JPH07223206A - Decorative veneer and manufacture thereof - Google Patents
Decorative veneer and manufacture thereofInfo
- Publication number
- JPH07223206A JPH07223206A JP3641194A JP3641194A JPH07223206A JP H07223206 A JPH07223206 A JP H07223206A JP 3641194 A JP3641194 A JP 3641194A JP 3641194 A JP3641194 A JP 3641194A JP H07223206 A JPH07223206 A JP H07223206A
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- decorative veneer
- synthetic resin
- resin sheet
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は家屋における建材や家具
用板として用いられる化粧単板およびその製造方法に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative veneer used as a building material or a plate for furniture in a house and a method for manufacturing the veneer.
【０００２】[0002]
【従来の技術】従来より各種の化粧単板が提供されてい
る。また、裏面に和紙、不織布等の裏打ち材を貼着する
ことにより強度および取り扱い性を向上させたものや、
表面にシーラー塗装を施し、更に表面サンディングを施
して耐研磨性を向上させたものも提供されている。2. Description of the Related Art Conventionally, various types of decorative veneer have been provided. In addition, a backing material such as Japanese paper or non-woven fabric is attached to the back surface to improve strength and handleability,
There is also provided a sealer coating on the surface and further sanding the surface to improve the abrasion resistance.
【０００３】このような化粧単板は、接着剤を介して基
板の表面に貼着した後、必要に応じて化粧単板面に着色
塗料を塗布して着色塗装を施し、更に上塗り塗料を塗布
して上塗り塗装を施して表面保護層を形成し、化粧板と
することが広く行われている。Such a decorative veneer is adhered to the surface of the substrate via an adhesive, and if necessary, a colored paint is applied to the surface of the decorative veneer to give a colored coating, and then a top coat is applied. It is widely practiced to apply a top coat to form a surface protective layer and make a decorative plate.
【０００４】[0004]
【発明が解決しようとする課題】上記従来技術におい
て、化粧単板の表面に形成される表面保護層に十分な機
能を与えるためには上塗り塗料を何度も塗り重ねて厚塗
りする必要があり、作業工程が煩雑化する。In the above-mentioned prior art, in order to give a sufficient function to the surface protective layer formed on the surface of the decorative veneer, it is necessary to repeatedly coat the top coating material several times for thick coating. , The work process becomes complicated.
【０００５】また、粘度の高い塗料を用いて厚塗りを行
おうとする場合、塗装速度または乾燥速度が速いと、均
一塗装ができず、また乾燥時に発泡が生ずるため、実際
には塗装速度および乾燥速度をいずれも遅くしてこれら
の問題を回避しているが、反面、生産性の低下が不可避
となる。Further, in the case of attempting a thick coating using a paint having a high viscosity, if the coating speed or the drying speed is high, uniform coating cannot be performed and foaming occurs during the drying, so that the coating speed and the drying speed are actually reduced. Although all of these problems are avoided by slowing down the speed, a decrease in productivity is inevitable.
【０００６】また、上記のような事情から、上塗り塗料
の厚塗りを断念し、比較的薄い表面保護層を形成するこ
とも行われているが、この場合には表面保護層の強度が
弱くなるため、傷がつきやすく、耐摩耗性に乏しいもの
となり、また深みのある化粧表面を得ることができない
等の問題を有する。Under the circumstances as described above, it has been attempted to give up the thick coating of the top coat and form a relatively thin surface protective layer, but in this case, the strength of the surface protective layer becomes weak. Therefore, there are problems that the surface is easily scratched, the abrasion resistance is poor, and a deep makeup surface cannot be obtained.
【０００７】化粧単板に予め最終の上塗り塗料まで塗布
して仕上げ層ないし表面保護層を形成させる試みもなさ
れているが、上塗り塗料の塗布による化粧単板自体の膨
張、乾燥による収縮に伴って、化粧単板の繊維方向と直
角方向の反りやねじれが発生し、基板表面への貼着が困
難となるため、実用に供することはできないものであっ
た。[0007] Attempts have also been made to apply a final topcoat paint to a decorative veneer in advance to form a finishing layer or a surface protective layer. However, with the application of the topcoat paint, the veneer itself expands and shrinks due to drying. However, warping and twisting in the direction perpendicular to the fiber direction of the decorative veneer occur, making it difficult to attach the decorative veneer to the surface of the substrate, so that it cannot be put to practical use.
【０００８】[0008]
【課題を解決するための手段】本発明は上記従来技術の
問題点を解消することを目的とし、より具体的には、十
分な機能を有する表面保護層を予め有する高品質の化粧
単板を比較的簡単な作業工程により安定的に供給し、生
産性も向上させることを目的とする。SUMMARY OF THE INVENTION The present invention aims to solve the above-mentioned problems of the prior art. More specifically, a high-quality decorative veneer having a surface protective layer having a sufficient function in advance is provided. The purpose is to provide a stable supply through a relatively simple work process and improve productivity.
【０００９】かかる目的を達成するために鋭意工夫の末
に創案された本発明による化粧単板は、表面に、透明あ
るいは硬化すると透明となる接着剤を介して透明合成樹
脂シートが接着されてなる表面保護層が形成されること
を特徴とする。The decorative veneer according to the present invention, which has been devised after earnest efforts to achieve the above object, has a transparent synthetic resin sheet adhered to the surface thereof via an adhesive which becomes transparent or becomes transparent when cured. The surface protective layer is formed.
【００１０】また、本発明による化粧単板の製造方法
は、表面に、透明あるいは硬化すると透明となる接着剤
を介して透明合成樹脂シートを載置して圧締接着するこ
とにより該透明合成樹脂シートよりなる表面保護層を形
成することを特徴とする。Further, in the method for producing a decorative veneer according to the present invention, the transparent synthetic resin sheet is placed on the surface of the transparent synthetic resin sheet via an adhesive which is transparent or becomes transparent when cured, and the transparent synthetic resin sheet is pressure-bonded. It is characterized in that a surface protective layer made of a sheet is formed.
【００１１】化粧単板としては、スライサー、ロータリ
ーレース、ハーフランドロータリーレース、丸鋸、帯鋸
等の切断切削装置により得られるスライス単板、ロータ
リー単板、ハーフランド単板、ソード単板等が用いられ
る。化粧単板の厚さは一般に０．１５〜５ｍｍの範囲で
用いられる。As the decorative veneer, slice veneers, rotary veneers, half land veneers, sword veneers, etc. obtained by a cutting and cutting device such as a slicer, a rotary race, a half land rotary race, a circular saw and a band saw are used. To be The decorative veneer generally has a thickness of 0.15 to 5 mm.
【００１２】化粧単板の裏面に、和紙、洋紙、合成紙、
不織布、織布、寒冷紗、含浸紙、合成樹脂シート等の裏
打ち材を貼着して用いてもよい。裏打ち材を貼着するこ
とにより、化粧単板自体の補強、化粧単板の干割れ防
止、接着剤の化粧単板表面への染み出し防止等の作用が
なされ、不良品の発生が防止されると共に、取り扱いが
容易となることにより割れを防止し、生産性を向上する
ことができる。裏打ち材は、化粧単板毎葉に貼着して
も、複数の化粧単板に亙って連続して貼着してもよい。On the back surface of the decorative veneer, Japanese paper, Western paper, synthetic paper,
A backing material such as a non-woven fabric, a woven fabric, a gauze cloth, an impregnated paper, a synthetic resin sheet or the like may be stuck and used. By sticking the backing material, the decorative veneer itself can be reinforced, the decorative veneer can be prevented from cracking, and the adhesive can be prevented from seeping out to the surface of the decorative veneer. At the same time, the ease of handling can prevent cracks and improve productivity. The backing material may be applied to each leaf of the decorative veneer or may be continuously applied to a plurality of decorative veneers.
【００１３】化粧単板の表面に、透明あるいは硬化する
と透明となる接着剤をスプレー、スプレッダー、フロー
コーター、カーテンコーター、バーコーター等の塗布装
置を用いて塗布した後、透明合成樹脂シートを載置す
る。透明合成樹脂シートは、化粧単板毎葉ごとにあるい
は複数の化粧単板に亙って連続して、化粧単板の表面に
載置される。A transparent synthetic resin sheet is placed on the surface of the decorative veneer after applying an adhesive that is transparent or becomes transparent when cured with a coating device such as a sprayer, spreader, flow coater, curtain coater or bar coater. To do. The transparent synthetic resin sheet is placed on the surface of the decorative veneer for each decorative veneer or continuously over a plurality of decorative veneers.
【００１４】このときに用いられる透明あるいは硬化す
ると透明となる接着剤は、酢酸ビニル樹脂系、ユリア樹
脂系、メラミン樹脂系、フェノール樹脂系、アクリル樹
脂系、ウレタン樹脂系、イソシアネート系等の接着剤で
あり、単独であるいは任意混合した混合型接着剤として
用いられる。この接着剤には必要に応じて着色剤を添加
して、着色接着剤として用いることができる。また、必
要に応じてタルク、炭カル、クレー、チタン白等の無機
質粉末、小麦粉、木粉、プラスチック粉、防虫剤、防カ
ビ剤等を添加混合して用いることができる。この接着剤
は、それ自体が透明あるいは少なくとも硬化すると透明
となるものであるため、得られた化粧板においては化粧
単板表面が隠蔽されることなく化粧板表面に現出され
る。The transparent or transparent adhesive used at this time is a vinyl acetate resin-based, urea resin-based, melamine resin-based, phenol resin-based, acrylic resin-based, urethane resin-based, isocyanate-based adhesive, etc. It is used alone or as a mixed adhesive which is arbitrarily mixed. A colorant may be added to this adhesive as needed to use it as a colored adhesive. Further, if necessary, inorganic powders such as talc, calcium carbonate, clay and titanium white, wheat flour, wood powder, plastic powder, insect repellents, fungicides and the like can be added and mixed. The adhesive itself is transparent, or at least becomes transparent when cured, and therefore, in the obtained decorative board, the surface of the decorative veneer is not concealed and appears on the surface of the decorative board.
【００１５】透明合成樹脂シートとしては、ポリエチレ
ンシート、セロファン、アセテートシート、ポリ塩化ビ
ニルシート、ポリプロピレンシート、ポリスチレンシー
ト、ポリエステルシート、ナイロンシート、サランシー
ト等が好適に用いられる。一般に透明合成樹脂シートは
０．００５〜１ｍｍの厚さを有するものとして用いられ
る。As the transparent synthetic resin sheet, polyethylene sheet, cellophane, acetate sheet, polyvinyl chloride sheet, polypropylene sheet, polystyrene sheet, polyester sheet, nylon sheet, saran sheet and the like are preferably used. Generally, a transparent synthetic resin sheet is used as having a thickness of 0.005 to 1 mm.
【００１６】透明合成樹脂シートとして、任意着色され
た着色透明合成樹脂シートを用いることにより、木質感
を強調し、新たな樹種を表現し、あるいは深みを表現す
ることができ、化粧板としての意匠性を更に向上させる
ことができる。また、同様に意匠性の向上を目的とし
て、裏面に任意柄模様が印刷された無色または着色した
透明合成樹脂シートを用いてもよい。By using a colored transparent synthetic resin sheet that is arbitrarily colored as the transparent synthetic resin sheet, the wood texture can be emphasized, new tree species can be expressed, or depth can be expressed. The property can be further improved. Further, similarly, for the purpose of improving the design, a colorless or colored transparent synthetic resin sheet having an arbitrary pattern printed on the back surface may be used.
【００１７】表面に透明あるいは硬化すると透明となる
接着剤を介して透明合成樹脂シートが載置された化粧単
板を、コールドプレス、ホットプレス、ロールプレス、
ラミネーター、ラッピング、縁貼り機、真空プレス等の
圧締装置を用いて圧締することにより、透明合成樹脂シ
ートが化粧単板の表面に接着されて、表面保護層が形成
される。A decorative veneer on which a transparent synthetic resin sheet is placed via an adhesive that becomes transparent or becomes transparent when cured is cold pressed, hot pressed, roll pressed,
The transparent synthetic resin sheet is adhered to the surface of the decorative veneer by pressing with a pressing device such as a laminator, wrapping, an edge pasting machine, or a vacuum press to form a surface protective layer.
【００１８】以上のようにして本発明の化粧単板が得ら
れる。The decorative veneer of the present invention is obtained as described above.
【００１９】本発明の化粧単板は、接着剤を介して基板
の表面に載置し、圧締接着することにより、化粧板とす
ることができる。化粧単板は基板毎葉ごとに、あるいは
複数の基板に亙って連続して貼着される。The decorative veneer of the present invention can be made into a decorative plate by placing it on the surface of the substrate via an adhesive and press-bonding. The decorative veneer is pasted on each substrate or continuously over a plurality of substrates.
【００２０】基板には、合板、木質板、木質繊維板、木
削片板、集成材、単板積層板等が、単独であるいは任意
積層してなる積層板として用いられる。また、該基板を
任意切断し、表面や木口部にルーター、カッター等の切
削加工機を用いて溝加工、面取加工等の任意加飾を施し
た幅木、廻り縁、モール、ドア、窓等に用いられる面
材、造作材等の基材として用いることもできる。As the substrate, plywood, wood board, wood fiber board, wood shaving board, laminated wood, single board laminated board, etc. are used alone or as a laminated board which is arbitrarily laminated. In addition, the board is cut arbitrarily, and a skirting board, a rim, a molding, a door, a window on which the surface and the mouth end are optionally decorated by grooving or chamfering using a cutting machine such as a router or a cutter. It can also be used as a base material for face materials, sculpture materials, etc.
【００２１】接着剤は、基板の表面に、および／または
化粧単板の裏面に、スプレー、スプレッダー、バーコー
ター等の塗布装置を用いて塗布される。この接着剤に
は、酢酸ビニル樹脂系、ユリア樹脂系、メラミン樹脂
系、フェノール樹脂系、イソシアネート系等の接着剤
を、単独であるいは任意混合した混合型接着剤として用
いられる。接着剤には、必要に応じてタルク、炭カル、
クレー、チタン白等の無機質粉末、小麦粉、木粉、プラ
スチック粉、着色剤、防虫剤、防カビ剤等を添加混合し
て用いることができる。一般に、接着剤は固形分を３５
〜８０％とし、塗布量５０〜３００ｇ／ｍ２の範囲で塗
布される。The adhesive is applied to the front surface of the substrate and / or the back surface of the decorative veneer by using a coating device such as a sprayer, a spreader or a bar coater. As this adhesive, a vinyl acetate resin-based, urea resin-based, melamine resin-based, phenol resin-based, isocyanate-based, etc. adhesive is used alone or as a mixed adhesive. For the adhesive, talc, calcium char,
Clay, inorganic powder such as titanium white, wheat flour, wood flour, plastic powder, colorant, insect repellent, fungicide and the like can be added and mixed. Generally, the adhesive has a solid content of 35
˜80%, and the application amount is 50 to 300 g / m 2 .
【００２２】このようにして接着剤を介して毎葉ごとに
あるいは連続して化粧単板が載置された基板を、コール
ドプレス、ホットプレス、ロールプレス、ラミネータ
ー、ラッピング、縁貼り機，真空プレス等の貼着装置を
用いて圧締して、化粧単板を基板表面に接着することに
より、上記化粧板を得ることができる。In this way, the substrate on which the decorative veneer is placed on each leaf or continuously through the adhesive is cold pressed, hot pressed, roll pressed, laminator, wrapping, edge pasting machine, vacuum press. The above decorative plate can be obtained by pressing with a sticking device such as the above to adhere the decorative veneer to the surface of the substrate.
【００２３】[0023]
【作用】透明合成樹脂シートを用いてこれを透明あるい
は硬化すると透明となる接着剤を介して化粧単板表面に
接着することにより表面保護層が形成される。表面保護
層は、用いられる透明合成樹脂シートの厚さに対応し、
しかも均等な厚さに形成される。The surface protective layer is formed by using a transparent synthetic resin sheet and adhering it to the surface of the decorative veneer through an adhesive which becomes transparent when it is transparent or cured. The surface protection layer corresponds to the thickness of the transparent synthetic resin sheet used,
Moreover, it is formed to have a uniform thickness.
【００２４】[0024]
【実施例】図１は本発明による化粧単板を模式的に示す
ものであり、化粧単板１の表面に透明合成樹脂シート２
が、透明または硬化すると透明となる接着剤を介して積
層接着されて表面保護層を形成している。３は透明接着
剤層である。EXAMPLE FIG. 1 schematically shows a decorative veneer according to the present invention, in which a transparent synthetic resin sheet 2 is provided on the surface of the decorative veneer 1.
However, they are laminated and adhered via an adhesive that is transparent or becomes transparent when cured to form a surface protective layer. 3 is a transparent adhesive layer.
【００２５】[0025]
【発明の効果】本発明によれば、化粧単板の表面に均一
厚さの表面保護層を簡単な作業工程で容易に形成するこ
とができる。本発明によって得られる化粧単板は、強度
や耐摩耗性に優れたものであり、建材用や家具用に好適
に用いられる。According to the present invention, a surface protective layer having a uniform thickness can be easily formed on the surface of a decorative veneer by a simple working process. The decorative veneer obtained by the present invention has excellent strength and abrasion resistance, and is suitably used for building materials and furniture.
【００２６】また、用いられる透明合成樹脂シートの厚
さを変更することによって表面保護層の厚さを調整する
ことができる。この場合、製造設備には何ら変更を要し
ない。The thickness of the surface protective layer can be adjusted by changing the thickness of the transparent synthetic resin sheet used. In this case, the manufacturing equipment does not need any change.
【図１】本発明による化粧単板を模式的に示す断面図で
ある。FIG. 1 is a sectional view schematically showing a decorative veneer according to the present invention.
１ 化粧単板 ２ 透明合成樹脂シート（表面保護層） ３ 透明接着剤層 1 Decorative veneer 2 Transparent synthetic resin sheet (surface protection layer) 3 Transparent adhesive layer
Claims (5)
すると透明となる接着剤を介して透明合成樹脂シートが
接着されてなる表面保護層が形成されることを特徴とす
る化粧単板。1. A decorative veneer characterized in that a surface protective layer is formed on the surface of the decorative veneer by bonding a transparent synthetic resin sheet through an adhesive that is transparent or becomes transparent when cured.
れた着色透明合成樹脂シートであることを特徴とする請
求項１の化粧単板。2. The decorative veneer according to claim 1, wherein the transparent synthetic resin sheet is a colored transparent synthetic resin sheet which is arbitrarily colored.
様が印刷されてなることを特徴とする請求項１または２
の化粧単板。3. The pattern pattern is printed on the back surface of the transparent synthetic resin sheet.
Makeup veneer.
る接着剤が任意着色された着色接着剤であることを特徴
とする請求項１の化粧単板。4. The decorative veneer according to claim 1, wherein the adhesive that is transparent or becomes transparent when cured is a colored adhesive that is arbitrarily colored.
すると透明となる接着剤を介して透明合成樹脂シートを
載置して圧締接着することにより該透明合成樹脂シート
よりなる表面保護層を形成することを特徴とする化粧単
板の製造方法。5. A surface protective layer made of a transparent synthetic resin sheet by placing a transparent synthetic resin sheet on the surface of a decorative veneer with an adhesive that is transparent or transparent when cured and pressure-bonding the transparent synthetic resin sheet. A method for producing a decorative veneer characterized by forming.