JPH0754293A - Bulky paper - Google Patents
Bulky paperInfo
- Publication number
- JPH0754293A JPH0754293A JP21907493A JP21907493A JPH0754293A JP H0754293 A JPH0754293 A JP H0754293A JP 21907493 A JP21907493 A JP 21907493A JP 21907493 A JP21907493 A JP 21907493A JP H0754293 A JPH0754293 A JP H0754293A
- Authority
- JP
- Japan
- Prior art keywords
- enzyme
- pulp
- paper
- treated
- bulky
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、嵩高紙に関し、特に、
多糖類を分解する酵素やその酵素を生産する微生物によ
り処理されたパルプを利用する嵩高紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to bulky paper, and in particular,
The present invention relates to a high-bulk paper that uses a pulp treated with an enzyme that decomposes a polysaccharide and a microorganism that produces the enzyme.
【0002】[0002]
【従来の技術】紙製品は、その使用目的に応じて様々な
物性が要求され、その物性としては、例えば機械的強
度、寸法安定性及び地合等が挙げられる。近年、感触が
良好な紙製品を得る上から、これらの物性の中でも、特
に嵩高性が重要となり、嵩高紙を得るために種々の製造
方法が検討されている。例えば、特開平01−1186
25号公報には、パルプ、炭素繊維製造用有機繊維及び
有機高分子物質のエマルジョンの特定割合からなる抄紙
シートを加熱処理した後、更に加熱して炭化させること
により、嵩高な炭素板を得る方法が開示されている。2. Description of the Related Art Paper products are required to have various physical properties according to the purpose of use, and examples of the physical properties include mechanical strength, dimensional stability and formation. In recent years, in order to obtain a paper product having a good feel, among these physical properties, bulkiness is particularly important, and various manufacturing methods have been studied to obtain bulky paper. For example, Japanese Patent Laid-Open No. 01-1186
No. 25, a method for obtaining a bulky carbon plate by heat-treating a papermaking sheet comprising a specific proportion of pulp, organic fibers for carbon fiber production and an emulsion of an organic polymer substance, and then further heating and carbonizing. Is disclosed.
【0003】同様に、特開平03−174089号公報
には、ガラスウール等の鉱物繊維をセルロース繊維に混
合することにより、嵩高で剛性のあるパルプを得る方法
が開示されている。また、特開平03−269199号
公報には、パルプ、特定のポリエステル複合繊維及び熱
融着性バインダー繊維を高速撹拌ミキサーで混合分散し
た後、得られたパルプスラリーから抄紙した原紙を積層
し、熱処理することにより、嵩高なパルプシートを製造
する方法が開示されている。Similarly, Japanese Patent Application Laid-Open No. 03-174089 discloses a method for obtaining bulky and rigid pulp by mixing mineral fibers such as glass wool with cellulose fibers. Further, in Japanese Patent Laid-Open No. 03-269199, after pulp, a specific polyester composite fiber and a heat-fusible binder fiber are mixed and dispersed by a high-speed stirring mixer, a base paper made from the obtained pulp slurry is laminated and heat treated. By doing so, a method for producing a bulky pulp sheet is disclosed.
【0004】更に、填料を改良した例として、特開平0
3−124895号公報には、粒子径が0.5〜30μ
mの範囲にある中空球状パテライト型炭酸カルシウム
を、填料として3重量%以上含有させ、嵩高な中性紙を
製造する方法が開示されている。しかしながら、上記の
方法は、いずれもパルプに、他の繊維、高分子物質又は
填料等の添加剤を添加することにより、嵩高さを付与し
ようとするものであり、従って、これらの方法において
は、セルロース繊維自体が改質されるわけではない。ま
た、添加された他の繊維や高分子物質等によって、製造
される紙の性質が大きく左右されることになる。Further, as an example in which the filler is improved, Japanese Patent Laid-Open No.
In JP-A-3-124895, the particle size is 0.5 to 30 μm.
There is disclosed a method for producing a bulky neutral paper by incorporating 3% by weight or more of hollow spherical puterite type calcium carbonate in the range of m as a filler. However, any of the above methods is to add bulk to the pulp by adding other fibers, additives such as polymer substances or fillers, and therefore, in these methods, in these methods, The cellulose fiber itself is not modified. In addition, the properties of the produced paper are greatly influenced by other added fibers and polymer substances.
【0005】一方、弾性ロールを用いてカレンダー仕上
げをするソフトカレンダー処理も試みられている。例え
ば、特開平4−370293号公報には、グラビア用紙
のカレンダー処理直前に、低圧で軽度の加熱蒸気を付与
して紙面を加湿、加熱した後、ロール温度を100〜1
50℃としてソフトカレンダー処理をすることにより、
目的の嵩高紙を得る方法が開示されている。しかしなが
ら、ソフトカレンダー法は、カレンダー処理における
『紙の押し潰し方』をやわらかくする方法であり、この
方法においてもセルロース繊維自体が嵩高な性質に改質
されるわけではない。また、この方法は新たに弾性ロー
ル等の装置を導入する必要のある方法であり、初期投資
が必要である。On the other hand, a soft calendering process for calendering using an elastic roll has been attempted. For example, in Japanese Unexamined Patent Publication No. 4-370293, immediately before the calendar processing of gravure paper, a low heating pressure is applied to slightly heat steam to moisten and heat the paper surface, and then the roll temperature is set to 100 to 1
By soft calendering at 50 ℃,
A method for obtaining the desired bulky paper is disclosed. However, the soft calendering method is a method for softening the "how to crush paper" in the calendering process, and even in this method, the cellulose fibers themselves are not modified to have bulky properties. Moreover, this method requires a new device such as an elastic roll, and requires an initial investment.
【0006】[0006]
【発明が解決しようとする課題】そこで、本発明者ら
は、新たな投資を必要とすることがない上、セルロース
繊維そのものを改質した嵩高紙を得るために鋭意検討し
た結果、多糖類を分解する酵素又は該酵素を生産する微
生物により処理された酵素処理パルプが嵩高となるこ
と、従って、それを原料とした紙も又嵩高となることを
見い出し、本発明に到達した。従って、本発明の目的
は、初期投資を必要とすることなく、原料であるパルプ
そのものを改質した崇高紙を得ることにある。Therefore, the inventors of the present invention did not require new investment and, as a result of diligent studies to obtain bulky paper in which the cellulose fiber itself was modified, as a result, polysaccharides were identified. It has been found that the enzyme-treated pulp treated with an enzyme that decomposes or a microorganism that produces the enzyme becomes bulky, and therefore paper made from it becomes bulky, and the present invention was reached. Therefore, an object of the present invention is to obtain sublime paper obtained by modifying pulp itself, which is a raw material, without requiring an initial investment.
【0007】[0007]
【課題を解決するための手段】本発明の上記の目的は、
多糖類を分解する酵素及び/又は該酵素を生産する微生
物により処理された酵素処理パルプを原料として製造さ
れてなることを特徴とする嵩高紙により達成された。以
下、本発明を更に詳細に説明する。The above objects of the present invention are as follows.
The present invention has been achieved by a high-bulk paper characterized by being produced using an enzyme-treated pulp treated with an enzyme that decomposes a polysaccharide and / or a microorganism that produces the enzyme as a raw material. Hereinafter, the present invention will be described in more detail.
【0008】本発明に使用するパルプは、例えば、木材
パルプ、稲わらパルプ及びケナフパルプ等の公知のパル
プの中から適宜選択して使用することができる。本発明
において使用する酵素は、パルプに含有されるセルロー
ス等の多糖類を分解することができる酵素である限り、
特に制限されず、例えば、セルラーゼ、ヘミセルラーゼ
及びキシラナーゼ等を挙げることができる。更に、こう
した特質を有する酵素を生産する微生物も含まれる。The pulp used in the present invention can be appropriately selected and used from known pulps such as wood pulp, rice straw pulp and kenaf pulp. As long as the enzyme used in the present invention is an enzyme capable of decomposing polysaccharides such as cellulose contained in pulp,
It is not particularly limited, and examples thereof include cellulase, hemicellulase, and xylanase. Further included are microorganisms that produce enzymes with these attributes.
【0009】これらのセルラーゼやキシラナーゼのよう
な多糖類を分解する酵素としては、目的とする効果が得
られるものであれば、現在市販されている各種の酵素製
剤、例えば、セルラーゼアマノ(天野製薬株式会社製の
商品名)、セルクラスト(Novo社製の商品名)、バグト
ゾールDCLQ(サンド社製の商品名)等を使用するこ
とができる。As enzymes for degrading polysaccharides such as cellulase and xylanase, various enzyme preparations currently on the market, such as cellulase amano (Amano Pharmaceutical Co., Ltd.), can be used so long as the desired effects can be obtained. Company-made product name), Celcrust (Novo product name), Bagtosol DCLQ (Sand product name) and the like can be used.
【0010】本発明においては、前記酵素に代えて、又
は前記酵素と共に、前記酵素を生産する微生物を用いて
も良い。上記の微生物は、前記の酵素を生産する微生物
であれば良い。このような微生物としては、例えば、ト
リコデルマ属やアスペルギルス属等の糸状菌、カワラタ
ケ属やマクカワタケ属等の担子菌を挙げることができ
る。これらの担子菌の中でも、特に、カワラタケ属やマ
クカワタケ属等の白色腐朽菌を用いた場合には、パルプ
の漂白も同時に行うことができるという二次的効果をも
得ることができる。In the present invention, a microorganism which produces the enzyme may be used instead of the enzyme or together with the enzyme. The above microorganism may be any microorganism that produces the above enzyme. Examples of such microorganisms include filamentous fungi such as Trichoderma spp. And Aspergillus spp. And basidiomycetes such as Kawaratake spp. Among these basidiomycetes, in particular, when a white-rot fungus of the genus Kawaratake or Macawatake is used, a secondary effect that pulp can be bleached at the same time can be obtained.
【0011】次に、酵素又は微生物を用いてパルプを処
理する方法について説明する。パルプの酵素処理は、基
本的には酵素を溶解した液にパルプを浸積し、酵素反応
を行わせれば良い。酵素の種類によりその酵素活性や至
適条件は大きく異なるので、酵素反応を行わせる際の酵
素の使用量及び反応条件は、用いる酵素の種類に応じて
設定する必要がある。Next, a method of treating pulp with an enzyme or a microorganism will be described. Basically, the enzyme treatment of the pulp may be carried out by immersing the pulp in a liquid in which the enzyme is dissolved and causing the enzyme reaction. Since the enzyme activity and the optimum conditions vary greatly depending on the type of enzyme, it is necessary to set the amount of the enzyme used and the reaction conditions for carrying out the enzymatic reaction according to the type of enzyme used.
【0012】また、微生物処理の場合には、培養した菌
を直接パルプに添加しても、培養液を適度に希釈した液
にパルプを浸漬しても良い。その際の条件についても、
酵素の場合と同様に用いる菌の種類により条件が異なる
ので、その都度、条件の検討を行う必要がある。パルプ
の酵素及び/又は微生物処理に関係する因子としては、
パルプ濃度、酵素量、微生物量、pH、温度及び反応時
間等が挙げられるが、基本的には、使用する酵素や微生
物の生理学的性質の範囲内の条件で処理すれば良い。In the case of microbial treatment, the cultivated bacteria may be added directly to the pulp, or the pulp may be immersed in a liquid obtained by appropriately diluting the culture liquid. Regarding the conditions at that time,
Since conditions vary depending on the type of bacteria used, as in the case of enzymes, it is necessary to examine the conditions each time. Factors related to enzyme and / or microbial treatment of pulp include
The pulp concentration, the amount of enzyme, the amount of microorganisms, pH, temperature, reaction time and the like can be mentioned. Basically, the treatment may be carried out under the conditions within the range of physiological properties of the enzyme or microorganism used.
【0013】例えば、白色腐朽菌であるマクカワタケ属
のきのこであるファネロケーテ・クリソスポリウム(Ph
anerocheate chrysosporium )を用いて固体培養を行う
場合には、パルプ濃度が重要な因子となり、その濃度は
10〜20重量%の範囲であることが好ましい。パルプ
濃度が10重量%未満となると、菌糸とパルプが接触し
にくくなり、逆に20重量%を超えると、水分が少なく
なるため菌糸が生育しにくくなる。[0013] For example, funerocete chrysosporium (Ph), which is a mushroom of the genus McKawatake, which is a white-rot fungus
When solid culture is performed using anerocheate chrysosporium), the pulp concentration is an important factor, and the concentration is preferably in the range of 10 to 20% by weight. When the pulp concentration is less than 10% by weight, it is difficult for the hyphae to come into contact with the pulp. On the contrary, when the pulp concentration is more than 20% by weight, the water content is small and the hyphae are difficult to grow.
【0014】一方、振盪培養の場合には、パルプ濃度を
低くしなければ振盪することができないので、最適パル
プ濃度は10重量%以下である。本発明においては、同
様の活性を有する複数の酵素又は微生物を併用して、処
理を行っても良い。例えば、同じセルラーゼであって
も、トリコデルマ属菌由来のものとアスペルギルス属菌
由来のものでは、その性質が相違するため、両者を併用
するとセルロースの加水分解がより効果的に進行するこ
とが良く知られているが、このことは本発明においても
同様である。On the other hand, in the case of shake culture, the optimum pulp concentration is not more than 10% by weight because it cannot be shaken unless the pulp concentration is lowered. In the present invention, a plurality of enzymes or microorganisms having the same activity may be used in combination for the treatment. For example, even if the same cellulase, the Trichoderma spp. And Aspergillus spp. However, this also applies to the present invention.
【0015】従って、市販の酵素製剤の中の、その由来
の異なるものを幾つか選択して使用しても良く、あるい
はその菌を培養した培養液を混合して使用しても良い。
本発明においては、これらの酵素又は微生物処理におけ
る処理効果をあげる為に、無機膨潤剤水溶液によってパ
ルプを前処理しても良い。この前処理を行うことによ
り、セルロースの結晶領域を膨潤させることができるの
で、一層効果的に酵素を作用させることができる。上記
の無機膨潤剤としては、水酸化ナトリウム、水酸化カリ
ウム又は水酸化リチウム等のアルカリ剤や、2−エチル
ヘキシ化硫酸ナトリウム等が挙げられる。Therefore, among commercially available enzyme preparations, some of them having different origins may be selected and used, or a culture solution in which the bacterium is cultured may be mixed and used.
In the present invention, the pulp may be pretreated with an aqueous solution of an inorganic swelling agent in order to enhance the treatment effect in treating these enzymes or microorganisms. By carrying out this pretreatment, the crystalline region of cellulose can be swollen, so that the enzyme can act more effectively. Examples of the above-mentioned inorganic swelling agent include alkali agents such as sodium hydroxide, potassium hydroxide and lithium hydroxide, and 2-ethylhexylated sodium sulfate.
【0016】本発明においては、原料であるパルプ自体
に嵩高さを持たせることにより、製品である紙に嵩高さ
を付与しているが、酵素又は微生物処理によりパルプが
嵩高くなる理由については明らかではない。多糖分解酵
素には加水分解能だけでなく、結晶領域の水素結合や繊
維間結合を切断して繊維を膨潤させ、酵素が繊維に接し
易くさせる能力があるといわれている。この繊維膨潤能
力により、繊維そのものが膨潤し、崇高になるのではな
いかと考えられる。In the present invention, the pulp, which is the raw material, is made bulky to give bulk to the paper, which is the product, but the reason why the pulp becomes bulky by the enzyme or microbial treatment is clear. is not. It is said that the polysaccharide-degrading enzyme has not only the ability to hydrolyze, but also the ability to swell the fiber by breaking hydrogen bonds and interfiber bonds in the crystal region, so that the enzyme can easily contact the fiber. It is thought that this fiber swelling ability causes the fibers themselves to swell and become sublime.
【0017】[0017]
【発明の効果】本発明の嵩高紙は、単に多糖類を分解す
る酵素又は該酵素を生産する微生物により処理された酵
素処理パルプを原料として用いることにより、製造に際
して特別の装置を必要とせず容易に得ることができるの
で、本発明の意義は極めて有意義である。Industrial Applicability The bulky paper of the present invention can be easily manufactured without using a special apparatus by using an enzyme-treated pulp treated with an enzyme that decomposes a polysaccharide or a microorganism that produces the enzyme as a raw material. Therefore, the significance of the present invention is extremely significant.
【0018】[0018]
【実施例】以下、実施例により本発明を更に詳細に説明
するが、本発明はこれによって限定されるものではな
い。EXAMPLES The present invention will be described in more detail with reference to examples below, but the present invention is not limited thereto.
【0019】実施例1.酵素処理パルプの調製 広葉樹の晒パルプ(日本製紙株式会社製)を以下の条件
で、セルラーゼ処理(天野製薬株式会社製の商品名:セ
ルラーゼアマノ)し、酵素処理パルプを調製した。 パルプ濃度 10重量% 酵素(セルラーゼアマノ) 0.05重量%(対
パルプ) pH 5.0 温度 50℃ 反応時間 1.5時間Example 1. Preparation of Enzyme-treated Pulp A bleached hardwood pulp (manufactured by Nippon Paper Industries Co., Ltd.) was subjected to a cellulase treatment (trade name of Amano Pharmaceutical Co., Ltd .: Cellulase Amano) under the following conditions to prepare an enzyme-treated pulp. Pulp concentration 10% by weight Enzyme (cellulase amano) 0.05% by weight (vs. pulp) pH 5.0 Temperature 50 ° C Reaction time 1.5 hours
【0020】手抄紙の調製 上記の酵素処理パルプを原料として丸型シートマシンを
用い、JIS P−8209に従って秤量40g/m2
の手抄紙シートを調製した。手抄紙シートの厚さ及び嵩比重の測定 上記のようにして調製した手抄シートの厚さ及び裂断長
を、JIS P−8113に従って測定した。結果は表
1に示した通りである。 Preparation of hand-made paper Using the above enzyme-treated pulp as a raw material and using a round sheet machine, the basis weight is 40 g / m 2 according to JIS P-8209.
A handmade paper sheet was prepared. Measurement of thickness and bulk specific gravity of handmade paper sheet The thickness and tear length of the handmade sheet prepared as described above were measured according to JIS P-8113. The results are as shown in Table 1.
【0021】比較例1.セルラーゼを添加しないことの
他は、実施例1と全く同一の条件でパルプ処理を行い、
同様にして手抄紙を調製し、その評価を行った。評価の
結果を第1表に示す。Comparative Example 1. Pulp treatment was carried out under exactly the same conditions as in Example 1 except that cellulase was not added,
Similarly, handmade paper was prepared and evaluated. The results of evaluation are shown in Table 1.
【0022】実施例2.実施例1でセルラーゼアマノを
用いて実施したセルラーゼ処理の代わりにセルクラスト
(Novo社製の商品名)を用いて、以下の条件でセルラー
ゼ処理し、酵素処理パルプを得た。 パルプ濃度 3重量% 酵素(セルクラスト) 0.03ml/10
0ml pH 5.2 温度 60℃ 反応時間 1 時間 得られた酵素処理パルプを原料とし、実施例1と同様に
して手抄紙を調製し、その評価を行った。評価の結果を
第1表に示す。Example 2. Instead of the cellulase treatment performed with cellulase amano in Example 1, cellcrust (trade name manufactured by Novo Co.) was used for cellulase treatment under the following conditions to obtain an enzyme-treated pulp. Pulp concentration 3% by weight Enzyme (cell crust) 0.03 ml / 10
0 ml pH 5.2 Temperature 60 ° C. Reaction time 1 hour Using the enzyme-treated pulp obtained as a raw material, a handmade paper was prepared in the same manner as in Example 1 and evaluated. The results of evaluation are shown in Table 1.
【0023】比較例2.セルラーゼを添加しないことの
他は、実施例2と全く同一の条件によりパルプ処理を行
い、同様にして手抄紙を調製し、その評価を行った。評
価の結果を第1表に示す。Comparative Example 2. Pulp treatment was carried out under exactly the same conditions as in Example 2 except that cellulase was not added, and handmade paper was prepared and evaluated in the same manner. The results of evaluation are shown in Table 1.
【0024】実施例3.酸素漂白パルプ(日本製紙株式
会社製)を、以下の条件でキシラナーゼ処理(新日本化
学工業株式会社製の商品名:スミザイム)し、酵素処理
パルプを得た。 パルプ濃度 3重量% 酵素(スミザイム) 0.015重量% pH 6.3 温度 45℃ 反応時間 2時間 得られた酵素処理パルプを、実施例1と同様に手抄紙を
調製し、その評価を行った。評価結果を第1表に示す。Example 3. Oxygen bleached pulp (manufactured by Nippon Paper Industries Co., Ltd.) was treated with xylanase (trade name: Sumizyme manufactured by Shin Nippon Chemical Industry Co., Ltd.) under the following conditions to obtain an enzyme-treated pulp. Pulp concentration 3% by weight Enzyme (Sumizyme) 0.015% by weight pH 6.3 Temperature 45 ° C. Reaction time 2 hours Using the obtained enzyme-treated pulp, hand paper was prepared in the same manner as in Example 1 and evaluated. . The evaluation results are shown in Table 1.
【0025】比較例3.キシラナーゼを添加しないこと
の他は、実施例3と全く同一の処理を行い、同様にして
手抄紙を調製し、その評価を行った。評価の結果を第1
表に示す。Comparative Example 3. Except that xylanase was not added, the same treatments as in Example 3 were carried out, and handmade papers were prepared in the same manner and evaluated. First evaluation result
Shown in the table.
【0026】実施例4.酸素漂白パルプ(日本製紙株式
会社製)を、ファネロケーテ・クリソスポリウム(Phan
erocheate chrysosporium )を用いて、以下の条件で処
理し、微生物処理パルプを得た後、実施例1と同様にし
て手抄紙を調整し、その評価を行った。評価の結果を第
1表に示す。 パルプ濃度 15重量% 菌体接種量 5重量% pH 6.5 温度 40℃ 反応時間 10日Example 4. Oxygen bleached pulp (manufactured by Nippon Paper Industries Co., Ltd.)
erocheate chrysosporium) was treated under the following conditions to obtain a microbial-treated pulp, and then handmade papers were prepared and evaluated in the same manner as in Example 1. The results of evaluation are shown in Table 1. Pulp concentration 15% by weight Cell inoculum 5% by weight pH 6.5 Temperature 40 ° C Reaction time 10 days
【0027】比較例4.微生物を用いなかった他は実施
例4と全く同一の処理を行い、同様にして手抄紙を調製
し、その評価を行った。評価の結果を第1表に示す。Comparative Example 4. The same treatment as in Example 4 was carried out except that no microorganism was used, and handmade papers were prepared and evaluated in the same manner. The results of evaluation are shown in Table 1.
【0028】実施例5.酸素漂白パルプ(日本製紙株式
会社製)を、ファネロケーテ・クリソスポリウム(Phan
erocheate chrysosporium )を用いて、以下の条件で処
理し、微生物処理パルプを得た後、実施例1と同様にし
て手抄紙を調整し、その評価を行った。評価結果を表1
に示す。 パルプ濃度 15重量% 菌体培養液 5重量% セルラ−ゼ 0.05重量% pH 6.0 温度 50℃ 反応時間 1時間Example 5. Oxygen bleached pulp (manufactured by Nippon Paper Industries Co., Ltd.) was mixed with Phanelocete chrysosporium (Phan
erocheate chrysosporium) was treated under the following conditions to obtain a microbial-treated pulp, and then handmade papers were prepared and evaluated in the same manner as in Example 1. Table 1 shows the evaluation results
Shown in. Pulp concentration 15% by weight Cell culture solution 5% by weight Cellulase 0.05% by weight pH 6.0 Temperature 50 ° C Reaction time 1 hour
【0029】比較例5.微生物を添加しないことの他
は、実施例5と全く同一の処理を行い、同様にして手抄
紙を調整し、その評価を行った。評価の結果を第1表に
示す。Comparative Example 5. Except that no microorganism was added, the same treatment as in Example 5 was carried out, and handmade papers were prepared and evaluated in the same manner. The results of evaluation are shown in Table 1.
【表1】 表1に示した結果から明らかなごとく、本発明の実施に
より得られた紙は、顕著にその嵩高性が改善されている
ことが明らかである。[Table 1] As is clear from the results shown in Table 1, it is clear that the paper obtained by the practice of the present invention has significantly improved bulkiness.
Claims (2)
生産する微生物により処理された酵素処理パルプを原料
として製造されてなることを特徴とする嵩高紙。1. A bulky paper produced by using, as a raw material, an enzyme-treated pulp treated with an enzyme that decomposes a polysaccharide and / or a microorganism that produces the enzyme.
ある請求項1に記載の嵩高紙。2. The bulky paper according to claim 1, wherein the enzyme is cellulase or hemicellulase.