JPH0797900A - Highly waterproof lining for tunnel - Google Patents
Highly waterproof lining for tunnelInfo
- Publication number
- JPH0797900A JPH0797900A JP5264021A JP26402193A JPH0797900A JP H0797900 A JPH0797900 A JP H0797900A JP 5264021 A JP5264021 A JP 5264021A JP 26402193 A JP26402193 A JP 26402193A JP H0797900 A JPH0797900 A JP H0797900A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- tunnel
- concrete
- nonwoven fabric
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】】Detailed Description of the Invention]
【０００１】[0001]
【産業上の利用分野】開示技術は、山岳トンネルをＮＡ
ＴＭ工法により形成するに、該トンネルの内面にアイソ
レーションを兼ねる防水を効率良く行って覆工を行う工
法の技術分野に属する。[Industrial field of use] The disclosed technology is used for NA in mountain tunnels.
When it is formed by the TM method, it belongs to the technical field of a method of performing a lining by efficiently waterproofing the inner surface of the tunnel that also serves as isolation.
【０００２】[0002]
【従来の技術】周知の如く、林野，山間部が多く、複雑
に入り込んだ海岸線に接近している地勢条件の我が国に
あっては農耕，牧畜は勿論のこと、住居のみならず、各
種の産業施設に供する平野部が著しく少く、したがっ
て、産業に有効に用いる土地は全国的に散在し、そのた
め、製品輸送は勿論のこと、資材供給やこれらに必要な
情報伝達も兼ねて鉄道，道路網がネックワーク的に全国
津々浦々に行き亘るようになり、そのため、山間部等に
あってはトンネルは必要不可欠であり、該トンネルの施
工を安全、且つ、能率的に低コストで正確に行う技術が
旧くから種々研究開発され、今猶改善研究が鋭意行われ
ている。2. Description of the Related Art As is well known, in Japan where there are many forests and mountains, and the terrain is close to a complicated coastline, not only farming and stock raising, but also housing and various industries The number of plains used for facilities is extremely small, and therefore the land used effectively for industry is scattered all over the country. Therefore, not only the product transportation but also the railway and road network not only for supplying materials but also for transmitting necessary information for these. Since it becomes a neckwork and spreads all over the country, a tunnel is indispensable in the mountainous area, etc., and there is an old technology for performing the construction of the tunnel safely, efficiently, and accurately at low cost. Various researches and developments have been carried out, and the improvement research is now being earnestly conducted.
【０００３】特に、山岳トンネルは山間部の多い我が国
の国土事情にあってその施工にさまざまな優れた技術が
開発され実用化されている。In particular, mountain tunnels have been developed and put into practical use with various excellent techniques for their construction in view of the national territory of Japan, which has many mountains.
【０００４】それらの１つにＮＡＴＭ工法があり、図９
に示す様に、所定の地山１に対しトンネル本体２を成す
掘削面３を形成させ、更に、該掘削面３の内面に吹付コ
ンクリート施工を行ってロックボルト５を打設し、更に
はＨ型をした鋼製の支保工で補強を行った後、その内側
に所定の不織布６、塩化ビニール，合成ゴム製等の防水
シート７を重層状に添設し、最後にその内面に覆工コン
クリート８を可及的に滑らかに施して高防水性のライニ
ングの施工を行うようにしている。One of them is the NATM method.
As shown in FIG. 2, a digging surface 3 forming a tunnel body 2 is formed on a predetermined natural ground 1, and further, an inner surface of the digging surface 3 is sprayed with concrete and a rock bolt 5 is struck. After reinforcement with a steel support that has been shaped, a predetermined non-woven fabric 6, a vinyl chloride, and a synthetic rubber waterproof sheet 7 are added in layers inside, and finally the inner surface is lined with concrete. 8 is applied as smoothly as possible to make the highly waterproof lining work.
【０００５】而して、掘削面３の内側に吹付コンクリー
ト４やロックボルト５、不織布６、防水シート７、覆工
コンクリート８等の施工を行うのはトンネル本体２の保
形性にかかわるものであるが、掘削面３の崩落等は地山
１からの漏水や湧水による場合が多く、これに対処する
ものであって、最内側の覆工コンクリート８にクラック
が生じたり、漏水や湧水により劣化する等の点に対処す
るべく、防水シート７と不織布６により分離されるアイ
ソレーション施工が一般に用いられている。The construction of the sprayed concrete 4, the rock bolt 5, the nonwoven fabric 6, the waterproof sheet 7, the lining concrete 8 and the like on the inside of the excavation surface 3 is concerned with the shape retention of the tunnel body 2. However, the collapse of the excavated surface 3 is often caused by water leakage or spring water from the natural ground 1, which is dealt with, and cracks occur in the innermost lining concrete 8, or water leakage or spring water In order to deal with the problem of deterioration due to, for example, isolation construction in which the waterproof sheet 7 and the nonwoven fabric 6 are separated is generally used.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、在来態
様のＮＡＴＭ工法における不織布６や防水シート７の支
保工施工済の吹付コンクリート４内面に対する不織布６
や防水シート７の貼り付け作業は該吹付コンクリート４
が掘削面３に不可避的に形成されている凹凸面に対し行
われるために、可及的に滑らかに仕上りを求められる作
業が通常手作業によって行われることから、極めて煩瑣
である難点があり、施工治具等が相当の重量であるにも
かかわらず、これらの治具を上向き姿勢でハンドリング
しながら作業せざるを得ないため、作業条件が極めて苛
酷であり、近時３Ｋ（キタナイ，キケン，キツイ）等の
悪条件の代表作業として嫌われるマイナス点があり、し
かも、防水シート７のユニットシート相互を継ぎ足して
所定エリアに防水層を形成するに、継目部分に於ける防
水性を確保するべく継目相互を重層状態に溶着、或い
は、接着する必要があって工数が多くなり、コスト高に
つながるというデメリットがある。However, the nonwoven fabric 6 in the conventional NATM method and the nonwoven fabric 6 for the inner surface of the sprayed concrete 4 after the supporting construction of the waterproof sheet 7 have been carried out.
The work of attaching the waterproof sheet 7 and the waterproof sheet 7 is done with the sprayed concrete 4
Is performed on an uneven surface which is unavoidably formed on the excavation surface 3, and therefore the work that requires a finish as smooth as possible is usually performed manually, which is a very troublesome point. Despite the heavy weight of construction jigs and the like, it is inevitable to work while handling these jigs in an upright position, so the working conditions are extremely severe, and 3K (Kitanai, Kiken, There is a negative point that is disliked as a representative work of bad conditions such as (Tight), and moreover, in order to form a waterproof layer in a predetermined area by adding the unit sheets of the waterproof sheet 7 together, in order to ensure the waterproof property in the joint part There is a demerit that it is necessary to weld or bond the seams to each other in a multi-layered state, resulting in a large number of steps and an increase in cost.
【０００７】[0007]
【発明の目的】この出願の発明の目的は上述従来技術に
基づく本来的には秀れたＮＡＴＭ工法による山岳トンネ
ル等のトンネル施工の防水性確保の問題点を解決すべき
技術的課題とし、地山に形成した掘削面の内側に不織布
を通常に添設し、該不織布表面に所定の防水液の吹き重
ね作業を行うだけで完全な防水層が形成出来、作業性が
良く、高能率で安全性が高く、低コストで施工が行え、
しかも、作業が省力的で機械化，自動化が可能であって
アイソレーションを兼ねた防水施工が行えるようにして
建設産業における土木施工技術利用分野に益する優れた
トンネルの高防水覆工方法を提供せんとするものであ
る。OBJECT OF THE INVENTION The purpose of the invention of this application is to solve the problem of ensuring waterproofness of tunnel construction such as a mountain tunnel by the originally excellent NATM method based on the above-mentioned prior art. A non-woven fabric is normally attached to the inside of the excavated surface formed in the mountain, and a complete waterproof layer can be formed simply by spraying a predetermined waterproof liquid on the non-woven fabric surface, which has good workability, high efficiency and safety. High performance, low cost construction,
Moreover, the work is labor-saving, mechanization and automation can be performed, and waterproof construction that also serves as isolation can be performed. Therefore, an excellent tunnel highly waterproof lining method that benefits the field of civil engineering construction application in the construction industry cannot be provided. It is what
【０００８】[0008]
【課題を解決するための手段・作用】上述目的に沿い先
述特許請求の範囲を要旨とするこの出願の発明の構成
は、前述課題を解決するために、山岳トンネル等のトン
ネルをＮＡＴＭ工法により所定に形成するに際し、当該
地山を掘削してトンネル本体を形成し、その掘削面に吹
付コンクリート施工を行い、ロックボルトやＨ型の鋼製
の支保工を施し、その後、吹付コンクリートの表面に不
織布をポリエステルスパンボンド不織布排水層、そし
て、更にポリエチレンフィルム非透水性層を中間層と
し、その内側にポリエステルスパンポンド不織布表面層
をサンドラミ法によって形成した不織布と成して添設
し、その際、ユニット不織布相互の継目に対しては一方
側の端縁部に他方側の端縁部を重ね合せてコンクリート
ピンにより吹付コンクリートに串刺しにして固定し、そ
の後、該不織布に対し速硬化ポリウレタンエラストマ
ー、及び、又は、ポリウレアエラストマー組成液をプロ
プラーガン等により所定厚さの防水層になるように吹付
させ瞬間的に硬化させて垂れ下がりや発泡が生じないよ
うにし、継目なく、所定範囲に滑らかで均一なアイソレ
ーションを兼ねた防水層が能率良く、短時間で経時的変
化なく形成されるようにした技術的手段を講じたもので
ある。In order to solve the above-mentioned problems, a tunnel such as a mountain tunnel is specified by the NATM method in order to solve the above-mentioned problems. At the time of forming, the ground is excavated to form the tunnel body, and the excavated surface is subjected to shotcrete construction, rock bolts and H-shaped steel support are applied, and then non-woven fabric is applied to the surface of shotcrete. A polyester spunbond nonwoven fabric drainage layer, and a polyethylene film water impermeable layer as an intermediate layer, and a polyester spunpond nonwoven fabric surface layer inside the nonwoven fabric formed by the sand laminating method. For the joints of non-woven fabrics, the edge of one side is overlapped with the edge of the other side and a concrete pin is used for spraying concrete. Then, the fast-curing polyurethane elastomer and / or the polyurea elastomer composition liquid is sprayed onto the non-woven fabric by a propeller gun or the like so as to form a waterproof layer having a predetermined thickness, and is momentarily cured to hang down. We have taken technical measures to prevent foaming and to form a waterproof layer that is seamless and has a smooth and uniform isolation over a predetermined range efficiently and in a short time without change over time. .
【０００９】[0009]
【実施例】次に、この出願の発明の１実施例を図１〜図
８に従って説明すれば以下の通りである。Next, one embodiment of the invention of this application will be described below with reference to FIGS.
【００１０】尚、図９と同一態様部分は同一符号を用い
て説明するものとする。The same parts as in FIG. 9 will be described using the same reference numerals.
【００１１】図示態様はＮＡＴＭ工法による山岳トンネ
ルを鉄道，道路を対象に形成施工する態様であって、支
保工としてはロックボルトによるものを示すものであ
る。The illustrated mode is a mode in which a mountain tunnel by the NATM method is formed and constructed for railroads and roads, and a rock bolt is used as the support work.
【００１２】図１に示す様に、所定の地山１に対しトン
ネル本体２を掘削し、その掘削面３は在来態様同様に崩
落等が生じないようにされる。As shown in FIG. 1, a tunnel main body 2 is excavated from a predetermined natural ground 1, and its excavated surface 3 is prevented from collapsing as in the conventional manner.
【００１３】そして、これまた在来態様同様に図２に示
す様に、該掘削面３のアーチ部を中心に吹付コンクリー
ト４を形成させ、次いで、ロックボルト５を打設し、該
ロックボルト５が貫設された吹付コンクリート４の内面
（表面）に図７に詳示する不織布６' を適宜な図示しな
い足場を介して貼付け添設する。As in the conventional mode, as shown in FIG. 2, spray concrete 4 is formed around the arch portion of the excavation surface 3, and then the rock bolt 5 is driven to form the rock bolt 5. The non-woven fabric 6'shown in detail in FIG. 7 is attached and attached to the inner surface (surface) of the sprayed concrete 4 through which the above is provided through an appropriate scaffold not shown.
【００１４】而して、添設する不織布６' はポリプロピ
レン，ポリエステル等の長繊維からなるスパンボンド法
によって得られる不織布等が好適に使用され、等方性で
所定の伸びが可能であり、充分な剛性を有するものが好
ましく、目付については１００〜３０００ｇ／ｍ2 （好
ましくは２００〜１０００ｇ／ｍ2 ），厚さ１〜２０ｍ
ｍ（２〜８ｍｍ）のものが使用可能である。As the attached non-woven fabric 6 ', a non-woven fabric or the like obtained by the spunbond method composed of long fibers such as polypropylene and polyester is preferably used, and it is isotropic and can be stretched to a predetermined extent. Having a high rigidity is preferable, and the basis weight is 100 to 3000 g / m 2 (preferably 200 to 1000 g / m 2 ), and the thickness is 1 to 20 m.
Those of m (2 to 8 mm) can be used.
【００１５】そして、吹付コンクリート４の不織布添設
面（内表面）が湿潤していたり、軽度の湧水，漏水があ
る場合には、添設する不織布６' が全体的に透水性の態
様のものを用いると、その後に吹付する速硬化性防水材
のエラストマー組成液の塗膜に吹付後発泡を伴う虞があ
るために、透水性の基層と内側の表面層との間に非透水
性層を中間層として組込むように形成された不織布６'
を使用し、例えば、透水性のポリエステル、又は、ポリ
プロピレン不織布片面にポリエチレン，ポリ塩化ビニー
ル等のフィルムをラミネートした不織布、つまり、ポリ
エステルスパンボンド層の中間にポリエチレン等のフィ
ルムをサンドラミ法によりサンドイッチ状にした不織布
等が使用可能であり、図７に示す様に、吹付コンクリー
ト４側に基層となるポリエステルスパンボンド不織布排
水層８１、そして、中間層としてポリエチレンフィルム
非透水性層８２、そして、内側層としてのポリエステル
スパンボンド不織布表面層８３から成る３層を所謂サン
ドラミ法によって厚さ５ｍｍ，幅１．８ｍのものをユニ
ット不織布６' に形成されたものを使用する。When the surface (inner surface) on which the non-woven fabric of the shotcrete 4 is wet is wet, or when there is a slight spring water or water leak, the non-woven fabric 6'to be attached is entirely water-permeable. If used, the coating film of the elastomer composition liquid of the quick-curing waterproof material that is subsequently sprayed may cause foaming after spraying.Therefore, a water-impermeable layer between the water-permeable base layer and the inner surface layer. Nonwoven fabric 6'formed so as to be incorporated as an intermediate layer
For example, a non-woven fabric obtained by laminating a film of polyethylene, polyvinyl chloride or the like on one surface of a water-permeable polyester or polypropylene non-woven fabric, that is, a film of polyethylene or the like in the middle of a polyester spun bond layer is formed into a sandwich by a sand laminating method. As shown in FIG. 7, a polyester spunbonded nonwoven fabric drainage layer 81 serving as a base layer on the side of the sprayed concrete 4, a polyethylene film impermeable layer 82 as an intermediate layer, and an inner layer as shown in FIG. The three-layered polyester spunbonded non-woven fabric surface layer 83 having a thickness of 5 mm and a width of 1.8 m is formed into a unit non-woven fabric 6 ′.
【００１６】尚、設計的に例示すると、基層のポリエス
テルスパンボンド不織布排水層８１は目付８００ｇ／ｍ
2 ，内側層のポエステルスパンボンド不織布表面層８３
は目付５０ｇ／ｍ2 とされる。As a design example, the polyester spunbonded nonwoven fabric drainage layer 81 as a base layer has a basis weight of 800 g / m 2.
2 , inner layer of polyester spunbonded nonwoven fabric surface layer 83
Is a basis weight of 50 g / m 2 .
【００１７】そして、各ユニット不織布６' の所定エリ
ア分の連続添設については図８に示す様に、一方側の端
縁部９に対し他方側の端縁部９を重ね合せ、吹付コンク
リート４に対しコンクリートピン５' により串刺して刺
し込み式に固設させて形成する。As for the continuous installation of each unit non-woven fabric 6'for a predetermined area, as shown in FIG. 8, the edge 9 on one side is overlapped with the edge 9 on the other side, and the sprayed concrete 4 On the other hand, it is formed by skewering with concrete pins 5'and fixing it in a stab style.
【００１８】尚、当該図８に示す実施例は模式態様であ
って各ユニット不織布６' の取り合いは設計的には連続
するものである。The embodiment shown in FIG. 8 is a schematic mode, and the unit non-woven fabrics 6'are continuous in design.
【００１９】したがって、ユニット不織布６' ，６' 相
互の継目取り合いはトンネル本体２の横断面方向は勿
論、縦断面方向の吹付コンクリート４に対し隈なく添設
されるものであり、所定エリアごとにユニット不織布６
' の添設が終了したところで順に次述する速硬化ポリウ
レタンポリウレアエラストマー防水材組成液７' をスプ
レーシステムにより吹付けする。Therefore, the joints between the unit nonwoven fabrics 6'and 6'are installed along the spray concrete 4 not only in the transverse direction of the tunnel body 2 but also in the longitudinal direction thereof. Unit non-woven fabric 6
When the installation of 'is completed, the rapid-curing polyurethane polyurea elastomer waterproofing material composition liquid 7', which will be described below, is sprayed by a spray system.
【００２０】この時、設計によってトンネル本体２の横
断方向に沿って吹付を行っても良いが、縦断面方向に沿
って行うようにする。At this time, the spraying may be carried out along the transverse direction of the tunnel body 2 depending on the design, but it is carried out along the longitudinal sectional direction.
【００２１】そして、吹付けでは、例えば、プロプラー
ガンを不織布６' の面に直交する姿勢で指向させドラム
缶等に充填してある主剤、及び、硬化剤をドラムヒータ
等により加温しながら、ドラムポンプによりホースを介
し循環させて所定の温度、例えば、５０℃になったとこ
ろで吹付を開始するようにする。In the spraying, for example, the propellant gun is oriented in a posture orthogonal to the surface of the non-woven fabric 6'and the main agent and the curing agent filled in the drum can are heated by the drum heater or the like while the drum pump is heated. Thus, the spraying is started when the temperature reaches a predetermined temperature, for example, 50 ° C., through the hose.
【００２２】そして、実験的に、或いは、機械的に吹付
け厚さが２ｍｍ等所定の塗膜厚さにするように適宜に作
業足場等を介して行う。Then, it is carried out experimentally or mechanically through a working scaffold or the like so that the sprayed film has a predetermined coating film thickness such as 2 mm.
【００２３】勿論、当該図８に示す様に、継目９に対す
る部分に於てもその一般部同様に、吹付コンクリート４
に対するライニング層の厚みが可及的に均一になるよう
に吹付して該吹付コンクリート４の凹凸面に倣いつつも
可及的に滑らかな面にするようにする そのため、防水層としての不織布６' は施工後継目が露
呈されず、均一なアイソレーションを兼ねた防水層とし
て形成され、数分後硬化した不織布６' に対する塗膜層
は垂れ下がりも発泡もせず、アイソレーション機能、及
び、防水機能を確実に有し、例えば、実験によれば、そ
の物性は伸び率６００％，引張り強度１２０ｋｇｆ／ｃ
ｍ2 ，引裂強度５０ｋｇｆ／ｃｍ2 と極めて良好な防水
性能を維持されるようにされる。Of course, as shown in FIG. 8, in the portion corresponding to the seam 9, as in the general portion, the shotcrete concrete 4 is used.
The lining layer is sprayed so that the thickness of the lining layer is as uniform as possible, and the surface is made as smooth as possible while following the uneven surface of the sprayed concrete 4. Therefore, the nonwoven fabric 6'as a waterproof layer. Is a waterproof layer that does not expose the seams after construction and also functions as a uniform isolation, and the coating layer on the nonwoven fabric 6'cured after a few minutes does not sag or foam, providing an isolation function and a waterproof function. It surely has, for example, according to the experiment, its physical properties are an elongation rate of 600% and a tensile strength of 120 kgf / c.
m 2 and tear strength of 50 kgf / cm 2 are maintained so that extremely good waterproof performance is maintained.
【００２４】そして、不織布６' の内側に塗布する速硬
化エラストマー組成液７' については主剤と硬化剤の２
成分から成るものであり、該主剤は過剰のＭＤＩ、及
び、ＭＴＬ（カルボジイミドで部分変性したＭＤＩ）と
ポリプロピレンエーテルポリオールとの反応により得ら
れた部分プレポリマー（若干の可塑剤を加えて粘度を調
整した），硬化剤は芳香族ポリアミンとポリプロピレン
エチレンエーテルポリオールと少量の有機金属触媒等を
含む混合溶液とする。The fast-curing elastomer composition liquid 7'applied to the inside of the non-woven fabric 6'is composed of a main agent and a curing agent.
The main component is an excess MDI and a partial prepolymer obtained by the reaction of MTL (MDI partially modified with carbodiimide) and polypropylene ether polyol (the viscosity is adjusted by adding some plasticizers). The curing agent is a mixed solution containing an aromatic polyamine, polypropylene ethylene ether polyol, and a small amount of an organometallic catalyst.
【００２５】そして、吹付はプロプラーガン併用の高圧
混合式吹付機、及び、静止型管内混合器を装備した２液
混合吐出スプレー装置等が使用可能であり、実験によれ
ば、数秒、乃至、数分の極めて短時間で引張り強度８０
〜１６０ｋｇｆ／ｃｍ2 ，伸び率３５０〜７５０％，引
裂強度４０〜６０ｋｇｆ／ｃｍ2 の高性能の防水性能を
有する吹付塗膜が不織布６' と一体化されて形成され
る。For spraying, it is possible to use a high-pressure mixing sprayer combined with a propeller gun, a two-liquid mixing discharge sprayer equipped with a static type in-pipe mixer, etc. According to experiments, several seconds to several minutes can be used. Tensile strength of 80 in an extremely short time
A sprayed coating film having a high performance of waterproofing of 160 kgf / cm 2 , elongation of 350 to 750% and tear strength of 40 to 60 kgf / cm 2 is formed integrally with the nonwoven fabric 6 ′.
【００２６】尚、速硬化エラストマー組成液吹付作業は
施設的にはガイドレールと駆動装置の組合せ方式による
自動化プラントを用いることが可能である。Incidentally, for the operation of spraying the liquid of the quick-curing elastomer composition, it is possible to use an automated plant as a facility by a combination system of a guide rail and a driving device.
【００２７】而して、この出願の発明の要旨の中心を成
す速硬化エラストマー組成液については速硬化ポリウレ
タンエラストマー、及び、又は、ポリウレアエラストマ
ーの組成液が用いられ得、有機ポリイソシアネートを成
分とする主剤とポリオール、又は、ポリエーテルアミ
ン、及び、芳香族ポリアミンを必須成分とする硬化剤と
の２成分から成るものが使用され得、主剤の必須成分と
して用いられる有機ポリイソシアネートとしてはジフェ
ニルメタン−２，４' 、及び、４，４' −ジイソシアネ
ート（ＭＤＩ），ポリメチレンポリフェニルイソシアネ
ート，カルボジイミドで部分変性した常温で液状のＭＤ
Ｉ、又は、過剰のＭＤＩとポリオールとの反応により得
られるイソシアネート末端部分プレポリマー等が使用さ
れ得、これらの有機ポリイソシアネートの粘度調整のた
めに若干の可塑剤を添加することも可能である。Thus, for the fast-curing elastomer composition liquid which forms the center of the gist of the invention of this application, a quick-curing polyurethane elastomer and / or polyurea elastomer composition liquid can be used, and contains an organic polyisocyanate as a component. It is possible to use a two-component composition containing a main agent and a polyol, or a polyether amine, and a curing agent having an aromatic polyamine as an essential component, and as an organic polyisocyanate used as an essential component of the main agent, diphenylmethane-2, MD at room temperature which is partially modified with 4'and 4,4'-diisocyanate (MDI), polymethylene polyphenyl isocyanate, carbodiimide
I, or an isocyanate-terminated partial prepolymer obtained by the reaction of excess MDI with a polyol can be used, and it is possible to add some plasticizer for adjusting the viscosity of these organic polyisocyanates.
【００２８】一方、硬化剤の必須成分として用いられる
ポリオールとしてはポリプロピレンエーテルポリオー
ル，ポリプロピレンエチレンエーテルポリオール，ポリ
テトラメチレンエーテルポリオール等のポリエーテルポ
リオール，ポリカプロラクトンポリオール等が使用可能
であり、この場合、平均分子量が１０００〜５０００の
ポリエーテルポリオールが好ましくエチレングリコー
ル，１．４ブタンジオール等のグリコール類を併用する
ことも出来る。On the other hand, as the polyol used as an essential component of the curing agent, polypropylene ether polyol, polypropylene ethylene ether polyol, polyether polyol such as polytetramethylene ether polyol, polycaprolactone polyol, etc. can be used. A polyether polyol having a molecular weight of 1000 to 5000 is preferable, and glycols such as ethylene glycol and 1.4 butanediol can be used in combination.
【００２９】硬化剤の１つの成分としてポリオールを使
用すると、芳香族ポリアミンの使用と共に主剤の有機イ
ソシアネートとの反応によってポリウレタンポリウレア
エラストマーを生成することが出来る。The use of a polyol as one component of the curing agent allows the use of aromatic polyamines as well as reaction with the base isocyanate to form polyurethane polyurea elastomers.
【００３０】この場合、主剤のイソシアネートと硬化剤
のポリオール，芳香族ポリアミンとの反応性を調整する
べくオクテン酸鉛等の有機金属触媒が使用可能である。In this case, an organometallic catalyst such as lead octenoate can be used in order to adjust the reactivity between the main component isocyanate and the curing agent polyol and aromatic polyamine.
【００３１】そして、ポリエーテルアミンとしてはポリ
プロピレン、又は、ポリテトラメチレンエーテルポリオ
ールの末端のＯＨ基のアミノ基に変換した商品名ジエフ
ァミン等のポリエーテルアミンの使用が可能であるが、
好ましくは平均分子量１０００〜５０００のポリエーテ
ルアミンが望ましい。As the polyetheramine, it is possible to use polypropylene, or a polyetheramine such as diefamin under the trade name of polytetramethylene ether polyol, which is converted into an amino group of the terminal OH group.
A polyether amine having an average molecular weight of 1,000 to 5,000 is desirable.
【００３２】そして、硬化剤の１成分として用いられる
芳香族ポリアミンとしては３．５ジエチル−２．４−及
び２．６−ジアミノトルエン（ＤＥＴＤＡ）３，３' ，
５，５' −テトライソプロピル−４．４' −ジアミノジ
フェニルメタン，アニリンフォルムアルデヒド縮合によ
って得られるポリフェニルポリメチレンポリアミン，
３．５−ジメチルチオ−２，４及び２，６−ジアミノト
ルエン等が使用可能である。As the aromatic polyamine used as one component of the curing agent, 3.5 diethyl-2.4- and 2.6-diaminotoluene (DETDA) 3,3 ',
5,5'-tetraisopropyl-4.4'-diaminodiphenylmethane, polyphenyl polymethylene polyamine obtained by aniline formaldehyde condensation,
3.5-Dimethylthio-2,4 and 2,6-diaminotoluene can be used.
【００３３】而して、かかる主剤と硬化剤とから成る速
硬化エラストマー組成液については主剤のＮＣＯ基と硬
化剤のＮＨ2 基、又は、該ＮＨ2 基とＯＨ基との合計の
当量基比が０．９〜１．３（好ましく１．０〜１．２）
とされるように調整する。In the case of the fast-curing elastomer composition liquid containing the main agent and the curing agent, the NCO group of the main agent and the NH 2 group of the curing agent, or the equivalent group ratio of the total of the NH 2 group and the OH group is used. Is 0.9 to 1.3 (preferably 1.0 to 1.2)
Adjust so that
【００３４】尚、この出願の発明の実施態様は上述実施
例に限るものでないことは勿論であり、例えば、支保工
についてはロックボルトの代わりに鋼製支保工を用いて
も良い等種々の態様が採用可能である。The embodiment of the invention of the present application is not limited to the above-mentioned embodiment, and for example, for the support work, a steel support work may be used instead of the lock bolt. Can be adopted.
【００３５】そして、適用対象は山岳トンネル以外のト
ンネルにも適用可能である。The application target is applicable to tunnels other than mountain tunnels.
【００３６】[0036]
【発明の効果】以上、この出願の発明によれば、基本的
に山岳トンネル等のトンネルの施工に際しＮＡＴＭ工法
を用いて防水施工を行うに、覆工コンクリートを施すプ
ロセスでアイソレーションを兼ねた防水層の形成が確実
に行われ、掘削面に施された吹付コンクリートの凹凸面
が不可避的に形成されても、これを緩和して平滑なトン
ネル内面とすることが可能であり、該吹付コンクリート
の内面が湿潤していたり、或いは、軽度の湧水，漏水が
あっても、吹付コンクリート面に添設する不織布が排水
層の機能をも有していることにより、該不織布に速硬化
エラストマー組成液を吹付して発泡が生じない均一な不
織布と一体化した高防水性の防水層が極めて短時間に効
率良く、正確に設計通りに形成されるという優れた効果
が奏される。As described above, according to the invention of the present application, basically, when the waterproof construction is carried out by using the NATM method when constructing a tunnel such as a mountain tunnel, the waterproofing which also serves as isolation in the process of applying the lining concrete. Even if the layer is formed reliably and the uneven surface of the shotcrete applied to the excavated surface is unavoidably formed, it is possible to relax it to form a smooth tunnel inner surface. Even if the inner surface is wet, or even if there is slight spring water or water leakage, the non-woven fabric attached to the sprayed concrete surface also has the function of a drainage layer. The excellent effect that a highly waterproof waterproof layer integrated with a uniform non-woven fabric that is sprayed with and is formed in an extremely short time efficiently and accurately as designed is exhibited.
【００３７】そして、従来のＮＡＴＭ工法に用いられる
塩化ビニールや合成ゴム製等の防水シートに比して不織
布は軽量であることから、吹付コンクリートの内面に貼
付け等の添設作業を行う際にも取り扱いが容易で作業が
し易く、労力が軽減され、それだけ、高精度の防水層形
成が成される効果がある。Since the non-woven fabric is lighter than the waterproof sheet made of vinyl chloride, synthetic rubber or the like used in the conventional NATM method, it can be attached to the inner surface of the sprayed concrete when it is attached. It is easy to handle, easy to work with, less labor is required, and a highly accurate waterproof layer is formed.
【００３８】そして、速硬化エラストマー組成液の吹付
により短時間で充分な引張り強度，引裂強度を具備する
ようにされ、加えて充分な伸び率をも具備させることが
出来、そのうえ、ガイドレールや駆動装置の機能を有す
るプラントにより完全自動化が図れるという効果も奏さ
れる。By spraying the quick-curing elastomer composition liquid, sufficient tensile strength and tear strength can be provided in a short time, and in addition, sufficient elongation can be provided. There is also an effect that the plant having the function of the apparatus can achieve full automation.
【００３９】このようにして継目がなく、不織布と一体
化して均一なアイソレーション機能をも具備する防水層
が能率良く、正確に短時間で形成され得、しかも、該防
水層の物性も充分であり、耐久性も確実に保証されると
いう効果が奏される。In this way, the waterproof layer which is seamless and integrated with the non-woven fabric and has a uniform isolation function can be formed efficiently and accurately in a short time, and the physical properties of the waterproof layer are sufficient. There is an effect that the durability is surely guaranteed.
【図１】トンネル掘削によってトンネル本体を形成する
施工概略断面図である。FIG. 1 is a schematic cross-sectional view of a construction for forming a tunnel body by tunnel excavation.
【図２】トンネル本体の掘削面内側に対する吹付コンク
リートの施工の概略断面図である。FIG. 2 is a schematic cross-sectional view of construction of shotcrete on the inside of the excavated surface of the tunnel body.
【図３】吹付コンリートに対するロックボルト貫設の概
略断面図である。FIG. 3 is a schematic cross-sectional view of a lock bolt penetrating the spraying fillet.
【図４】吹付コンクリートとロックボルトの内面に不織
布を添設する施工概略断面図である。FIG. 4 is a schematic cross-sectional view of a construction in which a nonwoven fabric is attached to the inner surfaces of shotcrete and rock bolts.
【図５】不織布の内面に対する速硬化エラストマー組成
液吹付の施工概略断面図である。FIG. 5 is a schematic cross-sectional view of a quick-curing elastomer composition liquid spraying process on the inner surface of the nonwoven fabric.
【図６】覆工コンクリートの施工概略断面図である。FIG. 6 is a schematic cross-sectional view of construction of lining concrete.
【図７】不織布の構造概略断面図である。FIG. 7 is a schematic cross-sectional view of a nonwoven fabric structure.
【図８】不織布の継目部の概略構造断面図である。FIG. 8 is a schematic structural cross-sectional view of a joint portion of a nonwoven fabric.
【図９】従来技術によるＮＡＴＭ工法を介してのトンネ
ル施工概略断面図である。FIG. 9 is a schematic cross-sectional view of tunnel construction through the NATM method according to the conventional technique.
１ 地山 ２ トンネル本体 ３ 掘削面 ４ 吹付コンクリート ５ ロックボルト ６ 防水性シート ６' 不織布 ７' 速硬化エラストマー組成液 ８ 覆工コンクリート ９ 継目 ５' コンクリートピン 1 Ground 2 Tunnel body 3 Excavation surface 4 Shotcrete 5 Rock bolt 6 Waterproof sheet 6'Nonwoven fabric 7'Fast curing elastomer composition liquid 8 Lining concrete 9 Seam 5 'Concrete pin
───────────────────────────────────────────────────── フロントページの続き (72)発明者 相沢 林作 静岡県富士市中野337−６ (72)発明者 亀岡 美友 静岡県富士市石坂91 (72)発明者 望月 茂 神奈川県横浜市中区仲尾台55 ヴィルヌー ブ山手Ｂ414 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Ryosaku Aizawa 337-6 Nakano, Fuji City, Shizuoka Prefecture (72) Inventor Mitomo Kameoka 91 Ishizaka, Fuji City, Shizuoka Prefecture (72) Inventor Shigeru Mochizuki Naka Ward, Yokohama City, Kanagawa Prefecture Nakaodai 55 Villeneuve Yamate B414
Claims (5)
削面に吹付コンクリートを施し該吹付コンクリートの表
面に非透水層を有する不織布を縁切り材（アイソレーシ
ョン）として添設し該不織布表面に覆工コンクリートを
打設するようにするトンネルの高防水覆工方法におい
て、上記不織布の表面に対し速硬化ポリウレタンエラス
トマーとポリウレアエラストマーの少くともいずれか一
方のエラストマー組成液を吹付けるようにすることを特
徴とするトンネルの防水覆工方法。1. A ground for tunnel formation is excavated in a predetermined manner, sprayed concrete is applied to the excavated surface, and a non-woven fabric having a water impermeable layer is attached to the surface of the sprayed concrete as an edging material (isolation). In a highly waterproof lining method for a tunnel in which lining concrete is poured, it is preferable to spray at least one elastomer composition liquid of a fast-curing polyurethane elastomer and a polyurea elastomer onto the surface of the non-woven fabric. Characteristic tunnel lining method.
布を用いるようにすることを特徴とする特許請求の範囲
第１項記載のトンネルの高防水覆工方法。2. The highly waterproof lining method for a tunnel according to claim 1, wherein a nonwoven fabric having a water impermeable layer is used as the nonwoven fabric.
ソシアネートを必須成分とする主剤とポリオール，ポリ
エーテルアミンのいずれか及び芳香族ポリアミンを必須
成分とする硬化剤とから成るエラストマー組成液を用い
るようにすることを特徴とする特許請求の範囲第１項記
載のトンネルの高防水覆工方法。3. An elastomer composition liquid comprising a main agent containing an organic polyisocyanate as an essential component and a curing agent containing any one of a polyol and a polyether amine and an aromatic polyamine as an essential component is used as the elastomer composition liquid. A highly waterproof lining method for a tunnel according to claim 1, wherein
相互の継目を一方の不織布の端縁部に対し他方の不織布
の端縁部を単に重ね合せ、ピン打ち込みにより吹付コン
クリートに固定するようにすることを特徴とする特許請
求の範囲第１項記載のトンネルの高防水覆工方法。4. A seam between adjacent unit non-woven fabrics attached to the non-woven fabrics is simply superposed on one end fabric edge end fabric and the other non-woven fabric end joint is fixed to the spray concrete by pin driving. The highly waterproof lining method for a tunnel according to claim 1, wherein
湧水がある場合には、不織布間に接着テープ等を用いて
貼り付ける、或いは重ね部分に接着テープを貼る、その
後ピン打ち込みにより吹付コンクリートに固定すること
を特徴とする特許請求の範囲第１項記載のトンネルの高
防水覆工方法。5. When the edges of the non-woven fabrics are superposed on each other, if there is a slight spring water, the non-woven fabrics are pasted with an adhesive tape or the like, or the superposed regions are pasted with an adhesive tape, and then sprayed by pin driving. The method for lining a tunnel with high waterproofness according to claim 1, characterized in that it is fixed to concrete.