JPH0735498B2 - Adhesive tape or sheet - Google Patents
Adhesive tape or sheetInfo
- Publication number
- JPH0735498B2 JPH0735498B2 JP61008706A JP870686A JPH0735498B2 JP H0735498 B2 JPH0735498 B2 JP H0735498B2 JP 61008706 A JP61008706 A JP 61008706A JP 870686 A JP870686 A JP 870686A JP H0735498 B2 JPH0735498 B2 JP H0735498B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sheet
- adhesive tape
- sensitive adhesive
- release agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、多孔性基材からなる粘着テープ又はシートに
関するものである。さらに詳しくは、ロール状に捲回し
ても巻き戻し性に優れ、またテープ又はシートの重ね貼
りが可能な粘着テープ又はシートを提供するものであ
る。The present invention relates to an adhesive tape or sheet made of a porous substrate. More specifically, the present invention provides an adhesive tape or sheet that has excellent rewindability even when wound in a roll shape, and that can be overlaid with a tape or sheet.
支持体の一面に粘着剤層を設けて、ロール状に捲回して
なる粘着テープ又はシートは多数知られており、包装、
マスキング、接合等に汎用されている。A number of pressure-sensitive adhesive tapes or sheets obtained by providing a pressure-sensitive adhesive layer on one surface of a support and winding the roll are known, and packaging,
It is commonly used for masking and joining.
当該粘着テープ又はシートにおいて、紙、織布等の多孔
性基材を支持体に使用する場合、通常基材の少なくとも
一面にポリエチレン等のラミネート材が目止め層として
設けられており、さらに必要に応じて離型剤層が積層さ
れている。この場合、ロール状に捲回しても良好な巻き
戻し性を得るために、JIS Z 0237に規定されている背面
に対する180度引きはがし粘着力が20gf/10mm未満になる
ように粘着剤及び、離型剤が選ばれている。この種の粘
着テープ又はシートは、ロール状に捲回しても巻き戻し
性は優れるものの、重ね貼りができない問題がある。In the adhesive tape or sheet, when a porous base material such as paper or woven cloth is used as a support, a laminate material such as polyethylene is usually provided as a sealing layer on at least one surface of the base material, and it is further necessary. Accordingly, the release agent layer is laminated. In this case, in order to obtain a good rewinding property even when wound in a roll shape, a 180 ° peeling adhesive force to the back surface specified in JIS Z 0237 and an adhesive agent so that the adhesive force is less than 20 gf / 10 mm, and a release A mold is selected. Although this type of pressure-sensitive adhesive tape or sheet has excellent rewindability even when wound in a roll, it has a problem that it cannot be overlaid.
かかる問題を解決するために、離型剤層を設けないで、
かつアクリル系粘着剤を使用した粘着テープ又はシート
が公知である。In order to solve such a problem, without providing a release agent layer,
Moreover, an adhesive tape or sheet using an acrylic adhesive is known.
しかしながら、この種の粘着テープ又はシートは、その
粘着剤層の主成分がアクリル酸エステルの場合には、ロ
ール状に捲回しても優れた巻き戻し性を有するものの、
天然及び/又は合成ゴムを主成分とする粘着剤に対して
は、ラミネート材が基材から剥れたり、基材が層間破壊
してしまい、テープ又はシートの機能を満たさないのが
実情である。これは、一般にアクリル酸エステルを主成
分とする粘着剤は、ポリエチレン等のラミネート材に対
し難接着性を有するため離型剤層がなくても巻き戻すこ
とができるのに対して、天然及び/又は合成ゴムを主成
分とする粘着剤は、柔らかく、流動性に富み、接着面積
が広くなるため巻き戻し力がラミネート材の接着強度又
は基材の層間強度以上に大きくなるためである。However, this type of pressure-sensitive adhesive tape or sheet has an excellent rewinding property even when wound in a roll when the main component of the pressure-sensitive adhesive layer is an acrylic ester,
With respect to adhesives containing natural and / or synthetic rubber as a main component, the laminate material may be peeled from the base material or the base material may be interlaminarly broken, so that the function of the tape or sheet is not satisfied. . This is because the pressure-sensitive adhesive containing an acrylic ester as a main component generally has a poor adhesion property to a laminate material such as polyethylene and thus can be rewound without a release agent layer. Alternatively, the pressure-sensitive adhesive containing synthetic rubber as a main component is soft and rich in fluidity and has a wide adhesive area, so that the unwinding force becomes larger than the adhesive strength of the laminate material or the interlaminar strength of the base material.
さらに、アクリル酸エステルを主成分とする粘着材は、
低温時の初期タックが弱く、またコストも高いので使用
するテープ又はシートに制限がある等の問題がある。Furthermore, the adhesive material mainly composed of acrylic acid ester is
Since the initial tack at low temperature is weak and the cost is high, there is a problem that the tape or sheet used is limited.
本発明の目的は、多孔性基材を支持体に使用し、粘着剤
層の主成分が天然及び/又は合成ゴムである場合でも、
優れた巻き戻し性を有し、しかも、重ね貼りができる粘
着テープ又はシートを提供するものである。An object of the present invention is to use a porous substrate as a support and even when the main component of the pressure-sensitive adhesive layer is natural and / or synthetic rubber,
It is intended to provide an adhesive tape or sheet which has excellent rewinding property and can be overlaid.
本発明者等は、かかる問題点を解決するために鋭意検討
した結果、基材の一面に、以下に規定する如くメルトイ
ンデックス(以下、MIと略記)と密度の異なる二種類の
ラミネート材及び離型剤を一定の順序で積層し、他面に
粘着剤層を設けた構造とした粘着テープ又はシートは、
ロール状に捲回されても良好な巻き戻し性を有し、しか
も、重ね貼りができることを知見し、本発明に至ったも
のである。The inventors of the present invention have made extensive studies in order to solve such problems, and as a result, on one surface of the substrate, two kinds of laminate materials having different melt indexes (hereinafter, abbreviated as MI) and densities as defined below and separating An adhesive tape or sheet having a structure in which molds are laminated in a certain order and an adhesive layer is provided on the other surface is
The present invention has been made based on the finding that it has a good rewinding property even when wound in a roll shape, and that it can be overlaid.
即ち、本発明は、多孔性基材の一面に粘着剤層が設けら
れ、他面に、ASTM D−1238に規定されているメルトイ
ンデックスが15dg/分より大きく、かつASTM D−1505
に規定されている密度が0.93g/cm3未満のラミネート材
(a)及び、当該メルトインデックスが15dg/分以下、
かつ当該密度が0.93g/cm3以上であるラミネート材
(b)及び、離型剤(c)が、基材−ラミネート材
(a)−ラミネート材(b)−離型剤(c)の順序に積
層されてなることを特徴とする粘着テープ又はシートを
提供するものである。That is, in the present invention, a pressure-sensitive adhesive layer is provided on one surface of a porous substrate, and the melt index defined in ASTM D-1238 is larger than 15 dg / min and ASTM D-1505 is provided on the other surface.
Laminated material (a) whose density is less than 0.93 g / cm 3 and its melt index is 15 dg / min or less,
A laminate material (b) having a density of 0.93 g / cm 3 or more and a release agent (c) are in the order of base material-laminate material (a) -laminate material (b) -release agent (c). The present invention provides an adhesive tape or sheet, which is characterized in that the adhesive tape or sheet is laminated.
本発明の実施に当たって用いられる多孔性基材は、従来
この分野で使用されているものであれば特に制限はな
く、たとえばクラフト紙、和紙等の紙類、織布、不織布
等の布類、多孔性プラスチックフィルム等の単体又は複
合体が挙げられる。The porous substrate used in the practice of the present invention is not particularly limited as long as it is conventionally used in this field, for example, paper such as kraft paper and Japanese paper, cloth such as woven cloth and non-woven cloth, and porous material. A simple substance or a composite of a flexible plastic film and the like can be mentioned.
本発明の実施に当たって用いられるラミネート材(a)
及びラミネート材(b)用の材料としては、通常ポリエ
チレン、ポリプロピレン等のポリアルキレン、当該ポリ
アルキレンとこれを共重合可能な単量体との共重合体
(たとえば、エチレン−酢酸ビニル共重合体、エチレン
−アクリル酸共重合体等)等の熱可塑性ポリマーが挙げ
られる。しかして、ラミネート材(a)としては、ASTM
D−1238に規定されているMIが15dg/分より大きく、
好ましくは18dg/分より大きく、さらに好ましくは20dg/
分より大きくかつASTM D−1505に規定されている密度
が0.93g/cm3未満のポリマー、好ましくは0.928g/cm3未
満のポリマーの一種類又は数種類の混合物が用いられ
る。一方、ラミネート材(b)には、当該MIが15dg/分
以下、好ましくは13dg/分以下、更に好ましくは11dg/分
以下かつ当該密度が0.93g/cm3以上であるポリマー、好
ましくは0.935g/cm3以上であるポリマーの一種類又は数
種類の混合物が用いられる。なお、本発明に用いられる
ラミネート材は、必要に応じて、顔料、安定剤、充填
剤、滑剤、架橋剤、ブロッキング防止剤等を含んでいて
もよい。Laminate material (a) used for carrying out the present invention
As the material for the laminate material (b), polyalkylene such as polyethylene or polypropylene is usually used, and a copolymer of the polyalkylene and a monomer capable of copolymerizing the polyalkylene (for example, ethylene-vinyl acetate copolymer, Thermoplastic polymers such as ethylene-acrylic acid copolymer). As a laminate material (a), ASTM
MI specified in D-1238 is larger than 15 dg / min,
Preferably greater than 18 dg / min, more preferably 20 dg / min
Min from large and ASTM D-1505 to a defined by that density of 0.93 g / cm 3 less than the polymer, preferably one kind or several kinds of mixture of 0.928 g / cm 3 less than the polymer is used. On the other hand, in the laminate material (b), the MI is 15 dg / min or less, preferably 13 dg / min or less, more preferably 11 dg / min or less and the density is 0.93 g / cm 3 or more, preferably 0.935 g. A single polymer or a mixture of several polymers having a density of not less than / cm 3 is used. The laminating material used in the present invention may contain a pigment, a stabilizer, a filler, a lubricant, a cross-linking agent, an antiblocking agent, etc., if necessary.
本発明の粘着テープ又はシートにおいては、基材−ラミ
ネート材(a)−ラミネート材(b)の順序に各層が積
層されていることが必要である。この順序が逆になる
と、基材とラミネート材との密着性が悪くなり、良好な
巻き戻し性が得られなくなるほか、ラミネート材表面が
凹凸になるため均一な離型剤層を設けることが困難にな
る。In the pressure-sensitive adhesive tape or sheet of the present invention, it is necessary that each layer is laminated in the order of base material-laminate material (a) -laminate material (b). If this order is reversed, the adhesion between the base material and the laminating material will deteriorate, and good rewindability will not be obtained, and it will be difficult to provide a uniform release agent layer because the surface of the laminating material will be uneven. become.
本発明の実施に当たって用いられる離型剤は、特に制限
されるものではなく、当該分野で使用されるものであれ
ば好適に使用しうる。かかるものの具体例としては、た
とえば長鎖アルキル基含有化合物、シリコーン系化合
物、フッ素系化合物等が挙げられる。The release agent used in the practice of the present invention is not particularly limited, and any release agent used in the art can be preferably used. Specific examples of such compounds include long chain alkyl group-containing compounds, silicone compounds, fluorine compounds and the like.
また、粘着剤層に使用される接着剤は特に限定されるも
のではなく、従来既知の粘着剤、例えば天然及び/又は
合成ゴムを主成分とする粘着剤、アクリル系粘着剤等が
例示される。特に、本発明においては柔らかく流動性に
富む天然及び/又は合成ゴムが主成分である粘着剤を用
いた場合においても、優れた巻き戻し性が得られ、且つ
良好に重ね貼りができるので、本発明の効果がより顕著
に発揮される。The adhesive used for the pressure-sensitive adhesive layer is not particularly limited, and conventionally known pressure-sensitive adhesives, for example, pressure-sensitive adhesives containing natural and / or synthetic rubber as a main component, acrylic pressure-sensitive adhesives, etc. are exemplified. . In particular, in the present invention, even when a pressure-sensitive adhesive containing a soft and fluid natural and / or synthetic rubber as a main component is used, excellent rewinding property can be obtained, and good lamination can be performed. The effects of the invention are more significantly exhibited.
ところで、当該離型剤と当該粘着剤との材料の組み合わ
せ方は特に限定されるものではないが、JIS Z 0237に規
定されているテープ又はシートの背面に対する180度引
きはがし粘着力が20gf/10mm以上、300gf/10mm以下、好
ましくは40gf/10mm以上、200gf/10mm以下になる組み合
わせ方が好ましい。同該粘着力が20gf/10mm未満の場合
は、十分な重ね貼り性が得られない。また、同該粘着力
が300gf/10mmよりも大きい場合は、ロール状に捲回され
たテープ又はシートを巻き戻した時に、多孔性基材が層
間破壊するため良好な巻き戻し性が得られないので好ま
しくない。上記の組み合わせの具体例としては、たとえ
ば次の如きものが例示される: 天然及び/又は合成ゴムが主成分である粘着剤の場合、
ポリビニルオクタデシルカルバメイト系、ポリエチレン
イミンオクタデシルカルバメイト系等の長鎖アルキル化
合物、フェニル変性系、シリコーンレジン含有系等のシ
リコーン系化合物の中から選ばれた離型剤が組み合わせ
られる。By the way, the method of combining the materials of the release agent and the pressure-sensitive adhesive is not particularly limited, but the 180 ° peeling adhesive force to the back surface of the tape or sheet specified in JIS Z 0237 is 20 gf / 10 mm. As described above, a combination method of 300 gf / 10 mm or less, preferably 40 gf / 10 mm or more and 200 gf / 10 mm or less is preferable. When the adhesive strength is less than 20 gf / 10 mm, sufficient lapability cannot be obtained. Further, when the adhesive strength is more than 300 gf / 10 mm, when the tape or sheet wound into a roll is unwound, the porous base material causes interlayer breakage, and good unwinding property cannot be obtained. It is not preferable. Specific examples of the above combination include, for example, the following: In the case of an adhesive containing natural and / or synthetic rubber as a main component,
A release agent selected from long-chain alkyl compounds such as polyvinyl octadecylcarbamate type and polyethyleneimine octadecylcarbamate type, silicone compounds such as phenyl modified type and silicone resin-containing type is combined.
本発明の粘着テープ又はシートは、通常、紙管、合成樹
脂管等に粘着剤層を内側にしてロール状に捲回して使用
に供される。The pressure-sensitive adhesive tape or sheet of the present invention is usually wound around a paper tube, a synthetic resin tube, or the like with the pressure-sensitive adhesive layer inside and used in a roll.
MIと密度の異なる二種類のラミネート材(a)および
(b)ならびに、離型剤を一定の順序で積層することに
よる作用は次の通りである。即ち、MIが15dg/分より大
きく、かつ密度が0.93g/cm3未満のラミネート材(a)
は、流動性に富むため、多孔性基材と堅固に密着する。
又、MIが15dg/分以下、かつ密度が0.93g/cm3以上である
ラミネート材(b)は、耐熱性に富み表面が凹凸になり
にくいため、均一な離型剤層を設けることができる。両
者の相乗作用により良好な巻き戻し性が得られると思わ
れる。The effects of laminating two types of laminating materials (a) and (b) having different densities from MI and a release agent in a fixed order are as follows. That is, a laminated material (a) having an MI of more than 15 dg / min and a density of less than 0.93 g / cm 3.
Has high fluidity, and therefore firmly adheres to the porous substrate.
Further, the laminate material (b) having an MI of 15 dg / min or less and a density of 0.93 g / cm 3 or more is rich in heat resistance and the surface is less likely to be uneven, so that a uniform release agent layer can be provided. . It is considered that good unwinding property can be obtained by the synergistic action of both.
従って、本発明によれば、粘着剤層の主成分が天然及び
/又は合成ゴムである場合でも、優れた巻き戻し性を有
する粘着テープ又はシートを得ることができる。特に、
本発明の粘着テープ又はシートにおいて、背面に対する
180度引きはがし粘着力が20gf/10mm以上、300gf/10mm以
下に設定することによって、極めて良好な重ね貼り性を
有する新規な粘着テープ又はシートを提供することがで
きる。Therefore, according to the present invention, even when the main component of the pressure-sensitive adhesive layer is natural and / or synthetic rubber, a pressure-sensitive adhesive tape or sheet having excellent rewinding property can be obtained. In particular,
In the adhesive tape or sheet of the present invention,
By setting the 180-degree peeling adhesive strength to 20 gf / 10 mm or more and 300 gf / 10 mm or less, it is possible to provide a novel adhesive tape or sheet having extremely good layering properties.
本発明の粘着テープ又はシートを以下に実施例をもって
具体的に説明するとともに、本発明の粘着テープ又はシ
ートが優れた巻き戻し性及び、良好な重ね貼り性を有す
る事実を、以下の実験例により明らかにする。The pressure-sensitive adhesive tape or sheet of the present invention will be specifically described with reference to Examples below, and the fact that the pressure-sensitive adhesive tape or sheet of the present invention has excellent rewinding property and good lapability can be described by the following experimental examples. Make it clear.
本発明はこの実施例に限られるものではない。なお、文
中、部とあるのは重量部を意味する。The invention is not limited to this embodiment. In the text, “part” means “part by weight”.
実施例1 ASTM D−1238に規定されているMIが20dg/分、ASTM
D−1505に規定されている密度が0.916g/cm3の低密度ポ
リエチレンと、当該MIが7dg/分、当該密度が0.944g/cm3
の高密度ポリエチレンを、坪量73g/m2のクラフト紙にク
ラフト紙−低密度ポリエチレン−高密度ポリエチレンの
順序で各8μmの厚さにラミネートした支持体を作製す
る。この支持体のラミネート層上に、ポリビニルオクタ
デシルカルバメイト系離型剤を固形分重量で0.08g/m2塗
布する。Example 1 MI specified in ASTM D-1238 is 20 dg / min, ASTM
Low density polyethylene with a density of 0.916 g / cm 3 specified in D-1505, MI of 7 dg / min, and a density of 0.944 g / cm 3
The high-density polyethylene of 1. is laminated on kraft paper having a basis weight of 73 g / m 2 in the order of kraft paper-low density polyethylene-high density polyethylene to a thickness of 8 μm to prepare a support. On the laminate layer of this support, a polyvinyl octadecylcarbamate type release agent is applied at a solid content of 0.08 g / m 2 .
一方、スチレン−イソプレン−スチレンブロック共重合
体100部、石油系粘着付与樹脂100部、液状軟化剤20部、
老化防止剤1部を加圧ニーダーで混練した粘着剤を用意
する。On the other hand, styrene-isoprene-styrene block copolymer 100 parts, petroleum-based tackifying resin 100 parts, liquid softener 20 parts,
An adhesive is prepared by kneading 1 part of the antioxidant with a pressure kneader.
次に、前記支持体に、固形分重量で45g/m2の粘着剤を溶
融押出塗工し、ロール状に捲回した粘着テープを得る。Next, a pressure-sensitive adhesive having a solid content of 45 g / m 2 is melt-extruded on the support to obtain a pressure-sensitive adhesive tape wound in a roll shape.
比較例1 実施例1で使用したラミネート材をクラフト紙−高密度
ポリエチレン−低密度ポリエチレンの順序にラミネート
した以外は、実施例1と同様にして粘着テープを得る。Comparative Example 1 An adhesive tape is obtained in the same manner as in Example 1 except that the laminating material used in Example 1 is laminated in the order of kraft paper-high density polyethylene-low density polyethylene.
比較例2 実施例1で離型剤を塗布しない以外は、実施例1と同様
にして粘着テープを得る。Comparative Example 2 An adhesive tape is obtained in the same manner as in Example 1 except that the release agent is not applied in Example 1.
実験例1 以上の実施例1及び比較例1〜2で得た粘着テープの巻
き戻し性、重ね貼り性を測定し、その結果を第1表に示
した。その測定方法は次の通りである。Experimental Example 1 The rewinding property and the re-adhesive property of the adhesive tapes obtained in the above Example 1 and Comparative Examples 1 and 2 were measured, and the results are shown in Table 1. The measuring method is as follows.
(巻き戻し性の測定方法) 粘着テープを40℃、25%相対湿度雰囲気下で約60m/分の
速度で巻き戻した時、基材からのラミネート層の剥れ状
態を測定する。(Measurement method of rewinding property) When the adhesive tape is rewound at a speed of about 60 m / min in an atmosphere of 40 ° C and 25% relative humidity, the peeling state of the laminate layer from the substrate is measured.
(重ね貼り性) JIS Z 0237に準じて、背面に対して180度引き剥がし、
接着力を測定する。(Overlapability) According to JIS Z 0237, peel off 180 degrees from the back,
Measure the adhesive strength.
実施例2 ASTM D−1238に規定されているMIが22dg/分、ASTM
D−1505に規定されている密度が0.926g/cm3の低密度ポ
リエチレンと、当該MIが15dg/分、当該密度が0.935g/cm
3の高密度ポリエチレンを、坪量73g/m2のクラフト紙に
クラフト紙−低密度ポリエチレン−高密度ポリエチレン
の順序で各6μmの厚さにラミネートした支持体を作製
する。この支持体のラミネート層上に、無溶剤付加反応
型フェニル変性シリコーン系離型剤を固形分重量で0.6g
/m2塗布する。 Example 2 MI specified in ASTM D-1238 is 22 dg / min, ASTM
Low density polyethylene with a density of 0.926 g / cm 3 specified in D-1505, MI of 15 dg / min, and density of 0.935 g / cm
A high density polyethylene of 3 is laminated on kraft paper having a basis weight of 73 g / m 2 in the order of kraft paper-low density polyethylene-high density polyethylene to a thickness of 6 μm to prepare a support. On the laminate layer of this support, a solvent-free addition reaction type phenyl-modified silicone release agent was added in an amount of 0.6 g in terms of solid content.
Apply / m 2
一方、天然ゴム100部、石油系粘着付与樹脂100部、液状
軟化剤30部、老化防止剤0.5部をトルエンに溶解した粘
着剤を用意する。On the other hand, an adhesive prepared by dissolving 100 parts of natural rubber, 100 parts of petroleum-based tackifying resin, 30 parts of a liquid softening agent and 0.5 part of an antioxidant in toluene is prepared.
次に、前記支持体に、乾燥後の厚みが30μmとなるよう
に当該粘着剤を塗布乾燥し、ロール状に捲回した粘着テ
ープを得る。Next, the pressure-sensitive adhesive is applied to the support so as to have a dried thickness of 30 μm and dried to obtain a pressure-sensitive adhesive tape wound into a roll.
比較例3 実施例2で使用したラミネート材をクラフト紙−高密度
ポリエチレン−低密度ポリエチレンの順序にラミネート
した以外は、実施例2と同様にして粘着テープを得る。Comparative Example 3 An adhesive tape is obtained in the same manner as in Example 2 except that the laminating material used in Example 2 is laminated in the order of kraft paper-high density polyethylene-low density polyethylene.
比較例4 実施例2で離型剤を塗布しない以外は、実施例2と同様
にして粘着テープを得る。Comparative Example 4 An adhesive tape is obtained in the same manner as in Example 2 except that the release agent is not applied in Example 2.
実験例2 以上の実施例2及び比較例3〜4で得た粘着テープの巻
き戻し性、重ね貼り性を測定し、その結果を第2表に示
した。なお、測定方法は実験例1と同様である。Experimental Example 2 The rewinding property and the re-adhesive property of the adhesive tapes obtained in the above Example 2 and Comparative Examples 3 to 4 were measured, and the results are shown in Table 2. The measuring method is the same as in Experimental Example 1.
以上の実施例からも明らかなように、多孔性基材の一面
に、MIが15dg/分より大きく、かつ密度が0.93g/cm3未満
のラミネート材(a)及び、MIが15dg/分以下、かつ密
度が0.93g/cm3以上であるラミネート材(b)および、
離型剤(c)が、基材−ラミネート材(a)−ラミネー
ト材(b)−離型材(c)の順序に積層した時に初めて
本発明に特有の効果が得られる。 As is clear from the above examples, the laminated material (a) having an MI of more than 15 dg / min and a density of less than 0.93 g / cm 3 and the MI of 15 dg / min or less on one surface of the porous substrate. And a laminate material (b) having a density of 0.93 g / cm 3 or more, and
Only when the release agent (c) is laminated in the order of base material-laminate material (a) -laminate material (b) -release material (c), the effect peculiar to the present invention can be obtained.
Claims (3)
他面に、ASTM D−1238に規定されているメルトインデ
ックスが15dg/分より大きく、かつASTM D−1505に規
定されている密度が0.93g/cm3未満のラミネート材
(a)及び、当該メルトインデックスが15dg/分以下、
かつ当該密度が0.93g/cm3以上であるラミネート材
(b)及び、離型剤(c)が、基材−ラミネート材
(a)−ラミネート材(b)−離型剤(c)の順序に積
層されてなることを特徴とする粘着テープ又はシート。1. A pressure-sensitive adhesive layer is provided on one surface of a porous substrate,
On the other side, a laminate material (a) having a melt index specified by ASTM D-1238 of more than 15 dg / min and a density specified by ASTM D-1505 of less than 0.93 g / cm 3 and the melt Index is less than 15dg / min,
A laminate material (b) having a density of 0.93 g / cm 3 or more and a release agent (c) are in the order of base material-laminate material (a) -laminate material (b) -release agent (c). An adhesive tape or sheet characterized by being laminated on.
ムである特許請求の範囲第(1)項記載の粘着テープ又
はシート。2. The pressure-sensitive adhesive tape or sheet according to claim 1, wherein the main component of the pressure-sensitive adhesive layer is natural and / or synthetic rubber.
JIS Z 0237に規定されているテープ又はシートの背面に
対する180度引きはがし粘着力が20gf/10mm以上、300gf/
10mm以下となるような組み合わせである特許請求の範囲
第(1)項または第(2)項記載の粘着テープ又はシー
ト。3. A combination of materials of a release agent and a pressure-sensitive adhesive,
180 degree peeling adhesion to the back surface of the tape or sheet specified in JIS Z 0237 has an adhesive force of 20gf / 10mm or more, 300gf /
The adhesive tape or sheet according to claim (1) or (2), which is a combination of 10 mm or less.