JPH07319127A - Case for film-integrated camera and its manufacture - Google Patents
Case for film-integrated camera and its manufactureInfo
- Publication number
- JPH07319127A JPH07319127A JP13079094A JP13079094A JPH07319127A JP H07319127 A JPH07319127 A JP H07319127A JP 13079094 A JP13079094 A JP 13079094A JP 13079094 A JP13079094 A JP 13079094A JP H07319127 A JPH07319127 A JP H07319127A
- Authority
- JP
- Japan
- Prior art keywords
- case
- film
- integrated camera
- main body
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はフィルム一体型カメラの
ケース及びその製造方法に関し、更に詳しくは、安価で
簡単で、リサイクル、リユースが容易なフィルム一体型
カメラに用いられるケース及びその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a case for a film-integrated camera and a method for manufacturing the same, and more particularly to a case for a film-integrated camera which is inexpensive, simple, and easy to recycle and reuse, and a method for manufacturing the same. .
【０００２】[0002]
【従来の技術】近時、簡単なプラスチック製ケースを用
いたカメラにフィルムを装填した状態で販売されるフィ
ルム一体型カメラが普及してきている。このカメラは、
通常のカメラにフィルムを装填する煩わしさがなく、
又、装填ミスもないこと及び、旅行等に重いカメラを携
帯する必要もなく、行く先々でも容易に入手して使用し
得る簡便性も備えていることから、一般の人に写真撮影
を容易ならしめている。ここに用いられるフィルム一体
型のカメラの構造は特開平４−３４８３４０号公報ある
いは特開平４−３４７８２７号公報に記載されているよ
うに、カメラの主要部を構成するレンズ、シャッターか
らなる光学ユニットやストロボユニット並びにシャッタ
ーボタン、巻上機構、フィルム室、巻取室及びフィルム
等を有する本体ユニットを、プラスチックケースの中に
収容したもので、このプラスチックケースはカメラの主
機構を装填した本体ケースとフィルムにレンズを介して
撮影時露光するためのレンズ開放部及びファインダーを
備えた前部ケースと後部を密閉する後部ケースとからな
り、それらはいずれもプラスチック成型体で嵌合により
一体化できるようになっている。そして実際にはその周
囲は包装紙で包まれてなるものである。このようなカメ
ラを使用して撮影後は使用者はフィルムを取出さずにそ
のまゝ現像焼付店へ持参し、現像焼付を行ない、カメラ
は再度使用することなく廃棄されていた。2. Description of the Related Art Recently, a film-integrated camera which is sold with a film loaded in a camera using a simple plastic case has become widespread. This camera is
Without the hassle of loading film into a normal camera,
Also, because there is no mistake in loading and it is not necessary to carry a heavy camera for traveling, etc., and it is easy to obtain and use everywhere you go, making it easy for ordinary people to take pictures. It is tight. The structure of the film-integrated camera used here is, as described in JP-A-4-348340 or JP-A-4-347827, an optical unit including a lens and a shutter constituting a main part of the camera, A flash unit, a shutter button, a hoisting mechanism, a film chamber, a take-up chamber, a main unit having a film, and the like are housed in a plastic case. The plastic case is a main case with a main mechanism of the camera and a film. It consists of a front case equipped with a lens opening and a finder for exposure during shooting through the lens, and a rear case that seals the rear, both of which can be integrated by fitting with a molded plastic body. ing. In reality, the surrounding area is wrapped with wrapping paper. After taking a picture with such a camera, the user brought the film to the developing and printing shop without taking it out, performed the developing and printing, and the camera was discarded without being used again.
【０００３】[0003]
【発明が解決しようとする課題】このようなフィルム一
体型カメラではいわゆる使い切りであるために、１画面
当りの価格が高価であり、レンズ交換できないために作
画性が不十分で、しかも使用時のフィルム一体型カメラ
がプラスチックや金属の複合材料からなっているため再
生使用が困難で、廃棄物とした場合燃焼し難く、環境へ
の影響も大きいという問題があった。本発明はこのよう
な問題点を解決することを目的とするものである。この
問題点を解決するために特開平４−３４７８２７号に於
ては、光学ユニットと本体ユニットとを着脱可能にした
り、本体ユニットはフィルム以外はすべてプラスチック
としたり、撮影後フィルムを抜き取り、光学ユニットと
本体ユニットとを分離し、光学ユニットを未使用の本体
ユニットに結合してフィルム一体型カメラを製造すると
いうことが提案されている。しかしながらこの提案によ
ってもカメラケースは本体部ケースと前部ケース、後部
ケースいずれもプラスチックケースの組合せからなるも
ので、本体部ケース部分を再利用するとしてもプラスチ
ックの廃棄物が多量に発生し、地中分解することなく、
且つ燃焼カロリーも高いことから焼却炉を傷める等問題
があり、更に改良が求められている。Since such a film-integrated type camera is so-called used up, the price per screen is expensive, and because the lens cannot be replaced, the image drawing property is insufficient, and at the time of use. Since the film-integrated camera is made of a plastic or metal composite material, it is difficult to recycle it, and it is difficult to burn it as a waste, and it has a large impact on the environment. The present invention aims to solve such problems. In order to solve this problem, in JP-A-4-347827, the optical unit and the main body unit are made detachable, the main body unit is made of plastic except for the film, and the film is taken out after photographing to make the optical unit It has been proposed to separate the main body unit and the main body unit, and couple the optical unit to an unused main body unit to manufacture a film-integrated camera. However, even with this proposal, the camera case consists of a combination of a main body case, a front case, and a rear case, and even if the main body case is reused, a large amount of plastic waste is generated, and Without decomposing inside
Moreover, since the calories burned are high, there are problems such as damage to the incinerator, and further improvement is required.
【０００４】[0004]
【課題を解決するための手段】本発明は上記の状況に鑑
みなされたもので、光学ユニットや本体ボディーを装着
した本体部ケース部分はそのまゝフィルムを入れ替える
だけで再利用することとし、廃棄される前部ケース、後
部ケースを可燃性でしかも低カロリーで燃焼するか、バ
クテリヤで分解し易い紙パルプを主体としたものであ
る。すなわち本発明の概略は以下に記すとおりである。 （１）撮影レンズ及びシャッター等の撮影機構を備え、
かつ未露光のフィルムを収納した本体ユニットを内蔵す
るフィルム一体型カメラに於いて、前部ケース及び後部
ケースは広葉樹クラフトパルプを主成分とする坪量５０
〜１０００ｇ／ｍ2 のシート状パルプ基材に熱硬化性樹
脂を１０〜３０重量％含浸してなる樹脂含浸紙による成
形ケースとしたことを特徴とするフィルム一体型カメラ
のケース。 （２）撮影レンズ及びシャッター等の撮影機構を備え、
かつ未露光のフィルムを収納した本体ユニットを内蔵す
るフィルム一体型カメラに於いて、前部ケース及び後部
ケースとして広葉樹クラフトパルプを主成分とするシー
ト状のパルプ基材に熱硬化性樹脂のプリポリマーを１０
〜３０重量％含浸後、加熱乾燥してプリプレグを作成
し、しかる後、所定の前部ケース及び後部ケースの形状
に成形した後加熱硬化するかもしくは成形しながら樹脂
を加熱硬化させるフィルム一体型カメラのケースの製造
方法。 （３）撮影レンズ及びシャッター等の撮影機構を備え、
かつ未露光のフィルムを収納した本体ユニットを内蔵す
るフィルム一体型カメラに於いて、前部ケース及び後部
ケースとして広葉樹クラフトパルプを主成分とするシー
ト状のパルプ基材に熱硬化性樹脂のプリポリマーを１０
〜３０重量％含浸後、加熱乾燥してプリプレグを作成
し、しかる後、所定の前部ケース及び後部ケースの形状
に成形しながら樹脂を加熱硬化させるフィルム一体型カ
メラのケースの製造方法。上記のようにすることにより
カメラの本体部分は従来と全く同様な構成で、前部と後
部のケースは紙質でフィルムさえ入れかえれば再使用が
可能であり、かつ前部ケースと後部ケースは主として広
葉樹クラフトパルプを主成分とするものであるから、廃
棄後分解もしくは燃焼し易いものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and the main body case portion on which the optical unit and the main body body are mounted can be reused by simply replacing the film, and then discarded. The front case and the rear case are mainly made of paper pulp which is flammable and burns with low calorie or is easily decomposed by bacteria. That is, the outline of the present invention is as described below. (1) Equipped with a photographing mechanism such as a photographing lens and a shutter,
Also, in a film-integrated camera having a built-in main body unit containing unexposed film, the front case and the rear case have a basis weight of hardwood kraft pulp as a main component.
A film-integrated camera case, characterized by being a molded case made of resin-impregnated paper obtained by impregnating a sheet-like pulp base material of up to 1000 g / m 2 with a thermosetting resin in an amount of 10 to 30% by weight. (2) Equipped with a photographing mechanism such as a photographing lens and a shutter,
Also, in a film-integrated camera that has a built-in main unit that contains unexposed film, a thermosetting resin prepolymer is used as a front case and a rear case of a hardwood kraft pulp-based sheet-like pulp base material. 10
-30% by weight impregnation, heating and drying to create a prepreg, and then molding into predetermined front and rear case shapes followed by heat curing or heat curing of resin during molding, film-integrated camera Manufacturing method of case. (3) Equipped with a photographing mechanism such as a photographing lens and a shutter,
Also, in a film-integrated camera that has a built-in main unit that contains unexposed film, a thermosetting resin prepolymer is used as a front case and a rear case of a hardwood kraft pulp-based sheet-like pulp base material. 10
A method for manufacturing a case of a film-integrated camera, in which a resin is heat-cured while being impregnated with 30% by weight and then dried by heating to form a prepreg, and then being molded into a predetermined shape of a front case and a rear case. By doing the above, the camera body has the same configuration as the conventional one, the front and rear cases can be reused as long as the film is replaced with paper quality, and the front case and the rear case are mainly Since it is composed mainly of hardwood kraft pulp, it is easily decomposed or burned after disposal.
【０００５】いま本発明によるケースが適用されるフィ
ルム一体型カメラケースの構造を図面により説明する。
図１は内蔵される部分を省略して示したフィルム一体型
カメラの簡略分離斜視図で、その基本構造となる外部ケ
ースは、（Ａ）カメラの光学的ユニット、フィルム、そ
の他のユニットを内蔵したプラスチックケースと一体成
型された本体部ケース１と、（Ｂ）その前方で露光撮
影、ファインダー等を備えた前部ケース（表蓋）２及び
（Ｃ）裏側を密閉状態にする後部ケース３（裏蓋）より
なり、前後部のケースは本体部ケースに嵌着係止されて
一体に構成できるようになっている。（係止構造は省略
してある。） 図２は前記外部ケース（Ａ）、（Ｂ）及び（Ｃ）の表側
から見た組立斜視図であり、図１の本体部ケース１は図
２においては側面のみが露出された本体部ケース１’と
して構成され、その他は本発明による前部ケース２と後
部ケース３により覆われている。又図３は前記外部ケー
ス（Ａ）、（Ｂ）及び（Ｃ）の裏側から見た組立斜視図
である。この基本構造は従来のこの種カメラで採用され
ている構造であるが、従来技術によれば各ケースは、全
部同じプラスチック製としていたが、本発明では前部ケ
ースと後部ケースは主として広葉樹クラフトパルプを主
成分とするもので構成されている。なお、図示のものは
一例でこれに限定されるものではない。Now, the structure of a film-integrated type camera case to which the case according to the present invention is applied will be described with reference to the drawings.
FIG. 1 is a simplified perspective view of a film-integrated type camera in which the parts to be incorporated are omitted. The external case, which is the basic structure of the film-integrated type camera, includes (A) a camera optical unit, a film, and other units. A main body case 1 integrally molded with a plastic case, (B) a front case (front cover) 2 provided with a finder and the like for exposure photography in front of it, and (C) a rear case 3 (back side) for sealing the back side. The front and rear cases are fitted and locked to the main body case so that they can be integrally formed. (The locking structure is omitted.) FIG. 2 is an assembly perspective view of the outer cases (A), (B) and (C) as seen from the front side, and the main body case 1 of FIG. Is configured as a main body case 1 ′ whose side surface is exposed, and the others are covered by a front case 2 and a rear case 3 according to the present invention. FIG. 3 is an assembly perspective view of the outer cases (A), (B) and (C) as viewed from the back side. Although this basic structure is a structure adopted in a conventional camera of this type, according to the prior art, all the cases were made of the same plastic, but in the present invention, the front case and the rear case are mainly hardwood kraft pulp. It is composed of those whose main component is. It should be noted that the illustrated one is an example, and the present invention is not limited to this.
【０００６】本発明のケースが適用されるフィルム一体
型カメラは、この場合の中央の本体部は各種の撮影機構
を本体部ケースとともに一体化して作成するために、従
来どおりプラスチックのままとし、その前後部を構成す
るケースを広葉樹クラフトパルプを主成分とする坪量５
０〜１０００ｇ／ｍ2 のシート状パルプ基材に熱硬化性
樹脂を１０〜３０重量％含浸してなる樹脂含浸紙を用い
た成形ケースとするものである。従来のフィルム一体型
カメラでは、プラスチック成形体で本体部ケースを作成
し、前部ケース、後部ケースも同種のプラスチック成形
体からなるもので、これらは嵌着して一体として密封す
るようにしたものであった。本発明では前部ケースと後
部ケースとを広葉樹クラフトパルプに熱硬化性樹脂を含
浸硬化させたものとし、前記した本体部ケースと嵌着し
て一体化して販売し、使用後各部を分離し前部ケースと
後部ケースとは廃棄される。In the film-integrated type camera to which the case of the present invention is applied, the central main body portion in this case is made of plastic as in the prior art in order to integrally form various photographing mechanisms together with the main body case, and The cases that form the front and rear parts are made of hardwood kraft pulp.
The molded case uses a resin-impregnated paper obtained by impregnating a sheet-like pulp base material of 0 to 1000 g / m 2 with a thermosetting resin in an amount of 10 to 30% by weight. In a conventional film-integrated camera, the main body case is made of a plastic molded body, and the front case and the rear case are also made of the same kind of plastic molded body, and these are fitted and sealed as one body. Met. In the present invention, the front case and the rear case are hardwood kraft pulp impregnated and cured with a thermosetting resin, and are fitted and sold integrally with the main body case described above. The rear case and the rear case are discarded.
【０００７】本発明のケースが適用されるフィルム一体
型カメラに於て本体部ケースを従来通りプラスチック製
とした理由は、該部がカメラの光学ユニット、フィルム
その他のカメラの本質的機能を具備する部分を軽量しか
もコンパクトに一体成型された部分であるからこの部分
はそのまゝとすることにより、再利用する場合でも生産
工程や品質管理上従来と全く同じとして、問題の発生を
防止すると共に、フィルムさえ交換すればリサイクルが
できる。又、本体部ケースに嵌着して使用する前部ケー
ス、後部ケースは従来どおり廃棄する部分であるが、本
発明によれば廃棄部分にあたる前部ケースと後部ケース
はパルプを主体とするものであるから低コストであり、
樹脂を含浸する程度のものでも気密性は十分保持され、
セットとしてフィルム一体型カメラを組み立てている場
合に内部を機械的に保護するとともに湿気の影響も排除
し、カメラ性能を低下させるおそれがなく、しかも撮影
完了後此の部分を廃棄しても、主材が紙質であるから燃
焼カロリーが低く、又地中埋没した場合でもパルプ部分
はバクテリアにより分解し易いという作用効果を奏す
る。In the film-integrated camera to which the case of the present invention is applied, the main body case is made of plastic as in the conventional case. That is, the main body has an optical unit of the camera, a film and other essential functions of the camera. Since the part is a lightweight and compact integrally molded part, by making this part as it is, it is exactly the same as the conventional in the production process and quality control even if it is reused, while preventing the occurrence of problems, You can recycle by replacing the film. Further, although the front case and the rear case which are fitted to the main body case and used are the parts to be discarded as usual, according to the present invention, the front case and the rear case, which are the discarded parts, are mainly made of pulp. Low cost,
Even if it is impregnated with resin, airtightness is sufficiently maintained,
When assembling the film-integrated camera as a set, it protects the inside mechanically and eliminates the influence of moisture, so there is no risk of degrading the camera performance, and even if this part is discarded after the shooting is completed, Since the material is paper quality, it has a low calorific value, and even if it is buried in the ground, the pulp part is easily decomposed by bacteria.
【０００８】本発明においては前部ケース、後部ケース
は広葉樹クラフトパルプ（Ｌ材）を主成分とし、晒パル
プ（ＬＢＫＰ）でも未晒パルプ（ＬＵＫＰ）でも差支へ
ない。本発明のケースは広葉樹クラフトパルプを主成分
とするので、パルプの組成もその８０％程度は広葉樹パ
ルプであることが望ましいが物理強度を向上するために
１０〜２０％程度の針葉樹パルプ（Ｎ材）を配合しても
よい。本発明でこのパルプを用いた抄紙用スラリーは、
上記パルプ原料以外に０．１〜０．３％程度の硫酸バン
ドを配合し、ＰＨを７〜８にコントロールして抄紙す
る。ＰＨのコントロールなしで抄紙すると樹脂含浸後、
熱硬化した後に、クラックが発生するおそれがある。本
発明の実施に際して抄紙機には特に限定なく、長網抄紙
機、円網抄紙機、ヤンキー抄紙機等が使用できる。叩解
度は５００〜５５０ｃｃ程度（カナディアンフリーネ
ス）に行ない、坪量は５０〜１０００ｇ／ｍ2 好ましく
は１００〜２３０ｇ／ｍ2 である。又このシート状パル
プ基材に含浸する熱硬化性樹脂には特に限定はないが、
ジアリル（イソ）フタレート樹脂、レゾール型フェノー
ル樹脂、ノボラック型フェノール樹脂、エポキシ樹脂、
メラミン樹脂、アクリル系樹脂等の中から適宜選択され
る。更にこの熱硬化性樹脂の含浸量はシート状パルプ基
材絶乾重量に対して、１０〜３０重量％であることが必
要で、１０重量％未満ではケースの吸湿性と物理的強度
の点で問題を生ずる。又３０重量％を超えて多い場合は
樹脂の量が多くなるために、使用後廃棄時の焼却の際カ
ロリーが高くなり過ぎ、かつ地中で分解しないで残存す
る成分が多過ぎるので好ましくない。In the present invention, the front case and the rear case are mainly made of hardwood kraft pulp (L material), and it does not matter whether bleached pulp (LBKP) or unbleached pulp (LUKP). Since the case of the present invention is mainly composed of hardwood kraft pulp, it is desirable that about 80% of the pulp composition is hardwood pulp, but 10 to 20% of softwood pulp (N material is used in order to improve physical strength. ) May be blended. Papermaking slurry using this pulp in the present invention,
In addition to the above pulp raw material, a sulfuric acid band of about 0.1 to 0.3% is blended, and PH is controlled to 7 to 8 for papermaking. When papermaking without pH control, after resin impregnation,
After thermosetting, cracks may occur. In carrying out the present invention, the paper machine is not particularly limited, and a Fourdrinier paper machine, a cylinder paper machine, a Yankee paper machine or the like can be used. The beating degree is about 500 to 550 cc (Canadian freeness), and the basis weight is 50 to 1000 g / m 2, preferably 100 to 230 g / m 2 . The thermosetting resin impregnated into the sheet-shaped pulp base material is not particularly limited,
Diallyl (iso) phthalate resin, resol type phenol resin, novolac type phenol resin, epoxy resin,
It is appropriately selected from melamine resin, acrylic resin and the like. Further, the impregnated amount of the thermosetting resin is required to be 10 to 30% by weight with respect to the absolute dry weight of the sheet-shaped pulp base material, and if less than 10% by weight, the hygroscopicity and physical strength of the case will be considered. Cause problems. On the other hand, when the amount is more than 30% by weight, the amount of the resin is large, so that the calorie becomes too high when incinerated at the time of disposal after use, and too many components remain without being decomposed in the ground, which is not preferable.
【０００９】樹脂含浸紙から箱型の紙ケース（前部ケー
ス、後部ケース）に立体成形するには、自動製箱機又は
金型により一旦成形加工し、しかる後加熱処理して樹脂
を硬化させるか又は製箱機で製箱すると同時に加熱処理
し硬化させてもよい。コーナー部分のクラック防止のた
めには後者の方が好ましい。又、製箱の際コーナー部分
の接合にはアクリル系、エポキシ系等の接着剤を使用し
てもよいが、カメラユニット内蔵後の本体ユニットと一
体化することを考えると、なるべく揮発性成分のない無
溶剤接着剤が好ましい。また、高温雰囲気での接着剤の
揮発性成分の影響を防止するためには、その接合に接着
剤を使用することなく物理的な嵌合による方が好まし
い。In order to three-dimensionally mold resin-impregnated paper into a box-shaped paper case (front case, rear case), the resin-impregnated paper is once molded by an automatic box-making machine or a mold, and then heat-treated to cure the resin. Alternatively, it may be heat-treated and cured at the same time when it is made in a box by a box making machine. The latter is preferable in order to prevent cracks at the corners. In addition, an acrylic-based or epoxy-based adhesive may be used to join the corners in the box-making process, but considering that it is integrated with the main unit after the camera unit is built in, it is recommended to use volatile components as much as possible. Solventless adhesives are preferred. Further, in order to prevent the influence of the volatile component of the adhesive in a high temperature atmosphere, it is preferable to use physical fitting without using an adhesive for the joining.
【００１０】[0010]
実施例１ ＬＵＫＰ１００％のパルプ原料をカナディアンクリーネ
ステスターによる叩解度で５５０ｃｃとなるように叩解
して抄紙用スラリーとし、これに硫酸バンド０．３％添
加しＰＨを７〜８に調整したスラリーを長網多筒式抄紙
機にて厚さ４４０μｍ、坪量２９０ｇ／ｍ2 の樹脂含浸
用原紙を抄造した。一方ジアリルフタレートのプリポリ
マー（ダイソー社製 商品名；ダイソーダップＡ）をア
セトン／トルエン（７５／２５）の混合溶媒に溶解し、
含浸用樹脂溶液を作成した。しかる後含浸機により２０
ｍｍ／ｍｉｎの含浸速度で１１０℃の温度にて前記原紙
に樹脂を含浸し、プリプレグ（１次キュア）の樹脂含浸
紙を得た。得られた樹脂含浸紙の含浸量〔（含浸樹脂量
／含浸紙の全重量）×１００％〕は１７．４％であっ
た。次に幅方向の長さＸ＝１２ｃｍ，縦方向の長さＹ＝
７ｃｍ，、深さ方向の長さＺ＝３ｃｍの箱型となるよう
に前記樹脂含浸紙を金型にてプレス加工し、同時に１７
０℃で２０分間、加熱硬化し（２次キュア）、本発明の
フィルム一体型カメラの前部ケース及び後部からなるケ
ースを作成した。Example 1 A pulp raw material of 100% LUKP was beaten so as to have a beating degree of 550 cc with a Canadian Kleene tester to form a slurry for papermaking, and a slurry in which 0.3% of a sulfuric acid band was added to adjust the pH to 7 to 8 was prepared. A raw paper for resin impregnation having a thickness of 440 μm and a basis weight of 290 g / m 2 was produced using a fourdrinier cylinder paper machine. On the other hand, a prepolymer of diallyl phthalate (commercial name by Daiso; Daiso Dup A) was dissolved in a mixed solvent of acetone / toluene (75/25),
A resin solution for impregnation was prepared. After that, 20 by the impregnator
The base paper was impregnated with resin at a temperature of 110 ° C. at an impregnation speed of mm / min to obtain a resin-impregnated paper of prepreg (first cure). The amount of impregnation of the obtained resin-impregnated paper [(amount of impregnated resin / total weight of impregnated paper) × 100%] was 17.4%. Next, the length in the width direction X = 12 cm, the length in the vertical direction Y =
The resin-impregnated paper was pressed with a mold so as to form a box having a length of 7 cm and a length Z in the depth direction of Z = 3 cm.
The film was heat-cured (secondary cure) at 0 ° C. for 20 minutes to prepare a case composed of the front case and the rear part of the film-integrated camera of the present invention.
【００１１】実施例２ 含浸用樹脂液としてレゾール型液状フェノール樹脂（住
友デュレズ社製 商品名；スミライトレジンＰＲ−５４
０７６）のメタノール溶液（固型分５０重量％）を用い
た他は実施例１と同様にして本発明のフィルム一体型カ
メラ用の前部ケース及び後部ケースからなるケースを作
成した。Example 2 Resol type liquid phenol resin as impregnating resin liquid (trade name of Sumitomo Durez Co., Ltd .; Sumilite Resin PR-54)
076) was used in the same manner as in Example 1 except that a methanol solution (solid content: 50% by weight) was used to prepare a case including a front case and a rear case for the film-integrated camera of the present invention.
【００１２】上記実施例１〜２で得られた前部ケース及
び後部ケースを使用し、図１に示した本体ケースと嵌着
してフィルム一体型カメラを作成したところ、実用上何
等問題なく使用することができた。Using the front case and the rear case obtained in Examples 1 and 2 and fitting the main case shown in FIG. 1 to make a film-integrated camera, practically no problem was found. We were able to.
【００１３】[0013]
【発明の効果】本発明によれば本体部は従来よりプラス
チックケースにより作成され、フィルムを入れ替えるだ
けで、撮影機構を備えた本体部ケースだけを再使用でき
るので廃棄部分が少なくなりコストが低減し、かつ再使
用部分は生産設備、生産材料等に変更なく、生産管理上
問題が発生しない。又、廃棄処分される前部ケース、後
部ケースは共に紙材料を主とするものであるから、軽量
化されしかもコストも低廉で、廃棄処理にあたっても低
カロリーで燃焼できるので焼却炉の炉材料を傷めるおそ
れがなく、更に地中埋設した場合にも、バクテリアで容
易に分解できるので公害問題の発生が極めて少ないと言
う効果を奏する。According to the present invention, the main body is conventionally made of a plastic case, and only the main body case equipped with a photographing mechanism can be reused by simply changing the film, so that the discarded portion is reduced and the cost is reduced. In addition, the reuse part has no change in production equipment, production materials, etc., and no problems occur in production management. Also, since the front case and the rear case to be discarded are mainly made of paper materials, they are light in weight and low in cost, and can be burned with low calorie even when they are disposed of. There is no risk of damage, and even when it is buried in the ground, it can be easily decomposed by bacteria, so that the problem of pollution is extremely small.
【図１】本発明のケースが適用されるフィルム一体型カ
メラの簡略分解斜視図FIG. 1 is a simplified exploded perspective view of a film-integrated camera to which a case of the present invention is applied.
【図２】本発明のケースが適用されるフィルム一体型カ
メラの表側から見た組立斜視図FIG. 2 is an assembly perspective view of a film-integrated camera to which the case of the present invention is applied, as seen from the front side.
【図３】本発明のケースが適用されるフィルム一体型カ
メラの裏側から見た組立斜視図FIG. 3 is an assembled perspective view of the film-integrated camera to which the case of the present invention is applied, viewed from the back side.
１ 本体部ケース ２ 前部ケース ３ 後部ケース 1 Body case 2 Front case 3 Rear case
Claims (3)
を備え、かつ未露光のフィルムを収納した本体ユニット
を内蔵するフィルム一体型カメラを構成する前部ケース
および後部ケースであって、該ケースが広葉樹クラフト
パルプを主成分とする坪量５０〜１０００ｇ／ｍ2 のシ
ート状パルプ基材に熱硬化性樹脂を１０〜３０重量％含
浸してなる樹脂含浸紙による成形ケースとしたことを特
徴とするフィルム一体型カメラのケース。1. A front case and a rear case that constitute a film-integrated camera that includes a photographing mechanism such as a photographing lens and a shutter, and that has a main body unit that accommodates an unexposed film. A film made of resin-impregnated paper obtained by impregnating a sheet-like pulp base material having a basis weight of kraft pulp of 50 to 1000 g / m 2 with a thermosetting resin in an amount of 10 to 30% by weight. Integrated camera case.
を備え、かつ未露光のフィルムを収納した本体ユニット
を内蔵するフィルム一体型カメラを構成する前部ケース
および後部ケースの製造方法であって、該製造方法が広
葉樹クラフトパルプを主成分とするシート状のパルプ基
材に熱硬化性樹脂のプリポリマーを１０〜３０重量％含
浸後、加熱乾燥してプリプレグを作成し、しかる後所定
の前部ケース及び後部ケースの形状に成形した後、加熱
硬化することを特徴とするフィルム一体型カメラのケー
スの製造方法。2. A method for manufacturing a front case and a rear case, which comprises a film-integrated camera including a photographing mechanism such as a photographing lens and a shutter and having a main body unit accommodating an unexposed film, the method comprising: A sheet-like pulp base material having a hardwood kraft pulp as a main component is impregnated with a thermosetting resin prepolymer in an amount of 10 to 30% by weight and then dried by heating to prepare a prepreg, and then a predetermined front case And a method of manufacturing a case for a film-integrated camera, which comprises forming the shape of the rear case and then heating and curing.
を備え、かつ未露光のフィルムを収納した本体ユニット
を内蔵するフィルム一体型カメラを構成するケースの製
造方法であって、該製造方法が広葉樹クラフトパルプを
主成分とするシート状のパルプ基材に熱硬化性樹脂のプ
リポリマーを１０〜３０重量％含浸後、加熱乾燥してプ
リプレグを作成し、しかる後所定の前部ケース及び後部
ケースの形状に成形しながら樹脂を加熱硬化させるフィ
ルム一体型カメラのケースの製造方法。3. A method for manufacturing a case, which comprises a film-incorporated camera having a photographing mechanism such as a photographing lens and a shutter and having a main body unit accommodating an unexposed film, the manufacturing method being a hardwood craft. A sheet-like pulp base material containing pulp as a main component is impregnated with a thermosetting resin prepolymer in an amount of 10 to 30% by weight, and then dried by heating to form a prepreg, and then a predetermined shape of a front case and a rear case. A method for manufacturing a film-integrated camera case, wherein a resin is heated and cured while being molded into a sheet.