JPH07216764A - Revresible cloth and production thereof - Google Patents
Revresible cloth and production thereofInfo
- Publication number
- JPH07216764A JPH07216764A JP448494A JP448494A JPH07216764A JP H07216764 A JPH07216764 A JP H07216764A JP 448494 A JP448494 A JP 448494A JP 448494 A JP448494 A JP 448494A JP H07216764 A JPH07216764 A JP H07216764A
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- layer
- hologram
- reversible
- forming layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、片面に花柄などのプリ
ント絵柄層を施して、一方の面にホログラム形成層を積
層してなるリバーシブル布地で、例えば、傘、帽子、レ
インコートなどに用いる両面に絵柄層を有するリバージ
ル布地とその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention is a reversible cloth having a print pattern layer such as a floral pattern on one side and a hologram forming layer laminated on one side, for example, for umbrellas, hats, raincoats and the like. The present invention relates to a reversil fabric having a pattern layer on both sides and a method for producing the same.
【０００２】[0002]
【従来の技術】従来、リバーシブル（両面）布地とし
て、片面は無地染色で他の面にプリント絵柄を施した布
地、或いは両面にプリント絵柄を施した布地、また、両
面ともに無地染色が施された布地（いずれも図示はしな
い）が一般的に知られている。更に、近年、布地の片面
にアルミニウムなどの金属蒸着を施し、他の面に、昇華
転写によるプリント絵柄を施した布地、或いは不織布に
アルミニウム蒸着を施して、この不織布を布地に貼り合
わせたリバーシブル布地（いずれも図示はしない）にお
いても、例えば、傘、帽子、又はレインコートなどに利
用されるようになってきた。2. Description of the Related Art Conventionally, as a reversible (double-sided) fabric, one side is a plain dyed fabric and the other side is a printed pattern, or both sides are a printed pattern, or both sides are plain dyed. Fabrics (none of which are shown) are generally known. Furthermore, in recent years, a metal such as aluminum has been vapor-deposited on one side of a fabric, and the other side of the fabric has a print pattern printed by sublimation transfer. Even in (not shown), it has come to be used, for example, for an umbrella, a hat, or a raincoat.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、これら
一般的なリバーシブル布地は、例えば、傘、帽子、レイ
ンコートなどに用いた場合には、太陽光、或いは雨水な
どにより、染色されたプリント絵柄が変色（色が褪せた
り、濁った色になる）されやすく、また、アルミニウム
などの金属蒸着層、プリント絵柄を含む布地の耐久性が
弱かった。However, when these general reversible cloths are used, for example, for umbrellas, hats, raincoats, etc., the dyed print pattern is discolored by sunlight or rainwater. (The color fades or becomes cloudy), and the durability of the metal vapor-deposited layer of aluminum or the like and the fabric including the print pattern were weak.
【０００４】そこで本発明は、片面にプリント絵柄を施
した布地の他の面に、転写によりホログラム形成層と、
この上に透明な保護層を積層し、ホログラム形成層を構
成する金属蒸着層により紫外線をカツトして、布地の耐
久性を向上させ、かつ、意匠性に優れた両面に絵柄層を
有するリバーシブル布地とその製造方法を提供するもの
である。Therefore, in the present invention, a hologram forming layer is formed by transfer on the other side of the cloth having a print pattern on one side,
A reversible cloth with a transparent protective layer laminated on it, cut with ultraviolet rays by a metal vapor deposition layer constituting the hologram forming layer to improve the durability of the cloth, and having a design layer on both sides with excellent design. And a method of manufacturing the same.
【０００５】[0005]
【課題を解決するための手段】上記の課題を解決するた
めに本発明のリバーシブル布地（１８）は、片面にプリ
ント絵柄（１０ａ）が施された布地（１０）の他の面
に、接着剤（１１）を介してホログラム形成層（１５）
と、該ホログラム形成層（１５）上に、透明な保護層
（１４）を設けたことを特徴とするものである。In order to solve the above-mentioned problems, the reversible cloth (18) of the present invention has an adhesive on the other surface of the cloth (10) having a print pattern (10a) on one surface. Hologram forming layer (15) via (11)
And a transparent protective layer (14) provided on the hologram forming layer (15).
【０００６】また、本発明のリバーシブル布地（１８）
の製造方法は、片面にプリント絵柄（１０ａ）が施され
た布地（１０）と、基材シート（２０）に、ホログラム
層（１３）とアルミニウム蒸着層（１２）からなるホロ
グラム形成層（１５）を積層してなるホログラム転写シ
ート（２０ａ）を重ね合わせ、該ホログラム転写シート
のアルミニウム蒸着層（１２）面と該布地（１０）面を
接着剤（１１）を介して熱圧着し、エージングした後
に、基材シート（２０）を剥離して、前記布地（１０）
上にホログラム形成層（１５）を積層し、更に、該ホロ
グラム形成層（１５）上に接着剤（１１）を介して、透
明な保護層（１４）を転写積層したことを特徴とするも
のである。Also, the reversible fabric (18) of the present invention
In the method for producing, a hologram forming layer (15) including a hologram layer (13) and an aluminum vapor deposition layer (12) on a fabric (10) having a print pattern (10a) on one side and a substrate sheet (20). After laminating the hologram transfer sheets (20a), the aluminum vapor deposition layer (12) surface and the cloth (10) surface of the hologram transfer sheet are thermocompression bonded with an adhesive (11), and after aging The base material sheet (20) is peeled off, and the cloth (10) is obtained.
A hologram forming layer (15) is laminated thereon, and a transparent protective layer (14) is further laminated on the hologram forming layer (15) via an adhesive (11). is there.
【０００７】また、前記リバーシブル布地全面に、パン
チング加工により、所望の通気孔を形成し、このリバー
シブル布地に通気性を付与することを特徴とする。Further, a desired ventilation hole is formed on the entire surface of the reversible cloth by punching, so that the reversible cloth is provided with air permeability.
【０００８】[0008]
【作用】本発明のリバーシブル布地（１８）は、布地
（１０）の片面にプリント絵柄を施し、他の布地面にホ
ログラム形成層（１５）を接着剤（１１）を介して転
写、積層することで、意匠性が優れた両面可視可能な布
地となる。この布地上のホログラム形成層（１５）を構
成するアルミニウム蒸着層（１２）によって、太陽光な
どによる紫外線をカットして断熱効果が生ずるととも
に、ウレタン樹脂からなる透明な保護層（１４）によ
り、ホログラム形成層（１５）の表面保護と柔軟性を布
地に付与して、ホログラム形成層を含むリバーシブル布
地の耐久性を向上させる。In the reversible cloth (18) of the present invention, a print pattern is provided on one side of the cloth (10), and the hologram forming layer (15) is transferred and laminated on the other cloth through the adhesive (11). Thus, the fabric has excellent design and is visible on both sides. The aluminum vapor-deposited layer (12) constituting the hologram forming layer (15) on the cloth cuts off ultraviolet rays due to sunlight or the like to produce a heat insulating effect, and the transparent protective layer (14) made of urethane resin allows the hologram to be formed. The surface protection and flexibility of the forming layer (15) are imparted to the fabric to improve the durability of the reversible fabric containing the hologram forming layer.
【０００９】更に、このリバーシブル布地（１８）の全
面に、必要に応じてパンチング加工により大小の通気孔
を形成することで、この布地（１８）に通気性が付与さ
れるので、このリバージル布地の利用範囲が一段と広が
る。Further, by forming large and small ventilation holes on the entire surface of the reversible cloth (18) by punching, if necessary, the cloth (18) is provided with air permeability, so that the reversible cloth (18) is The range of use expands further.
【００１０】[0010]
【実施例】図に基づき実施例を説明する。図１は、本発
明に係わるリバーシブル布地の一例を示す断面図であ
る。また、図２は、本発明に係わるリバーシブル布地の
全面に、所望の通気孔を形成し通気性を付与したリバー
シブル布地の一例を示す断面図である。Embodiment An embodiment will be described with reference to the drawings. FIG. 1 is a cross-sectional view showing an example of a reversible cloth according to the present invention. FIG. 2 is a cross-sectional view showing an example of a reversible cloth in which desired ventilation holes are formed on the entire surface of the reversible cloth according to the present invention to provide air permeability.
【００１１】本発明の両面に絵柄層を有するリバーシブ
ル布地（１８）は、図１に示すように、片面に花柄など
のプリント絵柄（１０ａ）が施された布地（１０）の他
の面に、接着剤（１１）を介してホログラム形成層（１
５）を積層し、このホログラム形成層（１５）上の全面
に接着剤（１１）を介してウレタン樹脂からなる透明な
保護層（１４）を転写、積層したものである。このリバ
ーシブル布地（１８）は、表面は透明な保護層（１４）
により被覆されたホログラム形成層の絵柄と、裏面は花
柄などのプリント絵柄（１０ａ）などによる優れた意匠
性を有するリバーシブル布地が得られる。As shown in FIG. 1, a reversible cloth (18) having a pattern layer on both sides of the present invention has a print pattern (10a) such as a flower pattern on one side and the other side of the cloth (10) as shown in FIG. , The hologram forming layer (1
5) is laminated, and a transparent protective layer (14) made of urethane resin is transferred and laminated on the entire surface of the hologram forming layer (15) via an adhesive (11). This reversible fabric (18) has a transparent protective surface (14)
A reversible cloth having an excellent design by the pattern of the hologram forming layer covered with and the print pattern (10a) such as a flower pattern on the back surface is obtained.
【００１２】また、図２に示すように、このリバーシブ
ル布地（１８）の全面に、通気性を付与するために、必
要に応じて通気孔（Ｈ）を形成したものである。この通
気孔（Ｈ）は、例えば、傘やレインコートなど使用する
場合には、細い針のようなものでパンチング加工して、
雨水が浸透しない程度の微細な通気孔（Ｈ）を多数形成
し、また、帽子などに使用する場合には、所定の径にし
た通気孔（Ｈ）を形成するもので、使用目的に応じ適宜
選択することが好ましい。Further, as shown in FIG. 2, ventilation holes (H) are formed on the entire surface of the reversible cloth (18) as needed in order to impart air permeability. For example, when using an umbrella or a raincoat, this vent hole (H) is punched with something like a thin needle,
A large number of minute vent holes (H) are formed so that rainwater does not permeate, and when used for a hat, etc., the vent holes (H) having a predetermined diameter are formed, depending on the purpose of use. It is preferable to select.
【００１３】本発明におけるリバーシブル布地の製造方
法は、図３（Ａ）に示すように、予めポリエステルサテ
ンの片面に、昇華転写により花柄などのプリント絵柄
（１０ａ）を施した布地（１０）を準備する。この布地
の他の面（被絵柄面）にホログラム転写シート（２０
ａ）を重ね、ホログラム形成層（１５）を構成するアル
ミニウム蒸着層（１２）の面に二液混合接着剤（１１）
を塗布し、転写、積層したものである。As shown in FIG. 3 (A), the method for producing a reversible cloth according to the present invention is a cloth (10) in which a print pattern (10a) such as a flower pattern is previously applied to one side of polyester satin by sublimation transfer. prepare. On the other surface (the surface to be painted) of this cloth, the hologram transfer sheet (20
a) is overlaid, and the two-component mixed adhesive (11) is applied to the surface of the aluminum vapor deposition layer (12) which constitutes the hologram forming layer (15).
Is applied, transferred, and laminated.
【００１４】具体的には、このホログラム転写シート
（２０ａ）は、厚さ約２５μｍのＰＥＴフィルム基材
（２０）に、アクリル樹脂からなる剥離層（厚さ約０．
７μｍ）と、ホログラム層（ウレタン樹脂０．５μｍ）
（１３）及びアルミニウム蒸着層（５００Å）（１２）
からなるホログラム形成層（１５）を積層構成したもの
である。次いで、このホログラム転写シート（２０ａ）
のアルミニウム蒸着層（１２）面に、ロールコーター機
で二液タイプのウレタン系接着剤（１１）を塗布し、前
記布地（１０）面に重ね、温度１２０℃で加熱圧着して
乾燥させる。更に、常温でエージングした後に、ホログ
ラム転写シートのＰＥＴフィルム基材（２０）を剥がす
と、ホログラム形成層が積層された布地が得られる。Specifically, this hologram transfer sheet (20a) comprises a PET film substrate (20) having a thickness of about 25 μm and a release layer (thickness of about 0.
7 μm) and hologram layer (urethane resin 0.5 μm)
(13) and aluminum vapor deposition layer (500Å) (12)
The hologram forming layer (15) made of is laminated. Then, this hologram transfer sheet (20a)
The two-component type urethane adhesive (11) is applied to the surface of the aluminum vapor-deposited layer (12) of the above with a roll coater, and the urethane adhesive (11) of the two-component type is applied to the surface of the fabric (10), heated and pressed at a temperature of 120 ° C. and dried. Furthermore, after aging at room temperature, the PET film base material (20) of the hologram transfer sheet is peeled off to obtain a fabric on which the hologram forming layer is laminated.
【００１５】次いで、図３（Ｂ）に示すように、ホログ
ラム形成層（１５）を被覆する透明な保護層（１４）
は、予め、厚さ約７０μｍの離型紙（２１）に、厚さ約
１０μｍのウレタン樹脂層（１４）を積層して、転写シ
ート（２１ａ）にしたもので、ホログラム層（１３）面
にウレタン系の二液混合接着剤（１１）を塗布し、ホロ
グラム形成層（１５）に転写シートのウレタン樹脂層
（１４）面を重ね、圧着し温度１２０℃で乾燥する。更
に、常温でエージングした後に、離型紙（２１）を剥が
す。これによりリバーシブル布地（１８）が得られる。Next, as shown in FIG. 3B, a transparent protective layer (14) covering the hologram forming layer (15).
Is a transfer sheet (21a) prepared by laminating a urethane resin layer (14) having a thickness of about 10 μm on a release paper (21) having a thickness of about 70 μm in advance. A system two-component mixed adhesive (11) is applied, the urethane resin layer (14) surface of the transfer sheet is superposed on the hologram forming layer (15), and pressure bonding is performed, followed by drying at a temperature of 120 ° C. Furthermore, after aging at room temperature, the release paper (21) is peeled off. This gives a reversible fabric (18).
【００１６】このようにして得られたリバーシブル布地
の全面に、必要に応じてパンチング加工を行って、所望
の通気孔（Ｈ）を形成することで、通気性を付与したリ
バーシブル布地（１８）となる。The reversible cloth thus obtained is punched, if necessary, to form desired ventilation holes (H), thereby forming a reversible cloth (18) having breathability. Become.
【００１７】[0017]
【発明の効果】本発明のリバーシブル布地は、布地の片
面にプリント絵柄を施して、この布地の他の面上にホロ
グラム形成層を転写、積層することで、両面可視可能な
意匠性に優れたリバーシブル布地となる。この布地のホ
ログラム形成層を構成するアルミニウム蒸着層が、太陽
光などの紫外線をカットすることで断熱効果が生ずると
ともに、ウレタン樹脂からなる透明な保護層で被覆する
ことで、ホログラム形成層の表面保護と柔軟性を布地に
付与するので、ホログラム形成層を含むリバーシブル布
地の耐久性が向上する。INDUSTRIAL APPLICABILITY The reversible cloth of the present invention has a print design on one side of the cloth, and by transferring and laminating the hologram forming layer on the other side of the cloth, the reversible cloth has an excellent design property visible on both sides. Reversible fabric. The aluminum vapor deposition layer that constitutes the hologram forming layer of this cloth produces a heat insulating effect by cutting off ultraviolet rays such as sunlight, and by covering it with a transparent protective layer made of urethane resin, the surface of the hologram forming layer is protected. Since the fabric is imparted with flexibility, durability of the reversible fabric including the hologram forming layer is improved.
【００１８】更に、このリバーシブル布地の全面に、パ
ンチング加工を行って所望の通気孔を形成することで、
このリバーシブル布地に通気性が付与され、このリバー
シブル布地の利用範囲が一段と広がるなどの優れた効果
が生ずる。Further, punching is performed on the entire surface of the reversible cloth to form desired ventilation holes,
Breathability is imparted to the reversible cloth, and an excellent effect is obtained such that the utilization range of the reversible cloth is further expanded.
【図１】本発明の実施例におけるリバーシブル布地の積
層構成の一例を示す断面図である。FIG. 1 is a cross-sectional view showing an example of a laminated structure of a reversible cloth according to an embodiment of the present invention.
【図２】本発明の実施例におけるリバーシブル布地の全
面に、通気孔を形成し通気性を付与したリバーシブル布
地の一例を示す断面図である。FIG. 2 is a cross-sectional view showing an example of a reversible cloth in which ventilation holes are formed on the entire surface of the reversible cloth in an example of the present invention to provide air permeability.
【図３】本発明の実施例におけるリバーシブル布地の製
造工程の一例を示す断面説明図である。FIG. 3 is a cross-sectional explanatory view showing an example of a manufacturing process of a reversible cloth according to the embodiment of the present invention.
１０ …布地 １０ａ…プリント絵柄 １１ …接着剤層 １２ …アルミニウム蒸着層 １３ …ホログラム層 １４ …保護層 １５ …ホログラム形成層 １８ …リバーシブル布地 ２０ …ＰＥＴフィルム基材 ２０ａ…ホログラム転写シート ２１ …離型紙 ２１ａ…転写シート Ｈ …小孔 10 ... Cloth 10a ... Print pattern 11 ... Adhesive layer 12 ... Aluminum vapor deposition layer 13 ... Hologram layer 14 ... Protective layer 15 ... Hologram forming layer 18 ... Reversible fabric 20 ... PET film substrate 20a ... Hologram transfer sheet 21 ... Release paper 21a … Transfer sheet H… Small hole
Claims (4)
面に、接着剤を介してホログラム形成層と、該ホログラ
ム形成層上に透明な保護層を設けたことを特徴とする両
面に絵柄層を有するリバーシブル布地。1. A hologram-forming layer and a transparent protective layer provided on the hologram-forming layer via an adhesive on the other surface of the fabric having a print pattern on one side. Reversible fabric with a pattern layer.
孔を設けたことを特徴とする請求項１に記載の両面に絵
柄層を有するリバーシブル布地。2. A reversible fabric having a pattern layer on both sides thereof, wherein desired ventilation holes are provided on the entire surface of the reversible fabric.
材シートにホログラム層とアルミニウム蒸着層からなる
ホログラム形成層を形成してなるホログラム転写シート
を重ね合わせ、該ホログラム転写シートのアルミニウム
蒸着層面と該布地面を接着剤を介して熱圧着し、エージ
ングした後、基材シートを剥離して、前記布地上にホロ
グラム形成層を積層し、該ホログラム形成層上に接着剤
を介して、透明な保護層を積層したことを特徴とする両
面に絵柄層を有するリバーシブル布地の製造方法。3. A cloth having a print pattern on one side thereof and a hologram transfer sheet formed by forming a hologram forming layer composed of a hologram layer and an aluminum vapor deposition layer on a substrate sheet are superposed, and the aluminum vapor deposition of the hologram transfer sheet is performed. After thermocompression bonding the layer surface and the cloth ground with an adhesive, after aging, the base material sheet is peeled off, a hologram forming layer is laminated on the cloth, and the hologram forming layer is laminated with an adhesive. A method for producing a reversible fabric having a pattern layer on both sides, characterized by laminating a transparent protective layer.
加工を施して所望の通気孔を形成することを特徴とする
請求項３に記載の両面に絵柄層を有するリバーシブル布
地の製造方法。4. The method for producing a reversible fabric having a pattern layer on both sides according to claim 3, wherein a desired ventilation hole is formed by punching the entire surface of the reversible fabric.