JPH07279061A - Decorative sheet - Google Patents
Decorative sheetInfo
- Publication number
- JPH07279061A JPH07279061A JP8236494A JP8236494A JPH07279061A JP H07279061 A JPH07279061 A JP H07279061A JP 8236494 A JP8236494 A JP 8236494A JP 8236494 A JP8236494 A JP 8236494A JP H07279061 A JPH07279061 A JP H07279061A
- Authority
- JP
- Japan
- Prior art keywords
- elongation
- fiber
- decorative sheet
- water
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、装飾シートに関し、詳
しくは、該シートを所定箇所へ貼着する際の糊付け作業
が極めて容易であるとともに、貼着終了後に着色のため
の、あるいは貼着されていた該シートの表面における剥
落や擦過傷などを補修するためなどの塗装が可能で、し
かも耐水性にも優れた装飾シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet, and more specifically, it is extremely easy to carry out a gluing operation when sticking the sheet to a predetermined place, and for coloring or sticking after the sticking is completed. The present invention relates to a decorative sheet which can be coated for repairing peeling and scratches on the surface of the sheet that has been used, and is also excellent in water resistance.
【０００２】[0002]
【従来の技術および発明が解決しようとする課題】各種
建造物の壁や天井などの表面を装飾する目的で使用され
るいわゆる装飾シートは、従来、難燃紙や不燃紙などの
裏打紙などからなる基材上に、発泡性または非発泡性の
合成樹脂インクによる各種の模様層を設けたもの、ある
いは合成樹脂層をコーティング加工し、必要に応じてグ
ラビア印刷を施し、その上にエンボス加工を施したもの
などが一般的である。2. Description of the Related Art So-called decorative sheets used for decorating surfaces such as walls and ceilings of various structures have hitherto been made from backing paper such as flame-retardant paper or non-combustible paper. A substrate with various pattern layers made of expandable or non-expandable synthetic resin ink, or a synthetic resin layer is coated, and if necessary, gravure printing is performed and embossing is performed on it. It is generally applied.
【０００３】ところで、上記のような装飾シートを、壁
や天井に貼着させる（これらの貼着施工対象は、一般に
「下地材」と呼ばれる）には、一般には、装飾シートの
裏面にデンプン糊などの接着剤を塗布し、これを下地材
に貼着することにより行われている。By the way, in order to attach the above-mentioned decorative sheet to a wall or ceiling (the object to be attached is generally called a "base material"), a starch paste is generally applied to the back surface of the decorative sheet. It is carried out by applying an adhesive such as the above and adhering this to a base material.
【０００４】このとき、従来の装飾シートに使用されて
いる裏打紙などの基材は、デンプン糊などが塗布された
際に、このデンプン糊などに含まれる水分がしみ込んで
伸びる性質がある（一般に使用されている裏打紙では、
後述する水中伸度が０．８〜１．２％程度）ため、刷毛
塗りなどの塗布作業に長時間を要しかつ塗布量にムラが
生じ易い手段で、デンプン糊などを塗布すると、基材の
伸びにもムラを生じ、皺が入り易くなる。At this time, a base material such as a backing paper used for a conventional decorative sheet has a property that, when starch paste or the like is applied, the water contained in the starch paste or the like is soaked in and stretches (generally, In the backing paper used,
Since the elongation in water described later is about 0.8 to 1.2%), when a starch paste or the like is applied by a means that requires a long time for application work such as brush application and tends to cause uneven application amount, Unevenness also occurs in the elongation of the wrinkles and wrinkles are easily formed.
【０００５】したがって、従来の装飾シートにおいて
は、短時間で、かつ均一にデンプン糊などの接着剤を塗
布することができる特別な塗布装置（この塗布装置は、
一般に「糊付け機」と呼ばれる）の使用が余儀なくされ
ている。しかも、装飾シートを裏面にデンプン糊などの
接着剤を塗布した直後に下地材に貼着すると、貼着した
後も基材が伸びてジョイント部の収まりが悪いことか
ら、デンプン糊などを塗布した後、基材の伸びが安定す
るのを待って下地材に貼着する必要があり、作業性にも
劣っている。Therefore, in a conventional decorative sheet, a special coating device capable of uniformly coating an adhesive such as starch paste in a short time (this coating device:
(Generally called a "gluing machine"). Moreover, if the decorative sheet is attached to the base material immediately after the adhesive such as starch glue is applied to the back surface, the base material will be stretched even after the attachment and the joint part will not fit properly. After that, it is necessary to wait for the elongation of the base material to stabilize and then to attach the base material to the base material, and the workability is also poor.
【０００６】さらに、テンプン糊などを、装飾シートの
裏面に塗布するのではなく、下地材側に塗布して、この
上に装飾シートを貼着することも考えられるが、この場
合には貼着した後に基材が伸びて、やはりジョイント部
の収まりが悪くなるため、デンプン糊などは基材裏面
に、上記の糊付け機を使用して塗布することが必須とさ
れている。Further, it is possible to apply tempun glue or the like to the base material side instead of applying it to the back surface of the decorative sheet, and to stick the decorative sheet on this, but in this case, it is applied. After that, the base material is stretched and the joint part is poorly set. Therefore, it is indispensable to apply starch paste or the like to the back surface of the base material using the above-mentioned gluing machine.
【０００７】また、一枚の装飾シートで下地材の全面あ
るいは貼着所望面の全面を貼着できる場合は問題ない
が、通常は、複数枚の装飾シートを必要とする。したが
って、各装飾シート間のジョイント部において、できる
だけ隙間が生じないようにするのは勿論のこと、ジョイ
ント部が目立たないように特別の注意を払う必要がある
のみならず、装飾シートの種類によっては、模様合わせ
が必要な場合もあり、施工には熟練を要している。There is no problem if one decorative sheet can be used to adhere the entire surface of the base material or the desired adhesion surface, but usually, a plurality of decorative sheets are required. Therefore, it is not only necessary to prevent as much gaps as possible from occurring at the joints between the decorative sheets, but it is also necessary to take special care so that the joints are not conspicuous. However, pattern matching may be required, and construction requires skill.
【０００８】さらに、室内のリフォームに際しては、従
来、古い装飾シートを下地材より完全に剥がし取り、こ
の後に上記した施工法により新規な装飾シートを貼着す
るという言わば張り替え施工が一般に行われている。特
に、賃貸のオフィスビルや飲食店などにおいて、賃貸者
が入れ替わる度に室内のリフォームが行われることが近
年の慣習となっており、この入れ替わりが極めて頻繁に
行われるビルなどにおいては、上記の張り替え作業にか
なりの労力とコストを要している。Further, when remodeling the interior of the room, it has been customary in the past to replace the old decorative sheet completely from the base material, and then to attach a new decorative sheet by the above-mentioned construction method, so to speak, relining work. . Particularly in rental office buildings and restaurants, it has become a common practice in recent years to perform indoor remodeling every time the tenant is replaced, and in buildings where this replacement is extremely frequent, the above replacement The work requires considerable effort and cost.
【０００９】そこで、本発明では、上記した貼着施工
（作業）の際の各種の煩わしさを解消するために、刷毛
塗りなど簡単な手段において貼着施工することができ、
しかも貼着施工後に装飾シートの上から各種の塗料、特
に水性タイプの塗料による塗装を可能にするとともに、
優れた耐水性をも有する装飾シートを提供することを目
的とする。Therefore, in the present invention, in order to eliminate the various inconveniences in the above-mentioned sticking work (work), the sticking work can be carried out by a simple means such as brushing,
Moreover, it enables painting with a variety of paints, especially water-based paints, from the decorative sheet after attachment.
It is an object to provide a decorative sheet that also has excellent water resistance.
【００１０】[0010]
【課題を解決するための手段】本発明の装飾シートは、
上記目的を達成するために、水中伸度が０．６％以下の
基材上に立体模様層が形成されてなることを特徴とす
る。The decorative sheet of the present invention comprises:
In order to achieve the above object, a three-dimensional pattern layer is formed on a substrate having an elongation in water of 0.6% or less.
【００１１】本発明において、使用できる基材は、水中
伸度が０．６％であればどのようなものでもよく、例え
ば、パルプ成分にガラス繊維、アスベスト、金属繊維、
カーボン繊維などの無機繊維、ポリエステル、ポリアミ
ド、アクリル、塩化ビニル、ポリエチレン、ポリプロピ
レン、ポリウレタンなどの合成繊維などを混抄したも
の、これらの繊維からなる不織布、あるいは難燃紙や不
燃紙などの通常の裏打紙に織布、編布、不織布やプラス
チックシートなどを貼り合わせたものなどが挙げられ
る。これらの基材のうち、層間剥離が可能なものであれ
ば、リフォームの際の剥がし取り作業が容易となるた
め、より好ましい。In the present invention, any substrate may be used as long as it has an elongation in water of 0.6%. For example, the pulp component may be glass fiber, asbestos, metal fiber,
Inorganic fibers such as carbon fibers, synthetic fibers such as polyester, polyamide, acrylic, vinyl chloride, polyethylene, polypropylene, polyurethane, etc., non-woven fabric made of these fibers, or ordinary backing such as flame-retardant paper or non-combustible paper Examples include paper, to which a woven cloth, a knitted cloth, a non-woven fabric, a plastic sheet, or the like is attached. Of these base materials, those capable of delamination are more preferable because they facilitate the peeling work during reforming.
【００１２】ところで、本発明における水中伸度とは、
水中に上記のような基材を置いたときる伸び率を示すも
ので、その測定方法は、（１）基材を幅２８０ｍｍ、縦
５０ｍｍの大きさに裁断して試験片を調製し、（２）試
験片の中央部に、幅方向に平行な約２００ｍｍの直線を
１本引き、その長さ（Ｘ）をノギスを用いて測定し、
（３）直線を引いた試験片を水中に５分間浸漬した後、
上記の直線の長さ（Ｙ）を同様にして測定し、（４）こ
れらのＸ、Ｙから数１の式にて算出することにより行わ
れる。By the way, the underwater elongation in the present invention means
It shows the elongation percentage when the above-mentioned base material is placed in water, and its measuring method is (1) cutting the base material into a size of width 280 mm and length 50 mm to prepare a test piece, 2) Draw a straight line of about 200 mm parallel to the width direction at the center of the test piece and measure its length (X) using a caliper,
(3) After immersing the straight test piece in water for 5 minutes,
The length (Y) of the above straight line is measured in the same manner, and (4) it is calculated from these X and Y by the formula (1).
【００１３】[0013]
【数１】 [Equation 1]
【００１４】本発明では、水中伸度が０．６％以下（乾
燥状態で長さ１ｍの基材を水中に５分間浸漬したときの
伸びが６ｍｍ以下）、好ましくは０．４％以下のものを
使用する。In the present invention, an elongation in water of 0.6% or less (elongation of 6 mm or less when a base material having a length of 1 m is immersed in water for 5 minutes in a dry state) is preferably 0.4% or less. To use.
【００１５】水中伸度が０．６％を超える基材を用いる
と、装飾シートの裏面にデンプン糊などが塗布された
り、装飾シートの表面に水性塗料などが塗装されたりな
どして基材に水分が含まれると、基材が伸びてしまうた
め、貼着施工時には、従来の装飾シートと同様に特別な
糊付け機を要し、作業性が悪化するとともに、貼着後に
は、水性塗料などを用いて塗装するとジョイント部の目
開きなどの問題が生じる。When a base material having an elongation in water of more than 0.6% is used, a starch paste or the like is applied to the back surface of the decorative sheet, or an aqueous paint is applied to the surface of the decorative sheet. When water is contained, the base material stretches, so a special gluing machine is required at the time of sticking construction, similar to the conventional decorative sheet, and workability deteriorates. If it is used for painting, problems such as opening of joints will occur.
【００１６】以上のような基材上に設けられる立体模様
層としては、従来の装飾シートと同様に合成樹脂により
構成されるものが採用される。この合成樹脂としては、
例えば、塩化ビニル系樹脂、酢酸ビニル系樹脂、塩化ビ
ニル−酢酸ビニル共重合樹脂、アクリル系樹脂、または
これらの樹脂を混合した合成樹脂ペーストに、必要に応
じて、可塑剤、安定剤、発泡剤、膨張剤、充填剤、印刷
適性改良剤、増粘剤、減粘剤、防カビ剤、消泡剤、着色
剤などの各種添加剤を添加したものや、アクリル系樹
脂、エチレン−酢酸ビニル共重合樹脂、酢酸ビニル系樹
脂などの合成樹脂エマルジョンに、必要に応じて、上記
の各種添加剤を添加したものなどが使用できる。これら
の合成樹脂ペーストや合成樹脂エマルジョンは、発泡性
のもの（すなわち、後述する膨張剤や化学発泡剤などを
含有させたものなど）であってもよいし、非発泡性のも
の（すなわち、これらが含有されていないもの）であっ
てもよい。As the three-dimensional pattern layer provided on the base material as described above, one made of a synthetic resin is adopted as in the conventional decorative sheet. As this synthetic resin,
For example, a vinyl chloride resin, a vinyl acetate resin, a vinyl chloride-vinyl acetate copolymer resin, an acrylic resin, or a synthetic resin paste obtained by mixing these resins with a plasticizer, a stabilizer, a foaming agent, if necessary. , Swelling agents, fillers, printability improvers, thickeners, thickeners, fungicides, defoamers, colorants, and other additives, acrylic resins, ethylene-vinyl acetate A synthetic resin emulsion such as a polymer resin or a vinyl acetate resin to which the above-mentioned various additives are added, if necessary, can be used. These synthetic resin pastes and synthetic resin emulsions may be foamable (that is, those containing an expanding agent or a chemical foaming agent described later) or non-foaming ones (that is, these May not be contained).
【００１７】上記した合成樹脂ペーストや合成樹脂エマ
ルジョンからなる立体模様層を発泡したものとするに
は、上記したようにペーストやエマルジョンに熱膨張剤
を含有させたマイクロカプセルなどの膨張剤、熱分解型
化学発泡剤を含有させる手段の外に、機械的撹拌手段な
どによりエアーを含有させるメカニカル発泡手段などの
を採用することもできる。In order to make the three-dimensional pattern layer made of the above-mentioned synthetic resin paste or synthetic resin emulsion foamed, an expanding agent such as microcapsules containing a thermal expansion agent in the paste or emulsion as described above, and thermal decomposition. In addition to the means for containing the type chemical foaming agent, a mechanical foaming means for containing air by a mechanical stirring means or the like can be adopted.
【００１８】基材上に立体模様層を形成する手段として
は、グラビア印刷法、スクリーン印刷法、ロータリース
クリーン印刷法、凹版印刷法など公知の手段にて、上記
の合成樹脂ペーストや合成樹脂エマルジョンを基材の上
に印刷し、加熱乾燥させ、ゲル化、発泡させることによ
り得られる。なお、このようにして形成される立体模様
層は、単層であっても複層であっても良い。As a means for forming a three-dimensional pattern layer on a substrate, known methods such as a gravure printing method, a screen printing method, a rotary screen printing method and an intaglio printing method are used, and the above synthetic resin paste or synthetic resin emulsion is used. It is obtained by printing on a substrate, heating and drying, gelling and foaming. The three-dimensional pattern layer thus formed may be a single layer or a multilayer.
【００１９】また、本発明における立体模様層は、上記
の合成樹脂ペーストや合成樹脂エマルジョンなどで単層
あるいは複層に形成した立体模様層上に、通常の印刷イ
ンキを用いて絵柄や模様などを印刷したものであっても
よい。Further, the three-dimensional pattern layer in the present invention has a pattern or a pattern formed by using ordinary printing ink on the three-dimensional pattern layer formed by the above-mentioned synthetic resin paste or synthetic resin emulsion in a single layer or a plurality of layers. It may be printed.
【００２０】[0020]
【作用】本発明の装飾シートは、基材にデンプン糊など
を使用しても基材が伸びるようなことがないため、従来
のように特別な糊付け機を用いずとも、刷毛塗りなどの
簡便な塗布手段を用いることで簡便な貼着作業が可能で
ある。しかも、本発明の装飾シートは、デンプン糊など
を基材ではなく下地材に塗布した直後に、該下地材上に
貼着しても、皺の発生がなく、かつジョイント部の収ま
りがよく、作業性が向上する。In the decorative sheet of the present invention, the base material does not stretch even if starch paste or the like is used as the base material. Therefore, it is possible to easily apply a brush or the like without using a special gluing machine as in the past. Simple application work is possible by using various application means. Moreover, the decorative sheet of the present invention has no wrinkles and has a good fit in the joint portion even when it is adhered onto the base material immediately after the starch paste or the like is applied to the base material instead of the base material, Workability is improved.
【００２１】また、装飾シートの着色やリフォームを、
水性塗料などを用いて塗装するといった簡便な手段にて
行うことができ、低コストにてリフォームを行うことが
可能であり、頻繁な居住者変更にも容易に適応すること
ができる。Also, coloring and reforming of the decorative sheet
It can be performed by a simple means such as painting with a water-based paint, can be reformed at low cost, and can be easily adapted to frequent occupant changes.
【００２２】[0022]
実施例１ パルプ成分にガラス繊維を２０ｗｔ％混抄した基材（日
本製紙株式会社製商品名“ＡＦ−ＥＸＴ”、水中伸度
０．２％）上に、表１に示す組成の塩化ビニル樹脂ペー
ストを、ロータリースクリーン法にて適宜のパターンに
印刷し、２１０℃にて１分間加熱処理して模様層を形成
し、本発明の装飾シートを調製した。Example 1 A vinyl chloride resin paste having the composition shown in Table 1 on a base material (trade name "AF-EXT" manufactured by Nippon Paper Industries Co., Ltd., elongation 0.2% in water) obtained by mixing 20 wt% of glass fibers into a pulp component. Was printed in an appropriate pattern by a rotary screen method and heat-treated at 210 ° C. for 1 minute to form a pattern layer, thereby preparing a decorative sheet of the present invention.
【００２３】[0023]
【表１】 [Table 1]
【００２４】以上のようにして得られた本発明の装飾シ
ート３枚を、室内の壁面下地材（石膏ボード）にデンプ
ン糊（ヤヨイ化学社製、商品名“アドウォール”）をロ
ーラー刷毛塗りした上に、貼着したところ、皺の発生は
見られず、ジョイント部の収まりもよく、きれいな貼着
状態であった。その後、電気式温風暖房機を用いて室温
を高めてデンプン糊を急激に乾燥させたが、各装飾シー
トのジョイント部には目開き（すなわち空隙）は生じな
かった。The three decorative sheets of the present invention obtained as described above were roller-brushed with starch paste (trade name "ADWALL", manufactured by Yayoi Chemical Co., Ltd.) on the interior wall surface material (gypsum board). No wrinkles were observed on the top, and the joint part was well fitted, and the state of attachment was clean. Then, the room temperature was raised using an electric warm air heater to rapidly dry the starch paste, but no openings (that is, voids) were formed at the joints of the decorative sheets.
【００２５】また、デンプン糊が乾燥した後、装飾シー
トの表面に市販されているベージュ色の水性塗料（アサ
ヒペン社製のカベ・浴室用のもの）をローラーにて塗布
して仕上げたところ、装飾シートに皺の発生は見られ
ず、壁面から約１ｍ離れたところから目視による観察を
行っても、ジョイント部は目立たずきれいな仕上がりが
得られた。After the starch paste was dried, a commercially available beige-colored water-based paint (a wallet made by Asahipen Corporation for bathroom) was applied on the surface of the decorative sheet with a roller to finish the decoration. No wrinkles were observed on the sheet, and even when visually observed from about 1 m away from the wall surface, the joint portion was not noticeable and a clean finish was obtained.
【００２６】実施例２ パルプ成分にポリエステル繊維を２０ｗｔ％混抄した基
材（日本製紙株式会社製商品名“ＺＢ−Ｉ９０ＰＥ”、
水中伸度０．３％）上に、表２に示す組成のアクリルエ
マルジョンを、ロータリースクリーン法にて適宜のパタ
ーンに印刷し、１６０℃にて１分間加熱処理して模様層
を形成し、本発明の装飾シートを調製した。Example 2 A base material prepared by mixing 20 wt% of polyester fiber into a pulp component (trade name "ZB-I90PE" manufactured by Nippon Paper Industries Co., Ltd.,
Acrylic emulsion having the composition shown in Table 2 was printed on a (water elongation 0.3%) in an appropriate pattern by a rotary screen method, and heat-treated at 160 ° C. for 1 minute to form a pattern layer. The decorative sheet of the invention was prepared.
【００２７】[0027]
【表２】 [Table 2]
【００２８】以上のようにして得られた本発明の装飾シ
ート３枚を、室内の壁面下地材（石膏ボード）に実施例
１で用いたデンプン糊をローラー刷毛塗りした上に、貼
着したところ、皺の発生は見られず、またジョイント部
の収まりもよく、きれいな貼着状態であった。その後、
実施例１と同様にしてデンプン糊を急激に乾燥させた
が、各装飾シートのジョイント部には目開きは生じなか
った。The three decorative sheets of the present invention obtained as described above were applied to the interior wall surface material (gypsum board) on which the starch paste used in Example 1 had been roller-brushed and then adhered. No wrinkles were found, and the joint part was well fitted, and the state of adhesion was clean. afterwards,
The starch paste was rapidly dried in the same manner as in Example 1, but no openings were formed at the joints of the decorative sheets.
【００２９】また、デンプン糊が乾燥した後、装飾シー
トの表面に実施例１と同様のベージュ色の水性塗料をロ
ーラーにて塗布して仕上げたところ、装飾シートに皺の
発生は見られず、壁面から約１ｍ離れたところから目視
による観察を行っても、ジョイント部は目立たずきれい
な仕上がりが得られた。After the starch paste was dried, the surface of the decorative sheet was coated with the same beige-colored aqueous coating material as that of Example 1 by a roller to finish, and no wrinkles were observed on the decorative sheet. Even when visually observed from about 1 m away from the wall surface, the joint portion was not noticeable and a clean finish was obtained.
【００３０】比較例１ パルプ成分のみ（実施例１のガラス繊維、実施例２のポ
リエステル繊維を混合していないパルプのみの意）で抄
造され、難燃処理加工された壁紙用原紙（日本製紙株式
会社製商品名“８０ＡＦ−１０Ｋ”、水中伸度１．２
％）を基材とする以外は、実施例１と同様にして比較の
装飾シートを調製した。Comparative Example 1 Flame-retardant base paper for wallpaper (Nippon Paper Industries Co., Ltd.), which was made from only pulp components (meaning only pulp without mixing glass fiber of Example 1 and polyester fiber of Example 2) Company name "80AF-10K", elongation in water 1.2
%) Was used as the base material, and a comparative decorative sheet was prepared in the same manner as in Example 1.
【００３１】以上のようにして得られた比較の装飾シー
ト３枚を、室内の壁面下地材（石膏ボード）に実施例１
で用いたデンプン糊をローラー刷毛塗りした上に、貼着
したところ、装飾シートの寸法変化が大きく、ジョイン
ト部の収まりが悪かった。その後、実施例１と同様にし
てデンプン糊を急激に乾燥させたが、各装飾シートのジ
ョイント部には目開きが一部生じていた。Three comparative decorative sheets obtained as described above were used as an interior wall surface material (gypsum board) in Example 1
When the starch paste used in Step 2 was applied with a roller brush and then applied, the decorative sheet showed a large dimensional change and the joint part was poorly fitted. After that, the starch paste was rapidly dried in the same manner as in Example 1, but some openings were formed in the joint portion of each decorative sheet.
【００３２】[0032]
【発明の効果】以上詳述したように、本発明の装飾シー
トによれば、次のような効果を奏することができる。As described in detail above, according to the decorative sheet of the present invention, the following effects can be obtained.
【００３３】（１）デンプン糊のような水分を含む接着
剤を使用しても、伸び率が極めて小さいため、特別の糊
付け機などを使用せずとも、刷毛塗りなどの簡単な塗布
作業により、裏面あるいは下地材に該接着剤を塗布する
のみで、下地材に容易に貼着することができる。(1) Even if an adhesive containing water such as starch paste is used, the elongation is very small. Therefore, even if a special gluing machine is not used, a simple coating operation such as brush coating can be performed. By simply applying the adhesive to the back surface or the base material, it can be easily attached to the base material.
【００３４】（２）装飾シート表面に水性タイプの塗料
を使用しても、伸び率が極めて小さいため、皺などの発
生が見られず、各装飾シート間のジョイント部が目立つ
場合には、該塗料による塗装にて、当該部分の目立ちを
極めて容易に解消することができ、また擦過傷などの傷
の補修やリフォームも該塗料による塗装にて簡単に行う
ことができる。(2) Even when a water-based paint is used on the surface of the decorative sheet, the elongation is extremely small, so that wrinkles are not observed and the joint portion between the decorative sheets is conspicuous. By coating with a paint, the conspicuousness of the portion can be eliminated extremely easily, and repair of scratches such as scratches and reforming can be easily performed by coating with the paint.
【００３５】（３）装飾シートに種々の傷や汚れが生じ
た場合には、該シートを剥がし取ることなく、該シート
表面を水性タイプの塗料による塗装にて修復あるいは新
品同様のものにすることができる。(3) When various scratches or stains occur on the decorative sheet, the surface of the sheet is restored by painting with a water-based paint or made to be like new without peeling off the sheet. You can
【００３６】（４）優れた耐水性を有するため、水のか
かり易い箇所において使用しても、皺の発生がなく、美
麗な状態を長期間保つことができる。(4) Since it has excellent water resistance, it can be kept in a beautiful state for a long period of time without wrinkling even when used in a place where it is easily splashed with water.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成６年６月１５日[Submission date] June 15, 1994
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２７[Name of item to be corrected] 0027
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２７】[0027]
【表２】 [Table 2]
Claims (1)
模様層が形成されてなることを特徴とする装飾シート。1. A decorative sheet comprising a three-dimensional pattern layer formed on a base material having an elongation in water of 0.6% or less.