JPH07266761A - Medium with security magnetic data and production thereof - Google Patents

Abstract

PURPOSE:To surely prevent forgery, unjust use, and the like, reduce the cost, eliminate a possibility that characteristics of magnetic recording may be affected, realize easy production and easy reading, and perfectly visually hide where signals and data are contained. CONSTITUTION:In a medium that is so constructed that a center core 11 made of a thermoplastic resin, such as a hard vinyl chloride, is sandwiched between over sheets 12 made of a thermoplastic resin, such as a hard vinyl chloride, at the both surfaces thereof, a random magnetic pattern 13 made of a magnetic material is provided between the center core 11 and the over sheet 12 at least on one side.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、熱可塑性樹脂からなる
クレジットカード、キャッシュカード、ＩＤカード等の
媒体およびその製造方法に係り、特に媒体本体にセキュ
リティ磁気データを付与して、媒体の偽造、改竄を防止
するようにしたセキュリティ磁気データ付き媒体および
その製造方法に関するものであめ。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a medium such as a credit card, a cash card, and an ID card made of a thermoplastic resin and a method for manufacturing the medium, and in particular, forgery the medium by adding security magnetic data to the medium body, The present invention relates to a medium with security magnetic data for preventing falsification and a manufacturing method thereof.

【０００２】[0002]

【従来の技術】近年、代金等の支払いを、クレジットカ
ード、キャッシュカード、プリペイドカード等の有価証
券類によって行なうことが、一般化してきている。そし
て、これらのカードの偽造防止対策としては、高保磁力
磁気記録、ホログラム箔のカードへの貼着、特殊インキ
の使用、磁気シールド等が実施されてきている。2. Description of the Related Art In recent years, it has become common for payments to be made using securities such as credit cards, cash cards, and prepaid cards. As measures against counterfeiting of these cards, high coercive force magnetic recording, attachment of hologram foil to cards, use of special ink, magnetic shield, etc. have been implemented.

【０００３】しかしながら、これらのセキュリティ対策
も、現時点においては、その効果が薄らいできている。However, the effect of these security measures is weakened at the present moment.

【０００４】また、使用に際しては、カード等の有価証
券が正当であるか否か、さらにその所持者が正当である
か否かを判別する必要がある。In use, it is necessary to determine whether the securities such as cards are valid, and whether the holder of the securities is valid.

【０００５】例えば、キャッシュカードの磁気データを
改竄して、他人名義のデータに書き換えたとすると、キ
ャッシュディスペンサーにおいて暗証番号さえ入力でき
れば、不正に使用することが可能となる。For example, if the magnetic data of the cash card is falsified and rewritten with the data in the name of another person, if the personal identification number can be entered in the cash dispenser, it can be used illegally.

【０００６】さらに、利用者を特定しないプリペイドカ
ード等において、使用済みカードを用意し、磁気データ
のデッドコピーが行なわれると、そのカードは有効とな
り、正当なカードと同等の価値を持ってしまうことにな
る。Further, in a prepaid card or the like which does not specify a user, when a used card is prepared and dead copy of magnetic data is performed, the card becomes valid and has the same value as a legitimate card. become.

【０００７】そこで、最近では、このような磁気データ
の改竄、不正使用を防止するために、例えば“特開昭６
３−５１２５０号公報”に開示されているように、その
チェック領域に微細にステンレスファイバをランダムに
分布、埋設した書類を使用した技術が知られている。Therefore, in recent years, in order to prevent such falsification and illegal use of magnetic data, for example, "Japanese Patent Laid-Open No. Sho 6-36
As disclosed in Japanese Patent Laid-Open No. 3-51250, there is known a technique using a document in which stainless fibers are randomly distributed and embedded in the check area.

【０００８】すなわち、これは、チェック領域にマイク
ロ波を入射して、ステンレスファイバのランダムパター
ンを読み取り、それを磁気ストライプ情報と照合するこ
とによって、当該書類の真偽をチェックするものであ
る。That is, this is to check the authenticity of the document by injecting a microwave into the check area, reading the random pattern of the stainless fiber, and comparing it with the magnetic stripe information.

【０００９】しかしながら、このような方法を、仮にカ
ードに適用した場合には、導電性のステンレスファイバ
をプラスチック製のカード基体の全体に分布させること
になるため、チェック領域以外の導電性のステンレスフ
ァイバが無駄になり、コスト高になったり、大量生産に
しか対応できなくなるという問題が生じる。However, if such a method were applied to a card, the conductive stainless fibers would be distributed over the entire plastic card substrate, so that the conductive stainless fibers other than the check area would be distributed. However, there arises a problem that it is wasted, cost is increased, and only mass production can be supported.

【００１０】また、磁気カードにおいては、その磁気記
録の特性にも影響を及ぼし、磁気記録の読み取りに支障
をきたす場合がある。Further, in a magnetic card, the characteristics of the magnetic recording may be affected, and the reading of the magnetic recording may be hindered.

【００１１】そこで、ステンレスファイバを埋設した紙
によって、サインパネルを形成することも考えられる
が、この方法では以下のような問題が生じる。Therefore, it is conceivable to form the sign panel from paper in which the stainless fiber is embedded, but this method causes the following problems.

【００１２】まず、第１に、微細なステンレスファイバ
ーを紙の抄造時に紙繊維に混ぜ込むことにより、サイン
パネルを製造するが、その製造が非常に困難である。First, a sign panel is manufactured by mixing fine stainless fibers with paper fibers during paper making, but the manufacture is very difficult.

【００１３】すなわち、微細なステンレスファイバは、
裁断等の微細加工そのものが非常に難しいと共に、その
封入時に、静電気により凝集してダマになり易く、分散
させ難い。That is, the fine stainless fiber is
It is very difficult to perform fine processing such as cutting, and at the time of encapsulation, it is easy to disperse due to aggregation due to static electricity, which makes it difficult to disperse.

【００１４】また、第２に、８μｍ程度の微細なステン
レスファイバからは、パターン情報を読み取り難い。Secondly, it is difficult to read pattern information from a fine stainless fiber of about 8 μm.

【００１５】例えば、読み取りに用いるギガヘルツ帯の
マイクロ波は、その制御が非常に難しく、読み取りの誤
差が大きい。より詳しくは、マイクロ波をステンレスフ
ァイバのランダムパターンに透過、反射させて、そのパ
ターン固有のデータを得て、このデータを相関係数に近
似させ、同一性を判断する。この場合、高精度の判断を
可能とするためには、相関係数の設定が非常に難しく、
実用性に乏しいものである。さらには、マイクロ波の読
み取り装置自体も、大型化、複雑化するという問題もあ
る。For example, the microwave of the GHz band used for reading is very difficult to control, and the reading error is large. More specifically, microwaves are transmitted and reflected in a random pattern of stainless fiber to obtain data unique to the pattern, and this data is approximated to a correlation coefficient to determine the identity. In this case, it is very difficult to set the correlation coefficient in order to enable highly accurate judgment,
It is of poor practicality. Further, there is a problem that the microwave reading apparatus itself becomes large and complicated.

【００１６】[0016]

【発明が解決しようとする課題】以上のように、従来の
カード等の媒体においては、偽造、不正使用等を防止す
ることが困難であるばかりでなく、コストが高く、また
磁気記録の特性に影響を及して磁気記録の読み取り支障
をきたし、さらに製造が困難であるという問題があっ
た。As described above, in the conventional media such as cards, it is not only difficult to prevent forgery and unauthorized use, but also the cost is high and the magnetic recording characteristics are high. This adversely affects the reading of the magnetic recording and further makes it difficult to manufacture.

【００１７】本発明は、上記のような問題点を解消する
ために成されたもので、偽造、不正使用等を確実に防止
することができると共に、コストの低減を図ることがで
き、かつ磁気記録の特性に影響を及ぼすことがなく、製
造が容易で読み取りも容易であり、さらに見た目にはど
こに信号やデータが入っているか全く分からないように
することが可能なセキュリティ磁気データ付き媒体およ
びその製造方法を提供することを目的とする。The present invention has been made to solve the above problems, and it is possible to reliably prevent counterfeiting, illegal use, etc., and to reduce the cost, and to reduce the magnetic field. A medium with security magnetic data, which does not affect the characteristics of recording, is easy to manufacture and easy to read, and has no possibility of recognizing where the signal or data is contained, and its medium. It is intended to provide a manufacturing method.

【００１８】[0018]

【課題を解決するための手段】上記の目的を達成するた
めに、硬質塩ビ等の熱可塑性樹脂からなるセンターコア
の両側を、硬質塩ビ等の熱可塑性樹脂からなるオーバー
シートで挟んだ構成とした媒体において、まず、請求項
１に係る発明では、少なくとも一方のセンターコアとオ
ーバーシートとの間に、磁性材料からなるランダムな磁
気パターンを設けて成る。In order to achieve the above object, the center core made of a thermoplastic resin such as hard PVC is sandwiched on both sides by oversheets made of a thermoplastic resin such as hard PVC. In the medium according to the first aspect of the invention, first, a random magnetic pattern made of a magnetic material is provided between at least one of the center core and the oversheet.

【００１９】また、請求項２に係る発明では、少なくと
も一方のセンターコアとオーバーシートとの間に、磁性
材料からなるランダムな磁気パターンを設け、かつオー
バーシートとランダムな磁気パターンとの間に、隠蔽層
を設けて成る。In the invention according to claim 2, a random magnetic pattern made of a magnetic material is provided between at least one of the center core and the oversheet, and between the oversheet and the random magnetic pattern, A concealing layer is provided.

【００２０】さらに、請求項３に係る発明では、少なく
とも一方のセンターコアとオーバーシートとの間に、磁
性材料からなるランダムな磁気パターンを設け、かつラ
ンダムな磁気パターンを設けた側のオーバーシート上
に、隠蔽層を設けて成る。Further, in the invention according to claim 3, a random magnetic pattern made of a magnetic material is provided between at least one of the center core and the oversheet, and on the oversheet on the side where the random magnetic pattern is provided. And a concealing layer.

【００２１】一方、硬質塩ビ等の熱可塑性樹脂からなる
センターコアの両側を、硬質塩ビ等の熱可塑性樹脂から
なるオーバーシートで挟んだ構成の媒体を製造する方法
において、まず、請求項４に係る発明では、ロール状の
オーバーシート上に、シート状のセンターコアの長さと
異なるピッチで磁性材料からなるランダムな磁気パター
ンを、所定の印刷法（グラビア印刷、スクリーン印刷、
オフセット印刷等）により少なくとも２回以上印刷し、
しかる後に、シート状のセンターコアを一枚一枚貼り合
わせて、可能な限りランダムな磁気データを付与するよ
うにしている。On the other hand, in a method for producing a medium in which both sides of a center core made of a thermoplastic resin such as hard vinyl chloride are sandwiched between oversheets made of a thermoplastic resin such as hard vinyl chloride, first, a medium according to claim 4 is concerned. In the invention, on the roll-shaped oversheet, a random magnetic pattern made of a magnetic material at a pitch different from the length of the sheet-shaped center core is subjected to a predetermined printing method (gravure printing, screen printing,
Printing at least twice more by offset printing, etc.,
After that, the sheet-shaped center cores are attached one by one to give random magnetic data as much as possible.

【００２２】また、請求項５に係る発明では、シート状
もしくはロール状のオーバーシート上に、所定の方法に
より所定の磁性材料によって、プログラム済みの所定の
ランダムな磁気パターンに印字を行ない、しかる後に、
シート状もしくはロール状のセンターコアを貼り合わせ
るようにしている。Further, in the invention according to claim 5, a programmed random magnetic pattern is printed on a sheet-shaped or roll-shaped oversheet with a predetermined magnetic material by a predetermined method, and thereafter, after that. ,
Sheet-shaped or roll-shaped center cores are stuck together.

【００２３】さらに、請求項６に係る発明では、シート
状もしくはロール状のセンターコア上に、所定の方法に
より所定の磁性材料によって、プログラム済みの所定の
ランダムな磁気パターンに印字を行ない、しかる後に、
シート状もしくはロール状のオーバーシートを貼り合わ
せるようにしている。Further, in the invention according to claim 6, a predetermined random magnetic pattern programmed is printed on a sheet-shaped or roll-shaped center core with a predetermined magnetic material by a predetermined method, and thereafter, after that. ,
Sheet-shaped or roll-shaped oversheets are pasted together.

【００２４】ここで、特に上記所定の方法による所定の
磁性材料としては、静電印刷法による磁性トナー、また
は熱転写法による磁性リボン、あるいはインキジェット
法による磁性インキのいずれかによって、プログラム済
みの所定のランダムな磁気パターンの印字を行なうよう
にしている。Here, in particular, as the predetermined magnetic material according to the above-mentioned predetermined method, either a magnetic toner by an electrostatic printing method, a magnetic ribbon by a thermal transfer method, or a magnetic ink by an ink jet method is programmed. The random magnetic pattern is printed.

【００２５】[0025]

【作用】従って、本発明に係るセキュリティ磁気データ
付き媒体およびその製造方法においては、センターコア
とオーバーシートとの間に、目視不可能な情報として、
磁性材料からなるランダムな磁気パターンを設けること
により、磁気ヘッド等の磁気センサーで出力波形を読み
取ることによって、媒体の磁気バーコードとしての情報
やランダム化された磁気パターンによる書き換えの不可
能な固有情報を得ることができ、これらの固有情報とは
別に設けられた従来の磁気ストライプへの磁気記録によ
るエンコード情報や光学バーコード情報と比較、照合す
ることによって、その媒体の真偽判定を行なうことがで
きる。Therefore, in the medium with security magnetic data and the method for manufacturing the same according to the present invention, as the invisible information between the center core and the oversheet,
By providing a random magnetic pattern made of a magnetic material and reading the output waveform with a magnetic sensor such as a magnetic head, information as a magnetic barcode of the medium or unique information that cannot be rewritten by a randomized magnetic pattern The authenticity of the medium can be determined by comparing and collating the encoded information and the optical bar code information by magnetic recording on the conventional magnetic stripe provided separately from these unique information. it can.

【００２６】すなわち、媒体本体の内部にセキュリティ
磁気データが存在するため、比較的容易に隠蔽できると
共に改竄され難く、仮に磁気ストライプ上のデータや目
視可能な光学バーコードのみがデータ改竄されたとして
も、媒体が持つ固有データとの照合を行なうことによっ
て、不真正な媒体であることを発見することができる。That is, since the security magnetic data exists inside the medium body, it can be concealed relatively easily and is not easily tampered with. Even if only the data on the magnetic stripe or the visible optical bar code is tampered with. By checking the unique data of the medium, it is possible to discover that the medium is untrue.

【００２７】また、請求項２、請求項３、および請求項
５、請求項６に係る発明のセキュリティ磁気データ付き
媒体およびその製造方法においては、オーバーシートと
ランダムな磁気パターンとの間、もしくはランダムな磁
気パターンを設けた側のオーバーシート上に、隠蔽層を
設けることにより、磁気パターンを目視不可能にして、
内部の磁気情報を完全に隠蔽することができ、より一層
効果的である。Further, in the medium with security magnetic data and the manufacturing method thereof according to the second, third, fifth, and sixth aspects of the invention, between the oversheet and the random magnetic pattern, or at random. By providing a concealing layer on the oversheet on the side where a magnetic pattern is provided, the magnetic pattern is made invisible,
The magnetic information inside can be completely hidden, which is even more effective.

【００２８】これにより、偽造、不正使用等を確実に防
止することができ、コストの低減を図ることができ、か
つ磁気記録の特性に影響を及ぼすことがなく、製造が容
易で読み取りも容易であり、さらに見た目にはどこに信
号やデータが入っているか全く分からないようにするこ
とができる。As a result, forgery, illegal use, etc. can be surely prevented, cost can be reduced, the characteristics of magnetic recording are not affected, and the manufacture and reading are easy. Yes, it can be completely opaque to the signal or data.

【００２９】[0029]

【実施例】以下、本発明の実施例について図面を参照し
て詳細に説明する。Embodiments of the present invention will now be described in detail with reference to the drawings.

【００３０】（第１の実施例）図１は、本発明の第１の
実施例によるセキュリティ磁気データ付きカードの構成
例を示す断面図である。(First Embodiment) FIG. 1 is a sectional view showing a structural example of a card with security magnetic data according to the first embodiment of the present invention.

【００３１】すなわち、本実施例のセキュリティ磁気デ
ータ付きカードは、図１に示すように、硬質塩ビ等の熱
可塑性樹脂からなるセンターコア１１の両側を、やはり
硬質塩ビ等の熱可塑性樹脂からなるオーバーシート１２
で挟み、一方のセンターコア１１とオーバーシート１２
との間に、磁性材料からなるランダムな磁気パターン１
３を設けた構成としている。That is, in the card with security magnetic data of this embodiment, as shown in FIG. 1, both sides of the center core 11 made of a thermoplastic resin such as hard vinyl chloride are overlaid with a thermoplastic resin such as hard vinyl chloride. Sheet 12
It is sandwiched between the center core 11 and the overseat 12
Random magnetic pattern 1 made of magnetic material between
3 is provided.

【００３２】（第２の実施例）図２は、本発明の第２の
実施例によるセキュリティ磁気データ付きカードの構成
例を示す断面図である。(Second Embodiment) FIG. 2 is a sectional view showing a structural example of a card with security magnetic data according to the second embodiment of the present invention.

【００３３】すなわち、本実施例のセキュリティ磁気デ
ータ付きカードは、図２に示すように、硬質塩ビ等の熱
可塑性樹脂からなるセンターコア２１の両側を、やはり
硬質塩ビ等の熱可塑性樹脂からなるオーバーシート２２
で挟み、一方のセンターコア２１とオーバーシート２２
との間に、磁性材料からなるランダムな磁気パターン２
３を設け、さらにオーバーシート２２とランダムな磁気
パターン２３との間に、隠蔽層２４を設けた構成として
いる。That is, in the card with security magnetic data of the present embodiment, as shown in FIG. 2, both sides of the center core 21 made of a thermoplastic resin such as hard PVC are overlaid also with a thermoplastic resin such as hard PVC. Seat 22
It is sandwiched between one center core 21 and the overseat 22.
Random magnetic pattern 2 made of magnetic material between
3 is provided, and a concealing layer 24 is provided between the oversheet 22 and the random magnetic pattern 23.

【００３４】（第３の実施例）図３は、本発明の第３の
実施例によるセキュリティ磁気データ付きカードの構成
例を示す断面図である。(Third Embodiment) FIG. 3 is a sectional view showing a structural example of a card with security magnetic data according to a third embodiment of the present invention.

【００３５】すなわち、本実施例のセキュリティ磁気デ
ータ付きカードは、図３に示すように、硬質塩ビ等の熱
可塑性樹脂からなるセンターコア３１の両側を、やはり
硬質塩ビ等の熱可塑性樹脂からなるオーバーシート３２
で挟み、一方のセンターコア３１とオーバーシート３２
との間に、磁性材料からなるランダムな磁気パターン３
３を設け、さらにランダムな磁気パターン３３を設けた
側のオーバーシート３２上に、隠蔽層３４を設けた構成
としている。That is, in the card with security magnetic data of the present embodiment, as shown in FIG. 3, both sides of the center core 31 made of a thermoplastic resin such as hard PVC are overlaid with a thermoplastic resin such as hard PVC. Sheet 32
It is sandwiched between one center core 31 and the overseat 32.
Random magnetic pattern 3 made of magnetic material between
3 is provided, and the concealing layer 34 is provided on the oversheet 32 on the side where the random magnetic pattern 33 is provided.

【００３６】ここで、センターコア１１，２１，３１、
およびオーバーシート１２，２２，３２の材料として用
いられる熱可塑性樹脂としては、例えば硬質塩化ビニ
ル、軟質塩化ビニル、ポリカーポネート、アクリル、ポ
リエステル、ＡＢＳ、セルロース、ポリプロピレン、ポ
リエチレン等の樹脂フィルムまたはシートを用いること
ができる。Here, the center cores 11, 21, 31,
As the thermoplastic resin used as the material of the oversheets 12, 22, 32, for example, resin film or sheet of hard vinyl chloride, soft vinyl chloride, polycarbonate, acrylic, polyester, ABS, cellulose, polypropylene, polyethylene, etc. Can be used.

【００３７】特に、熱可塑性樹脂である必要性は、熱プ
レス加工による熱融着がし易く、またエンボス等の後に
加工を施し易いためであり、これらの中でも硬質塩ビが
最も多く用いられる。Particularly, the necessity of being a thermoplastic resin is because it is easy to perform heat fusion by hot pressing, and it is easy to perform processing after embossing, and among these, hard PVC is most often used.

【００３８】また、磁気パターン１３、２３、３３は、
カードに固有の磁気的情報を付与するものであり、セン
ターコア１１，２１，３１、もしくはオーバーシート１
２，２２，３２上に、例えば図４に示すような磁気パタ
ーン４４として、印刷、転写、蒸着、分散、印字等の方
法により設けることができる。The magnetic patterns 13, 23 and 33 are
Magnetic information unique to the card is added to the center cores 11, 21, 31 or the oversheet 1.
The magnetic patterns 44 as shown in FIG. 4, for example, can be provided on 2, 22, 32 by a method such as printing, transfer, vapor deposition, dispersion, or printing.

【００３９】そして、この磁気パターン１３、２３、３
３を設けるための磁性材料としては、例えばＦｅ、Ｎ
ｉ、Ｍｎ、Ｚｎ、Ｃｏ、パーマロイ、センダスト、Ｍｎ
−Ｚｎフェライト、Ｎｉ−Ｚｎフェライト、Ｍｎフェラ
イト、Ｚｎフェライト、ＦｅＳ、マグネタイト、γ−酸
化鉄、Ｃｏ被着γ−酸化鉄、バリウムフェライト、スト
ロンチウムフェライト、二酸化クロム等の金属・合金及
び金属化合物の粉末もしくはワイヤー等を使用すること
ができるが、保磁力が６００ｅ以下の軟質磁性材料を用
いるのがより好ましい。The magnetic patterns 13, 23, 3
As the magnetic material for providing 3, Fe, N
i, Mn, Zn, Co, permalloy, sendust, Mn
-Zn ferrite, Ni-Zn ferrite, Mn ferrite, Zn ferrite, FeS, magnetite, γ-iron oxide, Co-deposited γ-iron oxide, barium ferrite, strontium ferrite, chromium dioxide and other metals / alloys and metal compound powders Alternatively, a wire or the like can be used, but it is more preferable to use a soft magnetic material having a coercive force of 600e or less.

【００４０】また、保磁力が６００ｅ以下の軟質磁性材
料を用いるのは、３００ガウス以下の弱い外部バイアス
磁場にも材料が応答し出力が得られると共に、読み取り
の際のバイアス磁場による残留磁化が極めて少ないた
め、マグネットビューアーや磁性流体等によってもその
磁気材料の着磁パターンが見えず、セキュリティ上好ま
しいためである。The soft magnetic material having a coercive force of 600 e or less is used because the material responds to a weak external bias magnetic field of 300 Gauss or less to obtain an output, and the residual magnetization due to the bias magnetic field during reading is extremely high. Because the number is small, the magnetization pattern of the magnetic material cannot be seen even by a magnet viewer or a magnetic fluid, which is preferable for security.

【００４１】さらに、隠蔽層２４、３４は、磁性材料の
茶褐色から黒色の色相を目視不可能にする目的のもので
あり、例えばＡｌ、Ｓｎ、Ｃｕ等の金属を蒸着、スパッ
タリング等の方法により設けた金属薄膜、Ａｌ、Ｎｉ、
パーマロイ、眞ちゅう等の鱗片状の金属粉末をバインダ
ー中に分散させた塗膜を使用することができるが、金属
を用いた場合、下層の磁気パターン２３、３３のデータ
を忠実に読み取るためには、非磁性金属であることがよ
り望ましい。Further, the hiding layers 24 and 34 are provided for the purpose of making the dark brown to black hue of the magnetic material invisible. For example, a metal such as Al, Sn, or Cu is provided by a method such as vapor deposition or sputtering. Thin metal film, Al, Ni,
It is possible to use a coating film in which a scale-like metal powder such as permalloy or cinnabar is dispersed in a binder. However, when a metal is used, in order to faithfully read the data of the magnetic patterns 23 and 33 of the lower layer, More preferably, it is a non-magnetic metal.

【００４２】また、その他のものとしては、例えば硫化
亜鉛、酸化亜鉛、酸化チタン、硫酸バリウム等の白色度
の高い隠蔽性顔料をやはりバインダー中に分散させた塗
膜、あるいはカーボンブラック、酸化鉄等の黒色または
茶褐色系の濃い色相の隠蔽性顔料をバインダー中に分散
させた塗膜等を用いることができるが、金属の場合と同
様に、各種顔料についても、データ読み取りの正確性と
いう点からは非磁性顔料であることがより望ましい。Other examples include a coating film in which a hiding pigment having high whiteness such as zinc sulfide, zinc oxide, titanium oxide, barium sulfate, etc. is also dispersed in a binder, carbon black, iron oxide, etc. It is possible to use a coating film or the like in which a black or brownish dark-hued concealing pigment having a dark hue is dispersed in a binder. More preferably, it is a non-magnetic pigment.

【００４３】なお、各層の間の接着性は、磁気パターン
１３，２３、３３、隠蔽層２４、３４等のバインダー樹
脂系の選択によって、加熱接着、熱融着が可能である
が、必要に応じて、接着剤層を設けることにより、より
耐久性や耐候性に優れたカードを作成することができ
る。The adhesiveness between the layers can be heat-bonded or heat-sealed by selecting a binder resin system such as the magnetic patterns 13, 23, 33 and the concealing layers 24, 34. By providing the adhesive layer, a card having more excellent durability and weather resistance can be prepared.

【００４４】次に、本発明によるセキュリティ磁気デー
タ付きカードの製造方法について、図５ないし図７を用
いて具体的に説明する。Next, a method of manufacturing a card with security magnetic data according to the present invention will be specifically described with reference to FIGS.

【００４５】（具体例１）ロール状の透明硬質塩ビ樹脂
（住友ベークライト、１００μｍ）上に、マグネタイト
（Ｆｅ₃ Ｏ₄ 、保磁力１００Ｏｅ）磁性顔料１００部
を、塩化ビニル−酸ビニル共重合体（積水化学、エスレ
ックＡ）３０部、ポリウレタン樹脂（日本ポリウレタ
ン、Ｎ２３０４、不揮発分４０％）５０部、ＭＥＫ／ト
ルエン（＝１／１）からなる高分子樹脂溶液中に分散さ
せたグラビア用磁性インキを、図４に示すように、線幅
と間隔および角度がランダムな格子パターンをエンドレ
スに製版したシリンダー径が２２インチのグラビア版
（版深３０μｍ）にてロールの全面に印刷を行ない、カ
ードのオーバーシートとした。(Specific Example 1) 100 parts of a magnetic pigment (Fe ₃ O ₄ , coercive force of 100 Oe) magnetic pigment and a vinyl chloride-vinyl acetate copolymer (on a transparent hard vinyl chloride resin in roll form (Sumitomo Bakelite, 100 μm)) Sekisui Chemical Co., Ltd., Eslek A) 30 parts, polyurethane resin (Nippon Polyurethane, N2304, non-volatile content 40%) 50 parts, magnetic ink for gravure dispersed in a polymer resin solution consisting of MEK / toluene (= 1/1) As shown in FIG. 4, a gravure plate with a cylinder diameter of 22 inches (plate depth 30 μm) in which a grid pattern with random line widths, intervals and angles was plateless was used to print over the entire surface of the roll, and the card was overprinted. It was a sheet.

【００４６】さらに、反対面側のオーバーシートとし
て、磁性印刷処理していない上記ロール状の硬質塩化ビ
ニル樹脂を用意し、シート状の白色硬質塩化ビニル樹脂
（住友ベークライト、５６０μｍ）の両側から重ね合わ
せ、摂氏１４０度、５０Ｋｇ／ｃｍ、５０分間のプレス
条件で熱融着を行ない、セキュリティ磁気データ付きカ
ードを作製した。Further, as the oversheet on the opposite side, the roll-shaped hard vinyl chloride resin which has not been magnetically printed is prepared, and the sheet-shaped white hard vinyl chloride resin (Sumitomo Bakelite, 560 μm) is overlaid from both sides. Then, heat fusion was performed under a pressing condition of 140 degrees Celsius, 50 Kg / cm, and 50 minutes to prepare a card with security magnetic data.

【００４７】（具体例２）上記具体例１において、ロー
ル状の透明硬質塩ビ樹脂上に磁性インキを印刷する前
に、５０オングストロームの膜厚となるようにＡｌ蒸着
を行ない、隠蔽層を設けた後に、具体例１の場合と同様
に、磁性インキを印刷し、センターコアともう片方のオ
ーバーシートとを熱融着によって貼り合わせ、セキュリ
ティ磁気データ付きカードを作製した。(Specific Example 2) In the above specific example 1, before printing the magnetic ink on the roll-shaped transparent hard PVC resin, Al vapor deposition was carried out so as to have a film thickness of 50 angstroms to provide a hiding layer. After that, as in the case of Example 1, magnetic ink was printed, and the center core and the other oversheet were bonded by heat fusion to produce a card with security magnetic data.

【００４８】（具体例３）上記具体例１において、熱融
着により貼り合わせた後に、磁性印刷を施した側のオー
バーシート上に、Ａｌペースト（東洋アルミ、＃２００
０、不揮発分６０％）１００部をスクリーンメジウム
（東洋インキ、＃８０００、塩化ビニル−酢酸ビニル共
重合体／アクリル樹脂、不揮発分４０％）１００中に分
散させたシルバー系スクリーンインキを用いて、乾燥後
の膜厚が３μｍとなるようにベタ印刷を行ない、隠蔽層
を設けた。(Specific Example 3) In the above specific example 1, Al paste (Toyo Aluminum, # 200, Toyo Aluminum, # 200) was applied on the oversheet on the side where magnetic printing was performed, after bonding by heat fusion.
0, non-volatile content 60%) 100 parts of screen medium (Toyo Ink, # 8000, vinyl chloride-vinyl acetate copolymer / acrylic resin, non-volatile content 40%) 100 were dispersed in silver-based screen ink, Solid printing was performed so that the film thickness after drying was 3 μm, and a hiding layer was provided.

【００４９】（具体例４）上記具体例１において、ロー
ル状の透明硬質塩ビ樹脂上に磁性インキをグラビア印刷
する代わりに、マグネタイト（３０Ｏｅ、Ｆｅ₂ Ｏ₃ ）
１００部をアクリル樹脂（ローム＆ハース社、パラロイ
ドＡ−３０）５０部、塩化ビニル−酢酸ビニル共重合体
（ＵＣＣ ＶＡＧＨ）５０部、ＭＥＫ／トルエン（＝１
／１）１００部からなる高分子樹脂溶液中に分散させた
塗料を、２５μｍの透明ＰＥＴフィルム上に、乾燥後の
膜厚７μｍとなるように塗布して、乾燥させたものを磁
性リボンとし、図６に示すように、例えばサーマル印字
ヘッドによる熱転写法によって磁性バーコードの印字を
行ない、カードのＩＤとして設けた。(Specific Example 4) In Specific Example 1, magnetite (30 Oe, Fe ₂ O ₃ ) was used instead of gravure-printing the magnetic ink on the roll-shaped transparent hard PVC resin.
100 parts of acrylic resin (Rohm & Haas Company, Paraloid A-30) 50 parts, vinyl chloride-vinyl acetate copolymer (UCC VAGH) 50 parts, MEK / toluene (= 1)
/ 1) A coating material dispersed in a polymer resin solution consisting of 100 parts was applied onto a transparent PET film having a thickness of 25 µm so that the film thickness after drying was 7 µm, and the dried material was used as a magnetic ribbon, As shown in FIG. 6, for example, a magnetic bar code was printed by a thermal transfer method using a thermal print head, and was provided as a card ID.

【００５０】その後、上記具体例１の場合と同様に、セ
ンターコアともう片方のオーバーシートとを熱融着によ
って貼り合わせ、セキュリティ磁気データ付きカードを
作製した。Then, in the same manner as in the above-mentioned specific example 1, the center core and the other oversheet were bonded by heat fusion to manufacture a card with security magnetic data.

【００５１】（具体例５）図７に示すように、シート状
の白色硬質塩化ビニル樹脂（住友ベークライト、５６０
μｍ）上に、マグネタイト磁性粉（１００Ｏｅ、Ｆｅ₃
Ｏ₄ ）と熱可塑性樹脂からなる磁性トナーを用い、例え
ば静電印刷法により、カードの固有番号としての磁性文
字を印字した後に、シート状の透明硬質塩ビ樹脂（住友
ベークライト、１００μｍ）をオーバーシートとしてセ
ンタコアの両側に重ね合わせ、摂氏１４０度、５０Ｋｇ
／ｃｍ、５０分間のプレス条件で熱融着を行ない、セキ
ュリティ磁気データ付きカードを作製した。(Specific Example 5) As shown in FIG. 7, a sheet-shaped white hard vinyl chloride resin (Sumitomo Bakelite, 560
magnetite magnetic powder (100 Oe, Fe ₃
O ₄ ) and a magnetic toner composed of a thermoplastic resin are used to print magnetic characters as a unique number of the card by, for example, electrostatic printing, and then a sheet-shaped transparent hard PVC resin (Sumitomo Bakelite, 100 μm) is oversheeted. On both sides of the center core, 140 degrees Celsius, 50Kg
Fusing was performed under a pressing condition of 50 cm / cm for 50 minutes to produce a card with security magnetic data.

【００５２】（具体例６）上記具体例５において、シー
ト状の白色硬質塩化ビニル樹脂上に磁性トナーによって
静電印刷を行なう代わりに、マグネタイト磁性粉 （１
００Ｏｅ、Ｆｅ₃Ｏ₄ ）１００部をポリエステル樹脂
（東洋紡、バイロン１０３）１００部、トルエン／アセ
トン／ＩＰＡ（＝２／１／１）２００部からなる高分子
樹脂溶液中に分散させたインキを用いて、インキジェッ
ト法により、カードの固有番号としての磁性文字を印字
した後に、上記具体例５の場合と同様に、オーバーシー
ト加工を行ない、セキュリティ磁気データ付きカードを
作製した。(Specific Example 6) In the above specific example 5, instead of performing electrostatic printing with magnetic toner on the sheet-shaped white hard vinyl chloride resin, magnetite magnetic powder (1
An ink in which 100 parts of 00Oe, Fe ₃ O ₄ ) is dispersed in a polymer resin solution consisting of 100 parts of a polyester resin (TOYOBO, Byron 103) and 200 parts of toluene / acetone / IPA (= 2/1/1) is used. Then, magnetic characters as the unique number of the card were printed by the ink jet method, and then oversheet processing was carried out in the same manner as in the above-mentioned specific example 5 to produce a card with security magnetic data.

【００５３】なお、図５ないし図７において、５１，６
１，７１はシート状センターコア、５２，６２はロール
状オーバーシート、７２はシート状オーバーシート、５
３は磁気パターン、６３は磁気バーコード、７３は磁性
文字、６４，７４は印字ヘッド（静電印刷、または熱転
写、あるいはインキジェット）をそれぞれ示している。It should be noted that in FIGS.
1, 71 is a sheet-shaped center core, 52 and 62 are roll-shaped oversheets, 72 is a sheet-shaped oversheet, 5
3 is a magnetic pattern, 63 is a magnetic bar code, 73 is a magnetic character, and 64 and 74 are print heads (electrostatic printing, thermal transfer, or ink jet).

【００５４】次に、以上のように構成した第１ないし第
３の各実施例のセキュリティ磁気データ付きカードにお
いては、センターコア１１，２１，３１とオーバーシー
ト１２，２２，３２との間に、目視不可能な情報とし
て、磁性材料からなるランダムな磁気パターン１３，２
３，３３を設けていることにより、磁気ヘッド等の磁気
センサーで出力波形を読み取ることによって、媒体の磁
気バーコードとしての情報やランダム化された磁気パタ
ーンによる書き換えの不可能な固有情報を得ることがで
き、これらの固有情報とは別に設けられた従来の磁気ス
トライプへの磁気記録によるエンコード情報や光学バー
コード情報を比較、照合することによって、その媒体の
真偽判定を行なうことができる。Next, in the card with security magnetic data of each of the first to third embodiments configured as described above, between the center cores 11, 21, 31 and the oversheets 12, 22, 32, Random magnetic patterns 13 and 2 made of magnetic material are used as invisible information.
By providing 3, 33, it is possible to obtain the information as a magnetic bar code of the medium or the unique information that cannot be rewritten by the randomized magnetic pattern by reading the output waveform with a magnetic sensor such as a magnetic head. The authenticity of the medium can be determined by comparing and collating the encoded information and the optical barcode information by the magnetic recording on the conventional magnetic stripe provided separately from the unique information.

【００５５】すなわち、媒体本体の内部にセキュリティ
磁気データが存在するため、比較的容易に隠蔽できると
共に改竄され難く、仮に磁気ストライプ上のデータや目
視可能な光学バーコードのみがデータ改竄されたとして
も、媒体が持つ固有データとの照合を行なうことによっ
て、不真正な媒体であることを発見することができる。That is, since the security magnetic data exists inside the medium body, it can be concealed relatively easily and is not easily tampered with. Even if only the data on the magnetic stripe or the visible optical bar code is tampered with. By checking the unique data of the medium, it is possible to discover that the medium is untrue.

【００５６】より具体的には、これらのカード内部の磁
気情報は、磁気センサーにより読み出すことが可能であ
り、読み出した磁気固定情報を何らかの形で演算、暗号
化の後、カード上の磁気ストライプ（磁気記録層）への
磁気記録やサーマルリボンによる光学バーコード記録等
の他の記録方法によって記録、エンコードしておくこと
によって、カード自身の持つ磁気固定情報との比較が可
能となり、仮に磁気ストライプ上のエンコード情報や光
学バーコード情報が改竄されると、カード自身の持つ磁
気固定情報との照合ができなくなり、不正使用が発見で
きる。More specifically, the magnetic information inside these cards can be read by a magnetic sensor, and the read magnetic fixed information is calculated and encrypted in some form, and then the magnetic stripe ( By recording and encoding by other recording methods such as magnetic recording on the magnetic recording layer) or optical bar code recording with a thermal ribbon, it becomes possible to compare with the magnetic fixed information that the card itself has, and temporarily on the magnetic stripe. If the encoded information or optical barcode information of the card is tampered with, it will not be possible to collate it with the magnetic fixed information of the card itself, and unauthorized use can be found.

【００５７】さらに、第２および第３の各実施例のセキ
ュリティ磁気データ付きカードにおいては、オーバーシ
ート２２，３２とランダムな磁気パターン２３，３３と
の間、もしくはランダムな磁気パターン２３，３３を設
けた側のオーバーシート２２，３２上に、隠蔽層２４，
３４を設けていることにより、磁気パターン２３，３３
を目視不可能にして、内部の磁気情報を完全に隠蔽する
ことができ、より一層効果的である。Further, in the cards with security magnetic data of the second and third embodiments, the magnetic sheets 23, 33 are provided between the oversheets 22, 32 and the random magnetic patterns 23, 33 or the random magnetic patterns 23, 33. On the upper side oversheets 22 and 32, the hiding layer 24,
By providing 34, the magnetic patterns 23, 33
Is made invisible and the magnetic information inside can be completely hidden, which is even more effective.

【００５８】すなわち、第２および第３の各実施例のセ
キュリティ磁気データ付きカードは、カード内部に磁性
材料からなる固有データもしくは固有番号という情報を
持っており、特に隠蔽層２４，３４をオーバーシート２
２，３２の表面もしくは裏面に設けることにより、内部
の磁気情報を完全に隠蔽することができ、極めて効果的
である。That is, the cards with security magnetic data according to the second and third embodiments have the information of the unique data or the unique number of the magnetic material inside the cards, and in particular, the cover layers 24 and 34 are oversheeted. Two
By providing on the front surface or the back surface of 2, 32, the magnetic information inside can be completely hidden, which is extremely effective.

【００５９】上述したように、本各実施例においては、
硬質塩ビ等の熱可塑性樹脂からなるセンターコア１１の
両側を、やはり硬質塩ビ等の熱可塑性樹脂からなるオー
バーシート１２で挟み、一方のセンターコア１１とオー
バーシート１２との間に、磁性材料からなるランダムな
磁気パターン１３を設けるか、または、硬質塩ビ等の熱
可塑性樹脂からなるセンターコア２１の両側を、やはり
硬質塩ビ等の熱可塑性樹脂からなるオーバーシート２２
で挟み、一方のセンターコア２１とオーバーシート２２
との間に、磁性材料からなるランダムな磁気パターン２
３を設け、さらにオーバーシート２２とランダムな磁気
パターン２３との間に、隠蔽層２４を設けるか、もしく
は、硬質塩ビ等の熱可塑性樹脂からなるセンターコア３
１の両側を、やはり硬質塩ビ等の熱可塑性樹脂からなる
オーバーシート３２で挟み、一方のセンターコア３１と
オーバーシート３２との間に、磁性材料からなるランダ
ムな磁気パターン３３を設け、さらにランダムな磁気パ
ターン３３を設けた側のオーバーシート３２上に、隠蔽
層３４を設ける構成としたものである。As described above, in each of the embodiments,
Both sides of the center core 11 made of a thermoplastic resin such as hard vinyl chloride are sandwiched by oversheets 12 also made of a thermoplastic resin such as hard vinyl chloride, and made of a magnetic material between the one center core 11 and the oversheet 12. Random magnetic patterns 13 are provided, or both sides of a center core 21 made of a thermoplastic resin such as hard vinyl chloride are provided on both sides of an oversheet 22 also made of a thermoplastic resin such as hard vinyl chloride.
It is sandwiched between one center core 21 and the overseat 22.
Random magnetic pattern 2 made of magnetic material between
3 and a concealing layer 24 between the oversheet 22 and the random magnetic pattern 23, or a center core 3 made of a thermoplastic resin such as hard PVC.
Both sides of 1 are sandwiched between oversheets 32 also made of a thermoplastic resin such as hard vinyl chloride, and a random magnetic pattern 33 made of a magnetic material is provided between one center core 31 and the oversheet 32, and further random The concealing layer 34 is provided on the oversheet 32 on the side where the magnetic pattern 33 is provided.

【００６０】従って、カード内の特に完全に隠蔽された
磁気パターン１３，２３，３３は、目視不可能であり、
磁性流体等の磁気現像剤においても磁気パターン１３，
２３，３３を読み取ることが不可能であると共に、耐候
性にも優れており、またこのカード内部のセキュリティ
情報を読み取り、磁気ストライプや光学バーコード等の
カード内の記録情報と比較照合することによって、デー
タの偽造や改竄の極めて困難なカードを得ることが可能
となる。Therefore, the magnetic patterns 13, 23 and 33, which are completely hidden in the card, are invisible.
Even in a magnetic developer such as a magnetic fluid, the magnetic pattern 13,
It is impossible to read 23, 33 and has excellent weather resistance. Also, by reading the security information inside this card and comparing and collating it with the recorded information inside the card such as magnetic stripes and optical bar codes. It is possible to obtain a card that is extremely difficult to forge or falsify data.

【００６１】さらに、必要に応じて、オーバーシート２
２，３２とランダムな磁気パターン２３，３３との間、
もしくはランダムな磁気パターン２３，３３を設けた側
のオーバーシート２２，３２上に、隠蔽層２４，３４を
設けるようにすれば、磁気パターン２３，３３を目視不
可能にして、内部の磁気情報を完全に隠蔽することがで
き、より一層効果的である。Further, if necessary, the oversheet 2
2,32 and random magnetic patterns 23,33,
Alternatively, if the concealing layers 24 and 34 are provided on the oversheets 22 and 32 on the side where the random magnetic patterns 23 and 33 are provided, the magnetic patterns 23 and 33 are made invisible and the internal magnetic information is stored. It can be completely hidden and is even more effective.

【００６２】尚、本発明は上記各実施例に限定されるも
のではなく、次のようにしても同様に実施できるもので
ある。The present invention is not limited to the above embodiments, but can be implemented in the same manner as described below.

【００６３】（ａ）上記各実施例では、一方のセンター
コアとオーバーシートの間に、磁性材料からなる磁気パ
ターンを設ける場合について説明したが、これに限ら
ず、両方のセンターコアとオーバーシートの間に、磁性
材料からなる磁気パターンを設ける場合についても、本
発明を同様に適用して前述の場合と同様の効果が得られ
るものである。(A) In each of the above-described embodiments, the case where the magnetic pattern made of a magnetic material is provided between one of the center cores and the overseat has been described. However, the present invention is not limited to this. Even when a magnetic pattern made of a magnetic material is provided in between, the present invention is similarly applied and the same effect as the above case can be obtained.

【００６４】（ｂ）本発明において、センターコアとオ
ーバーシートの間に設ける磁気パターンとしては、上記
各実施例で説明したものに限定されるものではなく、そ
の他のランダムなパターンの磁気パターンを設けるよう
にしてもよいことは言うまでもない。(B) In the present invention, the magnetic pattern provided between the center core and the oversheet is not limited to that described in each of the above embodiments, and other random magnetic patterns are provided. It goes without saying that you can do so.

【００６５】（ｃ）本発明において、磁性材料からなる
ランダムな磁気パターンを設ける方法としては、グラビ
ア印刷、スクリーン印刷、オフセット印刷等の所定の印
刷法を適用することが可能である。(C) In the present invention, as a method for providing a random magnetic pattern made of a magnetic material, a predetermined printing method such as gravure printing, screen printing or offset printing can be applied.

【００６６】[0066]

【発明の効果】以上説明したように本発明によれば、硬
質塩ビ等の熱可塑性樹脂からなるセンターコアの両側
を、硬質塩ビ等の熱可塑性樹脂からなるオーバーシート
で挟んだ構成とした媒体において、少なくとも一方のセ
ンターコアとオーバーシートとの間に、磁性材料からな
るランダムな磁気パターンを設け、さらに必要に応じ
て、オーバーシートとランダムな磁気パターンとの間、
もしくはランダムな磁気パターンを設けた側のオーバー
シート上に、隠蔽層を設けて構成するようにしたので、
偽造、不正使用等を確実に防止することができると共
に、コストの低減を図ることができ、かつ磁気記録の特
性に影響を及ぼすことがなく、製造が容易で読み取りも
容易であり、さらに見た目にはどこに信号やデータが入
っているか全く分からないようにすることが可能なセキ
ュリティ磁気データ付き媒体およびその製造方法が提供
できる。As described above, according to the present invention, in a medium in which both sides of a center core made of a thermoplastic resin such as hard PVC are sandwiched by oversheets made of a thermoplastic resin such as hard PVC. , A random magnetic pattern made of a magnetic material is provided between at least one of the center core and the oversheet, and, if necessary, between the oversheet and the random magnetic pattern,
Alternatively, since the hiding layer is provided on the oversheet on the side where the random magnetic pattern is provided,
Forgery and unauthorized use can be reliably prevented, cost can be reduced, characteristics of magnetic recording are not affected, manufacturing is easy, and reading is easy. It is possible to provide a medium with security magnetic data and a method for manufacturing the medium, which makes it possible to completely not know where a signal or data is contained.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明によるセキュリティ磁気データ付きカー
ドの第１の実施例を示す断面図。FIG. 1 is a sectional view showing a first embodiment of a card with security magnetic data according to the present invention.

【図２】本発明によるセキュリティ磁気データ付きカー
ドの第２の実施例を示す断面図。FIG. 2 is a sectional view showing a second embodiment of the card with security magnetic data according to the present invention.

【図３】本発明によるセキュリティ磁気データ付きカー
ドの第３の実施例を示す断面図。FIG. 3 is a sectional view showing a third embodiment of a card with security magnetic data according to the present invention.

【図４】本発明のセキュリティ磁気データ付きカードに
使用される磁気パターンの一例を示す概要図。FIG. 4 is a schematic diagram showing an example of a magnetic pattern used in the card with security magnetic data of the present invention.

【図５】本発明によるセキュリティ磁気データ付きのカ
ードの製造方法の一例を説明するための概要図。FIG. 5 is a schematic diagram for explaining an example of a method for manufacturing a card with security magnetic data according to the present invention.

【図６】本発明によるセキュリティ磁気データ付きのカ
ードの製造方法の他の例を説明するための概要図。FIG. 6 is a schematic diagram for explaining another example of the method for manufacturing a card with security magnetic data according to the present invention.

【図７】本発明によるセキュリティ磁気データ付きのカ
ードの製造方法の他の例を説明するための概要図。FIG. 7 is a schematic diagram for explaining another example of the method for manufacturing a card with security magnetic data according to the present invention.

【符号の説明】[Explanation of symbols]

１１…センターコア、１２…オーバーシート、１３…磁
気パターン、２１…センターコア、２２…オーバーシー
ト、２３…磁気パターン、２４…隠蔽層、３１…センタ
ーコア、３２…オーバーシート、３３…磁気パターン、
３４…隠蔽層、４４…磁気パターン、５１…シート状セ
ンターコア、５２…ロール状オーバーシート、５３…磁
気パターン、６１…シート状センターコア、６２…ロー
ル状オーバーシート、６３…磁気バーコード、６４…印
字ヘッド（静電印刷、または熱転写、あるいはインキジ
ェット）、７１…シート状センターコア、７２…シート
状オーバーシート、７３…磁性文字、７４…印字ヘッド
（静電印刷、または熱転写、あるいはインキジェッ
ト）。11 ... Center core, 12 ... Oversheet, 13 ... Magnetic pattern, 21 ... Center core, 22 ... Oversheet, 23 ... Magnetic pattern, 24 ... Hiding layer, 31 ... Center core, 32 ... Oversheet, 33 ... Magnetic pattern,
34 ... Concealment layer, 44 ... Magnetic pattern, 51 ... Sheet-shaped center core, 52 ... Roll-shaped oversheet, 53 ... Magnetic pattern, 61 ... Sheet-shaped center core, 62 ... Roll-shaped oversheet, 63 ... Magnetic bar code, 64 ... print head (electrostatic printing, thermal transfer, or ink jet), 71 ... sheet-shaped center core, 72 ... sheet-shaped oversheet, 73 ... magnetic characters, 74 ... print head (electrostatic printing, thermal transfer, or ink jet) ).

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成とした媒体において、 少なくとも一方の前記センターコアとオーバーシートと
の間に、磁性材料からなるランダムな磁気パターンを設
けて成ることを特徴とするセキュリティ磁気データ付き
カード。1. A medium having a structure in which both sides of a center core made of a thermoplastic resin such as hard PVC are sandwiched between oversheets made of a thermoplastic resin such as hard PVC, at least one of the center core and the oversheet A card with security magnetic data, characterized in that a random magnetic pattern made of a magnetic material is provided between the two. 【請求項２】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成とした媒体において、 少なくとも一方の前記センターコアとオーバーシートと
の間に、磁性材料からなるランダムな磁気パターンを設
け、 かつ前記オーバーシートとランダムな磁気パターンとの
間に、隠蔽層を設けて成ることを特徴とするセキュリテ
ィ磁気データ付き媒体。2. A medium having a structure in which both sides of a center core made of a thermoplastic resin such as hard PVC are sandwiched between oversheets made of a thermoplastic resin such as hard PVC, at least one of the center core and the oversheet A medium with security magnetic data, characterized in that a random magnetic pattern made of a magnetic material is provided between, and a concealing layer is provided between the oversheet and the random magnetic pattern. 【請求項３】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成とした媒体において、 少なくとも一方の前記センターコアとオーバーシートと
の間に、磁性材料からなるランダムな磁気パターンを設
け、 かつ前記ランダムな磁気パターンを設けた側のオーバー
シート上に、隠蔽層を設けて成ることを特徴とするセキ
ュリティ磁気データ付き媒体。3. A medium having a structure in which both sides of a center core made of a thermoplastic resin such as hard PVC are sandwiched between oversheets made of a thermoplastic resin such as hard PVC, at least one of the center core and the oversheet A medium with security magnetic data, characterized in that a random magnetic pattern made of a magnetic material is provided in between, and a concealing layer is provided on the oversheet on the side where the random magnetic pattern is provided. 【請求項４】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成の媒体を製造する方法にお
いて、 ロール状のオーバーシート上に、シート状のセンターコ
アの長さと異なるピッチで磁性材料からなるランダムな
磁気パターンを、所定の印刷法により少なくとも２回以
上印刷し、 しかる後に、前記シート状のセンターコアを一枚一枚貼
り合わせて、可能な限りランダムな磁気データを付与す
るようにしたことを特徴とするセキュリティ磁気データ
付き媒体の製造方法。4. A method for producing a medium in which both sides of a center core made of a thermoplastic resin such as hard vinyl chloride are sandwiched between oversheets made of a thermoplastic resin such as hard vinyl chloride. , Printing a random magnetic pattern made of a magnetic material at a pitch different from the length of the sheet-shaped center cores at least twice by a predetermined printing method, and then laminating the sheet-shaped center cores one by one. Then, a method for manufacturing a medium with security magnetic data, characterized in that magnetic data is provided as randomly as possible. 【請求項５】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成の媒体を製造する方法にお
いて、 シート状もしくはロール状のオーバーシート上に、所定
の方法により所定の磁性材料によって、プログラム済み
の所定のランダムな磁気パターンに印字を行ない、 しかる後に、シート状もしくはロール状のセンターコア
を貼り合わせるようにしたことを特徴とするセキュリテ
ィ磁気データ付き媒体の製造方法。5. A method for producing a medium in which both sides of a center core made of a thermoplastic resin such as hard PVC are sandwiched by oversheets made of a thermoplastic resin such as hard PVC, in the form of a sheet or a roll. A predetermined random magnetic pattern programmed by a predetermined magnetic material is printed on a sheet by a predetermined method, and then a sheet-shaped or roll-shaped center core is attached. Method for manufacturing medium with security magnetic data. 【請求項６】 硬質塩ビ等の熱可塑性樹脂からなるセン
ターコアの両側を、硬質塩ビ等の熱可塑性樹脂からなる
オーバーシートで挟んだ構成の媒体を製造する方法にお
いて、 シート状もしくはロール状のセンターコア上に、所定の
方法により所定の磁性材料によって、プログラム済みの
所定のランダムな磁気パターンに印字を行ない、 しかる後に、シート状もしくはロール状のオーバーシー
トを貼り合わせるようにしたことを特徴とするセキュリ
ティ磁気データ付き媒体の製造方法。6. A method for producing a medium in which both sides of a center core made of a thermoplastic resin such as hard vinyl chloride are sandwiched by oversheets made of a thermoplastic resin such as hard vinyl chloride in a sheet-shaped or roll-shaped center A predetermined random magnetic pattern that has been programmed is printed on the core by a predetermined magnetic material by a predetermined method, and then a sheet-shaped or roll-shaped oversheet is attached. Method for manufacturing medium with security magnetic data. 【請求項７】 前記所定の方法による所定の磁性材料と
しては、静電印刷法による磁性トナー、または熱転写法
による磁性リボン、あるいはインキジェット法による磁
性インキのいずれかによって、プログラム済みの所定の
ランダムな磁気パターンの印字を行なうようにしたこと
を特徴とする請求項５または請求項６に記載のセキュリ
ティ磁気データ付き媒体の製造方法。7. The predetermined magnetic material according to the predetermined method is a magnetic toner by an electrostatic printing method, a magnetic ribbon by a thermal transfer method, or a magnetic ink by an ink jet method. 7. A method for manufacturing a medium with security magnetic data according to claim 5, wherein the magnetic pattern is printed.