JPH07257951A - Water reducing agent for cement added viscous soil - Google Patents
Water reducing agent for cement added viscous soilInfo
- Publication number
- JPH07257951A JPH07257951A JP4870194A JP4870194A JPH07257951A JP H07257951 A JPH07257951 A JP H07257951A JP 4870194 A JP4870194 A JP 4870194A JP 4870194 A JP4870194 A JP 4870194A JP H07257951 A JPH07257951 A JP H07257951A
- Authority
- JP
- Japan
- Prior art keywords
- acid
- cement
- reducing agent
- salt
- copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、セメントを添加した
粘性土用減水剤および該減水剤を使用してセメントを添
加した粘性土を流動化する方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cement-added water reducing agent for cohesive soil and a method for fluidizing cement-added cohesive soil using the water reducing agent.
【０００２】[0002]
【従来の技術】粘性土、例えば浚渫や堀削により生じた
軟弱粘土にセメントを添加し、固化処理することにより
埋立土に使用したり、軟弱地盤をセメントで固化処理す
る方法が行われている。このようなセメントを用いた軟
弱粘土処理工法の混練および打設方法には従来、次のよ
うな方法がある。 （１）処理ボンド内あるいは施工現場でバックホウやク
ラムシェルなどにより、バケットおよび回転攪拌機を用
いて固化材と土を混練する方法。 （２）建設残土あるいは軟弱土の輸送管もしくは圧送管
に直接セメントを注入することにより混練する方法。処
理ボンドに排出後さらにバックホウなどにより混練する
場合もあり得る。適用は高濃度輸送に限定される。 （３）プラント内でセメントを混練し、処理地まで管路
あるいはトラックなどにより輸送する方法。2. Description of the Related Art Cement is added to cohesive soil, for example, soft clay produced by dredging or excavation, and solidified to be used for landfill soil, or soft ground is solidified with cement. . Conventionally, the following methods have been known as kneading and placing methods in the soft clay processing method using such cement. (1) Treatment A method of kneading the solidified material and soil using a bucket and a rotary stirrer with a backhoe, a clam shell, or the like in the bond or at the construction site. (2) A method in which cement is directly injected into a transport pipe or a pressure-feed pipe of construction residual soil or soft soil to perform kneading. After discharging to the treated bond, it may be further kneaded with a backhoe or the like. Applications are limited to high-concentration transport. (3) A method of kneading cement in a plant and transporting it to a treatment site by a pipeline or a truck.
【０００３】[0003]
【発明が解決しようとする課題】上述した各方法の内、
（１）の方法で処分する場合には、小型重機のトラフィ
カビリティが良好であることが必要であり、また、均一
に混練することが困難であることから、品質のばらつき
が大きいという欠点がある。Among the above-mentioned methods,
In the case of disposing by the method (1), it is necessary that the trafficability of the small heavy equipment is good, and it is difficult to uniformly knead, so that there is a drawback that there is a large variation in quality. .
【０００４】（２）と（３）の方法により処理された土
砂を有効利用する場合には、初期強度が低いために中間
処分地において養生する場合があるが、十分な面積の中
間処分地を得ることが困難であることが多く、また費用
および期間が多大になるという問題を生ずる。When the soil treated by the methods (2) and (3) is effectively used, it may be cured at the intermediate disposal site due to its low initial strength. It is often difficult to obtain and creates a problem of high cost and time.
【０００５】また、中間処分地をもうけず直接最終処分
地に排泥する場合には、土砂の初期含水比が相当高いも
のでないと、セメントを添加した土砂の流動性はかなり
低く、施工性が良くないために、均しや締固めなどの処
置が必要になるという問題があった。Further, when sludge is discharged directly to the final disposal site without leaving the intermediate disposal site, unless the initial water content of the sediment is considerably high, the fluidity of the cement-added sediment is considerably low and the workability is low. Since it is not good, there is a problem that measures such as leveling and compaction are required.
【０００６】施工性を上げるために、土砂に加水して流
動性を確保する方法もあるが、加水することにより処理
土量が増加し、したがって、中間処分地もしくは最終処
分地の増大および施工量、セメントなどの材料費が増大
するという問題が生じていた。[0006] In order to improve the workability, there is also a method of adding fluidity to the soil to ensure the fluidity, but the addition of water increases the amount of treated soil, and therefore the increase of the intermediate disposal site or the final disposal site and the construction amount. The problem was that the cost of materials such as cement would increase.
【０００７】本発明は、このようなセメント添加土の処
理処分に際して生ずる体積増加および施工性を左右する
流動性の改善を目的としてなされたものである。[0007] The present invention has been made for the purpose of improving the fluidity that affects the increase in volume and workability that occur during the treatment and disposal of such cement-added soil.
【０００８】[0008]
【課題を解決するための手段】上記従来の課題を解決す
るため、鋭意研究の結果、ある種の化合物（重合体）が
セメントを添加した粘性土用減水剤として優れた効果を
有するという新知見を得、さらに研究を進めた結果、こ
の発明を完成した。本発明はセメントを添加した粘性土
用減水剤を提供するものであり、さらに該減水剤を用い
てセメントを添加した粘性土の流動化処理工法を提供す
るものである。[Means for Solving the Problems] In order to solve the above-mentioned conventional problems, as a result of intensive research, a new finding that a certain compound (polymer) has an excellent effect as a water-reducing agent for cement-containing cohesive soil As a result of further research, the present invention was completed. The present invention provides a water-reducing agent for cohesive soil to which cement is added, and further provides a fluidization treatment method for cohesive soil to which cement is added using the water-reducing agent.
【０００９】本発明の減水剤が用いられるセメントを添
加した粘性土における粘性土は通常、粒径が７５マイク
ロメーター以下の土粒子群が土全体の重量の２０％以上
含有するものを意味し、例えば浚渫や堀削により生じた
軟弱粘土（浚渫土や堀削土）、建設残土等が本発明を適
用する粘性土の好ましい例としてあげられる。そしてこ
のような粘性土にセメントを添加したものに、この発明
の減水剤が適用される。The cohesive soil in the cement-added cohesive soil in which the water reducing agent of the present invention is used usually means that the soil particle group having a particle size of 75 micrometers or less contains 20% or more of the total weight of the soil, For example, soft clay (dredge soil or excavated soil) produced by dredging or excavation, construction residual soil, and the like are preferable examples of the cohesive soil to which the present invention is applied. Then, the water reducing agent of the present invention is applied to such a clay soil to which cement is added.
【００１０】本発明のセメントを添加した粘性土用減水
剤としては、下記の（１）〜（５）の重合体が挙げられ
る。ここで記載した重量平均分子量はポリエチレングリ
コールを標準品としてゲルパーミュエーション（ＧＰ
Ｃ）法で測定したものである。Examples of the water-reducing agent for cohesive soil to which the cement of the present invention is added include the following polymers (1) to (5). The weight average molecular weight described here is based on gel permeation (GP) using polyethylene glycol as a standard product.
It is measured by method C).
【００１１】（１）アクリル酸、メタクリル酸、ビニル
酢酸およびクロトン酸から選ばれた１種または２種以上
の単量体より生成された単一重合体、共重合体、または
それらの塩であり、重量平均分子量が１，０００〜５０
０，０００であるもの。このうち単一重合体の好ましい
ものとしては、次のものが挙げられる。アクリル酸より
なる単一重合体もしくはその塩であり、単一重合体もし
くはその塩の重量平均分子量が１，０００〜２００，０
００の範囲であるもの、更に好ましいものとしては、重
量平均分子量が５，０００〜１００，０００の範囲であ
るもの。共重合体の好ましいものとしてはアクリル酸と
メタクリル酸よりなる共重合体もしくはその塩であり、
共重合体もしくはその塩の重量平均分子量が１，０００
〜２００，０００の範囲であり、共重合体もしくはその
塩の重合比がアクリル酸もしくはその塩１０〜９９モル
％、メタクリル酸もしくはその塩１〜９０モル％の範囲
であるもの。更に好ましいもとしては重量平均分子量が
５，０００〜１０，０００の範囲であり、共重合体もし
くはその塩の重合比が、アクリル酸もしくはその塩５０
〜９９モル％、メタクリル酸もしくはその塩１〜５０モ
ル％の範囲であるもの。(1) A homopolymer, a copolymer or a salt thereof formed from one or more monomers selected from acrylic acid, methacrylic acid, vinyl acetic acid and crotonic acid, Weight average molecular weight of 1,000 to 50
What is 10,000. Among these, the following are preferred as the homopolymers. A homopolymer of acrylic acid or a salt thereof, wherein the weight average molecular weight of the homopolymer or its salt is 1,000 to 200,0.
In the range of 00, and more preferably in the range of 5,000 to 100,000. A preferred copolymer is a copolymer of acrylic acid and methacrylic acid or a salt thereof,
The weight average molecular weight of the copolymer or its salt is 1,000.
To 200,000, and the polymerization ratio of the copolymer or its salt is in the range of 10 to 99 mol% of acrylic acid or its salt and 1 to 90 mol% of methacrylic acid or its salt. More preferably, the weight average molecular weight is in the range of 5,000 to 10,000, and the polymerization ratio of the copolymer or its salt is 50% or less of acrylic acid or its salt.
To 99 mol% and methacrylic acid or a salt thereof in the range of 1 to 50 mol%.
【００１２】具体例としては次のものが挙げられる。重
量平均分子量が１０，０００のポリアクリル酸ソーダ、
重量平均分子量が１００，０００のポリアクリル酸ソー
ダ、重量平均分子量が３００，０００のポリアクリル酸
ソーダ、重量平均分子量が１０，０００のポリアクリル
酸アンモニウム、重量平均分子量が１０，０００であ
り、重合比がアクリル酸ソーダ７０モル％、メタクリル
酸３０モル％であるアクリル酸ソーダとメタクリル酸の
共重合体。Specific examples include the following. Poly (sodium acrylate) having a weight average molecular weight of 10,000,
Poly (sodium acrylate) having a weight average molecular weight of 100,000, poly (sodium acrylate) having a weight average molecular weight of 300,000, ammonium polyacrylate having a weight average molecular weight of 10,000, and a weight average molecular weight of 10,000. A copolymer of sodium acrylate and methacrylic acid having a ratio of 70 mol% sodium acrylate and 30 mol% methacrylic acid.
【００１３】（２）下記（イ）および（ロ）の単量体よ
り生成された共重合体またはその塩であり、重量平均分
子量が１，０００〜５００，０００であるもの。 （イ）アクリル酸および／またはメタクリル酸、（ロ）
アルキル基の炭素数が１〜８のアクリル酸アルキルエス
テル、アルキル基の炭素数が１〜８のメタクリル酸アル
キルエステル、アルキル基の炭素数が１〜８のアクリル
酸ヒドロキシアルキルエステル、アルキル基の炭素数が
１〜８のメタクリル酸ヒドロキシアルキルエステル、ア
クリルアミド、スチレン、イソブチレンおよび酢酸ビニ
ルから選ばれた１種または２種以上の単量体。好ましい
ものとしては次のものが挙げられる。アクリル酸とアク
リルアミドよりなる共重合体もしくはその塩であり、共
重合体もしくはその塩の重量平均分子量が１，０００〜
２００，０００の範囲であり、共重合体もしくはその塩
の重合比が、アクリル酸もしくはその塩１０〜９９モル
％、アクリルアミド１〜９０モル％の範囲であるもの。(2) A copolymer or a salt thereof produced from the following monomers (a) and (b), having a weight average molecular weight of 1,000 to 500,000. (A) acrylic acid and / or methacrylic acid, (b)
Acrylic acid alkyl ester whose alkyl group has 1 to 8 carbon atoms, methacrylic acid alkyl ester whose alkyl group has 1 to 8 carbon atoms, acrylic acid hydroxyalkyl ester whose alkyl group has 1 to 8 carbon atoms, and alkyl group carbon One or more monomers selected from methacrylic acid hydroxyalkyl esters having a number of 1 to 8, acrylamide, styrene, isobutylene, and vinyl acetate. The following are preferred. A copolymer of acrylic acid and acrylamide or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is 1,000 to
It is in the range of 200,000, and the polymerization ratio of the copolymer or its salt is in the range of 10 to 99 mol% of acrylic acid or its salt and 1 to 90 mol% of acrylamide.
【００１４】更に好ましいものとしては次のものが挙げ
られる。アクリル酸とアクリルアミドよりなる共重合体
もしくはその塩であり、共重合体もしくはその塩の重量
平均分子量が５，０００〜１００，０００の範囲であ
り、共重合体もしくはその塩の重合比が、アクリル酸も
しくはその塩５０〜９９モル％、アクリルアミド１〜５
０モル％の範囲であるもの。具体例としては次のものが
挙げられる。重量平均分子量が１０，０００であり、重
合比がアクリル酸ソーダ９０モル％、アクリルアミド１
０モル％であるアクリル酸ソーダとアクリルアミドの共
重合体。More preferable examples include the following. A copolymer of acrylic acid and acrylamide or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is in the range of 5,000 to 100,000, and the polymerization ratio of the copolymer or its salt is acrylic. Acid or its salt 50-99 mol%, acrylamide 1-5
Those in the range of 0 mol%. Specific examples include the following. The weight average molecular weight is 10,000, the polymerization ratio is 90 mol% sodium acrylate, and acrylamide 1
A copolymer of sodium acrylate and acrylamide that is 0 mol%.
【００１５】（３）下記（ハ）および（ニ）の単量体よ
り生成された共重合体またはその塩であり、重量平均分
子量が１，０００〜５００，０００であるもの。 （ハ）アクリル酸および／またはメタクリル酸、（ニ）
マレイン酸、無水マレイン酸、フマール酸およびイタコ
ン酸から選ばれた１種または２種以上の不飽和ジカルボ
ン酸。好ましいものとしては次のものが挙げられる。ア
クリル酸とマレイン酸よりなる共重合体もしくはその塩
であり、共重合体もしくはその塩の重量平均分子量が
１，０００〜２００，０００の範囲であり、共重合体も
しくはその塩の重合比が、アクリル酸もしくはその塩５
０〜９９モル％、マレイン酸もしくはその塩１〜５０モ
ル％の範囲であるもの。(3) A copolymer produced from the following monomers (c) and (d) or a salt thereof, having a weight average molecular weight of 1,000 to 500,000. (C) Acrylic acid and / or methacrylic acid, (D)
One or more unsaturated dicarboxylic acids selected from maleic acid, maleic anhydride, fumaric acid and itaconic acid. The following are preferred. A copolymer of acrylic acid and maleic acid or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is in the range of 1,000 to 200,000, and the polymerization ratio of the copolymer or its salt is Acrylic acid or its salt 5
Those having a range of 0 to 99 mol% and 1 to 50 mol% of maleic acid or a salt thereof.
【００１６】更に好ましいものとしては、次のものが挙
げられる。アクリル酸とマレイン酸よりなる共重合体も
しくはその塩であり、共重合体もしくはその塩の重量平
均分子量が５，０００〜１００，０００の範囲であり、
共重合体もしくはその塩の重合比がアクリル酸もしくは
その塩８０〜９９モル％、マレイン酸もしくはその塩１
〜２０モル％の範囲であるもの。具体例としては次のも
のが挙げられる。重量平均分子量が１０，０００であ
り、重合比がアクリル酸ソーダ９５モル％、マレイン酸
ソーダ５モル％であるアクリル酸ソーダとマレイン酸ソ
ーダの共重合体。The following are more preferred. A copolymer of acrylic acid and maleic acid or a salt thereof, wherein the weight average molecular weight of the copolymer or salt thereof is in the range of 5,000 to 100,000,
The copolymerization ratio of the copolymer or its salt is 80 to 99 mol% of acrylic acid or its salt, and maleic acid or its salt 1
In the range of up to 20 mol%. Specific examples include the following. A copolymer of sodium acrylate and sodium maleate having a weight average molecular weight of 10,000 and a polymerization ratio of 95 mol% sodium acrylate and 5 mol% sodium maleate.
【００１７】（４）下記（ホ）および（ヘ）の単量体よ
り生成された共重合体またはその塩であり、重量平均分
子量が１，０００〜３００，０００であるもの。 （ホ）アクリル酸、メタクリル酸、マレイン酸、無水マ
レイン酸、フマール酸およびイタコン酸から選ばれた１
種または２種以上の不飽和カルボン酸、（ヘ）スチレン
スルホン酸、２−アクリルアミド−２−メチルプロパン
スルホン酸、３−アクリルオキシ−２−ヒドロキシ−プ
ロパンスルホン酸、ビニルスルホン酸、アリルスルホン
酸およびメタアリルスルホン酸から選ばれた１種または
２種以上の不飽和スルホン酸。好ましいものとしては、
次のものが挙げられる。アクリル酸とスチレンスルホン
酸または２−アクリルアミド−２−メチルプロパンスル
ホン酸よりなる共重合体もしくはその塩であり、共重合
体もしくはその塩の重量平均分子量が１，０００〜２０
０，０００の範囲であり、共重合体もしくはその塩の重
合比が、アクリル酸もしくはその塩１０〜９９モル％、
スチレンスルホン酸もしくはその塩または２−アクリル
アミド−２−メチルプロパンスルホン酸もしくはその塩
１〜９０モル％の範囲であるもの。(4) A copolymer or a salt thereof produced from the following monomers (e) and (f), which has a weight average molecular weight of 1,000 to 300,000. (E) 1 selected from acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid and itaconic acid
Or two or more unsaturated carboxylic acids, (f) styrenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 3-acryloxy-2-hydroxy-propanesulfonic acid, vinylsulfonic acid, allylsulfonic acid and One or more unsaturated sulfonic acids selected from methallyl sulfonic acids. The preferred one is
These include: A copolymer or a salt thereof of acrylic acid and styrene sulfonic acid or 2-acrylamido-2-methylpropane sulfonic acid, wherein the weight average molecular weight of the copolymer or the salt is 1,000 to 20.
And the polymerization ratio of the copolymer or its salt is 10 to 99 mol% of acrylic acid or its salt,
Styrene sulfonic acid or a salt thereof or 2-acrylamido-2-methylpropane sulfonic acid or a salt thereof in the range of 1 to 90 mol%.
【００１８】更に好ましいものとしては、次のものが挙
げられる。アクリル酸とスチレンスルホン酸または２−
アクリルアミド−２−メチルプロパンスルホン酸よりな
る共重合体もしくはその塩であり、共重合体もしくはそ
の塩の重量平均分子量が５，０００〜１００，０００の
範囲であり、共重合体もしくはその塩の重合比が、アク
リル酸もしくはその塩５０〜９９モル％、スチレンスル
ホン酸もしくはその塩または２−アクリルアミド−２−
メチルプロパンスルホン酸もしくはその塩１〜５０モル
％の範囲であるもの。具体例としては次のものが挙げら
れる。重量平均分子量が１２，０００であり重合比がア
クリル酸ソーダ７０モル％、スチレンスルホン酸ソーダ
３０モル％であるアクリル酸ソーダとスチレンスルホン
酸ソーダの共重合体、および重量平均分子量が１５，０
００であり重合比がアクリル酸ソーダ７０モル％、２−
アクリルアミド−２−メチルプロパンスルホン酸ソーダ
３０モル％であるアクリル酸ソーダと２−アクリルアミ
ド−２−メチルプロパンスルホン酸ソーダの共重合体。More preferred are the following. Acrylic acid and styrene sulfonic acid or 2-
A copolymer of acrylamido-2-methylpropanesulfonic acid or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is in the range of 5,000 to 100,000, and the copolymer or its salt is polymerized. The ratio is 50 to 99 mol% of acrylic acid or a salt thereof, styrenesulfonic acid or a salt thereof or 2-acrylamido-2-
Methyl propane sulfonic acid or a salt thereof in the range of 1 to 50 mol%. Specific examples include the following. A copolymer of sodium acrylate and sodium styrenesulfonate having a weight average molecular weight of 12,000 and a polymerization ratio of 70 mol% sodium acrylate and 30 mol% sodium styrenesulfonate, and a weight average molecular weight of 15.0.
00 and the polymerization ratio is 70 mol% of sodium acrylate, 2-
Copolymer of sodium acrylate and sodium acrylamido-2-methylpropanesulfonate, which is 30 mol% of sodium acrylamido-2-methylpropanesulfonate.
【００１９】（５）下記（ト）、（チ）および（リ）の
単量体より生成された共重合体またはその塩であり、重
量平均分子量が１，０００〜５００，０００であるも
の。 （ト）アクリル酸、メタクリル酸、マレイン酸、無水マ
レイン酸、フマール酸およびイタコン酸から選ばれた１
種または２種以上の不飽和カルボン酸、（チ）スチレン
スルホン酸、２−アクリルアミド−２−メチルプロパン
スルホン酸、３−アクリルオキシ−２−ヒドロキシ−プ
ロパンスルホン酸、ビニルスルホン酸、アリルスルホン
酸およびメタアリルスルホン酸から選ばれた１種または
２種以上の不飽和スルホン酸、（リ）アルキル基の炭素
数が１〜８のアクリル酸アルキルエステル、アルキル基
の炭素数が１〜８のメタクリル酸アルキルエステル、ア
ルキル基の炭素数が１〜８のアクリル酸ヒドロキシアル
キルエステル、炭素数が１〜８のメタクリル酸ヒドロキ
シアルキルエステル、アクリルアミド、スチレン、酢酸
ビニルおよびイソブチレンから選ばれた１種または２種
以上の単量体。(5) A copolymer or a salt thereof produced from the following monomers (G), (H) and (L), having a weight average molecular weight of 1,000 to 500,000. (G) 1 selected from acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid and itaconic acid
Or two or more kinds of unsaturated carboxylic acids, (h) styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, 3-acryloxy-2-hydroxy-propane sulfonic acid, vinyl sulfonic acid, allyl sulfonic acid and 1 or 2 or more types of unsaturated sulfonic acid selected from methallyl sulfonic acid, acrylic acid alkyl ester having (i) alkyl group having 1-8 carbon atoms, methacrylic acid having alkyl group having 1-8 carbon atoms One or more selected from alkyl ester, acrylic acid hydroxyalkyl ester having 1 to 8 carbon atoms of alkyl group, methacrylic acid hydroxyalkyl ester having 1 to 8 carbon atoms, acrylamide, styrene, vinyl acetate and isobutylene. Monomer.
【００２０】好ましいものとしては次のものが挙げられ
る。アクリル酸と２−アクリルアミド−２−メチルプロ
パンスルホン酸およびアクリルアミドよりなる共重合体
もしくはその塩であり、共重合体もしくはその塩の重量
平均分子量が、１，０００〜２００，０００の範囲であ
り、共重合体もしくはその塩の重合比が、アクリル酸も
しくはその塩３０〜９８モル％、２−アクリルアミド−
２−メチルプロパンスルホン酸もしくはその塩１〜２０
モル％、アクリルアミド１〜５０モル％の範囲であるも
の。The following are preferable examples. A copolymer of acrylic acid, 2-acrylamido-2-methylpropanesulfonic acid and acrylamide, or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is in the range of 1,000 to 200,000, The copolymerization ratio of the copolymer or its salt is 30 to 98 mol% of acrylic acid or its salt, 2-acrylamide-
2-Methylpropanesulfonic acid or its salt 1-20
Those in the range of 1 mol% to 50 mol% of acrylamide.
【００２１】更に好ましいものとしては、次のものが挙
げられる。アクリル酸と２−アクリルアミド−２−メチ
ルプロパンスルホン酸およびアクリルアミドよりなる共
重合体もしくはその塩であり、共重合体もしくはその塩
の重量平均分子量が、５，０００〜１００，０００の範
囲であり、共重合体もしくはその塩の重合比が、アクリ
ル酸もしくはその塩７０〜９８モル％、２−アクリルア
ミド−２−メチルプロパンスルホン酸もしくはその塩１
〜１０モル％、アクリルアミド１〜２０モル％の範囲で
あるもの。具体例としては次のものが挙げられる。重量
平均分子量が１５，０００であり重合比がアクリル酸ソ
ーダ７０モル％ 、２−アクリルアミド−２−メチルプ
ロパンスルホン酸ソーダ１０モル％、アクリルアミド２
０モル％であるアクリル酸ソーダと２−アクリルアミド
−２−メチルプロパンスルホン酸ソーダおよびアクリル
アミドの共重合体。More preferred are the following. A copolymer of acrylic acid, 2-acrylamido-2-methylpropanesulfonic acid and acrylamide or a salt thereof, wherein the weight average molecular weight of the copolymer or its salt is in the range of 5,000 to 100,000. The copolymer or the salt thereof has a polymerization ratio of acrylic acid or its salt of 70 to 98 mol%, 2-acrylamido-2-methylpropanesulfonic acid or its salt 1
A range of 10 to 10 mol% and 1 to 20 mol% of acrylamide. Specific examples include the following. The weight average molecular weight is 15,000 and the polymerization ratio is 70 mol% of sodium acrylate, 10 mol% of 2-acrylamido-2-methylpropanesulfonic acid soda, and 2% of acrylamide.
A copolymer of 0 mol% sodium acrylate, sodium 2-acrylamido-2-methylpropane sulfonate, and acrylamide.
【００２２】上記各重合体の塩としては、アンモニゥム
塩、アルカリ金属塩（ナトリゥム塩、カリゥム塩等）、
アルカリ土類金属塩（カルシゥム塩、マグネシゥム塩
等）が挙げられる。The salts of each of the above polymers include ammonium salts, alkali metal salts (such as sodium salts and potassium salts),
Examples thereof include alkaline earth metal salts (calcium salt, magnesium salt, etc.).
【００２３】重合体の製造方法は、通常行われている方
法を用いることが出来る。例えば、過硫酸ナトリウム等
の過酸化物またはアゾビスイソブチロール等のアゾ系化
合物の存在下で、水、アルコールまたはトルエン等の非
水系の溶媒中で窒素ガス気流下、常圧または加圧下で５
０〜１５０℃で１〜１０時間重合させた後、必要に応じ
てアルカリ例えば水酸化ナトリウムで中和することによ
って、各単量体の（共）重合物を得ることが出来る。重
合方法としては単量体の全量を重合槽に仕込んでもよ
く、また、単量体の全量または一部を滴下する方法を用
いても良い。また、予めアルカリ塩例えばナトリウム塩
の形にした単量体を重合しても良い。重合開始剤は全量
を重合槽に仕込んでも良く、連続的に投入していく方法
を用いても良い。As a method for producing the polymer, a commonly used method can be used. For example, in the presence of a peroxide such as sodium persulfate or an azo compound such as azobisisobutyrol, in a non-aqueous solvent such as water, alcohol or toluene under a nitrogen gas stream, under normal pressure or under pressure. 5
After being polymerized at 0 to 150 ° C. for 1 to 10 hours, if necessary, it may be neutralized with an alkali such as sodium hydroxide to obtain a (co) polymer of each monomer. As the polymerization method, the whole amount of the monomer may be charged into the polymerization tank, or a method of dropping the whole amount or a part of the monomer may be used. Alternatively, a monomer in the form of an alkali salt such as a sodium salt may be polymerized in advance. The polymerization initiator may be entirely charged in the polymerization tank, or may be continuously charged.
【００２４】本発明で用いられるセメントは、通常のセ
メント（普通ポルトランドセメント、早強セメント、超
早強セメント、高炉セメント、フライアッシュセメント
等）の他、ソイルセメントのようなセメント系固化剤も
使用することができる。粘性土に添加するセメントの量
は、固化処理土の使用目的によって種々決定されるが、
一般的には、粘性土１ｍ3に対し、５０〜２５０Ｋｇ、
好ましくは７５〜１５０Ｋｇ程度である。As the cement used in the present invention, in addition to ordinary cement (ordinary Portland cement, early-hardening cement, ultra-fast-hardening cement, blast furnace cement, fly ash cement, etc.), cement-based solidifying agents such as soil cement are also used. can do. The amount of cement added to cohesive soil is variously determined depending on the purpose of use of the solidified soil,
Generally, 50 to 250 kg for 1 m 3 of cohesive soil,
It is preferably about 75 to 150 kg.
【００２５】また、本発明の減水剤の添加量は、粘性土
の種類、その含水量、セメントの量等によって種々異な
るが、一般的には初期含水比１．０〜２．５ＷＬ％の粘
性土重量に対して０．０５〜２％、好ましくは０．５〜
１％程度である。ここにＷＬは粘性土の液性限界であ
る。本発明の減水剤を実際に用いる場合、一般的にはセ
メントを添加した粘性土に減水剤を添加して混練する
が、減水剤とセメントを同時に粘性土に添加して混練し
てもよいし、場合によっては減水剤を添加したあとセメ
ントを添加して混練してもよい。The amount of the water reducing agent of the present invention to be added varies depending on the type of cohesive soil, its water content, the amount of cement, etc., but generally the viscosity of the initial water content ratio is 1.0 to 2.5 WL%. 0.05 to 2% of soil weight, preferably 0.5 to
It is about 1%. Here, WL is the liquid limit of cohesive soil. When the water-reducing agent of the present invention is actually used, generally, the water-reducing agent is added to the clay to which the cement has been added and kneaded, but the water-reducing agent and the cement may be simultaneously added to the clay to be kneaded. Depending on the case, cement may be added and kneaded after adding the water reducing agent.
【００２６】また、セメントを添加した粘性土に減水剤
を添加して混練する場合、粘性土の初期含水比が１．０
ＷＬ％以下の粘性土を使用する場合のように含水量が少
ない場合には、粘性土の初期含水比が１．０〜２．５Ｗ
Ｌ％になるように水を加えて混練するのが好ましい。本
発明の減水剤をセメントを添加した粘性土に添加して使
用する場合、必要により他の添加剤、例えば、塩化カル
シゥム、トリエタノールアミン、チオシアン酸カルシウ
ム等の硬化促進剤等を使用してもよい。When the water-reducing agent is added to the clay-added clay to be kneaded, the initial water content of the clay is 1.0.
When the water content is low, such as when using a clay soil of WL% or less, the initial water content ratio of the clay soil is 1.0 to 2.5 W.
It is preferable to add water and knead so that L% may be obtained. When the water-reducing agent of the present invention is used by adding it to the cement-added cohesive soil, if necessary, other additives such as calcium chloride, triethanolamine, calcium thiocyanate, etc. may be used. Good.
【００２７】[0027]
【発明の効果】この発明のセメントを添加した粘性土用
減水剤は、これをセメントを添加した粘性土に添加した
場合に粘性土の分散性、減水性等が改善され流動性が著
しく改善される。したがって、要固化処理粘性土を処理
する場合に、施工性が改善され、さらに、水を多量に使
用することなく流動性を確保できるために、本発明の粘
性土用減水剤を使用しない場合と比較すると大きな体積
減少効果等がある。また、要固化処理粘性土を管路輸送
するに際して、好適であるばかりでなく、限定された処
分容積しかない場合にも多くの粘性土が処理できるので
好適であり、例えば埋立、軟弱地盤の固化処理等の施工
の際に大きなメリットがある。EFFECTS OF THE INVENTION The water-reducing agent for cohesive soil to which the cement of the present invention is added improves the dispersibility of the cohesive soil, the water-reducing property, etc. when added to the clay-containing cohesive soil, and the fluidity is remarkably improved. It Therefore, in the case of treating the solidification-requiring cohesive soil, the workability is improved, and since the fluidity can be secured without using a large amount of water, the case where the cohesive soil water reducing agent of the present invention is not used There is a large volume reduction effect and the like in comparison. In addition, it is suitable not only when transporting coagulation-requiring cohesive soil by pipeline, but also because it is possible to treat a large amount of cohesive soil when there is only a limited disposal volume. For example, landfill, solidification of soft ground. There is a great merit in construction such as treatment.
【００２８】次に本発明の実施の態様を図面に基づいて
説明する。第１図は本発明を実施するシステム全体を示
している。図中１はグラブ浚渫船であり、地山２の自然
含水比は液性限界程度である。浚渫された土砂を運搬す
る方法としては、土運船３により海上輸送し、バックホ
ウ４にて陸揚げされる。こうして運搬された土砂はま
ず、若干加水しながら、粗い振動スクリーン５によりふ
るわれ、解泥ユニット６でほぐされる。さらに、１．５
ＷＬ％に加水しながら、２ｍｍの振動スクリーン７を通
し、セメント混練および打設時に障害となる礫やゴミな
どの雑物を除去する。そして、モルタルミキサー８に
て、まずセメントを粘性土１ｍ3あたり１００Ｋｇ混合
し、混練攪拌後、本発明品である粘性土用減水剤を粘性
土１ｍ3あたり粘性土の重量の１％添加し、混練攪拌す
る。このようにして処理された浚渫土は、アジテータ９
に送られ、移送ポンプ１０によりスラリー輸送され、最
終処分地１１に打設される。Next, embodiments of the present invention will be described with reference to the drawings. FIG. 1 shows the overall system for implementing the present invention. In the figure, 1 is a grab dredger, and the natural water content of the ground 2 is about the liquid limit. As a method of transporting the dredged soil, it is transported by sea by a soil carrier 3 and unloaded by a backhoe 4. The earth and sand transported in this way are first sifted by a coarse vibrating screen 5 while being slightly watered, and then unraveled by a demolition unit 6. Furthermore, 1.5
While adding water to WL%, a 2 mm vibrating screen 7 is passed through to remove foreign matters such as gravel and dust, which are obstacles during cement kneading and placing. Then, in the mortar mixer 8, 100 kg of cement was first mixed per 1 m 3 of cohesive soil, and after kneading and stirring, the water reducing agent for cohesive soil of the present invention was added at 1% of the weight of cohesive soil per 1 m 3 of cohesive soil, Knead and stir. The dredged soil treated in this way is agitator 9
The slurry is transported by the transfer pump 10 to the final disposal site 11.
【００２９】なお上述の実施の態様の例では、２段階に
加水処理しているが、場合によっては必ずしも必要では
ない。以下、試験例により本発明をさらに説明する。In the example of the above-mentioned embodiment, the water treatment is carried out in two steps, but it is not always necessary in some cases. Hereinafter, the present invention will be further described with reference to test examples.
【００３０】試験例 試験は、含水比を１１８，１４０，１６０％に海水で調
整した粘性土を使用し、粘性土１ｍ3に対し普通ポルト
ランドセメント１００ｋｇを添加した配合に本発明の粘
性土用減水剤および比較例の水溶性分散剤を添加し、流
動性の改善効果を比較検討した。水溶性化合物は含水比
を調整する海水の中に事前に添加した。化合物の添加量
は粘性土に対する固形分の量を重量百分率で示した。Test Example In the test, cohesive soil adjusted to a water content of 118, 140, 160% with seawater was used, and 100 ml of ordinary Portland cement was added to 1 m 3 of cohesive soil to reduce the water content for the cohesive soil of the present invention. The agent and the water-soluble dispersant of Comparative Example were added, and the effect of improving the fluidity was comparatively examined. The water-soluble compound was added in advance to seawater whose water content ratio was adjusted. The amount of the compound added was indicated by the weight percentage of the solid content relative to the clay.
【００３１】粘性土へのセメントの混練攪拌はホバート
型モルタルミキサを使用し、粘性土と含水比調整水（水
溶性分散剤を含む）を低速で１分混練し、次いでセメン
トを添加後、低速で１分混練し、ミキサについている付
着物をかき落とした後さらに高速で２分混練した。流動
性の評価は混練物のフロー（広がり）で行った。フロー
はガラス板の上に置いた内径８ｃｍ×高さ８ｃｍのアク
リル性円筒容器に試料を詰め、鉛直に引上げたときの混
練物の直径方向の広がりを測定することによって求め
た。圧縮強度はφ５×１０ｃｍの型枠で成形し、材齢２
８日まで２０℃で封緘養生を行い、ＪＩＳＡ １１０８
に従って測定した。実験に使用した材料を以下に示す。A Hobart type mortar mixer is used for kneading and agitating the cement with the cohesive soil. The cohesive soil and the water content adjusting water (including the water-soluble dispersant) are kneaded at a low speed for 1 minute, and then the cement is added at a low speed. The mixture was kneaded for 1 minute, scraped off the deposits on the mixer, and further kneaded for 2 minutes at a higher speed. The flowability was evaluated by the flow (spreading) of the kneaded product. The flow was determined by packing a sample in an acrylic cylindrical container having an inner diameter of 8 cm and a height of 8 cm placed on a glass plate and measuring the spread of the kneaded product in the diametrical direction when the sample was pulled up vertically. The compressive strength is φ5 × 10cm, and the material is 2 years old.
Sealed and cured at 20 ° C for up to 8 days according to JISA 1108
Was measured according to. The materials used in the experiment are shown below.
【００３２】粘性土：粘性土の土質特性は表１に示す。Cohesive soil: The soil characteristics of cohesive soil are shown in Table 1.
【表１】粘性土の土質特性 セメント： 普通ポルトランドセメント（日本セメント
株式会社製） 海水：人工海水（商品名 マリンアート 千住製薬株式
会社製）[Table 1] Soil characteristics of cohesive soil Cement: Ordinary Portland Cement (manufactured by Nippon Cement Co., Ltd.) Seawater: Artificial seawater (Brand name Marine Art Senju Pharmaceutical Co., Ltd.)
【００３３】[0033]
化合物Ｎｏ．１ ポリアクリル酸ソーダ（重量平均分子
量１０，０００） 化合物Ｎｏ．２ ポリアクリル酸ソーダ（重量平均分子
量１００，０００） 化合物Ｎｏ．３ ポリアクリル酸ソーダ（重量平均分子
量３００，０００） 化合物Ｎｏ．４ ポリアクリル酸アンモニゥム（重量平
均分子量１０，０００） 化合物Ｎｏ．５ アクリル酸ソーダ７０モル％とメタク
リル酸３０モル％との反応で得られた重量平均分子量が
１０，０００の共重合体 化合物Ｎｏ．６ アクリル酸ソーダ９０モル％とアクリ
ルアミド１０モル％との反応 で得られた重量平均分子
量が１０，０００の共重合体 化合物Ｎｏ．７ アクリル酸ソーダ９５モル％とマレイ
ン酸ソーダ５モル％との反応 で得られた重量平均分子
量が１０，０００の共重合体 化合物Ｎｏ．８ アクリル酸ソーダ７０モル％とスチレ
ンスルホン酸ソーダ３０モル％との反応で得られた重量
平均分子量が１２，０００の共重合体 化合物Ｎｏ．９ アクリル酸ソーダ７０モル％とアクリ
ルアミドプロパンスルホン酸ソーダ３０モル％との反応
で得られた重量平均分子量が１５，０００の共重合体 化合物Ｎｏ１０ アクリル酸ソーダ７０モル％とアクリ
ルアミドプロパンスルホン酸ソーダ１０モル％とアクリ
ルアミド２０モル％との反応で得られた重量平均分子量
が１５，０００の共重合体 化合物Ｎｏ．１１ リグニンスルホン酸カルシゥム（商
品名：サンエキスＳＣＰ日本製紙株式会社製） 化合物Ｎｏ．１２ メラミンスルホン酸ホルマリン縮合
物（商品名：メルメント昭和電工株式会社製） 化合物Ｎｏ．１３ ナフタレンスルホン酸ソーダのホル
マリン縮合物（商品名：マイティ１５０ 花王株式会社
製）Compound No. 1 Sodium polyacrylate (weight average molecular weight 10,000) Compound No. 2 Sodium polyacrylate (weight average molecular weight 100,000) Compound No. 3 Sodium polyacrylate (weight average molecular weight 300,000) Compound No. 4 Ammonium polyacrylate (weight average molecular weight 10,000) Compound No. 5 Copolymer having a weight average molecular weight of 10,000 obtained by the reaction of 70 mol% sodium acrylate and 30 mol% methacrylic acid Compound No. 6 Copolymer having a weight average molecular weight of 10,000 obtained by the reaction of 90 mol% sodium acrylate and 10 mol% acrylamide Compound No. 7 Copolymer having a weight average molecular weight of 10,000 obtained by the reaction of 95 mol% sodium acrylate and 5 mol% sodium maleate Compound No. 8 Copolymer having a weight average molecular weight of 12,000, obtained by the reaction of 70 mol% sodium acrylate and 30 mol% sodium styrenesulfonate Compound No. 9 Copolymer having a weight average molecular weight of 15,000 obtained by the reaction of 70 mol% of sodium acrylate and 30 mol% of sodium acrylamide propane sulfonate Compound No10 70 mol% of sodium acrylate and 10 mol of sodium acrylamide propane sulfonate % And acrylamide 20 mol%, the copolymer having a weight average molecular weight of 15,000 Compound No. 11 Calcium lignin sulfonate (trade name: Sun Extract SCP Nippon Paper Industries Co., Ltd.) Compound No. 12 Melamine sulfonic acid formalin condensate (trade name: manufactured by Melment Showa Denko KK) Compound No. 13 Formalin condensate of sodium naphthalene sulfonate (Product name: Mighty 150 manufactured by Kao Corporation)
【００３４】[0034]
【表２】試験結果 分子量の測定はゲルパーミュエーション（ＧＰＣ）法に
より行った。 測定条件 カラム種類：ＴＳＫｇｅｌ Ｇ５０００ＰＷ
XL． ＴＳＫｇｅｌ Ｇ３０００ＰＷXL．（東ソー株式会社） カラム温度：４０℃ 移動相：リン酸バッファー水溶
液 流量：０．８ｍｌ／分 標準品：ポリエチレングリコー
ル[Table 2] Test results The molecular weight was measured by the gel permeation (GPC) method. Measurement conditions Column type: TSKgel G5000PW
XL . TSKgel G3000PW XL . (Tosoh Corporation) Column temperature: 40 ° C. Mobile phase: Phosphate buffer aqueous solution Flow rate: 0.8 ml / min Standard product: Polyethylene glycol
【００３５】上記の試験結果から、粘性土用減水剤であ
る本発明品をセメントを添加した粘性土に添加した場
合、無添加に比べて流動性が大幅に増大する。比較例に
示している３種の水溶性分散剤はいずれもコンクリート
などのセメントを分散させる効果が高いものとして広く
知られているものであるが、本結果からは粘性土、セメ
ントの混合系では流動性の改善効果はほとんど認められ
ない。これらの結果と比べても、本発明品は高い効果を
示している。陸上において、粘性土とセメント混練物を
施工する場合、セルフレベリングが確保できると言われ
ているのはフロー値約１６０ｍｍ以上である。フロー試
験の結果から添加量０．４３％では、フロー値が１６０
ｍｍ以上となるのは化合物Ｎｏ．１， Ｎｏ．２， Ｎ
ｏ．５， Ｎｏ．９， Ｎｏ．１０であるが、添加量を
増すことによって化合物Ｎｏ．３， Ｎｏ．４， Ｎ
ｏ．６， Ｎｏ．７， Ｎｏ．８，もフロー値が１６０
ｍｍ以上となる。圧縮強度は添加量が０．４３％では実
用上十分な強度を発現している。フロー値を１６０ｍｍ
以上とする場合、本発名品はフロー値が同程度の無添加
（含水比１６０％、フロー１６０ｍｍ）と比べて、同程
度以上の強度が得られる。From the above test results, when the product of the present invention, which is a water-reducing agent for cohesive soil, is added to cohesive soil to which cement is added, the fluidity is significantly increased as compared with the case where no addition is made. All of the three types of water-soluble dispersants shown in Comparative Examples are widely known to have a high effect of dispersing cement such as concrete, but from the results, it can be seen in the mixed system of cohesive soil and cement. Almost no improvement in fluidity is observed. Even when compared with these results, the product of the present invention shows a high effect. It is said that the self-leveling can be ensured when the clay and the cement kneaded material are applied on land, when the flow value is about 160 mm or more. From the results of the flow test, when the added amount is 0.43%, the flow value is
Compound No. is not less than mm. 1, No. 2, N
o. 5, No. 9, No. No. 10, but the compound No. was increased by increasing the addition amount. 3, No. 4, N
o. 6, No. 7, No. 8, the flow value is 160
mm or more. With respect to the compressive strength, when the addition amount is 0.43%, a practically sufficient strength is exhibited. Flow value is 160mm
In the case of the above, the product of the present invention has the same or higher strength as compared with the additive-free product having the same flow value (water content ratio 160%, flow 160 mm).
【００３６】フロー試験の結果から、フロー値が１６０
ｍｍ以上になる場合について、自然堆積状態と処理後の
堆積の比較を表２に示した。ここでの自然堆積状態の体
積は粘性土の液性限界ＷＬの含水比状態（本実験に用い
た粘性土の場合６５．６％である）を想定している。こ
の結果から、フロー値を１６０ｍｍ以上にするために
は、分散剤を添加しない場合は粘性土の含水比を１６０
％（２．４ＷＬ）以上にする必要があり、粘性土の体積
比は自然堆積状態の１．９以上となる。一方、本発明品
を０．８６％添加した場合は粘性土の含水比は１１８％
（１．８ＷＬ）以下でよく、体積比は１．５以下とな
り、無添加に比べて大きな体積減少効果がある。From the result of the flow test, the flow value is 160
Table 2 shows a comparison between the natural deposition state and the post-treatment deposition for the case where the thickness is greater than or equal to mm. The volume of the natural deposition state here is assumed to be the water content ratio state of the liquidity limit WL of the cohesive soil (65.6% in the case of the cohesive soil used in this experiment). From this result, in order to make the flow value 160 mm or more, when the dispersant is not added, the water content ratio of the cohesive soil should be 160
% (2.4 WL) or more, and the volume ratio of the cohesive soil becomes 1.9 or more in the natural deposition state. On the other hand, when 0.86% of the product of the present invention is added, the water content of the clay is 118%.
(1.8 WL) or less, and the volume ratio is 1.5 or less, which has a large volume reduction effect as compared with no addition.
【００３７】[0037]
【図１】本発明品を使用する場合の施工システム全体の
一例図である。FIG. 1 is a diagram showing an example of the entire construction system when the product of the present invention is used.
１． グラブ浚渫船 ２． 浚渫される地山 ３． 土運船 ４． バックホウ ５． 粗い振動スクリーン ６． 解砕ユニット ７． ２ｍｍの振動スクリーン ８． モルタルミキサー ９． アジテータ １０． 移送ポンプ １１． 最終処分地 1. Grab dredger 2. Ground that is dredged 3. Earth transport 4. Backhoe 5. Coarse vibrating screen 6. Crushing unit 7. 2mm vibrating screen 8. Mortar mixer 9. Agitator 10. Transfer pump 11. Final disposal site
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０４Ｂ 103:30 Ｃ０９Ｋ 103:00 (72)発明者 新舎 博 栃木県那須郡西那須野町四区町1534−１ 五洋建設株式会社技術研究所内 (72)発明者 井上 茂 栃木県那須郡西那須野町四区町1534−１ 五洋建設株式会社技術研究所内─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Reference number within the agency FI Technical display location C04B 103: 30 C09K 103: 00 (72) Inventor Hiroshi Hiroshi 4 wards, Nishinasuno-cho, Nasu-gun, Tochigi Prefecture Town, 534-1 Goyo Construction Co., Ltd. Technical Research Institute (72) Inoue Shigeru Inoue, Shichiku, Nishinasuno-cho, Nasu-gun, Tochigi Prefecture 1534-1 Goyo Construction Co., Ltd. Technical Research Center
Claims (10)
およびクロトン酸から選ばれた１種または２種以上の単
量体より生成された単一重合体、共重合体、またはそれ
らの塩であり、重量平均分子量が１，０００〜５００，
０００であるものを含有することを特徴とするセメント
添加粘性土用減水剤。1. A homopolymer, a copolymer, or a salt thereof formed from one or more monomers selected from acrylic acid, methacrylic acid, vinyl acetic acid and crotonic acid, and a weight thereof. Average molecular weight of 1,000 to 500,
A water-reducing agent for cement-containing cohesive soil, characterized in that it contains 000.
成された共重合体またはその塩であり、重量平均分子量
が１，０００〜５００，０００であるものを含有するこ
とを特徴とするセメント添加粘性土用減水剤。 （イ）アクリル酸および／またはメタクリル酸、（ロ）
アルキル基の炭素数が１〜８のアクリル酸アルキルエス
テル、アルキル基の炭素数が１〜８のメタクリル酸アル
キルエステル、アルキル基の炭素数が１〜８のアクリル
酸ヒドロキシアルキルエステル、アルキル基の炭素数が
１〜８のメタクリル酸ヒドロキシアルキルエステル、ア
クリルアミド、スチレン、イソブチレンおよび酢酸ビニ
ルから選ばれた１種または２種以上の単量体。2. A copolymer or a salt thereof produced from the following monomers (a) and (b), which has a weight average molecular weight of 1,000 to 500,000. Water reducing agent for cement-containing cohesive soil. (A) acrylic acid and / or methacrylic acid, (b)
Acrylic acid alkyl ester whose alkyl group has 1 to 8 carbon atoms, methacrylic acid alkyl ester whose alkyl group has 1 to 8 carbon atoms, acrylic acid hydroxyalkyl ester whose alkyl group has 1 to 8 carbon atoms, and alkyl group carbon One or more monomers selected from methacrylic acid hydroxyalkyl esters having a number of 1 to 8, acrylamide, styrene, isobutylene, and vinyl acetate.
成された共重合体またはその塩であり、重量平均分子量
が１，０００〜５００，０００であるものを含有するこ
とを特徴とするセメント添加粘性土用減水剤。 （ハ）アクリル酸および／またはメタクリル酸、（ニ）
マレイン酸、無水マレイン酸、フマール酸およびイタコ
ン酸から選ばれた１種または２種以上の不飽和ジカルボ
ン酸。3. A copolymer or a salt thereof produced from the following monomers (c) and (d), which has a weight average molecular weight of 1,000 to 500,000: Water reducing agent for cement-containing cohesive soil. (C) Acrylic acid and / or methacrylic acid, (D)
One or more unsaturated dicarboxylic acids selected from maleic acid, maleic anhydride, fumaric acid and itaconic acid.
成された共重合体またはその塩であり、重量平均分子量
が１，０００〜３００，０００であるものを含有するこ
とを特徴とするセメント添加粘性土用減水剤。 （ホ）アクリル酸、メタクリル酸、マレイン酸、無水マ
レイン酸、フマール酸およびイタコン酸から選ばれた１
種または２種以上の不飽和カルボン酸、（ヘ）スチレン
スルホン酸、２−アクリルアミド−２−メチルプロパン
スルホン酸、３−アクリルオキシ−２−ヒドロキシ−プ
ロパンスルホン酸、ビニルスルホン酸、アリルスルホン
酸およびメタアリルスルホン酸から選ばれた１種または
２種以上の不飽和スルホン酸。4. A copolymer or a salt thereof produced from the following monomers (e) and (e), which has a weight average molecular weight of 1,000 to 300,000. Water reducing agent for cement-containing cohesive soil. (E) 1 selected from acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid and itaconic acid
Or two or more unsaturated carboxylic acids, (f) styrenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 3-acryloxy-2-hydroxy-propanesulfonic acid, vinylsulfonic acid, allylsulfonic acid and One or more unsaturated sulfonic acids selected from methallyl sulfonic acids.
体より生成された共重合体またはその塩であり、重量平
均分子量が１，０００〜５００，０００であるものを含
有することを特徴とするセメント添加粘性土用減水剤。 （ト）アクリル酸、メタクリル酸、マレイン酸、無水マ
レイン酸、フマール酸およびイタコン酸から選ばれた１
種または２種以上の不飽和カルボン酸、（チ）スチレン
スルホン酸、２−アクリルアミド−２−メチルプロパン
スルホン酸、３−アクリルオキシ−２−ヒドロキシ−プ
ロパンスルホン酸、ビニルスルホン酸、アリルスルホン
酸およびメタアリルスルホン酸から選ばれた１種または
２種以上の不飽和スルホン酸、（リ）アルキル基の炭素
数が１〜８のアクリル酸アルキルエステル、アルキル基
の炭素数が１〜８のメタクリル酸アルキルエステル、ア
ルキル基の炭素数が１〜８のアクリル酸ヒドロキシアル
キルエステル、炭素数が１〜８のメタクリル酸ヒドロキ
シアルキルエステル、アクリルアミド、スチレン、酢酸
ビニルおよびイソブチレンから選ばれた１種または２種
以上の単量体。5. A copolymer or a salt thereof formed from the following monomers (G), (H) and (L), which has a weight average molecular weight of 1,000 to 500,000: A water-reducing agent for cement-containing cohesive soil, characterized by being (G) 1 selected from acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid and itaconic acid
Or two or more kinds of unsaturated carboxylic acids, (h) styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, 3-acryloxy-2-hydroxy-propane sulfonic acid, vinyl sulfonic acid, allyl sulfonic acid and 1 or 2 or more types of unsaturated sulfonic acid selected from methallyl sulfonic acid, acrylic acid alkyl ester having (i) alkyl group having 1-8 carbon atoms, methacrylic acid having alkyl group having 1-8 carbon atoms One or more selected from alkyl ester, acrylic acid hydroxyalkyl ester having 1 to 8 carbon atoms of alkyl group, methacrylic acid hydroxyalkyl ester having 1 to 8 carbon atoms, acrylamide, styrene, vinyl acetate and isobutylene. Monomer.
金属塩およびアルカリ土類金属塩より選ばれた少なくと
も１種の塩である請求項１，２，３，４または５記載の
減水剤。6. The water reducing agent according to claim 1, wherein the polymer salt is at least one salt selected from ammonium salts, alkali metal salts and alkaline earth metal salts.
３，４または５記載の減水剤を添加することを特徴とす
るセメント添加粘性土の流動化方法。7. Cement in cohesive soil and claims 1, 2,
A method for fluidizing cement-added cohesive soil, which comprises adding the water reducing agent according to 3, 4, or 5.
３，４または５記載の減水剤を添加し、これに水を加え
るかまたは加えずして混練し、スラリ−状にして管路輸
送することを特徴とするセメント添加粘性土の輸送方
法。8. Cement and cohesive clay, claim 1,
A method for transporting cement-added cohesive soil, which comprises adding the water reducing agent according to 3, 4, or 5 and kneading with or without adding water to form a slurry and pipe-conveying.
項７記載の流動化方法。9. The fluidizing method according to claim 7, wherein the water reducing agent is that according to claim 1.
求項８記載の輸送方法。10. The transportation method according to claim 8, wherein the water reducing agent is that according to claim 1.