JPH0660824A - Method for connecting ferrite tape with pressure sensitive type double-sided adhesive sheet - Google Patents

Abstract

PURPOSE:To exhibit high strength with respect to tensile force in the longitudinal direction of ferrite and sufficiently endure with respect to peeling force in the thickness direction without separation by mating cut edges with each other over a wide range by the use of engagement structure including an uneven shape, and connecting a ferrite tape within a predetermined range inclusive of a bonded portion. CONSTITUTION:A ferrite tape Ft where a deficient point has been removed is bonded with cut ends 4a, 4b facing each other. A ferrite sheet auxiliary piece (f) made of the same material as that of the tape Ft is attached to the tape Ft on a side where no adhesive layer is not disposed. A supporting table T' is located under the tape Ft. The auxiliary piece (f) is strongly pressurized at the upper surface thereof by a trowel or roller jig while heating the auxiliary piece (f) and the bonded point. The auxiliary piece (f) is integrated with the tape Ft in such a manner as to be melted in the tape Ft. Consequently, magnetic field generated in a deflection yoke is corrected.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明はテレビ受像機やＣＲＴデ
ィスプレイ等のブラウン管に装着される偏向ヨークが発
生する磁界を補正するために用いる感圧式両面接着シー
ト付フェライトテープの接続方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for connecting a ferrite tape with a pressure-sensitive double-sided adhesive sheet used for correcting a magnetic field generated by a deflection yoke mounted on a cathode ray tube such as a television receiver or a CRT display.

【０００２】[0002]

【従来の技術】テレビ受像機やＣＲＴディスプレイ等の
ブラウン管に装着される偏向ヨークの内面にフェライト
粉を配合した合成樹脂やゴムより形成されるフェライト
シート片を貼着して磁界補正をする技術は既に公知であ
る。このようなフェライトシート片Ｆは図５に示すよう
にフェライト粉配合樹脂やフェライト粉配合ゴムを素材
としたフェライトシート片本体Ｆｓの背面に粘着剤層Ｂ
ｓを積層した構成であり、その供給形態は図６に示すよ
うに多数のフェライトシート片Ｆ，Ｆ，………を破断用
溝部ｖを介して連設した状態で提供される。2. Description of the Related Art A technique for correcting a magnetic field by sticking a ferrite sheet piece made of synthetic resin or rubber mixed with ferrite powder to the inner surface of a deflection yoke mounted on a cathode ray tube of a television receiver or a CRT display is known. It is already known. As shown in FIG. 5, such a ferrite sheet piece F has a pressure-sensitive adhesive layer B on the back surface of a ferrite sheet piece body Fs made of ferrite powder-containing resin or ferrite powder-containing rubber.
.. is provided, and the supply form thereof is provided in a state in which a large number of ferrite sheet pieces F, F, ...

【０００３】このようなフェライトシート片Ｆの連設体
の形成は次の手順によっている。先ず図７に示すように
カレンダーロール成形によって作成された幅６００ｍｍ
〜１０００ｍｍ，長さ２０ｍ〜１００ｍの広幅長尺シー
トＪの背面に感圧式両面接着シートＫを供給し、重ね合
わせ状態となった両シートを加圧ローラーＲ間を通過さ
せて両シートの積層体Ｌを作成する。次いで図８に示す
ように、このシート積層体Ｌをスリッターによって複数
本のフェライトテープＦｔ，Ｆｔ，………に分割した
後、このフェライトテープＦｔに破断用溝ｖとしてのハ
ーフカットを形成する。そして使用に際しては各フェラ
イトシート片Ｆを剥離紙Ｓから取り外して使用するもの
である。The formation of such a continuous body of ferrite sheet pieces F is performed by the following procedure. First, as shown in FIG. 7, width 600 mm created by calender roll forming
The pressure-sensitive double-sided adhesive sheet K is supplied to the back surface of the wide and long sheet J having a length of up to 1000 mm and a length of 20 m to 100 m, and the two sheets in a superposed state are passed between the pressure rollers R to form a laminate of both sheets. Create L. Next, as shown in FIG. 8, this sheet laminated body L is divided into a plurality of ferrite tapes Ft, Ft, ... By a slitter, and then half cuts as breaking grooves v are formed in the ferrite tapes Ft. In use, each ferrite sheet piece F is detached from the release paper S and used.

【０００４】ところで、感圧式両面接着シートＫとは次
のようなものを意味している。上述の説明では感圧式両
面接着シートＫの構成を粘着剤層と剥離紙との積層体で
あると説明したが、その詳細は図９に示すように、剥離
紙Ｓの表裏両面にシリコン樹脂が塗布（以下、シリコン
被膜ｃと称す）され、このシリコン被膜ｃ，ｃを間に挟
んで粘着剤層Ｂｔを積層した構成である。剥離紙Ｓ下面
のシリコン被膜ｃは多数枚の感圧式両面接着シートＫを
積段したり、ロール状に巻回する際に互いに接着しない
ようにするためのものであり、また剥離紙Ｓと粘着剤層
Ｂｔとの間のシリコン被膜ｃは粘着剤層Ｂｔから剥離紙
Ｓを離型させるために設けられている。そしてこのよう
な構成の感圧式両面接着シートＫはその上面（Ａ）を図
１０に示すようにフェライトテープ本体Ｆｍの背面に接
着させることによってフェライトテープ本体Ｆｍと一体
化し、一体化後は剥離紙Ｓを剥がすことによって露出し
た下面（Ｂ）を対象物、例えば偏向ヨークの巻線表面に
圧接させることによって当該フェライトテープ本体Ｆｍ
を巻線表面に貼着することを可能にしている。このよう
に感圧式両面接着シートＫとは上面（Ａ）と下面（Ｂ）
が共に接着機能を有するシート体を意味している。尚、
以下の説明においては、説明を理解容易にする理由から
シリコン被膜ｃを省略して説明するが、これらにおいて
もシリコン被膜ｃが存在していることが前提である。By the way, the pressure-sensitive double-sided adhesive sheet K means the following. In the above description, the structure of the pressure-sensitive double-sided adhesive sheet K has been described as a laminate of the pressure-sensitive adhesive layer and the release paper, but the details are as shown in FIG. The adhesive layer Bt is applied (hereinafter, referred to as a silicon coating c), and the silicon coatings c and c are sandwiched between the adhesive layers Bt. The silicon coating c on the lower surface of the release paper S is for preventing a number of pressure-sensitive double-sided adhesive sheets K from being stuck to each other when stacked or wound in a roll shape, and is also adhered to the release paper S. The silicon coating c between the agent layer Bt is provided to release the release paper S from the adhesive layer Bt. The pressure-sensitive double-sided adhesive sheet K having such a structure is integrated with the ferrite tape body Fm by adhering the upper surface (A) to the back surface of the ferrite tape body Fm as shown in FIG. The ferrite tape body Fm is formed by pressing the lower surface (B) exposed by peeling S onto an object, for example, the winding surface of the deflection yoke.
It is possible to attach to the winding surface. Thus, the pressure-sensitive double-sided adhesive sheet K has an upper surface (A) and a lower surface (B).
Both mean a sheet body having an adhesive function. still,
In the following description, the silicon film c is omitted for the sake of easy understanding of the description, but it is premised that the silicon film c is present also in these.

【０００５】フェライトテープＦｔは上述した手順によ
って作成されるが、フェライトテープ本体Ｆｍにはピン
ホールや傷等の不良箇所が発生することがあり、このよ
うな不良箇所の発生があったときには、この不良箇所を
除去する必要がある。フェライトテープ本体Ｆｍに破断
用溝部ｖを形成した後はフェライトテープＦｔは自動機
内にセッティングされて自動貼り工程に移るため、これ
ら不良箇所のチェックは破断用溝部ｖを形成する以前の
各段階で行われている。例えば、破断用溝部形成前のフ
ェライトテープＦｔの段階で不良箇所が発見されたとき
には図１１に示すようにフェライトテープＦｔから不良
箇所Ｇを切断除去したうえ、切断箇所を接続することが
行われている。The ferrite tape Ft is produced by the above-mentioned procedure. However, defective portions such as pinholes and scratches may occur in the ferrite tape body Fm. It is necessary to remove the defective part. After the breaking groove v is formed in the ferrite tape body Fm, the ferrite tape Ft is set in the automatic machine and moves to the automatic bonding process. Therefore, these defects are checked at each stage before the breaking groove v is formed. It is being appreciated. For example, when a defective portion is found at the stage of the ferrite tape Ft before forming the breaking groove portion, the defective portion G is cut and removed from the ferrite tape Ft as shown in FIG. 11, and then the cut portion is connected. There is.

【０００６】この接続方法としては同出願人は既に次の
ような方法を提案している。この方法は図１２で示さ
れ、その手順は、先ずフェライトテープＦｔから不良箇
所を切断除去し、その後、一方の切断端部ａ背面の剥離
紙Ｓを一部剥がしたうえ当該切断端部ａを他方の切断端
部ｂの上面に一部重ね合わせ、この重ね合わせ部分の上
から加熱したコテ状治具又はローラー状治具を押しつけ
て加圧し、当該重ね合わせ部分の厚みを周囲のフェライ
トテープＦｔの厚みと同厚になすことによって接続作業
を完了させるものである。As this connection method, the same applicant has already proposed the following method. This method is shown in FIG. 12, and the procedure is as follows. First, the defective portion is cut and removed from the ferrite tape Ft, and then the release paper S on the back surface of one of the cut ends a is partially peeled off and the cut end a is removed. A part is superposed on the upper surface of the other cut end b, and a heated iron-shaped jig or roller-shaped jig is pressed from above the superposed part to apply pressure, and the thickness of the superposed part is set to the surrounding ferrite tape Ft. The connection work is completed by making the thickness the same as the thickness.

【０００７】[0007]

【発明が解決しようとする課題】前記接続方法は簡便で
あり、且つ図１３に示すようにフェライトテープＦｔの
長手方向（Ｘ方向）への引張り力に対して比較的強い引
張り強度を有するものの、接続部分の厚み方向中間に粘
着剤層Ｂｔが介在しているために、フェライトテープＦ
ｔの厚み方向（Ｙ方向）への引き剥がし力に対しては弱
いという問題があった。偏向ヨークの磁界補正用フェラ
イトシート片は自動機によって自動貼りされた後、その
貼着位置を手作業により再調整する必要が生ずる場合が
あるが、このように貼着位置の再調整を行う際の引き剥
がし動作によりフェライトシート片が厚み方向において
分離する懸念があった。また、フェライトシート片は物
理特性に加えて当然のことながら磁気特性についても特
性が揃っていることが好ましいが、上記接続方法によっ
て得られたフェライトシート片には厚み方向中間に粘着
剤層Ｂｔが存在するため、他のフェライトシート片と特
性が揃わない問題もあった。本発明はかかる現況に鑑み
てなされたものであり、長手方向に対する引張り強度並
びに厚み方向に対する引き剥がし強度のいずれにも優
れ、加えて接続箇所の磁気特性も他の部分と同じとなす
ことができる接続方法を提供せんとするものであり、し
かも工業的利用に適した簡易な接続方法を提供せんとす
るものである。Although the connection method is simple and has a relatively strong tensile strength against the tensile force in the longitudinal direction (X direction) of the ferrite tape Ft as shown in FIG. Since the adhesive layer Bt is present in the middle of the connection portion in the thickness direction, the ferrite tape F
There is a problem that it is weak against the peeling force of t in the thickness direction (Y direction). After the ferrite sheet for magnetic field correction of the deflection yoke is automatically pasted by an automatic machine, it may be necessary to manually readjust the pasting position, but when re-adjusting the pasting position in this way, There was a concern that the ferrite sheet pieces would separate in the thickness direction due to the peeling operation. Further, it is preferable that the ferrite sheet pieces have, as a matter of course, the magnetic characteristics in addition to the physical characteristics. However, in the ferrite sheet pieces obtained by the above connecting method, the adhesive layer Bt is formed in the middle in the thickness direction. Since it exists, there is also a problem that the properties are not uniform with those of other ferrite sheet pieces. The present invention has been made in view of the current situation, and is excellent in both tensile strength in the longitudinal direction and peeling strength in the thickness direction, and in addition, the magnetic characteristics of the connection portion can be the same as those of the other portions. It is intended to provide a connection method, and yet to provide a simple connection method suitable for industrial use.

【０００８】[0008]

【課題を解決するための手段】かかる課題を解決した本
発明は、不良箇所を切断除去したときに、相対峙状態と
なる切断端縁の一方と他方が凹凸形状を含む噛み合い構
造によって密に接合するような形状となるように感圧式
両面接着シート付フェライトテープの不良箇所を切り落
とし、その後、切断端縁相互を凹凸係合により密に接合
させたうえ、フェライトテープ本体と同材質製であり且
つ前記接合部の存在範囲全体を被覆し得る大きさを有す
るフェライトシート補助片を、フェライトテープ本体に
おける粘着剤層を設けていない側に沿わせた後、当該フ
ェライトシート補助片及び接合箇所を加熱しながらフェ
ライトシート補助片に加圧力を作用させることでフェラ
イトシート補助片をフェライトテープ本体と一体化させ
ることを特徴としている。切断端縁は凹凸係合できるも
のであれば適宜採用可能であるが、例えば鋸歯状に形成
することなどが好ましい。According to the present invention, which has solved the above-mentioned problems, one and the other of the cutting edges, which are in a relative rolling state when a defective portion is cut and removed, are closely joined by a meshing structure including an uneven shape. Cut off the defective part of the ferrite tape with pressure-sensitive double-sided adhesive sheet so that it will have a shape like that, and after that, cut edges are closely joined by concave and convex engagement, and are made of the same material as the ferrite tape body and After extending the ferrite sheet auxiliary piece having a size capable of covering the entire existing range of the joint portion along the side of the ferrite tape body where the adhesive layer is not provided, heating the ferrite sheet auxiliary piece and the joint portion. However, it is characterized in that the ferrite sheet auxiliary piece is integrated with the ferrite tape body by applying a pressing force to the ferrite sheet auxiliary piece. There. The cutting edge can be appropriately used as long as it can be engaged in concave and convex, but is preferably formed in a sawtooth shape, for example.

【０００９】[0009]

【作用】本接続方法は凹凸形状を含む噛み合い構造によ
って切断端縁相互を広範囲にわたって突き合し、且つ接
合箇所を含む一定の範囲にフェライトシート補助片を溶
け込ませ侵入させることにより、フェライトテープを接
続するものであるから、接続後のフェライトテープは長
手方向への引張り力に対して強い強度を発揮するととも
に、接続部分の厚み方向中間部分に粘着剤層が介在しな
いことから、フェライトテープ厚み方向への引き剥がし
力に対しても充分耐えることができる。また接続部分の
材質は他の非接続部分の材質と同じであるから物理特性
は勿論のこと磁気特性も他の部分と揃えることができ
る。[Operation] In this connection method, the ferrite tape is connected by causing the cut edges to abut each other over a wide range by the meshing structure including the uneven shape and by allowing the ferrite sheet auxiliary piece to melt and penetrate into a certain range including the joint portion. Therefore, the ferrite tape after connection exerts strong strength against tensile force in the longitudinal direction, and since there is no adhesive layer in the middle part in the thickness direction of the connection part, It can withstand the peeling force of. Further, since the material of the connecting portion is the same as the material of the other non-connecting portion, not only the physical characteristics but also the magnetic characteristics can be matched with those of the other portions.

【００１０】[0010]

【実施例】次に本発明の詳細を図示した実施例に基づき
説明する。図１はフェライトテープＦｔからピンホール
１や傷２が存在する範囲を除去すべくフェライトテープ
Ｆｔに鋸歯状の切り込み３ａ，３ｂを入れた様子を示し
ている。不良箇所Ｇを囲む切り込み３ａ，３ｂはフェラ
イトテープ本体Ｆｍ、粘着剤層Ｂｔ及び剥離紙Ｓを貫通
して形成されている。また鋸歯状の切り込み３ａ，３ｂ
は同じ形状であり、当該切り込み３ａ，３ｂによって形
成される切断端縁４ａ，４ｂが噛み合い構造によって密
に接合するようにしている。DESCRIPTION OF THE PREFERRED EMBODIMENTS The details of the present invention will be described below with reference to illustrated embodiments. FIG. 1 shows a state where serrated cuts 3a and 3b are made in the ferrite tape Ft in order to remove the area where the pinhole 1 and the scratch 2 exist from the ferrite tape Ft. The notches 3a and 3b surrounding the defective portion G are formed through the ferrite tape body Fm, the adhesive layer Bt, and the release paper S. In addition, sawtooth-shaped cuts 3a and 3b
Have the same shape, and cut edges 4a and 4b formed by the cuts 3a and 3b are closely joined by a meshing structure.

【００１１】図２はフェライトテープＦｔから不良箇所
Ｇを除去した段階から、接続が完了するまでの各段階を
簡略に示したものである。先ず不良箇所が除去されたフ
ェライトテープＦｔは相対峙状態となった切断端縁４
ａ，４ｂが端縁を突き合わした状態で接合される。切断
端縁４ａ，４ｂは互いに噛み合うように形成されている
ので、切断端縁４ａ，４ｂはその端縁全体が相手側と密
に接触する。次いでフェライトテープＦｔと同材質のフ
ェライトシート補助片ｆを、フェライトテープＦｔにお
ける粘着剤層を設けていない側から沿わせる。このフェ
ライトシート補助片ｆはフェライトシート補助片ｆと略
同幅であり、且つその大きさは接合部が存在する範囲全
体を被覆し得る大きさに設定されている。続いてフェラ
イトテープＦｔの下面に支持台Ｔ´を設置したうえ、フ
ェライトシート補助片及び接合箇所を加熱しながらフェ
ライトシート補助片ｆ上面からコテ状治具あるいはロー
ラー状治具を押し当てて強い力で加圧し、フェライトシ
ート補助片ｆをフェライトテープＦｔに溶かし込むよう
にしてフェライトシート補助片ｆをフェライトテープＦ
ｔと一体化するものである。一体化後は、接合箇所のフ
ェライトテープＦｔの厚みは他の部分の厚みと同厚にな
り、また突き合わせ状態となっていた切断端縁はフェラ
イトテープＦｔ自体の軟化現象並びにフェライトシート
補助片ｆの溶け込み現象によりほぼ消え去る。このよう
にして一体化したフェライトテープＦｔはその断面構造
においてもわかるように、接続箇所においてフェライト
テープ本体Ｆｍ及び粘着剤層Ｂｔはそれぞれ連続した状
態となる。また粘着剤層Ｂｔは本来の存在箇所であるフ
ェライトテープ本体Ｆｍ下面にのみ存在する構造となる
から、接続箇所の磁気特性は他の部分と同じにすること
ができ、且つフェライトテープ本体Ｆｍの厚み方向中間
に粘着剤層が介在しないことから接続箇所にフェライト
テープＦｔの厚み方向への比較的強い引き剥がし力が作
用した場合でも分離することなく充分耐えることができ
る。また、切断端縁を鋸歯状となし、この鋸歯状の切断
端縁同士を噛み合わせて密に接合させていることから、
切断端縁同士の接触面積を広くできることに加えてその
凹凸形状によって切断端縁に作用する引張り力を多方向
へ分散させることができるので、フェライトテープＦｔ
に長手方向の引張り力が作用した場合でも分離すること
なく充分耐えることができる。FIG. 2 schematically shows each step from the step of removing the defective portion G from the ferrite tape Ft to the completion of the connection. First, the ferrite tape Ft from which the defective portion has been removed is the cutting edge 4 which is in the relative rolling state.
The a and 4b are joined with their edges abutted against each other. Since the cutting edges 4a and 4b are formed so as to mesh with each other, the entire cutting edges 4a and 4b are in close contact with the other side. Next, a ferrite sheet auxiliary piece f of the same material as the ferrite tape Ft is placed along the side of the ferrite tape Ft where the adhesive layer is not provided. The ferrite sheet auxiliary piece f has substantially the same width as the ferrite sheet auxiliary piece f, and the size thereof is set to a size capable of covering the entire range where the joint portion exists. Subsequently, a support base T'is set on the lower surface of the ferrite tape Ft, and a trowel-shaped jig or a roller-shaped jig is pressed against the upper surface of the ferrite sheet auxiliary piece f while heating the ferrite sheet auxiliary piece and the joining portion to apply a strong force. The ferrite sheet auxiliary piece f is melted into the ferrite tape Ft by pressurizing with
It is integrated with t. After the integration, the thickness of the ferrite tape Ft at the joining portion becomes the same as the thickness of the other portions, and the cut edges that are in the butted state are the softening phenomenon of the ferrite tape Ft itself and the ferrite sheet auxiliary piece f. It almost disappears due to the phenomenon of melting. As can be seen from the sectional structure of the ferrite tape Ft integrated in this way, the ferrite tape body Fm and the adhesive layer Bt are in a continuous state at the connection points. Further, since the adhesive layer Bt has a structure that exists only on the lower surface of the ferrite tape body Fm, which is the original location, the magnetic characteristics at the connection location can be made the same as the other portions, and the thickness of the ferrite tape body Fm can be the same. Since the pressure-sensitive adhesive layer is not interposed in the middle of the direction, even if a relatively strong peeling force in the thickness direction of the ferrite tape Ft acts on the connection point, it can sufficiently endure without being separated. Further, since the cutting edges are formed in a sawtooth shape and the sawtooth cutting edges are meshed with each other to be closely joined,
Since the contact area between the cutting edges can be widened and the tensile force acting on the cutting edges can be dispersed in multiple directions due to the uneven shape, the ferrite tape Ft
Even if a tensile force in the longitudinal direction is applied to it, it can sufficiently withstand without separation.

【００１２】上記した実施例ではフェライトテープＦｔ
を下面で支える支持台Ｔ´は剥離紙Ｓの背後から押し当
てたが、図３に示すように剥離紙Ｓを一部剥がしたう
え、粘着剤層Ｂｔの下面に直接押し当ててもよい。In the above embodiment, the ferrite tape Ft
Although the support base T'supporting the bottom surface of the pressure sensitive adhesive sheet is pressed from behind the release paper S, the release paper S may be partially peeled off as shown in FIG. 3 and then directly pressed to the lower surface of the adhesive layer Bt.

【００１３】図４はフェライトテープＦｔに形成する切
り込みの他の例であり、切り込みによって分離された不
良箇所を除去した後、切断端縁４ａ，４ｂを突き合わせ
た状態を示している。切り込みの形状は切断除去によっ
て相対峙状態となる切断端縁の一方と他方が凹凸形状を
含む噛み合い構造によって密に接合し得るものであれば
適宜採用可能であり、（イ),（ロ),（ハ）として示すも
のやその他種々のものが採用できる。FIG. 4 shows another example of a notch formed in the ferrite tape Ft, and shows a state in which the cut edges 4a and 4b are butted after removing the defective portion separated by the notch. The shape of the notch can be appropriately adopted as long as one and the other of the cutting edges that are brought into a relative state by cutting and removal can be closely joined by a meshing structure including an uneven shape, (a), (b), Those shown as (C) and other various types can be adopted.

【００１４】[0014]

【発明の効果】本発明の感圧式両面接着シート付フェラ
イトテープの接続方法は、凹凸形状を含む噛み合い構造
によって切断端縁相互を広範囲にわたって突き合し、且
つ接合箇所を含む一定の範囲にフェライトシート補助片
を加熱加圧することによって溶け込ませ侵入させること
により、フェライトテープを接続するものであるから、
接続後のフェライトテープは長手方向への引張り力に対
して強い強度を発揮するとともに、接続部分の厚み方向
中間部分に粘着剤層が介在しないことから、フェライト
テープ厚み方向への引き剥がし力に対しても分離するこ
となく充分耐えることができる。また接続部分の材質は
他の非接続部分の材質と同じであるから物理特性は勿論
のこと磁気特性も他の部分と揃えることができる。しか
も本接続方法は切断端縁を突き合わした部分の上にフェ
ライトシート補助片を加熱状態で押しつけるだけで完了
するから、その作業が簡単で工業的に利用しやすい。According to the method of connecting the ferrite tape with pressure-sensitive double-sided adhesive sheet of the present invention, the cutting edges are widely abutted with each other in a wide range by the meshing structure including the uneven shape, and the ferrite sheet is included in a certain range including the joint portion. The ferrite tape is connected by allowing the auxiliary piece to melt and infiltrate by heating and pressurizing it,
The ferrite tape after connection exhibits strong strength against tensile force in the longitudinal direction, and since there is no adhesive layer in the middle part in the thickness direction of the connection part, it can resist peeling force in the thickness direction of the ferrite tape. However, it can endure without separation. Further, since the material of the connecting portion is the same as the material of the other non-connecting portion, not only the physical characteristics but also the magnetic characteristics can be matched with those of the other portions. Moreover, the present connecting method is completed by simply pressing the ferrite sheet auxiliary piece on the portion where the cut edges are butted against each other in a heated state, so that the work is simple and industrially applicable.

【図面の簡単な説明】[Brief description of drawings]

【図１】 本発明の１実施例を示し、フェライトテープ
上の不良箇所の存在範囲を囲む部分に鋸歯状の切り込み
を入れた状態であり、（イ）は平面図、（ロ）は断面図
である。FIG. 1 shows an embodiment of the present invention, showing a state in which a sawtooth-shaped cut is made in a portion surrounding a region where a defective portion exists on a ferrite tape, (a) is a plan view, and (b) is a sectional view. Is.

【図２】 同実施例において、フェライトテープから不
良箇所を除去した段階から、接続が完了するまでの各段
階を示した簡略説明図。FIG. 2 is a simplified explanatory view showing each step from the step of removing the defective portion from the ferrite tape to the completion of connection in the embodiment.

【図３】 本発明の他の実施例であり、支持台Ｔ´を粘
着剤層Ｂｔの下面に直接押し当てることによってフェラ
イトテープを支えた場合の断面説明図FIG. 3 is another embodiment of the present invention, and is a cross-sectional explanatory view of a case where a ferrite tape is supported by directly pressing a support base T ′ against the lower surface of the adhesive layer Bt.

【図４】 （イ),（ロ),（ハ）はフェライトテープに形
成する切り込みの他の例であり、切り込みによって分離
された不良箇所を除去した後、切断端縁を突き合わせた
状態を示している。[Fig. 4] (a), (b) and (c) are other examples of the notches formed in the ferrite tape, showing a state where the cut edges are butted after removing the defective portions separated by the notches. ing.

【図５】 フェライトシート片の外観を示す説明用斜視
図。FIG. 5 is an explanatory perspective view showing an appearance of a ferrite sheet piece.

【図６】 破断用溝部を形成したフェライトテープを示
す説明用斜視図。FIG. 6 is an explanatory perspective view showing a ferrite tape having a breaking groove formed therein.

【図７】 ロール状に巻回した広幅長尺フェライトシー
トと感圧式両面接着シートとを積層する工程の説明図。FIG. 7 is an explanatory view of a process of laminating a wide and long ferrite sheet wound in a roll shape and a pressure-sensitive double-sided adhesive sheet.

【図８】 広幅長尺フェライトシートと感圧式両面接着
シートとの積層体から破断用溝部が形成されたフェライ
トテープが形成されるまでの各工程を示す説明図。FIG. 8 is an explanatory view showing each process from the laminate of the wide and long ferrite sheet and the pressure-sensitive double-sided adhesive sheet to the formation of the ferrite tape having the breaking groove.

【図９】 感圧式両面接着シートの構造を示す断面説明
図。FIG. 9 is a cross-sectional explanatory view showing the structure of a pressure-sensitive double-sided adhesive sheet.

【図１０】 感圧式両面接着シートを積層したフェライ
トテープの構造を示す断面説明図。FIG. 10 is an explanatory sectional view showing the structure of a ferrite tape in which pressure-sensitive double-sided adhesive sheets are laminated.

【図１１】 フェライトテープから不良箇所を除去する
様子を示す説明図。FIG. 11 is an explanatory diagram showing how defective parts are removed from the ferrite tape.

【図１２】 従来のフェライトテープの接続方法を示す
工程説明図。FIG. 12 is a process explanatory view showing a conventional ferrite tape connecting method.

【図１３】 従来のフェライトテープの接続方法の問題
点を指摘した断面説明図。FIG. 13 is an explanatory cross-sectional view that points out a problem of a conventional ferrite tape connecting method.

【符号の説明】[Explanation of symbols]

Ｆ フェライトシート片 Ｆｓ フェライトシート片本体 Ｂｓ 粘着剤層 ｖ 破断用溝部 Ｊ 広幅長尺シート Ｋ 感圧式両面接着シート Ｌ 両シートの積層体 Ｒ 加圧ローラー Ｆｔ フェライトテープ Ｓ 剥離紙 ｃ シリコン被膜 Ｂｔ 粘着剤層 Ｆｍ フェライトテープ本体 Ｇ 不良箇所 ａ 切断端部 ｂ 切断端部 １ ピンホール ２ 傷 ３ａ 切り込み ３ｂ 切り込み ４ａ 切断端縁 ４ｂ 切断端縁 Ｔ 加圧治具 Ｔ´ 支持台 ｆ フェライトシート補助片 F Ferrite sheet piece Fs Ferrite sheet piece body Bs Adhesive layer v Breaking groove J Wide and long sheet K Pressure sensitive double-sided adhesive sheet L Both sheet laminate R Pressure roller Ft Ferrite tape S Release paper c Silicon coating Bt Adhesive Layer Fm Ferrite tape body G Defective part a Cutting edge b Cutting edge 1 Pinhole 2 Scratch 3a Notch 3b Notch 4a Cutting edge 4b Cutting edge T Pressing jig T ′ Support stand f Ferrite sheet auxiliary piece

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 フェライト粉配合樹脂又はフェライト粉
配合ゴムで作成したフェライトテープ本体の裏面に感圧
式両面接着テープを積層して構成した感圧式両面接着シ
ート付フェライトテープから不良部分を切断除去し、そ
の後切断箇所を接続する感圧式両面接着シート付フェラ
イトテープの接続方法において、 不良箇所を切断除去したときに、相対峙状態となる切断
端縁の一方と他方が凹凸形状を含む噛み合い構造によっ
て密に接合するような形状となるように感圧式両面接着
シート付フェライトテープの不良箇所を切り落とし、そ
の後、切断端縁相互を凹凸係合により密に接合させたう
え、フェライトテープ本体と同材質製であり且つ前記接
合部の存在範囲全体を被覆し得る大きさを有するフェラ
イトシート補助片を、フェライトテープ本体における粘
着剤層を設けていない側に沿わせた後、当該フェライト
シート補助片及び接合箇所を加熱しながらフェライトシ
ート補助片に加圧力を作用させることでフェライトシー
ト補助片をフェライトテープ本体と一体化させることを
特徴とする感圧式両面接着シート付フェライトテープの
接続方法。1. A defective portion is cut and removed from a ferrite tape with a pressure-sensitive double-sided adhesive sheet, which is formed by laminating a pressure-sensitive double-sided adhesive tape on the back surface of a ferrite tape main body made of ferrite powder-containing resin or ferrite powder-containing rubber, After that, in the method of connecting the ferrite tape with pressure-sensitive double-sided adhesive sheet that connects the cut points, when the defective points are cut and removed, one and the other of the cut edges are in close contact with each other due to the meshing structure including the uneven shape. The defective part of the ferrite tape with pressure-sensitive double-sided adhesive sheet is cut off so that it will have a shape to be joined, and then the cut edges are closely joined by concave and convex engagement, and made of the same material as the ferrite tape body. In addition, a ferrite sheet auxiliary piece having a size capable of covering the entire existing range of the above-mentioned joint portion is used as a ferrite tape. The ferrite sheet auxiliary piece is integrated with the ferrite tape main body by applying a pressure to the ferrite sheet auxiliary piece while heating the ferrite sheet auxiliary piece and the joint portion after the side of the body where the adhesive layer is not provided. A method for connecting ferrite tape with pressure-sensitive double-sided adhesive sheet, which is characterized by 【請求項２】 切断端縁の形状を鋸歯状に形成してなる
請求項１記載の感圧式両面接着シート付フェライトテー
プの接続方法。2. The method for connecting a ferrite tape with a pressure-sensitive double-sided adhesive sheet according to claim 1, wherein the cut edges are formed in a sawtooth shape.