JPH07286192A - Water-soluble processing oil agent - Google Patents
Water-soluble processing oil agentInfo
- Publication number
- JPH07286192A JPH07286192A JP10229194A JP10229194A JPH07286192A JP H07286192 A JPH07286192 A JP H07286192A JP 10229194 A JP10229194 A JP 10229194A JP 10229194 A JP10229194 A JP 10229194A JP H07286192 A JPH07286192 A JP H07286192A
- Authority
- JP
- Japan
- Prior art keywords
- acid
- water
- fatty acid
- hydroxy fatty
- carboxylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、切削研削加工や塑性加
工に使用する水溶性加工油剤に関する。さらに詳しく
は、潤滑性、消泡性、防錆性に優れ、更に摺動面潤滑
油、作動油等の他の油が混入しても汚染されにくく、ま
た性能劣化の少ない水溶性加工油剤に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a water-soluble working oil agent used for cutting and grinding and plastic working. More specifically, the present invention relates to a water-soluble processing oil that is excellent in lubricity, defoaming property, rust-prevention property, is less likely to be contaminated even if other oil such as sliding surface lubricating oil and hydraulic oil is mixed, and has little performance deterioration. .
【0002】[0002]
【従来の技術】従来から、切削研削加工や塑性加工等の
金属加工には、火災の危険性がなく、洗浄が容易である
等の理由から水溶性加工油剤が使用されている。特に切
削研削加工では、加工性能に優れ、冷却性の良い水溶性
加工油剤が広く用いられている。これらの水溶性加工油
剤は、オレイン酸、ひまし油脂肪酸等の脂肪酸類やナフ
テン酸、ロジン酸等のアルカリ金属塩、またはアミン塩
を主成分としており、一般に発泡しやすく、特に脂肪酸
塩は発泡しやすいため、発泡による作業性の低下、更に
防錆性や防食性に悪影響を及ぼす等の欠点があった。2. Description of the Related Art Conventionally, a water-soluble processing oil agent has been used for metal processing such as cutting and grinding processing and plastic processing because it has no risk of fire and is easy to clean. Particularly in the cutting and grinding process, a water-soluble processing oil having excellent processing performance and good cooling property is widely used. These water-soluble processing oils are mainly composed of fatty acids such as oleic acid and castor oil fatty acids, alkali metal salts such as naphthenic acid and rosin acid, or amine salts, and generally foam easily, and particularly fatty acid salts easily foam. Therefore, there are drawbacks such as a decrease in workability due to foaming and an adverse effect on rust resistance and corrosion resistance.
【0003】この様な欠点を改良した低起泡性で、防錆
性のある水溶性切削油剤が報告されている。例えば、ポ
リヒドロキシ脂肪酸の塩を用いる水溶性切削油剤組成物
(特開昭60−88096号)、リシノール酸重縮合物
の塩を用いる水溶性切削研削油剤(特開昭57−159
891号)、ジヒドロキシ脂肪酸、あるいは/およびモ
ノヒドロキシ脂肪酸との脱水縮合して得られる縮合脂肪
酸の塩を用いる水溶性切削油剤(特開平4−20229
8号)等が知られている。A water-soluble cutting oil having a low foaming property and an anticorrosive property, which has improved on such drawbacks, has been reported. For example, a water-soluble cutting oil composition using a salt of polyhydroxy fatty acid (JP-A-60-88096), a water-soluble cutting oil composition using a salt of ricinoleic acid polycondensate (JP-A-57-159).
891), dihydroxy fatty acid, and / or a water-soluble cutting oil agent using a salt of a condensed fatty acid obtained by dehydration condensation with a monohydroxy fatty acid (JP-A-4-20229).
No. 8) and the like are known.
【0004】[0004]
【発明が解決しようとする課題】しかしながら、これら
の水溶性切削研削油剤は実際の金属加工で使用した場
合、加工時の潤滑性が十分でなく、また長期間使用する
と、装置に使用されている摺動面潤滑油、作動油等の汚
染油が混入してくるが、これら汚染油が乳化をきたし、
金属加工液が汚染される。このため金属加工液は劣化を
速め、性能の低下を生じる。更に機械汚れを生じ、金属
加工液の腐敗を早め悪臭の発生の原因ともなり、作業環
境を悪化させる等の欠点があった。However, when these water-soluble cutting and grinding fluids are used in actual metal working, the lubricity during working is not sufficient, and when used for a long time, they are used in the apparatus. Contaminating oil such as sliding surface lubricating oil and hydraulic oil is mixed, but these contaminated oil causes emulsification,
Metalworking fluid is contaminated. For this reason, the metalworking fluid accelerates deterioration, resulting in deterioration in performance. Further, there are drawbacks such as mechanical fouling, accelerating the decay of the metalworking fluid and causing a bad odor, and deteriorating the working environment.
【0005】本発明は、上記課題を解決するために行わ
れたものであり、切削、研削加工等の金属加工におい
て、潤滑性、消泡性、防錆性に優れ、かつ装置に使用さ
れる摺動面潤滑油や作動油等の汚染油が混入しても乳化
しにくく、汚染、劣化の少ない水溶性加工油剤を提供す
ることを目的とする。The present invention has been made in order to solve the above problems, and is excellent in lubricity, defoaming property and rust preventive property in metal processing such as cutting and grinding, and is used for an apparatus. It is an object of the present invention to provide a water-soluble processing oil agent which is less likely to be emulsified even when contaminated oil such as sliding surface lubricating oil or hydraulic oil is mixed and which is less contaminated and deteriorated.
【0006】[0006]
【課題を解決するための手段】本発明者等は、上記課題
を解決するための研究を行った結果、ヒドロキシ脂肪
酸、または縮合ヒドロキシ脂肪酸の分子中に残存するヒ
ドロキシル基の一基乃至全部を、カルボン酸でエステル
縮合して得られるエステル化物の塩を水溶性加工油剤に
用いることにより、優れた加工性能を有すると共に、消
泡性、防錆性に優れ、かつ摺動面潤滑油、作動油等の混
入してくる油を乳化しにくく、汚染、劣化が少なくなる
ことを見出だし、本発明を完成した。Means for Solving the Problems As a result of research to solve the above problems, the present inventors have found that one or all of the hydroxyl groups remaining in the molecule of hydroxy fatty acid or condensed hydroxy fatty acid are By using a salt of an esterified product obtained by ester condensation with a carboxylic acid as a water-soluble processing oil agent, it has excellent processing performance, as well as excellent defoaming properties and rust resistance, and a sliding surface lubricating oil and hydraulic oil. The present invention was completed by finding that it is difficult to emulsify oils mixed in with oils, etc., and contamination and deterioration are reduced.
【0007】即ち、本発明の水溶性加工油剤は、(A)
ヒドロキシ脂肪酸、または該ヒドロキシ脂肪酸を脱水縮
合して得られる縮合ヒドロキシ脂肪酸と、(B)炭素数
2〜20の脂肪族カルボン酸、及び脂環族カルボン酸、
あるいは芳香族カルボン酸とを反応して得られるエステ
ル化物のアルカリ金属塩、アンモニウム塩、またはアミ
ン塩を含有することを特徴とする水溶性加工油剤に関す
る。That is, the water-soluble processing oil agent of the present invention is (A)
Hydroxy fatty acid or a condensed hydroxy fatty acid obtained by dehydration condensation of the hydroxy fatty acid, and (B) an aliphatic carboxylic acid having 2 to 20 carbon atoms, and an alicyclic carboxylic acid,
Alternatively, the present invention relates to a water-soluble processing oil containing an alkali metal salt, ammonium salt, or amine salt of an esterified product obtained by reacting with an aromatic carboxylic acid.
【0008】本発明に用いるヒドロキシ脂肪酸として
は、モノヒドロキシ脂肪酸とジヒドロキシ脂肪酸であ
り、ヒドロキシ脂肪酸の炭素数は、10〜20であるこ
とが好ましく、炭素数が9以下では潤滑性や防錆性が劣
るため好ましくない。20以上では、水溶性が乏しくな
り、水溶性加工油剤には適さない。The hydroxy fatty acids used in the present invention are monohydroxy fatty acids and dihydroxy fatty acids, and the hydroxy fatty acids preferably have 10 to 20 carbon atoms. It is inferior and not preferable. When it is 20 or more, the water solubility becomes poor and it is not suitable as a water-soluble processing oil.
【0009】具体的には、モノヒドロキシ脂肪酸として
は、オキシラウリン酸(サビニン酸)、2−ヒドロキシ
テトラデカン酸、ヤラピノール酸、16−ヒドロキシヘ
キサデカン酸(ユニペリン酸)、2−ヒドロキシオクタ
デカン酸、12−ヒドロキシ−9−オクタデセン酸、1
2−ヒドロキシオクタデカン酸等が例示され、ジヒドロ
キシ脂肪酸としては、3,11−ジヒドロキシテトラデ
カン酸、9,10−ジヒドロキシオクタデカン酸等が例
示される。これらは一般に植物油、ロウ等を常法により
加水分解、精製して得ることができる。また、ウンデシ
レン酸、オレイン酸、リノール酸等の不飽和脂肪酸の不
飽和結合に公知の方法でヒドロキシル基を導入してジヒ
ドロキシ脂肪酸を得ることができる。Specific examples of monohydroxy fatty acids include oxylauric acid (sabinic acid), 2-hydroxytetradecanoic acid, yarapinolic acid, 16-hydroxyhexadecanoic acid (uniperic acid), 2-hydroxyoctadecanoic acid, and 12-hydroxy. -9-octadecenoic acid, 1
2-Hydroxyoctadecanoic acid and the like are exemplified, and examples of the dihydroxy fatty acid include 3,11-dihydroxytetradecanoic acid and 9,10-dihydroxyoctadecanoic acid. These can generally be obtained by hydrolyzing and purifying vegetable oil, wax and the like by a conventional method. In addition, a dihydroxy fatty acid can be obtained by introducing a hydroxyl group into an unsaturated bond of an unsaturated fatty acid such as undecylenic acid, oleic acid or linoleic acid by a known method.
【0010】本発明に用いる縮合ヒドロキシ脂肪酸は、
例えば、前記ヒドロキシ脂肪酸の1種、または2種以上
の混合物を窒素ガス等の不活性ガスの気流下、100〜
200℃で30分〜12時間脱水縮合反応することによ
り得られる。縮合ヒドロキシ脂肪酸の縮合度は酸価で規
定することができ、酸価から換算することにより縮合度
を求めることができる。本発明に用いる縮合ヒドロキシ
脂肪酸の縮合度は2〜6量体が望ましく、これら各縮合
物および未縮合ヒドロキシ脂肪酸の混合物を用いてもよ
い。縮合度が7量体以上の縮合ヒドロキシ脂肪酸は、水
溶性低くなり好ましくない。The condensed hydroxy fatty acid used in the present invention is
For example, one kind of the hydroxy fatty acid or a mixture of two or more kinds of the hydroxy fatty acid may be added to 100-
It can be obtained by a dehydration condensation reaction at 200 ° C. for 30 minutes to 12 hours. The degree of condensation of the condensed hydroxy fatty acid can be defined by the acid value, and the degree of condensation can be calculated by converting from the acid value. The condensation degree of the condensed hydroxy fatty acid used in the present invention is preferably a dimer to a hexamer, and a mixture of these condensates and uncondensed hydroxy fatty acids may be used. Condensed hydroxy fatty acids having a degree of condensation of 7-mer or more are not preferable because their water solubility becomes low.
【0011】本発明に用いる炭素原子数2〜20の脂肪
族カルボン酸、脂環族カルボン酸、および芳香族カルボ
ン酸は、モノカルボン酸、またはジカルボン酸が好まし
い。特に、モノカルボン酸が好ましい。また、炭素数が
20以上の場合はエステル化物の水溶性が低くなり好ま
しくない。The aliphatic carboxylic acid having 2 to 20 carbon atoms, alicyclic carboxylic acid and aromatic carboxylic acid used in the present invention are preferably monocarboxylic acid or dicarboxylic acid. Particularly, monocarboxylic acid is preferable. Further, if the carbon number is 20 or more, the water solubility of the esterified product becomes low, which is not preferable.
【0012】例示すると炭素数2〜20の脂肪族カルボ
ン酸として酢酸、イソ酪酸、ブタン酸、ヘプタン酸、ソ
ルビン酸、オクタン酸、ウンデシレン酸、ラウリン酸、
パルミチン酸、ステアリン酸、オレイン酸、リノール酸
等が例示される。脂環族カルボン酸としては、炭素数1
〜12のアルキル基を有してもよいシクロアルカンにカ
ルボン酸、または炭素数1〜3の鎖状カルボン酸の付い
たものが例示され、例えば、シクロヘキシルカルボン
酸、シクロヘキシルジカルボン酸、シクロヘキシル酢酸
等が挙げられる。芳香族カルボン酸としては、炭素数1
〜12のアルキル基を有してもよい芳香環にカルボン
酸、または炭素数1〜3の鎖状カルボン酸の付いたもの
が例示され、例えば、安息香酸、フタル酸、トルイル
酸、フェニル酢酸、けい皮酸、ナフタレン酢酸、ナフト
エ酸等が挙げられる。For example, as the aliphatic carboxylic acid having 2 to 20 carbon atoms, acetic acid, isobutyric acid, butanoic acid, heptanoic acid, sorbic acid, octanoic acid, undecylenic acid, lauric acid,
Examples include palmitic acid, stearic acid, oleic acid, linoleic acid and the like. The alicyclic carboxylic acid has 1 carbon atom
Examples of the cycloalkane which may have an alkyl group of 1 to 12 have a carboxylic acid or a chain carboxylic acid having 1 to 3 carbon atoms, and examples thereof include cyclohexylcarboxylic acid, cyclohexyldicarboxylic acid and cyclohexylacetic acid. Can be mentioned. An aromatic carboxylic acid has 1 carbon atom
To carboxylic acid or a chain carboxylic acid having 1 to 3 carbon atoms attached to an aromatic ring which may have an alkyl group of 1 to 12 are exemplified, for example, benzoic acid, phthalic acid, toluic acid, phenylacetic acid, Examples thereof include cinnamic acid, naphthalene acetic acid and naphthoic acid.
【0013】本発明に用いる、前記(A)と(B)との
反応によるエステル化物は、常法のエステル化反応によ
って得られる。エステル化反応の例としては、(A)と
(B)を適当な縮合触媒の存在下、100〜200℃で
反応させ生成する所定量の水を除去して得る方法や、
(B)を予め塩化チオニルで処理して酸塩化物にした
後、(A)と反応させてエステル化物を得る方法等があ
る。The esterification product used in the present invention by the reaction of the above (A) and (B) can be obtained by a conventional esterification reaction. Examples of the esterification reaction include a method in which (A) and (B) are reacted at 100 to 200 ° C. in the presence of a suitable condensation catalyst to remove a predetermined amount of water, and
(B) is previously treated with thionyl chloride to give an acid chloride, and then reacted with (A) to obtain an esterified product.
【0014】また、(A)と(B)をエステル化する際
の反応比率は、(A)の分子中の水酸基の少なくとも1
基をエステル化するに必要な(B)を用いる。The reaction ratio for esterifying (A) and (B) is at least 1 of the hydroxyl groups in the molecule of (A).
Use (B), which is necessary to esterify the group.
【0015】上記エステル化物を常法に従って、アルカ
リ金属の水酸化物、アンモンニア、またはアミン化合物
で中和することにより、本発明に用いるエステル化物の
アルカリ金属塩、アンモニウム塩、およびアミン塩が得
られる。アルカリ金属としては、ナトリウム、カリウム
等を、アミン化合物としては、エチルアミン、プロピル
アミン等の炭素数1〜5のアルキルアミン、(モノ、
ジ、トリ)エタノールアミン、(モノ、ジ、トリ)イソ
プロパノールアミン等のアルカノールアミン、モルホリ
ン、シクロヘキシルアミン、ジシクロヘキシルアミン等
のシクロアルキルアミン類を用いることができる。特に
好ましくは、水溶性アミンである。By neutralizing the above-mentioned esterified product with an alkali metal hydroxide, ammonia or amine compound according to a conventional method, an alkali metal salt, an ammonium salt and an amine salt of the esterified product used in the present invention can be obtained. . Alkali metals include sodium and potassium, and amine compounds include alkylamines having 1 to 5 carbon atoms such as ethylamine and propylamine.
Alkanolamines such as di, tri) ethanolamine and (mono-, di-, tri) isopropanolamine, and cycloalkylamines such as morpholine, cyclohexylamine and dicyclohexylamine can be used. A water-soluble amine is particularly preferable.
【0016】本発明による水溶性加工油剤は、本発明の
エステル化物のアルカリ金属塩、アンモニウム塩、およ
び、またはアミン塩を油剤原液中に配合することによっ
て調整される。配合量は通常5〜80重量%、好ましく
は10〜60重量%である。配合量が5重量%以下では
防錆性が悪くなり、好ましくない。The water-soluble processing oil according to the present invention is prepared by incorporating the alkali metal salt, ammonium salt, and / or amine salt of the esterified product of the present invention into an oil solution stock solution. The compounding amount is usually 5 to 80% by weight, preferably 10 to 60% by weight. If the blending amount is 5% by weight or less, the rust preventive property is deteriorated, which is not preferable.
【0017】尚、本発明の水溶性加工油剤は、所望によ
り鉱物油、動植物油、脂肪酸、脂肪酸エステル、極圧添
加剤、界面活性剤、防腐剤、等の常套の添加剤を適宜配
合してもよい。The water-soluble processed oil agent of the present invention may be optionally mixed with conventional additives such as mineral oil, animal and vegetable oil, fatty acid, fatty acid ester, extreme pressure additive, surfactant, preservative and the like. Good.
【0018】本発明の水溶性加工油剤は、水に希釈して
使用されるが、希釈倍率は、一般には5〜100倍に希
釈して使用されるが、被加工物の材質等に応じて適宜選
定すればよい。The water-soluble processing oil of the present invention is used by diluting it with water. The dilution ratio is generally 5 to 100 times, and it is used depending on the material to be processed. It may be selected appropriately.
【0019】[0019]
【実施例】以下に、本発明を実施例により説明するが、
本発明はこれら実施例に限定されるものではない。EXAMPLES The present invention will be described below with reference to examples.
The present invention is not limited to these examples.
【0020】(1)縮合ヒドロキシ脂肪酸の調製 縮合ヒドロキシ脂肪酸は、常法に従い、ヒドロキシ脂肪
酸を窒素気流下、200℃で所定時間加熱して得た。用
いたヒドキシ脂肪酸とそれから得られた縮合ヒドロキシ
脂肪酸の酸価、水酸基価、酸価から換算した平均分子量
を表1に示す。(1) Preparation of Condensed Hydroxy Fatty Acid The condensed hydroxy fatty acid was obtained by heating the hydroxy fatty acid at 200 ° C. for a predetermined time under a nitrogen stream in a conventional manner. Table 1 shows the average molecular weights calculated from the acid value, the hydroxyl value, and the acid value of the hydroxy fatty acid used and the condensed hydroxy fatty acid obtained therefrom.
【0021】[0021]
【表1】 [Table 1]
【0022】(2)エステル化物の調製 本発明に用いるエステル化物は、常法に従い、先ず、所
定量のカルボン酸に塩化チオニルを80〜100℃で反
応させてα−クロロカルボン酸を合成し、次いで、この
α−クロロカルボン酸と所定量のヒドロキシ脂肪酸また
は縮合ヒドロキシ脂肪酸とを、窒素気流下、室温にて反
応させた後、反応物を純水洗浄により副成する塩化水素
を除去し乾燥して得た。表2に、用いたヒドキシ脂肪
酸、縮合ヒドロキシ脂肪酸、およびカルボン酸の種類、
更にその反応モル比を示す。表2中のNoは、表1に記
載するNoを示す。(2) Preparation of Esterified Compound The esterified compound used in the present invention is prepared by reacting a predetermined amount of carboxylic acid with thionyl chloride at 80 to 100 ° C. to synthesize α-chlorocarboxylic acid, according to a conventional method. Next, this α-chlorocarboxylic acid is reacted with a predetermined amount of hydroxy fatty acid or condensed hydroxy fatty acid at room temperature under a nitrogen stream, and then the reaction product is washed with pure water to remove by-product hydrogen chloride and dried. I got it. Table 2 shows the types of hydroxy fatty acids, condensed hydroxy fatty acids, and carboxylic acids used,
Furthermore, the reaction molar ratio is shown. The No in Table 2 indicates the No described in Table 1.
【0023】[0023]
【表2】 [Table 2]
【0024】[実施例1〜26]表2に示すエステル化
物No.1〜21のトリエタノールアミン、およびナト
リウム塩の0.5wt%水溶液として試料液を調製した。
この試料液を用いて以下に示す試験方法により防錆力、
摩擦係数、消泡性、潤滑油乳化性を測定した。防錆力、
摩擦係数、消泡性の結果を表3と表4に、潤滑油分離性
の結果を表5と表6に示す。表3と表5は、エステル化
物のトリエタノールアミン塩について、表4と表6は、
ナトリウム塩についての結果を示す。[Examples 1 to 26] The esterified product Nos. A sample solution was prepared as a 0.5 wt% aqueous solution of 1 to 21 triethanolamine and sodium salt.
Rust prevention by the following test method using this sample solution,
The friction coefficient, defoaming property, and lubricating oil emulsifying property were measured. Rust prevention,
The results of friction coefficient and defoaming property are shown in Tables 3 and 4, and the results of lubricating oil separability are shown in Tables 5 and 6. Tables 3 and 5 show triethanolamine salts of esterified products, and Tables 4 and 6 show
The results for the sodium salt are shown.
【0025】試験方法を次に示す。 (A)防錆性試験 (イ)鋳物切粉法−−鋳物のドライカッティング切粉を
試験液に10分間浸漬後、切粉を試験液を切ってからシ
ャーレに移し、72時間後の発錆状態を観察した。発錆
の状態を以下の5段階の基準によって評価した。 発錆階級: 5:発錆なし 4:10%以下の発錆 3:10〜50%の発錆 2:50%以上の発錆 1:100%の発錆The test method is shown below. (A) Anticorrosion test (a) Casting chip cutting method --- Dry cutting of castings After dipping cutting chips in a test solution for 10 minutes, cutting the chips and transferring them to a petri dish, rusting after 72 hours The condition was observed. The state of rusting was evaluated according to the following five-stage criteria. Rust class: 5: No rust 4: 10% or less rust 3: 10-50% rust 2: 50% or more rust 1: 100% rust
【0026】(ロ)冷間圧延鋼板法−−研磨脱脂した冷
間圧延鋼板を試験液に10分間浸漬後、引上げ風乾させ
室内に72時間放置後、鋼板の発錆状態を(イ)と同じ
発錆階級によって評価した。(B) Cold-rolled steel sheet method: The cold-rolled steel sheet polished and degreased is immersed in a test solution for 10 minutes, then pulled up and air-dried, and left in the room for 72 hours. It was evaluated by the rust rank.
【0027】(B)摩擦係数−−曽田式II型振り子油性
試験機を用いて25℃にて測定した。(B) Coefficient of Friction--Measured at 25 ° C. using a Soda type II pendulum oiliness tester.
【0028】(C)消泡性試験−−試料液50mlを10
0ml容の共栓付メスシリンダーに入れ、密栓後、液温3
0℃でメスシリンダーを上下に10回振盪し、その後静
置して、直後、30秒後、60秒後の泡の容積(ml)を
測定した。(C) Defoaming test--10 ml of 50 ml sample solution
Place in a 0 ml graduated cylinder with a ground-in stopper, seal tightly, and then liquid temperature 3
The graduated cylinder was shaken up and down 10 times at 0 ° C., and then left still, and immediately after, 30 seconds and 60 seconds later, the volume (ml) of foam was measured.
【0029】(D)潤滑油分離性試験−−試料液50ml
と潤滑油10mlとを100ml容の共栓付メスシリンダー
に入れ、密栓後、液温30℃でメスシリンダーを上下に
10回振盪し、その後静置して、直後、10分後、30
分後、及び60分後の潤滑油の分離量を測定した。潤滑
油としては、(a)モービル石油(株)製バクトラオイ
ルNo2(摺動面潤滑油)、(b)モービル石油(株)
製DTE22(油圧作動油)の2種を用いた。(D) Lubricating oil separability test--Sample liquid 50 ml
And 10 ml of lubricating oil were placed in a graduated cylinder with a stopper of 100 ml, and after tightly sealing, the graduated cylinder was shaken up and down 10 times at a liquid temperature of 30 ° C., and then left still, and immediately after 10 minutes, 30 minutes later.
The amount of lubricant separated was measured after 60 minutes and after 60 minutes. As the lubricating oil, (a) Bactra Oil No. 2 (sliding surface lubricating oil) manufactured by Mobil Oil Co., Ltd., (b) Mobil Oil Co., Ltd.
Two types of DTE22 (hydraulic oil) manufactured by DTE22 were used.
【0030】[比較例1〜14]実施例と同様に、ヒド
ロキシ脂肪酸、及び縮合ヒドロキシ脂肪酸のトリエタノ
ールアミン塩、およびナトリウム塩を比較例として試験
を行い、結果を表3〜表6に示した。[Comparative Examples 1 to 14] In the same manner as in Examples, tests were carried out using hydroxy fatty acids, triethanolamine salts of condensed hydroxy fatty acids, and sodium salts as comparative examples, and the results are shown in Tables 3 to 6. .
【0031】[0031]
【表3】
[Table 3]
【0032】[0032]
【表4】 [Table 4]
【0033】[0033]
【表5】 [Table 5]
【0034】[0034]
【表6】 [Table 6]
【0035】[実施例27〜30]、[比較例15〜1
8] 表7に示す組成で配合した水溶性加工油剤を調整し、該
水溶性加工油剤を水を用いて30倍の希釈液を調整し、
下記に示す実機による切削試験を行い切削性能(タップ
の工具寿命)、および混入してきた潤滑油の乳化状態を
評価した。その結果を表7に示す。[Examples 27 to 30], [Comparative Examples 15 to 1]
8] A water-soluble processing oil agent formulated with the composition shown in Table 7 was prepared, and the water-soluble processing oil agent was diluted with water to a 30-fold dilution,
The following cutting test was carried out using an actual machine to evaluate the cutting performance (tool life of the tap) and the emulsified state of the mixed lubricating oil. The results are shown in Table 7.
【0036】(E)切削試験条件と評価方法 加工機械:立型NCフライス盤(エンシュウ製) 加工工具:M12×1.25 ハンドタップ(ハイス
鋼、ヤマワ製) 加工条件:切削速度6m/min 、送り200mm/min、深さ
20mm不貫通、下穴径10.7mm 被削材 :S45C(E) Cutting test conditions and evaluation method Processing machine: Vertical NC milling machine (manufactured by Enshu) Processing tool: M12 x 1.25 Hand tap (high speed steel, manufactured by Yamaha) Processing conditions: Cutting speed 6 m / min, feed 200 mm / min, depth 20 mm, no penetration, prepared hole diameter 10.7 mm Work material: S45C
【0037】評価方法:加工後のねじ穴を、ねじ用限界
ゲージ(クロダ製GPII−M12×1.25)で検査
し、ねじ穴に異常がみられるまで1本の工具で加工を連
続し、正常に加工できるねじ穴の個数を工具寿命とし
た。Evaluation method: The threaded holes after processing were inspected with a thread limit gauge (GPII-M12 × 1.25 manufactured by Kuroda), and the processing was continued with one tool until abnormalities were found in the threaded holes. The tool life was defined as the number of screw holes that can be machined normally.
【0038】(F)潤滑油の乳化状態の評価 混入してきた潤滑油の乳化の状態を次の基準で評価し
た。 評価基準 ◎:潤滑油は乳化せず、完全に分離浮上する △:潤滑油の一部は乳化し、液中に分散 ×:潤滑油は完全に乳化し、液は変色する(F) Evaluation of emulsified state of lubricating oil The emulsified state of the mixed lubricating oil was evaluated according to the following criteria. Evaluation criteria ◎: Lubricating oil does not emulsify and completely separates and floats △: Part of lubricating oil emulsifies and disperses in liquid ×: Lubricating oil completely emulsifies and discolors liquid
【0039】[0039]
【表7】 [Table 7]
【0040】[0040]
【発明の効果】以上のように、本発明のエステル化物の
塩は、優れた加工性能を有すると共に、消泡性、防錆性
に優れ、かつ潤滑油が混入しても乳化しにくい。従っ
て、本発明の水溶性加工油剤は、従来油剤に比べて加工
性能が優れるだけでなく、消泡性や防錆性が優れるため
作業性が良好で、かつ、摺動面潤滑油、作動油等の汚染
油が混入してもこれらの乳化による汚染、劣化が少ない
ため長期間安定に使用できる。INDUSTRIAL APPLICABILITY As described above, the salt of the esterified product of the present invention has excellent processing performance, is excellent in defoaming property and rust preventive property, and is difficult to be emulsified even when lubricating oil is mixed. Therefore, the water-soluble processing oil agent of the present invention is not only excellent in processing performance as compared with conventional oil agents, but also has good defoaming property and rust-preventing property, and thus has good workability, and a sliding surface lubricating oil and hydraulic oil. Even if contaminated oil such as the above is mixed, contamination and deterioration due to emulsification of these are small, and therefore stable use can be achieved for a long time.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 C10N 30:12 30:18 40:22 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location C10N 30:12 30:18 40:22
Claims (3)
キシ脂肪酸を脱水縮合して得られる縮合ヒドロキシ脂肪
酸と、(B)炭素数2〜20の脂肪族カルボン酸、およ
び脂環族カルボン酸、あるいは芳香族カルボン酸との反
応により得られるエステル化物のアルカリ金属塩、アン
モニウム塩、またはアミン塩を含有することを特徴とす
る水溶性加工油剤。1. A hydroxy fatty acid (A) or a condensed hydroxy fatty acid obtained by dehydration condensation of a hydroxy fatty acid, and (B) an aliphatic carboxylic acid having 2 to 20 carbon atoms, and an alicyclic carboxylic acid, or an aromatic compound. A water-soluble processing oil agent containing an alkali metal salt, an ammonium salt, or an amine salt of an esterified product obtained by the reaction with a carboxylic acid.
のモノヒドロキシ、またはジヒドロキシ脂肪酸であり、
縮合ヒドロキシ脂肪酸が、ヒドロキシ脂肪酸の2〜6量
体、またはこれらの混合物である請求項1記載の水溶性
加工油剤。2. The hydroxy fatty acid has 10 to 20 carbon atoms.
Is a monohydroxy or dihydroxy fatty acid of
The water-soluble processing oil according to claim 1, wherein the condensed hydroxy fatty acid is a dimer or hexamer of hydroxy fatty acid, or a mixture thereof.
よび脂環族カルボン酸、あるいは芳香族カルボン酸が、
モノカルボン酸である請求項2の水溶性加工油剤。3. An aliphatic carboxylic acid having 2 to 20 carbon atoms, and an alicyclic carboxylic acid or an aromatic carboxylic acid,
The water-soluble processing oil according to claim 2, which is a monocarboxylic acid.