JPH07258919A - Polyester katch spun-dyed yarn and fishing net using the same spun-dyed yarn - Google Patents

Abstract

PURPOSE:To obtain polyester Katch spun-dyed yarn suitable for general industrial materials, especially for a fishing net, having an excellent color tone, namely improved brightness and chroma and excellent deepness of the color tone. CONSTITUTION:A polyester comprising a main repeating unit composed of ethylene terephthalate and having >=0.7 intrinsic viscosity is mixed with 0.3-0.5wt.% of a red colorant having absorption spectrum of 500-520nm maximum absorption wavelength and 105-135nm half value width, 0.1-0.3wt.% of a brown colorant having absorption spectrum of 440-460nm maximum absorption wavelength and 80-100nm half value width, 0.01-0.06wt.% of anthraquinone-based purple colorant having absorption spectrum of 540-560nm maximum absorption wavelength and 85-105nm half value width and <=0.005wt.% of titanium dioxide as a delustering agent to give the objective polyester Katch spun-dyed yarn. A fishing net comprising the spun-dyed yarn is expected to have an excellent catch in fishing because of excellent deepness of color tone.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、色調、すなわち明度お
よび彩度が良好で、一般産業資材用途、特に漁網用途に
好適なポリエステルカッチ原着糸およびこの原着糸を用
いた漁網に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester catch raw yarn having good color tone, that is, lightness and saturation and suitable for general industrial materials, particularly fishing net, and a fishing net using the raw yarn. is there.

【０００２】[0002]

【従来の技術】一般に、漁網用原糸としては、主にポリ
アミド、ポリエチレンおよびポリエステルなどの合成繊
維が広く使用されている。2. Description of the Related Art Generally, synthetic fibers such as polyamide, polyethylene and polyester are widely used as raw yarns for fishing nets.

【０００３】そして、漁網の製網工程としては、原糸を
施撚し、製網し、染色し、次いで種々の熱処理を施すこ
とからなるのが一般的である。すなわち、製網、編網方
法としては、蛙又結節編網および無結節編網などがあ
り、これらの網を熱水または乾熱により、経または緯方
向に延伸するといった中間工程を経た後、所定の色調に
染色され、さらに、仕上げ熱処理により規定の寸法、目
合いにするべく処理される。The net-making process for fishing nets generally comprises twisting the raw yarn, netting, dyeing, and then subjecting it to various heat treatments. That is, as the net-making and knitting methods, there are frog or knotted knitted nets and knotless knitted nets, etc., which are subjected to an intermediate step of stretching in a warp or weft direction by hot water or dry heat, It is dyed in a predetermined color tone and further processed by finishing heat treatment so as to have predetermined dimensions and texture.

【０００４】しかしながら、近年、製網工程のコストダ
ウン追及の要求が高まるとともに、環境汚染防止のた
め、多大の設備投資を余儀無くされていることから、染
色工程の省略を望む傾向が強くなったきた。However, in recent years, the demand for cost reduction in the net-making process has increased, and a large amount of capital investment has been forced to prevent environmental pollution. Therefore, there is a strong tendency to omit the dyeing process. Came.

【０００５】さらに、ポリエステル原糸の後工程におけ
る染色は、分散染料を用いる染色が主であり、しかも黒
染め、カッチ（茶褐色）染めといったような濃色の染色
が多いため、染料残液も多く、染色コストおよび公害防
止対策にも大きな問題があった。Further, the dyeing in the post-process of the polyester raw yarn is mainly dyeing with a disperse dye, and moreover, there are many dark-colored dyeings such as black dyeing and catch (brown) dyeing. However, there were major problems in dyeing costs and pollution control measures.

【０００６】そこで、ポリエステル原着糸とすることに
よって後染め工程を省略し、かつポリエステルカッチ原
着糸の色調を、後染めによる染色品あるいはポリアミド
などの他素材の原着糸により近似させることを目的とし
た検討が従来から種々なされており、例えば一定の吸収
スペクトルを有するアントラキノン系褐色着色剤と、ペ
リノン系赤色着色剤とを一定量含有する原着ポリエステ
ル糸（特開昭５７−７７３１８号公報）、一定の吸収ス
ペクトルを有するアントラキノン系褐色着色剤と、ペリ
ノン系赤色着色剤と、さらにアントラキノン系紫色着色
剤とを一定量含有する原着ポリエステル糸（特開昭６１
−４１３２２号公報）、および一定の吸収スペクトルを
有するアントラキノン系褐色着色剤と、ペリノン系赤色
着色剤とキノフタロン系黄色着色剤とを一定量含有する
原着ポリエステル糸（特開昭６３−１２３３２８号公
報）などが提案されている。Therefore, it is possible to omit the post-dyeing step by using the polyester dyed yarn and to make the color tone of the polyester catch dyed yarn closer to the dyed product by the dyeing or the dyed yarn of another material such as polyamide. Various studies have been made for the purpose, for example, a dyed polyester yarn containing a certain amount of an anthraquinone brown colorant having a certain absorption spectrum and a perinone red colorant (Japanese Patent Laid-Open No. 57-77318). ), An anthraquinone brown colorant having a constant absorption spectrum, a perinone red colorant, and an anthraquinone purple colorant in a fixed amount.
No. 41322), and an anthraquinone brown colorant having a constant absorption spectrum, a perinone red colorant, and a quinophthalone yellow colorant in a fixed amount (JP-A-63-123328). ) Etc. have been proposed.

【０００７】[0007]

【発明が解決しようとする課題】しかしながら、上述し
た従来技術に記載される着色剤のみを含有するポリエス
テルカッチ原着糸は、依然として染色品あるいはポリア
ミドなどの他素材の原着糸の色調、すなわち「色合い」
および「深み」などを再現することができず、色調が微
妙に漁獲高に影響する漁網に適用した場合には、その要
求性能としての色調を十分に満たすことができなかっ
た。However, the polyester cutty dyed yarn containing only the colorant described in the above-mentioned prior art is still the color tone of the dyed fabric or the dyed yarn of other materials such as polyamide, that is, "hue"
In addition, when it was applied to a fishing net in which the color depth and the "depth" could not be reproduced and the color tone subtly affects the catch, it was not possible to sufficiently satisfy the required color tone.

【０００８】本発明は、上述した従来技術における問題
点を解消するために検討した結果、達成されてものであ
る。The present invention has been achieved as a result of a study for solving the above-mentioned problems in the prior art.

【０００９】したがって、本発明の目的は、カッチ色と
いう微妙な中間色の色調において、すぐれた色調、すな
わち良好な明度および彩度を有すると共に、この色調の
深みが良好であり、一般産業資材用途、特に漁網用途に
好適なポリエステルカッチ原着糸およびこの原着糸を用
いた漁網を提供することにある。Therefore, an object of the present invention is to provide an excellent color tone, that is, good lightness and saturation in a delicate intermediate color tone such as a Kutch color, and the depth of this color tone is good, and the general industrial material application, In particular, it is intended to provide a polyester catch primary yarn and a fishing net using the primary yarn, which are suitable for fishing net applications.

【００１０】[0010]

【課題を解決するための手段】本発明者らは、上記の目
的を達成すべく鋭意検討した結果、特定の褐色着色剤、
赤色着色剤および紫色着色剤の３種類の着色剤をそれぞ
れ特定量使用すると共に、艶消剤である二酸化チタン量
を規定濃度以下にすることによって、色調が良好で、か
つ「深み」のあるポリエステルカッチ原着糸が得られる
ことを見出し本発明に到達した。Means for Solving the Problems As a result of intensive studies to achieve the above object, the present inventors have found that a specific brown colorant,
Polyester with good color tone and "deepness" by using three kinds of colorants, red colorant and purple colorant, in specific amounts, respectively, and by controlling the amount of titanium dioxide, which is a matting agent, to a specified concentration or less. The present invention has been achieved by finding that a catch-dyed yarn can be obtained.

【００１１】すなわち、本発明のポリエステルカッチ原
着糸は、主たる繰り返し単位がエチレンテレフタレート
からなり、固有粘度が０．７以上であるポリエステル中
に、最大吸収波長が５００〜５２０ｎｍ、半価幅が１０
５〜１３５ｎｍの吸収スペクトルを有する赤色着色剤を
０．３〜０．５重量パーセント、最大吸収波長が４４０
〜４６０ｎｍ、半価幅が８０〜１００ｎｍの吸収スペク
トルを有する褐色着色剤を０．１〜０．３重量パーセン
ト、最大吸収波長が５４０〜５６０ｎｍ、半価幅が８５
〜１０５ｎｍの吸収スペクトルを有するアントラキノン
系紫色着色剤を０．０１〜０．０６重量パーセントおよ
び艶消剤としての二酸化チタンを０．００５重量パーセ
ント以下、それぞれ含有することを特徴とする。That is, in the polyester cut fabric-dyed yarn of the present invention, the maximum absorption wavelength is 500 to 520 nm and the half-value width is 10 in the polyester whose main repeating unit is ethylene terephthalate and whose intrinsic viscosity is 0.7 or more.
0.3 to 0.5 weight percent of a red colorant having an absorption spectrum of 5 to 135 nm and a maximum absorption wavelength of 440
0.1 to 0.3% by weight of a brown colorant having an absorption spectrum of 460 nm and a half width of 80 to 100 nm, a maximum absorption wavelength of 540 to 560 nm, and a half width of 85.
It is characterized by containing 0.01 to 0.06 weight percent of anthraquinone-based purple colorant having an absorption spectrum of ˜105 nm and 0.005 weight percent or less of titanium dioxide as a matting agent, respectively.

【００１２】そして、本発明において、赤色着色剤とし
てはペリノン系赤色着色剤の使用が、褐色着色剤として
はアゾメチン系褐色着色剤の使用が、また紫色着色剤と
してはアントラキノン系紫色着色剤の使用が、それぞれ
最も有効である。In the present invention, the red colorant is a perinone red colorant, the brown colorant is an azomethine brown colorant, and the purple colorant is an anthraquinone purple colorant. However, each is the most effective.

【００１３】また、本発明の漁網は、上記ポリエステル
カッチ原着糸を用いて構成したことを特徴とする。Further, the fishing net of the present invention is characterized in that it is constructed by using the above polyester catch dying yarn.

【００１４】以下、本発明を詳細に説明する。The present invention will be described in detail below.

【００１５】本発明で使用する赤色着色剤の色相として
は、最大吸収波長が５００〜５２０ｎｍ、半価幅が１０
５〜１３５ｎｍである吸収スペクトルを有する赤色を、
褐色着色剤の色相としては、最大吸収波長が４４０〜４
６０ｎｍ、半価幅が８０〜１００ｎｍである吸収スペク
トルを有する褐色を、紫色着色剤の色相としては、最大
吸収波長が５４０〜５６０ｎｍ、半価幅が８５〜１０５
ｎｍである吸収スペクトルを有する黄色を使用すること
が、後染めによるポリエステル染色品、あるいはポリア
ミドなどの他素材の原着品の色調と同等の色調を得るた
めに、不可欠の条件である。The hue of the red colorant used in the present invention has a maximum absorption wavelength of 500 to 520 nm and a half-value width of 10.
A red color with an absorption spectrum of 5 to 135 nm,
The hue of the brown colorant has a maximum absorption wavelength of 440 to 4
As the hue of the purple colorant, a brown color having an absorption spectrum of 60 nm and a half-value width of 80 to 100 nm is used as a hue of the purple colorant having a maximum absorption wavelength of 540 to 560 nm and a half value width of 85 to 105.
The use of yellow with an absorption spectrum of nm is an indispensable condition in order to obtain a color tone equivalent to that of a polyester dyed product by post-dyeing or an original product of another material such as polyamide.

【００１６】本発明において、上記各着色剤の添加量
は、赤色着色剤が０．３〜０．５重量パーセント、好ま
しくは０．３５〜０．４５重量パーセント、紫色着色剤
が０．０１〜０．０６重量パーセント、好ましくは０．
０２〜０．０５重量パーセント、褐色着色剤が０．１〜
０．３重量パーセント、好ましくは０．１５〜０．２５
重量パーセントの範囲であり、それぞれの所定量を含有
させることにより、所望の色調の漁網用ポリエステルカ
ッチ原着糸を得ることができる。In the present invention, the amount of each colorant added is 0.3 to 0.5% by weight of the red colorant, preferably 0.35 to 0.45% by weight, and 0.01 to 0.5% of the purple colorant. 0.06 weight percent, preferably 0.
02-0.05 weight percent, brown colorant 0.1-
0.3 weight percent, preferably 0.15-0.25
The content is in the range of weight percent, and by containing the respective predetermined amounts, the polyester catch primary yarn for fishing nets having a desired color tone can be obtained.

【００１７】本発明で使用する上記各着色剤は、色調に
すぐれるばかりでなく、耐熱性も良好で、ポリエステル
溶融成型、溶融紡糸においても熱分解しにくく、ポリエ
ステル中での分散性が良好で、紡糸時の紡糸機内圧の変
動、とくに急激な上昇が少なく、さらには、紡糸前の乾
燥、それに続く紡糸時における着色剤の昇華の少ないも
のである。また、編網、熱セット後の製品での着色剤の
耐摩耗堅牢度も良好である。Each of the above-mentioned colorants used in the present invention has not only excellent color tone but also good heat resistance, is not easily decomposed by heat in polyester melt molding and melt spinning, and has good dispersibility in polyester. The fluctuation of the internal pressure of the spinning machine at the time of spinning is small, especially abrupt increase, and further, the drying before the spinning and the sublimation of the colorant at the time of the subsequent spinning are small. Further, the abrasion resistance fastness of the colorant in the product after knitting and heat setting is also good.

【００１８】また、艶消剤として添加される二酸化チタ
ンは、その添加量が過剰になると「シラケ感」、「不透
明感」が増加し、「深み」のある色調が実現できなくな
るため、その添加量は、０．００５重量パーセント以
下、好ましくは０．００３重量パーセント以下であるこ
とが必須である。When titanium dioxide added as a matting agent is added in an excessive amount, "silk feel" and "opacity" increase, and "deep" color tone cannot be realized. It is essential that the amount be 0.005 weight percent or less, preferably 0.003 weight percent or less.

【００１９】さらに、本発明のポリエステルカッチ原着
糸は、これを漁網用原糸としての用途に供することを考
慮すると、その破断強度が５．０ｇ／デニール以上、好
ましくは６．０ｇ／デニール以上であり、破断伸度が２
０パーセント以上、好ましくは２５パーセント以上であ
ることが不可欠の条件である。Further, in consideration of the fact that the polyester catch spun-dyed yarn of the present invention is used as a raw yarn for fishing nets, the breaking strength thereof is 5.0 g / denier or more, preferably 6.0 g / denier or more. And the elongation at break is 2
It is an essential condition that it is 0% or more, preferably 25% or more.

【００２０】本発明に使用するポリエステルは、テレフ
タル酸を主たる二官能カルボン酸とし、エチレングリコ
ールを主たるグリコール成分とするポリエチレンテレフ
タレートであることが好ましいが、テレフタル酸を一部
をたとえばイソフタル酸、アジピン酸など他の二官能カ
ルボン酸と置き換えたもの、また、エチレングリコール
の一部をたとえばテトラメチレングリコール、１、４−
ヘキサメチレンジメタノール、ポリエチレングリコール
など他のグリコール成分と置き換えたものであっても差
支えない。さらに、少量であれば、トリメシン酸、トリ
メリット酸、ホウ酸、グリセリン、トリメチロールプロ
パンなどの三官能化合物を共重合してもよい。The polyester used in the present invention is preferably polyethylene terephthalate containing terephthalic acid as a main bifunctional carboxylic acid and ethylene glycol as a main glycol component. However, a part of terephthalic acid is used, for example, isophthalic acid or adipic acid. Those which are replaced with other bifunctional carboxylic acids, and a part of ethylene glycol is, for example, tetramethylene glycol, 1,4-
It may be replaced with other glycol components such as hexamethylene dimethanol and polyethylene glycol. Furthermore, if it is a small amount, a trifunctional compound such as trimesic acid, trimellitic acid, boric acid, glycerin, and trimethylolpropane may be copolymerized.

【００２１】本発明のポリエステルカッチ原着糸は、漁
網用糸としての強力、タフネス、耐久性などの機能を確
保するため、固有粘度が、０．７以上、好ましくは０．
８以上であることが必須である。In order to secure functions such as tenacity, toughness and durability as the yarn for fishing net, the polyester cut fabric-dyed yarn of the present invention has an intrinsic viscosity of 0.7 or more, preferably 0.
It is essential that it is 8 or more.

【００２２】本発明で規定する赤色、紫色、褐色の各着
色剤および二酸化チタンの添加方法としては、ポリエス
テル重縮合のためのエステル化工程、あるいは、エステ
ル交換工程、また、重縮合工程において添加する方法、
紡糸時に各着色剤を直接添加する方法、各着色剤を高濃
度で含有するマスターチップをベースチップとブレンド
して紡糸するチップブレンド方式、あるいは各着色剤を
高濃度で含有する溶融マスターポリマを溶融ベースポリ
マに紡糸機中でブレンドして紡糸するメルトブレンド方
式などが挙げられるが、色調、品質の安定性および生産
コストなどの観点からすると、チップブレンド方式ある
いはメルトブレンド方式がとくに有効である。The red, purple, and brown colorants and titanium dioxide specified in the present invention are added in the esterification step for polyester polycondensation, the transesterification step, or the polycondensation step. Method,
A method of directly adding each colorant during spinning, a chip blending method in which a master chip containing a high concentration of each colorant is blended with a base chip and spinning, or a molten master polymer containing a high concentration of each colorant is melted. The melt blending method, in which the base polymer is blended in a spinning machine and spun, can be mentioned. From the viewpoints of color tone, stability of quality and production cost, the chip blending method or the melt blending method is particularly effective.

【００２３】また、必要であれば、これらの着色剤の添
加のために、分散剤、耐熱性向上剤などを、さらにポリ
エステルカッチ原着糸の高機能化のために、耐光剤、酸
化防止剤などを添加しても差支えない。If necessary, a dispersant, a heat resistance improver, etc. may be added for the addition of these colorants, and a light resistance agent, an antioxidant, etc. may be added for enhancing the functionality of the polyester cut yarn. It does not matter even if such as adding.

【００２４】本発明におけるポリエステルカッチ原着糸
は、以下に記述するような通常の製造方法により得るこ
とができる。すなわち、たとえば固有粘度１．０以上の
ポリエステルベースチップと、上記各着色剤を高濃度に
含有するポリエステルマスターチップを、ポリエステル
カッチ原着糸中の各着色剤濃度が所定量の範囲となるよ
うに計量、混合し、前記混合チップを押出機に供給し、
溶融ポリエステルポリマとなし、続いて紡糸口金から紡
糸する。The polyester cut fabric-dyed yarn in the present invention can be obtained by a usual production method as described below. That is, for example, a polyester base chip having an intrinsic viscosity of 1.0 or more and a polyester master chip containing each of the above colorants in a high concentration are adjusted so that the concentration of each colorant in the polyester catch fiber yarn falls within a predetermined range. Weighing, mixing, feeding the mixing chip to the extruder,
It is made of molten polyester polymer and subsequently spun from a spinneret.

【００２５】紡糸された糸条は、加熱筒、断熱筒を通過
した後、冷風により冷却、固化される。さらに引き続
き、油剤を付与した後、引取速度５００〜１０００ｍ／
分に周速を制御された引取ロールで引取られる。The spun yarn passes through a heating cylinder and a heat insulating cylinder and is then cooled and solidified by cold air. Further, subsequently, after applying the oil agent, the take-up speed is 500 to 1000 m /
It is taken by a take-up roll whose peripheral speed is controlled.

【００２６】引取られた未延伸糸は、通常一旦巻取る事
なく延伸に供される。もちろん、一旦未延伸糸を巻取っ
た後延伸してもよい。前記未延伸糸は、連続して７０〜
１２０℃の範囲で加熱制御された２対の供給ロール間
で、１〜１０％のプレストレッチを与えられた後、実質
延伸工程に引続いて導かれる。The drawn undrawn yarn is usually used for drawing without being once wound. Of course, the undrawn yarn may be once wound and then drawn. The undrawn yarn is continuously 70-
After being provided with a prestretch of 1 to 10% between two pairs of feed rolls heated and controlled in the range of 120 ° C., it is introduced subsequently to the substantial stretching step.

【００２７】延伸は２段以上で、延伸倍率が３．５〜
６．０倍の範囲となるように行われる。この延伸と同時
に、１８０℃以上、好ましくは２００℃以上の温度で熱
セットした後、リラックスロールによりリラックスを施
してから、延伸糸は巻取機でパッケージに巻取られる。Stretching is performed in two or more steps, and the stretching ratio is 3.5 to
It is performed so that the range becomes 6.0 times. Simultaneously with this drawing, after heat-setting at a temperature of 180 ° C. or higher, preferably 200 ° C. or higher, after relaxing with a relaxing roll, the drawn yarn is wound into a package by a winding machine.

【００２８】本発明の漁網は、上記ポリエステルカッチ
原着糸を用いて織成（編網）することにより構成された
ものである。The fishing net of the present invention is constructed by weaving (knitting net) using the above polyester catch spun yarn.

【００２９】具体的には、上記ポリエステルカッチ原着
糸を施撚して蛙又結節編網および無結節編網などに製網
し、次いでこれらの網を熱水または乾熱により、経また
は緯方向に延伸するといった中間工程を経た後、仕上げ
熱処理により規定の寸法、目合いにすることにより製造
される。Specifically, the polyester catch dyed yarn is twisted to form a frog or knotted knitted net or a knotless knitted net, and these nets are then warped or wefted with hot water or dry heat. After undergoing an intermediate step of stretching in the direction, it is manufactured by finishing heat treatment so as to have specified dimensions and meshes.

【００３０】かくして得られる本発明のポリエステルカ
ッチ原着糸は、すぐれた色調、すなわち良好な明度およ
び彩度を有するばかりか、この色調の「深み」もすぐれ
たものであって、漁網、シートベルト、陸上ネットおよ
びロープなどの一般産業資材用途として好適であり、と
くにこのポリエステルカッチ原着糸を用いて構成した本
発明の漁網は、そのすぐれた色調、深みに起因して、漁
獲高の増大を期待することができる。The polyester cut fiber-dyed yarn of the present invention thus obtained has not only an excellent color tone, that is, good lightness and saturation, but also an excellent "depth" of this color tone, which is a fishing net or a seat belt. It is suitable for general industrial materials such as land nets and ropes, and in particular, the fishing net of the present invention constituted by using this polyester catch sown yarn, due to its excellent color tone and depth, increases the catch amount. Can be expected.

【００３１】[0031]

【実施例】以下、実施例により、本発明をさらに詳細に
説明する。なお、実施例中の物性は、次のようにして求
めた。EXAMPLES The present invention will be described in more detail below with reference to examples. The physical properties in the examples were determined as follows.

【００３２】（Ａ）着色剤の最大吸収波長：着色剤１２
ｍｇをオルソクロロフェノール１０００ｍｌに添加し、
１００℃、３０分間加熱溶解する。次いで、前記溶液を
１０ｍｍの石英セルに入れ、タングステンランプを光源
とし、吸収スペクトルを分光光度計で測定した。(A) Maximum absorption wavelength of colorant: Colorant 12
mg to 1000 ml of orthochlorophenol,
Heat and dissolve at 100 ° C. for 30 minutes. Then, the solution was put into a 10 mm quartz cell, a tungsten lamp was used as a light source, and an absorption spectrum was measured by a spectrophotometer.

【００３３】（Ｂ）着色剤の半価幅：上記（Ａ）で得た
吸収スペクトルにおいて、各吸収ピークのベースライン
を、各吸収スペクトルが７００ｎｍの波長で示す吸光度
をベースラインの起点として引く。最大吸収ピーク位置
からベースラインに降ろした垂線の垂直二等分線と交わ
る２点間の間隔を半価幅とした。(B) Half-width of colorant: In the absorption spectrum obtained in (A) above, the baseline of each absorption peak is subtracted from the absorbance of each absorption spectrum at a wavelength of 700 nm as the starting point of the baseline. The half-value width was defined as the interval between two points that intersect the perpendicular bisector of the perpendicular drawn from the maximum absorption peak position to the baseline.

【００３４】（Ｃ）固有粘度：オルソクロロフェノール
を溶媒とし、２５℃でオストワルド粘計を使用して測定
した。(C) Intrinsic viscosity: measured with an Ostwald viscometer at 25 ° C. using orthochlorophenol as a solvent.

【００３５】（Ｄ）強伸度：オリエンテック社製テンシ
ロン引張試験機を使用し、試長が２５０ｍｍ、引張速度
が３００ｍｍ／分で測定した。(D) Strength and Elongation: A Tensilon tensile tester manufactured by Orientec Co., Ltd. was used, and the test length was 250 mm and the tensile speed was 300 mm / min.

【００３６】（Ｅ）色調：６ｋｇ巻きのチーズパッケー
ジ表面を、ミノルタ製色彩色差計により測色し、Ｌ値を
求めた。(E) Color tone: The surface of a cheese package of 6 kg was measured by a color difference meter manufactured by Minolta to determine the L value.

【００３７】［実施例１］５１１ｎｍに最大吸収波長を
有し、半価幅が１１０ｎｍであるペリノン系赤色着色剤
を１５．５重量パーセントと、５２０ｎｍに最大吸収波
長を有し、半価幅が１０５ｎｍであるアントラキノン系
紫色着色剤を１．５重量パーセントと、４５０ｎｍに最
大吸収波長を有し、半価幅が９０ｎｍであるアゾメチン
系褐色着色剤を８．０重量パーセントと、二酸化チタン
を０．１重量パーセントとを含有するポリエチレンテレ
フタレートマスターチップと、固有粘度が１．０で、二
酸化チタンを含有しないポリエチレンテレフタレートベ
ースチップとを、重量比で１対４０となるように計量、
混合し、エクストルーダー型紡糸機で紡糸した。[Example 1] 15.5% by weight of a perinone red colorant having a maximum absorption wavelength at 511 nm and a half width of 110 nm, and a maximum absorption wavelength at 520 nm, and a half width. Anthraquinone purple colorant having a wavelength of 105 nm is 1.5% by weight, an azomethine brown colorant having a maximum absorption wavelength at 450 nm and a half value width of 90 nm is 8.0% by weight, and titanium dioxide is 0.1% by weight. A polyethylene terephthalate master chip containing 1% by weight and a polyethylene terephthalate base chip having an intrinsic viscosity of 1.0 and containing no titanium dioxide are weighed to a weight ratio of 1:40,
The mixture was mixed and spun by an extruder type spinning machine.

【００３８】紡糸温度は３００℃、また、紡糸口金は、
孔径０．６ｍｍ、８４ホールのものを使用した。The spinning temperature is 300 ° C., and the spinneret is
A hole having a hole diameter of 0.6 mm and 84 holes was used.

【００３９】紡糸された糸条を、３２０℃に加熱制御さ
れた加熱筒と無加熱の断熱筒を通過させ、冷却風によ
り、冷却、固化した後、続いて油剤を付与し、５００ｍ
／分で引き取った。The spun yarn is passed through a heating cylinder whose temperature is controlled at 320 ° C. and an unheated heat-insulating cylinder, cooled and solidified by cooling air, and subsequently an oil agent is applied to the yarn for 500 m.
/ Min.

【００４０】引き取られた糸条を、一旦巻き取ることな
く、これに６パーセントのプレストレッチを与えた後、
延伸倍率が４．２倍、リラックス率６パーセント、熱セ
ット温度２２０℃の条件で処理した後、パッケージに巻
き取った。なお、延伸は２段で行い、１段目の延伸倍率
は３．７倍とした。The wound yarn was given a 6% pre-stretch to it without winding it once,
The film was wound on a package after being treated under the conditions of a draw ratio of 4.2 times, a relaxation rate of 6%, and a heat setting temperature of 220 ° C. The stretching was performed in two stages, and the stretching ratio in the first stage was 3.7 times.

【００４１】得られたポリエステルカッチ原着糸中の着
色剤含有量は、赤色着色剤が０．３７８重量パーセン
ト、紫色着色剤が０．０３７重量パーセント、褐色着色
剤が０．１９５重量パーセント、二酸化チタンが０．０
０２４重量パーセントであった。The content of the coloring agent in the obtained polyester cut dyed yarn was 0.378% by weight of red coloring agent, 0.037% by weight of purple coloring agent, 0.195% by weight of brown coloring agent, and 0.0 for titanium
It was 024 weight percent.

【００４２】上記のようにして得られた１０００デニー
ル、８４フィラメントのポリエステルカッチ原着糸の各
種特性を評価した結果を表１に示した。Table 1 shows the results of evaluation of various properties of the polyester denier yarn of 1000 denier and 84 filaments obtained as described above.

【００４３】なお、表１には、一般的なポリアミドカッ
チ原着糸の色調評価結果を併せて示した。Table 1 also shows the color tone evaluation results of a general polyamide cut fabric-dyed yarn.

【００４４】表１の結果から明らかなように、本発明の
ポリエステルカッチ原着糸は、所望の固有粘度、強度お
よび伸度が満足されるとともに、ポリアミドカッチ原着
糸と同等の色調を有する。As is clear from the results shown in Table 1, the polyester cut fiber-dyed yarn of the present invention satisfies the desired intrinsic viscosity, strength and elongation and has the same color tone as the polyamide cut fiber-dyed yarn.

【００４５】［比較例１］実施例１と同様の方法で、ポ
リエステルカッチ原着糸中の赤色着色剤が０．２７７重
量パーセント、紫色着色剤が０．０２７重量パーセン
ト、褐色着色剤が０．１４３重量パーセント、二酸化チ
タンが０．００１８重量パーセントである１０００デニ
ール、８４フィラメントのポリエステルカッチ原着糸を
得た。Comparative Example 1 In the same manner as in Example 1, 0.277% by weight of the red colorant, 0.027% by weight of the purple colorant and 0. A 1000 denier, 84 filament polyester cut fiber dyed yarn having 143 weight percent and titanium dioxide 0.0018 weight percent was obtained.

【００４６】このポリエステルカッチ原着糸の各種特性
を評価した結果を表１に併せて示した。Table 1 also shows the results of evaluation of various properties of the polyester cut fabric-dyed yarn.

【００４７】表１の結果から明らかなように、本比較例
品は、固有粘度、強度および伸度は満足するが、色調の
Ｌ値が高く、「深み」に欠けるものであった。As is clear from the results in Table 1, the product of this comparative example satisfied the intrinsic viscosity, strength and elongation, but had a high L value of the color tone and lacked "depth".

【００４８】［比較例２］実施例１において、二酸化チ
タンを０．１重量パーセントを含有するポリエチレンテ
レフタレートベースチップを使用した以外は同様にし
て、赤色着色剤が０．３７８重量パーセント、紫色着色
剤が０．０３７重量パーセント、褐色着色剤が０．１９
５重量パーセント、二酸化チタンが０．１重量パーセン
トである１０００デニール、８４フィラメントのポリエ
ステルカッチ原着糸を得た。COMPARATIVE EXAMPLE 2 The procedure of Example 1 was repeated except that polyethylene terephthalate base chips containing 0.1% by weight of titanium dioxide were used. 0.037 weight percent, brown colorant 0.19
A 1000 denier, 84 filament polyester cut fiber dyed yarn having 5 weight percent and 0.1 weight percent titanium dioxide was obtained.

【００４９】このポリエステルカッチ原着糸の各種特性
を評価した結果を表１に併せて示した。Table 1 also shows the results of evaluation of various properties of the polyester cut fiber-dyed yarn.

【００５０】表１の結果から明らかなように、本比較例
品は、固有粘度、強度および伸度は満足するが、色調の
Ｌ値が高く、「深み」に欠け、さらに「シラケ感」のあ
るものであった。As is clear from the results in Table 1, the product of this comparative example satisfies the intrinsic viscosity, strength and elongation, but has a high L value of color tone, lacks in "depth", and has "silky feeling". It was something.

【００５１】[0051]

【表１】 [Table 1]

【００５２】[0052]

【発明の効果】以上、説明したように、本発明のポリエ
ステルカッチ原着糸は、すぐれた色調、すなわち良好な
明度および彩度を有するばかりか、この色調の「深み」
もすぐれたものである。As described above, the polyester cut fabric-dyed yarn of the present invention has not only an excellent color tone, that is, good lightness and saturation, but also "depth" of this color tone.
It is also excellent.

【００５３】しかも、本発明のポリエステルカッチ原着
糸は、強度、タフネス、耐久性にすぐれており、漁網、
シートベルト、陸上ネットおよびロープなどの一般産業
資材用途として好適である。Moreover, the polyester cut yarn-dyed yarn of the present invention is excellent in strength, toughness, and durability.
Suitable for general industrial materials such as seat belts, land nets and ropes.

【００５４】そして、上記ポリエステルカッチ原着糸を
用いて構成した本発明の漁網は、そのすぐれた色調、深
みに起因して、漁獲高の増大を期待することができる。The fishing net of the present invention constructed by using the above polyester catch spun yarn can be expected to have an increased catch due to its excellent color tone and depth.

フロントページの続き (51)Int.Cl.⁶ 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０１Ｆ 6/62 ３０２ Ｃ Continuation of front page (51) Int.Cl. ⁶ Identification number Office reference number FI technical display location D01F 6/62 302 C

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 主たる繰り返し単位がエチレンテレフ
タレートからなり、固有粘度が０．７以上であるポリエ
ステル中に、最大吸収波長が５００〜５２０ｎｍ、半価
幅が１０５〜１３５ｎｍの吸収スペクトルを有する赤色
着色剤、最大吸収波長が４４０〜４６０ｎｍ、半価幅が
８０〜１００ｎｍの吸収スペクトルを有する褐色着色
剤、および最大吸収波長が５４０〜５６０ｎｍ、半価幅
が８５〜１０５ｎｍの吸収スペクトルを有するアントラ
キノン系紫色着色剤を含有せしめたことを特徴とするポ
リエステルカッチ原着糸。1. A red colorant having an absorption spectrum with a maximum absorption wavelength of 500 to 520 nm and a half width of 105 to 135 nm in a polyester whose main repeating unit is ethylene terephthalate and which has an intrinsic viscosity of 0.7 or more. , A brown colorant having an absorption spectrum with a maximum absorption wavelength of 440 to 460 nm and a half width of 80 to 100 nm, and an anthraquinone-based purple coloring having an absorption spectrum of a maximum absorption wavelength of 540 to 560 nm and a half width of 85 to 105 nm A polyester-catch-dyed yarn characterized by containing an agent. 【請求項２】 主たる繰り返し単位がエチレンテレフ
タレートからなり、固有粘度が０．７以上であるポリエ
ステル中に、最大吸収波長が５００〜５２０ｎｍ、半価
幅が１０５〜１３５ｎｍの吸収スペクトルを有する赤色
着色剤を０．３〜０．５重量パーセント、最大吸収波長
が４４０〜４６０ｎｍ、半価幅が８０〜１００ｎｍの吸
収スペクトルを有する褐色着色剤を０．１〜０．３重量
パーセント、最大吸収波長が５４０〜５６０ｎｍ、半価
幅が８５〜１０５ｎｍの吸収スペクトルを有するアント
ラキノン系紫色着色剤を０．０１〜０．０６重量パーセ
ントおよび艶消剤としての二酸化チタンを０．００５重
量パーセント以下、それぞれ含有することを特徴とする
ポリエステルカッチ原着糸。2. A red colorant having an absorption spectrum with a maximum absorption wavelength of 500 to 520 nm and a half-value width of 105 to 135 nm in a polyester whose main repeating unit is ethylene terephthalate and which has an intrinsic viscosity of 0.7 or more. 0.3 to 0.5 weight percent, a maximum absorption wavelength of 440 to 460 nm, a half-value width of a brown colorant having an absorption spectrum of 80 to 100 nm, and a maximum absorption wavelength of 540. .About.560 nm, 0.01 to 0.06% by weight of anthraquinone purple colorant having an absorption spectrum having a half width of 85 to 105 nm, and 0.005% by weight or less of titanium dioxide as a matting agent, respectively. Polyester-catch-dyed yarn characterized by 【請求項３】 赤色着色剤がペリノン系赤色着色剤、
褐色着色剤がアゾメチン系褐色着色剤、紫色着色剤がア
ントラキノン系紫色着色剤であることを特徴とする請求
項１または２に記載のポリエステルカッチ原着糸。3. The red colorant is a perinone red colorant,
The polyester cut fiber yarn according to claim 1 or 2, wherein the brown colorant is an azomethine brown colorant and the purple colorant is an anthraquinone purple colorant. 【請求項４】 二酸化チタンの含有量が、０．００３
重量パーセント以下であることを特徴とする請求項１、
２または３に記載のポリエステルカッチ原着糸。4. The content of titanium dioxide is 0.003.
A weight percent or less, Claim 1,
The polyester cut fabric-dyed yarn according to 2 or 3. 【請求項５】 原着糸の破断強度が、５．０ｇ／デニ
ール以上であり、破断伸度が２０パーセント以上である
ことを特徴とする請求項１、２、３または４に記載のポ
リエステルカッチ原着糸。5. The polyester cut according to claim 1, 2, 3 or 4, wherein the spun yarn has a breaking strength of 5.0 g / denier or more and a breaking elongation of 20% or more. Moped yarn. 【請求項６】 原着糸の破断強度が、６．０ｇ／デニ
ール以上であり、破断伸度が２５パーセント以上である
ことを特徴とする請求項１、２、３、４または５に記載
のポリエステルカッチ原着糸。6. The breaking strength of the spun yarn is 6.0 g / denier or more and the breaking elongation is 25% or more, according to claim 1, 2, 3, 4 or 5. Polyester cut yarn. 【請求項７】 請求項１、２、３、４、５または６に
記載のポリエステルカッチ原着糸を用いて構成したこと
を特徴とする漁網。7. A fishing net, which is constructed by using the polyester catch-dyed yarn according to any one of claims 1, 2, 3, 4, 5 or 6.