JPH06304239A - Adhesive tape for skin therapy - Google Patents
Adhesive tape for skin therapyInfo
- Publication number
- JPH06304239A JPH06304239A JP5099957A JP9995793A JPH06304239A JP H06304239 A JPH06304239 A JP H06304239A JP 5099957 A JP5099957 A JP 5099957A JP 9995793 A JP9995793 A JP 9995793A JP H06304239 A JPH06304239 A JP H06304239A
- Authority
- JP
- Japan
- Prior art keywords
- water
- adhesive tape
- adhesive
- skin
- water absorptive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ガーゼ等の固定に用い
られる医療補助用の皮膚用粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a medical adhesive skin adhesive tape used for fixing gauze or the like.
【０００２】[0002]
【従来の技術】従来、ガーゼなどの固定に使用する医療
補助用の粘着テープは、粘着剤層の厚さ方向に複数の微
細な貫通孔を設けたり、また通気性基材又は複数の貫通
孔を設けた基材を用いることにより、貼付箇所の皮膚の
発汗や、代謝を妨げないようにしている。しかしなが
ら、従来の粘着テープは、汗の透過吸収が不十分なた
め、発汗が多い場合には発汗（代謝）を妨げるという欠
点があり、また皮膚と粘着テープとの間に貯留した汗
で、テープの粘着力が低下するという欠点があった。2. Description of the Related Art Conventionally, an adhesive tape for medical assistance, which is used for fixing gauze or the like, has a plurality of fine through holes formed in the thickness direction of the adhesive layer, a breathable substrate or a plurality of through holes. By using the base material provided with, the perspiration and metabolism of the skin at the application site are prevented. However, the conventional adhesive tape has a drawback that it prevents perspiration (metabolism) when perspiration is large because the permeation and absorption of sweat are insufficient. Also, the sweat accumulated between the skin and the adhesive tape causes However, there was a drawback that the adhesive strength of was decreased.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、汗の
透過吸収性が優れているため、皮膚の発汗や、代謝を妨
げることがなく、また皮膚と粘着テープとの間に汗が貯
留することがないので、粘着力が低下することがない皮
膚用粘着テープを提供することにある。The object of the present invention is that the permeation and absorption of sweat is excellent, so that it does not interfere with perspiration and metabolism of the skin, and that sweat accumulates between the skin and the adhesive tape. Since it does not occur, it is an object of the present invention to provide an adhesive tape for skin in which the adhesive force does not decrease.
【０００４】[0004]
【課題を解決するための手段】本発明は、吸水性高分子
を担持した通気性基材に粘着剤層を備えた皮膚用粘着テ
ープである。以下、本発明を詳細に説明する。本発明に
用いる吸水性高分子としては、公知の水溶性又は非水溶
性の吸水性高分子を用いることができる。The present invention is a pressure-sensitive adhesive tape for skin comprising an air-permeable base material carrying a water-absorbing polymer and an adhesive layer. Hereinafter, the present invention will be described in detail. As the water-absorbent polymer used in the present invention, a known water-soluble or water-insoluble water-absorbent polymer can be used.
【０００５】水溶性の吸水性高分子の具体例としては、
アルギン酸、寒天、ゼラチン、グアーガム、キサンタン
ガム、デンプン、キトサン等の天然物；メチルセルロー
ス、エチルセルロース、ヒドロキシエチルセルロース、
ヒドロキシプロピルセルロース、カルボキシメチルセル
ロース、アルギン酸ナトリウム、アルギン酸プロピレン
グリコールエステル、ポリビニルアルコール、ポリビニ
ルピロリドン、ポリビニルメチルエーテル、ポリアクリ
ル酸ナトリウム、カルボキシビニルポリマー、ポリアク
リルアミド、ポリエチレンオキシド、ポリアミン等の合
成物；これらの変性物及び混合物などを挙げることがで
きる。Specific examples of the water-soluble water-absorbing polymer include:
Natural products such as alginic acid, agar, gelatin, guar gum, xanthan gum, starch, chitosan; methyl cellulose, ethyl cellulose, hydroxyethyl cellulose,
Hydroxypropyl cellulose, carboxymethyl cellulose, sodium alginate, propylene glycol alginate, polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl methyl ether, sodium polyacrylate, carboxy vinyl polymer, polyacrylamide, polyethylene oxide, polyamine, and other synthetic compounds; modified products thereof And mixtures.
【０００６】非水溶性の吸水性高分子の具体例として
は、ポリアクリル酸塩架橋物、酢酸ビニル−アクリル酸
エステル共重合体のケン化物、デンプン−ポリアクリロ
ニトリル加水分解物、デンプン−ポリアクリル酸塩架橋
物、デンプン−アクリル酸グラフト共重合物、カルボキ
シメチルセルロース架橋物等を挙げることができる。本
発明に用いる通気性基材としては、上記吸水性高分子を
後述する方法で担持することができるものであれば特に
制限はなく、例えば不織布、紙等を挙げることができ
る。中でも好ましいのは、ＪＩＳ Ｚ ０２０８に規定
する防湿包装材料の透湿度試験方法（カップ法）に準拠
して測定した透湿度が、３０００g/m2・日以上のものが
好ましい。Specific examples of the water-insoluble water-absorbing polymer include cross-linked polyacrylates, saponified vinyl acetate-acrylic acid ester copolymers, starch-polyacrylonitrile hydrolysates, starch-polyacrylic acid. Examples thereof include salt cross-linked products, starch-acrylic acid graft copolymers and carboxymethyl cellulose cross-linked products. The breathable substrate used in the present invention is not particularly limited as long as it can support the water-absorbing polymer by the method described below, and examples thereof include non-woven fabric and paper. Among them, those having a moisture permeability measured in accordance with the moisture permeability test method (cup method) of the moisture-proof packaging material defined in JIS Z 0208 is preferably 3000 g / m 2 · day or more.
【０００７】基材の厚さは、３０〜３００μm が好まし
い。本発明の粘着テープは、このような通気性基材に吸
水性高分子を担持させた後、この基材に粘着剤層を設け
ることにより、或は通気性基材に粘着剤層を設けた後、
この基材に吸水性高分子を担持させることにより得るこ
とができる。通気性基材に、吸水性高分子を担持させる
方法としては、例えば、上記吸水性高分子の水溶液又は
分散液を、上記通気性基材に含浸後、乾燥する方法を挙
げることができる。The thickness of the substrate is preferably 30 to 300 μm. In the pressure-sensitive adhesive tape of the present invention, such a breathable substrate is made to carry a water-absorbing polymer, and then the pressure-sensitive adhesive layer is provided on this substrate, or the pressure-sensitive adhesive layer is provided on the breathable substrate. rear,
It can be obtained by supporting a water-absorbing polymer on this base material. Examples of the method for supporting the water-absorbent polymer on the breathable substrate include a method of impregnating the breathable substrate with an aqueous solution or dispersion of the water-absorbent polymer and then drying.
【０００８】上記水溶液又は分散液中の吸水性高分子含
有率は、これを基材に含浸し、次いで乾燥した後に担持
できる吸水性高分子の量が、０．０１〜１０g/m2、好ま
しくは、０．０２〜２g/m2になるように適宜に調節する
ことができる。粘着剤層は、基材に粘着剤を塗工して形
成することができる。粘着剤は、公知のものを用いるこ
とができ、例えば、ゴム系粘着剤、アクリル系粘着剤、
シリコーン系粘着剤、これら２種以上の混合物等を挙げ
ることができる。本発明の粘着テープには、粘着剤層が
形成されていない基材面に、いわゆるブロッキングを防
止するための剥離処理を行っても良い。The content of the water-absorbing polymer in the above-mentioned aqueous solution or dispersion is such that the amount of the water-absorbing polymer that can be carried after impregnating the base material with the base material and then drying is 0.01 to 10 g / m 2 , preferably Can be appropriately adjusted to be 0.02 to 2 g / m 2 . The adhesive layer can be formed by applying an adhesive to a base material. Known adhesives can be used as the adhesive, for example, a rubber adhesive, an acrylic adhesive,
Examples thereof include silicone-based pressure-sensitive adhesives and mixtures of two or more of these. The adhesive tape of the present invention may be subjected to a peeling treatment for preventing so-called blocking on the surface of the base material on which the adhesive layer is not formed.
【０００９】[0009]
実施例１ セルロース繊維が主体の、バインダ加工した不織布（坪
量３０g/m2、厚さ１００μm ）に、ヒドロキシプロピル
セルロース（信越化学工業（株）製）の１重量％水溶液
を含浸させた後、１２０℃で２分間乾燥し、ヒドロキシ
プロピルセルロースを０．４g/m2担持する基材を作製し
た。得られた処理基材の切片（１２mm×１２mm）と、こ
れと同寸の未処理の不織布とを水に接触させ、その水の
浸透性を比較観察したところ、処理基材の方が浸透速度
が速かった。Example 1 A nonwoven fabric (basis weight: 30 g / m 2 , thickness: 100 μm) mainly composed of cellulose fibers was impregnated with a 1% by weight aqueous solution of hydroxypropyl cellulose (manufactured by Shin-Etsu Chemical Co., Ltd.), It was dried at 120 ° C. for 2 minutes to prepare a base material carrying 0.4 g / m 2 of hydroxypropyl cellulose. The section (12 mm x 12 mm) of the obtained treated base material and an untreated non-woven fabric of the same size were brought into contact with water, and the permeability of the water was compared and observed. Was fast.
【００１０】一方、剥離紙の片面に、固形分が２７重量
％の溶剤型アクリル粘着剤を、ハンディーアプリケータ
で塗工した直後、これに水を霧吹で散布し、次いでこれ
を加熱乾燥することにより、適度に貫通孔を有するアク
リル粘着剤からなるドライフィルムを得た。このドライ
フィルムを上記処理基材と、未処理の不織布とにそれぞ
れ転写し粘着シートを作製した。処理基材を用いた粘着
シートと、未処理の不織布を用いた粘着シートの透湿度
を、ＪＩＳ Ｚ ０２０８に規定する防湿包装材料の透
湿度試験方法（カップ法）に準拠して測定した。結果を
表１に示す。On the other hand, a solvent-type acrylic adhesive having a solid content of 27% by weight is applied to one side of a release paper with a handy applicator, immediately after that, water is sprayed on the adhesive, and then this is dried by heating. Thus, a dry film made of an acrylic pressure-sensitive adhesive having appropriate through holes was obtained. This dry film was transferred to each of the above-mentioned treated substrate and untreated non-woven fabric to prepare an adhesive sheet. The moisture vapor transmission rates of the pressure-sensitive adhesive sheet using the treated substrate and the pressure-sensitive adhesive sheet using the untreated non-woven fabric were measured according to the moisture vapor permeability test method (cup method) of the moisture-proof packaging material defined in JIS Z 0208. The results are shown in Table 1.
【００１１】実施例２ ヒドロキシプロピルセルロースの１重量％水溶液に代え
て、水にサンウェットＩＭ−１０００（デンプン−アク
リル酸グラフト共重合体、三洋化成工業（株）製）０．
１５重量％を分散した液を用いた外は、実施例１と同様
にしてサンウェットＩＭ−１０００を０．１g/m2担持す
る基材を作製した。得られた処理基材と、未処理の不織
布の水の浸透性を、実施例１と同様にして比較観察した
ところ、処理基材の方が浸透速度が速かった。上記処理
基材を用いて実施例１と同様にして粘着シートを作製
し、透湿度を測定した。結果を表１に示す。Example 2 Sunwet IM-1000 (starch-acrylic acid graft copolymer, manufactured by Sanyo Chemical Industry Co., Ltd.) was added to water in place of 1% by weight aqueous solution of hydroxypropyl cellulose.
A base material carrying 0.1 g / m 2 of Sunwet IM-1000 was prepared in the same manner as in Example 1 except that a liquid in which 15% by weight was dispersed was used. When the water permeabilities of the obtained treated substrate and untreated nonwoven fabric were compared and observed in the same manner as in Example 1, the treated substrate had a higher permeation rate. A pressure-sensitive adhesive sheet was produced in the same manner as in Example 1 using the above-mentioned treated substrate, and the water vapor transmission rate was measured. The results are shown in Table 1.
【００１２】[0012]
【表１】 [Table 1]
【００１３】表１から明らかなように、本実施例で得ら
れた粘着シートは、未処理の不織布に比べ透湿度が高
い。As is clear from Table 1, the pressure-sensitive adhesive sheet obtained in this example has a higher moisture vapor transmission rate than the untreated nonwoven fabric.
【００１４】[0014]
【発明の効果】本発明の皮膚用粘着テープは、汗の透過
吸収性が優れているため、皮膚の発汗や、代謝を妨げる
ことがなく、また皮膚と粘着テープとの間に汗が貯留す
ることがないので、粘着力が低下することがない。Since the adhesive tape for skin of the present invention has excellent permeation and absorption of sweat, it does not interfere with perspiration and metabolism of the skin, and the sweat is accumulated between the skin and the adhesive tape. Therefore, the adhesive strength does not decrease.
Claims (2)
着剤層を備えた皮膚用粘着テープ。1. A pressure-sensitive adhesive tape for skin comprising an air-permeable base material carrying a water-absorbing polymer and an adhesive layer.
が、不織布又は紙に吸水性高分子の水溶液又は分散液を
含浸後、乾燥した基材である請求項１記載の皮膚用粘着
テープ。2. The adhesive for skin according to claim 1, wherein the breathable substrate carrying the water-absorbent polymer is a substrate obtained by impregnating a nonwoven fabric or paper with an aqueous solution or dispersion of the water-absorbent polymer and then drying. tape.