JPH07261684A - Display for magnetic display and magnetic display device - Google Patents

Abstract

PURPOSE:To provide a display for magnetic display which is distinct in bright ness and darkness varying in the parts impressed with magnetism and parts not impressed with the magnetism, has high resolution, is bright, has excellent stability of images and is capable of making reversible display, and a magnetic display device. CONSTITUTION:This display 1 for magnetic display has a magnetic display layer 12 contg. microcapsules 15 including dispersion media 24 dispersed with magnetic powder 22 and exhibiting a solid phase state at ordinary temp. This magnetic display device has the display 1 for magnetic display and a thermo- magnetic head driving section consisting of a thermo-magnetic head device for recording and erasing. The display is scanned from the front surface side at the time of recording. The entire surface is heated and the magnetism is impressed over the entire surface from the rear surface or the rear surface is partially scanned at the time of erasing.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、加熱とともに磁気によ
って画像を表示する磁気表示用ディスプレー及びこれを
利用した磁気表示装置に係り、とくに解像度及び画像の
安定性に優れた可逆表示可能な磁気表示用ディスプレー
及びこれを利用した磁気表示装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic display for displaying an image by magnetism upon heating and a magnetic display device using the same, and particularly to a magnetic display capable of reversible display excellent in resolution and image stability. The present invention relates to a display and a magnetic display device using the same.

【０００２】[0002]

【従来の技術】従来、磁気を利用したディスプレーとし
て、例えば、特開昭４８−５６３９３号公報に記載され
ているように、着色分散媒中に磁性粒子が分散されたサ
スペンジョンに磁界を作用させることにより、磁性粒子
を移動させ、着色分散媒の色を変化させて表示を行う方
法が知られている。2. Description of the Related Art Conventionally, as a display utilizing magnetism, a magnetic field is applied to a suspension in which magnetic particles are dispersed in a coloring dispersion medium, as described in, for example, JP-A-48-56393. A method is known in which the magnetic particles are moved to change the color of the colored dispersion medium and display is performed.

【０００３】しかし、このようなディスプレーは、サス
ペンジョンを２枚の基板間に封じこんで一方の基板から
磁気ペンで文字、模様を描いて磁気を作用させると、サ
スペンジョンの磁性粒子が吸引されて、その通りの文字
や模様が得られるが、磁性粒子の比重は分散媒のそれよ
りも極めて大きいので吸引された磁性粒子は、時間とと
もに沈降するため文字や模様を長時間保持できない欠点
を有する。However, in such a display, when a suspension is sealed between two substrates and a magnetic pen is used to draw characters and a pattern from one substrate to apply magnetism, magnetic particles of the suspension are attracted, Although the characters and patterns can be obtained as they are, since the specific gravity of the magnetic particles is much larger than that of the dispersion medium, the attracted magnetic particles have a drawback that the characters and patterns cannot be retained for a long time because they settle out with time.

【０００４】また、磁気ペンにより磁気を受けた磁性粒
子はすべて磁気ペンに吸引されるので、磁気ペンから離
れて存在していた磁性粒子まで吸引されるため、不鮮明
な文字や模様しか得られない欠点も有していた。磁性粒
子の沈降を防止するため、例えば磁性粒子を細かくする
か、磁性粒子に低比重のポリマー等を被覆して、磁性粒
子の見かけの比重を分散媒のそれと近似させると、磁性
粒子に働く磁気力が極端に小さくなるため、磁気ペンに
よって吸引されにくくなり、濃度の濃い、鮮明な文字や
模様が得られなくなるという欠陥を生じる。Further, since all the magnetic particles magnetized by the magnetic pen are attracted to the magnetic pen, the magnetic particles existing apart from the magnetic pen are also attracted, so that only unclear characters and patterns are obtained. It also had drawbacks. In order to prevent sedimentation of magnetic particles, for example, if the magnetic particles are made finer or the magnetic particles are coated with a polymer having a low specific gravity, and the apparent specific gravity of the magnetic particles approximates that of the dispersion medium, the magnetic particles Since the force becomes extremely small, it becomes difficult to be sucked by the magnetic pen, which causes a defect that it is not possible to obtain a clear character or pattern with high density.

【０００５】さらに、磁性粒子の見かけの比重を分散媒
のそれと近似させると、文字や模様を消去する際も、磁
性粒子が基板の反対側に吸引されにくくなり、完全に消
去できず、これを繰り返していると全体的に黒ずんでし
まい、実用的ではなかった。Further, if the apparent specific gravity of the magnetic particles is approximated to that of the dispersion medium, the magnetic particles are difficult to be attracted to the opposite side of the substrate even when characters and patterns are erased, and the particles cannot be completely erased. Repeatedly, it turned black overall, which was not practical.

【０００６】これらの欠点を解決する形態として、例え
ば、特公昭５７−２７４６３号公報、特開昭６２−５３
３５９号公報に記載されているように、分散媒として、
一定値以上の降伏値を有する液体、あるいは、増稠剤を
用いることによって、ぼけのない鮮明でコントラストの
高い文字、画像が表示でき、その表示は長時間安定に保
持でき、かつ、消去を完全にきれいに行えるディスプレ
ーが知られている。As a mode for solving these drawbacks, for example, Japanese Patent Publication No. 57-27463 and Japanese Patent Laid-Open No. 62-53.
As described in Japanese Patent No. 359, as a dispersion medium,
By using a liquid that has a yield value of a certain value or more, or by using a thickener, clear and high-contrast characters and images without blur can be displayed, and the display can be kept stable for a long time, and erasure can be completed completely. There are known displays that can be used beautifully.

【０００７】しかし、このディスプレーは、透明プラス
チックシートの全面に、一辺および深さが各２ｍｍ程度
のハニカム状のセルを設けるように成形して、そのセル
の中に、磁性粒子と白色顔料を分散媒に分散したサスペ
ンジョンを注入し、これを透明シートで密封した形態で
あり、以下の欠点を有していた。即ち、ハニカム状のセ
ルの中で磁性粒子を裏面より表面に移動させて像を形成
するため、像の解像度をハニカム状のセルより小さくす
ることは不可能である。また、ハニカム状のセルを成形
すること、ハニカム状のセルを大型化、あるいは非常に
小型化すること、ハニカム状のセルにサスペンジョンを
注入する工程等が困難である。However, this display is formed by forming a honeycomb-shaped cell having a side and a depth of about 2 mm on the entire surface of a transparent plastic sheet, and magnetic particles and a white pigment are dispersed in the cell. The suspension dispersed in a medium was injected, and the suspension was sealed with a transparent sheet, which had the following drawbacks. That is, since the image is formed by moving the magnetic particles from the back surface to the front surface in the honeycomb-shaped cell, it is impossible to make the resolution of the image smaller than that of the honeycomb-shaped cell. Further, it is difficult to form the honeycomb-shaped cells, increase the size of the honeycomb-shaped cells, or make the honeycomb-shaped cells very small, and the process of injecting the suspension into the honeycomb-shaped cells.

【０００８】別の形態として、例えば、特開平１−１４
５６３７号公報、あるいは、Ｅｙｎｅ Ｓ．Ｔｒｕｍｂ
ｌｅ Ｐ．Ｓ．＆Ｅ．７ ２１３（１９６３）に記載さ
れているように、前記のようなハニカム状のセルに磁性
粒子と顔料を密封したディスプレーとは異なり、磁性粒
子をマイクロカプセルに封入し、これを支持体上に塗布
したディスプレーが知られている。この方法によれば、
マイクロカプセルの粒径を制御することにより、解像度
を高くすることができ、製造工程も容易である。また、
マイクロカプセルを塗布する基板に種々のフィルム等の
選択が可能となり、形状、大きさも自由に選択が可能と
なる。As another mode, for example, Japanese Patent Laid-Open No. 1-14
5637 or Eyne S. et al. Trumb
le P.L. S. & E. No. 7 213 (1963), unlike a display in which magnetic particles and a pigment are sealed in a honeycomb-shaped cell as described above, the magnetic particles are encapsulated in microcapsules and coated on a support. Display is known. According to this method
By controlling the particle size of the microcapsules, the resolution can be increased and the manufacturing process is easy. Also,
Various films and the like can be selected as the substrate on which the microcapsules are applied, and the shape and size can be freely selected.

【０００９】しかし、ここで示される画像形成の方法
は、まずディスプレー作製時に、塗布したカプセル中の
磁性粒子をあらかじめディスプレー平面に平行に配向さ
せることにより入射光を全部反射させ明るく見せてお
く。次に、磁気的な記録をすることにより、磁性粒子が
回転し入射光を散乱、吸収するようになり、コントラス
トが生じ黒色の像が形成される。即ち、ここで用いられ
る磁性粒子は、一般にニッケル、鉄、バリウム−フェラ
イト等の偏平な粒子に限られ、また像形成の原理が、磁
性粒子の配向に基づいているため、ディスプレー作製時
に磁性粒子の偏平な面を磁気記録体の平面に対し、常に
平行に配向させておく必要があるが、このように一定方
向に均一に、完全に配向させるのは困難であり、完全に
は配向されない磁性粒子によって、明暗のはっきりしな
い像となる。However, in the image forming method shown here, first, at the time of manufacturing a display, the magnetic particles in the coated capsules are orientated in advance in parallel with the plane of the display so that all the incident light is reflected to make it appear bright. Next, by magnetically recording, the magnetic particles rotate to scatter and absorb the incident light, and a contrast is produced, so that a black image is formed. That is, the magnetic particles used here are generally limited to flat particles such as nickel, iron and barium-ferrite, and since the principle of image formation is based on the orientation of the magnetic particles, it is It is necessary to always orient the flat surface in parallel with the plane of the magnetic recording medium, but it is difficult to orient it uniformly and in a certain direction in this way. The result is an unclear image of light and dark.

【００１０】さらに、マイクロカプセルを利用した別の
形態として、例えば、特開平２−１４６０８２号公報、
特開平４−２３３５８１号公報に記載されているよう
に、光吸収性の磁性粒子と、光反射性の非磁性粒子をマ
イクロカプセルに封入したディスプレーが知られてい
る。Further, as another mode using the microcapsules, for example, Japanese Patent Laid-Open No. 2-146082,
As described in JP-A-4-233581, a display in which light-absorbing magnetic particles and light-reflecting non-magnetic particles are enclosed in microcapsules is known.

【００１１】この形態の画像形成は、まず永久磁石によ
って、マイクロカプセル内の光吸収性の磁性粒子をディ
スプレーの裏面側に吸引し、それに伴い、光反射性の非
磁性粒子がディスプレーの表面に残留することによっ
て、表面が非磁性粒子の色となり、消去状態となる。次
にディスプレー表面から永久磁石によって磁気を印加・
記録することにより、表面に光吸収性の磁性粒子が磁気
によって吸引され、所望の文字、画像が形成される。In the image formation of this form, first, the permanent magnet attracts the light-absorbing magnetic particles in the microcapsules to the back surface side of the display, and accordingly, the light-reflecting non-magnetic particles remain on the surface of the display. By doing so, the surface becomes the color of the non-magnetic particles and the erased state is achieved. Next, apply magnetism from the display surface with a permanent magnet.
By recording, the light absorbing magnetic particles are attracted to the surface by magnetism, and desired characters and images are formed.

【００１２】しかし、このようにして得たディスプレー
は、磁気の力が広範囲に及ぶため、解像度が他の熱や光
による記録と比べ、非常に劣るものである。さらに、上
記ディスプレーは、磁気の力で容易に印字、消去が行え
るため、磁石に触れただけで、未印字部にかぶりを生じ
たり、画像が消去されてしまったりとするように画像の
安定性が悪いという欠点を有する。However, since the display thus obtained has a wide range of magnetic force, its resolution is very inferior to that of recording by other heat or light. Furthermore, since the above-mentioned display can be easily printed and erased by magnetic force, the stability of the image may be caused by fogging the unprinted part or erasing the image just by touching the magnet. Has the disadvantage of being bad.

【００１３】[0013]

【発明が解決しようとする課題】以上から従来の磁性体
を表示手段として利用したディスプレーは、高い解像度
の画像を表示することができず、また外部からの磁気の
影響により表示した画像の部分的又は判読が不可能な状
態に画像が消去或いは未印字部にかぶりを生じるため、
安定した記録を行うことができなった。また内包される
磁性粒子の移動性、すなわち記録の反応性の良さと記録
画像の安定性の両方を備えるディスプレーは存在してい
なかった。そこで本発明は、磁気を印加した部分が、無
印加の部分とは異なる明暗がはっきりし、かつ解像度の
高く、鮮明で、さらに画像の安定性に優れた、可逆表示
可能な磁気表示用ディスプレー及び磁気表示装置を提供
することを目的とする。From the above, the conventional display using a magnetic material as a display means cannot display a high resolution image, and a partial display of an image displayed due to the influence of external magnetism. Or because the image is erased or fog occurs in the unprinted part in an unreadable state,
Stable recording could not be performed. Further, there has not been a display having the mobility of the magnetic particles contained therein, that is, both the good recording reactivity and the recorded image stability. In view of the above, the present invention provides a reversible display capable of reversible display, in which a portion to which magnetism is applied has a bright and dark distinction from a portion to which no magnetism is applied, has high resolution, is clear, and has excellent image stability. An object is to provide a magnetic display device.

【００１４】[0014]

【課題を解決するための手段】本発明は、上記目的を達
成するためになされたものであり、請求項１に記載の発
明は、少なくとも一方が透明性を有する非磁性材料から
なる支持体間に、少なくとも磁性粒子と、これを分散し
てなる常温において固相状態を示す分散媒とを内包する
マイクロカプセルをバインダー中に分散配置してなる磁
気表示層を形成したことを特徴とする磁気表示用ディス
プレーである。The present invention has been made to achieve the above object, and the invention according to claim 1 is one in which at least one is made of a nonmagnetic material having transparency. In addition, a magnetic display layer is formed in which a microcapsule containing at least magnetic particles and a dispersion medium which is dispersed and shows a solid state at room temperature is dispersedly arranged in a binder. Display.

【００１５】請求項２の発明は、請求項１に記載の磁気
表示用ディスプレーにおいて、磁気表示層上に透明性を
有する着色層を積層してなることを特徴とするものであ
る。The invention of claim 2 is the display for magnetic display according to claim 1, characterized in that a colored layer having transparency is laminated on the magnetic display layer.

【００１６】請求項３の発明は、請求項１に記載の磁気
表示用ディスプレーにおいて、磁性粒子の平均粒径が
０．１μｍから１０μｍの間にあることを特徴とするも
のである。According to a third aspect of the present invention, in the magnetic display according to the first aspect, the average particle size of the magnetic particles is between 0.1 μm and 10 μm.

【００１７】請求項４の発明は、請求項１に記載の磁気
表示用ディスプレーにおいて、磁性粒子が着色磁性粒子
であることを特徴とするものである。According to a fourth aspect of the present invention, in the magnetic display according to the first aspect, the magnetic particles are colored magnetic particles.

【００１８】請求項５の発明は、請求項１に記載の磁気
表示用ディスプレーにおいて、分散媒が融点３５℃以上
８０℃以下の有機化合物であることを特徴とするもので
ある。According to a fifth aspect of the invention, in the magnetic display according to the first aspect, the dispersion medium is an organic compound having a melting point of 35 ° C. or higher and 80 ° C. or lower.

【００１９】請求項６の発明は、請求項１に記載の磁気
表示用ディスプレーにおいて、マイクロカプセルの平均
粒径が１０μｍから１０００μｍの間にあることを特徴
とするものである。According to a sixth aspect of the present invention, in the magnetic display according to the first aspect, the average particle size of the microcapsules is between 10 μm and 1000 μm.

【００２０】請求項７の発明は、少なくとも一方が透明
性を有する非磁性材料からなる支持体間に、少なくとも
磁性粒子と、これらを分散してなる常温において固相状
態を示す分散媒とを内包するマイクロカプセルをバイン
ダー中に分散配置してなる磁気表示層を形成してなる磁
気表示用ディスプレーと、磁気表示用ディスプレーの表
示面側に配置され、加熱及び磁気印加により前記マイク
ロカプセル中の磁性粒子を部分的に吸引移動せしめる加
熱磁気発生手段と、磁気表示用ディスプレーの裏面側に
配置され、加熱及び磁気印加により前記マイクロカプセ
ル中の磁性粒子を吸引移動せしめる加熱磁気発生手段と
を備えてなり、マイクロカプセル中の磁性粒子を一方の
面に偏在せしめることを特徴とする磁気表示装置であ
る。According to a seventh aspect of the present invention, at least one magnetic particle and a dispersion medium having a solid state at room temperature, which is formed by dispersing these particles, are included between the supports, at least one of which is a transparent non-magnetic material. Magnetic display in which a magnetic display layer is formed by dispersing microcapsules in a binder, and magnetic particles in the microcapsules disposed on the display surface side of the magnetic display by heating and magnetic application. A heating magnetism generating means for partially attracting and moving the magnetism, and a heating magnetism generating means disposed on the back surface side of the magnetic display for attracting and moving the magnetic particles in the microcapsules by heating and magnetic application, A magnetic display device characterized in that magnetic particles in microcapsules are unevenly distributed on one surface.

【００２１】[0021]

【作用】本発明の磁気表示用ディスプレー及び磁気表示
装置は、磁性粒子を分散した、常温において固相状態を
示す分散媒を内包するマイクロカプセルを含む磁気表示
層を有しており、通常は、磁気表示用ディスプレーの一
方の面である裏面側に、即ちマイクロカプセルの下方に
磁性粒子が引き寄せられており、他方の面である磁気表
示用ディスプレーの表面は分散媒の色、或いはその屈折
率差による光散乱により磁性粒子の色が隠蔽されるた
め、均一な色調となる。The magnetic display and the magnetic display device of the present invention have a magnetic display layer containing microcapsules in which magnetic particles are dispersed and which contain a dispersion medium exhibiting a solid state at room temperature. The magnetic particles are attracted to the back side, which is one side of the magnetic display, that is, below the microcapsules, and the surface of the magnetic display that is the other side is the color of the dispersion medium or the difference in the refractive index thereof. Since the color of the magnetic particles is hidden by the light scattering due to, the color tone becomes uniform.

【００２２】また本発明の磁気表示用ディスプレー及び
磁気表示装置への記録は、磁気表示用ディスプレーの表
面側から、加熱手段を有する磁気発生手段で走査し、熱
によって粘度が低下し流動状態となった分散媒の部分の
磁性粒子が、磁気によりマイクロカプセルの上方、即
ち、磁気発生手段側の表面に移動し、磁性粒子による像
が形成され、さらに消去は全面を加熱し、磁気表示用デ
ィスプレーの裏面から全面に磁気をかけるか、あるいは
加熱手段を有する磁気発生手段等で裏面を走査すること
により、磁性粒子はマイクロカプセルの下方である磁気
発生手段側に引き寄せられ、磁気表示用ディスプレーの
表面は再び均一な色調となり、像は消去される。Further, in recording on the magnetic display and the magnetic display device of the present invention, scanning is performed from the surface side of the magnetic display by magnetic generation means having a heating means, and the viscosity is lowered by heat to be in a fluidized state. The magnetic particles in the dispersion medium portion are magnetically moved to the upper side of the microcapsule, that is, to the surface on the side of the magnetic generation means, and an image is formed by the magnetic particles. By applying magnetism to the entire surface from the back surface or scanning the back surface with a magnetism generating means having a heating means, the magnetic particles are attracted to the magnetism generating means side below the microcapsules, and the surface of the magnetic display is A uniform tone is obtained again and the image is erased.

【００２３】[0023]

【実施例】以下、本発明を図面を用いて詳細に説明す
る。図１は、本発明の一実施例を示す断面図であり、図
２は、本発明の他の実施例を示す断面図であり、図３
は、本発明で磁気表示層に用いられるマイクロカプセル
の一実施例を示す断面図であり、図４は、本発明の着色
被覆層で被覆された着色磁性粒子の一実施例を示す断面
図であり、図５は、本発明の着色被覆層及び隠蔽層で被
覆された着色磁性粒子の一実施例を示す断面図であり、
図６は、本発明の磁気表示用ディスプレーの製造時の状
態を示す説明図であり、図７は、本発明の磁気表示用デ
ィスプレーの消去動作により未記録の状態を示す説明図
であり、図８は、本発明の磁気表示用ディスプレーの記
録時の状態を示す説明図であり、図９は、本発明の磁気
表示装置を説明する概念図であり、図１０は、本発明の
磁気表示装置の記録用熱・磁気ヘッド駆動部の構成を説
明する説明図であり、図１１は、本発明の磁気表示装置
の消去用熱・磁気ヘッド駆動部の構成を説明する説明図
である。The present invention will be described in detail below with reference to the drawings. 1 is a sectional view showing an embodiment of the present invention, FIG. 2 is a sectional view showing another embodiment of the present invention, and FIG.
FIG. 4 is a sectional view showing an example of microcapsules used in the magnetic display layer of the present invention, and FIG. 4 is a sectional view showing an example of colored magnetic particles coated with the colored coating layer of the present invention. FIG. 5 is a sectional view showing an example of the colored magnetic particles coated with the colored coating layer and the hiding layer of the present invention,
FIG. 6 is an explanatory diagram showing a state of the magnetic display according to the present invention during manufacturing, and FIG. 7 is an explanatory diagram showing an unrecorded state due to an erasing operation of the magnetic display according to the present invention. 8 is an explanatory diagram showing a state of the magnetic display of the present invention during recording, FIG. 9 is a conceptual diagram illustrating the magnetic display device of the present invention, and FIG. 10 is a magnetic display device of the present invention. FIG. 12 is an explanatory diagram for explaining the configuration of the recording thermal / magnetic head drive unit, and FIG. 11 is an explanatory diagram for explaining the configuration of the erasing thermal / magnetic head drive unit of the magnetic display device of the present invention.

【００２４】図１は、本発明の磁気表示用ディスプレー
１の構成を示し、支持体１１、磁性粒子等を含んだマイ
クロカプセル１５をバインダー１６に分散した塗布材が
塗布される磁気表示層１２、保護支持体１４が順次積層
されている。FIG. 1 shows the structure of the magnetic display 1 of the present invention, in which a support 11 and a magnetic display layer 12 coated with a coating material in which microcapsules 15 containing magnetic particles are dispersed in a binder 16, The protective support 14 is sequentially laminated.

【００２５】また、図２は本発明の他の実施例における
磁気表示用ディスプレー１０の構成を示し、支持体１
１、磁性粒子等を含んだマイクロカプセル１４をバイン
ダー１５に分散した塗布材が塗布される磁気表示層１
２、透明性を有する着色層１３、保護支持体１４が順次
積層されている。FIG. 2 shows the structure of a magnetic display 10 according to another embodiment of the present invention, which is a support 1
1. A magnetic display layer 1 coated with a coating material in which microcapsules 14 containing magnetic particles are dispersed in a binder 15.
2. A transparent colored layer 13 and a protective support 14 are sequentially laminated.

【００２６】さらに図３は本発明で磁気表示層１２に用
いられるマイクロカプセル１５の一実施例を示す断面図
である。マイクロカプセル１５は、磁性粒子２２が常温
において固相状態を示す分散媒（例えばワックスなど）
２４中に分散されたサスペンジョンを主成分とする芯物
質２１を、ポリマーよりなる殻物質２７でカプセル化し
た構成である。Further, FIG. 3 is a sectional view showing an embodiment of the microcapsules 15 used in the magnetic display layer 12 in the present invention. The microcapsules 15 are dispersion media (for example, wax) in which the magnetic particles 22 are in a solid state at room temperature.
The core material 21 mainly composed of suspensions dispersed in 24 is encapsulated by a shell material 27 made of a polymer.

【００２７】磁性粒子２２としては、磁性粒子単独、あ
るいは数種の磁性粒子の混合物、さらには、磁性粒子と
ポリマーからなる混合物が使用可能である。例えば、マ
グネタイト、フェライトをはじめとする鉄、コバルト、
ニッケル等の強磁性を示す金属、もしくはこれらの元素
を含む合金、または化合物の微粒子が用いられる。この
場合、磁性粒子はワックス等との親和性を高めるため
に、シランカップリング処理等の表面疎水化処理を施す
とよい。また、磁性粒子とポリマーからなる混合物を用
いる場合には、上述の磁性粒子とポリマーを混練後、粉
砕する、あるいは磁性粒子を分散したモノマーを、乳化
重合、懸濁重合、分散重合等の方法を用いて、重合等の
方法が用いられる。この場合、ポリマーは架橋性のもの
とすることが好ましい。磁性粒子の大きさは、磁気によ
る移動のしやすさ、画像濃度等を考えると、０．１μｍ
から１０μｍの間が好ましい。As the magnetic particles 22, it is possible to use magnetic particles alone, a mixture of several kinds of magnetic particles, or a mixture of magnetic particles and a polymer. For example, magnetite, ferrite and other iron, cobalt,
A metal exhibiting ferromagnetism such as nickel, an alloy containing these elements, or fine particles of a compound is used. In this case, the magnetic particles may be subjected to surface hydrophobizing treatment such as silane coupling treatment in order to enhance affinity with wax or the like. When a mixture of magnetic particles and a polymer is used, the above-mentioned magnetic particles and a polymer are kneaded and then pulverized, or a monomer in which the magnetic particles are dispersed is subjected to a method such as emulsion polymerization, suspension polymerization, or dispersion polymerization. A method such as polymerization is used. In this case, the polymer is preferably crosslinkable. The size of the magnetic particles is 0.1 μm in consideration of the ease of movement due to magnetism and the image density.
It is preferably between 1 and 10 μm.

【００２８】磁性粒子２２の色を薄色、或いは黒褐色、
茶褐色等の磁性体固有の色以外の色とする場合は、磁性
粒子を顔料或いは染料とバインダーで混練したものや図
４に示すように磁性粒子２２の表面を顔料単独、あるい
は数種の顔料の混合物、さらには、顔料とポリマーから
なる混合物を用いて着色被覆層２５を形成した着色磁性
粒子２３を用いることができる。着色被覆層２５は、例
えば一般に知られている二酸化チタン、硫化亜鉛、チタ
ン酸鉛、酸化ジルコニウム、鉛白、カドミウム赤、カド
ミウム黄等の無機顔料、フタロシアニン系顔料等の有機
顔料の微粒子が用いられる。着色被覆層２５の調整方法
は、顔料を分散したポリマー溶液に分散してなる磁性粒
子２１の周囲に、顔料を分散したポリマーの濃厚相を分
離させる相分離法、顔料を分散したポリマー溶液中に分
散させた磁性粒子２１の周囲にポリマー硬化試験薬等の
硬化剤によりポリマーを硬化させる液中硬化被覆法、磁
性粒子２１を分散させたサスペンジョンに顔料を分散し
たモノマーや重合触媒を供給し磁性粒子２２の表面を顔
料を分散したポリマーで覆う分散重合法、磁性粒子の表
面を顔料を直接混合摩砕する気流中衝撃法、或いは顔料
を分散したポリマー溶液に磁性粒子を分散させたサスペ
ンジョンを噴霧して乾燥させるスプレードライング法な
どのマイクロカプセル化技法が好適である。他の方法に
は、磁性粒子を有機金属化合物溶液に浸漬し引き上げて
乾燥し、その後焼成して有機金属化合物を分解すること
により金属酸化物よりなる顔料層を形成する方法、また
金属塩の希薄酸性溶液中に磁性粒子を懸濁させ金属塩を
加水分解してその表面に水和金属酸化物を析出させ、焼
成することにより金属化合物よりなる顔料層を形成する
方法などが挙げられる。なお、着色層２５の調整方法
は、これらの方法に限定されるものではない。The color of the magnetic particles 22 is light or dark brown,
When the color other than the color unique to the magnetic material such as dark brown is used, the magnetic particles are kneaded with a pigment or a dye and a binder, or as shown in FIG. It is possible to use the colored magnetic particles 23 in which the colored coating layer 25 is formed by using a mixture, or a mixture of a pigment and a polymer. As the coloring coating layer 25, for example, fine particles of commonly known inorganic pigments such as titanium dioxide, zinc sulfide, lead titanate, zirconium oxide, lead white, cadmium red, and cadmium yellow, and organic pigments such as phthalocyanine pigments are used. . The coloring coating layer 25 is prepared by a phase separation method in which a concentrated phase of the polymer in which the pigment is dispersed is separated around the magnetic particles 21 dispersed in the polymer solution in which the pigment is dispersed, and in a polymer solution in which the pigment is dispersed. A liquid curing coating method in which a polymer is cured around a dispersed magnetic particle 21 with a curing agent such as a polymer curing test agent, and a suspension of magnetic particles 21 is supplied with a monomer or a polymerization catalyst in which a pigment is dispersed to supply magnetic particles. 22 is a dispersion polymerization method in which the surface of the magnetic particles is covered with a polymer in which a pigment is dispersed, an air current impact method in which the surface of magnetic particles is directly mixed and ground with a pigment, or a suspension in which magnetic particles are dispersed in a polymer solution in which a pigment is dispersed is sprayed. A microencapsulation technique such as a spray drying method of drying by drying is preferable. Another method is to form a pigment layer composed of a metal oxide by immersing magnetic particles in an organometallic compound solution, pulling it up and drying it, and then firing it to decompose the organometallic compound, or diluting a metal salt. Examples include a method in which magnetic particles are suspended in an acidic solution, a metal salt is hydrolyzed to precipitate a hydrated metal oxide on the surface thereof, and the pigment is baked to form a pigment layer made of a metal compound. The method of adjusting the colored layer 25 is not limited to these methods.

【００２９】また図５に示すように着色磁性粒子２３’
は着色被覆層２５の下層にさらに隠蔽層２６を設けても
よい。これによれば、磁性粒子の色が隠蔽されるため、
外郭に形成される着色被覆層２５を単独で形成するとき
と比べ、磁性粒子の色が透けて見えるなどの影響を受け
ることなく着色層２５を薄くすることが可能となる。な
お、隠蔽層２６は有機ポリマーに分散させた無機粉末又
は金属薄膜により形成される。Further, as shown in FIG. 5, colored magnetic particles 23 '
A concealing layer 26 may be further provided below the colored coating layer 25. According to this, since the color of the magnetic particles is hidden,
As compared with the case where the colored coating layer 25 formed on the outer shell is formed alone, the colored layer 25 can be made thinner without being affected by the color of the magnetic particles being seen through. The hiding layer 26 is formed of an inorganic powder or a metal thin film dispersed in an organic polymer.

【００３０】隠蔽層２６は、上記したように着色層２５
を通して磁性粒子の色が透けて見えるなどの影響を少な
くすることができ、とくに着色層を黄色等の薄色とする
場合に有効である。具体的には無機粉末を有機ポリマー
に分散させたもの、或いは金属薄膜からなる。調整方法
は無機粉末を分散したポリマー溶液に分散してなる磁性
粒子の周囲に、無機粉末を分散したポリマー溶液の濃厚
相を分離させる相分離法、顔料を分散したポリマー溶液
中に分散させた磁性粒子２１の周囲にポリマー硬化試験
薬等の硬化剤によりポリマーを硬化させる液中硬化被覆
法、磁性粒子２１を分散させたサスペンジョンに顔料を
分散したモノマーや重合触媒を供給し磁性粒子２１の表
面を顔料を分散したポリマーで覆う分散重合法、磁性粒
子の表面を顔料を直接混合摩砕する気流中衝撃法、或い
は顔料を分散したポリマー溶液に磁性粒子を分散させた
サスペンジョンを噴霧して乾燥させるスプレードライン
グ法などのマイクロカプセル化技法が好適である。な
お、調整方法は、これらの方法に限定されるものではな
い。上記した無機粉末は、屈折率が高く、隠蔽力の大き
いことが望ましく、例えば二酸化チタン、硫化亜鉛、チ
タン酸鉛、酸化ジルコニウム等が好ましいが、とくにこ
れらに限定されるものではない。また金属薄膜による隠
蔽層２６の調整方法は、主に無電解メッキによる方法、
磁性粒子表面に有機金属化合物を化学吸着或いは物理吸
着させた後、有機金属化合物を分解する方法等がある。
用いられる金属は磁気的特性はほとんどなく、着色層の
色調に影響を及ぼさない、例えばアルミニウム、銀、亜
鉛、錫などが好ましい。The concealing layer 26 is the colored layer 25 as described above.
It is possible to reduce the effect that the color of the magnetic particles can be seen through, and it is particularly effective when the colored layer is a light color such as yellow. Specifically, it is composed of an inorganic polymer dispersed in an organic polymer or a metal thin film. The adjustment method is a phase separation method in which the concentrated phase of the polymer solution in which the inorganic powder is dispersed is separated around the magnetic particles formed by dispersing the inorganic powder in the polymer solution, and the magnetic property in which the pigment is dispersed in the polymer solution is separated. A liquid curing coating method in which a polymer is cured around a particle 21 with a curing agent such as a polymer curing test agent, a suspension of the magnetic particles 21 in which a monomer in which a pigment is dispersed and a polymerization catalyst are supplied to clean the surface of the magnetic particles 21. Dispersion polymerization method in which the pigment is dispersed in a polymer, magnetic particle surface is directly mixed and milled with the pigment in an air stream, or a suspension in which magnetic particles are dispersed in a polymer solution in which a pigment is dispersed is sprayed and dried. Microencapsulation techniques such as the drying method are preferred. The adjustment method is not limited to these methods. The above-mentioned inorganic powder preferably has a high refractive index and a large hiding power, and for example, titanium dioxide, zinc sulfide, lead titanate, zirconium oxide and the like are preferable, but the inorganic powder is not particularly limited thereto. The method for adjusting the concealing layer 26 using a metal thin film is mainly a method using electroless plating,
There is a method of decomposing the organometallic compound after chemically or physically adsorbing the organometallic compound on the surface of the magnetic particles.
It is preferable that the metal used has almost no magnetic properties and does not affect the color tone of the colored layer, such as aluminum, silver, zinc or tin.

【００３１】分散媒２４としては、常温（約１０〜３５
℃の範囲）で固体のもの（固相状態を示す）で、かつ常
温以上の温度（約４０〜８０℃の範囲）に加熱されると
流動状態になるものであればよく、例えば有機化合物
で、パラフィンワックス、カルナバワックスなどの合成
或いは天然ワックス、天然或いは合成樹脂、またはカル
ボン酸エステルなど上記条件を満たす一般に公知である
ものを適宜使用することができる。The dispersion medium 24 is at room temperature (about 10-35).
It should be solid (in the range of ° C) (in a solid state) and be in a fluid state when heated to a temperature higher than room temperature (in the range of about 40 to 80 ° C), such as an organic compound. Commonly known substances such as synthetic or natural waxes such as paraffin wax and carnauba wax, natural or synthetic resins, or carboxylic acid esters which satisfy the above conditions can be appropriately used.

【００３２】上記した磁性粒子２２、着色磁性粒子２
３、２３’、分散媒２４などを主成分とする芯物質２１
をポリマー等の殻物質２７で覆い、マイクロカプセル化
する。この殻物質２７として用いられる樹脂には、一般
に用いられている樹脂、例えばアクリル系樹脂、メタク
リル系樹脂、ポリスチレン、ポリエステル樹脂、ポリウ
レタン樹脂、ポリウレア樹脂、ポリアミド樹脂、エポキ
シ樹脂、天然樹脂等が挙げられ、これらを単独、あるい
は２種以上混合して使用することも可能である。The above-mentioned magnetic particles 22 and colored magnetic particles 2
Core material 21 containing 3, 23 ', dispersion medium 24, etc. as main components
Is covered with a shell material 27 such as a polymer to be microencapsulated. Examples of the resin used as the shell substance 27 include commonly used resins such as acrylic resin, methacrylic resin, polystyrene, polyester resin, polyurethane resin, polyurea resin, polyamide resin, epoxy resin and natural resin. It is also possible to use these alone or in combination of two or more.

【００３３】上述の殻物質を有するマイクロカプセル１
５の製造法としては、ポリマー溶液に分散させた芯物質
のまわりにポリマーの濃厚相を分離させる相分離法、ポ
リマー溶液中の芯物質のまわりにポリマーの硬化試験薬
等によりポリマーを硬化させる液中硬化被覆法、芯物質
を分散させたエマルジョンの内、あるいは外相のいずれ
か一方からモノマーや重合触媒を供給し芯物質の表面を
ポリマーで覆うインシチュー重合法、芯物質を分散させ
たエマルジョンの内相と外相の両方からモノマーを供給
する界面重合法等のマイクロカプセル化技法が好適であ
るが、これらの方法に限定されるものではない。Microcapsules 1 having the above shell material
The method for producing 5 includes a phase separation method in which a concentrated phase of the polymer is separated around the core substance dispersed in the polymer solution, and a liquid for curing the polymer around the core substance in the polymer solution with a curing test agent for the polymer or the like. Medium-cure coating method, in-situ polymerization method in which the surface of the core material is covered with a polymer by supplying a monomer or a polymerization catalyst from either one of the emulsion in which the core material is dispersed, or the external phase, and the emulsion in which the core material is dispersed. A microencapsulation technique such as an interfacial polymerization method in which a monomer is supplied from both the internal phase and the external phase is suitable, but the method is not limited to these methods.

【００３４】とくに芯物質２１である磁性粒子２２、或
いは着色磁性粒子２３、２３’を分散媒２４に均一に分
散させたサスペンジョンの外相からモノマーを供給する
インシチュー重合法、あるいは相分離法を用いて製造す
ることにより、粒径の揃った、かつ磁性粒子２２、着色
磁性粒子２３、２３’の移動が容易なマイクロカプセル
１５を製造することができる。ここで用いる重合性モノ
マーは、アクリル酸エステル、メタクリル酸エステル、
スチレンおよびその誘導体、イソシアネート、各種アミ
ン、エポキシ基を有する化合物等が好適である。In particular, the in-situ polymerization method or the phase separation method in which the magnetic particles 22 as the core substance 21 or the colored magnetic particles 23 and 23 'are uniformly dispersed in the dispersion medium 24 to supply the monomer from the outer phase of the suspension is used. The microcapsules 15 having a uniform particle size and in which the magnetic particles 22 and the colored magnetic particles 23 and 23 ′ can be easily moved can be manufactured by manufacturing the microcapsules 15. The polymerizable monomer used here is acrylic acid ester, methacrylic acid ester,
Styrene and its derivatives, isocyanate, various amines, compounds having an epoxy group and the like are preferable.

【００３５】本発明の磁気表示用ディスプレー１、１０
は、支持体１１上に上述の構成を有するマイクロカプセ
ル１５をバインダー１６とともに塗布し磁気表示層１２
を形成、さらに保護支持体１４を積層することにより作
製される。また磁気表示層１２上に透明性を有する着色
層１３を設けることもできる。Magnetic display devices 1 and 10 of the present invention
Is coated on the support 11 with the microcapsules 15 having the above-described structure together with the binder 16 to form the magnetic display layer 12.
Is formed, and further, the protective support 14 is laminated thereon. Further, a colored layer 13 having transparency can be provided on the magnetic display layer 12.

【００３６】支持体１１はポリ塩化ビニル、ポリエステ
ル、ポリカーボネート、ポリメタクリル酸メチル、ポリ
スチレン，ポリエチレンテレフタレート等の合成樹脂
類、天然樹脂、紙、合成紙、金属、セラッミクスなどを
単独または組み合わせた複合体として用いることができ
る。またその形状もカード状あるいはシート状、フィル
ム状など用途に応じて選択でき、さらに用途に応じて要
求される物性、例えば強度、剛性、隠蔽性、光不透過性
等を考慮し、上記材料から適宜選択することができる。The support 11 is a synthetic resin such as polyvinyl chloride, polyester, polycarbonate, polymethylmethacrylate, polystyrene, polyethylene terephthalate, natural resin, paper, synthetic paper, metal, ceramics, etc., alone or in combination. Can be used. In addition, its shape can be selected according to the application such as a card shape or a sheet shape, a film shape, and further considering the physical properties required according to the application, for example, strength, rigidity, hiding power, light opacity, etc. It can be appropriately selected.

【００３７】また、マイクロカプセル１５を分散するバ
インダー１６としては、水系バインダー、溶剤系バイン
ダー、エマルション系バインダー等が適宜用いられる。
さらに、保護支持体１４としては、エポキシ樹脂、テト
ラフルオロエチレン等、またはポリ塩化ビニル、ポリエ
ステル、ポリカーボネート、ポリメタクリル酸メチル、
ポリスチレン，ポリエチレンテレフタレート等の合成樹
脂、天然樹脂等が使用可能である。この保護支持体１３
は、支持体１１上に形成されたマイクロカプセル１４を
保持するとともに、外部からマイクロカプセル１４が見
えるような透明性を有している必要があり、強度など必
要な条件を満たすものであれば用いることができる。As the binder 16 in which the microcapsules 15 are dispersed, a water-based binder, a solvent-based binder, an emulsion-based binder or the like is appropriately used.
Further, as the protective support 14, epoxy resin, tetrafluoroethylene or the like, or polyvinyl chloride, polyester, polycarbonate, polymethyl methacrylate,
It is possible to use synthetic resins such as polystyrene and polyethylene terephthalate, and natural resins. This protective support 13
Is required to hold the microcapsules 14 formed on the support 11 and be transparent so that the microcapsules 14 can be seen from the outside. be able to.

【００３８】なお、透明性を有する着色層１３は、顔料
又は染料をバインダー等に分散、或いは溶解させたもの
を磁気表示層１２上に塗布することにより形成する。顔
料又は染料としては、顔料単独、数種の顔料の混合物、
顔料とポリマーからなる混合物、染料単独、数種の染料
の混合物などを用いることができる。例えば、顔料は一
般に知られている二酸化チタン、硫化亜鉛、チタン酸
鉛、酸化ジルコニウム、鉛白、カドミウム赤、カドミウ
ム黄等の無機顔料、フタロシアニン系顔料等の有機顔料
の微粒子、また染料はアゾ染料、キノリン染料、フタロ
シアニン系染料など公知の各種顔料、染料が用いられ
る。また、顔料或いは顔料とポリマーからなる混合物を
用いる場合には、上述の顔料或いは顔料とポリマーを混
練後、粉砕する、または、顔料或いは顔料を分散したモ
ノマーを、乳化重合、懸濁重合、分散重合等の方法を用
い重合する等の方法が用いられる。この場合、ポリマー
は架橋性のものとすることが好ましい。これらの顔料又
は染料を分散、溶解させるバインダーは、水系バインダ
ー、溶剤系バインダー、エマルジョン系バインダーなど
が用いられる。The transparent colored layer 13 is formed by coating the magnetic display layer 12 with a pigment or dye dispersed or dissolved in a binder or the like. As the pigment or dye, a pigment alone, a mixture of several pigments,
A mixture of a pigment and a polymer, a dye alone, or a mixture of several dyes can be used. For example, pigments are generally known inorganic pigments such as titanium dioxide, zinc sulfide, lead titanate, zirconium oxide, lead white, cadmium red and cadmium yellow, fine particles of organic pigments such as phthalocyanine pigments, and dyes are azo dyes. Known pigments and dyes such as quinoline dyes and phthalocyanine dyes are used. When a pigment or a mixture of a pigment and a polymer is used, the above pigment or the pigment and the polymer are kneaded and then pulverized, or the pigment or the monomer in which the pigment is dispersed is subjected to emulsion polymerization, suspension polymerization, dispersion polymerization. A method of polymerizing using such a method is used. In this case, the polymer is preferably crosslinkable. As a binder for dispersing and dissolving these pigments or dyes, an aqueous binder, a solvent binder, an emulsion binder and the like are used.

【００３９】これらの形成方法は、例えばオフセット印
刷法、グラビア印刷法、シルクスクリーン印刷法等の周
知の印刷方式や、ロール塗布法、ナイフエッジ法などの
塗布方式、上述のマイクロカプセル１５を混入した転写
層に有する転写シートによる転写方式、また上述のマイ
クロカプセル１５を混入したインキを基材に吹き付ける
インキジェット方式、支持体１１と保護支持体１４との
間に上述のマイクロカプセル１５を混入した溶液を充填
する方式などの形成方法により作成することができ、作
成する情報記録媒体の用途、数量に応じて上述の方式か
ら適宜選択することができる。These forming methods include well-known printing methods such as offset printing method, gravure printing method and silk screen printing method, roll coating method, coating method such as knife edge method, and the above-mentioned microcapsules 15. A transfer method using a transfer sheet in the transfer layer, an ink jet method in which the ink containing the microcapsules 15 is sprayed onto a base material, and a solution containing the microcapsules 15 between the support 11 and the protective support 14. Can be prepared by a forming method such as a filling method, and can be appropriately selected from the above-mentioned methods depending on the use and quantity of the information recording medium to be prepared.

【００４０】次に、本発明の磁気表示用ディスプレーに
おける像形成方法を説明する。図６は、磁性粒子２２が
有機溶媒２４に分散されたサスペンジョンを内包したマ
イクロカプセル１５を支持体１１上に塗布した本発明の
磁気表示用ディスプレー１の一部を拡大した断面を表す
説明図である。作製された当初は、マイクロカプセル１
５内で、磁性粒子２２は均一に分散された状態で分散媒
２４中に固定化されている。Next, an image forming method in the magnetic display of the present invention will be described. FIG. 6 is an explanatory view showing an enlarged cross-section of a part of the magnetic display 1 of the present invention in which the microcapsules 15 containing the suspension in which the magnetic particles 22 are dispersed in the organic solvent 24 are applied on the support 11. is there. Originally made, microcapsule 1
In 5, the magnetic particles 22 are fixed in the dispersion medium 24 in a uniformly dispersed state.

【００４１】図７は、通常の画像の消去時、或いは未記
録時の状態を示す説明図である。磁気表示用ディスプレ
ー全面が一様に加熱され、マイクロカプセル内の分散媒
２４が溶融状態となり、磁気表示用ディスプレー裏面か
ら一様に印加された磁気により、磁気表示層１２のマイ
クロカプセル中の磁性粒子２２はマイクロカプセルの下
方に引き寄せられ、磁気表示用ディスプレー表面は、分
散媒の色、或いはその屈折差による光散乱により均一な
色調となる。また図２の磁気表示用ディスプレーのよう
に着色層１３を有する場合は、着色層１３の色の均一な
色調となる。FIG. 7 is an explanatory diagram showing a state when a normal image is erased or when no image is recorded. The entire surface of the magnetic display is uniformly heated, the dispersion medium 24 in the microcapsule is melted, and the magnetic particles uniformly applied from the back surface of the magnetic display cause magnetic particles in the microcapsules of the magnetic display layer 12. 22 is drawn below the microcapsules, and the magnetic display surface has a uniform color tone due to the color of the dispersion medium or light scattering due to the difference in refraction. When the colored layer 13 is provided as in the magnetic display shown in FIG. 2, the color of the colored layer 13 is uniform.

【００４２】図８は、磁気表示用ディスプレー１の上方
から、加熱機能付きの磁気発生手段の磁気の印加により
記録された状態を示す説明図である。加熱機能付きの磁
気発生手段である熱・磁気ヘッド装置３２により加熱さ
れた部分のマイクロカプセル内の分散媒２４、例えばワ
ックスは溶融状態となり、磁気によりマイクロカプセル
中の磁性粒子２２はマイクロカプセルの上方に引き寄せ
られる。一方、熱・磁気ヘッド装置３２により加熱され
ない部分は、マイクロカプセル内で磁性粒子２２の移動
はなく、顔料２３がマイクロカプセルの上方に存在す
る。従って、記録情報に応じて記録箇所を加熱・磁気印
加することで、記録されていない部分の顔料の色の中
に、記録された部分の磁性粒子の色の像が得られる。熱
・磁気ヘッド装置３２は、通常の磁気ヘッドにヒーター
などの加熱手段が付加されたものであり、加熱手段はワ
ックスなど上記した分散媒２４を溶融させるだけの加熱
能力を有していればよい。FIG. 8 is an explanatory view showing a state in which recording is performed by applying magnetism from the magnetic generating means having a heating function from above the magnetic display display 1. The dispersion medium 24, for example, wax in the portion of the microcapsule heated by the heat / magnetic head device 32, which is a magnetism generating means with a heating function, is melted, and the magnetic particles 22 in the microcapsule are magnetized above the microcapsule. Attracted to. On the other hand, in the portion that is not heated by the thermal / magnetic head device 32, the magnetic particles 22 do not move inside the microcapsule, and the pigment 23 exists above the microcapsule. Therefore, by heating and magnetically applying the recording portion according to the recording information, an image of the color of the magnetic particles in the recorded portion can be obtained in the color of the pigment in the unrecorded portion. The thermal / magnetic head device 32 is an ordinary magnetic head to which a heating unit such as a heater is added, and the heating unit may have a heating capacity enough to melt the dispersion medium 24 such as wax. .

【００４３】この像形成は、磁気と有機溶媒の粘度を低
下させる程度の低エネルギーの熱による単純なものであ
るため、記録が容易であり、マイクロカプセルの粒径を
制御することにより、解像度の高い像形成が可能であ
る。また常温で固相状態を示す分散媒の色、或いはその
屈折率差による光散乱により、磁性粒子がディスプレー
の裏面に引き寄せられている時、磁性粒子の色が隠蔽さ
れる。この磁性粒子を着色することにより表示を磁性粒
子固有の色から任意の色へ、すなわちカラー化すること
ができる。さらに加熱機能付きの熱・磁気ヘッド装置３
２で形成された像は、分散媒が常温に戻ると同時に固定
状態となるため、記録安定性がよく、しかも、溶融状態
以外では磁気のみでは像形成が行えないため、磁石に触
れてかぶりを生ずることがない。本発明によるディスプ
レーは内包される磁性粒子の記録時の移動性、すなわち
記録の反応性の良さと記録画像の安定性の両方を備える
ものである。また加熱によって、流動状態となった有機
溶媒の部分のみ、磁性粒子が移動可能となるため、解像
度の高い像が得られる。Since this image formation is simple due to heat of low energy enough to lower the magnetism and viscosity of the organic solvent, recording is easy, and the resolution can be improved by controlling the particle size of the microcapsules. High image formation is possible. Also, when the magnetic particles are attracted to the back surface of the display, the color of the magnetic particles is hidden due to the color of the dispersion medium that exhibits a solid state at room temperature or the light scattering due to the difference in the refractive index. By coloring the magnetic particles, the display can be changed from a color unique to the magnetic particles to an arbitrary color, that is, a color. Furthermore, a thermal / magnetic head device 3 with a heating function
The image formed in No. 2 has a good recording stability because the dispersion medium is fixed at the same time when the dispersion medium returns to room temperature, and since the image cannot be formed only by magnetism except in the melted state, fogging is caused by touching the magnet. It never happens. The display according to the present invention has the mobility of the contained magnetic particles at the time of recording, that is, both the good recording reactivity and the stability of the recorded image. Further, by heating, the magnetic particles can move only in the portion of the organic solvent that is in a fluidized state, so that an image with high resolution can be obtained.

【００４４】さらに、マイクロカプセルはバインダーに
混ぜることで塗液化することができるため、様々な支持
体に塗布することができ、また、様々な形状に加工する
ことが可能であり、製造工程も簡単であることから、用
途範囲を広げることができる。特に紙上に塗布した場合
は家庭用ファックス等の情報記録紙として使用でき、熱
と磁気の印加により、印字・消去が容易にかつ可逆的に
行えるため、リサイクルペーパーとして用いることが可
能である。Furthermore, since the microcapsules can be made into a coating solution by mixing with a binder, they can be applied to various supports and can be processed into various shapes, and the manufacturing process is simple. Therefore, the range of applications can be expanded. In particular, when applied on paper, it can be used as information recording paper for household faxes and the like, and can be used as recycled paper because printing and erasing can be performed easily and reversibly by applying heat and magnetism.

【００４５】次に図９は、本発明の磁気表示装置２の構
成を説明する概念図であり、それぞれ図１０、図１１に
示すような磁気表示用ディスプレー１の画像記録手段と
して表面、すなわち表示画面側に加熱機能付きの磁気発
生手段である熱・磁気ヘッド装置３２が複数配置された
記録用熱・磁気ヘッド駆動部３４と画像消去手段として
裏面、すなわち表示画面の反対面側に加熱機能付きの磁
気発生手段である熱・磁気ヘッド装置３２が複数配置さ
れた消去用熱・磁気ヘッド駆動部３５と記録・消去を制
御する制御手段３６とが設けられている。この熱・磁気
ヘッド装置３２、３３は、通常の磁気ヘッドにヒーター
などの加熱手段が付加されたものであり、加熱手段は分
散媒２４を溶融させるだけの加熱能力を有していればよ
い。例えばヒーター機能を付加した永久磁石として、選
択的に磁気表示用ディスプレー１面に接近させるように
してもよい。Next, FIG. 9 is a conceptual diagram for explaining the structure of the magnetic display device 2 of the present invention. The surface, ie, the display, is used as the image recording means of the magnetic display 1 as shown in FIGS. 10 and 11, respectively. A recording heat / magnetic head drive unit 34 in which a plurality of heat / magnetic head devices 32, which are magnetic generating means with a heating function, are arranged on the screen side, and a back surface as an image erasing means, that is, a surface opposite to the display screen, has a heating function There are provided an erasing thermal / magnetic head drive section 35 in which a plurality of thermal / magnetic head devices 32, which are magnetic generation means, are arranged, and a control means 36 for controlling recording / erasing. The thermal / magnetic head devices 32 and 33 are ordinary magnetic heads to which a heating unit such as a heater is added, and the heating unit may have a heating capacity enough to melt the dispersion medium 24. For example, a permanent magnet having a heater function may be selectively brought close to the surface of the magnetic display display 1.

【００４６】記録用熱・磁気ヘッド駆動部３４は、制御
手段３６によって表示画像データをデータ処理された表
示データに基づき、対応する各熱・磁気ヘッド装置３２
を動作させる。これにより磁気表示用ディスプレー１の
所定箇所を加熱、磁気印加を行うとともに図示しない移
動装置により、磁気表示用ディスプレー１上を記録用熱
・磁気ヘッド駆動部３４が移動し、画像が記録されるも
のである。また記録用熱・磁気ヘッド駆動部３４は、熱
・磁気ヘッド装置３２を一つ又は複数個熱・磁気ヘッド
駆動部を主走査方向及び副走査方向に移動可能となるよ
うな機構として、磁気表示用ディスプレー１上を主走査
方向及び副走査方向に走査し記録を行なうようにしても
よい。The recording thermal / magnetic head drive unit 34 corresponds to each thermal / magnetic head device 32 on the basis of the display data obtained by processing the display image data by the control means 36.
To operate. As a result, a predetermined portion of the magnetic display 1 is heated and a magnetic field is applied, and the recording thermal / magnetic head drive unit 34 is moved on the magnetic display 1 by a moving device (not shown) to record an image. Is. The recording thermal / magnetic head drive unit 34 uses one or more thermal / magnetic head devices 32 as a mechanism for moving the thermal / magnetic head drive unit in the main scanning direction and the sub-scanning direction. The display 1 may be scanned in the main scanning direction and the sub-scanning direction for recording.

【００４７】また消去用熱・磁気ヘッド駆動部３５も同
様に制御手段３６により各熱・磁気ヘッド装置３２を動
作させ、磁気表示用ディスプレー１の消去箇所をを加
熱、磁気印加を行うとともに図示しない移動装置によ
り、磁気表示用ディスプレー１上を消去用熱・磁気ヘッ
ド駆動部３５が移動し、画像が消去されるものである。
なお、磁気表示用ディスプレー１の主走査方向への消去
用熱・磁気ヘッド駆動部３５の移動による全面消去以外
に、記録用熱・磁気ヘッド駆動部３４と同様の構造と
し、部分的な消去も可能である。Similarly, the erasing thermal / magnetic head drive section 35 operates the thermal / magnetic head devices 32 by the control means 36 to heat the erasing portion of the magnetic display 1 to apply a magnetism and not shown. The moving device moves the erasing thermal / magnetic head drive unit 35 on the magnetic display 1 to erase an image.
In addition to the entire erasing by moving the erasing heat / magnetic head drive unit 35 in the main scanning direction of the magnetic display 1, the structure is similar to that of the recording heat / magnetic head drive unit 34, and partial erasure is also possible. It is possible.

【００４８】[0048]

【発明の効果】本発明の磁気表示用ディスプレー及び磁
気表示装置は、磁性粒子が分散された常温で固相状態を
示す分散媒を内包するマイクロカプセルを含む磁気表示
層を有し、非記録状態は磁気表示用ディスプレーの一方
の面である裏面側に磁性粒子が引き寄せられており、他
方の面である磁気表示用ディスプレーの表面は分散媒の
色、或いはその屈折率差による光散乱により均一な色調
または着色層の色による均一な色調を示し、記録状態
は、磁気表示用ディスプレーの表面側から、加熱手段を
有する熱・磁気ヘッド装置で走査し、加熱と磁気の印加
により磁性粒子が磁気表示用ディスプレーの表面側に移
動し、磁性粒子による黒色の像が形成される。また消去
は全面の加熱と磁気表示用ディスプレーの裏面から全面
に磁気の印加、あるいは加熱と磁気の印加を磁気表示用
ディスプレーの裏面を走査することにより、磁性粒子は
マイクロカプセルの下方に引き寄せられ、磁気表示用デ
ィスプレーの表面は再び分散媒の色、或いはその屈折率
差による光散乱により均一な色調または着色層の色とな
り、像は消去される。INDUSTRIAL APPLICABILITY The magnetic display and magnetic display device of the present invention have a magnetic display layer including a microcapsule containing a dispersion medium in which magnetic particles are dispersed and exhibiting a solid phase state at room temperature, and a non-recorded state. The magnetic particles are attracted to the back side, which is one side of the magnetic display, and the surface of the magnetic display, which is the other side, is uniform due to the color of the dispersion medium or light scattering due to the difference in the refractive index. The color tone or the color of the colored layer shows a uniform color tone, and the recording state is scanned from the surface side of the magnetic display by a thermal / magnetic head device having a heating means, and magnetic particles are magnetically displayed by heating and applying magnetic force. Moving to the surface side of the display, a black image is formed by the magnetic particles. For erasing, heating of the entire surface and application of magnetism from the back surface of the magnetic display to the entire surface, or heating and application of magnetism by scanning the back surface of the magnetic display, magnetic particles are attracted below the microcapsules. On the surface of the magnetic display, the color of the dispersion medium or the light scattering due to the difference in the refractive index between the magnetic display and the surface becomes a uniform color or the color of the colored layer, and the image is erased.

【００４９】すなわち本発明の磁気表示用ディスプレー
及び磁気表示装置は、磁気を印加した部分が、無印加の
部分とは明確に異なるように明暗がはっきりし、かつ解
像度の高く、鮮明で、さらに画像の安定性に優れるなど
の優れた効果を有する。さらに磁性粒子に着色磁気粒子
を用いることによりカラー化が可能となる。That is, in the magnetic display and the magnetic display device of the present invention, the portions to which magnetism is applied are clearly bright and dark so that the portions to which no magnetism is applied are clearly different, the resolution is high, and the image is clear. It has excellent effects such as excellent stability. Furthermore, by using colored magnetic particles as the magnetic particles, colorization is possible.

【００５０】本発明は、低温度の加熱と磁気の印加によ
り簡易に像形成を行うことができるため、低エネルギー
消費であり、記録層にマイクロカプセルを用いることに
より、マイクロカプセルの粒径を制御することで解像度
を高めることができる。しかもマイクロカプセル内で磁
性粒子が常温で固相状態を示す分散媒に分散されてお
り、記録時以外は固定されているため、情報記録後に外
部から磁石などの磁気が印加されても、マイクロカプセ
ル内の磁性粒子に移動を生じることがなく、安定した記
録が得られる。またマイクロカプセル化することで磁気
の影響を受ける範囲が広がらないため、加熱・磁気印加
された部分のみに磁性粒子の移動をほぼ限定できるた
め、解像度が高く、常温で固相状態を示す分散媒を用い
ることで画像の安定性も優れる。In the present invention, since image formation can be easily performed by heating at a low temperature and applying magnetism, the energy consumption is low, and the particle size of the microcapsules can be controlled by using the microcapsules in the recording layer. By doing so, the resolution can be increased. Moreover, since the magnetic particles are dispersed in the dispersion medium that shows a solid state at room temperature in the microcapsule and are fixed except during recording, even if magnetism is externally applied after recording the information, the microcapsule can be Stable recording can be obtained without causing the magnetic particles inside to move. In addition, since the area affected by magnetism does not expand by encapsulating microcapsules, the movement of magnetic particles can be almost limited only to the part where heating and magnetism is applied, so the dispersion medium has high resolution and shows a solid state at room temperature. By using, the image stability is also excellent.

【００５１】またマイクロカプセルを含む塗液を塗布す
る工程とすることができるため、磁気表示用ディスプレ
ーの製造工程を簡略化することができる。Further, since the step of applying the coating liquid containing the microcapsules can be applied, the manufacturing steps of the magnetic display can be simplified.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の磁気表示用ディスプレーの一実施例の
断面図である。FIG. 1 is a sectional view of an embodiment of a magnetic display according to the present invention.

【図２】本発明の他の実施例における磁気表示用ディス
プレーの構成を示す。FIG. 2 shows a structure of a magnetic display according to another embodiment of the present invention.

【図３】本発明の磁気表示用ディスプレーの磁気表示層
に用いられるマイクロカプセルの一実施例を示す断面図
である。FIG. 3 is a cross-sectional view showing an example of microcapsules used in the magnetic display layer of the magnetic display according to the present invention.

【図４】本発明の着色被覆層で被覆された着色磁性粒子
の一実施例を示す断面図である。FIG. 4 is a cross-sectional view showing an example of colored magnetic particles coated with a colored coating layer of the present invention.

【図５】本発明の着色被覆層及び隠蔽層で被覆された着
色磁性粒子の一実施例を示す断面図である。FIG. 5 is a cross-sectional view showing an example of colored magnetic particles coated with a colored coating layer and a masking layer of the present invention.

【図６】本発明の磁気表示用ディスプレーの製造時の状
態を示す説明図である。FIG. 6 is an explanatory view showing a state at the time of manufacturing the magnetic display according to the present invention.

【図７】本発明の磁気表示用ディスプレーの消去動作に
より未記録の状態を示す説明図である。FIG. 7 is an explanatory diagram showing a non-recorded state by the erase operation of the magnetic display of the present invention.

【図８】本発明の磁気表示用ディスプレーの記録時の状
態を示す説明図である。FIG. 8 is an explanatory diagram showing a state of the magnetic display of the present invention during recording.

【図９】本発明の磁気表示装置を説明する概念図であ
る。FIG. 9 is a conceptual diagram illustrating a magnetic display device of the present invention.

【図１０】本発明の磁気表示装置の記録用熱・磁気ヘッ
ド駆動部の構成を説明する説明図である。FIG. 10 is an explanatory diagram illustrating a configuration of a recording thermal / magnetic head drive unit of the magnetic display device of the present invention.

【図１１】本発明の磁気表示装置の消去用熱・磁気ヘッ
ド駆動部の構成を説明する説明図である。FIG. 11 is an explanatory diagram illustrating a configuration of an erasing thermal / magnetic head drive unit of the magnetic display device of the present invention.

【符号の説明】[Explanation of symbols]

１、１０ 磁気表示用ディスプレー ２ 磁気表示装置 １１ 支持体 １２ 磁気表示層 １３ 着色層 １４ 保護支持体 １５ マイクロカプセル １６ バインダー ２１ 芯物質 ２２ 磁性粒子 ２３ 着色磁性粒子 ２３’ 着色磁性粒子 ２４ 分散媒 ２５ 着色被覆層 ２６ 隠蔽層 ２７ 殻物質 ３２、３３ 熱・磁気ヘッド装置 ３４ 記録用熱・磁気ヘッド駆動部 ３５ 消去用熱・磁気ヘッド駆動部 ３６ 制御手段 1, 10 Display for Magnetic Display 2 Magnetic Display Device 11 Support 12 Magnetic Display Layer 13 Coloring Layer 14 Protective Support 15 Microcapsule 16 Binder 21 Core Material 22 Magnetic Particle 23 Colored Magnetic Particle 23 ′ Colored Magnetic Particle 24 Dispersion Medium 25 Colored Coating layer 26 Concealment layer 27 Shell material 32, 33 Thermal / magnetic head device 34 Recording thermal / magnetic head drive unit 35 Erase thermal / magnetic head drive unit 36 Control means

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 少なくとも一方が透明性を有する非磁性
材料からなる支持体間に、少なくとも磁性粒子と、これ
を分散してなる常温において固相状態を示す分散媒とを
内包するマイクロカプセルをバインダー中に分散配置し
てなる磁気表示層を形成したことを特徴とする磁気表示
用ディスプレー。1. A binder comprising microcapsules containing at least magnetic particles and a dispersion medium which is in a solid state at room temperature and is formed by dispersing magnetic particles between supports, at least one of which is a transparent nonmagnetic material. A display for magnetic display, characterized in that a magnetic display layer is formed dispersedly inside. 【請求項２】 前記磁気表示層上に透明性を有する着色
層を積層してなることを特徴とする請求項１記載の磁気
表示用ディスプレー。2. The display for magnetic display according to claim 1, wherein a colored layer having transparency is laminated on the magnetic display layer. 【請求項３】 前記磁性粒子の平均粒径が０．１μｍか
ら１０μｍの間にあることを特徴とする請求項１記載の
磁気表示用ディスプレー。3. The display for magnetic display according to claim 1, wherein the average particle size of the magnetic particles is between 0.1 μm and 10 μm. 【請求項４】 前記磁性粒子が着色磁性粒子であること
を特徴とする請求項１記載の磁気表示用ディスプレー。4. The display for magnetic display according to claim 1, wherein the magnetic particles are colored magnetic particles. 【請求項５】 前記分散媒が融点３５℃以上８０℃以下
の有機化合物であることを特徴とする請求項１記載の磁
気表示用ディスプレー。5. The display for magnetic display according to claim 1, wherein the dispersion medium is an organic compound having a melting point of 35 ° C. or higher and 80 ° C. or lower. 【請求項６】 前記マイクロカプセルの平均粒径が１０
μｍから１０００μｍの間にあることを特徴とする請求
項１記載の磁気表示用ディスプレー。6. The average particle size of the microcapsules is 10
The display for magnetic display according to claim 1, wherein the display is in the range of μm to 1000 μm. 【請求項７】 少なくとも一方が透明性を有する非磁性
材料からなる支持体間に、少なくとも磁性粒子と、これ
らを分散してなる常温において固相状態を示す分散媒と
を内包するマイクロカプセルをバインダー中に分散配置
してなる磁気表示層を形成してなる磁気表示用ディスプ
レーと、 前記磁気表示用ディスプレーの表示面側に配置され、加
熱及び磁気印加により前記マイクロカプセル中の磁性粒
子を部分的に吸引移動せしめる加熱磁気発生手段と、 前記磁気表示用ディスプレーの裏面側に配置され、加熱
及び磁気印加により前記マイクロカプセル中の磁性粒子
を吸引移動せしめる加熱磁気発生手段とを、備えてな
り、前記マイクロカプセル中の磁性粒子を一方の面に偏
在せしめることを特徴とする磁気表示装置。7. A binder, which is a microcapsule containing at least magnetic particles and a dispersion medium having a solid state at room temperature, in which at least one magnetic particle is dispersed, between at least one support made of a non-magnetic material having transparency. A magnetic display for forming a magnetic display layer dispersedly arranged therein, and disposed on the display surface side of the magnetic display, the magnetic particles in the microcapsules partially by heating and magnetic application. A heating magnetism generating means for attracting and moving, and a heating magnetism generating means disposed on the back surface side of the magnetic display for attracting and moving the magnetic particles in the microcapsules by heating and magnetic application. A magnetic display device characterized in that magnetic particles in a capsule are unevenly distributed on one surface.