JPH06347664A - Composite type optical fiber coupler and its production - Google Patents
Composite type optical fiber coupler and its productionInfo
- Publication number
- JPH06347664A JPH06347664A JP5158073A JP15807393A JPH06347664A JP H06347664 A JPH06347664 A JP H06347664A JP 5158073 A JP5158073 A JP 5158073A JP 15807393 A JP15807393 A JP 15807393A JP H06347664 A JPH06347664 A JP H06347664A
- Authority
- JP
- Japan
- Prior art keywords
- optical fiber
- optical
- optical fibers
- fiber coupler
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、一般には、光通信、光
計測等に利用される光ファイバカプラに関するものであ
り、特に、2種類の異なる伝搬定数を有する各2本のシ
ングルモード光ファイバからなる合計4本の光ファイバ
を一括融着延伸して形成され、2×2光ファイバカプラ
及び分波合波光ファイバカプラとして動作することので
きる、4出力端を有する複合型の光ファイバカプラ及び
その製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention generally relates to an optical fiber coupler used for optical communication, optical measurement, etc., and particularly to two single mode optical fibers each having two different propagation constants. And a composite type optical fiber coupler having four output ends, which is formed by fusion-spreading a total of four optical fibers each of which is composed of 4 and which can operate as a 2 × 2 optical fiber coupler and a demultiplexing / multiplexing optical fiber coupler. The present invention relates to a manufacturing method thereof.
【0002】[0002]
【従来の技術】石英製シングルモード光ファイバを用い
て作製された、入力、出力端がそれぞれ2端子とされる
種々の機能を有した光ファイバカプラは、従来より知ら
れている。例えば、光ファイバカプラのうち、特定の波
長において、光出力の分岐比率を各光出力端で50:5
0にした「2×2光ファイバカプラ」、或は特定の2つ
の波長において、光出力の分岐比率を実質的に0:10
0にした「分波合波光ファイバカプラ」は、同一の光伝
搬定数を有する二本の光ファイバを融着延伸することに
よって作製されている。通常、光通信で要望される光フ
ァイバカプラにおいては、上記の特定の波長は、1.3
1μm及び1.55μmのレーザ光が使用される。2. Description of the Related Art Optical fiber couplers made of quartz single-mode optical fibers and having various functions, each having two input and two output terminals, have been conventionally known. For example, among optical fiber couplers, the branching ratio of optical output at a specific wavelength is 50: 5 at each optical output end.
“2 × 2 optical fiber coupler” set to 0, or the branching ratio of the optical output at substantially two specific wavelengths is 0:10.
The "demultiplexing / multiplexing optical fiber coupler" set to 0 is produced by fusion splicing two optical fibers having the same optical propagation constant. Usually, in the optical fiber coupler required for optical communication, the above specific wavelength is 1.3.
Laser light of 1 μm and 1.55 μm is used.
【0003】このように、2×2光ファイバカプラと分
波合波光ファイバカプラとは、分岐比率の波長特性が異
なっており、従来、分岐比率の波長特性が異なる2×2
光ファイバカプラ及び分波合波光ファイバカプラを複合
したものが要求される場合には、2×2光ファイバカプ
ラと分波合波光ファイバカプラとを個々に作製し個別に
支持板に固定して、その後、これら二つの光ファイバカ
プラを同一のパッケージ内に収容する方法が採られてい
た。As described above, the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler have different wavelength characteristics of the branching ratio, and conventionally, the 2 × 2 optical fiber couplers have different wavelength characteristics of the branching ratio.
When a composite of the optical fiber coupler and the demultiplexing / combining optical fiber coupler is required, the 2 × 2 optical fiber coupler and the demultiplexing / combining optical fiber coupler are individually prepared and individually fixed to the support plate, After that, a method of housing these two optical fiber couplers in the same package has been adopted.
【0004】[0004]
【発明が解決しようとする課題】しかしながら、このよ
うな構成の、2×2光ファイバカプラと分波合波光ファ
イバカプラとの2個の光ファイバカプラからなる複合型
光ファイバカプラは、その製造に際しての作業性が悪い
という問題の他に、 (1)2×2光ファイバカプラと分波合波光ファイバカ
プラとはそれぞれ異なる支持板に固定されているため
に、これらを収容するパッケージの大きさは自ら大きく
なる。 (2)2×2光ファイバカプラと分波合波光ファイバカ
プラとは一般に光結合長が異なり、また互いに温度特
性、即ち、周囲温度の変化に伴なう光結合長の変化に因
る分岐比率の変化が異なっており、同一パッケージに収
容した場合に両カプラの温度特性を一致するような構成
にすることは困難であり、温度特性を小さくし得ない。 (3)2×2光ファイバカプラと分波合波光ファイバカ
プラとは共に、2本の光ファイバにより光結合部が形成
されており、個々の光ファイバカプラの機械的強度は、
複合化により強化されてはいない。 という問題を有している。However, the composite type optical fiber coupler having two optical fiber couplers of the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler having such a structure is manufactured. In addition to the problem of poor workability of (1), since the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler are fixed to different support plates, the size of the package accommodating them is Grow bigger by myself. (2) Generally, the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler have different optical coupling lengths, and the temperature characteristics, that is, the branching ratio due to the change of the optical coupling length with the change of the ambient temperature. Are different from each other, and it is difficult to make the temperature characteristics of both couplers the same when housed in the same package, and the temperature characteristics cannot be reduced. (3) Both the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler have an optical coupling part formed by two optical fibers, and the mechanical strength of each optical fiber coupler is
It is not strengthened by compounding. I have a problem.
【0005】換言すれば、従来の複合型の光ファイバ
は、複合化することによる利点は、単に、単一のパッケ
ージに収容され、その取扱が有利であるという点にのみ
あった。In other words, the conventional composite type optical fiber has a merit in that it is simply housed in a single package, and its handling is advantageous.
【0006】従って、本発明の目的は、温度特性が小さ
く、更に光結合部の機械的強度が強化され、しかも小型
化を達成し得る、2×2光ファイバカプラ及び分波合波
光ファイバカプラとして動作することのできる、4出力
端を有する複合型光ファイバカプラを提供することであ
る。Therefore, an object of the present invention is to provide a 2 × 2 optical fiber coupler and a demultiplexing / multiplexing optical fiber coupler which have small temperature characteristics, further enhance the mechanical strength of the optical coupling portion, and can achieve miniaturization. An object of the present invention is to provide a composite optical fiber coupler having four output ends, which is operable.
【0007】[0007]
【課題を解決するための手段】上記目的は本発明に係る
4出力端を有する複合型光ファイバカプラにて達成され
る。要約すれば、本発明は、2種類の異なる伝搬定数を
有する各2本のシングルモード光ファイバからなる合計
4本の光ファイバが一括融着延伸された光結合部を有す
る光ファイバカプラであって、前記光ファイバ4本は左
右対称な配置をとり、且つ異なる伝搬定数を有する光フ
ァイバが隣接し、しかも各光ファイバはそれぞれ隣接す
る2本の光ファイバとのみ融着延伸されていることを特
徴とする複合型光ファイバカプラである。The above object is achieved by a composite type optical fiber coupler having four outputs according to the present invention. In summary, the present invention relates to an optical fiber coupler having an optical coupling section in which a total of four optical fibers each consisting of two single mode optical fibers having two different propagation constants are fused and stretched. The four optical fibers are symmetrically arranged, and the optical fibers having different propagation constants are adjacent to each other, and each optical fiber is fused and drawn only with two adjacent optical fibers. Is a composite optical fiber coupler.
【0008】この複合型光ファイバカプラにて、同じ伝
搬定数を有する一方の光ファイバ組は、2×2光ファイ
バカプラとして動作し、他方の同じ伝搬定数を有する光
ファイバ組は、2つの波長の光に対して合波、分波する
ことのできる分波合波光ファイバカプラとして動作す
る。In this composite optical fiber coupler, one optical fiber set having the same propagation constant operates as a 2 × 2 optical fiber coupler, and the other optical fiber set having the same propagation constant has two wavelengths. It operates as a demultiplexing / combining optical fiber coupler that can combine and demultiplex light.
【0009】上記複合型光ファイバカプラは、(a)コ
ア径及びクラッド外径が同じ4本のシングルモード光フ
ァイバを準備すること、(b)前記4本の光ファイバの
中の少なくとも2本の光ファイバは、クラッド外径が同
じ径に縮径されること、(c)次いで、前記4本の光フ
ァイバを、左右対称な配置をとり、且つ異なるクラッド
外径の光ファイバが隣接し、しかも各光ファイバはそれ
ぞれ隣接する2本の光ファイバとのみ接触するようにし
て、前記各光ファイバを長手方向に平行に沿わせて4本
の光ファイバを一括融着し、その後に融着延伸処理する
こと、(d)前記各光ファイバの融着延伸時には、いず
れかの光ファイバの入力側に所定波長のモニター光を入
射し、前記各光ファイバの出力側には光出力検知手段を
接続して前記各光ファイバからの出力をモニターするこ
と、そして、(e)前記各光ファイバからの出力が所望
の値となった時に、一括融着延伸を停止すること、を特
徴とする製造方法にて好適に製造される。The above-mentioned composite optical fiber coupler comprises: (a) preparing four single-mode optical fibers having the same core diameter and clad outer diameter; and (b) at least two of the four optical fibers. The optical fiber has a clad outer diameter reduced to the same diameter. (C) Next, the four optical fibers are symmetrically arranged, and optical fibers having different clad outer diameters are adjacent to each other. Each optical fiber is brought into contact with only two adjacent optical fibers, and the four optical fibers are collectively fused along the longitudinal direction of the respective optical fibers, and then fused and stretched. (D) At the time of fusion-stretching of each of the optical fibers, monitor light of a predetermined wavelength is incident on the input side of one of the optical fibers, and an optical output detection means is connected to the output side of each of the optical fibers. The above each light The manufacturing method is preferably characterized in that the output from the fiber is monitored, and (e) the collective fusion drawing is stopped when the output from each of the optical fibers reaches a desired value. To be done.
【0010】このとき、好ましくは、前記2種類の異な
るクラッド外径を有するシングルモード光ファイバの融
着延伸前のクラッド外径をD1 、D2 とするとき、クラ
ッド外径比D2 /D1 は、0.24以上、0.85以下
の範囲に、特に好ましくは0.75以上、0.81以下
となるように選ばれる。At this time, preferably, when the cladding outer diameters before fusion drawing of the single mode optical fibers having the two different cladding outer diameters are D 1 and D 2 , the cladding outer diameter ratio D 2 / D 1 is selected in the range of 0.24 or more and 0.85 or less, particularly preferably 0.75 or more and 0.81 or less.
【0011】[0011]
【実施例】以下、本発明に係る4出力端を有する複合型
光ファイバカプラ及びその製造方法を図面に則して更に
詳しく説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A composite optical fiber coupler having four output ends and a method for manufacturing the same according to the present invention will be described below in more detail with reference to the drawings.
【0012】図1を参照すると、本発明に係る複合型光
ファイバカプラ1は、4本のシングルモード光ファイバ
f1 〜f4 を一括融着延伸して光結合部2が形成され
る。本発明に従えば、4本のシングルモード光ファイバ
f1 〜f4 は2種類の異なる伝搬定数を有するシングル
モード光ファイバからなり、この実施例では、光ファイ
バf1 とf3 が同じ伝搬定数を有し、光ファイバf2 と
f4 が同じ伝搬定数を有する。本発明の複合型光ファイ
バカプラ1の光結合部2は、図1(B)にその断面を示
すように、4本の各光ファイバf1 〜f4 は、左右対称
な配置をとり、且つ異なる伝搬定数を有する光ファイバ
が隣接し、又、各光ファイバはそれぞれ隣接する2本の
光ファイバとのみ融着延伸されていることを特徴とす
る。Referring to FIG. 1, in a composite optical fiber coupler 1 according to the present invention, four single mode optical fibers f 1 to f 4 are collectively fused and extended to form an optical coupling portion 2. According to the present invention, the four single-mode optical fibers f 1 to f 4 are single-mode optical fibers having two different propagation constants, and in this embodiment, the optical fibers f 1 and f 3 have the same propagation constant. And the optical fibers f 2 and f 4 have the same propagation constant. In the optical coupling section 2 of the composite optical fiber coupler 1 of the present invention, as shown in the cross section of FIG. 1B, the four optical fibers f 1 to f 4 are arranged symmetrically, and It is characterized in that optical fibers having different propagation constants are adjacent to each other, and each optical fiber is fused and drawn only with two adjacent optical fibers.
【0013】斯かる構成により、本発明の複合型光ファ
イバカプラ1は、例えば2×2光ファイバカプラと分波
合波光ファイバカプラとを複合した光ファイバカプラと
なる。つまり、本実施例では、光ファイバf1 とf3 に
て2×2光ファイバカプラが構成され、光ファイバf2
とf4 にて分波合波光ファイバカプラが構成される。With such a configuration, the composite optical fiber coupler 1 of the present invention is an optical fiber coupler that combines, for example, a 2 × 2 optical fiber coupler and a demultiplexing / combining optical fiber coupler. That is, in this embodiment, the optical fibers f 1 and f 3 form a 2 × 2 optical fiber coupler, and the optical fiber f 2
And f 4 form a demultiplexing / combining optical fiber coupler.
【0014】つまり、光結合部2は、2種類の異なる伝
搬定数を有するシングルモード光ファイバ各2本が左右
対称な配置とされるので、同じ伝搬定数を有する各2本
を光入力・出力端とするとき、或る波長で光分岐比率を
実質的に0:100にすることができる。異なる伝搬定
数を有する他の2本の光ファイバは、異なる波長で光分
岐比率が実質的に0:100とされる。従って、延伸量
を適当に選ぶとき、2本の光ファイバ組の一つを、本実
施例では光ファイバf2 、f4 を光入力・出力端とする
と少なくとも2つの波長で分岐比率を実質的に0:10
0にすることができ、分波合波光ファイバカプラとする
ことができる。又、他の2本の光ファイバ組f1 、f3
を光入力・出力端とすると、特定の波長で光分岐比率が
等しくなるようにすることができ、その時、別の2本の
光ファイバ組f2 、f4 への光出力は、十分小さくな
り、従って、 実質的に2×2カプラとなる。That is, in the optical coupling section 2, two single mode optical fibers each having two kinds of different propagation constants are symmetrically arranged, so that each two optical fibers having the same propagation constant are input / output terminals. Then, the optical branching ratio can be substantially 0: 100 at a certain wavelength. The other two optical fibers having different propagation constants have an optical branching ratio of substantially 0: 100 at different wavelengths. Therefore, when one of the two optical fiber groups, that is, the optical fibers f 2 and f 4 in this embodiment, are used as the optical input / output ends when properly selecting the amount of extension, the branching ratio is substantially equal to at least two wavelengths. At 0:10
It can be 0, and it can be a demultiplexing / combining optical fiber coupler. In addition, the other two optical fiber sets f 1 , f 3
When the optical input and output terminals are, the optical branching ratios can be made equal at a specific wavelength, and at that time, the optical output to the other two optical fiber groups f 2 and f 4 becomes sufficiently small. Therefore, it is substantially a 2 × 2 coupler.
【0015】斯かる本発明の複合型光ファイバカプラ1
の特徴ある構成は、次に説明する製造方法を参照すると
より良く理解されるであろう。The composite optical fiber coupler 1 of the present invention
The characteristic construction of will be better understood with reference to the manufacturing method described below.
【0016】本実施例によれば、図2に示すように、先
ず、コア径がd、クラッド外径がDとされる同じシング
ルモード光ファイバを適度の長さに切断して4本準備す
る。例えば2本の光ファイバは、つまり、第1及び第3
の光ファイバf1 、f3 は、クラッド外径を縮径するこ
となく、そのまま使用する。即ち、光ファイバf1 、f
3 の外径D1 、D3 は、D1 =D3 =Dである。一方、
他の2本の光ファイバ、つまり、第2及び第4の光ファ
イバf2 、f4 のクラッド外径Dは、所定の径D2 (=
D4 )にまで縮径され、縮径部分f2 ’(f4 ’)が形
成される。この縮径作業をエッチングにて行なう場合に
は、フッ酸若しくはフッ酸とエッチピット防止剤(例え
ばフッ化アンモニウム)混合液のようなエッチング液を
用いて、このエッチング液に光ファイバf2 、f4 を接
触させることにより行うことができる。エッチング条件
は、所望される縮径量により種々に変更可能であるが、
通常、エッチング温度30〜60℃、処理時間5〜30
分とされる。According to this embodiment, as shown in FIG. 2, first, the same single mode optical fiber having a core diameter of d and a cladding outer diameter of D is cut into an appropriate length to prepare four pieces. . For example, two optical fibers are the first and the third.
The optical fibers f 1 and f 3 are used as they are without reducing the cladding outer diameter. That is, the optical fibers f 1 and f
Outer diameter of 3 D 1, D 3 is D 1 = D 3 = D. on the other hand,
The clad outer diameter D of the other two optical fibers, that is, the second and fourth optical fibers f 2 and f 4 is a predetermined diameter D 2 (=
The diameter is reduced to D 4 ), and a reduced diameter portion f 2 ′ (f 4 ′) is formed. When this diameter reducing operation is performed by etching, an etching solution such as hydrofluoric acid or a mixed solution of hydrofluoric acid and an etch pit inhibitor (for example, ammonium fluoride) is used, and the optical fibers f 2 and f are added to the etching solution. It can be performed by bringing 4 into contact. The etching conditions can be variously changed according to the desired diameter reduction amount,
Usually, etching temperature is 30 to 60 ° C., processing time is 5 to 30
Considered as minutes.
【0017】光ファイバf2 、f4 の縮径は、上述のよ
うにエッチングにより行なうこともできるが、これに限
定されず、例えば砥粒による機械的研磨などをも採用す
ることができる。更には、光ファイバの一部を予め溶融
延伸によりクラッド外径を縮径する方法も採用すること
ができる。又、もともと光ファイバのクラッド外径Dが
縮径後の外径D2 (=D4 )にて作製されたものであれ
ば、これをそのまま使用することができ上記縮径工程は
省略することができる。The optical fibers f 2 and f 4 can be reduced in diameter by etching as described above, but the invention is not limited to this. For example, mechanical polishing with abrasive grains can be employed. Furthermore, a method of previously reducing the outer diameter of the cladding by melt-drawing a part of the optical fiber can also be adopted. Further, if the cladding outer diameter D of the optical fiber is originally manufactured with the outer diameter D 2 (= D 4 ) after the diameter reduction, this can be used as it is and the above diameter reduction step can be omitted. You can
【0018】更に、光ファイバf2 、f4 を所定の系D
2 (=D4 )にまで縮径するのみでなく、光ファイバf
1 、f3 も所定の径D1 ’(=D3 ’)にまで縮径し、
例えばD1 ’>D2 とすることで、2種類の融着延伸さ
れる部分のクラッド外径が異なる光ファイバ、即ち2種
類の異なる伝搬定数を有するようにすることもできる。Further, the optical fibers f 2 and f 4 are connected to a predetermined system D
Not only is the diameter reduced to 2 (= D 4 ), but the optical fiber f
1 and f 3 are also reduced to a predetermined diameter D 1 ′ (= D 3 ′),
For example, by setting D 1 ′> D 2 , it is possible to have two types of optical fibers having different cladding outer diameters in the fusion-stretched portions, that is, two different propagation constants.
【0019】次いで、各光ファイバf1 〜f4 を、光フ
ァイバf2 、f4 に関してはその縮径部分f2 ’、f
4 ’が、図3に示されるように、隣接する2本の光ファ
イバとのみ接触するように、即ち、第1の光ファイバf
1 に関して言えば、第2及び第4の光ファイバf2 、f
4 の縮径部分f2 ’、f4 ’とのみ接触し、第3の光フ
ァイバf3 とは接触せず、又、第3の光ファイバf3 に
関して言えば、第2及び第4の光ファイバf2 、f4 の
縮径部分f2 ’、f4 ’とのみ接触し、更に、第2及び
第4の光ファイバf2 、f4 の縮径部分f2 ’、f4 ’
も又互いに接触することがないようにして、各光ファイ
バを長手方向に平行に沿わせて、つまり、光ファイバf
1 とf3 のコア中心を結ぶ線L1 並びに光ファイバf2
とf4 のコア中心を結ぶ線L2 に対してそれぞれ左右対
称となるよう配置して、融着延伸台に取り付ける。そし
て、先ず、各光ファイバf1 〜f4 を、前記配置状態を
維持しながら、例えば火炎トーチを用いて1000〜2
000℃に加熱して、所定長さに亘って融着する。その
後、引き続いて、この融着部を一括して融着延伸処理す
る。通常、融着及びその後の融着延伸処理は同一工程に
て実施される。Next, each of the optical fibers f 1 to f 4 is reduced in diameter with respect to the optical fibers f 2 and f 4 , f 2 ′ and f.
As shown in FIG. 3, 4 ′ contacts only two adjacent optical fibers, that is, the first optical fiber f
With respect to 1 , the second and fourth optical fibers f 2 , f
4 of reduced diameter portion f 2 ', f 4' in contact only, the third optical fiber f 3 without contact, also a third As for the optical fiber f 3, the second and fourth light fiber f 2, reduced diameter portion f 2 of f 4 ', f 4' in contact only with the further second and fourth reduced diameter portion f 2 of the optical fiber f 2, f 4 ', f 4'
Also, the respective optical fibers are arranged parallel to the longitudinal direction so that they do not contact each other, that is, the optical fiber f.
A line L 1 connecting the core centers of 1 and f 3 and an optical fiber f 2
And f 4 are arranged symmetrically with respect to a line L 2 connecting the center of the cores and attached to the fusion drawing stand. Then, first, each optical fiber f 1 to f 4 is maintained in the above-described arrangement state, for example, by using a flame torch, 1000 to 2
Heat to 000 ° C. and fuse over a predetermined length. Then, subsequently, the fusion-bonded portion is collectively subjected to fusion-bonding and stretching treatment. Usually, the fusion bonding and the subsequent fusion stretching process are performed in the same step.
【0020】融着延伸処理は、通常の方法に従って行な
うことができ、例えば、火炎バーナ、ヒーターレーザ、
小型電気炉等適宜の加熱装置を用いて、一般に1300
〜2000℃の温度で加熱しながら、融着延伸台を、例
えばラック−ピニオン機構を介して光ファイバを軸方向
両側に例えば0.05〜10mm/分の速度で引っ張る
ことにより行い得る。The fusion-stretching treatment can be carried out according to a usual method, for example, flame burner, heater laser,
Using a suitable heating device such as a small electric furnace, generally 1300
The fusion-stretching stage can be carried out by pulling the optical fiber axially on both sides in the axial direction at a rate of, for example, 0.05 to 10 mm / minute while heating at a temperature of ˜2000 ° C., for example, via a rack-pinion mechanism.
【0021】本実施例によれば、光ファイバf1 〜f4
の融着延伸時には、いずれかの光ファイバ、本実施例で
は第1の光ファイバf1 の入力側にLD光源から、所定
波長の、例えば1.55μmのモニター光を入射し、各
光ファイバf1 〜f4 の出力側には光出力検知手段、例
えばホトダイオードのような受光素子を接続し、各光フ
ァイバf1 〜f4 からの出力をモニターする。そして、
各光ファイバf1 〜f4 からの出力が所望の値となった
時に、例えば、光ファイバf1 とf3 からの出力が最初
に等しくなった延伸量にて停止する。別法として、第2
の光ファイバf2 の入力側にLD光源から、所定波長
の、例えば1.31μmのモニター光を入射し、各光フ
ァイバf1 〜f4 の出力側には光出力検知手段、例えば
ホトダイオードのような受光素子を接続し、各光ファイ
バf1 〜f4 からの出力をモニターする。そして、各光
ファイバf1 〜f4 からの出力が所望の値となった時
に、例えば、光ファイバf4 からの出力が最初に極大と
なった延伸量にて停止する。According to this embodiment, the optical fibers f 1 to f 4 are
At the time of fusion splicing and drawing, a monitor light of a predetermined wavelength, for example, 1.55 μm is incident from the LD light source on the input side of any one of the optical fibers, in this embodiment the first optical fiber f 1 , 1 to the output side of ~f 4 connected optical output detecting means, for example, a light receiving element such as a photodiode, for monitoring the output from the optical fibers f 1 ~f 4. And
When the output from each of the optical fibers f 1 to f 4 reaches a desired value, for example, the outputs from the optical fibers f 1 and f 3 are stopped at the first stretched amount. Alternatively, the second
A monitor light of a predetermined wavelength, for example 1.31 μm, is incident on the input side of the optical fiber f 2 from the LD light source, and the output side of each of the optical fibers f 1 to f 4 has a light output detecting means, such as a photodiode. connect Do light receiving elements, to monitor the output from the optical fibers f 1 ~f 4. Then, when the output from each of the optical fibers f 1 to f 4 reaches a desired value, for example, the output from the optical fiber f 4 is stopped at the first stretched amount.
【0022】本発明によれば、上述のようにして、1回
の融着延伸により、図1に示すような、4入力端と4出
力端とを有する複合型光ファイバカプラ1を極めて効率
よく製造することができる。According to the present invention, as described above, the composite optical fiber coupler 1 having four input ends and four output ends as shown in FIG. It can be manufactured.
【0023】このような本発明の複合型光ファイバカプ
ラ1においては、上述からも理解されるように、融着延
伸部の、つまり、融着延伸される各光ファイバf1 〜f
4 を特定の位置関係に維持して融着延伸することが極め
て重要である。同時に、各光ファイバf1 〜f4 の融着
延伸前のクラッド外径D1 〜D4 の関係も又重要であ
る。In the composite optical fiber coupler 1 of the present invention as described above, as will be understood from the above, each of the optical fibers f 1 to f of the fusion extending portion, that is, the fusion extending.
It is extremely important to perform fusion-bonding stretching while maintaining 4 in a specific positional relationship. At the same time, the relationship of the optical fibers f 1 ~f before fusing stretching 4 cladding diameter D 1 to D 4, it is also important.
【0024】本発明者らの研究実験の結果によれば、本
発明の複合型光ファイバカプラ1は、それを構成する第
1、第2、第3及び第4の光ファイバf1 〜f4 の融着
延伸前のクラッド外径D1 〜D4 を、融着延伸前に光フ
ァイバf1 〜f4 4本の中の少なくとも2本、例えば、
光ファイバf2 〜f4 のクラッド外径を縮径し、クラッ
ド外径比D2 (=D4 )/D1 (=D3 )を0.24以
上0.85以下とすることで好適に製造し得るものであ
る。特に、クラッド外径比D2 (=D4 )/D1 (=D
3 )が0.75以上0.81以下とした時に極めて好適
に製造し得ることを見出した。According to the results of the research conducted by the present inventors, the composite optical fiber coupler 1 of the present invention has the first, second, third and fourth optical fibers f 1 to f 4 constituting the composite optical fiber coupler 1. of the fused and extended previous cladding diameter D 1 to D 4, at least two in an optical fiber f 1 ~f 4 4 present before fused and extended, for example,
It is preferable to reduce the cladding outer diameter of the optical fibers f 2 to f 4 and set the cladding outer diameter ratio D 2 (= D 4 ) / D 1 (= D 3 ) to 0.24 or more and 0.85 or less. It can be manufactured. In particular, the cladding outer diameter ratio D 2 (= D 4 ) / D 1 (= D
It was found that when 3 ) is 0.75 or more and 0.81 or less, it can be manufactured very suitably.
【0025】クラッド外径比D2 (=D4 )/D1 (=
D3 )が0.85を超えると、伝搬定数の差異が充分大
きくないので、例えば光ファイバf1 (又は光ファイバ
f3)を入力端にするとき、光ファイバf2 及びf4 の
出力端の分岐比率が十分に小さくならず、実質的に2×
2光ファイバカプラとならず、好ましくない。又、クラ
ッド外径比D2 (=D4 )/D1 (=D3 )が0.24
より小さいと、伝搬定数の差異は充分大きいが、図4に
示す特定の位置関係に各光ファイバf1 〜f4を維持し
つつ融着延伸することが困難となり、即ち融着延伸が進
むと、図3において各光ファイバf1 〜f4 で囲まれる
空隙が、溶融したクラッドにより満たされることが頻々
起き、好ましくない。Clad outer diameter ratio D 2 (= D 4 ) / D 1 (=
If D 3 ) exceeds 0.85, the difference in the propagation constants is not sufficiently large, so that when the optical fiber f 1 (or the optical fiber f 3 ) is used as the input end, the output ends of the optical fibers f 2 and f 4 are used. The branching ratio of is not sufficiently small, and is substantially 2 ×
It is not preferable because it does not work as a two-fiber coupler. In addition, the cladding outer diameter ratio D 2 (= D 4 ) / D 1 (= D 3 ) is 0.24.
If it is smaller, the difference in propagation constant is sufficiently large, but it becomes difficult to perform fusion splicing while maintaining the respective optical fibers f 1 to f 4 in the specific positional relationship shown in FIG. 4, that is, when fusion fusion stretching proceeds. 3, the voids surrounded by the optical fibers f 1 to f 4 are often filled with the melted cladding, which is not preferable.
【0026】一方、クラッド外径比D2 (=D4 )/D
1 (=D3 )を0.85以下、より好ましくは0.81
以下とすることで、伝搬定数の差異を充分大きくでき、
例えば光ファイバf1 (又は光ファイバf3 )を入力端
にするとき、光ファイバf2及びf4 の出力端の分岐比
率を十分に小さくでき、実質的に2×2光ファイバカプ
ラとすることが容易となる。又、クラッド外径比D2
(=D4 )/D1 (=D3 )を0.24以上、より好ま
しくは0.75以上とすると、図3に示す特定の位置関
係に各光ファイバf1 〜f4 を維持しつつ融着延伸する
ことが極めて容易となり、融着延伸が進むとも、図3に
おいて各光ファイバf1 〜f4 で囲まれる空隙が、溶融
したクラッドにより満たされることはない。On the other hand, the cladding outer diameter ratio D 2 (= D 4 ) / D
1 (= D 3 ) is 0.85 or less, more preferably 0.81
By setting the following, the difference in propagation constant can be made sufficiently large,
For example, when the optical fiber f 1 (or the optical fiber f 3 ) is used as the input end, the branching ratio of the output ends of the optical fibers f 2 and f 4 can be made sufficiently small, and a substantially 2 × 2 optical fiber coupler is used. Will be easier. Also, the clad outer diameter ratio D 2
When (= D 4 ) / D 1 (= D 3 ) is 0.24 or more, more preferably 0.75 or more, while maintaining the respective optical fibers f 1 to f 4 in the specific positional relationship shown in FIG. The fusion-stretching becomes extremely easy, and even if the fusion-stretching proceeds, the voids surrounded by the optical fibers f 1 to f 4 in FIG. 3 are not filled with the melted cladding.
【0027】このように、第1、第2、第3及び第4の
光ファイバf1 〜f4 のクラッド外径D1 〜D4 を上記
の極めて好適な関係となるように選定して製造された、
本発明の複合型光ファイバカプラにおける分岐比率の波
長依存性を図4及び図5に示す。図4は、第1或は第3
光ファイバf1 、f3 の入力端に入力した場合の各光フ
ァイバf1 〜f4 の出力端の分岐比率を示し、図5は、
第2或は第4光ファイバf2 、f4 の入力端に入力した
場合の各光ファイバf1 〜f4 の出力端の分岐比率を示
す。図4及び図5から、本発明の複合型光ファイバカプ
ラ1は、1.55μmの波長にて、第1と第3の光ファ
イバf1 、f3 が2×2光ファイバカプラとして動作
し、又、第2と第4の光ファイバf2 、f4 は、波長
1.31μmと波長1.55μmとを合波及び分波する
ことのできる分波合波光ファイバカプラとして動作して
いることが分かる。As described above, the cladding outer diameters D 1 to D 4 of the first, second, third and fourth optical fibers f 1 to f 4 are selected and manufactured so as to have the above-mentioned extremely suitable relationship. Was done,
The wavelength dependence of the branching ratio in the composite optical fiber coupler of the present invention is shown in FIGS. FIG. 4 shows the first or third
FIG. 5 shows the branching ratios of the output ends of the optical fibers f 1 to f 4 when input to the input ends of the optical fibers f 1 and f 3 .
The branching ratios at the output ends of the respective optical fibers f 1 to f 4 when input to the input ends of the second or fourth optical fibers f 2 and f 4 are shown. From FIG. 4 and FIG. 5, the composite optical fiber coupler 1 of the present invention has the first and third optical fibers f 1 and f 3 operating as a 2 × 2 optical fiber coupler at a wavelength of 1.55 μm. Further, the second and fourth optical fibers f 2 and f 4 operate as a demultiplexing / combining optical fiber coupler capable of multiplexing and demultiplexing the wavelength of 1.31 μm and the wavelength of 1.55 μm. I understand.
【0028】本発明の複合型光ファイバカプラ1は、光
結合部2がシングルモード光ファイバ4本を一括延伸し
構成されるので、機械的強度が増大される。又、周囲温
度の変化に対し、光結合長の変化量が等しく且つ小さ
く、結果として支持板に固定するとき温度特性が小さく
される。In the composite type optical fiber coupler 1 of the present invention, since the optical coupling portion 2 is constructed by extending four single mode optical fibers at a time, the mechanical strength is increased. Further, the change amount of the optical coupling length is equal to and small with respect to the change of the ambient temperature, and as a result, the temperature characteristic is reduced when fixing to the support plate.
【0029】更に、本発明を実施例について詳しく説明
する。Further, the present invention will be described in detail with reference to Examples.
【0030】実施例1 本発明に従って、複合型光ファイバカプラを、以下の手
順にて製造した。Example 1 In accordance with the present invention, a composite optical fiber coupler was manufactured by the following procedure.
【0031】シングルモード光ファイバf1 〜f4 とし
て、コア径(d)が10μm、クラッド外径(D)が1
25μmのシングルモード光ファイバを使用した。各光
ファイバは、適度の長さに切断した後、各光ファイバの
所定のファイバ長の部分の被覆コーティングを除去し
た。これによって露出したクラッド部分を洗浄クリーニ
ングして、UV被覆などの残渣を除いた。As the single mode optical fibers f 1 to f 4 , the core diameter (d) is 10 μm and the cladding outer diameter (D) is 1.
A 25 μm single mode optical fiber was used. Each optical fiber was cut to an appropriate length, and then the coating coating on the predetermined fiber length portion of each optical fiber was removed. The clad portion exposed by this was washed and cleaned to remove residues such as UV coating.
【0032】次いで、2本の光ファイバ、即ち、第1及
び第3の光ファイバf1 、f3 はこのまま使用し、即
ち、D1 =D3 =125μmとし、他の2本の光ファイ
バ、即ち、第2及び第4の光ファイバf2 及びf4 は、
フッ酸若しくはフッ酸とエッチピット防止剤の混合液を
用いて、エッチング温度30℃、処理時間10分にてエ
ッチングし、クラッド径(D2 、D4 )を96μmにま
で縮径した。Then, the two optical fibers, that is, the first and third optical fibers f 1 and f 3 are used as they are, that is, D 1 = D 3 = 125 μm, and the other two optical fibers, That is, the second and fourth optical fibers f 2 and f 4 are
Etching was performed using hydrofluoric acid or a mixed solution of hydrofluoric acid and an etch pit inhibitor at an etching temperature of 30 ° C. for a processing time of 10 minutes to reduce the cladding diameters (D 2 , D 4 ) to 96 μm.
【0033】このようにして得た光ファイバf1 〜f4
を、特に光ファイバf2 及びf4 に関してはその縮径部
分f2 ’、f4 ’を、長手方向に沿わせて、しかも、図
3示すように、各光ファイバは隣接する2本の光ファイ
バとのみ接触するようにして、且つ、各光ファイバf1
〜f4 は、第1の光ファイバf1 と第3の光ファイバf
3 のコア中心を結ぶ線に対して、更に、第2の光ファイ
バf2 と第4の光ファイバf4 のコア中心を結ぶ線に対
しても左右対称となるように配置して、この配置状態を
維持しながら火炎トーチを用いて1200℃に加熱して
融着した。融着長さは15mmであった。次いで、この
融着部15mmを、火炎トーチを用いて1500〜16
00℃に加熱しながら、1.6mm/分の速度で引っ張
ることにより、一括して融着延伸処理を行なった。The optical fibers f 1 to f 4 thus obtained
In particular, regarding the optical fibers f 2 and f 4 , the reduced diameter portions f 2 ′ and f 4 ′ are arranged along the longitudinal direction, and as shown in FIG. 3, each optical fiber has two adjacent optical fibers. Each optical fiber f 1 is made to contact only with the fiber.
To f 4 are the first optical fiber f 1 and the third optical fiber f
The line connecting the core centers of 3 and the line connecting the core centers of the second optical fiber f 2 and the fourth optical fiber f 4 are symmetrically arranged. While maintaining the state, a flame torch was used to heat to 1200 ° C. for fusion. The fusion length was 15 mm. Then, the fused portion 15 mm is heated to 1500 to 16 using a flame torch.
While being heated to 00 ° C., the film was stretched at a rate of 1.6 mm / min to collectively perform the fusion drawing process.
【0034】融着延伸時には、第1の光ファイバf1 の
入力側にLD光源から、1.55μmのモニター光を入
射し、各光ファイバf1 〜f4 の出力側の光出力をホト
ダイオードにて検知して、個々の光ファイバの光出力を
モニターしながら一括延伸した。そして、第1の光ファ
イバf1 と第3の光ファイバf3 の光出力値が最初に等
しくなった点で光ファイバの融着延伸を停止した。最適
の延伸量は13.0mmであった。[0034] when fused and extended from LD light source to a first input side of the optical fiber f 1, incident monitor light 1.55 .mu.m, the light output of the output side of the optical fibers f 1 ~f 4 to photodiode Was detected and the optical output of each optical fiber was monitored, and the fiber was collectively stretched. Then, the fusion splicing of the optical fibers was stopped at the point where the optical output values of the first optical fiber f 1 and the third optical fiber f 3 first became equal. The optimum stretch amount was 13.0 mm.
【0035】このようにして作製された複合型光ファイ
バカプラを、一つの同じ支持板に樹脂で固定し、一つの
パッケージ内に収納した。従来の、2×2光ファイバカ
プラと分波合波光ファイバカプラとを個々に作製し個別
に支持板に固定して、その後、これら二つの光ファイバ
カプラを同一のパッケージ内に収容する方法にて作製さ
れた複合型光ファイバカプラに比較すると、例えば円筒
状のパッケージに収納する場合には、パッケージの直径
が従来の50mmから38mmへと縮小された。更に、
一つの複合型光ファイバカプラを作製するに要する時間
も、従来の2/3にまで減少することができた。The composite optical fiber coupler manufactured in this manner was fixed to one and the same support plate with resin and housed in one package. In the conventional method, a 2 × 2 optical fiber coupler and a demultiplexing / multiplexing optical fiber coupler are individually manufactured and individually fixed to a support plate, and then these two optical fiber couplers are housed in the same package. In comparison with the produced composite optical fiber coupler, for example, in the case of housing in a cylindrical package, the diameter of the package has been reduced from 50 mm of the conventional package to 38 mm. Furthermore,
The time required to manufacture one composite optical fiber coupler could be reduced to 2/3 of the conventional one.
【0036】更に重要なことに、本発明によれば、本発
明の複合型光ファイバカプラは、光結合部が4本のシン
グルモード光ファイバを一括融着延伸し光結合部を形成
するために、2×2光ファイバカプラと分波合波光ファ
イバカプラにおいて温度特性が概ね揃い、しかも、光結
合部が4本の光ファイバで形成されているので、光ファ
イバカプラ自体の機械的強度を増大することができた。More importantly, according to the present invention, in the composite optical fiber coupler of the present invention, a single mode optical fiber having four optical coupling portions is collectively fused and drawn to form an optical coupling portion. The temperature characteristics of the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler are almost the same, and since the optical coupling portion is formed by four optical fibers, the mechanical strength of the optical fiber coupler itself is increased. I was able to.
【0037】このようにして得られた本発明の複合型光
ファイバカプラの分岐比率の波長依存性を調べたとこ
ろ、本発明の複合型光ファイバカプラ1は、 第1の光
ファイバf1 を入力端に選び分岐比率の波長依存性を測
定したところ、図4に一例を示すように、第1の光ファ
イバf1 或は第3の光ファイバf3 から光入力すると
き、第2及び第4の光ファイバf2 、f4 の出力端の分
岐比率は十分に小さく、実質的に第1の光ファイバf1
と第3の光ファイバf3 とからなる入力、出力端がそれ
ぞれ2端子の光ファイバカプラと見做せ、1.55μm
の波長にて、第1と第3の光ファイバf1 、f3 が2×
2光ファイバカプラとして動作し、又、第2の光ファイ
バf2 を入力端に選び分岐比率の波長依存性を測定した
ところ、図5に一例を示すように、第2の光ファイバf
2 或は第4の光ファイバf4 から光入力するとき、第1
及び第3の光ファイバf1 、f3 の出力端の分岐比率は
十分に小さく、実質的に第2の光ファイバf2 と第4の
光ファイバf4 とからなる入力、出力端がそれぞれ2端
子の光ファイバカプラと見做せ、第2と第4の光ファイ
バf2 、f4 は、波長1.31μmと波長1.55μm
とを合波及び分波することのできる分波合波光ファイバ
カプラとして動作した。When the wavelength dependence of the branching ratio of the thus obtained composite optical fiber coupler of the present invention was investigated, the composite optical fiber coupler 1 of the present invention inputs the first optical fiber f 1 . When the wavelength dependence of the branching ratio selected at the end is measured, as shown in an example in FIG. 4, when the light is input from the first optical fiber f 1 or the third optical fiber f 3 , Of the optical fibers f 2 and f 4 of the first optical fiber f 1 are substantially small.
, And the third optical fiber f 3 can be regarded as an optical fiber coupler having two terminals at the input and output ends.
Of the first and third optical fibers f 1 and f 3 at the wavelength
It operates as a two-optical fiber coupler, and when the second optical fiber f 2 is selected as the input end and the wavelength dependence of the branching ratio is measured, the second optical fiber f 2 is shown as an example in FIG.
When light is input from the second or fourth optical fiber f 4 , the first
And the branching ratios of the output ends of the third optical fibers f 1 and f 3 are sufficiently small, and the input and output ends of the second optical fiber f 2 and the fourth optical fiber f 4 are 2 each. Considered as the optical fiber coupler of the terminal, the second and fourth optical fibers f 2 and f 4 have a wavelength of 1.31 μm and a wavelength of 1.55 μm.
It operated as a demultiplexing / combining optical fiber coupler capable of multiplexing and demultiplexing.
【0038】なお、この実施例では、2×2光ファイバ
カプラに対する波長1.55μmにおける挿入損失は、
最大3.59dBであり、分波合波光ファイバカプラに
対する過剰損失も、波長1.31μmに対して0.21
dB以内であり、波長1.55μmに対して0.21d
B以内であった。更に、温度安定性について言えば、温
度範囲−20℃〜70℃の挿入損失変化量が何れも最大
0.20dBである。In this embodiment, the insertion loss at the wavelength of 1.55 μm for the 2 × 2 optical fiber coupler is
The maximum is 3.59 dB, and the excess loss for the demultiplexing / multiplexing optical fiber coupler is 0.21 for a wavelength of 1.31 μm.
Within dB and 0.21d for wavelength 1.55 μm
It was within B. Further, regarding the temperature stability, the maximum insertion loss change amount in the temperature range of −20 ° C. to 70 ° C. is 0.20 dB.
【0039】[0039]
【発明の効果】以上説明したように、本発明による複合
型光ファイバカプラは、2種類の異なる伝搬定数を有す
る各2本のシングルモード光ファイバ、合計4本が一括
融着延伸された光結合部を有し、しかも、この光結合部
は、各光ファイバ4本は左右対称な配置をとり、且つ異
なる伝搬定数を有する光ファイバが隣接し、各光ファイ
バはそれぞれ隣接する2本の光ファイバとのみ融着延伸
されて構成されるので、伝搬定数を同じくする一組の光
ファイバ2本を光入力・出力端とする時、光出力端にお
ける分岐比率が等しい2×2光ファイバカプラとして動
作し、伝搬定数を同じくする他の光ファイバ2本を光入
力・出力端とする時、分波合波光ファイバカプラとして
動作することができる。又、本発明による複合型の光フ
ァイバカプラは、従来の2×2光ファイバカプラと分波
合波光ファイバカプラとを同一のパッケージに収納した
複合型の光ファイバカプラと比べて、大きさが著しく小
さくなり、加えて、4本のシングルモード光ファイバを
一括融着延伸し光結合部を形成される構造のため、温度
特性が概ね揃うという利点を有する。更に、光結合部が
4本の光ファイバで形成されているので、カプラの機械
的強度が大であるという利点をも有する。As described above, the composite optical fiber coupler according to the present invention is an optical coupling in which two single mode optical fibers each having two different propagation constants, a total of four fibers are fused and drawn at one time. In this optical coupling part, each of the four optical fibers is symmetrically arranged, and the optical fibers having different propagation constants are adjacent to each other. Each optical fiber is two adjacent optical fibers. Since it is constructed by fusion splicing and drawing only two optical fibers with the same propagation constant as the optical input and output ends, it operates as a 2 × 2 optical fiber coupler with the same branching ratio at the optical output end. However, when two other optical fibers having the same propagation constant are used as optical input / output ends, they can operate as a demultiplexing / combining optical fiber coupler. Further, the composite optical fiber coupler according to the present invention is significantly larger in size than the conventional composite optical fiber coupler in which the 2 × 2 optical fiber coupler and the demultiplexing / multiplexing optical fiber coupler are housed in the same package. In addition, the structure is such that the optical coupling portion is formed by collectively fusion-stretching four single-mode optical fibers at the same time, which has the advantage that the temperature characteristics are substantially the same. Further, since the optical coupling portion is formed by four optical fibers, there is also an advantage that the mechanical strength of the coupler is large.
【図1】図1(A)は、本発明に係る複合型光ファイバ
カプラの概略構成を示す図であり、図1(B)は、図1
(A)の線A−Aに取った光結合部の断面拡大図であ
る。1 (A) is a diagram showing a schematic configuration of a composite optical fiber coupler according to the present invention, and FIG. 1 (B) is FIG.
It is an expanded sectional view of the optical coupling part taken along the line AA of (A).
【図2】本発明に係る複合型光ファイバカプラを製造す
る時に使用する各光ファイバの斜視図である。FIG. 2 is a perspective view of each optical fiber used when manufacturing the composite optical fiber coupler according to the present invention.
【図3】光結合部における一括融着延伸前の断面拡大図
である。FIG. 3 is an enlarged cross-sectional view of the optical coupling portion before collective fusion drawing.
【図4】本発明に係る複合型光ファイバカプラにて、第
1或は第3の光ファイバに入力した場合の各光ファイバ
の出力端における分岐比率を示す図である。FIG. 4 is a diagram showing the branching ratio at the output end of each optical fiber when inputting to the first or third optical fiber in the composite optical fiber coupler according to the present invention.
【図5】本発明に係る複合型光ファイバカプラにて、第
2或は第4の光ファイバに入力した場合の各光ファイバ
の出力端における分岐比率を示す図である。FIG. 5 is a diagram showing a branching ratio at the output end of each optical fiber when inputting to the second or fourth optical fiber in the composite optical fiber coupler according to the present invention.
1 複合型光ファイバカプラ 2 光結合部 1 Composite type optical fiber coupler 2 Optical coupling section
Claims (7)
のシングルモード光ファイバからなる合計4本の光ファ
イバが一括融着延伸された光結合部を有する光ファイバ
カプラであって、前記光ファイバ4本は左右対称な配置
をとり、且つ異なる伝搬定数を有する光ファイバが隣接
し、しかも各光ファイバはそれぞれ隣接する2本の光フ
ァイバとのみ融着延伸されていることを特徴とする複合
型光ファイバカプラ。1. An optical fiber coupler having an optical coupling section in which a total of four optical fibers each consisting of two single-mode optical fibers having two different propagation constants are fused and stretched together. The four fibers are symmetrically arranged, and the optical fibers having different propagation constants are adjacent to each other, and each optical fiber is fused and drawn only with two adjacent optical fibers. Type optical fiber coupler.
ングルモード光ファイバは、融着延伸される部分のクラ
ッド外径が異なることを特徴とする請求項1の複合型光
ファイバカプラ。2. The composite optical fiber coupler according to claim 1, wherein the single mode optical fibers having two kinds of different propagation constants have different cladding outer diameters in the fusion spliced portions.
ングルモード光ファイバの融着延伸前のクラッド外径を
D1 、D2 とするとき、クラッド外径比D2/D1 が
0.75以上、0.81以下となるように選ばれること
を特徴とする請求項2の複合型光ファイバカプラ。3. A clad outer diameter ratio D 2 / D 1 of 0.75, where D 1 and D 2 are the clad outer diameters of the single mode optical fibers having different propagation constants before fusion drawing. 3. The composite optical fiber coupler according to claim 2, wherein the composite optical fiber coupler is selected so as to be 0.81 or less.
組は、2×2光ファイバカプラとして動作し、他方の同
じ伝搬定数を有する光ファイバ組は、2つの波長の光に
対して合波、分波することのできる分波合波光ファイバ
カプラとして動作することを特徴とする請求項1〜3の
いずれかの複合型光ファイバカプラ。4. One optical fiber set having the same propagation constant operates as a 2 × 2 optical fiber coupler, and the other optical fiber set having the same propagation constant combines the two wavelengths of light, 4. The composite optical fiber coupler according to claim 1, which operates as a demultiplexing / combining optical fiber coupler capable of demultiplexing.
本のシングルモード光ファイバを準備すること、(b)
前記4本の光ファイバの中の少なくとも2本の光ファイ
バは、クラッド外径が同じ径に縮径されること、(c)
次いで、前記4本の光ファイバを、左右対称な配置をと
り、且つ異なるクラッド外径の光ファイバが隣接し、し
かも各光ファイバはそれぞれ隣接する2本の光ファイバ
とのみ接触するようにして、前記各光ファイバを長手方
向に平行に沿わせて4本の光ファイバを一括融着し、そ
の後に融着延伸処理すること、(d)前記各光ファイバ
の融着延伸時には、いずれかの光ファイバの入力側に所
定波長のモニター光を入射し、前記各光ファイバの出力
側には光出力検知手段を接続して前記各光ファイバから
の出力をモニターすること、そして、(e)前記各光フ
ァイバからの出力が所望の値となった時に、一括融着延
伸を停止すること、を特徴とする複合型光ファイバカプ
ラの製造方法。5. (a) 4 having the same core diameter and clad outer diameter
A book of single-mode optical fibers, (b)
At least two of the four optical fibers have a cladding outer diameter reduced to the same diameter, (c)
Then, the four optical fibers are arranged symmetrically, and optical fibers having different cladding outer diameters are adjacent to each other, and each optical fiber is in contact with only two adjacent optical fibers, 4 optical fibers are fused together at a time along each of the optical fibers parallel to the longitudinal direction, and then fused and stretched; and (d) when the optical fiber is fused and stretched, one of the optical fibers Monitor light of a predetermined wavelength is incident on the input side of the fiber, and optical output detection means is connected to the output side of each optical fiber to monitor the output from each optical fiber; and (e) each of the above A method for manufacturing a composite type optical fiber coupler, characterized in that when the output from the optical fiber reaches a desired value, the collective fusion drawing is stopped.
るシングルモード光ファイバの融着延伸前のクラッド外
径をD1 、D2 とするとき、クラッド外径比D2 /D1
が0.75以上、0.81以下となるように選ばれるこ
とを特徴とする請求項5の複合型光ファイバカプラの製
造方法。6. The cladding outer diameter before fusing stretching a single-mode optical fiber having a cladding diameter of different the two when the D 1, D 2, cladding outer diameter ratio D 2 / D 1
Is selected to be 0.75 or more and 0.81 or less. 6. The method for manufacturing a composite optical fiber coupler according to claim 5, wherein
外径がエッチングにより縮径されることを特徴とする請
求項5又は6の複合型光ファイバカプラの製造方法。7. The method for manufacturing a composite optical fiber coupler according to claim 5, wherein the outer diameter of the clad of the two optical fibers is reduced by etching.