JPH07187907A - Disinfectant - Google Patents

Abstract

PURPOSE:To obtain a long-acting disinfectant useful for sterilizing a hospital to prevent the hospital infection or preventing the proliferation of saprophyte on the wall and glass window in a house. CONSTITUTION:This disinfectant is composed mainly of an antibacterial agent produced by adsorbing one or more antibacterial materials such as silver complex salt, vegetable extract, quaternary ammonium salt or chlorhexidine gluconate to the surface of a silica material and coating a part or total of the surface of the silica material with a coating material. The silica material may be a silica gel, white carbon, vapor-produced silica, etc., or hollow microspheres and may be subjected to acid treatment or baking treatment as necessary. The coating material is e.g. an organic silicon compound, wax, stearic acid compound, resin and inorganic oxide. The coating material is effective for improving the stability and sustained release property of the antibacterial material.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、消毒剤に関する。FIELD OF THE INVENTION This invention relates to disinfectants.

【０００２】[0002]

【従来の技術】従来、例えば、病院内を消毒して感染を
防止したり、また家内の壁やガラス窓等の雑菌繁殖を防
止したりする際には、アルコール等を適用箇所に吹き付
けて、消毒を行っていた。2. Description of the Related Art Conventionally, for example, when disinfecting a hospital to prevent infection, or to prevent the growth of various bacteria such as walls and glass windows in the house, alcohol is sprayed on the application site, I was disinfecting.

【０００３】[0003]

【発明が解決しようとする課題】しかしながら、アルコ
ールは、一時的には消毒されるが、揮発性であるため、
短期間に消毒する効力がなくなる。このため、頻繁に消
毒作業を行わなければならなかった。このことは面倒で
あるとともに、消毒した後から次に消毒するまでの間に
菌が繁殖し、この間に感染してしまう可能性があった。However, although alcohol is temporarily disinfected, alcohol is volatile,
The effectiveness of disinfection in a short period of time is lost. Therefore, disinfection work had to be performed frequently. This is troublesome, and there is a possibility that the bacteria will propagate between the disinfection and the next disinfection, and the bacteria will be infected during this period.

【０００４】従って、本発明は、上記課題を解決し、持
続性のある消毒剤を提供することを目的とする。[0004] Therefore, an object of the present invention is to solve the above problems and provide a disinfectant having a long-lasting effect.

【０００５】[0005]

【課題を解決するための手段及び作用】本発明の消毒剤
は、１種あるいは２種以上の抗菌性材料を吸着させたシ
リカ表面の一部または全部をコーティング材料で被覆し
た抗菌剤を主成分とすることを特徴とする。The disinfectant of the present invention is mainly composed of an antibacterial agent obtained by coating a part or all of the silica surface adsorbing one or more antibacterial materials with a coating material. It is characterized by

【０００６】本発明において消毒剤の主成分となる抗菌
剤は、担体としてシリカを用いている。シリカとして
は、シリカゲル、ホワイトカーボン、気相法シリカ等い
ずれの形態のシリカであってもよく、また中空微小球で
あってもよい。さらに、シリカは、所望により微量な他
の成分、例えば、ホウ素、ナトリウム、リン、カルシウ
ム、カリウム、バリウム、アルミニウム等が含まれる複
合珪酸塩であってもよい。本発明におけるシリカは、必
要に応じて酸処理または焼成処理されたものであっても
よい。In the present invention, the antibacterial agent which is the main component of the disinfectant uses silica as a carrier. The silica may be any form of silica such as silica gel, white carbon, vapor grown silica, or hollow microspheres. In addition, the silica may be a complex silicate optionally containing minor amounts of other components such as boron, sodium, phosphorus, calcium, potassium, barium, aluminum and the like. The silica in the present invention may be acid-treated or calcined as necessary.

【０００７】シリカは、細孔が存在し、表面積が大きい
ために、抗菌性材料を吸着し、かつ吸着した抗菌性材料
の徐放効果がある。また、シリカは、安全性に優れてい
る。さらに、シリカには、脱臭効果もある。抗菌性材料
としては、シリカに吸着可能な従来公知のいずれの抗菌
性材料であってもよく、例えば、銀錯塩、植物抽出物、
第４級アンモニウム塩、グルコン酸クロルヘキシジン等
が挙げられる。これらは、単独で用いてもよいし、複数
を用いてもよい。これら抗菌性材料は、全て安全性に優
れている。Since silica has pores and has a large surface area, it has an effect of adsorbing the antibacterial material and has an effect of gradually releasing the adsorbed antibacterial material. Further, silica is excellent in safety. Furthermore, silica also has a deodorizing effect. The antibacterial material may be any conventionally known antibacterial material capable of being adsorbed on silica, for example, a silver complex salt, a plant extract,
Examples thereof include quaternary ammonium salts and chlorhexidine gluconate. These may be used alone or in combination. All of these antibacterial materials are excellent in safety.

【０００８】抗菌性材料とシリカとの配合比は、重量比
で３：１〜１：３、好ましくは２：１〜１：２であるこ
とが適当である。この配合比よりも抗菌性材料が多すぎ
ると、シリカに抗菌性材料を担持しきれず、溶出しやす
い。さらに、コスト高で、経済的に不適当である。ま
た、この配合比よりも抗菌性材料が少なすぎると、抗菌
性能を発揮しずらい傾向にある。さらに、シリカとコー
ティング材料との配合比は、１：０．１〜１：０．５が
抗菌性能や徐放効果、経済的な面の点から好ましい。The weight ratio of the antibacterial material to silica is 3: 1 to 1: 3, preferably 2: 1 to 1: 2. If the amount of the antibacterial material is more than this mixing ratio, the antibacterial material cannot be fully supported on the silica and the silica is likely to be eluted. Furthermore, it is costly and economically unsuitable. If the amount of the antibacterial material is less than the compounding ratio, the antibacterial performance tends to be difficult to be exhibited. Further, the compounding ratio of silica to the coating material is preferably 1: 0.1 to 1: 0.5 from the viewpoint of antibacterial performance, sustained release effect and economical aspect.

【０００９】さらに、本発明によれば、抗菌性材料を吸
着させたシリカ表面に、コーティング材料を付与してい
る。コーティング材料としては、有機珪素化合物、ワッ
クス、ステアリン酸化合物、スチレン樹脂やＰＭＭＡ樹
脂やフッ素樹脂等の樹脂化合物、無機酸化物等が挙げら
れる。このコーティング材料によって、抗菌性材料の安
定性と徐放性が向上する。Further, according to the present invention, the coating material is applied to the silica surface on which the antibacterial material is adsorbed. Examples of the coating material include organic silicon compounds, waxes, stearic acid compounds, resin compounds such as styrene resins, PMMA resins and fluororesins, and inorganic oxides. This coating material improves the stability and sustained release of the antibacterial material.

【００１０】本発明の消毒剤は、上記のように構成され
る抗菌剤を主成分としている。従って、本発明の消毒剤
によれば、シリカに吸着された抗菌性材料が徐々に放出
されるので、持続性がある。消毒剤中の抗菌剤の割合
は、好ましくは３０重量％〜１重量％である。１重量％
よりも少ないと、抗菌性能が低下する傾向にあり、また
３０重量％よりも多すぎても、それ以上の効果が得られ
ず、経済的に無駄である。The disinfectant of the present invention contains an antibacterial agent having the above-mentioned structure as a main component. Therefore, according to the disinfectant of the present invention, the antibacterial material adsorbed on silica is gradually released, which is durable. The proportion of the antibacterial agent in the disinfectant is preferably 30% by weight to 1% by weight. 1% by weight
If it is less than the above range, the antibacterial performance tends to be lowered, and if it exceeds 30% by weight, no further effect can be obtained and it is economically wasteful.

【００１１】抗菌剤の分散媒としては、上記抗菌剤を均
一に分散可能で無害なものであればよく、溶液、固体の
いずれにも限られない。例えば、流動パラフィン、ブタ
ン等の炭化水素系溶液、精製水、またはロウ状の固体等
が挙げられる。あるいは、本発明の消毒剤には、他の成
分、例えば、洗剤、芳香剤、付着防止剤、静電気防止剤
等を混合することもできる。この場合には、洗浄、芳
香、付着防止、静電気防止等が兼用できる。The dispersion medium of the antibacterial agent is not limited to a solution or solid as long as it can disperse the antibacterial agent uniformly and is harmless. For example, liquid paraffin, a hydrocarbon-based solution such as butane, purified water, or a waxy solid may be used. Alternatively, the disinfectant of the present invention may be mixed with other components such as detergents, fragrances, anti-adhesion agents, anti-static agents and the like. In this case, cleaning, fragrance, prevention of adhesion, prevention of static electricity, etc. can be combined.

【００１２】本発明の消毒剤を塗布する方法は、いずれ
の方法であってもよく、例えば、液体状であれば、スプ
レーで噴霧する方法、刷毛や布等で塗り付ける方法等が
挙げられる。また、固体であれば、そのまま擦り付ける
方法、水等で希釈して刷毛や布等で塗り付ける方法等が
挙げられる。The method of applying the disinfectant of the present invention may be any method, for example, in the case of a liquid state, a method of spraying with a spray, a method of applying with a brush or cloth, etc. may be mentioned. If it is a solid, it may be rubbed as it is, or may be diluted with water or the like and applied with a brush or cloth.

【００１３】塗布する部位としては、消毒したいいずれ
の部位にも適用可能であり、室内の壁、ガラス窓、天
井、ベッドや食器戸棚等の家具、キッチン等が挙げられ
る。特に、病院内で塗布する場合には、院内感染が防止
される点で有用である。また、衣類、特に病院内で使用
される白衣やシーツ等にも適用すれば、より感染防止が
強化される。The part to be applied can be applied to any part to be disinfected, and examples thereof include indoor walls, glass windows, ceilings, furniture such as beds and cupboards, and kitchens. In particular, when applied in a hospital, it is useful in preventing nosocomial infection. Further, when applied to clothes, especially white coats and sheets used in hospitals, infection prevention is further enhanced.

【００１４】[0014]

【実施例】以上説明した本発明の構成・作用を一層明ら
かにするために、以下に本発明の好適な実施例を説明す
る。 ＜１＞ 実施例 （１）抗菌剤の調整 イオン交換水６０ｍｌを４０℃に加熱し、それに酢酸銀
０．４６４ｇ（２．８×１０^ー3モル）を加え４０〜５０
℃で約５分間攪拌した。その後、濾紙（Ｎｏ．２）で濾
過し、未溶解の酢酸銀を除去した。こうして得られた溶
液に、亜硫酸ナトリウム２．０ｇ（７．９×１０^ー3モ
ル）を攪拌しながら加えた。亜硫酸ナトリウムを加えて
白く濁った溶液が透明になるまで攪拌し、その後、チオ
硫酸ナトリウム１．３２ｇ（５．３×１０^ー3モル）を加
えて攪拌し、さらにシリカゲル＜製品名「サイリシア＃
５５０」（平均粒子径２．８μｍ）：富士シリシア化学
（株）製＞５ｇを加えて、１０分間攪拌し、シリカゲル
にチオスルファト銀ナトリウム錯塩を担持させた。この
後、このチオスルファト銀ナトリウム錯塩溶液とシリカ
ゲルとの混合物をロータリーエバポレター＜製品名「ロ
ータリーエバポレターＲＥ４７」：ヤマト科学（株）製
＞に入れて温度６０℃、約３０００Ｐａ以下にて溶媒成
分を蒸発させて除去した。その後、得られたシリカゲル
を更に真空乾燥機にて温度６０℃、約３０００Ｐａ以下
のもとで１２時間真空乾燥した。Preferred embodiments of the present invention will be described below in order to further clarify the constitution and operation of the present invention described above. <1> Example (1) Preparation of antibacterial agent 60 ml of ion-exchanged water was heated to 40 ° C., and 0.464 g (2.8 × 10 ⁻³ mol) of silver acetate was added thereto to add 40 to 50.
Stir for about 5 minutes at ° C. Then, it filtered with filter paper (No. 2) and the undissolved silver acetate was removed. To the solution thus obtained, 2.0 g (7.9 × 10 ⁻³ mol) of sodium sulfite was added with stirring. Add sodium sulfite and stir until the cloudy white solution becomes clear, then add 1.32 g (5.3 × 10 ⁻³ mol) of sodium thiosulfate and stir, and further add silica gel <Product name “Sylysia #
550 "(average particle size 2.8 μm):> 5 g manufactured by Fuji Silysia Chemical Ltd. was added and stirred for 10 minutes to allow silica gel to support a sodium thiosulfato silver complex salt. Then, the mixture of this sodium thiosulfato silver complex salt solution and silica gel was placed in a rotary evaporator <Product name “Rotary evaporator RE47”: manufactured by Yamato Scientific Co., Ltd.> and a solvent component was added at a temperature of 60 ° C. and about 3000 Pa or less. It was removed by evaporation. Then, the obtained silica gel was further vacuum dried for 12 hours at a temperature of 60 ° C. and a pressure of about 3000 Pa or less by a vacuum dryer.

【００１５】こうして得られたチオスルファト銀ナトリ
ウム錯塩担持シリカゲルに、以下の方法でコーティング
を施した。まず、メチルアルコール１０ｍｌ、テトラエ
トキシシラン１０ｍｌ、上記チオスルファト銀ナトリウ
ム錯塩担持シリカゲル１０ｇ及びイオン交換水０．２ｍ
ｌを熱風乾燥機にいれて、温度７０℃、風速１ｍ／ｓ以
下にて溶媒成分の除去を行うと同時にシリカコーティン
グを施し、１２時間乾燥させ、抗菌剤を得た。この抗菌
剤は、抗菌性材料としてチオスルファト銀ナトリウム錯
塩、担体としてシリカゲルを用いているので、安全性に
優れている。The silica gel supporting the sodium thiosulfato silver complex salt thus obtained was coated by the following method. First, 10 ml of methyl alcohol, 10 ml of tetraethoxysilane, 10 g of the above-mentioned sodium thiosulfato silver complex salt-supporting silica gel and 0.2 m of ion-exchanged water.
1 was put in a hot air dryer to remove the solvent component at a temperature of 70 ° C. and a wind speed of 1 m / s or less, simultaneously with silica coating, and dried for 12 hours to obtain an antibacterial agent. This antibacterial agent is excellent in safety because it uses thiosulfato silver sodium complex salt as an antibacterial material and silica gel as a carrier.

【００１６】（２）消毒剤の調整 上記（１）で得られた抗菌剤（富士シリシア化学株式会
社製、商品名「シルウェル」）１０重量部を、流動パラ
フィン５重量部に混合し、さらにブタン８５重量部を混
合して、本実施例の消毒剤を得た。この消毒剤をスプレ
ー容器に入れてスプレー式とした。(2) Preparation of disinfectant 10 parts by weight of the antibacterial agent (manufactured by Fuji Silysia Chemical Ltd., trade name "Silwell") obtained in the above (1) was mixed with 5 parts by weight of liquid paraffin, and then butane was added. 85 parts by weight were mixed to obtain the disinfectant of this example. This disinfectant was put in a spray container to make it a spray type.

【００１７】（３）消毒剤の塗布 市販のスプレー式ガラスクリーナー（ジョンソン株式会
社製、商品名「ガラスクルー」）をプラスチック製プレ
ート＜ポリプロピレン樹脂（ＰＰ）２×３ｃｍ、厚さ１
ｍｍ＞に約３〜５秒間均一に噴霧した。その後、上記
（２）で得られたスプレー式消毒剤をプラスチック製プ
レートに約３〜５秒間均一に噴霧した。(3) Application of disinfectant A commercially available spray type glass cleaner (manufactured by Johnson Co., trade name "Glass Crew") was applied to a plastic plate <polypropylene resin (PP) 2 x 3 cm, thickness 1
mm> was uniformly sprayed for about 3-5 seconds. Then, the spray type disinfectant obtained in the above (2) was uniformly sprayed on the plastic plate for about 3 to 5 seconds.

【００１８】＜２＞ 比較例 市販のスプレー式ガラスクリーナー（ジョンソン株式会
社製、商品名「ガラスクルー」）をプラスチック製プレ
ート（ＰＰ．２×３ｃｍ、厚さ１ｍｍ）に約３〜５秒間
均一に噴霧した。<2> Comparative Example A commercially available spray type glass cleaner (manufactured by Johnson Co., trade name "Glass Crew") was uniformly applied to a plastic plate (PP.2 × 3 cm, thickness 1 mm) for about 3 to 5 seconds. Sprayed.

【００１９】［噴霧品の抗菌性試験］上記実施例でスプ
レー式消毒剤を噴霧したＰＰプレートと、比較例のＰＰ
プレートについて、以下に示す抗菌試験を行った。 （１）ドロップ法ー試料の菌液を滴下し、３７℃で２４
時間保存後、試料上の生菌数を測定するー 各種菌株を普通寒天培地（日水製薬）で３７℃、１８〜
２４時間培養後、乾燥ブイヨンを加えた減菌水［１リッ
トル蒸留水中に乾燥ブイヨン（日水製薬）０．３ｇを入
れた］に菌体を浮遊させ、約１０⁴ＣＦＵ（コロニーフ
ォーメーションユニット）／ｍｌになるように調整し
た。[Antibacterial Test of Sprayed Product] The PP plate sprayed with the spray type disinfectant in the above example and the PP of the comparative example.
The plate was subjected to the following antibacterial test. (1) Drop method-Drop the bacterial solution of the sample at 37 ° C for 24 hours
After storage for a period of time, the number of viable bacteria on the sample is measured. Various strains are cultured on ordinary agar medium (Nissui Pharmaceutical Co., Ltd.) at 37 ° C., 18-
After culturing for 24 hours, the cells were suspended in sterilized water containing dry broth [0.3 g of dry broth (Nissui Pharmaceutical Co., Ltd. was put in 1 liter distilled water), and about 10 ⁴ CFU (colony formation unit) / It was adjusted to be ml.

【００２０】本実施例及び比較例のＰＰプレート上に試
験菌液を０．２ｍｌ滴下した後、３７℃で保存した。保
存２４時間後に、滴下した菌液を別のシャーレにまい
た。この溶液中の生菌数を、普通寒天培地（日水製薬）
を用いた混釈平板培養法（３７℃、１日間）により測定
し、１ｍｌあたりのＣＦＵ値に換算した。結果を表１に
示す。After 0.2 ml of the test bacterial solution was dropped on the PP plates of this example and comparative examples, the plates were stored at 37 ° C. After 24 hours of storage, the dropped bacterial solution was spread on another petri dish. The number of viable bacteria in this solution can be calculated by using the ordinary agar medium (Nissui Pharmaceutical).
Was measured by the pour plate culture method (37 ° C., 1 day) using the above, and converted into CFU value per 1 ml. The results are shown in Table 1.

【００２１】[0021]

【表１】 [Table 1]

【００２２】表１より明らかなように、比較例のＰＰプ
レートでは、大腸菌、黄色ブドウ球菌及びＭＲＳＡがと
もに多量に繁殖しているのに対し、上記実施例のスプレ
ー式消毒剤を噴霧したＰＰプレートによれば、いずれの
菌も全く繁殖しておらず、ＰＰプレート表面を優れた効
力で殺菌していることがわかる。As is clear from Table 1, in the PP plate of the comparative example, Escherichia coli, Staphylococcus aureus and MRSA were all proliferated in large amounts, whereas the PP plate sprayed with the spray type disinfectant of the above example. According to the results, none of the bacteria propagated and the surface of the PP plate was sterilized with excellent efficacy.

【００２３】さらに、プラスチック製プレートに代え
て、ガラス板にも上記実施例のスプレー式消毒剤を適用
した結果、同様な効果が認められた。 ［抗菌性能の持続性試験］さらに、上記実施例のスプレ
ー式消毒剤と、アルコールのスプレーをＰＰプレートに
噴霧し、１日及び１週間室内で放置した後、抗菌性能を
ドロップ法で調べた。その結果を表２に示す。Further, as a result of applying the spray type disinfectant of the above-mentioned embodiment to the glass plate instead of the plastic plate, the same effect was recognized. [Continuation test of antibacterial performance] Further, after spraying the spray type disinfectant of the above-mentioned example and alcohol spray on the PP plate and left it indoors for one day and one week, the antibacterial performance was examined by the drop method. The results are shown in Table 2.

【００２４】[0024]

【表２】 [Table 2]

【００２５】表２から明らかなように、本実施例のスプ
レー式消毒剤によれば、シリカに吸着された抗菌性材料
が徐々に放出されるので、１週間経過後にも、抗菌性能
が発揮されるという持続性があった。一方、アルコール
で消毒したものは、１日で抗菌性能が低下している。従
って、本実施例のスプレー式消毒剤は、優れた抗菌性能
の持続性を有することがわかる。As is clear from Table 2, according to the spray type disinfectant of this embodiment, the antibacterial material adsorbed on silica is gradually released, so that the antibacterial performance is exhibited even after one week. There was sustainability. On the other hand, those disinfected with alcohol have a reduced antibacterial performance in one day. Therefore, it can be seen that the spray type disinfectant of this example has excellent antibacterial performance persistence.

【００２６】尚、上記実施例では、抗菌性材料として、
銀錯塩を単独で用いたが、２種以上の銀錯塩を組み合わ
せて用いることもできる。さらに、抗菌性材料として
は、銀錯塩に限らず、植物抽出物、第４級アンモニウム
塩、グルコン酸クロルヘキシジン等をそれぞれ単独で、
あるいは組み合わせて用いることができる。In the above embodiment, as the antibacterial material,
Although the silver complex salt was used alone, two or more kinds of silver complex salts may be used in combination. Further, the antibacterial material is not limited to the silver complex salt, but includes a plant extract, a quaternary ammonium salt, chlorhexidine gluconate, etc.
Alternatively, they can be used in combination.

【００２７】また、担体として、シリカゲルを用いてい
るが、所望の性質に応じて、ホワイトカーボン、気相法
シリカ、中空微小球等いずれの他の形態のシリカを適用
することもできる。さらに、上記実施例では、スプレー
式消毒剤中の抗菌剤の割合を１０重量部としたが、適用
部位、分散媒に応じて、適宜選択することができる。Although silica gel is used as the carrier, any other form of silica such as white carbon, vapor phase silica, hollow microspheres, etc. can be applied depending on the desired properties. Further, in the above-mentioned examples, the ratio of the antibacterial agent in the spray type disinfectant was set to 10 parts by weight, but it can be appropriately selected depending on the application site and the dispersion medium.

【００２８】また、抗菌剤の分散媒としては、上記流動
パラフィン、ブタン等の炭化水素系溶液に限定されず、
他の溶液または固体であってもよい。あるいは、本実施
例の消毒剤には、他の成分、例えば、洗剤、芳香剤、付
着防止剤剤、静電気防止剤等を混合してもよい。Further, the dispersion medium of the antibacterial agent is not limited to the above hydrocarbon-based solutions such as liquid paraffin and butane.
Other solutions or solids are possible. Alternatively, the disinfectant of this embodiment may be mixed with other components such as a detergent, a fragrance, an anti-adhesive agent, an antistatic agent and the like.

【００２９】さらに、塗布する方法は、スプレー式に限
られず、例えば、刷毛や布等で塗り付ける方法であって
もよい。本実施例のスプレー式消毒剤を塗布する部位と
しては、消毒したいいずれの部位にも適用可能であり、
室内の壁、ガラス窓、天井、ベッドや食器戸棚等の家
具、キッチン等が挙げられる。特に、病院内で塗布する
場合には、院内感染が防止される点で有用である。ま
た、衣類、特に病院内で使用される白衣やシーツ等にも
適用すれば、より感染防止が強化される。Further, the application method is not limited to the spray method, and may be a method of applying with a brush or cloth. The part to which the spray type disinfectant of the present embodiment is applied can be applied to any part to be disinfected,
Examples include interior walls, glass windows, ceilings, furniture such as beds and cupboards, and kitchens. In particular, when applied in a hospital, it is useful in preventing nosocomial infection. Further, when applied to clothes, especially white coats and sheets used in hospitals, infection prevention is further enhanced.

【００３０】以上本発明の実施例について説明したが、
本発明はこうした実施例に何等限定されるものではな
く、本発明の要旨を逸脱しない範囲において、種々なる
態様で実施し得ることは勿論である。The embodiment of the present invention has been described above.
The present invention is not limited to these examples, and it goes without saying that the present invention can be implemented in various modes without departing from the gist of the present invention.

【００３１】[0031]

【発明の効果】以上説明したように、本発明の抗菌剤に
よれば、持続性があるという優れた効果を奏する。As described above, according to the antibacterial agent of the present invention, the excellent effect of sustainability is exhibited.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 １種あるいは２種以上の抗菌性材料を吸
着させたシリカ表面の一部または全部をコーティング材
料で被覆した抗菌剤を主成分とすることを特徴とする消
毒剤。1. A disinfectant comprising an antibacterial agent, which is obtained by coating a part or all of the surface of silica to which one or more antibacterial materials are adsorbed with a coating material as a main component.