JPH06279728A - Coating application method - Google Patents
Coating application methodInfo
- Publication number
- JPH06279728A JPH06279728A JP7136593A JP7136593A JPH06279728A JP H06279728 A JPH06279728 A JP H06279728A JP 7136593 A JP7136593 A JP 7136593A JP 7136593 A JP7136593 A JP 7136593A JP H06279728 A JPH06279728 A JP H06279728A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- film
- ester
- coating film
- decorative coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、硬化した上塗塗面にさ
らに文字、模様または線などの形状に美粧用塗料を塗装
して意匠性または美粧性を改良するための塗装方法にお
いて、該上塗塗面と該美粧用塗料塗膜との付着性を向上
せしめた塗装方法に関する。FIELD OF THE INVENTION The present invention relates to a coating method for improving the design or beauty of a cured topcoat surface by further applying a cosmetic coating in the shape of letters, patterns or lines. The present invention relates to a coating method in which the adhesion between the coated surface and the cosmetic coating film is improved.
【０００２】[0002]
【従来の技術及びその課題】上塗り塗装された自動車の
外板部、特にドアーロッカー部分などに、線、模様また
は文字などの形状に美粧用塗料を部分的に塗装して意匠
性や美粧性を向上せしめることは多く行われている。こ
の美粧用塗料として、これまで乾性油変性アルキド樹脂
を主成分とする常温乾燥型塗料が使用されていたが、耐
摩耗性や耐候性が劣るという欠陥があった。これらの欠
陥を解消するものとして、水酸基含有樹脂とポリイソシ
アネート化合物を主成分とする二液型塗料が使用されて
いる。2. Description of the Related Art A coating material for cosmetics is partially applied in a shape such as a line, a pattern or a character on the outer panel portion of an automobile, especially a door locker portion, which has been overcoated to improve its design and beauty. There are many things that can be improved. As this cosmetic coating, a room-temperature-drying coating containing a drying oil-modified alkyd resin as a main component has been used so far, but it has a defect of poor abrasion resistance and weather resistance. As a solution to these drawbacks, a two-pack type coating containing a hydroxyl group-containing resin and a polyisocyanate compound as main components is used.
【０００３】しかし、一方において、地球環境汚染から
耐酸性にすぐれ、しかも耐スリキズ性などを改良した上
塗塗膜が開発されており、これらの上塗塗膜の表面は従
来のものに比べて一般的に静的ガラス転移温度が高いた
めに、上記二液型美粧用塗料では上塗塗膜との付着性が
十分でないという問題点が指摘されており、その解決が
希望されている。一般に、耐酸性および耐スリキズ性な
どが改良された上塗硬化塗膜の静的ガラス転移温度は６
０〜１３０℃の範囲内に含まれており、通常の塗膜の静
的ガラス転移温度はそれより低温である。On the other hand, on the other hand, top coats having excellent acid resistance due to global environmental pollution and improved scratch resistance have been developed, and the surface of these top coats is more common than conventional ones. In addition, it has been pointed out that the above two-component cosmetic coating composition has insufficient adhesion to the top coating film due to its high static glass transition temperature, and its solution is desired. Generally, the static glass transition temperature of a top-coat cured coating having improved acid resistance and scratch resistance is 6
It is contained in the range of 0 to 130 ° C., and the static glass transition temperature of a usual coating film is lower than that.
【０００４】さらに、走行中に跳ね上げられた小石が衝
突することによって容易に塗膜が剥がれる、いわゆるチ
ッピング現象が生じやすいという問題点もある。Further, there is also a problem that a coating film is easily peeled off due to collision of pebbles flipped up during traveling, so-called chipping phenomenon easily occurs.
【０００５】[0005]
【課題を解決するための手段】本発明は、上記の問題点
の解決を目的としており、その特徴は美粧用塗料とし
て、上記二液型塗料にりん酸エステルを添加せしめたと
ころにある。SUMMARY OF THE INVENTION The present invention is intended to solve the above problems, and is characterized in that a phosphoric acid ester is added to the above-mentioned two-pack type paint as a cosmetic paint.
【０００６】すなわち、本発明は、静的ガラス転移温度
が６０〜１３０℃である硬化上塗り塗膜面の一部に、水
酸基含有樹脂、ポリイソシアネート化合物およびりん酸
エステルを主成分とする美粧用塗料を塗装することを特
徴とする塗装方法に係る。That is, according to the present invention, a cosmetic coating composition containing a hydroxyl group-containing resin, a polyisocyanate compound and a phosphoric acid ester as a main component on a part of a cured topcoat film surface having a static glass transition temperature of 60 to 130 ° C. The present invention relates to a coating method characterized by coating.
【０００７】以下に、本発明の方法について具体的に説
明する。The method of the present invention will be specifically described below.
【０００８】本発明において使用する美粧用塗料は、水
酸基含有樹脂、ポリイソシアネート化合物およびりん酸
エステルを主成分としている。The cosmetic coating used in the present invention contains a hydroxyl group-containing resin, a polyisocyanate compound and a phosphoric acid ester as main components.
【０００９】水酸基含有樹脂は１分子中に水酸基を少な
くとも２個有する樹脂であって、例えばポリエステルポ
リオールやアクリルポリオールなどが好適に使用され
る。The hydroxyl group-containing resin is a resin having at least two hydroxyl groups in one molecule, and for example, polyester polyol or acrylic polyol is preferably used.
【００１０】ポリエステルポリオールは１分子中に２個
以上の水酸基を有する多価アルコールと１分子中に２個
以上のカルボキシル基を有する多塩基酸とをエステル反
応させることによって得られる。多塩基酸としては飽和
および不飽和のいずれのものでもよく、モノカルボン酸
も併用できる。該ポリエステルポリオールの数平均分子
量は約１０００〜８０００、水酸基価は２５〜１５０、
特に５０〜８０が好ましい。また酸価は２０以下が適し
ている。The polyester polyol can be obtained by esterifying a polyhydric alcohol having two or more hydroxyl groups in one molecule with a polybasic acid having two or more carboxyl groups in one molecule. The polybasic acid may be saturated or unsaturated, and a monocarboxylic acid may be used together. The polyester polyol has a number average molecular weight of about 1,000 to 8,000, a hydroxyl value of 25 to 150,
50 to 80 is particularly preferable. Further, an acid value of 20 or less is suitable.
【００１１】アクリルポリオールは、１分子中に重合性
二重結合および水酸基を有するアクリル系モノマーの
み、または該アクリル系モノマーと他の重合性モノマー
とを重合せしめてなる重合体である。他の重合性モノマ
ーとしては、１分子中に官能基として重合性二重結合の
みを有するもの、さらにカルボキシル基、グリシジル
基、アミノ基などの水酸基以外の官能基を有する重合性
モノマーがあげられる。該アクリルポリオールの数平均
分子量は約５０００〜３００００、水酸基価は２５〜１
５０、特に５０〜８０が好ましい。また酸価は２０以下
が適している。The acrylic polyol is a polymer obtained by polymerizing only an acrylic monomer having a polymerizable double bond and a hydroxyl group in one molecule, or polymerizing the acrylic monomer and another polymerizable monomer. Examples of the other polymerizable monomer include those having only a polymerizable double bond as a functional group in one molecule, and further polymerizable monomers having a functional group other than a hydroxyl group such as a carboxyl group, a glycidyl group and an amino group. The acrylic polyol has a number average molecular weight of about 5,000 to 30,000 and a hydroxyl value of 25 to 1
50, especially 50-80 is preferable. Further, an acid value of 20 or less is suitable.
【００１２】ポリイソシアネート化合物は、１分子中に
遊離のイソシアネート基を２個以上有する化合物であ
る。具体的には、脂肪族系、脂環族系、芳香族系のポリ
イソシアネートがあげられ、このうち、トリレンジイソ
シアネート、ジフェニルメタンジイソシアネート（ＭＤ
Ｉという）、キシリレンジイソシアネート、ナフチレン
ジイソシアネートなどの芳香族系のものが好ましい。The polyisocyanate compound is a compound having two or more free isocyanate groups in one molecule. Specific examples thereof include aliphatic, alicyclic and aromatic polyisocyanates, of which tolylene diisocyanate and diphenylmethane diisocyanate (MD
I)), xylylene diisocyanate, naphthylene diisocyanate, and other aromatic compounds are preferred.
【００１３】りん酸エステルとしては、例えばモノエチ
ルホスフェート、モノブチルホスフェート、モノプロピ
ルホスフェート、モノオクチルホスフェート、ジエチル
ホスフェート、ジブチルホスフェート、ジプロピルホス
フェート、ジオクチルホスフェート、トリメチルホスフ
ェート、トリエチルホスフェート、トリブチルホスフェ
ート、トリオクチルホスフェート、トリブトキシエチル
ホスフェートなどのりん酸アルキルエステルが好ましく
使用できるが、これら以外のハロゲン含有りん酸エステ
ル、芳香環含有りん酸エステル、高級アルキルりん酸エ
ステルなども適用できる。このうち、モノアルキルホス
フェートが特に好ましい。Examples of the phosphoric acid ester include monoethyl phosphate, monobutyl phosphate, monopropyl phosphate, monooctyl phosphate, diethyl phosphate, dibutyl phosphate, dipropyl phosphate, dioctyl phosphate, trimethyl phosphate, triethyl phosphate, tributyl phosphate, trioctyl. Phosphoric acid alkyl esters such as phosphate and tributoxyethyl phosphate can be preferably used, but halogen-containing phosphoric acid esters, aromatic ring-containing phosphoric acid esters, higher alkyl phosphoric acid esters and the like other than these can also be applied. Of these, monoalkyl phosphates are particularly preferable.
【００１４】該美粧用塗料は上記水酸基含有樹脂、ポリ
イソシアネート化合物およびりん酸エステルを主成分と
しており、これらの成分の構成比率は目的に応じて任意
に選択できる。例えば、水酸基含有樹脂とポリイソシア
ネート化合物とは、水酸基含有樹脂の水酸基１個あた
り、ポリイソシアネート化合物のイソシアネート基が
０．６〜１．３個の範囲が好ましく、またりん酸エステ
ルはこれらの両成分の合計１００重量部あたり０．０５
〜５重量部、特に０．１〜２重量部が適している。The cosmetic coating contains the above-mentioned hydroxyl group-containing resin, polyisocyanate compound and phosphoric ester as main components, and the composition ratio of these components can be arbitrarily selected according to the purpose. For example, the hydroxyl group-containing resin and the polyisocyanate compound are preferably such that the isocyanate group of the polyisocyanate compound is in the range of 0.6 to 1.3 per one hydroxyl group of the hydroxyl group-containing resin, and the phosphoric acid ester is both of these components. 0.05 per 100 parts by weight
-5 parts by weight, especially 0.1-2 parts by weight are suitable.
【００１５】また、本発明で使用する上記美粧用塗料に
おいて、水酸基含有樹脂とポリイソシアネート化合物と
は室温において容易に架橋反応するので、貯蔵中はこの
両成分は分離しておき、使用直前に混合することが好ま
しい。りん酸エステルはこのいずれかもしくは両成分中
にあらかじめ混合しておくのが好ましい。そして、これ
らの成分は、イソシアネート基と反応する官能基を持た
ない有機溶剤に溶解もしくは分散しておくことができ
る。In the cosmetic coating composition used in the present invention, the hydroxyl group-containing resin and the polyisocyanate compound readily undergo a crosslinking reaction at room temperature. Therefore, both components should be separated during storage and mixed immediately before use. Preferably. It is preferable that the phosphoric acid ester is premixed in either or both components. Then, these components can be dissolved or dispersed in an organic solvent having no functional group that reacts with an isocyanate group.
【００１６】該美粧用塗料には、さらに必要に応じて、
着色顔料、メタリック顔料、体質顔料、つや消し顔料な
どを配合することも可能である。If necessary, the cosmetic coating may further include
It is also possible to mix a color pigment, a metallic pigment, an extender pigment, a matte pigment and the like.
【００１７】本発明は、該美粧用塗料を、線、文字また
は模様などの形状に、静的ガラス転移温度が６０〜１３
０℃である硬化上塗塗膜面に塗装するところに特徴があ
る。この上塗塗膜は、特に、耐酸性や耐スリキズ性など
が改良されたもので、表面が不活性になっており、その
静的ガラス転移温度が６０〜１３０℃、特に６８〜１０
０℃の硬化上塗塗膜面に該美粧用塗料を適用することが
好ましい。According to the present invention, the cosmetic paint is applied to a shape such as a line, a character or a pattern and has a static glass transition temperature of 60 to 13.
It is characterized in that it is applied on the surface of the cured top coat which is 0 ° C. This top coating film has improved acid resistance, scratch resistance, etc., has an inactive surface, and has a static glass transition temperature of 60 to 130 ° C., particularly 68 to 10 ° C.
It is preferable to apply the cosmetic coating to the surface of the top coating film cured at 0 ° C.
【００１８】該上塗塗膜は不活性であるため、従来の美
粧用塗料では付着性が十分でなかったが、本発明におけ
る美粧用塗料ではかかる欠陥がすべて解消され、すぐれ
た付着性を示す。Since the above-mentioned top coating film is inactive, the conventional cosmetic coating has insufficient adhesion, but the cosmetic coating of the present invention eliminates all such defects and exhibits excellent adhesion.
【００１９】このような静的ガラス転移温度を有する上
塗塗膜を形成する塗料としては、例えば、水酸基および
カルボキシル基（さらにグリシジル基も含むことがあ
る）を含有する樹脂、水酸基およびグリシジル基（さら
にカルボキシル基も含むことがある）を含有する樹脂お
よびメラミン樹脂を主成分とする上塗り塗料；水酸基お
よびシラノール基（アルコキシシラン基であってもよ
い）を含有する樹脂およびメラミン樹脂を主成分とする
上塗り塗料；水酸基を含有する樹脂、メラミン樹脂およ
びポリシロキサン樹脂を主成分とする上塗り塗料；など
があげられ、これらの塗膜は複数の異なる架橋反応によ
って硬化している。As the paint for forming the top coat film having such a static glass transition temperature, for example, a resin containing a hydroxyl group and a carboxyl group (which may further include a glycidyl group), a hydroxyl group and a glycidyl group (further A top coat containing a resin containing a carboxyl group) and a melamine resin as main components; a top coat containing a resin containing a hydroxyl group and a silanol group (which may be an alkoxysilane group) and a melamine resin as a main component Paints; top-coat paints containing hydroxyl group-containing resins, melamine resins and polysiloxane resins as main components; and the like, and these coating films are cured by a plurality of different crosslinking reactions.
【００２０】本発明において、該美粧用塗料の被塗面で
ある上塗塗膜の静的ガラス転移温度は、硬化せしめた上
塗塗膜面に荷重２ｇのプローブを押しあてながら該塗膜
の温度を５℃／分の速度で昇温し、塗膜が軟化しプロー
ブが該塗膜中に進入した温度（℃）を測定し、それを上
塗塗膜の静的ガラス転移温度とした。この測定には、理
学電気（株）製の熱機械分析装置（Thermal Mechanical
Analysis ）を使用した。In the present invention, the static glass transition temperature of the top coating film, which is the surface to be coated of the cosmetic coating, is determined by pressing the probe with a load of 2 g against the surface of the cured top coating film to determine the temperature of the coating film. The temperature was raised at a rate of 5 ° C./minute to measure the temperature (° C.) at which the coating softened and the probe penetrated into the coating, which was taken as the static glass transition temperature of the top coating. This measurement is performed by Rigaku Denki Co., Ltd.
Analysis) was used.
【００２１】本発明において、硬化塗膜面への美粧用塗
料の塗装は既知の方法によって行われ、例えば、該塗料
が塗装されて好ましくない部分をマスキングテーブなど
で覆ってから、目的部分のみに美粧用塗料を、スプレイ
塗装、静電塗装などの方法で塗装し、その後、マスキン
グテープを剥離、除去することによって、硬化塗膜面に
美粧用塗料を任意の形状に塗装できる。美粧用塗料塗膜
は室温で放置しておくことによって硬化するが、加熱硬
化することも可能であり、その膜厚は例えば約５〜１０
０μｍが適している。In the present invention, the coating of the cosmetic coating on the surface of the cured coating film is carried out by a known method. For example, after coating the coating with an undesired portion with a masking tape or the like, only the desired portion is coated. The cosmetic coating can be applied to the cured coating surface in any shape by applying the cosmetic coating by a method such as spray coating or electrostatic coating, and then removing and removing the masking tape. The coating film for cosmetics is cured by leaving it at room temperature, but it can be cured by heating, and the film thickness is, for example, about 5-10.
0 μm is suitable.
【００２２】本発明によって形成された美粧用塗料塗膜
は、被塗面（硬化塗膜）との付着性や耐チッピング性な
どが著しく改善された。さらに、耐候性、耐磨耗性、耐
食性も良好であることも判明した。The coating film for cosmetics formed according to the present invention has markedly improved adhesion to the surface to be coated (cured coating) and chipping resistance. It was also found that the weather resistance, abrasion resistance, and corrosion resistance were good.
【００２３】[0023]
【実施例】次に、本発明の実施例および比較例について
説明する。EXAMPLES Next, examples of the present invention and comparative examples will be described.
【００２４】Ｉ．試料 １．被塗物 カチオン電着塗料および中塗り塗料を塗装した鋼板に、
水酸基およびシラノール基を含有するアクリル樹脂およ
びメラミン樹脂を主成分とする白色上塗り塗料を塗装し
（膜厚２０μｍ）、１６０℃で２０分加熱して硬化せし
めた上塗り塗膜を形成したものを用いた。硬化塗膜の静
的ガラス転移温度は７０℃であった。I. Sample 1. To be coated Steel plate coated with cationic electrodeposition paint and intermediate paint,
A white topcoating material containing a hydroxyl group-containing silanol group-containing acrylic resin and a melamine resin as a main component was applied (film thickness: 20 μm) and heated at 160 ° C. for 20 minutes to form a cured topcoating film. . The static glass transition temperature of the cured coating film was 70 ° C.
【００２５】２．美粧用塗料 （ｉ）水酸基含有アクリル樹脂（数平均分子量１０００
０、水酸基価７５、酸価１４）とＭＤＩとを水酸基：イ
ソシアネート基＝１：１（モル比）で混合し、さらにり
ん酸エステル（モノブチルホスフェート、「ＭＰ−
４」、大八化学社製、商品名）を、水酸基含有アクリル
樹脂とＭＤＩとの合計１００重量部あたり、０．２重量
部添加した塗料である。有機溶剤としてトルエン：キシ
レン＝１：１（重量比）の混合溶剤を使用し、固形分含
有率６０重量％に調整した。さらにカーボンブラック顔
料を水酸基含有アクリル樹脂とＭＤＩとの合計１００重
量部あたり、５重量部混合せしめた。2. Cosmetic coating (i) Hydroxyl group-containing acrylic resin (number average molecular weight 1000
0, a hydroxyl value of 75, an acid value of 14) and MDI were mixed at a hydroxyl group: isocyanate group = 1: 1 (molar ratio), and phosphoric acid ester (monobutyl phosphate, “MP-
4 ", manufactured by Daihachi Chemical Co., Ltd.) is added in an amount of 0.2 part by weight per 100 parts by weight of the total amount of the hydroxyl group-containing acrylic resin and MDI. A mixed solvent of toluene: xylene = 1: 1 (weight ratio) was used as the organic solvent, and the solid content was adjusted to 60% by weight. Further, 5 parts by weight of carbon black pigment was mixed with 100 parts by weight of the hydroxyl group-containing acrylic resin and MDI in total.
【００２６】（ii）水酸基含有ポリエステル樹脂（数平
均分子量２０００、水酸基価４０、酸価１４）とＭＤＩ
とを水酸基：イソシアネート基＝１：１（モル比）で混
合し、さらにりん酸エステル（「ＭＰ−４」）を、水酸
基含有ポリエステル樹脂とＭＤＩとの合計１００重量部
あたり、０．４重量部添加した塗料である。有機溶剤と
してトルエン：キシレン＝１：１（重量比）の混合溶剤
を使用し、固形分含有率６０重量％に調整した。さらに
カーボンブラック顔料を水酸基含有アクリル樹脂とＭＤ
Ｉとの合計１００重量部あたり、５重量部混合せしめ
た。(Ii) Hydroxyl group-containing polyester resin (number average molecular weight 2000, hydroxyl value 40, acid value 14) and MDI
And hydroxyl group: isocyanate group = 1: 1 (molar ratio), and further phosphoric acid ester (“MP-4”) is 0.4 parts by weight per 100 parts by weight of the total hydroxyl group-containing polyester resin and MDI. It is the added paint. A mixed solvent of toluene: xylene = 1: 1 (weight ratio) was used as the organic solvent, and the solid content was adjusted to 60% by weight. In addition, carbon black pigment and hydroxyl group-containing acrylic resin and MD
5 parts by weight were mixed per 100 parts by weight in total with I.
【００２７】（iii ）上記（ｉ）の組成からりん酸エス
テルを削除したものである。(Iii) The phosphoric acid ester is deleted from the composition of (i) above.
【００２８】（iV）上記（ii）の組成からりん酸エステ
ルを削除したものである。(IV) A composition obtained by removing the phosphate ester from the composition of (ii) above.
【００２９】II．実施例１〜２および比較例１〜２ 上記の被塗物に美粧用塗料（ｉ）〜（iV）を塗装し、７
０℃で３０分間加熱し硬化せしめた。得られた塗膜の性
能試験結果も併せて表１に示した。II. Examples 1 and 2 and Comparative Examples 1 and 2 The coating materials (i) to (iV) for cosmetics were applied to the above-mentioned objects, and 7
It was heated at 0 ° C. for 30 minutes to be cured. The results of the performance test of the obtained coating film are also shown in Table 1.
【００３０】[0030]
【表１】 [Table 1]
【００３１】試験方法は、次の通りである。The test method is as follows.
【００３２】付着性：素地に達するように塗膜面に刃物
で大きさ２×２ｍｍのゴバン目１００個をカットし、そ
の塗面に粘着セロハンテープを貼着し、それを急激に剥
離したのち、塗膜のゴバン目の残存数を調べた。Adhesiveness: Cut 100 pieces of 2 × 2 mm goggles on the surface of the coating film with a knife to reach the base material, affix adhesive cellophane tape to the coating surface, and then rapidly peel it off. Then, the number of remaining streaks in the coating film was examined.
【００３３】○：１００個残存、×：８０個以下残存。◯: 100 pieces remained, x: 80 pieces or less remained.
【００３４】耐チッピング性：試験片を試験片保持台に
とりつけ、塗面に対し９０°の角度で、下記条件で、砕
石を試験片に発射せしめた。Chipping resistance: The test piece was mounted on a test piece holder, and crushed stones were shot at the angle of 90 ° to the coated surface under the following conditions.
【００３５】（１）試験機器：Ｑ−Ｇ−Ｒグラベロメー
ター（Ｑパネル会社製品）、 （２）吹付けられる石：７号砕石、 （３）吹付けられる石の量：約１００ｇ、 （４）吹付けエアー圧力：約４．５Ｋｇ／ｃｍ2 、 （５）試験時の温度：約２０℃。(1) Test equipment: Q-G-R gravelometer (product of Q panel company), (2) Stone to be sprayed: No. 7 crushed stone, (3) Amount of stone to be sprayed: about 100 g, ( 4) Spraying air pressure: about 4.5 Kg / cm 2 , (5) Test temperature: about 20 ° C.
【００３６】塗面状態を目視観察し下記の基準で評価し
た。The state of the coated surface was visually observed and evaluated according to the following criteria.
【００３７】○：美粧性塗膜の一部に衝撃によるキズが
僅か認められる程度。◯: Slight scratches are recognized on a part of the cosmetic coating film.
【００３８】△：美粧性塗膜に衝撃によるキズが少し認
められる。Δ: Some scratches due to impact are observed on the cosmetic coating film.
【００３９】×：美粧性塗膜に衝撃によるキズが多く認
められる。X: Many scratches due to impact are observed on the cosmetic coating film.
【００４０】耐候性：ＪＩＳ Ｋ ５４００−９．８．
１に従い、サンシャインカーボンアーク方式で、４００
時間試験した結果である。Weather resistance: JIS K 5400-9.8.
According to 1, in the sunshine carbon arc system, 400
This is the result of a time test.
【００４１】○：異常（変色、フクレなど）なし。◯: No abnormality (discoloration, blistering, etc.)
【００４２】耐摩耗性：ＪＩＳ Ｋ ５４００−８．９
に準じて試験を行ない、摩耗輪が１０００回転後の塗膜
減量を調べた。Abrasion resistance: JIS K 5400-8.9
The test was carried out in accordance with the above, and the weight loss of the coating film after 1000 rotations of the wear wheel was examined.
【００４３】○：０．２ｍｇ以下。◯: 0.2 mg or less.
【００４４】耐食性：ＪＩＳ Ｋ ５４００−９．１に
準じて耐塩水噴霧性試験を行なった。試験板として素地
に達するように塗膜を刃物でクロスカットし、１０日間
試験後の塗膜をみた。Corrosion resistance: A salt spray resistance test was conducted according to JIS K 5400-9.1. The coating film was cross-cut with a knife so as to reach the substrate as a test plate, and the coating film after the test for 10 days was observed.
【００４５】○：カット部からのサビ発生ごくわずか、 △：カット部からのサビ発生やや多い、 ×：カット部からのサビ発生著しい。◯: Slight rust generation from the cut portion, Δ: Slight rust generation from the cut portion, ×: Rust generation significantly from the cut portion.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 中村 茂 愛知県西加茂郡三好町大字莇生字平地１番 地 関西ペイント株式会社内 (72)発明者 稲本 歩 愛知県西加茂郡三好町大字莇生字平地１番 地 関西ペイント株式会社内 (72)発明者 木谷田 弘明 愛知県西加茂郡三好町大字莇生字平地１番 地 関西ペイント株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Shigeru Nakamura No. 1 in Hirajyo, Miyoshi-cho, Nishikamo-gun, Aichi Prefecture Kansai Paint Co., Ltd. Address in Kansai Paint Co., Ltd. (72) Inventor Hiroaki Kiyata No. 1 flat land in Zuijoji, Miyoshi-cho, Nishikamo-gun, Aichi Prefecture Kansai Paint Co., Ltd.
Claims (1)
ある硬化上塗り塗膜面の一部に、水酸基含有樹脂、ポリ
イソシアネート化合物およびりん酸エステルを主成分と
する塗料を塗装することを特徴とする塗装方法。1. A coating comprising a hydroxyl group-containing resin, a polyisocyanate compound and a phosphoric acid ester as a main component is applied to a part of the surface of a cured topcoat film having a static glass transition temperature of 60 to 130 ° C. How to paint.