JPH0639857A - Method for molding fine part - Google Patents
Method for molding fine partInfo
- Publication number
- JPH0639857A JPH0639857A JP626892A JP626892A JPH0639857A JP H0639857 A JPH0639857 A JP H0639857A JP 626892 A JP626892 A JP 626892A JP 626892 A JP626892 A JP 626892A JP H0639857 A JPH0639857 A JP H0639857A
- Authority
- JP
- Japan
- Prior art keywords
- cavity
- mold
- vacuum
- atmospheric pressure
- injected
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、小型化が活発に行われ
ているビデオ，ビデオカメラ，ラジカセ等の家電製品
や、時計，カメラなどの小型精密機器及び今後注目され
るであろうマイクロマシン等に使用される、微小部品の
成形方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to home appliances such as video, video cameras, radio-cassettes and the like, which are being miniaturized actively, small precision equipment such as watches and cameras, and micromachines which will be attracting attention in future. The present invention relates to a method for molding a micro component used in.
【０００２】[0002]
【従来の技術】樹脂成形部品は、射出成形技術や金型加
工技術の発展により、小型，高精度な部品が成形されて
いる。2. Description of the Related Art With regard to resin molded parts, small-sized and highly accurate parts have been molded by the development of injection molding technology and mold processing technology.
【０００３】以下、従来の樹脂成形、組立技術について
説明する。図５（ａ），（ｂ）は、従来の樹脂射出成形
機及び金型を示す説明図である。図５において、４１は
縦型射出成形機、４２はホッパ−、４３は射出ノズル、
４４は射出成形金型、４５は加熱シリンダ−、４６は射
出シリンダ−、４７はスプル−部、４８は成形品、４９
はキャビティ−、５０は突き出しピンである。Conventional resin molding and assembly techniques will be described below. 5A and 5B are explanatory views showing a conventional resin injection molding machine and a mold. In FIG. 5, 41 is a vertical injection molding machine, 42 is a hopper, 43 is an injection nozzle,
44 is an injection mold, 45 is a heating cylinder, 46 is an injection cylinder, 47 is a sprue part, 48 is a molded product, 49
Is a cavity, and 50 is a protruding pin.
【０００４】以下その動作について説明する。ホッパ−
４２に供給された樹脂材料は、加熱シリンダ−４５で加
熱，溶融し、射出成形金型４４が型締めされた後、射出
シリンダ−４６により射出ノズル４３から射出成形金型
４４に射出される。射出された樹脂は、スプル−部４７
を通り、キャビティ−４９を満たし、成形品４８ができ
る。射出成形金型４４が開き、突き出しピン５０により
成形品４８が押し出され、図示されていないが、自動取
出装置などにより取り出される。The operation will be described below. Hopper
The resin material supplied to 42 is heated and melted by the heating cylinder-45, and the injection molding die 44 is clamped, and then is injected from the injection nozzle 43 to the injection molding die 44 by the injection cylinder-46. The injected resin is sprue part 47.
And the cavity-49 is filled, and a molded product 48 is formed. The injection molding die 44 is opened, and the molded product 48 is extruded by the ejection pin 50 and taken out by an automatic take-out device or the like (not shown).
【０００５】図６（ａ）〜（ｅ）は、従来の真空注型法
による成形工程を示す工程図である。図６において、５
１はマスタ−モデル、５２は真空槽、５３はシリコ−ン
ゴム、５４は気泡、５５はシリコ−ンゴム型、５６は注
型用樹脂、５７は注入口、５８はキャビティ−、５９は
成形品、６０は枠型である。FIGS. 6A to 6E are process charts showing a molding process by a conventional vacuum casting method. In FIG. 6, 5
1 is a master model, 52 is a vacuum tank, 53 is silicone rubber, 54 is air bubbles, 55 is silicone rubber mold, 56 is casting resin, 57 is inlet, 58 is cavity, 59 is molded product, 60 is a frame type.
【０００６】以下、その動作について説明する。まず図
６（ａ）に示すように、成形したい形状のマスタ−モデ
ル５１を作り、枠型６０を組立、その中にマスタ−モデ
ル５１が完全に埋まるまで、シリコ−ンゴム５３を流し
込み、真空槽５２内で気泡５４を除去する。The operation will be described below. First, as shown in FIG. 6 (a), a master model 51 having a shape to be molded is formed, a frame die 60 is assembled, and silicone rubber 53 is poured into the vacuum mold until the master model 51 is completely filled therein. Bubbles 54 are removed within 52.
【０００７】次に図６（ｂ）に示すようにシリコ−ンゴ
ム５３が硬化し、これを分割し、中からマスタ−モデル
５１を取り除くことにより、シリコ−ンゴム型５５が出
来る。Next, as shown in FIG. 6 (b), the silicone rubber 53 is hardened, the silicone rubber 53 is divided, and the master model 51 is removed from the silicone rubber 53 to form a silicone rubber mold 55.
【０００８】次に図６（ｃ）に示すように、シリコ−ン
ゴム型５５をテ−プなどで型締めし、真空槽５２に入
れ、同じ真空槽５２で脱泡した注型用樹脂５６を注入口
５７から注ぐ。このとき真空槽５２内は、負圧状態であ
る。Next, as shown in FIG. 6 (c), the silicone rubber mold 55 is clamped with a tape or the like, placed in a vacuum tank 52, and the casting resin 56 defoamed in the same vacuum tank 52 is placed. Pour from the inlet 57. At this time, the inside of the vacuum chamber 52 is in a negative pressure state.
【０００９】次に図６（ｄ）に示すように、注入後、真
空槽５２内を大気圧に戻し、大気圧により注型用樹脂５
６をキャビティ−５８に押し込む。そして図６（ｅ）に
示すように、樹脂硬化後、シリコ−ンゴム型５５を開
き、脱型すると成形品５９が出来上がる。Next, as shown in FIG. 6 (d), after the injection, the inside of the vacuum chamber 52 is returned to the atmospheric pressure, and the casting resin 5 is applied by the atmospheric pressure.
Push 6 into cavity-58. Then, as shown in FIG. 6 (e), after the resin is cured, the silicone rubber mold 55 is opened and released from the mold, whereby a molded product 59 is completed.
【００１０】[0010]
【発明が解決しようとする課題】しかしながら、上記の
従来例おいて、射出成形では、肉厚が０．５ｍｍ以下に
なると未充填になる確立が高くなり、さらに０．１〜
０．２ｍｍ程度の肉厚だとほとんど流れず、微小で薄肉
な成形品を成形することは大変困難である。However, in the above-mentioned conventional example, in injection molding, when the wall thickness becomes 0.5 mm or less, unfilling is more likely to occur, and further 0.1 to 0.1%.
If the wall thickness is about 0.2 mm, it hardly flows, and it is very difficult to mold a minute and thin molded product.
【００１１】また、真空注型法の場合は、流れは注型用
樹脂を用いることで、０．１ｍｍの肉厚でもかなり良く
充填されるが、さらに薄肉になったり、薄肉部の距離が
長くなると、十分な充填が出来なくなる。また通常試作
的な目的で使用され、数個つくるには良いが、多数個を
成形するには、シリコ−ンゴム型を用いるので型寿命が
短く、量産性はない。さらに微小部品（たとえば１ｍｍ
以下）のゴム型をマスタ−モデルから作るのは、かなり
難しい。Further, in the case of the vacuum casting method, the flow can be filled quite well even with a wall thickness of 0.1 mm by using the casting resin, but it becomes thinner and the distance of the thin wall portion becomes longer. If so, sufficient filling cannot be performed. Further, it is usually used for a trial purpose, and it is good to make several pieces, but in order to mold many pieces, a silicone rubber mold is used, so the mold life is short and mass production is not possible. Smaller parts (eg 1 mm
It is quite difficult to make the rubber mold of (below) from the master model.
【００１２】本発明は、上記従来技術の課題を解決する
もので、微小で薄肉な部品でも成形が可能で、また、型
寿命も長く、量産も可能な微小部品に適した成形技術を
提供することを目的としている。The present invention solves the above-mentioned problems of the prior art, and provides a molding technique suitable for minute parts that can mold even minute and thin-walled parts, has a long mold life, and can be mass-produced. Is intended.
【００１３】[0013]
【課題を解決するための手段】この目的を達成するため
に、本発明は、ガイドピンを基準に、微小部品の立体形
状を複数枚のキャビティ−プレ−トによって形成し、こ
れをベ−スプレ−トと固定プレ−ト間にはさんで固定
し、全てのプレ−トには、離型剤としてフッ素系の単分
子膜を形成し、次にこの成形用金型を真空雰囲気中に置
き、他の真空タンク内で脱泡された二液性樹脂の主剤と
硬化剤を、それぞれ計量，混合，吐出する機構により一
定量吐出し、真空中のキャビティ−内に注入する。その
後、大気圧に戻し、注入され硬化する。In order to achieve this object, the present invention forms a three-dimensional shape of a minute component by a plurality of cavity plates on the basis of a guide pin, which is a base plate. -A fixed monolithic film is formed as a release agent on all the plates, and then the molding die is placed in a vacuum atmosphere. The main component and the curing agent of the two-component resin degassed in the other vacuum tank are discharged by a predetermined amount by a mechanism for measuring, mixing and discharging, and injected into the cavity in vacuum. After that, the pressure is returned to atmospheric pressure, and the material is injected and cured.
【００１４】[0014]
【作用】本発明は上記成形方法により、流れのよい注型
用の二液性樹脂を用い、大気圧で注入、さらに流れずら
い場合には、数kg／cm2 の加圧が可能であり、従来でき
なかった微小で薄肉な部品でも成形が可能であり、また
金型に単分子膜を形成することで、離型性が良く、型寿
命も長くなり量産についても可能性を有する微小部品の
成形方法を得ることができる。According to the present invention, by the above-mentioned molding method, it is possible to use a two-component casting resin having a good flow and to inject it at atmospheric pressure, and to pressurize several kg / cm 2 when it is difficult to flow. , It is possible to mold even minute and thin parts that could not be done before, and by forming a monomolecular film on the mold, the mold releasability is good, the mold life is long, and there is a possibility of mass production. Can be obtained.
【００１５】[0015]
（実施例１）以下、本発明の第１の実施例について図面
を参照しながら説明する。(Embodiment 1) Hereinafter, a first embodiment of the present invention will be described with reference to the drawings.
【００１６】まず、図２（ａ），（ｂ），（ｃ）はそれ
ぞれ、本発明の第１の実施例における微小部品の成形方
法を実現する成形用金型の構成を示す断面図，平面図，
及び同（ｂ）のＡ部分詳細図である。First, FIGS. 2 (a), 2 (b) and 2 (c) are a cross-sectional view and a plan view showing the structure of a molding die for realizing the method for molding a minute component according to the first embodiment of the present invention. Figure,
FIG. 3 is a detailed view of part A of FIG.
【００１７】図２において、１はベ−スプレ−ト、２は
ガイドピン、３はキャビティプレ−ト群、４は固定プレ
−トＩ、５は固定プレ−トII、６は注入口である。この
成形用金型の構成は、ベ−スプレ−ト１上のガイドピン
２を基準に、キャビティプレ−ト群３を組立て、その上
に固定プレ−トＩ４および固定プレ−トII５をおいて、
挟み込むようにして固定する。In FIG. 2, 1 is a base plate, 2 is a guide pin, 3 is a cavity plate group, 4 is a fixed plate I, 5 is a fixed plate II, and 6 is an injection port. . The structure of this molding die is such that a cavity plate group 3 is assembled on the basis of a guide pin 2 on a base plate 1, and a fixed plate I4 and a fixed plate II5 are placed thereon. ,
Secure by sandwiching.
【００１８】次に図３を用いてキャビティプレ−ト群３
について詳細に説明する。図３は図２におけるキャビテ
ィプレ−ト群を示す断面図，平面図である。Next, referring to FIG. 3, the cavity plate group 3
Will be described in detail. FIG. 3 is a sectional view and a plan view showing the cavity plate group in FIG.
【００１９】図３において、７、８、９、１０はそれぞ
れキャビティプレ−トＩ、II、III、IVである。１１は
キャビティ−Ｉ、１２はキャビティ−IIである。次にそ
の組合せを説明する。In FIG. 3, reference numerals 7, 8, 9, and 10 are cavity plates I, II, III, and IV, respectively. Reference numeral 11 is a cavity-I, and 12 is a cavity-II. Next, the combination will be described.
【００２０】同図に示したように、キャビティプレ−ト
Ｉ７、II８、III ９、Ｉ７の組合せにより、キャビティ
−Ｉ１１のような一段のギヤを持つシャフトを形成で
き、また、キャビティプレ−トＩ７、II８、IV１０、Ｉ
７のように組み合わせれば、キャビティ−II１２のよう
な二段のギヤを持つシャフトを形成でき、このようにキ
ャビティプレ−ト群３の組合せにより、さまざまな立体
的なキャビティ−形状をつくることができる。また、図
２、図３で示したキャビティプレ−ト群３、固定プレ−
トＩ４、固定プレ−トII５、ベ−スプレ−ト１には、図
示していないが離型剤として、全て単分子膜コ−ティン
グが行われている。As shown in the figure, by combining the cavity plates I7, II8, III9 and I7, it is possible to form a shaft having a single-stage gear like the cavity plate I11. , II8, IV10, I
7 can be combined to form a shaft having two-stage gears such as Cavity-II12. By combining the cavity plate groups 3 in this way, various three-dimensional cavity shapes can be created. it can. In addition, the cavity plate group 3 and the fixed plate shown in FIGS.
Although not shown in the drawing, the monolayer coating is applied to all of the mold I4, the fixed plate II5 and the base plate 1 as a releasing agent.
【００２１】図１は本発明の第１の実施例における微小
部品の成形方法を実現するための装置の全体構成図であ
る。FIG. 1 is an overall configuration diagram of an apparatus for realizing a method of molding a minute component according to the first embodiment of the present invention.
【００２２】図１において、１３は真空タンク（Ａ）、
１４は真空タンク（Ｂ）、１５は主剤、１６は硬化剤、
１７は計量，混合，吐出機構、１８は真空ポンプ、１９
はバルブＩ、２０はバルブII、２１はバルブIII 、２３
は吐出ノズル、２６は真空オ−ブンである。In FIG. 1, 13 is a vacuum tank (A),
14 is a vacuum tank (B), 15 is a main agent, 16 is a curing agent,
17 is a measuring, mixing and discharging mechanism, 18 is a vacuum pump, 19
Is valve I, 20 is valve II, 21 is valve III, 23
Is a discharge nozzle, and 26 is a vacuum oven.
【００２３】以上の構成による成形方法について説明す
る。まず、キャビティプレ−ト群３によりキャビティ−
II１２を形成し、固定プレ−トＩ４、固定プレ−トII５
によって固定され、真空オ−ブン２６内に置かれる。次
にバルブII２０を開け、真空ポンプ１８により真空にす
る。このとき他のバルブは閉じている。A molding method having the above configuration will be described. First, the cavity plate group 3
Forming II12, fixed plate I4, fixed plate II5
And is placed in a vacuum oven 26. Next, the valve II 20 is opened, and the vacuum pump 18 is used to create a vacuum. At this time, the other valves are closed.
【００２４】次に、一定の真空度に達した後、すでに脱
泡済みの真空タンク（Ａ）１３内の主剤１５と、真空タ
ンク（Ｂ）１４内の硬化剤１６を、計量，混合，吐出機
構１７により一定量吐出する。このときに同時にバルブ
Ｉ１９を開く。吐出された樹脂は、吐出ノズル２３より
成形用金型内に注入される。次にバルブＩ１９を閉じ、
バルブIII ２１を開け、大気圧下に戻し、大気圧により
樹脂がさらに押し込まれる。そして、そのまま真空オ−
ブン２６中で硬化しても良く、また他の温度設定された
オ−ブンに移して硬化しても良い。Next, after reaching a certain degree of vacuum, the main agent 15 in the vacuum tank (A) 13 already degassed and the curing agent 16 in the vacuum tank (B) 14 are weighed, mixed and discharged. The mechanism 17 discharges a fixed amount. At the same time, the valve I19 is opened. The discharged resin is injected into the molding die from the discharge nozzle 23. Then close valve I19,
The valve III 21 is opened and returned to atmospheric pressure, and the resin is further pushed in by atmospheric pressure. Then, vacuum as it is.
It may be cured in the oven 26, or may be moved to another oven having a temperature set and cured.
【００２５】以上のように本実施例によれば、キャビテ
ィプレ−ト群３により、微小部品の立体形状を形成し、
これを固定プレ−トで固定し、それらは全て単分子膜コ
−ティングが行われており、その成形金型を真空オ−ブ
ン内に配置し、一定の真空度に達した後、二液性樹脂の
主剤１５と硬化剤１６を計量，混合，吐出機構１７によ
り吐出し、キャビティ−内に注入し、その後大気圧に戻
し、さらに注入、硬化するという成形方法により、微小
で薄肉な部品でも成形することができ、また単分子膜コ
−ティングにより離型性が良好であり、金属の型を使用
できるのでゴム型にくらべ、型寿命も長くなり、量産も
可能な成形方法を提供することができる。As described above, according to this embodiment, the cavity plate group 3 forms a three-dimensional shape of a minute component,
This was fixed with a fixing plate, and all of them were subjected to monomolecular film coating.The molding die was placed in a vacuum oven, and after reaching a certain degree of vacuum, two liquid Even a minute and thin-walled part can be manufactured by a molding method in which the main component 15 of the volatile resin and the curing agent 16 are discharged by the measuring, mixing and discharging mechanism 17, injected into the cavity, then returned to atmospheric pressure, and further injected and cured. To provide a molding method that can be molded, has good mold releasability by coating with a monomolecular film, and can use a metal mold so that it has a longer mold life than a rubber mold and can be mass-produced. You can
【００２６】（実施例２）以下、本発明の第２の実施例
について図面を参照しながら説明する。図４は本発明の
第２の実施例における微小部品の成形方法を実現する装
置の全体構成図である。図１の構成と異なる点は、バル
ブIV２２、加圧機構２４、圧力源２５、可動テ−ブル２
７を新たに設けた点である。(Second Embodiment) A second embodiment of the present invention will be described below with reference to the drawings. FIG. 4 is an overall configuration diagram of an apparatus that realizes a method for molding a minute component according to the second embodiment of the present invention. The difference from the configuration of FIG. 1 is that the valve IV 22, the pressurizing mechanism 24, the pressure source 25, and the movable table 2
This is the point where 7 is newly provided.
【００２７】以上の構成で、その動作について説明す
る。まず、計量，混合，吐出機構１７により樹脂をキャ
ビティ−II１２に吐出するまでは、図１の実施例と同様
である。The operation of the above configuration will be described. First, the procedure until the resin is discharged to the cavity-II 12 by the measuring, mixing and discharging mechanism 17 is the same as that of the embodiment shown in FIG.
【００２８】次にバルブＩ１９を閉じ、可動テ−ブル２
７により一度吐出ノズル２３を金型からはなし、バルブ
III ２１を開け、大気圧下にして樹脂を押し込み、再び
可動テ−ブル２７を下降させ、金型に密着、固定し、バ
ブルIV２２を開け、圧力源２５からの圧力を加圧機構２
４で調節して、数kg／cm2 の圧力で加圧注入することが
できる。また、大気圧下に戻す前に、真空状態で加圧す
ることもできる。Next, the valve I19 is closed and the movable table 2
7, the discharge nozzle 23 is once removed from the mold, and the valve
III 21 is opened, the resin is pushed under atmospheric pressure, the movable table 27 is lowered again, the movable table 27 is brought into close contact with and fixed to the mold, the bubble IV 22 is opened, and the pressure from the pressure source 25 is applied to the pressurizing mechanism 2.
It can be pressure-injected at a pressure of several kg / cm 2 by adjusting in step 4. It is also possible to pressurize in a vacuum state before returning to atmospheric pressure.
【００２９】以上のように、キャビティ−に樹脂が注入
された後で再度、加圧注入できる機構を設けることによ
り、薄肉でより複雑な立体形状や、流動性の悪い樹脂を
用いても、従来より確実に充填することができる。As described above, by providing a mechanism that allows pressure injection again after the resin is injected into the cavity, even if a thin and more complicated three-dimensional shape or a resin with poor fluidity is used, It can be filled more reliably.
【００３０】[0030]
【発明の効果】以上のように本発明は、ガイドピンを基
準に、微小部品の立体形状を複数枚のキャビティ−プレ
−トによって形成し、これをベ−スプレ−トと固定プレ
−ト間にはさんで固定し、全てのプレ−トには、離型剤
としてフッ素系の単分子膜を形成し、次にこの成形用金
型を真空雰囲気中に置き、他の真空タンク内で脱泡され
た二液性樹脂の主剤と硬化剤を、それぞれ計量，混合，
吐出する機構により一定量吐出し、真空中のキャビティ
−内に注入する。その後、大気圧に戻し、注入され硬化
する。またさらに数kg／cm2 の加圧をする機構を有して
いるということにより、従来できなかった微小で薄肉な
部品でも成形が可能であり、また金型に単分子膜を形成
することで、離型性が良く、型寿命も長くなり量産につ
いても可能な成形技術を実現できるものである。As described above, according to the present invention, the three-dimensional shape of the minute component is formed by a plurality of cavity plates with reference to the guide pin, and this is formed between the base plate and the fixed plate. It is fixed by sandwiching it, and a fluorine-based monomolecular film is formed as a release agent on all the plates, and then this molding die is placed in a vacuum atmosphere and removed in another vacuum tank. Weigh, mix, and mix the main component of the foamed two-component resin and the curing agent, respectively.
A certain amount is discharged by the discharging mechanism and is injected into the cavity in vacuum. After that, the pressure is returned to atmospheric pressure, and the material is injected and cured. In addition, since it has a mechanism to apply a pressure of several kg / cm 2 , it is possible to mold even minute and thin parts that could not be done before, and by forming a monomolecular film on the mold. Molding technology with good mold releasability, long mold life, and mass production can be realized.
【図１】本発明の第１の実施例における微小部品の成形
方法を実現する装置の全体構成図FIG. 1 is an overall configuration diagram of an apparatus that realizes a molding method for minute parts according to a first embodiment of the present invention.
【図２】同装置の要部である成形用金型の構造を示す図FIG. 2 is a view showing a structure of a molding die which is a main part of the apparatus.
【図３】同装置の要部であるキャビティプレ−ト群の詳
細構成図FIG. 3 is a detailed configuration diagram of a cavity plate group, which is a main part of the apparatus.
【図４】本発明の第２の実施例における微小部品の成形
方法を実現する装置の全体構成図FIG. 4 is an overall configuration diagram of an apparatus that realizes a molding method for minute parts according to a second embodiment of the present invention.
【図５】従来の樹脂射出成形機及び金型を示す図FIG. 5 is a view showing a conventional resin injection molding machine and a mold.
【図６】従来の真空注型法による成形工程を示す工程図FIG. 6 is a process diagram showing a molding process by a conventional vacuum casting method.
１ ベ−スプレ−ト ２ ガイドピン ３ キャビティ−プレ−ト群 ４ 固定プレ−トＩ ５ 固定プレ−トII ６ 注入口 ７ キャビティ−プレ−トＩ ８ キャビティ−プレ−トII ９ キャビティ−プレ−トIII １０ キャビティ−プレ−トIV １１ キャビティ−Ｉ １２ キャビティ−II １３ 真空タンク（Ａ） １４ 真空タンク（Ｂ） １５ 主剤 １６ 硬化剤 １７ 計量，混合，吐出機構 １８ 真空ポンプ １９ バルブＩ ２０ バルブII ２１ バルブIII ２２ バルブIV ２３ 吐出ノズル ２４ 加圧機構 ２５ 圧力源 ２６ 真空オ−ブン ２７ 可動テ−ブル 1 Base Plate 2 Guide Pin 3 Cavity Plate Group 4 Fixed Plate I 5 Fixed Plate II 6 Injection Port 7 Cavity Plate I 8 Cavity Plate II 9 Cavity Plate To III 10 Cavity-Plate IV 11 Cavity-I 12 Cavity-II 13 Vacuum tank (A) 14 Vacuum tank (B) 15 Main agent 16 Curing agent 17 Measuring, mixing and discharging mechanism 18 Vacuum pump 19 Valve I 20 Valve II 21 valve III 22 valve IV 23 discharge nozzle 24 pressurizing mechanism 25 pressure source 26 vacuum oven 27 movable table
Claims (2)
上のガイドピンと、前記ガイドピンを基準に微小部品の
立体形状を形成する複数枚のキャビティ−プレ−トと、
前記キャビティ−プレ−トを前記ベ−スプレ−トとの間
に挟むように固定する固定プレ−トから構成され、前記
ベ−スプレ−ト、キャビティ−プレ−ト、固定プレ−ト
の全面にフッ素系の単分子膜を形成した成形用金型を真
空雰囲気中に配置し、前記真空雰囲気とは別に、真空状
態にできるタンク中に入れられ、脱泡された二液性樹脂
の主剤と硬化剤を一定量吐出し、キャビティ−内に注入
し、その後、大気圧下に戻し、大気圧により再度キャビ
ティ−内に注入され、その後に硬化することを特徴とす
る微小部品の成形方法。1. A base plate, a guide pin on the base plate, and a plurality of cavity plates forming a three-dimensional shape of a minute component with the guide pin as a reference.
It is composed of a fixed plate for fixing the cavity plate so as to be sandwiched between the base plate, the base plate, the cavity plate, and the fixed plate. A mold for forming a fluorine-based monomolecular film is placed in a vacuum atmosphere, and separately from the vacuum atmosphere, it is placed in a tank that can be in a vacuum state and cured with the main component of the defoamed two-component resin. A method for molding a microparticulate, characterized in that a fixed amount of the agent is discharged, injected into the cavity, then returned to atmospheric pressure, injected again into the cavity under atmospheric pressure, and then cured.
いて、注入した樹脂にさらに数kg／cm2 の加圧をするこ
とができる機構を有することを特徴とする請求項１記載
の微小部品の成形方法。2. The microscopic device according to claim 1, further comprising a mechanism capable of further applying a pressure of several kg / cm 2 to the injected resin after returning to atmospheric pressure or in vacuum. Molding method of parts.