JPH0647486A - Casting method for casted product utilizing master pattern and lost foam model - Google Patents

Abstract

PURPOSE:To obtain an original or a little quantity of casting products by effectively utilizing a permanent master pattern as a basic form and a lost foam model made of a lost foam member as an original form. CONSTITUTION:In a cope flask and a drag flask, by utilizing a molding flask manufactured in the following processes, casting is executed. These processes are constituted with a pattern making process for shielding the master pattern 3 laid on the upper surface of a vacuum suction box table with a film sheet and laying the lost foam model 5 on this, a sand filling process for shielding this pattern with molding sand 7, a sand mold making process for laying the film sheet on the upper surface of the sand mold original form A constituted with the sand filling and fastening the sand by suction through a vacuum box and a process for manufacturing the molding flask for casting. By this method, the casting product providing sharp outer-line and having fine design, pattern, letter, etc., can be obtd. with a simple method.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、基本形態をなす、例え
ば、門扉、プレート、機械フレーム等の木枠、樹脂型、
鋳造型等でなる恒久的なマスターパターンと、独自形態
をなす、例えば、ネーム、家紋、図柄、その他模様、付
属部品等の消失性部材でなる（消失特性を有する）消失
性モデルと、を有効利用して独自又は少量の鋳造製品を
得ることができる鋳造方法に関するものである。BACKGROUND OF THE INVENTION The present invention has a basic form, for example, a gate, a plate, a wooden frame such as a machine frame, a resin mold,
A permanent master pattern made of a casting mold or the like, and a unique form, for example, a vanishing model (having vanishing characteristics) made up of vanishing members such as names, family crests, designs, other patterns, and accessories are effective. The present invention relates to a casting method that can be utilized to obtain a unique or small amount of a cast product.

【０００２】[0002]

【従来の技術】従来鋳造模型を生成するためには、多く
の工程とか、装置並びに機械を使用していることから、
少量生産には不向きなものであった。但し、コスト並び
に能率の優劣を問わない場合は、原則として問題はな
い。2. Description of the Related Art Conventionally, many processes, devices and machines are used to produce a cast model.
It was not suitable for small-scale production. However, there is no problem in principle, regardless of cost or efficiency.

【０００３】しかしながら、通常の大量並びに低コスト
化を思考する鋳造製品には、些か問題無しとは云えない
処である。However, it cannot be said that there is no problem in the case of casting products which are usually considered for mass production and cost reduction.

【０００４】また同様に各人の趣味並びに目的、装飾観
に合致した鋳造製品、又は各社の名入り表札並びに各店
の名入り表札等の用途又は目的に合致した、いわゆる個
別の鋳造製品を生成するに際しては、それぞれ個々に鋳
造模型を生成することを要し、大変な手間・暇等を要す
るとともに、能率が劣るなどの課題がある。また採算ベ
ースに合わない等の経済的な課題も、当然考えられる処
である。[0004] Similarly, a cast product that matches the hobby, purpose and decoration of each person, or a so-called individual cast product that matches the use or purpose of the nameplate of each company and the nameplate of each store, etc. In this case, it is necessary to generate cast models individually, which requires a great deal of labor and time, and there is a problem that efficiency is poor. Moreover, economic problems such as not meeting the profit base are naturally conceivable.

【０００５】以上の少量生産に於ける課題を解決するた
めの技術文献として、例えば、特公昭５８−３７８３号
の鋳造製親柱、束柱等への模様形成方法があり、この特
許発明は、親柱、束柱の形状を有する中子に、有機溶剤
又は加熱体等で溶解しつつ、一定模様を形成できる発泡
スチロール体を貼着して、この発泡スチロールの表面に
各種柄又は模様等（以下、単に模様とする。）を設けこ
とと、この模様並びに欄干用中子とを介して鋳型に、前
記模様入りとする欄干鋳造の造型を形成する方法であ
る。As a technical document for solving the problems in the above-mentioned small-scale production, for example, there is a pattern forming method on a cast master pillar, a bundle pillar, etc. of Japanese Patent Publication No. 58-3783. Parent pillar, a core having the shape of a bundle pillar, while being dissolved with an organic solvent or a heating body, a styrofoam body that can form a fixed pattern is attached, and various patterns or patterns on the surface of the styrofoam (hereinafter, A pattern) is provided, and a molding of the balustrade casting having the pattern is formed in the mold through the pattern and the balustrade core.

【０００６】[0006]

【発明が解決しようとする課題】前記特許発明は、確か
に発泡スチロール表面に適宜の模様を付すことにより、
種々の模様の欄干が鋳造される。SUMMARY OF THE INVENTION The above-mentioned patented invention is surely provided with an appropriate pattern on the styrofoam surface,
Parapets with various patterns are cast.

【０００７】しかしながら、この鋳型砂中から、この発
泡スチロール付き欄干用中子を取り出す（離型）に際し
て、これを収縮する必要があり、正確で、かつ細い模様
等を有する造型には難点があることと、工程が複雑にな
ること等の課題が考えられる。However, when the balustrade core with styrofoam is taken out (mold release) from the mold sand, it is necessary to shrink it, and there is a difficulty in molding with an accurate and thin pattern. Therefore, problems such as complicated process can be considered.

【０００８】また鋳型砂の硬化速度と、砂粘結剤の発泡
スチロール反応速度とを、時間的にずらす必要があり、
熟練と、時間的な管理等が要求され実用面で多くの課題
が考えられる。Further, it is necessary to temporally shift the hardening rate of the mold sand and the styrofoam reaction rate of the sand binder,
Skills and time management are required, and many practical problems are possible.

【０００９】また従来の消失性模型（消失性モデル）を
フイルムシートで、隠蔽する鋳造方法では、シャープな
外郭線（外郭輪郭線）が形成されず、美麗な図柄、又は
模様が鋳造できない課題がある。また極めて小さい隙間
を備えた鋳造製品を得る場合には、これらの形状維持又
は鋳造に際して、多くの難点が考えられる。Further, in the conventional casting method in which the disappearance model (disappearance model) is concealed with a film sheet, a sharp outline (outer outline) is not formed, and a beautiful pattern or pattern cannot be cast. is there. Further, when obtaining a cast product having an extremely small gap, many difficulties can be considered in maintaining the shape or casting.

【００１０】一方機械フレームに、オブションにより各
付属部品を付設する場合においても、従来の一体化方式
の鋳造製品模型を利用する鋳造方法では、前述と同様な
課題が考えられる。On the other hand, even when each accessory is attached to the machine frame by an option, the same problem as described above can be considered in the conventional casting method using the cast product model of the integrated system.

【００１１】[0011]

【課題を解決するための手段】上記に鑑み、本発明は、
消失性モデルと鋳造砂の特性及びＶプロセスとを有効利
用して、独自性、少量生産性を備え、かつ美麗な形状及
び立上壁、又は文字を備えるシャープな外郭線等を発揮
できる鋳造製品を得るために、下記に構成を採用する。In view of the above, the present invention provides
Cast products that have uniqueness, small-quantity productivity, and beautiful shapes and rising walls, or sharp outlines with letters, etc., by effectively utilizing the vanishability model, casting sand characteristics, and V process In order to obtain, the configuration is adopted below.

【００１２】即ち、本発明のマスターパターンと消失性
モデルとを利用して鋳造製品を得る鋳造方法は、少なく
とも上型枠又は下型枠のいずれか一方に、下記の型枠を
利用して鋳造製品を鋳造する方法であって、この型枠
は、下記のように構成される。That is, the casting method for obtaining a cast product using the master pattern and the disappearance model of the present invention is a casting method using at least one of the upper mold and the lower mold using the following mold. A method of casting a product, the form having the following construction.

【００１３】（１）真空吸引ボックス台上面に載置され
たマスターパターンを、フィルムシートで隠蔽した後、
当該フイルムシート上に消失性モデルを載置する鋳造製
品模型生成工程と、この鋳造製品模型生成工程で形成さ
れた鋳造製品模型を、鋳造砂で隠蔽する鋳造砂充填工程
と、この鋳造砂充填工程を介して構成された砂型原型の
上面にフルムシートを載置し、前記真空ボックスを介し
ての吸引により、前記鋳造砂を固める砂型製造工程と、
この砂型製造工程で製造された砂型より前記マスターパ
ターンを取り外し、前記砂型内に消失性モデルが残った
鋳造用型枠を製造する型枠製造工程と、で構成される。(1) After concealing the master pattern placed on the upper surface of the vacuum suction box base with a film sheet,
Casting product model generation step of placing the disappearance model on the film sheet, casting sand filling step of concealing the casting product model formed in this casting product model generation step with casting sand, and this casting sand filling step Placing a flume sheet on the upper surface of the sand mold prototype configured through, by suction through the vacuum box, a sand mold manufacturing step of hardening the casting sand,
A mold manufacturing process of removing the master pattern from the sand mold manufactured in this sand mold manufacturing process to manufacture a casting mold in which the disappearance model remains in the sand mold.

【００１４】[0014]

【作用】以下、本発明の作用（型枠の製造方法）を説明
する。The function of the present invention (method for manufacturing the form) will be described below.

【００１５】先ず、図１に示す真空吸引ボックスの台上
面にマスターパターンを載置する（図２参照）。その
後、真空吸引ボックス及びマスターパターンを加熱処理
したフィルムシートを介して隠蔽する。即ち、真空吸引
ボックスの台上面及びマスターパターンの露出外郭部位
面にそって加熱フィルムシートを延展する（図３）。First, a master pattern is placed on the table top of the vacuum suction box shown in FIG. 1 (see FIG. 2). Then, the vacuum suction box and the master pattern are concealed through the heat-treated film sheet. That is, the heating film sheet is extended along the upper surface of the vacuum suction box and the exposed outer surface of the master pattern (FIG. 3).

【００１６】そして、この真空吸引を介して、前記フィ
ルムシートを、真空吸引ボックスの台上面及びマスター
パターンの露出外郭部位面に吸着一体化させる（図４参
照）。Then, the film sheet is sucked and integrated with the base surface of the vacuum suction box and the exposed outer surface of the master pattern through the vacuum suction (see FIG. 4).

【００１７】続いて、真空吸引ボックスの台上面及びマ
スターパターンの露出外郭部位面に吸着されたフィルム
シート上で、かつマスターパターンを囲繞するようにし
て枠体を載置する（図５参照））。但し、後述する消失
性モデルを、先に配備することもあり得る。Then, a frame is placed on the film sheet adsorbed on the upper surface of the vacuum suction box and the exposed outer surface of the master pattern, and so as to surround the master pattern (see FIG. 5). . However, the disappearance model described later may be deployed first.

【００１８】以上のようにして、フィルムシート上に枠
体が載置されたならば、フィルムシートで隠蔽されてい
る前記マスターパターンの適所に、例えば、接着手段等
を介設して、消失性モデルを一個又は数個（本発明で
は、この数個に、多数個を含む概念である。）載置する
（図６参照）。但し、後述する鋳造砂を一部充填する場
合もあり得る。When the frame is placed on the film sheet as described above, the disappearance is achieved by providing, for example, an adhesive means at an appropriate position of the master pattern hidden by the film sheet. One or several models (in the present invention, a concept including many in this number) are placed (see FIG. 6). However, it may be possible to partially fill the casting sand described below.

【００１９】このようにして、当該フィルムシートで隠
蔽されている前記マスターパターンの上に、消失性モデ
ルが載置された段階で（鋳造製品模型生成工程の終了時
である。）、この枠体内に（鋳造製品模型を隠蔽するよ
うに）、順次鋳造砂を充填し、当該枠体内への鋳造砂の
充填作業を完了する（図７参照）。In this way, at the stage when the vanishing model is placed on the master pattern hidden by the film sheet (at the end of the cast product model generation step), the frame body is formed. Then (to hide the cast product model), the casting sand is sequentially filled, and the filling operation of the casting sand into the frame is completed (see FIG. 7).

【００２０】その後、枠体及び鋳造砂の上面にフィルム
シートを延展し（図８参照）、かつ真空吸引ボックスの
真空吸引を介して、枠体内に充填されている鋳造砂を固
めると、ここに、砂型原型が構成される（図９参照）。
そこで、続いて、前記真空吸引作業を停止する。これに
よって、砂型が製造される（図１０参照）。After that, the film sheet is spread on the upper surface of the frame and the casting sand (see FIG. 8), and the casting sand filled in the frame is solidified through the vacuum suction of the vacuum suction box. , A sand mold prototype is constructed (see FIG. 9).
Therefore, subsequently, the vacuum suction work is stopped. This produces a sand mold (see FIG. 10).

【００２１】以上のようにして、砂型が製造された後
は、真空吸引ボックスより砂型を取り外し、例えば、適
宜の台上に砂型を反転等して載置する（図１０参照）。
そして、次いで、マスターパターンを砂型より取り外す
と、砂型内に消失性モデルが残り、かつ空洞部（前記マ
スターパターンと同じ形状の空洞である。）を有する型
枠が構成される（図１１参照）。After the sand mold is manufactured as described above, the sand mold is removed from the vacuum suction box and, for example, the sand mold is inverted and placed on a suitable table (see FIG. 10).
Then, when the master pattern is removed from the sand mold, a disappearing model remains in the sand mold and a mold having a cavity (a cavity having the same shape as the master pattern) is formed (see FIG. 11). .

【００２２】そこで、この図例では、前記型枠を下型枠
として利用するとともに、前記空洞部に連通した湯道を
設け、かつ下型枠の上面に、上型枠を合体する（図１２
参照）。この合体作業を介して、合体型枠が構成される
ので、以後は、従来と同様な鋳造方法を介して鋳造製
品、例えば、図１３に示す表札、プレート等の鋳造製品
が鋳造される。Therefore, in this example, the mold is used as a lower mold, a runner communicating with the cavity is provided, and the upper mold is joined to the upper surface of the lower mold (FIG. 12).
reference). Since the united mold is constructed through this uniting operation, the cast product, for example, the cast product such as the nameplate and plate shown in FIG. 13 is cast afterward by the casting method similar to the conventional one.

【００２３】尚、前述の例では、下型枠にマスターパタ
ーンによる空洞部と消失性モデルが残留する型枠を使用
し、上型枠にむくの砂型よりなる型枠（いわゆる、型枠
内の全体に、鋳造砂が充填されている形態を云う。）を
使用して鋳造製品を得る方法を説明しましたが、その他
の方法でも可能であり、例えば、上型枠をマスターパタ
ーンによる空洞部と消失性モデルが残留する型枠、マス
ターパターンによる空洞部のみでなる型枠、更には在来
の方式の他の型枠等（上型枠の前記種類を、以下、単に
各種型枠構造とする。）に置き換えることも可能であ
る。In the above-mentioned example, the lower mold is a mold in which the voids due to the master pattern and the vanishing model remain, and the upper mold is a sand mold (so-called in the mold). We have described the method of obtaining a casting product by using casting sand filled in the whole.), But other methods are also possible, for example, the upper formwork and the cavity part by the master pattern. Formwork in which the vanishing model remains, formwork consisting only of cavities by the master pattern, and other formwork of the conventional method (the above type of upper formwork is simply referred to as various formwork structures hereinafter. .) Can also be substituted.

【００２４】同様に、図示しないが、上型枠にマスター
パターンによる空洞部と消失性モデルが残留する型枠を
使用し、下型枠に前記各種型枠構造を採用することも可
能である。Similarly, although not shown, it is also possible to use a mold in which the cavity part by the master pattern and the disappearance model remain in the upper mold, and to adopt the above-mentioned various mold structures in the lower mold.

【００２５】[0025]

【実施例】以下、本発明の一実施例を図面に基づいて説
明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described below with reference to the drawings.

【００２６】減圧ホース１が付設された真空吸引ボック
ス２の台上面２ａには、木型、鋳物型、樹脂型、その他
空洞部形成部材等抜き型として機能し、通常、鋳造製品
の基本パターンとなるマスターパターン３が載置され
る。そして、このマスターパターン３は、抜き勾配を備
えた構造となっている。The table top surface 2a of the vacuum suction box 2 provided with the decompression hose 1 functions as a die for a wooden mold, a casting mold, a resin mold, other cavity forming members, etc., and usually has a basic pattern of a cast product. The master pattern 3 is placed. The master pattern 3 has a structure with a draft.

【００２７】尚、マスターパターン３の具体例を挙げる
と、原則として、基本形態の門扉、プレート、置き物、
記念品、モニュメント、機械フレーム等であり、大量生
産方式で採用されるものが理想である。Incidentally, to give a concrete example of the master pattern 3, in principle, a gate, a plate, a tableware,
Ideal for souvenirs, monuments, machine frames, etc., which are used in mass production.

【００２８】そして、このマスターパターン３と後述す
る鋳造砂及び消失性モデルとを完全に区画するために、
前記台上面２ａ及びマスターパターン３上には、加熱フ
ィルムシート４が布設され、かつ真空吸引ボックス２の
細孔２ｂよりの吸引を介して、前記フィルムシート４
を、前記台上面２ａ及びマスターパターン３上に吸着
（延展）させる。In order to completely separate the master pattern 3 from the casting sand and the disappearance model, which will be described later,
A heating film sheet 4 is laid on the table top surface 2a and the master pattern 3, and the film sheet 4 is sucked through the pores 2b of the vacuum suction box 2.
Are attracted (extended) onto the table top surface 2a and the master pattern 3.

【００２９】即ち、当該フィルムシート４が、後述する
型枠の底面（天蓋面を含む、以下単に底面とする。）を
構成するＶプロセス特有の鋳造技術である。That is, the film sheet 4 is a casting technique peculiar to the V process that constitutes the bottom surface (including the canopy surface, hereinafter simply referred to as the bottom surface) of the mold frame to be described later.

【００３０】以上の如く構成された型枠の底面を構成す
るフィルムシート４上には、消失性モデル５か、或いは
型枠の側板を形成する枠体６のいずれか一方が、載置さ
れる。On the film sheet 4 constituting the bottom surface of the mold configured as described above, either the disappearance model 5 or the frame body 6 forming the side plate of the mold is placed. .

【００３１】そこで、例えば、消失性モデル５を設ける
例を説明すると、前記マスターパターン３と連繋関係が
保持されるようにして、かつマスターパターン３を隠蔽
するフィルムシート４上に、消失性モデル５を１個又は
数個設ける。Therefore, for example, an example of providing the vanishing model 5 will be described. The vanishing model 5 is provided on the film sheet 4 which holds the master pattern 3 so as to maintain the linking relationship with the master pattern 3. One or several are provided.

【００３２】この消失性モデル５を設ける場合、接着
剤、テープ等の接着手段を採用したり、マスターパター
ン３との間に鋳造砂７を介設することもあり得る。When the disappearance model 5 is provided, adhesive means such as an adhesive or a tape may be adopted, or the casting sand 7 may be provided between the master pattern 3.

【００３３】以上の例では、その後、吸着されているフ
ィルムシート４上であって、消失性モデル５を囲繞する
ようにして枠体６を設ける。勿論、前述の如く、枠体６
と消失性モデル５とを、逆に設ける場合もあり得る。In the above example, the frame 6 is then provided on the adsorbed film sheet 4 so as to surround the vanishing model 5. Of course, as described above, the frame 6
The disappearance model 5 and the disappearance model 5 may be provided in reverse.

【００３４】その後、枠体６で囲繞された型枠空間と消
失性モデル５との間に、鋳造砂７が充填されるが、その
粒径が極めて小さいことから（例えば、８号）、消失性
モデル５の外郭形状に沿って充填されることと、消失性
モデル５の極めて小さい隙間にも、スムーズに充填され
る。これによって、消失性モデル５と相似形の鋳造造型
物が生成されること、またシャープな外郭線が形成さ
れ、在来の鋳造造型品では不可能なシャープな図柄、文
字等を造型できる。Thereafter, the casting sand 7 is filled between the mold space surrounded by the frame 6 and the disappearance model 5, but since the particle size is extremely small (for example, No. 8), it disappears. The filling is performed along the outer shape of the sex model 5, and the extremely small gap of the disappearance model 5 is also filled smoothly. As a result, a casting molding similar in shape to the disappearance model 5 is generated, and a sharp outline is formed, so that a sharp pattern, character, etc., which cannot be obtained by a conventional casting molding, can be molded.

【００３５】尚、消失性モデル５の具体例を挙げると、
原則として、独自又は固有の形態を備える氏名、苗字、
家紋、付属部品等であり、少量生産方式で、個別特色を
表現するものを採用する。A specific example of the vanishing model 5 is as follows.
As a general rule, name, family name,
Family crests, accessory parts, etc., which are produced in small quantities and which express individual characteristics.

【００３６】よって、前記マスターパターン３と消失性
モデル５とを組合わせることによって、多種、多様の鋳
造製品を得ることができる。Therefore, by combining the master pattern 3 and the disappearance model 5, various kinds of cast products can be obtained.

【００３７】以上のような操作を介して、型枠空間と消
失性モデル５との間に鋳造砂７が充填されたならば、型
枠の天蓋面（底面を含む、以下単に天蓋面とする。）を
構成するフィルムシート８を延長することにより砂型原
型Ａが構成される。そこで、引き続いて真空吸引ボック
ス２の細孔２ｂよりの吸引を介して、充填されている鋳
造孔７を固めると、ここに砂型Ａ１が構成される。If the casting sand 7 is filled between the mold space and the disappearance model 5 through the above-mentioned operation, the canopy surface of the mold (including the bottom surface, hereinafter simply referred to as the canopy surface). .) Is formed to form a sand mold prototype A. Then, subsequently, the filled casting hole 7 is solidified through suction from the pores 2b of the vacuum suction box 2 to form the sand mold A1 therein.

【００３８】通常、この砂型Ａ１を真空吸引ボックス２
より離脱し、反転して、他の台８上に載置する（勿論、
真空吸引ボックス２上に、反転載置することも可能であ
る。）。その後、当該砂型Ａ１よりマスターパターン３
を取り外すと、ここに、型枠Ａ２が構成され、かつ前記
の如く、マスターパターン３を取り外すことにより、型
枠Ａ２の空洞部９が形成される。Usually, this sand mold A1 is placed in a vacuum suction box 2
More detached, inverted, and placed on another table 8 (of course,
It is also possible to reversely mount it on the vacuum suction box 2. ). Then, from the sand mold A1, master pattern 3
When the mold is removed, the mold A2 is formed here, and by removing the master pattern 3 as described above, the cavity 9 of the mold A2 is formed.

【００３９】そして、この例では、型枠Ａ２を下型枠Ａ
１２として採用し、この下型枠Ａ１２に上型枠Ａ１３を
合体して、合体型枠Ａ１４を構成するとともに、前記空
洞部９に連通する湯道１０を設ける。In this example, the form A2 is replaced with the lower form A
The lower mold A12 is combined with the upper mold A13 to form a combined mold A14, and the runner 10 communicating with the cavity 9 is provided.

【００４０】図中２１は鋳造製品２０のシャープな外郭
線、２２は鋳造製品２０の極めて小さい隙間を示す。こ
のような、シャープな外郭線１１、又は極めて小さい隙
間１２は、前記鋳造砂７が、直接消失性モデル５の外郭
又は極めて小さい隙間（図示せず）に、確実に充填され
ることによって達成される。In the figure, 21 indicates a sharp outline of the cast product 20, and 22 indicates an extremely small gap of the cast product 20. Such a sharp outline 11 or an extremely small gap 12 is achieved by reliably filling the casting sand 7 into the outline of the disappearing model 5 or an extremely small gap (not shown). It

【００４１】[0041]

【発明の効果】本発明は、以上詳述した如く、真空吸引
ボックス台上面に載置したマスターパターン上に、フィ
ルムシートを介して消失性モデル、及び枠体を設けた後
（前後関係は問わず）、鋳造砂を充填、密閉し、その
後、真空吸引して砂型を構成し、以後、前記マスターパ
ターンを取り外して型枠を構成し、この型枠を少なくと
も上下型枠のいずれか一方に採用する鋳造方法であり、
下記の効果を有する。As described in detail above, according to the present invention, after the disappearance model and the frame body are provided via the film sheet on the master pattern placed on the upper surface of the vacuum suction box base (the front and rear relationships are not limited). No.), filled and sealed with casting sand, and then vacuum-sucked to form a sand mold, and then the master pattern was removed to form a mold, and this mold was used for at least one of the upper and lower molds. Is a casting method that
It has the following effects.

【００４２】（１）シャープな外郭線を備えた、繊細な
図柄、模様、文字等の鋳造製品を得ることができる。(1) It is possible to obtain a casting product having a delicate pattern, pattern, character, etc., which has a sharp outline.

【００４３】（２）独自性、少量生産の鋳造製品を簡易
に製造できる。(2) Unique, easy-to-manufacture small-volume production of cast products.

【００４４】（３）独自性、少量生産の鋳造製品を低コ
ストで提供できる。(3) Unique and low-volume casting products can be provided at low cost.

【００４５】（４）在来の設備、部材を有効利用でき
る。(4) Conventional equipment and members can be effectively used.

【００４６】（５）各人の好み、希望などを十分に反映
できる。(5) Each person's preferences and wishes can be reflected sufficiently.

【００４７】（６）独自性、少量生産特性、又は季節性
等を備えた鋳造製品を、迅速かつ確実に提供できる。(6) It is possible to promptly and surely provide a cast product having uniqueness, small-lot production characteristics, seasonality, and the like.

【図面の簡単な説明】[Brief description of drawings]

【図１】真空吸引ボックスの一例を示す模式図である。FIG. 1 is a schematic view showing an example of a vacuum suction box.

【図２】真空吸引ボックスの台上面にマスターパターン
を載置した状態の模式図である。FIG. 2 is a schematic view of a state in which a master pattern is placed on a table top surface of a vacuum suction box.

【図３】真空吸引ボックスの台上面及びマスターパター
ンの上面にフィルムシートを延展した状態を示す模式図
である。FIG. 3 is a schematic view showing a state in which a film sheet is spread on the base surface of a vacuum suction box and the top surface of a master pattern.

【図４】図３のフィルムシートを真空吸引した状態を示
す模式図である。FIG. 4 is a schematic diagram showing a state where the film sheet of FIG. 3 is vacuum-sucked.

【図５】吸着したフィルムシート上に枠体を載置した状
態を示す模式図である。FIG. 5 is a schematic view showing a state in which a frame body is placed on an adsorbed film sheet.

【図６】吸着したフィルムシート上であって、マスター
パターンに連繋するように消失性モデルを載置した状態
を示す模式図である。FIG. 6 is a schematic diagram showing a state in which a vanishing model is placed on a sucked film sheet so as to be linked to a master pattern.

【図７】図６の枠体内に鋳造砂を充填した状態を示す模
式図である。FIG. 7 is a schematic view showing a state where the casting sand is filled in the frame of FIG.

【図８】図７の状態をフィルムシートで隠蔽し、砂型原
型を構成する状態を示す模式図である。FIG. 8 is a schematic view showing a state in which the state of FIG. 7 is covered with a film sheet to form a sand mold prototype.

【図９】図８の砂型原型を真空吸引する状態を示す模式
図である。9 is a schematic view showing a state where the sand mold prototype of FIG. 8 is vacuum-sucked.

【図１０】砂型を示す模式図である。FIG. 10 is a schematic view showing a sand mold.

【図１１】型枠を示す模式図である。FIG. 11 is a schematic view showing a mold.

【図１２】図１１の型枠を、下型枠に採用した一例を示
す模式図である。FIG. 12 is a schematic view showing an example in which the mold of FIG. 11 is adopted as a lower mold.

【図１３】鋳造製品の一例として、例えば、プレート、
表札を示す拡大斜視図である。FIG. 13 shows an example of a cast product, for example, a plate,
It is an expansion perspective view which shows a nameplate.

【図１４】図１３の鋳造製品の一部を、更に拡大して示
す側面図である。FIG. 14 is a side view showing a part of the cast product of FIG. 13 in a further enlarged manner.

【符号の説明】[Explanation of symbols]

１ 減圧ホース ２ 真空吸引ボックス ２ａ 台上面 ２ｂ 細孔 ３ マスターパターン ４ フィルムシート ５ 消失性モデル ６ 枠体 ７ 鋳造砂 ８ 台 ９ 空洞部 １０ 湯道 ２０ 鋳造製品 ２１ シャープな外郭線 ２２ 極めて小さい隙間 Ａ 砂型原型 Ａ１ 砂型 Ａ２ 型枠 Ａ１２ 下型枠 Ａ１３ 上型枠 Ａ１４ 合体型枠 1 Decompression hose 2 Vacuum suction box 2a Upper surface 2b Pore 3 Master pattern 4 Film sheet 5 Dissipative model 6 Frame 7 Cast sand 8 Unit 9 Cavity 10 Runway 20 Cast product 21 Sharp outline 22 Extremely small gap A Sand mold prototype A1 Sand mold A2 Formwork A12 Lower formwork A13 Upper formwork A14 Combined formwork

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 少なくとも上型枠又は下型枠のいずれか
一方に、下記の型枠を利用して鋳造製品を得る鋳造方
法。 （１）真空吸引ボックス台上面に載置されたマスターパ
ターンを、フィルムシートで隠蔽した後、当該フイルム
シート上に消失性モデルを載置する鋳造製品模型生成工
程と、 この鋳造製品模型生成工程で形成された鋳造製品模型
を、鋳造砂で隠蔽する鋳造砂充填工程と、 この鋳造砂充填工程を介して構成された砂型原型の上面
にフルムシートを載置し、前記真空ボックスを介しての
吸引により、前記鋳造砂を固める砂型製造工程と、 この砂型製造工程で製造された砂型より前記マスターパ
ターンを取り外し、前記砂型内に消失性モデルが残った
鋳造用型枠を製造する型枠製造工程と、 で構成される型枠。1. A casting method for obtaining a cast product by using the following mold on at least one of the upper mold and the lower mold. (1) In the cast product model generation process in which the master pattern placed on the top surface of the vacuum suction box is covered with a film sheet, and then the disappearance model is placed on the film sheet, and the cast product model generation process. The casting product model formed is concealed with casting sand, and a sand sheet filling step is performed, and a flume sheet is placed on the upper surface of the sand mold prototype configured through this casting sand filling step, and suction is performed through the vacuum box. A sand mold manufacturing step of hardening the casting sand, and a mold manufacturing step of manufacturing the casting mold in which the disappearance model remains in the sand mold by removing the master pattern from the sand mold manufactured in this sand mold manufacturing step, Formwork composed of. 【請求項２】 請求項１のマスターパターンが基本形態
で、消失性モデルが造形的特性を備えた独自形態である
請求項１のマスターパターンと消失性モデルとを利用し
て鋳造製品を得る鋳造方法。2. A casting for obtaining a cast product by using the master pattern according to claim 1 as a basic form and the disappearance model as a unique form having a molding characteristic. Method.