JPH0687299A - Method for manufacturing perspective decorative material - Google Patents

Abstract

PURPOSE:To obtain an ideally perspective material with incomparable ease of operation by applying a transparent resin layer of fine negative pattern on a transparent base to which an image is transferred and pressing thermally a lamination of a first pictorial ink layer, a solid concealing layer, a second pictorial ink layer and an adhesive layer formed on a transparent strippable varnish on a base film, as a transferrable foil, on the transparent base. CONSTITUTION:A transferrable foil 7 consists of a weakly adhesive transparent strippable varnish layer 2 formed on the entire surface of a base film 1, a first pictorial layer 3, a solid concealing layer 4 and a second pictorial layer 5 laminated sequentially on the transparent strippable varnish layer 2, and finally a transparent adhesive layer 6 formed on the entire surface of the second pictorial layer 5 or the solid concealing layer 5. In addition, on a transferrable base 9, a transparent resin layer 10 of dot or stripe-like fine negative pattern is prepared to obtain a base 8 to which data is transferred. The transferrable foil 7 is stacked on the transparent or translucent base 8 and thermally pressed. Consequently, a finished product with highly sensible design effects is obtained.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、特殊な装飾材に関し、
詳しくは透明な基材またはシートに転写された絵柄が、
該基材叉はシート側から見たものと、転写側から見たも
のとが、互いに同一または相違するものであり、また互
いに反対側の絵柄によって干渉されることなしに手前側
の絵柄だけを観察でき、さらに裏面からの光源の有無あ
るいはその光の強弱により手前側の絵柄があたかも消失
したように見えることを特徴とする透視性を有する装飾
材の製造方法に関するものである。BACKGROUND OF THE INVENTION The present invention relates to a special decorative material,
Specifically, the pattern transferred to the transparent substrate or sheet is
The material viewed from the side of the base material or the sheet and the material viewed from the transfer side are the same or different from each other, and only the design on the front side is not interfered with by the design on the opposite side. The present invention relates to a method for producing a decorative material having a see-through property, which is observable, and in which the picture on the front side looks as if it disappeared due to the presence or absence of a light source from the back surface or the intensity of the light.

【０００２】[0002]

【従来の技術】透明または半透明の基材やシートを境目
として表裏面の絵柄が異なり、裏面からの光があると手
前側の絵柄が消えたように見える装飾材は、従来より用
いられており、その意匠性の特徴からガラス窓や室内照
明器具等の装飾材や日用雑貨品として使用されており、
今後も幅広い用途への展開が可能であり、且つ期待され
ている。2. Description of the Related Art Decorative materials that have a different design on the front and back sides with a transparent or semi-transparent base material or sheet as a boundary, and appear to disappear on the front side when there is light from the back surface have been used conventionally. It is used as a decorative material such as glass windows and interior lighting fixtures and daily sundries due to its design characteristics.
It is possible and expected to be applied to a wide range of applications in the future.

【０００３】しかしながら、その製造方法として幾通り
かのものが提案されてはいるものの、未だ大きな問題を
残しているHowever, although several methods have been proposed for manufacturing the same, there still remains a big problem.

【０００４】すなわち、例えば透明叉は半透明のプラス
チックよりなる基材上に、基材に対して接着力の低い樹
脂を線状等のネガまたはポジの無地網状の微細パターン
層と、前記基材に対して接着力が強く前記微細パターン
層に対しても少なからず強い接着力を有する層と、前記
微細パターン層に対して接着力が強い白色乃至明色のイ
ンキ層と、図案絵柄等とをスクリーン印刷法またはグラ
ビア印刷法またはオフセット印刷法によりインキ層を設
け、化学的あるいは機械的処理によって前記基板と樹脂
を剥離させることにより得る製造方法がある。That is, for example, a resin having a low adhesive strength to a base material is formed on a base material made of transparent or semi-transparent plastic, and a negative or positive solid fine net pattern layer such as a linear shape, and the base material. A layer having a strong adhesive force to the fine pattern layer and a strong adhesive force to the fine pattern layer, a white to light color ink layer having a strong adhesive force to the fine pattern layer, and a pattern or the like. There is a manufacturing method in which an ink layer is provided by a screen printing method, a gravure printing method, or an offset printing method, and the resin is separated from the substrate by a chemical or mechanical treatment.

【０００５】あるいは、転写箔を用いて透明または半透
明な被転写基材に絵柄を転写して製造する場合に、転写
箔のベースフィルム上に、絵柄として、転写を必要とし
ない部分をフィルム状の剥離層として前記微細パターン
状に適宜印刷し、その上から絵柄やベタ柄を重ねて印刷
し、最後に前記フィルムの余分な部分を除去したり、前
記微細パターン状で見当を合わせを施しながら絵柄を積
層して印刷する製造方法がある。Alternatively, when a pattern is transferred onto a transparent or semi-transparent substrate to be transferred by using a transfer foil, a portion of the transfer foil which does not require transfer is formed on the base film of the transfer foil as a film. While appropriately printing on the fine pattern as a peeling layer of, the pattern or solid pattern is overlaid and printed from the top, and finally removing the excess portion of the film or while registering with the fine pattern. There is a manufacturing method in which patterns are laminated and printed.

【０００６】また、適宜隠蔽性を持たせながら絵柄、ベ
タ柄を印刷した転写箔を用いて、凹凸状の前記微細パタ
ーンのある転写ロールで転写する製造方法がある。[0006] Further, there is a manufacturing method in which a transfer foil having a pattern or a solid pattern printed thereon while appropriately concealing property is transferred by a transfer roll having the fine pattern of irregularities.

【０００７】もしくは、転写箔のベースフィルムに、該
透明または半透明なプラスチック基材に転写したときの
柄として必要のない部分を水溶性のインキで印刷し、そ
の上から絵柄やベタ柄を重ねて印刷し、最後に必要のな
い部分を水洗工程により除去する製造方法がある。Alternatively, a base film of the transfer foil is printed with a water-soluble ink on a portion which is unnecessary as a pattern when transferred to the transparent or semitransparent plastic substrate, and a pattern or a solid pattern is overlaid thereon. Then, there is a manufacturing method in which an unnecessary portion is finally removed by a water washing step.

【０００８】そして、絵柄やベタ柄を印刷し、接着層を
全面に設けた後に、必要のない部分を反応硬化性のイン
キで隠蔽し、必要のない部分を転写させない製造方法が
あり、適宜行われている。There is a manufacturing method in which a pattern or a solid pattern is printed, an adhesive layer is provided on the entire surface, and then unnecessary portions are covered with a reaction curable ink and unnecessary portions are not transferred. It is being appreciated.

【０００９】しかしながらこれらの方法は、高度な印刷
精度が要求され、且つ作業性はおろか、収率までも悪
く、他の製造方法もしくは改良された製造方法が待ち望
まれていた。However, these methods require a high degree of printing accuracy, and not only the workability but also the yield is poor, and other manufacturing methods or improved manufacturing methods have been desired.

【発明が解決しようとする課題】[Problems to be Solved by the Invention]

【００１０】本発明は、前記従来技術の問題点を鑑みて
なされたものであり、その目的とするところは、前記特
徴を持ち優れた意匠性を有する装飾材を製造するに際
し、作業性に優れ、且つ高収率をうることが可能な、生
産性の高い透視性を有する装飾材の製造方法を提供する
ことにある。The present invention has been made in view of the above-mentioned problems of the prior art, and an object thereof is to provide excellent workability in manufacturing a decorative material having the above characteristics and excellent designability. Another object of the present invention is to provide a method for manufacturing a decorative material having high productivity and high transparency, which can obtain a high yield.

【００１１】[0011]

【課題を解決するための手段】前記課題を解決するため
に、本発明は、透視性を有する装飾材の転写箔を使用し
た製造方法において、透明または半透明の被転写基材に
網状、点状、ストライプ状などからなる所望する微細ネ
ガパターン透明樹脂層を施しておき、前記転写箔として
ベースフィルム上の全面に透明剥離ニス層を備え、該剥
離ニス層上に、順に第一絵柄インキ層、ベタ隠蔽層、第
二絵柄インキ層、あるいはそのいずれかの層を積層し、
該積層体上にさらに接着剤層を積層したものを、前記被
転写基材上に重ね合わせて熱圧プレスすることにより、
転写箔を使用し該微細パターンの領域以外を前記被転写
基材上に転写することを特徴とする透視性を有する装飾
材の製造方法である。In order to solve the above-mentioned problems, the present invention provides a transparent or semitransparent transfer base material having a mesh shape and dots in a manufacturing method using a transfer foil of a transparent decorative material. , A stripe pattern, a desired fine negative pattern transparent resin layer having a stripe shape, and a transparent release varnish layer on the entire surface of the base film as the transfer foil, and the first pattern ink layer in order on the release varnish layer. , A solid hiding layer, a second pattern ink layer, or one of the layers,
By stacking an adhesive layer further laminated on the laminate and hot pressing it on the transferred substrate,
A method for producing a decorative material having transparency, which comprises transferring a portion other than the area of the fine pattern onto the substrate to be transferred using a transfer foil.

【００１２】また、実施態様として、前記ネガパターン
樹脂層は、耐熱性又は硬化性樹脂である上記の透視性を
有する装飾材の製造方法であり、ベタ隠蔽層は、ベタイ
ンキ層、蒸着層、ベタインキ層からなる上記の透視性を
有する装飾材の製造方法である。Further, as an embodiment, the negative pattern resin layer is a method for producing the above-mentioned transparent decorative material which is a heat resistant or curable resin, and the solid hiding layer is a solid ink layer, a vapor deposition layer or a solid ink. It is a method for producing the above-mentioned transparent decorative material including layers.

【００１３】[0013]

【作用】本発明の透視性を有する装飾材の製造方法は、
透明または半透明の被転写基材に網状、点状、ストライ
プ状などからなる所望する微細ネガパターン透明樹脂層
を施しておき、該被転写基材上に転写箔を熱圧プレスに
より転写するが、前記微細ネガパターン透明樹脂層には
転写箔は転写されず、微細ポジパターンが形成され、微
細ネガパターン樹脂層はそのまま残っていても透明であ
るので影響ないものである。従って、前記した従来技術
のように複雑な工程を必要とせず、転写箔に特別の処理
や転写後の処理を省くことができ、製造工程の安定化を
得ることができ、作業性に優れ、且つ高収率を得ること
を可能にすることができる。The method for producing a transparent decorative material of the present invention is
A transparent or semi-transparent transfer base material is provided with a desired fine negative pattern transparent resin layer having a mesh shape, a dot shape, a stripe shape, etc., and a transfer foil is transferred onto the transfer base material by a hot press. The transfer foil is not transferred to the fine negative pattern transparent resin layer, a fine positive pattern is formed, and even if the fine negative pattern resin layer is left as it is, it is transparent, so there is no influence. Therefore, it does not require a complicated process as in the above-mentioned conventional technique, it is possible to omit a special process or a process after transfer to the transfer foil, it is possible to obtain a stable manufacturing process, and excellent workability, In addition, it is possible to obtain a high yield.

【００１４】[0014]

【実施例】図１は、本発明ので使用する転写箔７の一実
施例であり、その構造は材質としてポリエステル、ポリ
プロピレン、ポリエチレン、ポリフェニレンサルファイ
ド、あるいはナイロン等からなるベースフィルム１があ
り、ベースフィルム１上の全面に、ベースフィルム１と
接着性が弱いバインダーとして透明な剥離ニス層２が、
例えばアクリル系樹脂からなるインキを用いて設けてあ
る。そして剥離ニス層２上には、第一絵柄層３、ベタ隠
蔽層４、および第二絵柄層５が順次設けられてあり、こ
れら第一絵柄層３、ベタ隠蔽層４、および第二絵柄層５
は通常の転写法に用いられるもので、且つ隠蔽性のある
ものがよく、材質としてはアクリル系、塩化ゴム系、塩
化ビニル系、酢酸ビニル系、塩化ビニル−酢酸ビニル共
重合系、ウレタン系、あるいはポリエステル系などを任
意に用いることができる。EXAMPLE FIG. 1 shows an example of a transfer foil 7 used in the present invention, which has a base film 1 made of polyester, polypropylene, polyethylene, polyphenylene sulfide, nylon or the like as its material. A transparent release varnish layer 2 as a binder having weak adhesion to the base film 1 is formed on the entire surface of
For example, it is provided by using an ink made of acrylic resin. A first pattern layer 3, a solid masking layer 4, and a second pattern layer 5 are sequentially provided on the peeling varnish layer 2. These first pattern layer 3, solid masking layer 4, and second pattern layer 5
Is used in a normal transfer method, and it is preferable that it has a concealing property, and as a material, an acrylic type, a chlorinated rubber type, a vinyl chloride type, a vinyl acetate type, a vinyl chloride-vinyl acetate copolymer type, a urethane type, Alternatively, a polyester type or the like can be arbitrarily used.

【００１５】また、前記の第二絵柄層５は該ベタ隠蔽層
４上の全面または１部に、グラビア印刷法、オフセット
印刷法、スクリーン印刷法、静電印刷法、あるいはイン
キジェット印刷法等の方式で設けられるものであり、そ
のデザインは文字、絵柄等に関して全く任意である。The second pattern layer 5 is formed on the entire surface or a part of the solid hiding layer 4 by a gravure printing method, an offset printing method, a screen printing method, an electrostatic printing method, an ink jet printing method, or the like. It is provided by a method, and its design is completely arbitrary with respect to characters, pictures and the like.

【００１６】そして透明接着剤層６が前記の第二絵柄層
５上またはベタ隠蔽層４上の全面に設けてある。透明接
着剤層６の材質は、転写する基材により異なるが、アク
リル系、ウレタン系、塩化ビニル−酢酸ビニル共重合体
系、ポリエステル系、エチレン酢酸ビニル系、塩化ポリ
プロピレン系等の樹脂が一般的である。A transparent adhesive layer 6 is provided on the entire surface of the second pattern layer 5 or the solid hiding layer 4. The material of the transparent adhesive layer 6 varies depending on the substrate to be transferred, but acrylic, urethane, vinyl chloride-vinyl acetate copolymer, polyester, ethylene vinyl acetate, polypropylene chloride, etc. resins are generally used. is there.

【００１７】図２は、本発明で使用する被転写基材８の
一実施例であり、ここで用いる転写可能な基材９として
は、例えばポリスチレン、ＡＳ、ＡＢＳ、ポリ塩化ビニ
ル、アクリル、ポリエチレン、ポリエチレンテレフタレ
ート、ポリプロピレン、ポリカーボネート、ポリアクリ
ロニトリル、あるいはガラス等の透明または半透明のも
のが使用できる。FIG. 2 shows an embodiment of the transferred substrate 8 used in the present invention. As the transferable substrate 9 used here, for example, polystyrene, AS, ABS, polyvinyl chloride, acryl, polyethylene is used. A transparent or translucent material such as polyethylene terephthalate, polypropylene, polycarbonate, polyacrylonitrile, or glass can be used.

【００１８】そして前記転写可能な基材９上には、所望
するように網状、点状、ストライプ状などの微細ネガパ
ターン透明樹脂層１０を作製しておき、被転写基材８を
得る。前記微細ネガパターン透明樹脂層１０の材質は、
被転写基材９や接着剤層６により異なるが、メラミン
系、ウレタン系等の熱硬化型、２液硬化型樹脂等が使用
できる。A fine negative pattern transparent resin layer 10 having a mesh shape, a dot shape, a stripe shape or the like is formed on the transferable base material 9 as desired to obtain a transfer target base material 8. The material of the fine negative pattern transparent resin layer 10 is
Although different depending on the transferred substrate 9 and the adhesive layer 6, a melamine-based or urethane-based thermosetting resin, a two-component curing resin, or the like can be used.

【００１９】図３は、透明または半透明な被転写基材８
上に転写箔７を重ね合わせて転写が施された状態を示す
ものであり、装飾材を得るまでの工程を示したものであ
る。FIG. 3 shows a transparent or semi-transparent transfer substrate 8.
It shows a state in which the transfer foil 7 is superposed on and transferred to the transfer foil, and shows the steps until the decorative material is obtained.

【００２０】[0020]

【発明の効果】本発明によると、透視性を有する装飾材
の製造方法として転写箔を使用したものであることか
ら、例えば仕切りパネル、窓ガラス、ドア等に用いる遮
光、装飾、あるいは宣伝広告に有効である。また照明器
具などに使用してその意匠性の向上、あるいはその他の
雑貨用品に対する転写絵付け等に幅広く活用できるもの
である。そしてこれらに適応する際はグラビア印刷法が
可能なため、グラビア印刷法が有する高度な印刷表現能
力により、意匠効果の高い製品を得ることができる。さ
らに本発明による製造方法は、従来の装飾性を有する遮
光パネルの製造方法と比較して、精度が良く、迅速な処
理が可能であり、そして安価でもある。結果として作業
性に優れ、且つ高収率が得られる生産性の高い製造方法
を提供することができる。According to the present invention, since a transfer foil is used as a method for producing a decorative material having a see-through property, it can be used for, for example, shading for a partition panel, a window glass, a door, a decoration, or a commercial advertisement. It is valid. Further, it can be widely used for lighting equipment and the like to improve its design and transfer painting to other miscellaneous goods. Since the gravure printing method is possible when adapting to these, a product with a high design effect can be obtained due to the high printing expression capability of the gravure printing method. Furthermore, the manufacturing method according to the present invention is more accurate, quicker in processing, and less expensive than the conventional method for manufacturing a light-shielding panel having decorative properties. As a result, it is possible to provide a highly productive manufacturing method which is excellent in workability and can provide a high yield.

【００２１】[0021]

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明で使用する転写箔７の一実地例を示す断
面説明図である。FIG. 1 is a cross-sectional explanatory view showing a practical example of a transfer foil 7 used in the present invention.

【図２】本発明で使用する被転写基材８の一実地例を示
す断面説明図である。FIG. 2 is a cross-sectional explanatory view showing a practical example of a transferred substrate 8 used in the present invention.

【図３】本発明で使用する転写箔７からの転写の一実地
例の様子を示す断面説明図である。FIG. 3 is a cross-sectional explanatory view showing a state of a practical example of transfer from the transfer foil 7 used in the present invention.

【符号の説明】[Explanation of symbols]

１…ベースフィルム ２…剥離ニス層 ３…第一絵柄層
４…ベタ隠蔽層 ５…第二絵柄層 ６…透明接着剤層
７…転写箔 ８…被転写基材 ９…被転写基材 １０…微細ネガパターン透明樹脂層DESCRIPTION OF SYMBOLS 1 ... Base film 2 ... Release varnish layer 3 ... 1st pattern layer 4 ... Solid masking layer 5 ... 2nd pattern layer 6 ... Transparent adhesive layer 7 ... Transfer foil 8 ... Transfer base material 9 ... Transfer base material 10 ... Fine negative pattern transparent resin layer

───────────────────────────────────────────────────── フロントページの続き (72)発明者 似内 保之 東京都台東区台東一丁目５番１号 凸版印 刷株式会社内 ─────────────────────────────────────────────────── ─── Continued Front Page (72) Inventor Yasuyuki Ninai 1-5-1 Taito, Taito-ku, Tokyo Toppan Printing Co., Ltd.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】透視性を有する装飾材の転写箔を使用した
製造方法において、透明または半透明の被転写基材に網
状、点状、ストライプ状などからなる所望する微細ネガ
パターン透明樹脂層を施しておき、前記転写箔としてベ
ースフィルム上の全面に透明剥離ニス層を備え、該剥離
ニス層上に、順に第一絵柄インキ層、ベタ隠蔽層、第二
絵柄インキ層、あるいはそのいずれかの層を積層し、該
積層体上にさらに接着剤層を積層したものを、前記被転
写基材上に重ね合わせて熱圧プレスすることにより、転
写箔を使用し該微細パターンの領域以外を前記被転写基
材上に転写することを特徴とする透視性を有する装飾材
の製造方法。1. A method for producing a transparent transfer material, comprising a transparent or semitransparent transfer base material, on which a desired fine negative pattern transparent resin layer having a net shape, a dot shape, a stripe shape or the like is formed. If provided, a transparent release varnish layer is provided on the entire surface of the base film as the transfer foil, and on the release varnish layer, a first pattern ink layer, a solid hiding layer, a second pattern ink layer, or any one of them is provided in this order. By laminating the layers, and further laminating an adhesive layer on the laminate, the layers are laminated on the substrate to be transferred and hot-pressed so that a transfer foil is used and a region other than the fine pattern region is formed. A method for producing a decorative material having transparency, which comprises transferring the material onto a base material to be transferred. 【請求項２】前記ネガパターン樹脂層は、耐熱性又は硬
化性樹脂であることを特徴とする請求項１記載の透視性
を有する装飾材の製造方法2. The method for producing a transparent decorative material according to claim 1, wherein the negative pattern resin layer is a heat-resistant or curable resin. 【請求項３】ベタ隠蔽層は、ベタインキ層、蒸着層、ベ
タインキ層からなることを特徴とする請求項１記載の透
視性を有する装飾材の製造方法。3. The method for producing a transparent decorative material according to claim 1, wherein the solid hiding layer comprises a solid ink layer, a vapor deposition layer, and a solid ink layer.