JPH0729879B2 - Translucent magnetic yttrium iron garnet film and method for producing the same - Google Patents
Translucent magnetic yttrium iron garnet film and method for producing the sameInfo
- Publication number
- JPH0729879B2 JPH0729879B2 JP2146455A JP14645590A JPH0729879B2 JP H0729879 B2 JPH0729879 B2 JP H0729879B2 JP 2146455 A JP2146455 A JP 2146455A JP 14645590 A JP14645590 A JP 14645590A JP H0729879 B2 JPH0729879 B2 JP H0729879B2
- Authority
- JP
- Japan
- Prior art keywords
- compound
- iron
- yttrium
- organic
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、磁気記録材料、電磁波遮蔽材料、磁気遮蔽材
料、光学機能性磁気材料及びセンサー等に用いられる光
透性磁性イットリウム鉄ガーネット（以下、YIGと略記
する）膜及びその製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a light-transmitting magnetic yttrium iron garnet (hereinafter referred to as a magnetic recording material, an electromagnetic wave shielding material, a magnetic shielding material, an optically functional magnetic material, a sensor, etc.). , YIG) and a manufacturing method thereof.
今日最も広く用いられている酸化物磁性材料は、マグネ
タイトで代表されるスピネル型フェライト、バリウムフ
ェライトで代表されるマグネトプランバイト型フェライ
ト、そしてYIGで代表されるガーネット型フェライトで
ある。この三種類の中でガーネット型フェライトは、使
用される量が非常に少なく、利用のされ方も付加価値の
高い所となっており、単結晶として用いられる例が多い
という特徴がある。The most widely used oxide magnetic materials today are spinel ferrites represented by magnetite, magnetoplumbite ferrites represented by barium ferrite, and garnet ferrites represented by YIG. Among these three types, the garnet-type ferrite is used in a very small amount, is highly value-added, and is often used as a single crystal.
単結晶としてのYIGの利用は、（１）マイクロ波用共鳴
素子、（２）光アイソレーター用素子、（３）磁気バブ
ル用素子である。マイクロ波用共鳴素子は、同調発振
器、同調ろ波器、周波数選択パワーリミッターなどの心
臓部品として、直径1mm以下の球の形で用いられる（特
開昭55−100702、51−86375、58−182302、59−10340
3、103404、60−2576078、62−11303、10102、200709、
256501、特開平01−14082、152802）。光アイソレータ
ー用素子は、YIGの磁気光学結晶に方解石等の偏光子を
組み合わせた形で、ファラデー回転形アイソレーター及
び共鳴形アイソレーターの部品として用いられる（特開
昭55−138711、58−173703、59−−74526、63−13250
3、特開平01−19309、90412）。磁気バルブ用素子は、
ハードバルブ抑制のためバルブ保持層の表面にYIG単結
晶をもうけている（特開昭56−143585）。The use of YIG as a single crystal is as follows: (1) microwave resonance element, (2) optical isolator element, (3) magnetic bubble element. The microwave resonance element is used in the form of a sphere having a diameter of 1 mm or less as a heart component such as a tuned oscillator, a tuned filter, and a frequency selective power limiter (JP-A-55-100702, 51-86375, 58-182302). , 59-10340
3, 103404, 60-2576078, 62-11303, 10102, 200709,
256501, JP-A-01-14082, 152802). The element for an optical isolator is a combination of a YIG magneto-optical crystal and a polarizer such as calcite, and is used as a component of a Faraday rotation type isolator and a resonance type isolator (JP-A-55-138711, 58-173703, 59- −74526, 63−13250
3, JP-A-01-19309, 90412). The element for the magnetic valve is
A YIG single crystal is provided on the surface of the valve holding layer to suppress the hard valve (JP-A-56-143585).
YIG単結晶の育成法は、（１）PbOを主体としたフラック
ス用いて徐冷する方法、（２）PbO以外を主体としたフ
ラックスを用いて徐冷する方法、（３）水熱法、（４）
気相法、（５）溶液引き上げ法等が試みられているが現
在市販されているYIG単結晶は、すべてPbO系フェラック
スを用いて育成されたものである。The YIG single crystal growth method includes (1) a slow cooling method using a flux mainly composed of PbO, (2) a slow cooling method using a flux mainly composed of other than PbO, (3) a hydrothermal method, ( 4)
Although the vapor phase method, (5) solution pulling method and the like have been tried, all the YIG single crystals currently on the market are grown using PbO-based ferrax.
しかし、近年ますます装置の小型化、低コスト化及び量
産化等の要望が増加しているため、YIGの直接薄膜化に
ついて検討が行なわれている。その結果、真空技術の進
歩により、YIG単結晶バルブを使用したデバイスに変わ
るものとして単結晶磁性YIG膜が使われるようになって
きた。However, in recent years, there has been an increasing demand for miniaturization, cost reduction, mass production, etc. of the device, and thus direct thinning of YIG is being studied. As a result, advances in vacuum technology have led to the use of single crystal magnetic YIG films as an alternative to devices that use YIG single crystal valves.
磁性YIG膜の作成法は、（１）真空蒸着法、（２）スパ
ッタリング法、（３）イオンプレーティング法、（４）
イオンビーム蒸着法、（５）イオン注入蒸着法、（６）
常圧・減圧CVD法、（７）プラズマCVD法、（８）MO−CV
D法、（９）光CVD法、（10）レーザーCVD法、（11）液
相エピタキシャル成長法などがある。（１）〜（10）の
方法は、基板に被膜を形成し、適当な雰囲気下の熱処理
で結晶性磁性YIG膜としている。これらの方法は、極め
て多量のエネルギーを消費することや、製造装置が高価
な上、大がかりで量産性に乏しいこと、操作が煩雑で基
板が高融点の物でなければならないことなどの大きな欠
点を持ち、工業的に難点が多くコスト高となる欠点があ
る（特開昭48−99100、49−12398、49−12399、50−904
96、50−119299、52−103385、53−142388、56−14358
5、60−257607）。（11）の液相エピタキシャル成長法
も、（１）〜（10）の磁性YIG膜の作成方法と同様に多
くの育成時間を必要とするため量産性に乏しく、ガドリ
ニウム・ガリウム・ガーネット（Gd3Ga5O12）のような
誘導体基板上に磁性YIG結晶を作成するためコスト高に
なる欠点がある（特開昭55−23661、143009、58−18230
2、59−103403、103404、175201、60−257607、61−224
702、62−11302、11303、200709、224101、234403、250
701、250702、256501、260121、271501、63−10901、10
902、10903、103501、122303、211901、特開平01−1930
9、51901、236724）。従って、（１）〜（11）の方法は
現在までのところ透光性磁性YIG膜を得る方法として利
用するには小型化、低コスト化、量産化の点で限界があ
る。The magnetic YIG film is produced by the following methods: (1) vacuum deposition method, (2) sputtering method, (3) ion plating method, (4)
Ion beam evaporation method, (5) Ion implantation evaporation method, (6)
Atmospheric pressure / decompression CVD method, (7) plasma CVD method, (8) MO-CV
D method, (9) photo CVD method, (10) laser CVD method, (11) liquid phase epitaxial growth method and the like. In the methods (1) to (10), a film is formed on the substrate and heat-treated in an appropriate atmosphere to obtain a crystalline magnetic YIG film. These methods have major drawbacks such as consumption of an extremely large amount of energy, expensive manufacturing equipment, large scale and poor mass productivity, complicated operation, and a substrate having a high melting point. However, it has many drawbacks in terms of industrial difficulty and high cost (JP-A-48-99100, 49-12398, 49-12399, 50-904).
96, 50-119299, 52-103385, 53-142388, 56-14358
5, 60-257607). The liquid phase epitaxial growth method of (11) also requires a large amount of growth time as in the method of forming the magnetic YIG film of (1) to (10), and thus has poor mass productivity, and gadolinium gallium garnet (Gd 3 Ga Since magnetic YIG crystals are formed on a dielectric substrate such as 5 O 12 ), there is a drawback that the cost becomes high (Japanese Patent Laid-Open Nos. 55-23661, 143009, 58-18230).
2, 59-103403, 103404, 175201, 60-257607, 61-224
702, 62-11302, 11303, 200709, 224101, 234403, 250
701, 250702, 256501, 260121, 271501, 63-10901, 10
902, 10903, 103501, 122303, 211901, JP-A-01-1930
9, 51901, 236724). Therefore, the methods (1) to (11) are so far limited in terms of downsizing, cost reduction, and mass production to be used as a method for obtaining a translucent magnetic YIG film.
本発明は、従来の技術の問題点を除去、克服すると共
に、さらに高度で新しい機能を発揮する透光性磁性YIG
膜及びその製造方法を提供することをその課題とするも
のである。The present invention eliminates and overcomes the problems of the conventional technology, and at the same time, exhibits translucent magnetic YIG that exhibits new and advanced functions.
It is an object of the present invention to provide a film and a manufacturing method thereof.
本発明者らは、前記課題を解決すべく、鋭意研究を重ね
た結果、本発明をなすに至った。The present inventors have completed the present invention as a result of intensive studies to solve the above problems.
すわち、本発明によれば、基体上に形成された有機化合
物が炭素数10以上の1,2−ジオール又はオキシカルボン
酸である可溶性有機鉄イットリウム化合物膜の熱分解に
より形成された透光性磁性イットリウム鉄ガーネット膜
が提供される。That is, according to the present invention, the organic compound formed on the substrate is a translucent film formed by thermal decomposition of a soluble organic iron yttrium compound film in which the organic compound is a 1,2-diol or oxycarboxylic acid having 10 or more carbon atoms. A magnetic yttrium iron garnet film is provided.
また、本発明によれば、有機化合物が炭素数10以上の1,
2−ジオール又はオキシカルボン酸である可溶性有機鉄
イットリウム化合物の有機溶媒溶液を基体上に塗布し、
乾燥させ、アニール処理して熱分解することを特徴とす
る透光性磁性イットリウム鉄ガーネット膜の製造方法が
提供される。Further, according to the present invention, the organic compound has 1, 10 or more carbon atoms,
A solution of a soluble organic iron yttrium compound, which is a 2-diol or oxycarboxylic acid, in an organic solvent is coated on a substrate,
Provided is a method for producing a translucent magnetic yttrium iron garnet film, which comprises drying, annealing and thermal decomposition.
本明細書で言う有機鉄イットリウム化合物とは、可溶剤
の鉄化合物及びイットリウム化合物と含酸素有機化合物
である、炭素数10以上のポリオールとがその酸素原子を
介して反応結合した化合物を意味する。また、この場合
の反応結合には、共有結合の他、錯結合も包含される。The organic iron yttrium compound referred to in the present specification means a compound in which an iron compound and a yttrium compound which are solubilizers and a polyol having 10 or more carbon atoms, which is an oxygen-containing organic compound, are reactively bonded via the oxygen atom. Further, the reactive bond in this case includes a complex bond as well as a covalent bond.
本発明で用いる有機鉄イットリウム化合物は、有機溶媒
可溶性のものであり、このようなもとしては、一般的に
は、炭素数10以上のポリオールとオキシカルボン酸と鉄
化合物及びイットリウム化合物とが反応した生成物が挙
げられるが、特に、炭素数10以上の1,2−ジオールやオ
キシカルボン酸と鉄化合物及びイットリウム化合物との
反応生成物が好ましい。有機溶媒に対して不溶性の有機
鉄イットリウム化合物たとえば後記する比較例１〜５に
示されるような低級ポリオールを有機成分とする有機鉄
イットリウム化合物を用いても、基体上に均質な塗膜を
形成することができず、目的とする透光性YIG膜を得る
ことはできない。The organic iron yttrium compound used in the present invention is soluble in an organic solvent, and as such, generally, a polyol having 10 or more carbon atoms, an oxycarboxylic acid, an iron compound and a yttrium compound are reacted. Examples of the reaction product include a reaction product of a 1,2-diol having 10 or more carbon atoms or an oxycarboxylic acid with an iron compound and a yttrium compound. Even when an organic iron yttrium compound insoluble in an organic solvent, for example, an organic iron yttrium compound containing a lower polyol as an organic component as shown in Comparative Examples 1 to 5 below is used, a uniform coating film is formed on a substrate. Therefore, the desired transparent YIG film cannot be obtained.
本発明で用いる有機鉄イットリウム化合物の有機化合物
成分として用いるポリオールとしては、価格、入手のし
やすさ及び作業性などから、1,2−デカンジオール及び
1,2−ドデカンジオールが特に優れている。As the polyol used as the organic compound component of the organic iron yttrium compound used in the present invention, 1,2-decanediol and 1,2-decanediol can be used in view of price, availability and workability.
1,2-dodecanediol is particularly excellent.
オキシカルボン酸は特に限定されるものではないが、価
格、入手のしやすさ及び作業性などから選ばれ、例えば
クエン酸、酒石酸、リンゴ酸、乳酸、テトラヒドロキシ
コハク酸、デソキサン酸、タルトロン酸、グリコール
酸、グリセリン酸などを挙げることができる。The oxycarboxylic acid is not particularly limited, but is selected from price, availability and workability, and examples thereof include citric acid, tartaric acid, malic acid, lactic acid, tetrahydroxysuccinic acid, desoxanoic acid, tartronic acid, Examples thereof include glycolic acid and glyceric acid.
有機鉄イットリウム化合物の有機化合物成分を形成する
前記有機化合物は、単独でも二種以上の混合物としても
使用でき、その添加量は鉄化合物とイットリウム化合物
の全量に対して一倍モル以上の使用でよい。The organic compound forming the organic compound component of the organic iron yttrium compound can be used alone or as a mixture of two or more kinds, and the addition amount thereof may be 1 time mol or more with respect to the total amount of the iron compound and the yttrium compound. .
鉄化合物及びイットリウム化合物は溶媒に溶解し易く、
上記含酸素有機化合物と所望の化合物を形成するもので
あればいずれも使用可能であるが、一般的には価格、使
い易さなどの点から、鉄化合物としては、硝酸鉄、塩化
鉄、酢酸鉄、アセチルアセトン鉄（III）などの鉄塩や
キレート化合物が、イットリウム化合物としては、硝酸
イットリウム、塩化イットリウム、酢酸イットリウム、
アセチルアセトンイットリウムなどのイットリウム塩や
キレート化合物が選ばれる。鉄化合物とイットリウム化
合物との使分割合は、鉄化合物１モルに対してイットリ
ウム化合物0.05〜2.0モル、好ましくは0.4〜0.8モルの
割合である。Iron compounds and yttrium compounds are easily dissolved in the solvent,
Any compound can be used as long as it forms a desired compound with the oxygen-containing organic compound, but in general, from the viewpoint of price, ease of use, etc., the iron compound is iron nitrate, iron chloride, acetic acid. Iron salts such as iron and acetylacetone iron (III) and chelate compounds can be used as yttrium compounds, including yttrium nitrate, yttrium chloride, yttrium acetate,
A yttrium salt such as yttrium acetylacetone or a chelate compound is selected. The proportion of the iron compound and the yttrium compound used is 0.05 to 2.0 moles, preferably 0.4 to 0.8 moles, of the yttrium compound relative to 1 mole of the iron compound.
前記有機鉄イットリウム化合物を製造するには、まず原
料の鉄化合物、イットリウム化合物及び含酸素有機化合
物を有機溶媒に溶解する。反応温度は、本反応が進行す
る温度であればいかなる温度でもよいが、反応速度や使
用する溶媒の沸点はなどの関係で適当に選ぶ。一般に
は、反応は、70〜120℃、好ましくは100〜120℃で１〜
５時間反応後、120〜150℃、好ましくは120〜140℃で１
〜５時間反応させ、徐々に有機溶媒を留去しながら濃縮
するように行うのが良い。150℃以上は有機鉄イットリ
ウム化合物の分解を招くおそれがあるので好ましくな
い。さらに過剰の含酸素有機化合物を油浴温度130℃以
下、好ましくは120℃以下で減圧留去することにより均
一で均質な粘性のある有機鉄イットリウム化合物を製造
することがきる。なお、本発明法によって透光性磁性YI
G膜を製造する場合、原料の有機鉄イットリウム化合物
中に多少の含酸素有機化合物が残留しても膜の製造には
支障はなく、含酸素有機化合物の使用量が比較的少量の
場合は、これらを留去することなく次工程へ進んでも大
きな支障はない。To produce the organic iron yttrium compound, first, the raw material iron compound, yttrium compound, and oxygen-containing organic compound are dissolved in an organic solvent. The reaction temperature may be any temperature as long as the reaction proceeds, but is appropriately selected depending on the reaction rate and the boiling point of the solvent used. Generally, the reaction is carried out at 70-120 ° C., preferably 100-120 ° C.
After reacting for 5 hours, 120 ~ 150 ℃, preferably 120 ~ 140 ℃ 1
It is advisable to carry out the reaction for ˜5 hours and to concentrate while gradually distilling off the organic solvent. A temperature of 150 ° C or higher is not preferable because it may cause decomposition of the organic iron yttrium compound. Further, by distilling off excess oxygen-containing organic compound under reduced pressure at an oil bath temperature of 130 ° C. or lower, preferably 120 ° C. or lower, a uniform and homogeneous viscous organic iron yttrium compound can be produced. In addition, according to the method of the present invention, the transparent magnetic YI
When producing the G film, even if some oxygen-containing organic compound remains in the raw material organic iron yttrium compound, there is no hindrance to the production of the film, and if the amount of the oxygen-containing organic compound used is relatively small, There is no major obstacle to proceeding to the next step without distilling these.
上記有機鉄イットリウム化合物の製造時に用いられる有
機溶媒は、原料の鉄塩、イットリウム化合物及び含酸素
有機化合物を溶解するものであれば特に規定されるもの
ではないが、沸点が70〜150℃、好ましくは100〜120℃
の範囲にある低級アルコール、ケトン、ジオキサン及び
これらの混合溶媒がよい。このようなものとしては、例
えば、メタノール、エタノール、１−プロパノール、２
−プロパノール、１−ブタノール、２−ブタノール、is
o−ブタノール、tert−ブタノール、１−ペンタノー
ル、２−メトキシエタノール、２−エトキシエタノー
ル、メチルエチルケトン、２−ペンタノン、メチルイソ
ブチルケトン、ジオキサンなどが挙げられる。The organic solvent used in the production of the organic iron yttrium compound is not particularly specified as long as it dissolves the raw material iron salt, the yttrium compound and the oxygen-containing organic compound, but the boiling point is 70 to 150 ° C, preferably Is 100 to 120 ° C
Lower alcohols, ketones, dioxane and mixed solvents thereof in the range of are preferable. Examples of such substances include methanol, ethanol, 1-propanol, and 2
-Propanol, 1-butanol, 2-butanol, is
Examples include o-butanol, tert-butanol, 1-pentanol, 2-methoxyethanol, 2-ethoxyethanol, methyl ethyl ketone, 2-pentanone, methyl isobutyl ketone, dioxane and the like.
本発明によれば、磁性YIG膜は有機鉄イットリウム化合
物を基体に塗布し、焼成することによって形成される。
塗布の段階では、磁性YIG膜が均一かつ均質にできるよ
うに有機鉄イットリウム化合物に流動性を付与するのが
好ましい。また、前記反応で得られる有機鉄イットリウ
ム化合物は、粘性が高く流動性が悪いためこの点から
も、有機鉄イットリウム化合物を有機溶媒に溶解希釈し
て塗布するのが好ましい。このとき使用する有機溶媒
は、有機鉄イットリウム化合物が溶解すればいずれのも
のでも良いが、入手の容易さ及び価格などから一般には
低級アルコール、ハロゲン化炭化水素、脂肪族炭化水
素、芳香族炭化水素などが選ばれる。具体的に例示する
と、メタノール、エタノール、１−プロパノール、２−
プロパノール、クロロホルム、四塩化炭素、1,2−ジク
ロロエタン、ベンゼン、トルエン、キシレン、ヘキサ
ン、ペンタン、２−メトキシエタノール、２−エトキシ
エタノールなどが挙げられるが、これらの溶媒に限定さ
れるものではない。According to the present invention, the magnetic YIG film is formed by applying an organic iron yttrium compound on a substrate and baking the same.
At the coating stage, it is preferable to impart fluidity to the organic iron yttrium compound so that the magnetic YIG film can be made uniform and uniform. In addition, since the organic iron yttrium compound obtained by the above reaction has high viscosity and poor fluidity, it is preferable to dissolve and dilute the organic iron yttrium compound in the organic solvent and to apply it also from this point. The organic solvent used at this time may be any one as long as the organic iron yttrium compound is dissolved, but in general, lower alcohols, halogenated hydrocarbons, aliphatic hydrocarbons and aromatic hydrocarbons are used because of their availability and price. Is selected. Specific examples include methanol, ethanol, 1-propanol, 2-
Examples thereof include propanol, chloroform, carbon tetrachloride, 1,2-dichloroethane, benzene, toluene, xylene, hexane, pentane, 2-methoxyethanol, 2-ethoxyethanol and the like, but are not limited to these solvents.
基体上に有機鉄イットリウム化合物膜を形成するための
塗布方法は、回転する基体のうえに有機鉄イットリウム
化合物の溶液を滴下し、回転時の遠心力によって塗布す
るスピンコート法でもよいし、基台を有機鉄イットリウ
ム化合物の溶液に浸すことによるディップ法でも良い
が、大面積に塗布する場合はスピンコート法で塗布する
方が均一性に優れた膜が得られ易い傾向にある。The coating method for forming the organic iron yttrium compound film on the substrate may be a spin coating method in which a solution of the organic iron yttrium compound is dropped on a rotating substrate and is applied by centrifugal force during rotation, or a base. The method may be a dipping method in which is immersed in a solution of an organic iron yttrium compound, but when it is applied to a large area, a spin coating method tends to give a film with excellent uniformity.
透光性磁性YIG膜とする最終段階のアニール処理は、塗
布で得られた有機鉄イットリウム化合物の薄膜を空気雰
囲気下、室温〜1400℃、好ましくは100〜1000℃の範囲
で多段階昇温させ、熱処理することによって行われる。
アニール処理の最終温度は、1000℃、好ましくは800〜1
000℃の範囲である。アニール処理開始温度は室温〜100
℃であるが、特に制約されない。最終アニール処理温度
までの１分間当りの平均昇温速度は、１〜40℃、好まし
くは５〜10℃である。The final stage annealing treatment for the transparent magnetic YIG film is carried out by heating the thin film of the organic iron yttrium compound obtained by coating in an air atmosphere at room temperature to 1400 ° C, preferably in a range of 100 to 1000 ° C. , By heat treatment.
The final temperature of the annealing treatment is 1000 ° C, preferably 800-1
It is in the range of 000 ° C. Annealing start temperature is room temperature to 100
It is ℃, but is not particularly limited. The average rate of temperature rise per minute up to the final annealing temperature is 1 to 40 ° C, preferably 5 to 10 ° C.
以上の操作で所望の基板上に透光性磁性YIG膜を形成さ
せることができ、溶液濃度の調整で膜厚も変えられる
が、一回の操作で好みの膜厚を得ることができない場合
は、塗布とアニール処理を繰り返せばよい。By the above operation, the translucent magnetic YIG film can be formed on the desired substrate, and the film thickness can be changed by adjusting the solution concentration, but if the desired film thickness cannot be obtained by one operation, The coating and annealing treatment may be repeated.
本発明の透光性磁性YIG膜は、少なくとも300Åの膜厚を
有するものであり、一般的には、300Å〜１μｍの膜厚
を有するものである。本発明の透光性磁性YIG膜は、こ
のような膜厚においてもすぐれた透光性を有し、可視光
線に対して高い光線透過率を示す。例えば、本発明の磁
性YIG膜は、300〜5000Åの膜厚において、可視光線であ
る波長700nmの光線に対し、少なくとも50％の光線透過
率を示す。The translucent magnetic YIG film of the present invention has a film thickness of at least 300Å, and generally has a film thickness of 300Å to 1 µm. The translucent magnetic YIG film of the present invention has excellent translucency even with such a film thickness, and exhibits a high light transmittance for visible light. For example, the magnetic YIG film of the present invention exhibits a light transmittance of at least 50% with respect to visible light having a wavelength of 700 nm at a film thickness of 300 to 5000 Å.
また、本発明の透光性磁性YIG膜は、良好な磁性特性を
有し、その飽和磁化量は、15KOeの条件で、40〜90emu/g
を示す。Further, the transparent magnetic YIG film of the present invention has good magnetic properties, and its saturation magnetization is 40 to 90 emu / g under the condition of 15 KOe.
Indicates.
本発明では、鉄化合物及びイットリウム化合物を上記含
酸素有機化合物である、炭素数10以上のポリオール又は
オキシカルボン酸と共に有機溶媒に溶解し、基体上に塗
布してから空気中又は酸素中でアニール処理するという
手軽で実用的な方法で透光磁性YIG膜を得ることができ
る。In the present invention, an iron compound and a yttrium compound are dissolved in an organic solvent together with the above oxygen-containing organic compound, a polyol having 10 or more carbon atoms or an oxycarboxylic acid, and applied on a substrate and then annealed in air or oxygen. The transparent magnetic YIG film can be obtained by a simple and practical method.
本発明で用いる含酸素有機化合物は、その特性により、
（１）鉄及びイットリウムと基体の間を架橋配位子とな
って固定したり、（２）YIGの前駆体である有機鉄イッ
トリウム化合物の構造を鋳型となって規定したり、ある
いは（３）熱処理時の有機鉄イットリウム化合物の重合
を制御したりする効果を示す。このため最終的に基体上
に生じるYIGは、（１）の効果により基体との密着性が
良く、剥がれにくく、シンタリングも起きにくいため光
透過性の良い細かい粒径を保持したものとなる。また
（２）の効果により、トリポタキシー的にYIGの構造が
規定され磁性の発現にきわめて好合となる。さらに
（３）の効果によって、粒子径が揃うので、本発明では
透光性も良く磁性も充分なYIGが極めて簡単に得られる
ことになる。以上のことは、現在までに得ることができ
なかった新事実である。さらに本発明では膜厚を自由か
つ手軽に調節できるという利点を持っている。本発明に
よれば、ガラス、陶磁器、コンクリートなどの表面を容
易に磁性化できるので、光電磁気材料の作成や電子機
器、調理器等の電波遮蔽なども容易に行うことができ、
YIGの用途拡大が期待される。The oxygen-containing organic compound used in the present invention, due to its characteristics,
(1) Fix between iron and yttrium and the substrate as a bridging ligand, (2) define the structure of the organic iron yttrium compound that is the precursor of YIG as a template, or (3) It shows the effect of controlling the polymerization of the organic iron yttrium compound during heat treatment. Therefore, YIG finally generated on the substrate has good adhesion to the substrate due to the effect of (1), is hard to peel off, and is less likely to cause sintering, and therefore has a fine particle size with good light transmittance. Further, due to the effect of (2), the structure of YIG is defined in a tripotaxi manner, which is extremely favorable for the expression of magnetism. Further, the particle size is made uniform by the effect of (3), so that in the present invention, a YIG having excellent translucency and sufficient magnetism can be obtained very easily. The above are new facts that have not been obtained so far. Further, the present invention has an advantage that the film thickness can be adjusted freely and easily. According to the present invention, the surface of glass, porcelain, concrete or the like can be easily magnetized, so that it is possible to easily create a magneto-optical material or an electronic device, a radio wave shield for a cooker, etc.
It is expected that YIG will be used for more applications.
以下、本発明を実施例によりさらに詳細に説明するが、
本発明はこれらの実施例に限定されるものではない。Hereinafter, the present invention will be described in more detail with reference to Examples.
The invention is not limited to these examples.
参考例１ 硝酸鉄（III）９水和物4.04g（0.01M）、硝酸イットリ
ウム６水和物2.30g（0.006M）及び1,2−デカンジオール
27.88g（0.16M）を、50mlのビーカー中で２−メトキシ
エタノール30gに溶解し、ホットプレート上、反応温度
を100〜120℃にコントロールしながら３時間反応させ
た。反応につれ、NO3イオンの分解によるNOｘ発生が起
こり、鉄、イットリウム及び1,2−ドデカンジオールの
有機鉄イットリウム化合物が生成し、溶液の色が、赤茶
色から黒褐色へと変化した。さらに、反応を120〜150℃
で３時間おこない、NOｘの発生を完結させると同時に２
−メトキシエタノールを留去した。最後にロータリーエ
バポレーターを用い、130℃、5mmHg減圧下、過剰の1,2
−ドデカンジオールを留去することにより均一な有機鉄
イットリウム化合物9.83gを得た。Reference Example 1 Iron (III) nitrate nonahydrate 4.04 g (0.01 M), yttrium nitrate hexahydrate 2.30 g (0.006 M) and 1,2-decanediol
27.88 g (0.16 M) was dissolved in 30 g of 2-methoxyethanol in a 50 ml beaker and reacted for 3 hours on a hot plate while controlling the reaction temperature at 100 to 120 ° C. As the reaction proceeded, NO x was generated by decomposition of NO 3 ions, and organic iron yttrium compounds of iron, yttrium and 1,2-dodecanediol were produced, and the color of the solution changed from red brown to black brown. Furthermore, the reaction is performed at 120-150 ℃
2 hours at the same time to complete the generation of NO x
-Methoxyethanol was distilled off. Finally, use a rotary evaporator to remove excess 1,2 at 130 ° C under reduced pressure of 5 mmHg.
-The dodecanediol was distilled off to obtain 9.83 g of a uniform organic iron yttrium compound.
参考例２ 硝酸鉄（III）９水和物4.04g（0.01M）、硝酸イットリ
ウム６水和物2.30g（0.006M）及び1,2−ドデカンジオー
ル32.37g（0.16M）を、50mlのビーカー中で２−メトキ
シエタノール30gに溶解し、ホットプレート上、反応温
度を100〜120℃にコントロールしながら３時間反応させ
た。後の工程は参考例１と同様に行ない、均一な有機鉄
イットリウム化合物10.25gを得た。Reference Example 2 Iron (III) nitrate 9 hydrate 4.04 g (0.01 M), yttrium nitrate hexahydrate 2.30 g (0.006 M) and 1,2-dodecanediol 32.37 g (0.16 M) were placed in a 50 ml beaker. Was dissolved in 30 g of 2-methoxyethanol and reacted for 3 hours on a hot plate while controlling the reaction temperature at 100 to 120 ° C. The subsequent steps were performed in the same manner as in Reference Example 1 to obtain 10.25 g of a uniform organic iron yttrium compound.
参考例３ 硝酸鉄（III）９水和物4.04g（0.01M）、硝酸イットリ
ウム６水和物2.30g（0.006M）、1,2−デカンジオール1
3.9g（0.08M）及び1,2−ドデカンジオール16.19g（0.08
M）を、50mlのビーカー中で２−メトキシエタノール30g
を溶解し、ホットプレート上、反応温度を100〜120℃に
コントロールしながら３時間反応させた。後の工程は参
考例１と同様に行い、均一な有機鉄イットリウム化合物
10.11gを得た。Reference Example 3 Iron (III) nitrate nonahydrate 4.04 g (0.01 M), yttrium nitrate hexahydrate 2.30 g (0.006 M), 1,2-decanediol 1
3.9g (0.08M) and 1,2-dodecanediol 16.19g (0.08M)
M) in a 50 ml beaker, 30 g of 2-methoxyethanol
Was dissolved and reacted for 3 hours on a hot plate while controlling the reaction temperature at 100 to 120 ° C. The subsequent steps are performed in the same manner as in Reference Example 1, and a uniform organic iron yttrium compound is used.
10.11 g was obtained.
比較例１〜５ 参考例１において、原料化合物として上記ジオールを用
いない場合及び他の各種低級1,2−ジオールを用いた場
合の結果を表−１に示す。低級1,2−ジオールを用いた
場合は、1,2−デカンジオール及び1,2−ドデカンジオー
ルと異なり、反応中に、不溶物を生成し均一な有機鉄イ
ットリウム化合物を合成することができなかった。Comparative Examples 1 to 5 Table 1 shows the results in Reference Example 1 when the above diol was not used as the raw material compound and when various other lower 1,2-diols were used. When a lower 1,2-diol is used, unlike 1,2-decanediol and 1,2-dodecanediol, an insoluble matter is generated during the reaction and a uniform organic iron yttrium compound cannot be synthesized. It was
参考例４ 硝酸鉄（III）９水和物20.2g（0.05M）及び硝酸イット
リウム６水和物11.49g（0.03M）を、500mlのビーカー中
でエタノール60mlに溶解し攪拌しながら60℃に保った。
その中にクエン酸84.06g（0.40M）をエタノール150mlに
溶解した溶液を徐々に加え、ホットプレート上、反応温
度を70〜80℃にコントロールしながら５時間反応させ
た。反応につれ、NO3イオンの分解によるNO3の発生が起
こり、鉄、イットリウム及びクエン酸の反応による有機
鉄イットリウム化合物が生成し、溶液の色が、赤茶色か
ら黒褐色へと変化した。さらに、反応を120℃で３時間
行い、NOｘの発生を完結させると同時にエタノールを留
去することにより均一な有機鉄イットリウム化合物90.2
2gを得た。 Reference Example 4 Iron (III) nitrate 9 hydrate 20.2 g (0.05 M) and yttrium nitrate hexahydrate 11.49 g (0.03 M) were dissolved in ethanol 60 ml in a 500 ml beaker and kept at 60 ° C with stirring. It was
A solution prepared by dissolving 84.06 g (0.40 M) of citric acid in 150 ml of ethanol was gradually added thereto, and the reaction was carried out for 5 hours on a hot plate while controlling the reaction temperature at 70 to 80 ° C. As the reaction takes place is the generation of NO 3 by decomposition of NO 3 ions, iron, organic iron yttrium compound by reaction of yttrium and citric acid produces the color of the solution was changed to dark brown from red-brown. Furthermore, the reaction is carried out at 120 ° C. for 3 hours to complete the generation of NO x and at the same time distilling off ethanol to obtain a uniform organic iron yttrium compound 90.2.
2g was obtained.
参考例５〜12 参考例４において、原料有機化合物として各種のオキシ
カルボン酸を用いた場合の結果を表−２に示す。Reference Examples 5 to 12 Table 2 shows the results when various oxycarboxylic acids were used as the raw material organic compounds in Reference Example 4.
比較例６〜９ 参考例４において、原料有機化合物として各種キレート
試薬を用いた場合の結果を表−３に示す。表からも明ら
かなようにキレート能の高い試薬でも反応途中、不溶物
を生じてしまい均一な有機鉄イットリウム化合物を合成
することができなかった。 Comparative Examples 6 to 9 Table 3 shows the results when various chelating reagents were used as the raw material organic compounds in Reference Example 4. As is clear from the table, even a reagent having a high chelating ability produced an insoluble matter during the reaction, and it was not possible to synthesize a uniform organic iron yttrium compound.
実施例１ 参考例４で得られた均一な有機鉄イットリウム化合物10
gを、エタノール100mlに溶解し、スピンコート用塗布溶
液とする。 Example 1 Uniform organic iron yttrium compound 10 obtained in Reference Example 4
g is dissolved in 100 ml of ethanol to prepare a coating solution for spin coating.
石英板（面積:2×2cm、厚さ:0.1mm）を回転円盤の中心
に固定し、1000rpmで円盤を回転させながら、塗布溶液
を石英板の中心に毎分6ccの速度で10秒間滴下した。次
いで、昇温プログラムの付いた箱型炉を用い、空気雰囲
気下、1000℃までのアニール処理を行った（室温→200
→400→600→800→1000℃、各焼成温度800℃までは10分
保持、1000℃では１時間保持）。こ一連の操作を10回繰
り返し、石英板上に亀裂のない剥離の生じにくい膜を作
成した。この膜は、Ｘ線回析の結果、YIGの曲型的なＸ
線パターンを示した。A quartz plate (area: 2 x 2 cm, thickness: 0.1 mm) was fixed to the center of a rotating disk, and the coating solution was dripped at the center of the quartz plate at a speed of 6 cc for 10 seconds while rotating the disk at 1000 rpm. . Then, using a box furnace equipped with a heating program, an annealing process was performed up to 1000 ° C in an air atmosphere (room temperature → 200
→ 400 → 600 → 800 → 1000 ℃, hold for 10 minutes up to each baking temperature of 800 ℃, hold for 1 hour at 1000 ℃). This series of operations was repeated 10 times to form a film on the quartz plate that was free from cracks and did not easily peel. As a result of X-ray diffraction, this film has a YIG curved X-shape.
A line pattern is shown.
この膜を、振動試料型磁力計を用い磁力測定を行うと、
強磁性を示し、15KOe（キロエルステッド）の時の飽和
磁化は35.7emu/gであった。When the magnetic force of this film is measured using a vibrating sample magnetometer,
It exhibited ferromagnetism, and the saturation magnetization at 15 KOe (kilo-Oersted) was 35.7 emu / g.
実施例２ 実施例１において、石英板の代わりにマイカ板（面積:2
×2cm、厚さ:0.1mm）を用いて８コートした場合、15KOe
の時の飽和磁化は35.4emu/gであった。Example 2 In Example 1, instead of the quartz plate, a mica plate (area: 2
15KOe when 8 coats using × 2cm, thickness: 0.1mm)
At that time, the saturation magnetization was 35.4 emu / g.
実施例３ 実施例１において、塗布工程とアニール工程とを繰返し
行うことによって基体上に種々の膜厚のYIG膜を形成
し、その光線透過率を測定した。その結果を表−４に示
す。Example 3 In Example 1, YIG films of various thicknesses were formed on the substrate by repeating the coating process and the annealing process, and the light transmittance thereof was measured. The results are shown in Table-4.
───────────────────────────────────────────────────── フロントページの続き 審査官 真々田 忠博 (56)参考文献 特開 昭58−41722（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of the front page Examiner Tadahiro Sanada (56) References JP-A-58-41722 (JP, A)
Claims (2)
以上の1,2−ジオール又はオキシカルボン酸である可溶
性有機鉄イットリウム化合物膜の熱分解により形成され
た透光性磁性イットリウム鉄ガーネット膜。1. An organic compound formed on a substrate has 10 carbon atoms.
A translucent magnetic yttrium iron garnet film formed by thermal decomposition of the above soluble organic iron yttrium compound film which is 1,2-diol or oxycarboxylic acid.
ル又はオキシカルボン酸である可溶性有機鉄イットリウ
ム化合物の有機溶媒溶液を基体上に塗布し、乾燥させ、
アニール処理して熱分解することを特徴とする透光性磁
性イットリウム鉄ガーネット膜の製造方法。2. A solution of a soluble organic iron yttrium compound in which the organic compound is a 1,2-diol or oxycarboxylic acid having 10 or more carbon atoms is applied onto a substrate and dried.
A method for producing a translucent magnetic yttrium iron garnet film, which is characterized by annealing and thermal decomposition.