JPH07216198A - Liquid crystal polyester resin composition and its preparation - Google Patents

Abstract

PURPOSE:To obtain an inexpensive liq. crystal polyester resin compsn. excellent in heat resistance and mechanical properties such as flexural modulus of elasticity, tensile strength and impact strength in particular. CONSTITUTION:A liq. crystal polyester (A) is blended with an arom. polycarbonate (B), a diamine (C) and a surface-untreated glass fiber (D) having a no.- average fiber diameter of 5 to 25mum, a no.-average fiber length of 30 to 1,000mum and a no.-average fiber length to no.-average fiber diameter ratio of 2 to 150 to prepare a liq. crystal polyester resin compsn. The amt. of the component (A) is 35 to 99wt.% based on the total amt. of the components (A) and (B), while the amt. of the component (B) is 65 to 1wt.% based on the total amt. of the components (A) and (B). The amt. of the component (C) is 0.0001 to 3 pts.wt. per 100 pts.wt. in total of the components (A) and (B), while the amt. of the component (D) is 1 to 100 pts.wt. per 100 pts.wt. in total of the components (A) and (B).

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、射出成形や押出成形に
より、成形品などに利用できる液晶ポリエステル樹脂組
成物およびその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a liquid crystal polyester resin composition which can be used for molded articles by injection molding or extrusion molding, and a method for producing the same.

【０００２】[0002]

【従来の技術】液晶ポリエステルは、ポリエチレンテレ
フタレートやポリブチレンテレフタレートのような結晶
性ポリエステルと異なり、分子が剛直なため溶融状態で
も絡み合いを起こさず、結晶状態を有するポリドメイン
を形成し、低剪断により分子鎖が流れ方向に著しく配向
する挙動を示し、一般に溶融型液晶（サーモトロピック
液晶）ポリマーと呼ばれている。この特異的な挙動のた
め、溶融流動性が極めて優れ、０．２〜０．５ｍｍ程度
の薄肉成形品を容易に得ることができ、しかもこの成形
品は高強度、高剛性を示すという長所を有するが、異方
性が極めて大きく、そのためウエルド強度が低いなどの
問題点があった。また、用途によってはより一層の高耐
熱性、高強度、高剛性が要求される。2. Description of the Related Art Unlike crystalline polyesters such as polyethylene terephthalate and polybutylene terephthalate, liquid crystal polyesters do not cause entanglement even in a molten state because they have rigid molecules and form a polydomain having a crystalline state, which results in low shear. It exhibits a behavior in which molecular chains are significantly oriented in the flow direction, and is generally called a melt-type liquid crystal (thermotropic liquid crystal) polymer. Due to this peculiar behavior, the melt fluidity is extremely excellent, and a thin-walled molded product of about 0.2 to 0.5 mm can be easily obtained, and this molded product has the advantage of exhibiting high strength and high rigidity. However, there is a problem that the anisotropy is extremely large and therefore the weld strength is low. Further, depending on the application, higher heat resistance, higher strength and higher rigidity are required.

【０００３】また、液晶ポリエステルは一般に高価であ
ることも問題であった。液晶ポリエステルの優れた耐熱
性、力学的性質を保持し、成形品の異方性が改良され、
かつ安価な液晶ポリエステル樹脂組成物は強く市場から
要望されていた。液晶ポリエステルに非晶性の高分子を
配合することにより液晶ポリエステルの成形加工性、強
度を改良することを目的とした試みとして、特開昭５６
−１１５３５７号公報に液晶ポリエステルにポリフェニ
レンエーテルなどの重合体を配合し液晶ポリエステルの
溶融加工性を改良した記載がみられる。また特開平２−
９７５５５号公報にハンダ耐熱性を向上させる目的で液
晶ポリエステルに各種のポリアリーレンオキサイドを配
合した記載がみられる。Another problem is that liquid crystal polyesters are generally expensive. Maintains the excellent heat resistance and mechanical properties of liquid crystal polyester, and improves the anisotropy of molded products.
Further, an inexpensive liquid crystal polyester resin composition has been strongly demanded from the market. As an attempt to improve the moldability and strength of the liquid crystal polyester by blending the liquid crystal polyester with an amorphous polymer, Japanese Patent Laid-Open No.
There is a description in JP-A-115357 in which a polymer such as polyphenylene ether is blended with a liquid crystal polyester to improve the melt processability of the liquid crystal polyester. In addition, JP-A-2-
In Japanese Patent No. 97555, there is a description in which various polyarylene oxides are mixed with liquid crystal polyester for the purpose of improving solder heat resistance.

【０００４】[0004]

【発明が解決しようとする課題】しかしながら、一般に
成形温度の高い液晶ポリエステルに、それより成形温度
の低いポリフェニレンエーテルなどの非晶性高分子を配
合してなる組成物は、組成物の溶融加工性は向上して
も、成形加工の際に配合樹脂の熱分解のために成形品の
外観不良が生じるという問題があった。また、該組成物
の機械的物性、耐熱性などが不十分という問題点があっ
た。本発明の目的は、耐熱性、及び機械的物性、特に曲
げ弾性率、引張強度、衝撃強度に優れ、かつ安価な液晶
ポリエステル樹脂組成物を提供するものである。However, a composition obtained by blending a liquid crystal polyester having a high molding temperature with an amorphous polymer such as polyphenylene ether having a lower molding temperature generally has a melt processability of the composition. However, there is a problem that the appearance of the molded product is deteriorated due to the thermal decomposition of the compounded resin during the molding process. Further, there is a problem that the mechanical properties and heat resistance of the composition are insufficient. An object of the present invention is to provide a liquid crystal polyester resin composition which is excellent in heat resistance and mechanical properties, particularly flexural modulus, tensile strength and impact strength, and is inexpensive.

【０００５】[0005]

【課題を解決するための手段】本発明者らは、これらの
問題点を解決するため鋭意検討の結果、本発明に至った
ものである。すなわち本発明は、次に記す発明である。 （１）（Ａ）液晶ポリエステル、（Ｂ）芳香族ポリカー
ボネート、（Ｃ）ジアミンおよび（Ｄ）数平均繊維径が
５〜２５μｍ、数平均繊維長が３０〜１０００μｍ、か
つ数平均繊維長／数平均繊維径が２〜１５０で、表面無
処理のガラス繊維を配合したものであり、成分（Ａ）と
成分（Ｂ）の合計量に対して成分（Ａ）が３５〜９９重
量％、成分（Ｂ）が６５〜１重量％であり、かつ成分
（Ａ）と成分（Ｂ）の合計量１００重量部に対して、成
分（Ｃ）が０．０００１〜３重量部および成分（Ｄ）が
１〜１００重量部である液晶ポリエステル樹脂組成物。 （２）液晶ポリエステル、芳香族ポリカーボネートおよ
びジアミンを溶融混練して得られた樹脂組成物と、液晶
ポリエステル、芳香族ポリカーボネートおよび数平均繊
維径が５〜２５μｍ、数平均繊維長が３０〜１０００μ
ｍ、かつ数平均繊維長／数平均繊維径が２〜１５０で、
表面無処理のガラス繊維とを溶融混練することを特徴と
する（１）記載の液晶ポリエステル樹脂組成物の製造方
法。The present inventors have arrived at the present invention as a result of extensive studies to solve these problems. That is, the present invention is the invention described below. (1) (A) liquid crystal polyester, (B) aromatic polycarbonate, (C) diamine and (D) number average fiber diameter of 5 to 25 μm, number average fiber length of 30 to 1000 μm, and number average fiber length / number average A glass fiber having a fiber diameter of 2 to 150 and no surface treatment is blended, and the component (A) is 35 to 99% by weight and the component (B is relative to the total amount of the component (A) and the component (B). ) Is 65 to 1% by weight, and 0.0001 to 3 parts by weight of the component (C) and 1 to 100 parts by weight of the total amount of the components (A) and (B). 100 parts by weight of a liquid crystal polyester resin composition. (2) A resin composition obtained by melt-kneading a liquid crystal polyester, an aromatic polycarbonate and a diamine, a liquid crystal polyester, an aromatic polycarbonate and a number average fiber diameter of 5 to 25 μm and a number average fiber length of 30 to 1000 μ.
m, and the number average fiber length / number average fiber diameter is 2 to 150,
The method for producing a liquid crystal polyester resin composition according to (1), characterized in that the surface-untreated glass fiber is melt-kneaded.

【０００６】以下本発明について詳細に説明する。本発
明で使用される成分（Ａ）の液晶ポリエステルは、サー
モトロピック液晶ポリマーと呼ばれるポリエステルであ
り、 （１）芳香族ジカルボン酸と芳香族ジオールと芳香族ヒ
ドロキシカルボン酸との組合せからなるもの、 （２）異種の芳香族ヒドロキシカルボン酸からなるも
の、 （３）芳香族ジカルボン酸と芳香族ジオールとの組み合
わせからなるもの、 （４）ポリエチレンテレフタレートなどのポリエステル
に芳香族ヒドロキシカルボン酸を反応させたものなどが
挙げられ、４００℃以下の温度て異方性溶融体を形成す
るものである。 なお、これらの芳香族ジカルボン酸、芳香族ジオールお
よび芳香族ヒドロキシカルボン酸の代わりに、それらの
エステル形成性誘導体が使用されることもある。該液晶
ポリエステルの繰り返し構造単位としては下記のものを
例示することができるがこれらに限定されるものではな
い。The present invention will be described in detail below. The liquid crystal polyester of the component (A) used in the present invention is a polyester called a thermotropic liquid crystal polymer, which is composed of (1) a combination of an aromatic dicarboxylic acid, an aromatic diol and an aromatic hydroxycarboxylic acid, 2) Different aromatic hydroxycarboxylic acids, (3) Combination of aromatic dicarboxylic acids and aromatic diols, (4) Polyesters such as polyethylene terephthalate reacted with aromatic hydroxycarboxylic acids. And the like, and forms an anisotropic melt at a temperature of 400 ° C. or lower. Incidentally, instead of these aromatic dicarboxylic acids, aromatic diols and aromatic hydroxycarboxylic acids, ester-forming derivatives thereof may be used. Examples of the repeating structural unit of the liquid crystal polyester include the following, but are not limited thereto.

【０００７】[0007]

【化１】 [Chemical 1]

【０００８】[0008]

【化２】 芳香族ジオールに由来する繰返し構造単位：[Chemical 2] Repeating structural units derived from aromatic diols:

【０００９】[0009]

【化３】 [Chemical 3]

【００１０】[0010]

【化４】 芳香族ヒドロキシカルボン酸に由来する繰返し構造単
位：[Chemical 4] Repeating structural unit derived from aromatic hydroxycarboxylic acid:

【００１１】[0011]

【化５】 耐熱性、機械的特性、加工性のバランスから特に好まし
い液晶ポリエステルは[Chemical 5] Especially preferred liquid crystal polyester from the balance of heat resistance, mechanical properties and processability

【００１２】[0012]

【化６】 なる繰り返し構造単位を含むものであり、具体的には繰
り返し構造単位の組み合わせが下記（Ｉ）〜（Ｖ）のも
のである。[Chemical 6] The following combinations (I) to (V) of the repeating structural units are specifically included.

【００１３】[0013]

【化７】 [Chemical 7]

【００１４】[0014]

【化８】 [Chemical 8]

【００１５】[0015]

【化９】 [Chemical 9]

【００１６】[0016]

【化１０】 [Chemical 10]

【００１７】[0017]

【化１１】 該液晶ポリエステル（Ｉ）、（ＩＩ）、（ＩＩＩ）、
（ＩＶ）については、それぞれ、例えば特公昭４７−４
７８７０号公報、特公昭６３−３８８８号公報、特公昭
６３−３８９１号公報、特公昭５６−１８０１６号公報
などに記載されている。本発明の液晶ポリエステル樹脂
組成物の成分（Ｂ）の芳香族ポリカーボネートは、二価
フェノールとフォスゲン、ハロホルメート、炭酸エステ
ルのようなカーボネート前駆体とを反応させて得られる
一般式（ＶＩ）で示される繰り返し構造単位を有する芳
香族ポリカーボネートである。[Chemical 11] The liquid crystal polyesters (I), (II), (III),
Regarding (IV), for example, Japanese Patent Publication No. 47-4
No. 7870, Japanese Patent Publication No. 63-3888, Japanese Patent Publication No. 63-3891, Japanese Patent Publication No. 56-18016. The aromatic polycarbonate as the component (B) of the liquid crystal polyester resin composition of the present invention is represented by the general formula (VI) obtained by reacting a dihydric phenol with a carbonate precursor such as phosgene, a haloformate or a carbonic acid ester. It is an aromatic polycarbonate having a repeating structural unit.

【００１８】[0018]

【化１２】 （Ａ：二価フェノールに由来する二価の芳香族基） ここで用いられる二価フェノールとは、単環式、あるい
は多環式芳香族化合物であり、芳香環中の炭素に直接結
合する２個の水酸基を有する。これら二価フェノールの
具体例としては、２，２─ビス（４─ヒドロキシフェニ
ル）プロパン（ビスフェノールＡ）、ヒドロキノン、レ
ゾルシン、２，２─ビス（ヒドロキシフェニル）ペンタ
ン、２，４’─ジヒドロキシ─ジフェニルメタン、ビス
（２─ヒドロキシフェニル）メタン、ビス（４─ヒドロ
キシフェニル）メタン、ビス（４─ヒドロキシ─５─ニ
トロフェニル）メタン、１，１─ビス（４─ヒドロキシ
フェニル）エタン、３，３─ビス（４─ヒドロキシフェ
ニル）ペンタン、２，２─ジヒドロキシジフェニル、
２，６─ジヒドロキシ─ナフタレン、ビス（４─ヒドロ
キシフェニル）スルホン、２，４’─ジヒドロキシジフ
ェニルスルホン、５─クロロ─２，４’─ジヒドロキシ
ジフェニルスルホン、ビス（４─ヒドロキシフェニル）
ジフェニルジスルホン、４，４─ジヒドロキシジフェニ
ルエーテル、４，４’─ジヒドロキシ─３，３’─ジク
ロロジフェニルエーテル、４，４’─ジヒドロキシ─
２，５─ジエトキシジフェニルエーテル等である。好ま
しくは、ビスフェノールＡおよびその核置換誘導体が挙
げられる。これらの二価フェノールは単独あるいは混合
して用いられる。[Chemical 12] (A: Divalent Aromatic Group Derived from Divalent Phenol) The divalent phenol used here is a monocyclic or polycyclic aromatic compound, and is directly bonded to carbon in the aromatic ring. It has one hydroxyl group. Specific examples of these dihydric phenols include 2,2-bis (4-hydroxyphenyl) propane (bisphenol A), hydroquinone, resorcin, 2,2-bis (hydroxyphenyl) pentane, and 2,4'-dihydroxy-diphenylmethane. , Bis (2-hydroxyphenyl) methane, bis (4-hydroxyphenyl) methane, bis (4-hydroxy-5-nitrophenyl) methane, 1,1-bis (4-hydroxyphenyl) ethane, 3,3-bis (4-hydroxyphenyl) pentane, 2,2-dihydroxydiphenyl,
2,6-dihydroxy-naphthalene, bis (4-hydroxyphenyl) sulfone, 2,4'-dihydroxydiphenyl sulfone, 5-chloro-2,4'-dihydroxydiphenyl sulfone, bis (4-hydroxyphenyl)
Diphenyldisulfone, 4,4-dihydroxydiphenyl ether, 4,4'-dihydroxy-3,3'-dichlorodiphenyl ether, 4,4'-dihydroxy-
2,5-diethoxydiphenyl ether and the like. Preferably, bisphenol A and its nuclear substitution derivative are mentioned. These dihydric phenols may be used alone or as a mixture.

【００１９】本発明の樹脂組成物に用いられる芳香族ポ
リカーボネートは上記の二価フェノールを原料として公
知の方法、すなわち、エステル交換法、溶液法、界面重
縮合法等により製造され、好ましくは粘度平均分子量１
５０００以上、さらに好ましくは２５０００以上のもの
である。これらの具体的な重合方法は、例えば“ＥＮＣ
ＹＣＬＯＰＥＤＩＡ ＯＦ ＰＯＬＹＭＥＲ ＳＣＩＥ
ＮＣＥ ＡＮＤ ＴＥＣＨＮＯＬＯＧＹ”第１０巻（Ｊ
ｈｏｎ Ｗｉｌｅｙ ＆ Ｓｏｎｓ，Ｉｎｃ．，１９６
９年）７１０〜７６４ページに示される「ポリカーボネ
ート」の項に記載されている。また、これらのポリカー
ボネートには特公昭４８─２５０７６号公報に示される
ポリカーボネート─スチレンブロック共重合体に例示さ
れるような共重合体も用いることができる。本発明の液
晶ポリエステル樹脂組成物における成分（Ｃ）のジアミ
ンは、次式で示される。The aromatic polycarbonate used in the resin composition of the present invention is produced by a known method using the above dihydric phenol as a raw material, that is, a transesterification method, a solution method, an interfacial polycondensation method or the like, preferably a viscosity average. Molecular weight 1
It is 5,000 or more, more preferably 25,000 or more. These specific polymerization methods are described, for example, in "ENC
YCLOPEDIA OF POLYMER SCIE
NCE AND TECHNOLOGY "Volume 10 (J
hon Wiley & Sons, Inc. , 196
9 years) "Polycarbonate" on page 710-764. Further, as these polycarbonates, copolymers exemplified by the polycarbonate-styrene block copolymers disclosed in JP-B-48-25076 can also be used. The diamine as the component (C) in the liquid crystal polyester resin composition of the present invention is represented by the following formula.

【００２０】[0020]

【化１３】 （Ｒ₁ は、炭素原子数２〜１２の直鎖状、分岐状もしく
は環状のアルキレン基、またはそれにエーテル結合の酸
素を含んだもの；二価の複素環基；置換もしくは非置換
の単環式芳香族炭化水素基；または置換もしくは非置換
の多環式芳香族炭化水素基を示す。Ｒ₂ 、Ｒ₃ は、水
素、アルキル基、シクロアルキル基、または芳香族基を
示す。[Chemical 13] (R ₁ is a linear, branched or cyclic alkylene group having 2 to 12 carbon atoms, or an ether bond-containing oxygen thereof; a divalent heterocyclic group; a substituted or unsubstituted monocyclic group An aromatic hydrocarbon group; or a substituted or unsubstituted polycyclic aromatic hydrocarbon group, R ₂ and R _{3 each} represent hydrogen, an alkyl group, a cycloalkyl group, or an aromatic group.

【００２１】該ジアミンは、具体的には、１，２─ジア
ミノエタン、１，３─ジアミノプロパン、１，４─ジア
ミノブタン、１，６─ジアミノヘキサン、１，８─ジア
ミノオクタン、１，１０─ジアミノデカン、１，１２─
ジアミノドデカン、１，４─ジアミノシクロヘキサン、
ビス（メチルアミノ）ヘキサン、ビス（３─アミノプロ
ピル）エーテル、１，２─ビス（３─アミノプロポキ
シ）エタン、エチルアミノエチルアミン、メチルアミノ
プロピルアミン、Ｎ，Ｎ’─ジ─ｔ─ブチルエチレンジ
アミン、ビス（２─アミノエチル）ベンゼン等が挙げら
れる。その中でも、Ｒ₂ 、Ｒ₃ の一方もしくは両方が水
素であることが好ましい。具体的には、１，３─ジアミ
ノプロパン、１，６─ジアミノヘキサン、１，１０─ジ
アミノデカン、１，１２─ジアミノドデカン、メチルア
ミノプロピルアミン、ビス（３─アミノプロピル）エー
テルが挙げられる。The diamine is specifically 1,2-diaminoethane, 1,3-diaminopropane, 1,4-diaminobutane, 1,6-diaminohexane, 1,8-diaminooctane, 1,10. -Diaminodecane, 1,12-
Diaminododecane, 1,4-diaminocyclohexane,
Bis (methylamino) hexane, bis (3-aminopropyl) ether, 1,2-bis (3-aminopropoxy) ethane, ethylaminoethylamine, methylaminopropylamine, N, N'-di-t-butylethylenediamine, Examples thereof include bis (2-aminoethyl) benzene. Among them, it is preferable that one or both of R ₂ and R ₃ be hydrogen. Specific examples include 1,3-diaminopropane, 1,6-diaminohexane, 1,10-diaminodecane, 1,12-diaminododecane, methylaminopropylamine and bis (3-aminopropyl) ether.

【００２２】本発明の液晶ポリエステル樹脂組成物の成
分（Ｄ）のガラス繊維は、数平均繊維径が５〜２５μ
ｍ、好ましくは５〜２０μｍ、数平均繊維長が３０〜１
０００μｍ、好ましくは３０〜３００μｍのものを用い
る。数平均繊維径または数平均繊維長が、この範囲外で
あるとガラス繊維の補強効果が小さくなり、充分な剛
性、耐熱性、加工性などが得られず好ましくない。The glass fiber as the component (D) of the liquid crystal polyester resin composition of the present invention has a number average fiber diameter of 5 to 25 μm.
m, preferably 5 to 20 μm, and the number average fiber length is 30 to 1
000 μm, preferably 30 to 300 μm is used. If the number average fiber diameter or the number average fiber length is out of this range, the reinforcing effect of the glass fiber becomes small, and sufficient rigidity, heat resistance, workability, etc. cannot be obtained, which is not preferable.

【００２３】また、ガラス繊維の数平均繊維長／数平均
繊維径、すなわちガラス繊維の数平均繊維長と数平均繊
維径との比で示される形態比（以下、アスペクト比とい
うことがある）の数平均が、２〜１５０、好ましくは３
〜２０であるガラス繊維を用いる。数平均アスペクト比
がこの範囲外であると、組成物の成形品外観が悪かった
り、成形加工性が不良であったりして好ましくない。The morphological ratio (hereinafter sometimes referred to as an aspect ratio) represented by the number average fiber length / number average fiber diameter of glass fibers, that is, the ratio of the number average fiber length and the number average fiber diameter of glass fibers. The number average is 2 to 150, preferably 3
Glass fibers of -20 are used. If the number average aspect ratio is out of this range, the appearance of the molded article of the composition is poor and the molding processability is unfavorable.

【００２４】本発明における成分（Ｄ）のガラス繊維
は、表面無処理のものである。表面無処理のガラス繊維
が優れた物性をもたらす理由は明らかではないが、表面
無処理のガラス繊維は成分（Ａ）の液晶ポリエステル中
に分散しやすく、そのため樹脂組成物の補強効果を高め
る作用があるためと考えられる。The glass fiber of the component (D) in the present invention has no surface treatment. Although the reason why the surface-untreated glass fiber brings about excellent physical properties is not clear, the surface-untreated glass fiber is easily dispersed in the liquid crystal polyester of the component (A), and therefore has the effect of enhancing the reinforcing effect of the resin composition. This is probably because there is.

【００２５】本発明の液晶ポリエステル樹脂組成物にお
いては、成分（Ａ）、成分（Ｂ）、成分（Ｃ）および成
分（Ｄ）の組成比が特定の範囲内の値をとることによっ
て、目的とする液晶ポリエステル樹脂組成物を得ること
ができる。本発明における成分（Ａ）と成分（Ｂ）の比
率は成分（Ａ）が３５〜９９重量％、成分（Ｂ）が６５
〜１重量％であり、好ましくは成分（Ａ）が４５〜９９
重量％、成分（Ｂ）が５５〜１重量％である。成分
（Ａ）が３５重量％未満であると、該組成物からなる成
形品の耐熱性、機械的性質が不充分であり、また９９重
量％を超えると組成物の寸法安定性が不充分となり、コ
スト的にも利点が少なく好ましくない。In the liquid crystal polyester resin composition of the present invention, the composition ratio of the component (A), the component (B), the component (C) and the component (D) is set within a specific range to achieve the purpose. A liquid crystal polyester resin composition can be obtained. In the present invention, the ratio of the component (A) to the component (B) is 35 to 99% by weight of the component (A) and 65 of the component (B).
˜1% by weight, preferably 45-99 of component (A)
%, And the component (B) is 55 to 1% by weight. When the content of the component (A) is less than 35% by weight, the heat resistance and mechanical properties of the molded article formed from the composition are insufficient, and when it exceeds 99% by weight, the dimensional stability of the composition is insufficient. However, there are few advantages in terms of cost, which is not preferable.

【００２６】本発明の液晶ポリエステル樹脂組成物にお
いては、成分（Ａ）と成分（Ｂ）の合計量１００重量部
に対して、成分（Ｃ）のジアミンは０．０００１〜３重
量部、好ましくは０．０００１〜０．２重量部である。
ジアミンが０．０００１重量部未満では組成物の耐熱
性、機械的物性を向上させる効果が少なく、また３重量
部を超えると組成物の耐熱性が著しく低下するため好ま
しくない。In the liquid crystal polyester resin composition of the present invention, the diamine of the component (C) is 0.0001 to 3 parts by weight, preferably 100 parts by weight of the total amount of the components (A) and (B). It is 0.0001 to 0.2 part by weight.
When the amount of diamine is less than 0.0001 part by weight, the effect of improving the heat resistance and mechanical properties of the composition is small, and when it exceeds 3 parts by weight, the heat resistance of the composition is significantly lowered, which is not preferable.

【００２７】本発明において成分（Ａ）と成分（Ｂ）の
合計量１００重量部に対し成分（Ｄ）は１〜１００重量
部であり、好ましくは２〜８０重量部である。成分
（Ｄ）が１重量部未満であると本発明の液晶ポリエステ
ル樹脂組成物の機械的強度、耐熱性などを向上させる効
果が少なく、コスト的にも利点が少ない。また、成分
（Ｄ）が１００重量部を越えると該組成物の成形加工性
が低下し、射出成形品の外観も不良となり好ましくな
い。In the present invention, the amount of the component (D) is 1 to 100 parts by weight, preferably 2 to 80 parts by weight, based on 100 parts by weight of the total amount of the components (A) and (B). When the amount of the component (D) is less than 1 part by weight, the effect of improving the mechanical strength, heat resistance and the like of the liquid crystal polyester resin composition of the present invention is small, and the cost is small. Further, when the amount of the component (D) exceeds 100 parts by weight, the moldability of the composition is deteriorated and the appearance of the injection-molded product is also unfavorable.

【００２８】本発明の液晶ポリエステル樹脂組成物にお
ける好ましい形態は、成分（Ａ）の液晶ポリエステルが
主に連続相を形成し、成分（Ｂ）の芳香族ポリカーボネ
ートが主に分散相を形成している場合である。このよう
な形態の場合、特に該組成物の耐熱性、機械的物性、耐
薬品性および薄肉物性などが優れたものとなる。In a preferred mode of the liquid crystal polyester resin composition of the present invention, the liquid crystal polyester of the component (A) mainly forms a continuous phase, and the aromatic polycarbonate of the component (B) mainly forms a dispersed phase. This is the case. In the case of such a form, the heat resistance, mechanical properties, chemical resistance, thin-wall properties and the like of the composition are particularly excellent.

【００２９】本発明における液晶ポリエステル樹脂組成
物を製造する方法に特に制限はなく、周知の方法を用い
ることができる。たとえば、溶液状態の樹脂成分とガラ
ス繊維とを混合し、溶剤を蒸発させるか、溶剤中に樹脂
成分とガラス繊維を沈澱させる方法が挙げられる。工業
的見地からみると溶融状態で各成分を混練する方法が好
ましい。溶融混練には一般に使用されている一軸または
二軸の押出機、各種のニーダー等の混練装置を用いるこ
とができる。特に二軸の高混練機が好ましい。溶融混練
に際しては、混練装置のシリンダー設定温度は２００〜
３６０℃の範囲が好ましく、さらに好ましくは２５０〜
３４０℃である。The method for producing the liquid crystal polyester resin composition in the present invention is not particularly limited, and known methods can be used. For example, a method may be mentioned in which a resin component in a solution state and glass fiber are mixed and the solvent is evaporated, or the resin component and glass fiber are precipitated in the solvent. From an industrial point of view, a method of kneading each component in a molten state is preferable. For melt kneading, generally used kneading devices such as a single-screw or twin-screw extruder and various kneaders can be used. A biaxial high kneader is particularly preferable. When melt-kneading, the cylinder setting temperature of the kneading device is 200-
It is preferably in the range of 360 ° C, more preferably 250 to
It is 340 ° C.

【００３０】混練に際しては、各成分は予めタンブラー
もしくはヘンシェルミキサーのような装置で各成分を均
一に混合してもよいし、必要な場合には混合を省き、混
練装置にそれぞれ別個に定量供給する方法も用いること
ができる。Upon kneading, the respective components may be mixed in advance by a device such as a tumbler or a Henschel mixer, or if necessary, the mixing may be omitted, and the respective amounts may be separately supplied to the kneading device. Methods can also be used.

【００３１】例えば、液晶ポリエステルと芳香族ポリカ
ーボネートをあらかじめ溶液ブレンド、または溶融混練
して混合物を得て、ついでこれとジアミンおよびガラス
繊維とを溶融混練して液晶ポリエステル樹脂組成物を得
ることもできる。また、芳香族ポリカーボネート、液晶
ポリエステルおよびジアミンを混練機の第一投入口から
投入し、第二投入口から液晶ポリエステルまたは芳香族
ポリカーボネートおよびガラス繊維を投入して一回の混
練で液晶ポリエステル樹脂組成物を得ることもできる。For example, liquid crystal polyester and aromatic polycarbonate may be previously solution-blended or melt-kneaded to obtain a mixture, and this, diamine and glass fiber may be melt-kneaded to obtain a liquid crystal polyester resin composition. Further, the aromatic polycarbonate, the liquid crystal polyester and the diamine are charged from the first charging port of the kneading machine, the liquid crystal polyester or the aromatic polycarbonate and the glass fiber are charged from the second charging port, and the liquid crystal polyester resin composition is kneaded once. You can also get

【００３２】また、液晶ポリエステル、芳香族ポリカー
ボネートおよびジアミンを溶融混練し、その混練物を液
晶ポリエステル、芳香族ポリカーボネートおよびガラス
繊維に配合して、さらに溶融混練して、液晶ポリエステ
ル樹脂組成物を得ることもできる。Liquid crystal polyester, aromatic polycarbonate and diamine are melt-kneaded, and the kneaded product is blended with liquid crystal polyester, aromatic polycarbonate and glass fiber, and further melt-kneaded to obtain a liquid crystal polyester resin composition. You can also

【００３３】混練された該樹脂組成物は、射出成形、押
出成形、その他各種の成形法によって成形されるが、予
め混練の過程を経ず、射出成形や押出成形時にドライブ
レンドして溶融加工操作中に混練して、本発明の樹脂組
成物とし、直接成形加工品を得ることもできる。The kneaded resin composition is molded by various molding methods such as injection molding, extrusion molding and the like, but it is melt-processed by dry blending during injection molding or extrusion molding without undergoing the kneading process in advance. It is also possible to directly knead into the resin composition of the present invention to obtain a molded product.

【００３４】本発明の液晶ポリエステル樹脂組成物にお
いては、所望により無機充填剤が用いられる。このよう
な無機充填剤としては、炭酸カルシウム、タルク、クレ
ー、シリカ、炭酸マグネシウム、硫酸バリウム、酸化チ
タン、アルミナ、石膏、炭素繊維、アルミナ繊維、シリ
カアルミナ繊維、ホウ酸アルミニウムウィスカ、チタン
酸カリウム繊維等が例示される。In the liquid crystal polyester resin composition of the present invention, an inorganic filler is optionally used. Such inorganic fillers include calcium carbonate, talc, clay, silica, magnesium carbonate, barium sulfate, titanium oxide, alumina, gypsum, carbon fiber, alumina fiber, silica-alumina fiber, aluminum borate whiskers, potassium titanate fiber. Etc. are illustrated.

【００３５】本発明の液晶ポリエステル樹脂組成物に、
必要に応じて、さらに、有機充填剤、酸化防止剤、熱安
定剤、光安定剤、難燃剤、滑剤、帯電防止剤、無機また
は有機系着色剤、防錆剤、架橋剤、発泡剤、蛍光剤、表
面平滑剤、表面光沢改良剤、フッ素樹脂などの離型改良
剤などの各種の添加剤を製造工程中あるいはその後の加
工工程において添加することができる。In the liquid crystal polyester resin composition of the present invention,
If necessary, further, an organic filler, an antioxidant, a heat stabilizer, a light stabilizer, a flame retardant, a lubricant, an antistatic agent, an inorganic or organic colorant, a rust preventive agent, a crosslinking agent, a foaming agent, a fluorescent agent. Various additives such as an agent, a surface smoothing agent, a surface gloss improving agent, and a release improving agent such as a fluororesin can be added during the manufacturing process or in the subsequent processing process.

【００３６】[0036]

【実施例】以下、実施例により本発明を説明するが、こ
れらは単なる例示であり、本発明はこれらに限定される
ことはない。 （１）成分（Ａ）の液晶ポリエステル 成分（Ａ）として使用した液晶ポリエステルは以下のも
のである。（ｉ）ｐ−アセトキシ安息香酸１０．８ｋｇ
（６０モル）、テレフタル酸２．４９ｋｇ（１５モ
ル）、イソフタル酸０．８３ｋｇ（５モル）および４，
４’−ジアセトキシジフェニル５．４５ｋｇ（２０．２
モル）を櫛型撹拌翼をもつ重合槽に仕込み、窒素ガス雰
囲気下で撹拌しながら昇温し３３０℃で１時間重合させ
た。この間に副生する酢酸を除去しながら、強力な撹拌
下で重合させた。その後、系を徐々に冷却し、２００℃
で得られたポリマーを系外へ取出した。この得られたポ
リマーを細川ミクロン（株）製のハンマーミルで粉砕
し、２．５ｍｍ径以下の粒子とした。これを更にロータ
リーキルン中で窒素ガス雰囲気下に２８０℃で３時間処
理することによって、流動温度が３２４℃の粒子状の下
記の繰り返し構造単位からなる全芳香族ポリエステルを
得た。以下該液晶ポリエステルをＡ−１と略記する。こ
のポリマーは加圧下で３４１℃で光学異方性を示した。
液晶ポリエステルＡ−１の繰り返し構造単位は、次の通
りである。EXAMPLES The present invention will be described below with reference to examples, but these are merely examples and the present invention is not limited to these. (1) Liquid Crystal Polyester of Component (A) The liquid crystal polyester used as the component (A) is as follows. (I) p-acetoxybenzoic acid 10.8 kg
(60 mol), terephthalic acid 2.49 kg (15 mol), isophthalic acid 0.83 kg (5 mol) and 4,
5.45 kg of 4'-diacetoxydiphenyl (20.2
(Mol) was charged into a polymerization tank having a comb-type stirring blade, and the temperature was raised with stirring under a nitrogen gas atmosphere to carry out polymerization at 330 ° C. for 1 hour. Polymerization was performed under strong stirring while removing acetic acid by-produced during this period. After that, the system is gradually cooled down to 200 ° C.
The polymer obtained in 1. was taken out of the system. The obtained polymer was pulverized with a hammer mill manufactured by Hosokawa Micron Co., Ltd. to obtain particles having a diameter of 2.5 mm or less. This was further treated in a rotary kiln under a nitrogen gas atmosphere at 280 ° C. for 3 hours to obtain a particulate wholly aromatic polyester having a repeating temperature of 324 ° C. and consisting of the following repeating structural units. Hereinafter, the liquid crystal polyester is abbreviated as A-1. This polymer exhibited optical anisotropy at 341 ° C. under pressure.
The repeating structural unit of the liquid crystal polyester A-1 is as follows.

【００３７】[0037]

【化１４】 [Chemical 14]

【００３８】（２）成分（Ｂ）の芳香族ポリカーボネー
ト 成分（Ｂ）として使用した芳香族ポリカーボネートは以
下のものである。ｂ−１（略称）：住友ダウ（株）製
ＣＡＬＩＢＲＥ（登録商標）３００−６〔ＭＦＲ（３０
０℃、１．２ｋｇ荷重）＝６〕(2) Aromatic Polycarbonate of Component (B) The aromatic polycarbonate used as the component (B) is as follows. b-1 (abbreviation): Sumitomo Dow Co., Ltd.
CALIBRE (registered trademark) 300-6 [MFR (30
0 ℃, 1.2kg load) = 6]

【００３９】（３）成分（Ｃ）のジアミン 成分（Ｃ）として使用したジアミンは以下のものであ
る。Ｃ−１（略称）：１，１２−ジアミノドデカンＣ−
２（略称）：１，６−ジアミノヘキサン(3) Diamine of component (C) The diamine used as the component (C) is as follows. C-1 (abbreviation): 1,12-diaminododecane C-
2 (abbreviation): 1,6-diaminohexane

【００４０】（４）成分（Ｄ）のガラス繊維 成分（Ｄ）として使用したガラス繊維は以下のものであ
る。 Ｄ−１（略称）：セントラル硝子（株）製 ＥＦＨ７５
−０１（商品名）、数平均繊維径１３μｍ、数平均繊維
長５０μｍ、アスペクト比３．８、表面無処理 Ｄ−２（略称）：日本板硝子（株）製 ＲＥＶ８（商品
名）、数平均繊維径１３μｍ、数平均繊維長３５μｍ、
アスペクト比２．７、アミノシラン処理 Ｄ−３（略称）：日本板硝子（株）製 ＲＥＳ０３−Ｔ
Ｐ７５（商品名）、数平均繊維径１０μｍ、数平均繊維
長３ｍｍ、アスペクト比３００、シラン系カップリング
剤処理(4) Glass Fiber of Component (D) The glass fiber used as the component (D) is as follows. D-1 (abbreviation): Central Glass Co., Ltd. EFH75
-01 (trade name), number average fiber diameter 13 μm, number average fiber length 50 μm, aspect ratio 3.8, surface-untreated D-2 (abbreviation): Nippon Sheet Glass Co., Ltd. REV8 (trade name), number average fiber Diameter 13 μm, number average fiber length 35 μm,
Aspect ratio 2.7, aminosilane treatment D-3 (abbreviation): Nippon Sheet Glass Co., Ltd. RES03-T
P75 (trade name), number average fiber diameter 10 μm, number average fiber length 3 mm, aspect ratio 300, silane coupling agent treatment

【００４１】実施例１〜３、比較例１〜４ 表１の組成で各成分を安定剤とともにヘンシェルミキサ
ーで混合したのち、池貝鉄工（株）製ＰＣＭ−３０型二
軸押出機を用いてシリンダー設定温度３４２℃で組成物
を脱揮しながら混練し、日精樹脂工業（株）製ＰＳ４０
Ｅ５ＡＳＥ型射出成形機を用いて、成形温度３４２℃、
金型温度１２０℃で射出成形した成形品について以下の
要領で物性測定を行なった。 引張強度、荷重たわみ温度（ＴＤＵＬ）：ＡＳＴＭ４号
引張ダンベル、ＴＤＵＬ測定用試験片（１２７ｍｍ長×
１２．７ｍｍ幅×６．４ｍｍ厚）を成形し、それぞれＡ
ＳＴＭ Ｄ６３８、ＡＳＴＭ Ｄ６４８に準じて引張強
度、ＴＤＵＬ（荷重１８．６ｋｇ）を測定した。Examples 1 to 3 and Comparative Examples 1 to 4 Each component having the composition shown in Table 1 was mixed with a stabilizer in a Henschel mixer, and then a cylinder was prepared using a PCM-30 type twin screw extruder manufactured by Ikegai Tekko KK. Knead while devolatilizing the composition at a set temperature of 342 ° C.
Using an E5ASE type injection molding machine, a molding temperature of 342 ° C.,
The physical properties of the molded product injection-molded at a mold temperature of 120 ° C. were measured as follows. Tensile strength, deflection temperature under load (TDUL): ASTM No. 4 tensile dumbbell, TDUL measurement test piece (127 mm length x
12.7 mm width x 6.4 mm thickness), and A
Tensile strength and TDUL (load 18.6 kg) were measured according to STM D638 and ASTM D648.

【００４２】曲げ弾性率：試験片（６．４ｍｍ厚）につ
いてＡＳＴＭ Ｄ７９０にしたがい、測定した。 アイゾット衝撃強度：試験片（６．４ｍｍ厚）について
ノッチ無でＪＩＳ Ｋ７１１０にしたがい測定した。Flexural Modulus: Measured according to ASTM D790 on a test piece (6.4 mm thick). Izod impact strength: A test piece (6.4 mm thick) was measured according to JIS K7110 without notching.

【００４３】形態：成形品の断面をミクロトームで切削
後、四塩化炭素でエッチングし、芳香族ポリカーボネー
ト部を溶出し、液晶ポリエステル部及びガラス繊維を残
して、次に金蒸着を施した上で走査型電子顕微鏡観察に
供した。形態は以下のように分類した。 Ａ：組成物中の液晶ポリエステル部が主に連続相、組成
物中の芳香族ポリカーボネート部が分散相。 Ｂ：組成物中の芳香族ポリカーボネート部が連続相、組
成物中の液晶ポリエステル部が主に分散相。 得られた結果を表１に示す。本発明の液晶ポリエステル
樹脂組成物は耐熱性、機械的性質などが優れ、しかも安
価な樹脂組成物であることがわかる。Morphology: The cross section of the molded product was cut with a microtome and then etched with carbon tetrachloride to elute the aromatic polycarbonate part, leaving the liquid crystal polyester part and the glass fiber, and then vapor deposition of gold followed by scanning. It was subjected to observation with a scanning electron microscope. The morphology was classified as follows. A: The liquid crystal polyester part in the composition is mainly the continuous phase, and the aromatic polycarbonate part in the composition is the dispersed phase. B: The aromatic polycarbonate part in the composition is a continuous phase, and the liquid crystal polyester part in the composition is mainly a dispersed phase. The results obtained are shown in Table 1. It can be seen that the liquid crystal polyester resin composition of the present invention is an inexpensive resin composition having excellent heat resistance and mechanical properties.

【００４４】[0044]

【表１】 [Table 1]

【００４５】[0045]

【発明の効果】本発明の液晶ポリエステル樹脂組成物
は、耐熱性、機械的物性、特に曲げ弾性率、引張強度、
衝撃強度に優れ、かつ安価なものである。該樹脂組成物
は、このような特性を生かして射出成形や押出成形によ
り成形品、シート、チューブ、フィルム、繊維、積層
物、コーティング材等に用いられる。The liquid crystal polyester resin composition of the present invention has heat resistance, mechanical properties, especially flexural modulus, tensile strength,
It has excellent impact strength and is inexpensive. The resin composition is used for molded articles, sheets, tubes, films, fibers, laminates, coating materials and the like by injection molding or extrusion molding by taking advantage of such characteristics.

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】（Ａ）液晶ポリエステル、（Ｂ）芳香族ポ
リカーボネート、（Ｃ）ジアミンおよび（Ｄ）数平均繊
維径が５〜２５μｍ、数平均繊維長が３０〜１０００μ
ｍ、かつ数平均繊維長／数平均繊維径が２〜１５０で、
表面無処理のガラス繊維を配合したものであり、成分
（Ａ）と成分（Ｂ）の合計量に対して成分（Ａ）が３５
〜９９重量％、成分（Ｂ）が６５〜１重量％であり、か
つ成分（Ａ）と成分（Ｂ）の合計量１００重量部に対し
て、成分（Ｃ）が０．０００１〜３重量部および成分
（Ｄ）が１〜１００重量部である液晶ポリエステル樹脂
組成物。1. A liquid crystal polyester (A), aromatic polycarbonate (B), diamine (C) and number average fiber diameter (D) of 5 to 25 .mu.m and number average fiber length of 30 to 1000 .mu.m.
m, and the number average fiber length / number average fiber diameter is 2 to 150,
The surface-untreated glass fiber is blended, and the amount of the component (A) is 35 relative to the total amount of the component (A) and the component (B).
To 99% by weight, the component (B) is 65 to 1% by weight, and the component (C) is 0.0001 to 3 parts by weight based on 100 parts by weight of the total amount of the components (A) and (B). And a liquid crystal polyester resin composition in which the component (D) is 1 to 100 parts by weight. 【請求項２】液晶ポリエステル、芳香族ポリカーボネー
トおよびジアミンを溶融混練して得られた樹脂組成物
と、液晶ポリエステル、芳香族ポリカーボネートおよび
数平均繊維径が５〜２５μｍ、数平均繊維長が３０〜１
０００μｍ、かつ数平均繊維長／数平均繊維径が２〜１
５０で、表面無処理のガラス繊維とを溶融混練すること
を特徴とする請求項１記載の液晶ポリエステル樹脂組成
物の製造方法。2. A resin composition obtained by melt-kneading a liquid crystal polyester, an aromatic polycarbonate and a diamine, a liquid crystal polyester, an aromatic polycarbonate and a number average fiber diameter of 5 to 25 μm and a number average fiber length of 30 to 1
000 μm, and the number average fiber length / number average fiber diameter is 2 to 1
The method for producing a liquid crystal polyester resin composition according to claim 1, wherein the surface-untreated glass fiber is melt-kneaded at 50.