JPH07309064A - Thermosensible recording paper - Google Patents

Abstract

PURPOSE:To provide a thermosensible recording paper for a second master drawing having high transparency, excellent fold endurance and preservability of recorded images. CONSTITUTION:In a thermosensible recording paper, a thermosensible recording layer which contains a colorless or light basic dye and a coloring agent and a protective layer are arranged in sequence on a base paper. For the base paper, a glassine paper having a synthetic resin emulsion of 5-30wt.% or below based on the total solid quantity of the base paper or being pressed with a size is used.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、無色ないし淡色の塩基
性染料と呈色剤との反応を利用した第二原図用感熱記録
紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat-sensitive recording paper for a second original drawing which utilizes the reaction between a colorless or light-colored basic dye and a color former.

【０００２】[0002]

【従来の技術】無色ないし淡色の塩基性染料と呈色剤と
の呈色反応を利用し、サーマルヘッドからの熱エネルギ
ーにより両発色物質を反応させて記録像を得るようにし
た感熱記録紙はよく知られている。かかる感熱記録紙は
比較的安価であり、また記録機器がコンパクトでかつそ
の保守も容易なため、ファクシミリや各種計算機器等の
記録媒体としてのみならず巾広い分野において使用され
ている。例えばその利用分野の一つとしてＣＡＤやＣＡ
Ｍシステムの拡大に伴って、そのプリンタ−用紙として
感熱記録紙の使用が増大している。しかし、一般に市販
されている感熱記録紙は、不透明度が高い為に、第二原
図用紙としては使用できない。第二原図用の感熱記録紙
を得るために、原紙にアクリル樹脂やイソシアネ−ト基
を有する化合物を含浸する方法が特開昭６１−１０８５
８１号公報、特公昭５７−１６９１３号公報に記載され
ているが、地肌の黄変や記録像の保存性や、支持体自体
の紙力も弱いため一般に普及しにくい。また、樹脂フィ
ルムを支持体として使用した場合は折れ部が白化するな
どの欠点があり、安価で折り畳んで保存できる感熱記録
紙が強く要請されている。2. Description of the Related Art A heat-sensitive recording paper which utilizes a color reaction between a colorless or light-colored basic dye and a color-developing agent to react both color-forming substances with thermal energy from a thermal head to obtain a recorded image is known. well known. Since such thermal recording paper is relatively inexpensive and the recording device is compact and its maintenance is easy, it is used not only as a recording medium for facsimiles and various computing devices but also in a wide range of fields. For example, CAD and CA are one of the application fields.
With the expansion of the M system, the use of thermal recording paper as the printer paper is increasing. However, the thermal recording paper which is generally commercially available cannot be used as the second original drawing paper because of its high opacity. A method of impregnating a base paper with an acrylic resin or a compound having an isocyanate group in order to obtain a heat-sensitive recording paper for a second original is disclosed in JP-A-61-1085.
No. 81 and Japanese Examined Patent Publication No. 57-16913, but it is generally difficult to spread due to yellowing of the background, storability of recorded images, and weak paper strength of the support itself. Further, when a resin film is used as a support, there is a defect that the folded portion is whitened, and there is a strong demand for a thermal recording paper which can be folded and stored at a low cost.

【０００３】[0003]

【発明が解決しようとする課題】本発明の課題は、上記
の如き問題を解決すると共に、透明性が高く、耐折強度
及び記録像の保存性に優れた第二原図用の感熱記録紙を
提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above problems and to provide a thermal recording paper for a second original image which has high transparency and is excellent in folding endurance and storability of recorded images. To provide.

【０００４】[0004]

【課題を解決するための手段】本発明者は、基紙上に、
無色ないし淡色の塩基性染料と呈色剤とを含有する感熱
記録層、および保護層を順次設けた感熱記録紙におい
て、基紙として、合成樹脂エマルジョンが基紙の全固形
量に対して５〜３０重量％内添またはサイズプレスされ
たグラシン紙を使用することにより、上記課題が解決さ
れることを見出し、本発明を完成するに至った。The present inventor has found that on a base paper,
In a thermosensitive recording paper in which a thermosensitive recording layer containing a colorless or light-colored basic dye and a coloring agent, and a protective layer are sequentially provided, a synthetic resin emulsion is used as a base paper in an amount of 5 to 5% of the total solid amount of the base paper. The inventors have found that the above problems can be solved by using glassine paper with 30% by weight internally added or size-pressed, and have completed the present invention.

【０００５】[0005]

【作用】本発明で使用する半透明のグラシン紙とは、高
度に粘状叩解したケミカルパルプを原料とし、スーパー
キャレンダーにかけて表面を平滑にした紙質の細密な薄
葉紙である。俗にツヤ付け紙、ガラス紙などとも呼ばれ
ており、種々の食品、煙草薬品、金属部品などに対する
保護包装や粘着紙の剥離紙用基材などに使用されてい
る。本発明では、合成樹脂エマルジョンが内添、若しく
はサイズプレスされたグラシン紙を感熱記録紙の基材と
して使用するが、坪量として１５〜１００ｇ／ｍ² 、好
ましくは２０〜６０ｇ／ｍ² のものが使用される。The semi-transparent glassine paper used in the present invention is a fine paper-like thin paper made of highly viscous beaten chemical pulp as a raw material and having its surface smoothed by a super calender. It is also commonly called glossy paper, glass paper, etc., and is used as a protective packaging for various foods, tobacco chemicals, metal parts, etc., and as a base material for release paper of adhesive paper. In the present invention, synthetic resin emulsion is internally added or size-pressed glassine paper is used as the base material of the thermal recording paper, but the basis weight is 15 to 100 g / m ² , preferably 20 to 60 g / m ² . Is used.

【０００６】本発明では、抄紙しる際に、紙料中に合成
樹脂エマルジョンを内添させ、且つ抄紙された基紙の全
固形量に対して合成樹脂エマルジョンを５〜３０重量％
含むグラシン紙、または抄紙機のサイズプレス部のおい
て合成樹脂エマルジョンが基紙の全固形料に対して５〜
３０重量％基紙の表面にサイズプレスされたグラシン紙
を用いるもので、合成樹脂エマルジョンの内添量が５重
量％未満になると感熱記録層用水性塗液を塗布、乾燥す
るとカールが強く発生したり、紙切れが発生し易くな
る。３０重量％を越えると抄紙された紙をスーパーキャ
レンダーでグラシン紙に仕上げる際、キャレンダー部に
樹脂が付着して操業性が低下する。In the present invention, a synthetic resin emulsion is internally added to a paper material at the time of papermaking, and the synthetic resin emulsion is contained in an amount of 5 to 30% by weight based on the total solid amount of the base paper.
Glassine paper containing, or synthetic resin emulsion in the size press part of the paper machine is 5 to the total solid content of the base paper.
A glassine paper size-pressed on the surface of 30% by weight base paper is used. When the amount of the synthetic resin emulsion added is less than 5% by weight, the aqueous coating solution for the heat-sensitive recording layer is applied, and when it is dried, curling occurs strongly. Or, it is easy for paper to run out. When the content exceeds 30% by weight, when the paper made is made into glassine paper with a super calender, the resin adheres to the calender portion to deteriorate the operability.

【０００７】半透明な原紙として、原紙に有機溶剤に溶
解された樹脂を含浸させたものや、有機溶剤に溶解され
た樹脂を原紙に塗布したものがあるが、これらは、含浸
・塗工という二次加工工程を必要とするので製品自体が
高価になるのと、樹脂の種類により地肌カブリや記録象
の褪色を起こすという欠点がある。また、一般のグラシ
ン紙はその紙力、柔軟性、耐水性が劣り、感熱記録層を
設ける際皺、紙切れ、カールが発生し易い。そこで、こ
のような欠点を改善するために、抄紙工程のウエットエ
ンドで透明性の高い合成樹脂エマルジョンを紙料に定着
させることにより、紙力・耐水性・透明性を上げること
ができる。As the semitransparent base paper, there are a base paper impregnated with a resin dissolved in an organic solvent and a base paper coated with a resin dissolved in an organic solvent. These are called impregnation / coating. Since the secondary processing step is required, the product itself is expensive, and there are drawbacks that the background fog and the fading of the recorded image are caused depending on the type of resin. In addition, general glassine paper is inferior in paper strength, flexibility, and water resistance, and wrinkles, paper breaks, and curls are likely to occur when a thermal recording layer is provided. Therefore, in order to improve such drawbacks, paper strength, water resistance, and transparency can be increased by fixing a highly transparent synthetic resin emulsion to the stock at the wet end of the papermaking process.

【０００８】内添若しくはサイズプレスされる合成樹脂
エマルジョンに使用される樹脂としては熱可塑性樹脂が
好ましく、具体例としては、例えばスチレン−ブタジエ
ン系エマルジョン、スチレン−酢酸ビニル系エマルジョ
ン、（メタ）アクリル酸メチル−酢酸ビニル系エマルジ
ョン、スチレン−酢酸ビニル系エマルジョン、（メタ）
アクリル酸エステル系エマルジョン、スチレン−（メ
タ）アクリル酸エチル系エマルジョン、スチレン−（メ
タ）アクリル酸ブチル系エマルジョン、エチレン−酢酸
ビニル系エマルジョン、塩化ビニル系エマルジョン、ポ
リエチレン系エマルジョン、ポリウレタン系エマルジョ
ン、塩化ビニリデン系エマルジョン等が挙げられる。更
に、合成樹脂を構成するモノマー成分としてはアクリル
ニトリル、（メタ）アクリル酸、無水マレイン酸等が挙
げられる。なかでも、樹脂成分として（メタ）アクリル
酸エステルを含む合成樹脂エマルジョンが好ましい。勿
論、これらの合成樹脂エマルジョンに限定されるもので
はい。The resin used in the synthetic resin emulsion to be internally added or size-pressed is preferably a thermoplastic resin, and specific examples thereof include styrene-butadiene type emulsion, styrene-vinyl acetate type emulsion and (meth) acrylic acid. Methyl-vinyl acetate emulsion, styrene-vinyl acetate emulsion, (meth)
Acrylic ester type emulsion, styrene- (meth) ethyl acrylate type emulsion, styrene- (meth) acrylate butyl type emulsion, ethylene-vinyl acetate type emulsion, vinyl chloride type emulsion, polyethylene type emulsion, polyurethane type emulsion, vinylidene chloride A system emulsion etc. are mentioned. Further, examples of the monomer component constituting the synthetic resin include acrylonitrile, (meth) acrylic acid, maleic anhydride and the like. Among them, a synthetic resin emulsion containing a (meth) acrylic acid ester as a resin component is preferable. Of course, it is not limited to these synthetic resin emulsions.

【０００９】本発明では該グラシン紙上に記録層が塗布
されるが、記録層に含有される無色ないし淡色の塩基性
染料としては各種のものが公知であり、例えば下記が例
示される。 ３，３−ビス（ｐ−ジメチルアミノフェニル）−６−ジ
メチルアミノフタリド、３，３−ビス（１，２−ジメチ
ルインドール−３−イル）−５−ジメチルアミノフタリ
ド、３，３−ビス（１，２−ジメチルインドール−３−
イル）−６−ジメチルアミノフタリド、３−（４−ジエ
チルアミノ−２−エトキシフェニル）−３−（１−エチ
ル−２−メチルインドール−３−イル）−７−アザフタ
リド、３，３−ビス（１−エチル−２−メチルインドー
ル−３−イル）フタリド等のトリアリールメタン系染
料、４，４′−ビス（ジメチルアミノ）ベンズヒドリル
ベンジルエーテル、Ｎ−ハロフェニル−ロイコオーラミ
ン、Ｎ−２，４，５−トリクロロフェニルロイコオーラ
ミン、４，４′−ビス（ジメチルアミノ）ベンズヒドリ
ル−ｐ−トルエンスルフィン酸エステル等のジフェニル
メタン系染料、３，３−ビス〔１−（４−メトキシフェ
ニル）−１−（４−ジメチルアミノフェニル）エチレン
−２−イル〕−４，５，６，７−テトラクロロフタリ
ド、３，３−ビス〔１−（４−メトキシフェニル）−１
−（４−ピロリジノフェニル）エチレン−２−イル〕−
４，５，６，７−テトラクロロフタリド等のジビニルフ
タリド系染料、３−ベンジルスピロジナフトピラン、３
−メチルナフト（６′−メトキシベンゾ）スピロピラ
ン、３−プロピルスピロジベンゾピラン、ジ−β−ナフ
トスピロピラン、３−メチル−ジ−β−ナフトスピロピ
ラン等のスピロ系染料、ローダミン−Ｂ−アニリノラク
タム、ローダミン（ｐ−ニトロアニリノ）ラクタム、ロ
ーダミン（ｏ−クロロアニリノ）ラクタム等のラクタム
系染料、３−ジエチルアミノ−６−メチルフルオラン、
３−ジメチルアミノ−７−メトキシフルオラン、３−ジ
エチルアミノ−６−メトキシフルオラン、３−ジエチル
アミノ−７−メトキシフルオラン、３−ジエチルアミノ
−６，７−ジメチルフルオラン、３−（Ｎ−エチル−ｐ
−トルイジノ）−６−メチル−７−フェニルアミノフル
オラン、３−ジエチルアミノ−６−メチル−７−フェニ
ルアミノフルオラン、３−ジメチルアミノ−６−メチル
−７−フェニルアミノフルオラン、３−ジ（ｎ−ブチ
ル）アミノ−６−メチル−７−フェニルアミノフルオラ
ン、３−（Ｎ−シクロヘキシル−Ｎ−メチルアミノ）−
６−メチル−７−フェニルアミノフルオラン、３−ジエ
チルアミノ−７−（ｏ−クロロフェニルアミノ）フルオ
ラン、３−ジブチルアミノ−７−（ｏ−クロロフェニル
アミノ）フルオラン、３−（Ｎ−エチル−Ｎ−テトラヒ
ドロフルフリルアミノ）−６−メチル−７−フェニルア
ミノフルオラン、３−（Ｎ−エチル−Ｎ−テトラヒドロ
フルフリルアミノ）−６−メチル−７−アニリノフルオ
ラン、３−（Ｎ−シクロペンチル−Ｎ−エチルアミノ）
−６−メチル−７−アニリノフルオラン、３−（Ｎ−エ
チル−Ｎ−ｐ−トリルアミノ）−６−メチル−７−アニ
リノフルオラン等のフルオラン系染料、３，６−ビス
（ジメチルアミノ）フルオレン−９−スピロ−３′−
（６′−ジメチルアミノ）フタリド、３，６−ビス（ジ
エチルアミノ）−３′−メチル−スピロ〔フルオレン−
９，６′−６′Ｈ−クロメノ（４，３−ｂ）インドー
ル〕等のフルオレン系染料等が挙げられる。勿論これら
の染料に限定されるものではなく、さらに二種以上の染
料の併用も可能である。In the present invention, the recording layer is coated on the glassine paper, and various kinds of colorless or light-colored basic dyes contained in the recording layer are known, and the following are exemplified. 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3,3-bis (1,2-dimethylindol-3-yl) -5-dimethylaminophthalide, 3,3-bis (1,2-Dimethylindole-3-
Yl) -6-dimethylaminophthalide, 3- (4-diethylamino-2-ethoxyphenyl) -3- (1-ethyl-2-methylindol-3-yl) -7-azaphthalide, 3,3-bis ( 1-Ethyl-2-methylindol-3-yl) phthalide and other triarylmethane dyes, 4,4′-bis (dimethylamino) benzhydrylbenzyl ether, N-halophenyl-leukoauramine, N-2, Diphenylmethane dyes such as 4,5-trichlorophenyl leuco auramine and 4,4'-bis (dimethylamino) benzhydryl-p-toluenesulfinic acid ester, 3,3-bis [1- (4-methoxyphenyl) -1 -(4-Dimethylaminophenyl) ethylene-2-yl] -4,5,6,7-tetrachlorophthalide, 3,3-bis [1 (4-methoxyphenyl) -1
-(4-Pyrrolidinophenyl) ethylene-2-yl]-
Divinylphthalide dyes such as 4,5,6,7-tetrachlorophthalide, 3-benzylspirodinaphthopyran, 3
-Spiro dyes such as methylnaphtho (6'-methoxybenzo) spiropyran, 3-propylspirodibenzopyran, di-β-naphthospiropyran, 3-methyl-di-β-naphthospiropyran, rhodamine-B-anilinolactam, rhodamine Lactam dyes such as (p-nitroanilino) lactam and rhodamine (o-chloroanilino) lactam, 3-diethylamino-6-methylfluorane,
3-Dimethylamino-7-methoxyfluorane, 3-diethylamino-6-methoxyfluorane, 3-diethylamino-7-methoxyfluorane, 3-diethylamino-6,7-dimethylfluorane, 3- (N-ethyl- p
-Toluidino) -6-methyl-7-phenylaminofluorane, 3-diethylamino-6-methyl-7-phenylaminofluorane, 3-dimethylamino-6-methyl-7-phenylaminofluorane, 3-di ( n-butyl) amino-6-methyl-7-phenylaminofluorane, 3- (N-cyclohexyl-N-methylamino)-
6-methyl-7-phenylaminofluorane, 3-diethylamino-7- (o-chlorophenylamino) fluorane, 3-dibutylamino-7- (o-chlorophenylamino) fluorane, 3- (N-ethyl-N-tetrahydro) Furfurylamino) -6-methyl-7-phenylaminofluorane, 3- (N-ethyl-N-tetrahydrofurfurylamino) -6-methyl-7-anilinofluorane, 3- (N-cyclopentyl-N -Ethylamino)
Fluorane dyes such as 6-methyl-7-anilinofluorane and 3- (N-ethyl-Np-tolylamino) -6-methyl-7-anilinofluorane, 3,6-bis (dimethylamino) ) Fluorene-9-spiro-3'-
(6'-Dimethylamino) phthalide, 3,6-bis (diethylamino) -3'-methyl-spiro [fluorene-
9,6'-6'H-chromeno (4,3-b) indole] and the like. Of course, the dyes are not limited to these dyes, and two or more dyes may be used in combination.

【００１０】また、本発明の感熱記録紙において、記録
層中の塩基性染料を発色させる顕色剤としては、各種公
知の顕色剤を併用することができ、例えば、下記が例示
できる。４，４′−イソプロピリデンジフェノール（ビ
スフェノールＡ）、４，４′−シクロヘキシリデンビス
フェノール、４，４′−〔１，４−フェニレンビス（１
−メチルエチリデン）〕ビスフェノール、４，４′−
〔１，３−フェニレンビス（１−メチルエチリデン）〕
ビスフェノール、４，４′−（１，３−ジメチルブチリ
デン）ビスフェノール、２，２−ビス（４−ヒドロキシ
フェニル）−４−メチル−ペンタン、４，４′−ジヒド
ロキシジフェニルサルファイド、４，４′−チオビス
（６−tert−ブチル−３−メチルフェノール）、４，
４′−ジヒドロキシジフェニルスルホン、２，４′−ジ
ヒドロキシジフェニルスルホン、４−ヒドロキシ−４′
−メチルジフェニルスルホン、４−ヒドロキシ−４′−
メトキシジフェニルスルホン、４−ヒドロキシ−４′−
イソプロポキシジフェニルスルホン、４−ヒドロキシ−
３′，４′−トリメチレンジフェニルスルホン、４−ヒ
ドロキシ−３′，４′−テトラメチレンジフェニルスル
ホン、３，４−ジヒドロキシ−４′−メチルジフェニル
スルホン、ビス（３−アリル−４−ヒドロキシフェニ
ル）スルホン、４−ヒドロキシベンゾフェノン、２，４
−ジヒドロキシベンゾフェノン、２，４，４′−トリヒ
ドロキシベンゾフェノン、２，２′，４，４′−テトラ
ヒドロキシベンゾフェノン、４−ヒドロキシ安息香酸フ
ェニル、４−ヒドロキシ安息香酸ベンジル、４−ヒドロ
キシ安息香酸トリル、ノボラック型フェノール樹脂、フ
ェノール重合体等のフェノール性化合物、３−sec −ブ
チル−４−ヒドロキシ安息香酸、３，５−ジメチル−４
−ヒドロキシ安息香酸、３，５−ジ−tert−ブチルサリ
チル酸、３−ベンジルサリチル酸、３−（α−メチルベ
ンジル）サリチル酸、３−クロル−５−（α−メチルベ
ンジル）サリチル酸、３−フェニル−５−（α，α−ジ
メチルベンジル）サリチル酸、３，５−ジ−α−メチル
ベンジルサリチル酸、４−（２−Ｐ−メトキシフェノキ
シエトキシ）サリチル酸、４−（３−Ｐ−トリルスルホ
ニルプロピルオキシ）サリチル酸等の芳香族カルボン
酸、およびこれら芳香族カルボン酸と例えば亜鉛、マグ
ネシウム等の多価金属との塩等の有機酸性物質、ｐ−ト
リルスルホニル尿素フェニル、４，４’−ビス（ｐ−ト
リルスルホニル尿素）ジフェニルメタン等。なお、これ
らの呈色剤も勿論必要に応じて２種以上を併用すること
ができる。Further, in the heat-sensitive recording paper of the present invention, various known developers can be used in combination as the developers for developing the basic dye in the recording layer, for example, the following can be exemplified. 4,4'-isopropylidene diphenol (bisphenol A), 4,4'-cyclohexylidene bisphenol, 4,4 '-[1,4-phenylenebis (1
-Methylethylidene)] bisphenol, 4,4'-
[1,3-Phenylenebis (1-methylethylidene)]
Bisphenol, 4,4 '-(1,3-dimethylbutylidene) bisphenol, 2,2-bis (4-hydroxyphenyl) -4-methyl-pentane, 4,4'-dihydroxydiphenyl sulfide, 4,4'- Thiobis (6-tert-butyl-3-methylphenol), 4,
4'-dihydroxydiphenyl sulfone, 2,4'-dihydroxydiphenyl sulfone, 4-hydroxy-4 '
-Methyldiphenyl sulfone, 4-hydroxy-4'-
Methoxydiphenyl sulfone, 4-hydroxy-4'-
Isopropoxydiphenyl sulfone, 4-hydroxy-
3 ', 4'-trimethylene diphenyl sulfone, 4-hydroxy-3', 4'-tetramethylene diphenyl sulfone, 3,4-dihydroxy-4'-methyldiphenyl sulfone, bis (3-allyl-4-hydroxyphenyl) Sulfone, 4-hydroxybenzophenone, 2,4
-Dihydroxybenzophenone, 2,4,4'-trihydroxybenzophenone, 2,2 ', 4,4'-tetrahydroxybenzophenone, phenyl 4-hydroxybenzoate, benzyl 4-hydroxybenzoate, tolyl 4-hydroxybenzoate, Novolac type phenolic resin, phenolic compounds such as phenolic polymer, 3-sec-butyl-4-hydroxybenzoic acid, 3,5-dimethyl-4
-Hydroxybenzoic acid, 3,5-di-tert-butylsalicylic acid, 3-benzylsalicylic acid, 3- (α-methylbenzyl) salicylic acid, 3-chloro-5- (α-methylbenzyl) salicylic acid, 3-phenyl-5 -(Α, α-Dimethylbenzyl) salicylic acid, 3,5-di-α-methylbenzylsalicylic acid, 4- (2-P-methoxyphenoxyethoxy) salicylic acid, 4- (3-P-tolylsulfonylpropyloxy) salicylic acid, etc. Aromatic carboxylic acids, and organic acidic substances such as salts of these aromatic carboxylic acids with polyvalent metals such as zinc and magnesium, p-tolylsulfonylureaphenyl, 4,4′-bis (p-tolylsulfonylurea) ) Diphenylmethane and the like. Of course, these colorants may be used in combination of two or more, if necessary.

【００１１】また、本発明では目的に応じて増感剤、お
よび記録像の保存性改良剤を併用することもできる。増
感剤の具体例としては例えばステアリン酸アミド、ステ
アリン酸メチレンビスアミド、オレイン酸アミド、パル
ミチン酸アミド、ヤシ脂肪酸アミド等の脂肪酸アミド
類、１，２−ジ（３−メチルフェノキシ）エタン、１，
２−ジフェノキシエタン、１−フェノキシ−２−（４−
メチルフェノキシ）エタン、パラベンジルビフェニル、
ナフチルベンジルエーテル、ベンジル−４−メチルチオ
フェニルエーテル、１−ヒドロキシ−２−ナフトエ酸フ
ェニルエステル、シュウ酸ジベンジルエステル、シュウ
酸−ジ−ｐ−メチルベンジルエステル、シュウ酸−ジ−
ｐ−クロルベンジルエステル、テレフタル酸ジメチルエ
ステル、テレフタル酸ジブチルエステル、テレフタル酸
ジベンジルエステル、イソフタル酸ジブチルエステル、
１−ヒドロキシナフトエ酸フェニルエステル及び各種公
知の熱可融性物質等が挙げられる。中でも１，２−ジ
（３−メチルフェノキシ）エタン、１，２−ジフェノキ
シエタン、１−フェノキシ−２−（４−メチルフェノキ
シ）エタンが特に好ましい。増感剤の使用量は特に限定
されないが、一般に呈色剤１００重量部に対して４００
重量部以下程度の範囲で調節するのが望ましい。In the present invention, a sensitizer and a preservative improving agent for recorded images may be used in combination according to the purpose. Specific examples of the sensitizer include stearic acid amide, stearic acid methylenebisamide, oleic acid amide, palmitic acid amide, coconut fatty acid amide and other fatty acid amides, 1,2-di (3-methylphenoxy) ethane, 1,
2-diphenoxyethane, 1-phenoxy-2- (4-
Methylphenoxy) ethane, parabenzyl biphenyl,
Naphthylbenzyl ether, benzyl-4-methylthiophenyl ether, 1-hydroxy-2-naphthoic acid phenyl ester, oxalic acid dibenzyl ester, oxalic acid-di-p-methylbenzyl ester, oxalic acid-di-
p-chlorobenzyl ester, terephthalic acid dimethyl ester, terephthalic acid dibutyl ester, terephthalic acid dibenzyl ester, isophthalic acid dibutyl ester,
Examples thereof include 1-hydroxynaphthoic acid phenyl ester and various known heat-fusible substances. Among them, 1,2-di (3-methylphenoxy) ethane, 1,2-diphenoxyethane and 1-phenoxy-2- (4-methylphenoxy) ethane are particularly preferable. The amount of the sensitizer used is not particularly limited, but is generally 400 with respect to 100 parts by weight of the color former.
It is desirable to adjust within the range of not more than parts by weight.

【００１２】また、記録像の保存性改良剤としては、例
えば２，２’−メチレンビス（４−メチル−６−tert−
ブチルフェノール）、４，４’−ブチリデンビス（６−
tert−ブチル−３−メチルフェノール）、２，２’−メ
チレンビス（４−エチル−６−tert−ブチルフェノー
ル）、２，４−ジ−tert−ブチル−３−メチルフェノー
ル、１，１，３−トリス（２−メチル−４−ヒドロキシ
−５−tert−ブチルフェニル）ブタン、１，１，３−ト
リス（５−シクロヘキシル−４−ヒドロキシ−２−メチ
ルフェニル）ブタン、１，３，５−トリス（４−tert−
ブチル−３−ヒドロキシ−２，６−ジメチルベンジル）
イソシアヌル酸等のヒンダードフェノール類、２−
（２’−ヒドロキシ−５’─メチルフェニル）ベンゾト
リアゾール、２−ヒドロキシ−４−ベンジルオキシベン
ゾフェノン等の紫外線吸収剤等が挙げられる。Examples of the preservability improving agent for recorded images include 2,2'-methylenebis (4-methyl-6-tert-).
Butylphenol), 4,4'-butylidene bis (6-
tert-butyl-3-methylphenol), 2,2′-methylenebis (4-ethyl-6-tert-butylphenol), 2,4-di-tert-butyl-3-methylphenol, 1,1,3-tris (2-Methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,1,3-tris (5-cyclohexyl-4-hydroxy-2-methylphenyl) butane, 1,3,5-tris (4 −tert−
Butyl-3-hydroxy-2,6-dimethylbenzyl)
Hindered phenols such as isocyanuric acid, 2-
Examples thereof include ultraviolet absorbers such as (2′-hydroxy-5′-methylphenyl) benzotriazole and 2-hydroxy-4-benzyloxybenzophenone.

【００１３】これらの物質を含む塗布液の調製には、一
般に水を分散媒体とし、ボールミル、アトライター、サ
ンドグラインダー等の撹拌・粉砕機により塩基性染料、
保存性改良剤としてチオサリチル酸、顕色剤そして増感
剤と一緒に又は別々に分散し、塗液として調製される。To prepare a coating liquid containing these substances, water is generally used as a dispersion medium, and a basic dye is prepared by stirring and pulverizing a ball mill, attritor, sand grinder or the like.
It is prepared as a coating liquid by dispersing thiosalicylic acid as a storage stability improving agent, a developer and a sensitizer together or separately.

【００１４】かかる塗液中には、接着剤としてデンプン
類、ヒドロキシエチルセルローズ、メチルセルローズ、
カルボキシメチルセルローズ、ゼラチン、カゼイン、ア
ラビヤゴム、ポリビニルアルコール、ジイソブチレン・
無水マレイン酸共重合体塩、スチレン・無水マレイン酸
共重合体塩、エチレン・アクリル酸共重合体塩、スチレ
ン・アクリル共重合体塩、スチレン・ブタジエン共重合
体塩エマルジョン等が全固形分の１０〜４０重量％、好
ましくは１５〜３０重量％程度用いられる。さらに、塗
液中には各種の助剤を添加することができ、例えばジオ
クチルスルフォコハク酸ナトリウム、ドデシルベンゼン
スルフォン酸ナトリウム、ラウリルアルコール硫酸エス
テル・ナトリウム塩、アルギン酸塩、脂肪酸金属塩など
の分散剤、その他消泡剤、蛍光染料、着色染料などが挙
げられる。In such a coating liquid, starch, hydroxyethyl cellulose, methyl cellulose,
Carboxymethyl cellulose, gelatin, casein, arabic gum, polyvinyl alcohol, diisobutylene
A maleic anhydride copolymer salt, a styrene / maleic anhydride copolymer salt, an ethylene / acrylic acid copolymer salt, a styrene / acrylic copolymer salt, a styrene / butadiene copolymer salt emulsion or the like has a total solid content of 10 -40% by weight, preferably about 15-30% by weight. Furthermore, various auxiliaries can be added to the coating liquid, for example, disodium dioctylsulfosuccinate, sodium dodecylbenzenesulfonate, lauryl alcohol sulfate / sodium salt, alginate, fatty acid metal salt, and other dispersants. , And other defoaming agents, fluorescent dyes, coloring dyes and the like.

【００１５】必要に応じてステアリン酸亜鉛、ステアリ
ン酸カルシウム、ポリエチレンワックス、カルナバロ
ウ、パラフィンワックス、エステルワックスなどの滑
剤、カオリン、クレー、タルク、炭酸カルシウム、焼成
クレー、酸化チタン、珪藻土、微粒子状無水シリカ、活
性白土等の無機顔料を添加することも可能である。If necessary, lubricants such as zinc stearate, calcium stearate, polyethylene wax, carnauba wax, paraffin wax, ester wax, kaolin, clay, talc, calcium carbonate, calcined clay, titanium oxide, diatomaceous earth, fine anhydrous silica, It is also possible to add an inorganic pigment such as activated clay.

【００１６】本発明は、感熱記録層上に水溶性樹脂を主
成分として含む保護層を設けることにより記録象の薬品
等に対する保存性の改善以外に、不透明度を低下させる
効果が得られる。かかる保護層に使用される水溶性樹脂
の具体例としては、例えばデンプン類、ヒドロキシエチ
ルセルロース、メチルセルロース、カルボキシメチルセ
ルロース、ゼラチン、カゼイン、アラビアガム、ポリビ
ニルアルコール、カルボキシ変性ポリビニルアルコー
ル、アセトアセチル基変性ポリビニルアルコール、珪素
変性ポリビニルアルコール、ジイソブチレン・無水マレ
イン酸共重合体塩、スチレン−無水マレイン酸共重合体
塩、エチレン−アクリル酸共重合体塩、スチレン・アク
リル酸共重合体塩、尿素樹脂、メラミン樹脂・アミド樹
脂・ポリウレタン樹脂等が例示できるが、中でもアセト
アセチル基変性ポリビニルアルコール及びカルボキシ変
性ポリビニルアルコールは、強固なフィルムを形成し、
更に透明性に優れているため特に好ましく用いられる。According to the present invention, by providing a protective layer containing a water-soluble resin as a main component on the heat-sensitive recording layer, in addition to improving the preservability of the recording material against chemicals and the like, the effect of lowering the opacity can be obtained. Specific examples of the water-soluble resin used in such a protective layer include starches, hydroxyethyl cellulose, methyl cellulose, carboxymethyl cellulose, gelatin, casein, gum arabic, polyvinyl alcohol, carboxy modified polyvinyl alcohol, acetoacetyl group modified polyvinyl alcohol, Silicon-modified polyvinyl alcohol, diisobutylene / maleic anhydride copolymer salt, styrene / maleic anhydride copolymer salt, ethylene / acrylic acid copolymer salt, styrene / acrylic acid copolymer salt, urea resin, melamine resin / Examples include amide resins and polyurethane resins. Among them, acetoacetyl group-modified polyvinyl alcohol and carboxy-modified polyvinyl alcohol form a strong film,
Furthermore, since it is excellent in transparency, it is particularly preferably used.

【００１７】保護層中には、印刷適性やステッキングを
より改善するために、必要に応じて顔料を添加すること
ができるが、その具体例としては、炭酸カルシウム、酸
化亜鉛、酸化アルミニウム、二酸化チタン、二酸化珪
素、水酸化アルミニウム、硫酸バリウム、硫酸亜鉛、タ
ルク、カオリン、クレー、焼成カオリン、コロイダルシ
リカ等の無機顔料、スチレンマイクロボール、ナイロン
パウダー、ポリエチレンパウダー、尿素・ホルマリン樹
脂フィラー、生デンプン粒子等の有機顔料等が挙げられ
る。その使用量は一般にバインダー成分１００重量部に
対して５〜３００重量部程度の範囲で調製するのが望ま
しい。If necessary, a pigment may be added to the protective layer in order to further improve printability and sticking. Specific examples thereof include calcium carbonate, zinc oxide, aluminum oxide, and dioxide. Inorganic pigments such as titanium, silicon dioxide, aluminum hydroxide, barium sulfate, zinc sulfate, talc, kaolin, clay, calcined kaolin, colloidal silica, styrene microballs, nylon powder, polyethylene powder, urea / formalin resin filler, raw starch particles And other organic pigments. In general, it is desirable that the amount used is in the range of about 5 to 300 parts by weight with respect to 100 parts by weight of the binder component.

【００１８】更に、保護層用塗液中には、必要に応じて
ステアリン酸亜鉛、ステアリン酸カルシウム、ポリエチ
レンワックス、カルナバウロ、パラフィンワックス、エ
ステルワックス等の滑剤、ジオクチルスルホコハク酸ナ
トリウム等の界面活性剤（分散剤、湿潤剤）、消泡剤、
カリミョウバンや酢酸アルミニウム等の水溶性多価金属
塩等の各種助剤を適宜添加することもできる。また耐水
性を一層向上させるためにグリオキザール、ホウ酸、ジ
アルデヒドデンプン、エポキシ系化合物等の硬化剤を併
用することもできる。Further, in the protective layer coating liquid, lubricants such as zinc stearate, calcium stearate, polyethylene wax, carnaubauro, paraffin wax and ester wax, and surfactants such as sodium dioctylsulfosuccinate (dispersion) may be added, if necessary. Agent, wetting agent), defoaming agent,
Various auxiliaries such as water-soluble polyvalent metal salts such as potassium alum and aluminum acetate may be appropriately added. Further, in order to further improve the water resistance, a curing agent such as glyoxal, boric acid, dialdehyde starch, and an epoxy compound can be used in combination.

【００１９】感熱記録層及び保護層の形成方法について
は特に限定されず、例えばエアーナイフコーテイング、
バリバーブレードコーテイング、ピュアーブレードコー
テイング、ロッドブレードコーテイング、ショートドウ
エルコーテイング、カーテンコーテイング、ダイコーテ
イング等の適当な塗布方法により記録層塗液を支持体上
に塗布・乾燥した後、更に保護層用塗液を記録層上に塗
布・乾燥する等の方法で形成される。また、記録層用塗
液の塗布量は乾燥重量で２〜１２ｇ／ｍ² 、好ましくは
３〜１０ｇ／ｍ² 程度、保護層用塗液の塗布量は乾燥重
量で０．１〜２０ｇ／ｍ² 、好ましくは０．５〜１０ｇ
／ｍ² 程度の範囲で調節される。尚、必要に応じて支持
体に下塗り層を設けたり、感熱記録層、保護層各層塗抹
後にスーパーカレンダー掛け等の平滑化処理を施すな
ど、感熱記録紙製造分野における各種の公知技術が必要
に応じて付加しえるものである。The method for forming the heat-sensitive recording layer and the protective layer is not particularly limited, and examples include air knife coating and
After coating and drying the recording layer coating liquid on the support by an appropriate coating method such as varibar blade coating, pure blade coating, rod blade coating, short dwell coating, curtain coating, die coating, etc. Is formed on the recording layer by coating and drying. The coating amount of the recording layer coating liquid for dry weight 2~12g / m ^2, preferably from 3 to 10 g / m ² approximately, 0.1 to 20 g / m coating amount of the protective layer coating composition in a dry weight ² , preferably 0.5-10 g
It is adjusted in the range of about / m ² . If necessary, various known techniques in the field of heat-sensitive recording paper production may be used, such as providing an undercoat layer on the support or applying a smoothing treatment such as supercalendering after coating each layer of the heat-sensitive recording layer and protective layer. Can be added.

【００２０】[0020]

【実施例】以下に実施例を示し、本発明をより具体的に
説明するが、勿論これらに限定されるものではない。ま
た、特に断らない限り例中の部および％はそれぞれ重量
部および重量％を示す。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. Unless otherwise specified, "parts" and "%" in the examples mean "parts by weight" and "% by weight" respectively.

【００２１】〔実施例１〕 Ａ液調製 ３−ジ（ｎ−ブチル）アミノ−６−メチル−７−フェニ
ルアミノフルオラン、１０部、１，２−ジ（３−メチル
フェノキシ）エタン２５部、メチルセルロースの５％水
溶液５部、および水６０部からなる組成物をサンドグラ
インダーで平均粒子径が１μｍとなるまで粉砕した。Example 1 Preparation of Solution A 3-di (n-butyl) amino-6-methyl-7-phenylaminofluorane 10 parts, 1,2-di (3-methylphenoxy) ethane 25 parts, A composition consisting of 5 parts of a 5% aqueous solution of methyl cellulose and 60 parts of water was pulverized with a sand grinder until the average particle size became 1 μm.

【００２２】 Ｂ液調製 ４，４’−イソプロピリデンジフェノール３５部、メチ
ルセルロースの５％水溶液５部、および水６０部からな
る組成物をサンドグラインダーで平均粒子径が２μｍと
なるまで粉砕した。Preparation of Solution B A composition consisting of 35 parts of 4,4′-isopropylidenediphenol, 5 parts of a 5% aqueous solution of methylcellulose, and 60 parts of water was pulverized with a sand grinder until the average particle size became 2 μm.

【００２３】 グラシン紙の製造 カナデイアンスタンダードフリーネス（以下ＣＳＦと記
す）が２００mlまで粘状叩解された広葉樹と針葉樹（広
葉樹と針葉樹の重量比が８対２）のクラフトパルプスラ
リー中に、パルプ固形量に対してロジンエマルジョンサ
イズ剤１．５重量％、メタクリル酸メチル−酢酸ビニル
共重合体エマルジョン２５重量％を順次添加・分散し、
硫酸バンドで紙料のｐＨを４．５に調整し、抄紙後、紙
水分が１５％の状態で、多段のスーパーカレンダーを通
して米坪６０ｇ／ｍ² の半透明のグラシン紙を得た。得
られたグラシン紙の全固形量に対してメタクリル酸メチ
ル−酢酸ビニル共重合体が１８重量％含まれていた。Manufacture of glassine paper Canadian standard freeness (hereinafter referred to as CSF) is viscously beaten up to 200 ml in a kraft pulp slurry of hardwood and softwood (the weight ratio of hardwood and softwood is 8: 2), and the solid pulp content is 1.5% by weight of rosin emulsion sizing agent and 25% by weight of methyl methacrylate-vinyl acetate copolymer emulsion were sequentially added and dispersed,
The pH of the stock was adjusted to 4.5 with a sulfuric acid band, and after papermaking, a translucent glassine paper having a basis weight of 60 g / m ² was obtained through a multi-stage super calender with a paper moisture content of 15%. The glassine paper thus obtained contained 18% by weight of methyl methacrylate-vinyl acetate copolymer with respect to the total solid content.

【００２４】 感熱記録層の形成 Ａ液１００部、Ｂ液３０部、ポリビニルアルコール（商
品名：ＰＶＡ１１７、クラレ社製）の１０％水溶液１０
０部、軽質炭酸カルシウム２部、および水２７部を混合
・攪拌して得られた塗液を上記のグラシン紙上に、乾燥
後の塗布量が４ｇ／ｍ² となるように塗布乾燥し、感熱
記録層を形成した。Formation of Thermosensitive Recording Layer 100 parts of solution A, 30 parts of solution B, 10% aqueous solution of polyvinyl alcohol (trade name: PVA117, manufactured by Kuraray Co., Ltd.) 10
A coating solution obtained by mixing and stirring 0 parts, 2 parts of light calcium carbonate, and 27 parts of water was applied onto the above-mentioned glassine paper so that the applied amount after drying was 4 g / m ^2, and dried to obtain heat. A recording layer was formed.

【００２５】 保護層の形成 アセトアセチル変性ポリビニルアルコールの１０％水溶
液３００部、ステアリン酸亜鉛の３０％分散液１５部、
水５０部、及びグリオキザールの１０％水溶液５部から
なる組成物を混合・攪拌して得られた保護層形成用塗液
を上記の感熱記録層上に、乾燥後の塗布量が１．５ｇ／
ｍ² となるように塗布乾燥し、スーパーカレンダー処理
して感熱記録紙を得た。Formation of Protective Layer 300 parts of a 10% aqueous solution of acetoacetyl-modified polyvinyl alcohol, 15 parts of a 30% dispersion of zinc stearate,
A coating solution for forming a protective layer obtained by mixing and stirring a composition comprising 50 parts of water and 5 parts of a 10% aqueous solution of glyoxal was coated on the heat-sensitive recording layer at a coating amount of 1.5 g / dry.
It was coated and dried so as to have a surface area of m ^2, and subjected to a super calendar treatment to obtain a heat-sensitive recording paper.

【００２６】〔実施例２〕実施例１のグラシン紙の製造
において、メタクリル酸メチル−酢酸ビニル共重合体エ
マルジョンの代わりにスチレン−酢酸ビニル共重合体エ
マルジョンを添加した以外は、実施例１と同様にして感
熱記録紙を得た。Example 2 Same as Example 1 except that a styrene-vinyl acetate copolymer emulsion was added instead of the methyl methacrylate-vinyl acetate copolymer emulsion in the production of the glassine paper of Example 1. A thermosensitive recording paper was obtained.

【００２７】〔実施例３〕 グラシン紙の製造 カナデイアンスタンダードフリーネス（以下ＣＳＦと記
す）が２２０mlまで粘状叩解された広葉樹クラフトパル
プスラリー中に、パルプ固形量に対してロジンエマルジ
ョンサイズ剤１．５重量％を添加し、硫酸バンドで紙料
のｐＨを４．５に調整して抄紙を行い、抄紙機上のサイ
ズプレス部において、固形濃度が３０％のスチレン−メ
タクリル酸ブチル共重合体エマルジョンをサイズプレス
し、紙水分が１５％の状態で、多段のスーパーカレンダ
ーを通して米坪６０ｇ／ｍ² の半透明のグラシン紙を得
た。得られたグラシン紙の全固形量に対してスチレン−
メタクリルブチル共重合体が１０重量％含まれていた。[Example 3] Production of glassine paper [0027] In a hardwood kraft pulp slurry which was viscously beaten to a Canadian standard freeness (hereinafter referred to as CSF) of up to 220 ml, a rosin emulsion sizing agent was added to a pulp solid amount of 1.5. Wt% was added, and the pH of the stock was adjusted to 4.5 with a sulfuric acid band to perform papermaking, and a styrene-butyl methacrylate copolymer emulsion having a solid concentration of 30% was prepared in the size press section on the papermaking machine. A size-pressed paper was passed through a multi-stage super calender with a paper moisture content of 15% to obtain a translucent glassine paper having a weight of 60 g / m ² of tsubo. Styrene-based on the total solids of the resulting glassine paper
The content of methacrylbutyl copolymer was 10% by weight.

【００２８】 感熱記録紙の製造 上記のグラシン紙を使用した以外は、実施例１と同様に
して感熱記録層および保護層を形成し、感熱記録体を得
た。Production of Thermal Recording Paper The thermal recording layer and the protective layer were formed in the same manner as in Example 1 except that the above glassine paper was used to obtain a thermal recording material.

【００２９】〔実施例４〕実施例３のグラシン紙の製造
において、スチレン−メタクリル酸ブチル共重合体エマ
ルジョンの代わりにポリウレタン系エマルジョンを用い
た以外は、実施例３と同様にして感熱記録紙をえた。Example 4 A thermal recording paper was prepared in the same manner as in Example 3 except that a polyurethane emulsion was used in place of the styrene-butyl methacrylate copolymer emulsion in the production of the glassine paper of Example 3. I got it.

【００３０】〔比較例１〕実施例１のグラシン紙の製造
において、メタクリル酸メチル−酢酸ビニル共重合体エ
マルジョンの代わりに、ポリビニルアルコールを用いた
以外は、実施例１と同様にして感熱記録紙を得た。Comparative Example 1 A thermosensitive recording paper was prepared in the same manner as in Example 1 except that polyvinyl alcohol was used in place of the methyl methacrylate-vinyl acetate copolymer emulsion in the production of the glassine paper of Example 1. Got

【００３１】〔比較例２〕 グラシン紙の製造 実施例３のグラシン紙の製造において、固形濃度３０％
のスチレン−メタクリル酸ブチル共重合体エマルジョン
の代わりに酸化デンブンの２０％水溶液を２０mlサイズ
プレスし、紙水分が１５％の状態で、多段のスーパーカ
レンダーを通して米坪６０ｇ／ｍ² の半透明のグラシン
紙を得た。Comparative Example 2 Production of Glassine Paper In the production of glassine paper of Example 3, the solid concentration was 30%.
Instead of the styrene-butyl methacrylate copolymer emulsion of 20 ml, 20 ml of 20% aqueous solution of denbun oxide is pressed, and the moisture content of the paper is 15%. Through a multi-stage super calender, 60 g / m ² of translucent glassine is used. Got the paper.

【００３２】 感熱記録紙の製造 上記のグラシン紙を使用した以外は、実施例１と同様に
して感熱記録層および保護層を形成し、感熱記録体を得
た。Production of Thermal Recording Paper The thermal recording layer and the protective layer were formed in the same manner as in Example 1 except that the above glassine paper was used to obtain a thermal recording material.

【００３３】かくして得られた感熱記録紙について以下
の品質評価テストを行い、その結果を表１に示した。 (1)〔記録濃度〕 感熱記録用シミュレーター（大倉電気社製、ＴＨ−ＰＭ
Ｄ型）を使用し、印加ヘッドエネルギ−０．４ｍｊ／ｄ
ｏｔの条件で記録し、得られた記録像の濃度をマクベス
濃度計（マクベス社製、ＲＤ−９１４）で測定した。 (2)〔不透明度〕 ＪＩＳ−Ｐ８１３８に基ずいて測定した。 (3)〔耐折強度〕 ＪＩＳ−Ｐ８１１５に基ずいて測定した。The heat-sensitive recording paper thus obtained was subjected to the following quality evaluation tests, and the results are shown in Table 1. (1) [Recording density] Thermal recording simulator (Okura Electric Co., TH-PM
D type), and applied head energy-0.4 mj / d
Recording was performed under the condition of ot, and the density of the obtained recorded image was measured with a Macbeth densitometer (RD-914, manufactured by Macbeth Co.). (2) [Opacity] Measured based on JIS-P8138. (3) [Folding endurance] It was measured based on JIS-P8115.

【００３４】(4)〔記録像の保存性〕 感熱記録用シミュレーターで記録後の感熱記録紙を４０
℃−９０％ＲＨ条件下に４８時間放置し、記録部及び地
肌部のカブリをマクベス濃度計で測定した。 (5)〔感熱記録紙のジアゾ複写適性〕 ＴＨＥＲＭＡＬ ＰＬＯＴＴＥＲ〔ＬＴＸ−１２０ ロ
−ランド社製〕で記録された感熱記録紙をマスターとし
て、ジアゾ複写紙にジアゾコピー機〔リコー社製、リコ
ピーＳＵＰＥＲ ＤＲＹ １００型〕で複写し、得られ
た複写像および地肌部の濃度をマクベス濃度計で測定し
た。(4) [Preservation of recorded image] 40 times the heat-sensitive recording paper after recording with a heat-sensitive recording simulator.
After left for 48 hours under the condition of 90 ° C.-90% RH, the fog on the recording part and the background part was measured by a Macbeth densitometer. (5) [Diazo copy suitability of thermosensitive recording paper] Using a thermosensitive recording paper recorded by THERMAL PLOTER (LTX-120 Roland Co.) as a master, a diazo copying machine (manufactured by Ricoh Co., Ricopy SUPER DRY) was used as a master. 100 type], and the resulting copy image and the density of the background part were measured with a Macbeth densitometer.

【００３５】[0035]

【表１】 [Table 1]

【００３６】[0036]

【発明の効果】表１の結果から明らかなように、本発明
の感熱記録紙は透明性が高く、耐折強度及び記録像の保
存性に優れた第二原図用の感熱記録紙であった。As is clear from the results shown in Table 1, the thermosensitive recording paper of the present invention was a thermosensitive recording paper for the second original, which had high transparency and excellent folding endurance and storability of recorded images. .

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】基紙上に、無色ないし淡色の塩基性染料と
呈色剤とを含有する感熱記録層、および保護層を順次設
けた感熱記録紙において、基紙として、合成樹脂エマル
ジョンが基紙の全固形量に対して５〜３０重量％内添ま
たはサイズプレスされたグラシン紙を用いたことを特徴
とする感熱記録紙。1. A thermosensitive recording paper in which a thermosensitive recording layer containing a colorless or light-colored basic dye and a coloring agent and a protective layer are sequentially provided on the base paper, and a synthetic resin emulsion is used as the base paper. 5-30% by weight based on the total solid content of glassine paper internally added or size-pressed. 【請求項２】合成樹脂エマルジョンが、アクリルエステ
ル系樹脂エマルジョンである請求項１記載の感熱記録
紙。2. The thermal recording paper according to claim 1, wherein the synthetic resin emulsion is an acrylic ester resin emulsion.