JPH0719814Y2 - Recording sheet having optical transparency - Google Patents
Recording sheet having optical transparencyInfo
- Publication number
- JPH0719814Y2 JPH0719814Y2 JP1990118716U JP11871690U JPH0719814Y2 JP H0719814 Y2 JPH0719814 Y2 JP H0719814Y2 JP 1990118716 U JP1990118716 U JP 1990118716U JP 11871690 U JP11871690 U JP 11871690U JP H0719814 Y2 JPH0719814 Y2 JP H0719814Y2
- Authority
- JP
- Japan
- Prior art keywords
- recording sheet
- receiving layer
- substrate
- ink receiving
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 「産業上の利用分野」 本考案は、オーバーヘッドプロジェクターでの読み取
り、あるいは、ジアゾコピーの用紙箋等に利用される光
透過性を有する記録用シートに関する。DETAILED DESCRIPTION OF THE INVENTION "Industrial Application Field" The present invention relates to a light-transmissive recording sheet which is used for reading with an overhead projector or for paper sheets for diazo copy.
「従来の技術」 オーバーヘッドプロジェクターでの読み取り利用される
記録用シートは、光透過性を具備するものであることは
勿論であるが、該記録シートは比較的多数回に亙って繰
り返して利用され、かつ、長期間に亙って保存される性
質のものであることから、機械的強度や堅牢性をも具備
することが必要とされている。"Prior Art" Needless to say, a recording sheet that is read and used by an overhead projector has optical transparency, but the recording sheet is repeatedly used a relatively large number of times. In addition, since it has a property of being stored for a long period of time, it is necessary to have mechanical strength and robustness.
したがって、機械的強度や堅牢性に優れ、しかも、透明
性を具備する各種のプラスチックシートが、感熱転写記
録方式による記録用のシートとして利用されたが、これ
らのプラスチックシートは、感熱転写用リボンインキに
対する印字適性が悪く、特に高速印字の場合には、転写
欠け，転写斑，尾引き等の弊害が頻発するだけでなく、
インキの定着性も悪く、印字部分を指先で擦すると簡単
に印字が脱落してしまう等の欠点を有していた。Therefore, various plastic sheets having excellent mechanical strength and fastness and transparency have been used as recording sheets for the thermal transfer recording method. These plastic sheets are thermal transfer ribbon inks. Is not suitable for printing, especially in the case of high-speed printing, in addition to frequent problems such as transfer defects, transfer spots, and tailing,
The fixing property of the ink was poor, and there was a defect that the print was easily dropped off when the print part was rubbed with a fingertip.
このため、プラスチックシートの表面をサンドブラスト
処理に付したマット化シート、あるいは、インキ受用適
性を具備する合成樹脂によるアンカーコート層を具備さ
せる等によって、印字適性を改良したプラスチックシー
トによる記録用シートが提案されている。For this reason, we propose a recording sheet made of a plastic sheet with improved printability by providing a matte sheet whose surface is sandblasted, or an anchor coat layer made of a synthetic resin having ink acceptability. Has been done.
また、他方、記録用シート表面のインキの受理適性を高
めるために、紙の表面に対して、クレー，タルク，酸化
チタン等の顔料と、メチルセルローズ，メトキシセルロ
ーズ，アラビアゴム，カゼイン等の水溶性結合剤とによ
る水溶性塗料層を有するシート（特開昭55−42824号公
報）や、紙等からなる支持体の表面に対して、飽和ポリ
エステル樹脂とヒドロキシエチルセルロースとの混合樹
脂と顔料とを含有する塗料による塗料層を有するシート
（特開昭57−137191号公報）等についても提案されてい
る。On the other hand, pigments such as clay, talc, and titanium oxide, and water-soluble pigments such as methyl cellulose, methoxy cellulose, gum arabic, and casein are used on the surface of the paper in order to improve the acceptability of ink on the surface of the recording sheet. A sheet having a water-soluble paint layer with a binder (Japanese Patent Laid-Open No. 55-42824) or the surface of a support made of paper or the like contains a mixed resin of a saturated polyester resin and hydroxyethyl cellulose and a pigment. A sheet having a paint layer of the paint (JP-A-57-137191) has also been proposed.
「考案が解決しようとする課題」 ところで、前述の表面がマット化されているプラスチッ
クシートは、マット化のために光透過性が低下してしま
い、オーバーヘッドプロジェクターでの読み取りのでき
る透明性が得られなくなり、また、アンカーコート層を
有するプラスチックシートは、高速印字の場合の転写性
が不安定であり、しかも、インキの定着性も十分ではな
い。"Problems to be solved by the device" By the way, the plastic sheet with a matt surface as described above has a reduced light transmittance due to the matte surface, and thus has transparency that can be read by an overhead projector. Further, the transferability of the plastic sheet having the anchor coat layer is unstable in the case of high-speed printing, and the fixing property of the ink is not sufficient.
また、先の特開昭55−42824号公報や、特開昭57−13719
1号公報等に説明されている塗料層を具備する記録用シ
ートは、そのいずれもが、オーバーヘッドプロジェクタ
ーでの読み取りに利用し得るような透明性については全
く考慮されていない。In addition, the above-mentioned JP-A-55-42824 and JP-A-57-13719.
None of the recording sheets provided with the paint layer described in Japanese Patent Laid-Open No. 1 etc. consider transparency that can be used for reading with an overhead projector.
これに対して、本考案は、顔料を含有する塗料層からな
るインキ受理層を具備する記録用シートからなるもの
で、オーバーヘッドプロジェクターでの読み取りに利用
し得るような透明性を有し、かつ、インキ受理層の印字
適性が高く、しかも、プラスチックフィルムからなる基
体とインキ受理層との間の接着強度に優れた光透過性の
記録用シートを提供する。On the other hand, the present invention is composed of a recording sheet having an ink receiving layer made of a paint layer containing a pigment, and has transparency such that it can be read by an overhead projector, and (EN) Provided is a light-transmissive recording sheet having a high printability of an ink-receiving layer and having excellent adhesive strength between a substrate made of a plastic film and the ink-receiving layer.
「課題を解決するための手段」 本考案の光透過性を有する記録用シートは、透明性を有
する厚さ25〜250μのプラスチックフィルムからなる基
体と、該基体の少なくとも片面に形成されている帯電防
止剤を含有し、かつワックスに対する親和性良好なイン
キ受理層とを具備しており、前記インキ受理層が、透明
な樹脂皮膜形成能を有する熱可塑性樹脂100重量部に対
して、平均粒径１μ以下の無機質あるいは有機質微粉末
25〜250重量部と、イソシアネート系化合物とを含有す
るコーティング用組成物によって、厚さ0.2〜２μに形
成されている塗膜からなっている。"Means for Solving the Problems" The light-transmitting recording sheet of the present invention is a transparent substrate of a plastic film having a thickness of 25 to 250μ, and a charging member formed on at least one surface of the substrate. An ink receiving layer containing an inhibitor and having a good affinity for wax, wherein the ink receiving layer has an average particle size with respect to 100 parts by weight of a thermoplastic resin having a transparent resin film forming ability. Inorganic or organic fine powder of 1μ or less
It is composed of a coating film having a thickness of 0.2 to 2 μm formed from a coating composition containing 25 to 250 parts by weight and an isocyanate compound.
前記構成からなる本考案の光透過性を有する記録用シー
トの代表的な構造は、第１図〜第３図に示される。A typical structure of the light-transmitting recording sheet of the present invention having the above structure is shown in FIGS.
すなわち、第１図に示される光透過性を有する記録用シ
ート１は、透明性を有するプラスチックフィルムによる
基体２と、該基体２の片面に形成されているインキ受理
層３とからなる。That is, the recording sheet 1 having a light transmitting property shown in FIG. 1 comprises a substrate 2 made of a transparent plastic film, and an ink receiving layer 3 formed on one surface of the substrate 2.
第２図に示される光透過性を有する記録用シート４は、
透明性を有するプラスチックフィルムによる基体５と、
該基体５の表，裏の両面に形成されているインキ受理層
６及び７とからなる。The recording sheet 4 having optical transparency shown in FIG.
A substrate 5 made of a transparent plastic film,
It is composed of ink receiving layers 6 and 7 formed on both the front and back surfaces of the substrate 5.
第３図に示される光透過性を有する記録用シート８は、
透明性を有するプラスチックフィルムによる基体９と、
該基体９の片面にプライマー層10を介して形成されてい
るインキ受理層11とからなる。The recording sheet 8 having optical transparency shown in FIG.
A base 9 made of a transparent plastic film,
An ink receiving layer 11 is formed on one surface of the substrate 9 with a primer layer 10 interposed therebetween.
前述の本考案の各記録用シートにおいて、基体2,5,9に
は、強度，取り扱い容易性，経済性等の点から、25〜25
0μの厚さのプラスチックフィルムが利用され、例え
ば、ポリエステルフィルム，ポリプロピレンフィルム，
トリアセテートフィルム，アルクリ系フィルム，ポリカ
ーボネートフィルム，ポリエチレンフィルム，セロファ
ン，塩化ビニリデンフィルム等が使用される。In each of the recording sheets of the present invention described above, the bases 2, 5 and 9 have a thickness of 25 to 25 in terms of strength, easy handling, economical efficiency, etc.
A plastic film having a thickness of 0 μ is used, and examples thereof include polyester film, polypropylene film,
Triacetate film, acrylic film, polycarbonate film, polyethylene film, cellophane, vinylidene chloride film, etc. are used.
基体2,5,9の少なくとも片面に形成されているインキ受
理層3,6,7,11は、本考案の記録用シートに対して良好な
印字適性をもたらすものであって、透明な樹脂皮膜形成
能を有する熱可塑性樹脂100重量部に対して平均粒径１
μ以下の無機質あるいは有機質微粉末25〜250重量部と
イソシアネート系化合物とを含有するコーティング用組
成物を、例えば、グラビアコート，ロールコート，ナイ
フコート，バーコート等の一般の塗工手段で塗工するこ
とによって形成される。The ink receiving layer 3,6,7,11 formed on at least one surface of the substrate 2,5,9 provides good printability to the recording sheet of the present invention, and is a transparent resin film. Average particle size of 1 per 100 parts by weight of thermoplastic resin with forming ability
A coating composition containing 25 to 250 parts by weight of an inorganic or organic fine powder of μ or less and an isocyanate compound is applied by a general coating means such as gravure coating, roll coating, knife coating, and bar coating. Is formed by
インキ受理層3,6,7,11における透明な樹脂皮膜形成能を
有する熱可塑性樹脂には、ワックスに対する親和性が良
好な樹脂、例えば、飽和ポリエステル樹脂、酢酸ビニル
樹脂、ポリアミド樹脂、塩化ビニル樹脂・酢酸ビニル共
重合樹脂、ポリビニルブチラール樹脂、ポリ塩化ビニリ
デン樹脂、アクリロニトリル・ブタジエン共重合樹脂等
が、透明な樹脂皮膜形成能を有する樹脂として用いられ
る。例えば、飽和ポリエステル樹脂，酢酸ビニル樹脂，
ポリアミド樹脂，塩化ビニル・酢酸ビニル共重合樹脂，
ポリビニルブチラール樹脂，ポリ塩化ビニリデン樹脂，
アクリロニトリル・ブタジエン共重合樹脂等が、透明な
樹脂皮膜形成能を有する樹脂として利用されることが好
ましい。The thermoplastic resin having the ability to form a transparent resin film in the ink receiving layers 3, 6, 7, 11 is a resin having a good affinity for wax, for example, saturated polyester resin, vinyl acetate resin, polyamide resin, vinyl chloride resin. -Vinyl acetate copolymer resin, polyvinyl butyral resin, polyvinylidene chloride resin, acrylonitrile-butadiene copolymer resin, etc. are used as the resin having the ability to form a transparent resin film. For example, saturated polyester resin, vinyl acetate resin,
Polyamide resin, vinyl chloride / vinyl acetate copolymer resin,
Polyvinyl butyral resin, polyvinylidene chloride resin,
Acrylonitrile / butadiene copolymer resin or the like is preferably used as the resin having the ability to form a transparent resin film.
本考案の記録用シートにおけるインキ受理層中のイソシ
アネート系化合物は、基体とインキ受理層との間の接着
力を高めるものであり、例えば、キシリレンジイソシア
ネートが好適である。The isocyanate compound in the ink receiving layer of the recording sheet of the present invention enhances the adhesive force between the substrate and the ink receiving layer, and for example, xylylene diisocyanate is preferable.
インキ受理層3,6,7,11における前述の熱可塑性樹脂中に
含有されている無機質または有機質微粉末は、平均粒径
１μ以下の微粉末であり、熱可塑性樹脂100重量部に対
して25〜250重量部の割合で含有される。The inorganic or organic fine powder contained in the above-mentioned thermoplastic resin in the ink receiving layers 3, 6, 7, 11 is a fine powder having an average particle diameter of 1 μ or less, and is 25 per 100 parts by weight of the thermoplastic resin. It is contained in a proportion of 250 parts by weight.
インキ受理層3,6,7,11は、該インキ受理層中における無
機質または有機質微粉末の存在によって、インキ受理層
の印字適性が効果的に改良されるもので、例えば、硫酸
バリウム，炭酸マグネシウム，シリカ，炭酸カルシウ
ム，酸化アルミニウム，二酸化スズ，ベンゾグアナミ
ン，二酸化チタン等の微粉末が利用される。The ink receiving layers 3, 6, 7, 11 are those in which the printability of the ink receiving layer is effectively improved due to the presence of the inorganic or organic fine powder in the ink receiving layer. For example, barium sulfate or magnesium carbonate. , Silica, calcium carbonate, aluminum oxide, tin dioxide, benzoguanamine, titanium dioxide and other fine powders are used.
インキ受理層における無機質または有機質微粉末の量
が、熱可塑性樹脂100重量部に対して25重量部未満にな
ると、無機質または有機質微粉末の添加の効果が十分で
はなく、また、250重量部を超えると、記録用シートの
透明性が十分ではなくなる。When the amount of the inorganic or organic fine powder in the ink receiving layer is less than 25 parts by weight with respect to 100 parts by weight of the thermoplastic resin, the effect of adding the inorganic or organic fine powder is not sufficient, and exceeds 250 parts by weight. If so, the transparency of the recording sheet becomes insufficient.
なお、インキ受理層における無機質または有機質微粉末
の平均粒径が１μを超えるような場合には、インキ受理
層における印字適性を改良するのに十分な量の微粉末を
添加すると、インキ受理層が十分な透明性が維持し得な
くなるので、無機質または有機質微粉末は、平均粒径が
１μ以下、好ましくは0.5μ以下のものが利用される。When the average particle size of the inorganic or organic fine powder in the ink receiving layer exceeds 1 μ, adding the fine powder in an amount sufficient to improve the printability in the ink receiving layer causes the ink receiving layer to Since sufficient transparency cannot be maintained, an inorganic or organic fine powder having an average particle size of 1 μm or less, preferably 0.5 μm or less is used.
インキ受理層における前述の微粉末として、シリカ，酸
化アルミニウム，炭酸マグネシウム，二酸化スズ等を利
用した場合には、これらの無機質微粉末による良好な吸
油性能によって、ワックス系バインダーを主成分とする
インキによる感熱転写プリンターに対して特に良好な転
写性能が奏され、解像度の高い記録シートとなる。When silica, aluminum oxide, magnesium carbonate, tin dioxide, etc. are used as the above-mentioned fine powder in the ink receiving layer, due to the good oil absorption performance of these inorganic fine powders, the ink containing a wax-based binder as a main component is used. Particularly good transfer performance is exhibited for a thermal transfer printer, and the recording sheet has high resolution.
第３図に示される光透過性を有する記録用シート８にお
けるプライマー層10は、基体９とインキ受理層11との間
の接着を強化するものであり、公知のプライマー用塗料
を適用することによって形成される。The primer layer 10 in the light-transmissive recording sheet 8 shown in FIG. 3 strengthens the adhesion between the substrate 9 and the ink receiving layer 11, and by applying a known primer coating composition. It is formed.
例えば、基体９が熱可塑性ポリエステルフィルムからな
る場合には、アクリル系樹脂，ポリエステル系樹脂，ポ
リ酢酸ビニル系樹脂，塩化ビニル・酢酸ビニル樹脂，ポ
リオールとジイソシアネート，ポリオールとメラミン，
エポキシ樹脂とジイソシアネー等によるプライマー用塗
料を利用することによって、基体９とインキ受理層11と
の間に、特に良好な接着強度が得られる。For example, when the substrate 9 is made of a thermoplastic polyester film, acrylic resin, polyester resin, polyvinyl acetate resin, vinyl chloride / vinyl acetate resin, polyol and diisocyanate, polyol and melamine,
Particularly good adhesive strength can be obtained between the substrate 9 and the ink receiving layer 11 by using a coating material for a primer such as epoxy resin and diisocyanate.
また、本考案の光透過性を有する記録用シートは、帯電
防止剤を含有しているので、塵埃付着防止性やフィーデ
ィング特性を具備させ得る。In addition, since the recording sheet having light transmittance of the present invention contains an antistatic agent, it can be provided with a dust adhesion preventing property and a feeding property.
帯電防止性能の付与は、例えば、アニオン系，カチオン
系，非イオン系，さらには両性の界面活性剤等による通
常の帯電防止剤が混合されているプラスチックフィルム
を基体として利用したり、あるいは、インキ受理層形成
用のコーティング組成物中に前述の帯電防止剤を添加し
たり、さらには、インキ受理層の表面に帯電防止剤を塗
布する等の手段によって行なわれる。For imparting antistatic performance, for example, a plastic film mixed with an ordinary antistatic agent such as anionic, cationic, nonionic or amphoteric surfactant is used as a substrate, or ink is used. The antistatic agent is added to the coating composition for forming the receiving layer, or the antistatic agent is applied to the surface of the ink receiving layer.
なお、インキ受理層中に含有されている微粉末が二酸化
スズの場合には、インキ受理層自体が導電性を有するよ
うになるため、前述の帯電防止性を付与する特別の工程
を付さなくても、塵埃付着防止性やフィーディング特性
において優れた作用を奏する記録用シートが得られる。When the fine powder contained in the ink-receiving layer is tin dioxide, the ink-receiving layer itself becomes conductive, so it is not necessary to add the above-mentioned special step for imparting antistatic properties. However, it is possible to obtain a recording sheet that exhibits excellent effects in dust adhesion prevention and feeding characteristics.
「実施例」 以下、本考案の光透過性を有する記録用シートの具体的
な構成を、製造実施例をもって説明し、得られた記録用
シートの光透過率と、感熱転写用リボンインキに対する
印字適性とを説明する。[Examples] Hereinafter, a specific configuration of the recording sheet having light transmittance of the present invention will be described with reference to manufacturing examples, and the light transmittance of the recording sheet obtained and printing on a ribbon ink for heat-sensitive transfer are described. Explain the aptitude.
参考例１〜参考例３ 厚さ100μの熱可塑性ポリエステルフィルム［東レ
（株）：ルミラーＴタイプ］による基体の片側表面に、
以下に記載する組成のコーティング用組成物Ｉ〜IIIか
らなるコーティング剤を、グラビア塗工方式にて、塗工
量0.5g（固形成分）／m2の割合に塗布することによって
インキ受理層を形成し、前記参考例品である光透過性を
有する記録用シート［Ａ］〜［Ｃ］を得た。Reference Example 1 to Reference Example 3 A thermoplastic polyester film having a thickness of 100 μ [Toray Industries, Inc .: Lumirror T type]
An ink receiving layer is formed by applying a coating agent comprising the coating compositions I to III having the composition described below at a coating amount of 0.5 g (solid component) / m 2 by a gravure coating method. Then, the light transmissive recording sheets [A] to [C] which are the reference example products were obtained.
コーティング用組成物Ｉ （１）γ・Al2O3（デグサ製） ・・・10重量部 （２）塩化ビニル・酢酸ビニル共重合樹脂（UCC製） ・
・・８重量部 （３）熱可塑性ポリエステル樹脂［バイロン200:東洋紡
績（株）製］ ・・・８重量部 （４）キシレンジイソシアネート ・・・６重量部 （５）トルエン ・・・70重量部 （６）MEK ・・・60重量部 コーティング用組成物II （１）沈降性硫酸バリウム ・・・15重量部 （２）ポリビニルブチラール ・・・10重量部 （３）トルエン ・・・40重量部 （４）MEK ・・・35重量部 （５）キシレンジイソシアネート ・・・３重量部 コーティング用組成物III （１）SnO2微粉末 ・・・16重量部 （２）熱可塑性ポリエステル樹脂 ・・・８重量部 （３）塩化ビニル・酢酸ビニル共重合樹脂・・・８重量
部 （４）トルエン ・・・90重量部 （５）MEK ・・・80重量部 （６）キシレンジイソシアネート ・・・５重量部 なお、コーティング用組成物は、イソシアネート成分を
除いた樹脂成分を溶剤に溶解した後、これに微粉末成分
を添加し、サンドミルで２時間混練し、さらに、コーテ
ィング剤の塗工工程の直前にイソシアネート成分を添加
することによって調製した。Coating composition I (1) γ ・ Al 2 O 3 (manufactured by Degussa) ・ ・ ・ 10 parts by weight (2) Vinyl chloride / vinyl acetate copolymer resin (manufactured by UCC) ・
..8 parts by weight (3) Thermoplastic polyester resin [Byron 200: manufactured by Toyobo Co., Ltd.] ・ ・ ・ 8 parts by weight (4) Xylene diisocyanate ・ ・ ・ 6 parts by weight (5) Toluene ・ ・ ・ 70 parts by weight (6) MEK ・ ・ ・ 60 parts by weight Coating composition II (1) Precipitating barium sulfate ・ ・ ・ 15 parts by weight (2) Polyvinyl butyral ・ ・ ・ 10 parts by weight (3) Toluene ・ ・ ・ 40 parts by weight ( 4) MEK ・ ・ ・ 35 parts by weight (5) Xylene diisocyanate ・ ・ ・ 3 parts by weight Coating composition III (1) SnO 2 fine powder ・ ・ ・ 16 parts by weight (2) Thermoplastic polyester resin ・ ・ ・ 8 parts by weight Parts (3) Vinyl chloride / vinyl acetate copolymer resin: 8 parts by weight (4) Toluene: 90 parts by weight (5) MEK: 80 parts by weight (6) Xylene diisocyanate: 5 parts by weight The coating composition is It was prepared by dissolving the resin component excluding the anate component in a solvent, adding the fine powder component thereto, kneading for 2 hours in a sand mill, and further adding the isocyanate component immediately before the coating step of the coating agent. .
また、前述の記録用シート［Ａ］〜［Ｃ］における樹脂
塗膜からなるインキ受理層の厚さは、いずれも略１μで
ある。Further, the thickness of the ink receiving layer formed of the resin coating film in each of the recording sheets [A] to [C] described above is approximately 1 μm.
記録用シート［Ａ］〜［Ｃ］の感熱転写用リボンインキ
に対する印字適性を、東芝（株）製の感熱プリンターTN
−5000によって判定し、鮮明な印字が得られたものを
○、鮮明な印字が得られなかったものを×で、第１表中
にて表示する。The printability of the recording sheets [A] to [C] for the thermal transfer ribbon ink is measured by the thermal printer TN manufactured by Toshiba Corporation.
It is judged in −5000, and those showing clear prints are indicated by ◯, and those not showing clear prints are indicated by x in Table 1.
さらに、記録用シート［Ａ］〜［Ｃ］の光透過率を、島
津（株）製自記分光度計RC−330（積分球使用）を利用
して、可視光域400〜700nmの透過率を測定することによ
って計測し、第１表に示す。Furthermore, the light transmittance of the recording sheets [A] to [C] was measured by using a self-recording spectrophotometer RC-330 (using an integrating sphere) manufactured by Shimadzu Corporation to measure the transmittance in the visible light range of 400 to 700 nm. It is measured by measuring and is shown in Table 1.
実施例 前述の参考例１で得られた光透過性を有する記録用シー
ト［Ａ］のインキ受理層の表面に、カチオン系界面活性
剤（エレクノンOR−5802−Ａ）の200倍エタノール溶液
をグラビアコート方式で塗布し、参考例品たる記録用シ
ート［Ｄ］を得た。 Example A 200 times ethanol solution of a cationic surfactant (Electnon OR-5802-A) was gravure-coated on the surface of the ink receiving layer of the recording sheet [A] having a light-transmitting property obtained in Reference Example 1 described above. Application was performed by a coating method to obtain a recording sheet [D] as a reference example product.
この記録用シート［Ｄ］に対して、参考例１〜３による
記録用シートの場合と同様に、感熱転写用リボンインキ
に対する印字適性を判定したところ、良好な印字適性が
得られた。The printability of the recording sheet [D] to the ribbon ink for thermal transfer was determined in the same manner as in the case of the recording sheets according to Reference Examples 1 to 3, and good printability was obtained.
また、光透過性も高く、かつ、帯電防止性においても極
めて優れた性質を有していた。Further, it had a high light transmittance and an extremely excellent antistatic property.
「作用，効果」 本考案の光透過性を有する記録用シートは、透明性を有
する厚さ25〜250μのプラスチックフィルムからなる基
体によって、比較的多数回に亙って繰り返し利用され、
かつ、長期間に亙って保存されるに必要とされる十分な
機械的諸強度が得られ、該基体の少なくとも片面に形成
されている無機質あるいは有機質微粉末を含有する樹脂
塗膜からなるインキ受理層の存在によって、感熱転写用
リボンインキに対する印字適性において優れた作用が奏
される。"Operation and Effect" The light-transmitting recording sheet of the present invention is repeatedly used for a relatively large number of times by a substrate made of a transparent plastic film having a thickness of 25 to 250 µ.
In addition, an ink having a resin coating film containing inorganic or organic fine powder formed on at least one surface of the substrate, which has sufficient mechanical strength required for long-term storage. The presence of the receiving layer exerts an excellent action in printability with respect to the thermal transfer ribbon ink.
さらに、本考案の光透過性を有する記録用シートは、基
体が透明性を有するプラスチックフィルムからなり、ま
た、該基体に対して形成されているインキ受理層が、透
明な合成樹脂皮膜形成能を有する熱可塑性樹脂100重量
部に対して、平均粒径１μ以下の無機質あるいは有機質
微粉末25〜250重量部を含有するコーティング用組成物
による厚さ0.2〜２μの塗膜で形成されているので、イ
ンキ受理層の存在が基体の透明性に大きく影響を及ぼす
ようなことがないため、通常、80％以上の可視光透過率
が維持される。Further, in the light-transmitting recording sheet of the present invention, the substrate is made of a transparent plastic film, and the ink receiving layer formed on the substrate has a transparent synthetic resin film forming ability. Since it is formed of a coating film having a thickness of 0.2 to 2 μm based on 100 parts by weight of the thermoplastic resin having the coating composition containing 25 to 250 parts by weight of an inorganic or organic fine powder having an average particle diameter of 1 μm or less, Since the presence of the ink receiving layer does not significantly affect the transparency of the substrate, the visible light transmittance of 80% or more is usually maintained.
したがって、本考案の記録用シートには、オーバーヘッ
ドプロジェクターでの読み取りに使用することのできる
透明性が具備されているので、比較的多数回に亙って繰
り返し利用され、かつ、長期間に亙って保存されること
の多いオーバーヘッドプロジェクターでの読み取りに利
用される記録用シートとしての用途において、極めて優
れた効果が得られる。Therefore, since the recording sheet of the present invention is provided with transparency that can be used for reading with an overhead projector, it is repeatedly used for a relatively large number of times and for a long period of time. In a use as a recording sheet used for reading with an overhead projector that is often stored as a file, a very excellent effect can be obtained.
さらに、本考案の記録用シートは、プラスチックフィル
ムからなる基体に対して形成されているインキ受理層
が、熱可塑性樹脂とイソシアネート系化合物とを含有す
るコーティング用組成物によって形成されているので、
インキ受理層における印字適性が高く、しかも、基体と
インキ受理層との間に優れた接着強度が形成されるの
で、品質の良好なものが得られる。Further, in the recording sheet of the present invention, since the ink receiving layer formed on the substrate made of a plastic film is formed by the coating composition containing a thermoplastic resin and an isocyanate compound,
The printability of the ink-receiving layer is high, and since excellent adhesive strength is formed between the substrate and the ink-receiving layer, good quality is obtained.
第１図〜第３図は、本考案の夫々異なる記録用シートを
模型的に示す拡大断面図である。 １……光透過性を有する記録用シート、２……透明性を
有する厚さ25〜250μのプラスチックフィルムからなる
基体、３……厚さ0.2〜２μの塗膜からなるインキ受理
層。1 to 3 are enlarged sectional views schematically showing different recording sheets of the present invention. 1 ... Recording sheet having light transmissivity, 2 ... Substrate made of transparent plastic film having a thickness of 25 to 250 .mu., 3 ... Ink receiving layer having a coating film having a thickness of 0.2 to 2 .mu.
フロントページの続き (56)参考文献 特開 昭57−14091（ＪＰ，Ａ) 特開 昭58−148794（ＪＰ，Ａ) 特開 昭56−89983（ＪＰ，Ａ) 特開 昭58−67497（ＪＰ，Ａ) 特開 昭58−215398（ＪＰ，Ａ)Continuation of front page (56) Reference JP-A-57-14091 (JP, A) JP-A-58-148794 (JP, A) JP-A-56-89983 (JP, A) JP-A-58-67497 (JP , A) JP-A-58-215398 (JP, A)
Claims (3)
ックフィルムの基体と、該基体の少なくとも片面に形成
されている帯電防止剤を含有し、かつワックスに対する
親和性良好なインキ受理層とを具備しており、前記イン
キ受理層が、透明な樹脂皮膜形成能を有する熱可塑性樹
脂100重量部に対して、平均粒径１μ以下の無機質ある
いは有機質微粉末25〜250重量部と、イソシアネート系
化合物とを含有するコーティング剤による厚さ0.2〜２
μの塗膜からなることを特徴とする光透過性を有する記
録用シート。1. A transparent plastic film substrate having a thickness of 5 to 250 μm, and an ink receiving layer containing an antistatic agent formed on at least one surface of the substrate and having a good affinity for wax. The ink receiving layer comprises 25 to 250 parts by weight of an inorganic or organic fine powder having an average particle diameter of 1 μm or less, and an isocyanate compound with respect to 100 parts by weight of a thermoplastic resin capable of forming a transparent resin film. 0.2 to 2 by the coating agent containing and
A recording sheet having a light-transmitting property, which comprises a coating film of μ.
処理に付されている実用新案登録請求の範囲第１項記載
の光透過性を有する記録用シート。2. A light-transmitting recording sheet according to claim 1, wherein the surface of the ink receiving layer is subjected to coating treatment with an antistatic agent.
ックフィルムの基体が、該基体中に帯電防止剤を含有す
る実用新案登録請求の範囲第１項記載の光透過性を有す
る記録用シート。3. A light-transmissive recording sheet according to claim 1, wherein the substrate of a plastic film having a thickness of 5-250 μm and having transparency contains an antistatic agent in the substrate. .