方
法は、半田付けする部分にあらかじめフラックス等の酸
性溶液を使用するため、半田付け後にフラックスが残留
して腐蝕などを起こすことがあり、これを防ぐため中和
洗浄をしたり、またその洗浄液を乾燥させたりしなけれ
ばならなかった。そしてこのような洗浄や乾燥の作業
は、設備も大規模なものが必要となり、また時間も要す
るものである。To manufacture such a metal rain gutter,
The ends of the molded metal parts are combined with a goby set, and this goby set part is fixed by soldering, etc.At this time, the solder penetrates into the gap of the goby and is fixed,
It was a strong connection method. In addition to the goby set, various structures such as a hooking method or a combination thereof are known for this engaging portion. However, in this joining method by soldering, an acidic solution such as flux is used in advance for the part to be soldered, so the flux may remain after soldering and cause corrosion, so neutralization cleaning is performed to prevent this. Or, the cleaning solution had to be dried. Further, such washing and drying operations require large-scale equipment and also require time.

【０００４】このように半田付けの作業は熟練が必要で
あり、洗いなどの後処理を考慮すると生産性も良好とは
言えなかった。また近年は都市部を中心に酸性雨などの
化学的物質による汚染が進み、半田付け部分が酸性の雨
水に腐蝕されることがあり、この腐蝕部分より長期間の
使用では水漏れの原因になることもあった。As described above, the soldering work requires skill, and the productivity cannot be said to be good in consideration of the post-treatment such as washing. Moreover, in recent years, pollution by chemical substances such as acid rain has progressed mainly in urban areas, and the soldered part may be corroded by acid rainwater. If used for a longer period than this corroded part, it may cause water leakage. There were things.

【０００５】[0005]

【発明が解決しようとする課題】この従来の半田付けに
よる組立は半田付け作業に加えて、洗浄、乾燥等の付帯
作業も加わるため、大規模な設備が必要となり、それが
コスト高にもつながるものであった。またこのような半
田付けの作業は熟練を要するため、限られた熟練者だけ
しか作業ができない等の問題もあり、大量生産に適して
いるとは言えず、さらには半田は金属の合金であるた
め、酸性雨などに対しても腐蝕する恐れもあった。This conventional assembly by soldering requires additional work such as cleaning and drying in addition to the soldering work, which requires a large-scale facility, which leads to high cost. It was a thing. Further, since such soldering work requires skill, there is a problem that only a limited number of skilled workers can work, and it cannot be said that it is suitable for mass production. Furthermore, solder is an alloy of metal. Therefore, there is a risk of corrosion due to acid rain.

【０００６】[0006]

【課題を解決するための手段】上記課題を解決するた
め、本願に係る発明の金属製雨といは組立時にハゼ組部
分を接続固着する際に、従来の半田付け等の接合方法の
代わりに、常温にて迅速に硬化する合成樹脂の接着シ−
ル剤を塗布し、ハゼ組部分に固着浸透させて組み立てる
ものである。また高温（１６０゜Ｃないし２００゜Ｃ程
度）に６０分間程度耐えられる接着シ−ル剤を使用する
ことにより、接着シールをした後に焼付け塗装などの高
温処理が可能なものである。In order to solve the above-mentioned problems, in order to solve the above-mentioned problems, the metal rain gutter of the invention of the present application, when connecting and fixing the goby assembly parts at the time of assembly, instead of the conventional joining method such as soldering, Adhesive sheet of synthetic resin that cures quickly at room temperature
It is assembled by applying an adhesive agent and fixing and permeating the goby assembly. Further, by using an adhesive sealant that can withstand high temperatures (about 160 ° C. to 200 ° C.) for about 60 minutes, it is possible to perform high temperature treatment such as baking coating after the adhesive sealing.

【０００７】[0007]

【作用】このように金属薄板をハゼ組し、その係合部分
に常温にて迅速に硬化する接着シ−ル剤を用いることに
より従来の半田付け作業のあとの洗浄作業や、それに伴
う乾燥作業などが不要となり作業が大幅に短縮出来るも
のとなり、塗布作業も将来的には作業の自動化なども可
能となるものである。また主原料が合成樹脂から製造さ
れる接着シ−ル剤は化学的にも安定なものであり、酸性
雨などによる腐食の恐れも無いものである。[Function] As described above, the thin metal plates are assembled into a goby, and an adhesive sealant that cures rapidly at room temperature is used for the engaging portions, so that the cleaning work after the conventional soldering work and the drying work accompanying it are performed. It becomes unnecessary and the work can be drastically shortened, and the coating work can be automated in the future. Further, the adhesive sealant whose main raw material is made of synthetic resin is chemically stable, and there is no fear of corrosion due to acid rain or the like.

【０００８】[0008]

【実施例】以下本発明を添付図面に示した一実施例に基
づいて詳説する。図１は本発明に係る一実施例であるエ
ルボ１の斜視図を示すが、図示する如く屈曲した角筒状
に成形されたエルボ１は、銅板あるいはステンレス鋼板
の薄板を成形し、端部でハゼ組１１にて係合接続されて
いる。このハゼ組１１には常温にて迅速に硬化する接着
シ−ル材２が全長にわたって塗布されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail based on an embodiment shown in the accompanying drawings. FIG. 1 shows a perspective view of an elbow 1 which is one embodiment according to the present invention. The elbow 1 formed into a bent rectangular tube shape as shown in the drawing is formed by forming a thin plate of a copper plate or a stainless steel plate, It is engaged and connected by the goby set 11. The gore set 11 is coated with the adhesive seal material 2 which is rapidly cured at room temperature over the entire length.

【０００９】図示例のエルボ１では四隅部分にそってハ
ゼ組１１が形成されているため、その部分の初めから終
端部分まで塗布してあるが、これは強度を必要としない
等の理由で一部分であってもかまわないものである。図
２はエルボ１の要部の拡大断面図であるが、同様にハゼ
部分１１には接着剤２を十分塗布して接続固定してい
る。In the elbow 1 of the illustrated example, since the goby set 11 is formed along the four corners, it is applied from the beginning to the end of the part, but this is partially due to the fact that it does not require strength. However, it does not matter. FIG. 2 is an enlarged cross-sectional view of a main part of the elbow 1. Similarly, the adhesive 2 is sufficiently applied to the goby portion 11 to connect and fix the same.

【００１０】この接着シ−ル材２は塗布してから、常温
にて５分ないし１０分程度で硬化する性能のものが作業
上からも使いやすいが、硬化時間は前記時間に限定され
ないのは当然である。作業に際しては塗布する部品の形
状に適した冶具と吐出機械を組み合わせて使用すれば作
業性もよいものとなる。It is easy to use this adhesive seal material 2 which is cured at room temperature for about 5 to 10 minutes after application, but the curing time is not limited to the above-mentioned time. Of course. When working, if a jig suitable for the shape of the parts to be coated and a discharging machine are used in combination, workability will be good.

【００１１】また作業性を向上させるために自動化の製
造ラインに組み込む事も可能であり、接着シ−ル剤の量
も塗布スピ−ドと吐出量との関係で調整可能としておけ
ば、量を多くしたときは塗布スピードを上げて作業し、
量を少なくしたときにはそれに応じてスピードを下げれ
ば一定量の接着シール材にて作業できるものである。Further, in order to improve workability, it can be incorporated in an automated production line, and if the amount of the adhesive sealant can be adjusted by the relationship between the coating speed and the discharge amount, the amount can be reduced. When increasing the number, increase the coating speed and work,
When the amount is reduced, the speed can be reduced accordingly, and a fixed amount of adhesive sealing material can be used.

【００１２】このとき、接着シ−ル材の粘度は不必要な
部分に流れ出したりせず、作業に適した粘度が必要であ
り、使用する場所や量に応じて適宜な粘性のものを選択
して使用すればよく、可能なら浸透性もあるものが好ま
しい。At this time, the viscosity of the adhesive seal material does not flow out to an unnecessary portion and a viscosity suitable for the work is required, and an appropriate viscosity is selected according to the place and amount to be used. It is preferable to use a compound that has permeability, if possible.

【００１３】図３は本発明を排水筒３に応用した時の斜
視図であり、図４は集水器４に応用したときの斜視図で
ある。図示するように、銅板あるいはステンレス鋼板な
どの金属薄板にて成形された部品の端部どうしをハゼ組
３１、４１し、この係合接続された部分には接着シ−ル
剤２が塗布され、強固に接続固着されている。FIG. 3 is a perspective view when the present invention is applied to the drain pipe 3, and FIG. 4 is a perspective view when the present invention is applied to the water collector 4. As shown in the drawing, the end portions of the parts formed of a thin metal plate such as a copper plate or a stainless steel plate are set to the goby sets 31, 41, and the adhesive sealant 2 is applied to the engaged and connected parts, It is firmly connected and fixed.

【００１４】この他、本発明は図示した以外にも、種々
の雨とい部品の係合接続した部分の接着シ−ルに応用で
き、その利用範囲は広範なものとなる。Besides the above, the present invention can be applied to the adhesive seal of the engaged and connected parts of various rain gutter parts, and its application range is wide.

【００１５】[0015]

【発明の効果】以上詳述したように、本発明に係る金属
製雨といは組立製作の際に従来のように半田付けなどを
使用せずに、常温乾燥の接着シ−ル剤を用いることによ
り、熟練を要する半田付け作業が不要となり、その半田
付けに伴う洗浄や乾燥などの作業も必要ないため、迅速
に製造できると共に歩留まりも向上し、大幅なコストダ
ウンが図れるものである。As described above in detail, the metal rain pit according to the present invention uses an adhesive sealant that is dried at room temperature without using soldering or the like as in the conventional case when assembling and manufacturing. This eliminates the need for skillful soldering work, and the work such as cleaning and drying associated with the soldering is not required. Therefore, rapid manufacturing is possible and the yield is improved, and a large cost reduction can be achieved.

【００１６】また熟練した作業者に限られることなく作
業でき、その作業も容易であるため品質の安定した製品
が大量に提供できるものである。さらに近年都市部で問
題となっている酸性雨等の公害に対しても、合成樹脂が
主原料である接着シ−ル剤は化学的にも安定しているた
め耐候性にも優れ、従来の半田付けによる接続固着のよ
うに、腐食の恐れもなく長期間の使用に耐えるものであ
る。この接着シ−ル剤を高温に耐える性質のものを使用
すれば、塗布した直後に焼付け塗装が行えるなど種々の
利点を有するものである。Further, since it is possible to work without being limited to skilled workers and the work is easy, a large quantity of products of stable quality can be provided. Further, even against pollution such as acid rain, which has become a problem in urban areas in recent years, the adhesive sealant, which is a synthetic resin as a main raw material, is chemically stable and thus has excellent weather resistance. It can withstand long-term use without fear of corrosion, such as connection and fixation by soldering. If an adhesive sealant having a property of withstanding high temperature is used, it has various advantages such as baking coating immediately after coating.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明に係るエルボの斜視図。FIG. 1 is a perspective view of an elbow according to the present invention.

【図２】図１に於けるエルボの係合部分の要部の拡大
図。FIG. 2 is an enlarged view of a main part of an engaging portion of the elbow shown in FIG.

【図３】他の実施例である排水筒の部分斜視図。FIG. 3 is a partial perspective view of a drainage pipe according to another embodiment.

【図４】他の実施例である集水器の斜視図。FIG. 4 is a perspective view of a water collector that is another embodiment.

【符号の説明】[Explanation of symbols]

１・・・エルボ １１・・ハゼ部 ２・・・接着シ−ル剤 ３・・・アンコ− ３１・・ハゼ部 ４・・・集水器 ４１・・ハゼ部 1 ... Elbow 11 ... Goby part 2 ... Adhesive sealant 3 ... Anco-31 ... Goby part 4 ... Water collector 41 ... Goby part

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】成形された金属薄板の端縁をハゼ組にて係
合接続してなる金属製雨といに於て、該係合接続したハ
ゼ組部分に常温迅速硬化性の接着シ−ル材を塗布してな
る金属製雨とい。1. In a metal rain pit in which the edges of a molded thin metal plate are engaged and connected by a goby set, a room-temperature quick-curing adhesive seal is attached to the engaged and joined goby set part. Metal rain is made by applying materials. 【請求項２】成形された金属薄板が銅板であることを特
徴とする、請求項１に記載の金属製雨とい。2. The metal rain gutter according to claim 1, wherein the formed metal thin plate is a copper plate. 【請求項３】成形された金属薄板がステンレス鋼板であ
ることを特徴とする、請求項１に記載の金属製雨とい。3. A metal rain glove according to claim 1, wherein the formed thin metal plate is a stainless steel plate. 【請求項４】常温硬化性の接着シ−ル材が１６０゜Ｃな
いし２００゜Ｃ程度の雰囲気中に６０分間程度、性能劣
下を起こさない耐高温性能を有する請求項１ないし請求
項３のいずれかに記載の金属製雨とい。4. The room temperature curable adhesive seal material has a high temperature resistance which does not cause performance deterioration for about 60 minutes in an atmosphere of about 160 ° C. to 200 ° C. Metal rain grate described in either one.