JPH06278768A - Ptp packing body - Google Patents

Abstract

PURPOSE:To prevent a baby from carelessly breaking a seal, to make it possible to break the seal easily when required, and to achieve excellent disposability by forming an inorganic oxide layer, as a seal breaking film, on a base film and providing a cut in the base film. CONSTITUTION:A formed sheet 1 and a seal breaking film 2 are provided, and the sheet 1 has a recess 3 for storing a solid item A such as chemicals. The film 2 is bonded to the sheet 1, excluding the recess 3, to seal the open end of the recess 3. As the formed sheet 1, a thermoplastic resin sheet is subjected to vacuum forming or press forming to form a recess 3 therein. For preparing the film 2, a metal oxide layer 22 is formed on the inner surface of a base film 21 by vapor deposition method and a cut (p) is formed through at least a portion of the base sheet 21 corresponding to the recess 3. Consequently, barrier characteristic equivalent to conventional aluminum foil is provided and protective property for contents is good and the solid item A can be taken out manually and simply, by pushing it with fingers.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、ＰＴＰ（Ｐｒｅｓｓ
ｔｈｒｏｕｇｈ Ｐａｃｋ）包装体に関し、幼児等が不
注意に破封することなく、使用時には容易に開封取り出
しでき、しかも廃棄性も優れたＰＴＰ包装体に関する。The present invention relates to a PTP (Press).
The present invention relates to a through pack (PTP) package which can be easily opened and taken out when used without causing an infant to inadvertently break the package, and which is also excellent in discardability.

【０００２】[0002]

【従来の技術】近年ＰＴＰ包装体は錠剤やカプセルタイ
プ等の薬品に常用されているもので、薄手のプラスチッ
クシートを成形して薬品収納用の凹部を形成し、この凹
部に薬品等を収納した後、破断容易な破封膜でこの凹部
を封止してなるものである。前記破封膜としてはアルミ
ニュウム箔等の裏面にヒートシール用の樹脂を塗工した
みのが一般的であり、前記凹部側から指で押すことによ
り、この破封膜が破断して薬品等を取り出すことができ
る。2. Description of the Related Art In recent years, PTP packages have been commonly used for tablets, capsules and other chemicals. A thin plastic sheet is formed to form a recess for storing the chemical, and the recess is filled with the chemical. After that, the concave portion is sealed with an easily rupturable sealing film. As the sealing film, it is common to coat a resin for heat sealing on the back surface of an aluminum foil or the like, and by pressing with a finger from the recess side, the sealing film is broken to prevent chemicals or the like. You can take it out.

【０００３】凹部側から指でおすことにより、破封膜が
破断する必要があることから、破封膜にプラスチックフ
ィルムが用いられことは通常はない、しかしながら、幼
児等による事故を防ぐため、その他の理由からプラスチ
ックフィルムを用いたものが提案されている。大別する
と、次の３種類である。 （１）アルミニュウム箔の外側にプラスチックフィルム
を剥離容易に積層したもので、プラスチックフィルムを
剥離除去した後破封して使用する（例えば実開昭５０−
３２３７１号、実開昭５１−１３９１７６号、実開昭５
１−１３９１７７号、実開昭５７−２４２６１号、実開
昭５６−１２３２７３号、特実開昭６１−２８７５６８
号各公報）。 （２）アルミニュウム箔に一軸延伸フィルムを積層した
もの（実開昭５１−４５０８３号、実開昭５１−４７７
８０号、実開昭５４−９２８８１号、実開昭５７−２９
５６５号各公報）。 （３）２０μ以下の薄いプラスチックフィルムを積層し
たもの（特開昭５４−７３８８４号、特開昭５９−４２
９５２号、実開昭５４−９２８８０号各公報）。Since it is necessary to break the rupture film by pushing it with a finger from the recess side, a plastic film is not usually used for the rupture film. However, in order to prevent accidents caused by infants, etc. For this reason, one using a plastic film has been proposed. Broadly speaking, there are the following three types. (1) A plastic film is laminated on the outer side of an aluminum foil so that it can be easily peeled off.
No. 32371, No. 51-139176, No. 5
No. 1-139177, No. 57-24261, No. 56-123273, No. 61-287568
No. (2) Laminated aluminum foil with a uniaxially stretched film (No. 51-45083, No. 51-477)
No. 80, No. 54-92881, No. 57-29, No. 57-29
565). (3) A laminate of thin plastic films having a thickness of 20 μm or less (JP-A-54-73884, JP-A-59-42)
952 and Japanese Utility Model Publication No. 54-92880).

【０００４】[0004]

【発明が解決しようとする課題】上記（１）の包装体は
開封前にプラスチックフィルムを剥離する必要があるか
ら、ＰＴＰ包装の簡便性を殺しているという欠点があ
り、上記（２）の包装体は、一軸延伸フィルムは延伸方
向に裂け易い反面、延伸と直角方向には破れ難いから、
錠剤やカプセル等の固形成形物を収納した包装体では、
充分に開封できないことがあり、上記（３）の包装体
は、単に薄く破れ易いプラスチックフィルムを貼合せた
に過ぎないから容易に開封できると共に、幼児等が誤っ
て開封するという事故を防ぐことができないという問題
点がある。The packaging body of the above (1) has a drawback that the convenience of PTP packaging is obviated because the plastic film must be peeled off before opening, and the packaging of the above (2). The body, while the uniaxially stretched film is easy to tear in the stretching direction, it is difficult to tear in the direction perpendicular to the stretching,
In the package containing the solid molded products such as tablets and capsules,
It may not be able to be opened sufficiently, and the package of (3) above can be easily opened because it is merely a thin and fragile plastic film stuck together, and it is possible to prevent accidents such as infants accidentally opening it. There is a problem that you cannot do it.

【０００５】さらに上記問題点を解決したものとして、
実開平１−１６１４６９号公報に記載されるように、前
記破封膜がアルミニュウム箔とプラスチックフィルムを
含む積層材料からなり、前記凹部に対応する部分のプラ
スチックフィルムの一部に切り込みが形成されているＰ
ＴＰ包装体が提案されているが、これらもアルミニュウ
ム箔等の金属箔を使用しているので、アルミニュウム箔
が焼却等において公害問題になってきている。As a solution to the above problems,
As described in Japanese Utility Model Laid-Open No. 1-164169, the sealing film is made of a laminated material including an aluminum foil and a plastic film, and a cut is formed in a part of the plastic film corresponding to the recess. P
TP packages have been proposed, but since these also use metal foils such as aluminum foil, aluminum foil has become a pollution problem in incineration and the like.

【０００６】[0006]

【課題を解決する手段】本発明は、上記問題点を解消し
たもので、成形シートの裏面に形成した凹部に固形物品
を収納し、破封膜でこの凹部を封止したＰＴＰ包装体に
おいて、前記破封膜が基材フィルムに無機酸化物層を形
成したものであり、かつ前記基材フィルムの上記凹部に
対応する部分の少なくとも一部に切り込みが形成されて
いることを特徴とするＰＴＰ包装体である。The present invention solves the above problems and provides a PTP package in which a solid article is housed in a recess formed on the back surface of a molded sheet and the recess is sealed with a rupturable film. A PTP package, wherein the rupturable film is formed by forming an inorganic oxide layer on a base film, and a cut is formed in at least a part of the base film corresponding to the recess. It is the body.

【０００７】[0007]

【作用】本発明のＰＴＰ包装体は上記の如き構成であ
り、破封膜として基材フィルムに無機酸化物層を形成し
たものを使用し、従来のアルミニュウム箔と同等のバリ
ヤー性を有し、かつ前記基材フィルムに切り込みを設け
てあるので、大人の適度の力で指で押して固形物品を簡
単に取り出せる。The PTP package of the present invention has the above-mentioned structure and uses a base film having an inorganic oxide layer formed as a sealing film and has a barrier property equivalent to that of a conventional aluminum foil. In addition, since the base film is provided with a notch, a solid article can be easily taken out by pushing with a finger with an appropriate force of an adult.

【０００８】[0008]

【実施例】図１は本発明によるＰＴＰ包装体の断面説明
図であり、本発明のＰＴＰ包装体は成形シート１と、破
封膜２とからなり、この成形シート１は薬品等の固形物
品Ａを収納する凹部３を有し、この凹部３の開口部４を
封鎖するように前記破封膜２が前記成形シート１の凹部
以外の接着部分１１で接着している。EXAMPLE FIG. 1 is a cross-sectional explanatory view of a PTP package according to the present invention. The PTP package of the present invention comprises a molded sheet 1 and a rupturable film 2, and this molded sheet 1 is a solid article such as a chemical. There is a concave portion 3 for accommodating A, and the rupturable film 2 is adhered by an adhesive portion 11 other than the concave portion of the molded sheet 1 so as to close the opening 4 of the concave portion 3.

【０００９】ここで、前記成形シート１としては、熱可
塑性樹脂シートを真空成形、プレス成形等の方法で前記
凹部３を成形してなるもので、熱可塑性樹脂シートとし
ては、ポリ塩化ビニル、ポリプロピレン等が使用でき
る。またこの凹部３に収納される固形物品Ａは錠剤タイ
プやカプセルタイプの薬剤やキャンデーが用いられる。Here, the molded sheet 1 is formed by molding the recess 3 by a method such as vacuum molding or press molding of a thermoplastic resin sheet. The thermoplastic resin sheet may be polyvinyl chloride or polypropylene. Etc. can be used. As the solid article A stored in the recess 3, a tablet type or capsule type drug or candy is used.

【００１０】前記破封膜２として本発明においては、基
材フィルム２１の内面に金属酸化物層２２を蒸着法によ
り形成したものを使用し、本実施例では、基材フィルム
２１としては厚さ１０乃至３０μのポリエチレンテレフ
タレートを使用し、金属酸化物層２２としては酸化ケイ
素蒸着膜層を使用し、通常ＳｉｘＯｙ（ｘ＝１，２、ｙ
＝０〜３）の化学式で示され、真空蒸着、スパッタリン
グ、イオンプレーティング等の公知の方法により形成可
能であり、金属酸化物層２２の厚さは、少なくとも２０
０Å、好ましくは４００Å以上である。In the present invention, the rupturable film 2 is formed by forming a metal oxide layer 22 on the inner surface of a base film 21 by a vapor deposition method. In this embodiment, the base film 21 has a thickness of Polyethylene terephthalate having a thickness of 10 to 30 μm is used, a silicon oxide vapor deposition film layer is used as the metal oxide layer 22, and normally SixOy (x = 1, 2, y) is used.
= 0 to 3), and can be formed by a known method such as vacuum deposition, sputtering, or ion plating, and the metal oxide layer 22 has a thickness of at least 20.
It is 0Å, preferably 400Å or more.

【００１１】また前記基材シート２１としてはポリエチ
レンテレフタレート以外にもナイロン、ポリオレフィン
系に代表されるプラスチックフィルムが使用でき、本発
明においては、図２に示す如く、この基材シート２１の
前記凹部に対応する部分の少なくとも一部に切り込みｐ
が形成されている。さらに、破封しやすい紙素材、例え
ばパーチメント紙を積層した構成としてもよい。In addition to polyethylene terephthalate, a plastic film typified by nylon or polyolefin can be used as the base sheet 21. In the present invention, as shown in FIG. Notch p in at least part of the corresponding part
Are formed. Further, a paper material that is easy to break, for example, parchment paper may be laminated.

【００１２】ここで、前記成形シート１と破封膜２の接
着は、破封膜２の内面にヒートシール性樹脂２３を塗工
しておき、前記凹部３に固形物品Ａを充填しながら、前
記成形シート１の開口部側に破封膜２を重ねてヒートシ
ール法にて接着することができる。このヒートシール性
樹脂２３としては、前記成形シート１と熱接着するため
のもので、塩酢ビ系ヒートシールニス、ポリアクリレー
ト系樹脂が使用できる。Here, in order to adhere the molded sheet 1 and the rupturable film 2 to each other, a heat-sealable resin 23 is applied to the inner surface of the rupturable film 2 while the recess 3 is filled with the solid article A, The breakable film 2 can be overlapped on the opening side of the molded sheet 1 and adhered by a heat sealing method. The heat-sealable resin 23 is for heat-bonding to the molding sheet 1, and a vinyl chloride vinyl acetate heat-seal varnish or a polyacrylate resin can be used.

【００１３】前記切り込みｐの形成方法としては、前記
破封膜２としての前記金属酸化物層が形成された基材シ
ート２１側からレーザービームを用いて上記形状に入れ
るようにする。この切り込みｐは図１に示すように、基
材シート２１の全厚、即ち貫通させ、図２（ａ）に示す
ように断続線（例えばミシン目状）にしても、また図に
は示していないが前記基材シート２１の半分の厚みまで
切り込みｐを入れ、図２（ｂ）に示すように前記凹部に
対応する所に十字形状にしても良く、前記凹部側から押
すことにより前記破封膜２が簡単に切断される程度の深
さであればよい。As a method of forming the notch p, a laser beam is used from the side of the base material sheet 21 on which the metal oxide layer as the rupturable film 2 is formed to make the above-mentioned shape. As shown in FIG. 1, this notch p is made to penetrate the entire thickness of the base material sheet 21, that is, penetrate, and as shown in FIG. Although not shown, a notch p may be formed to half the thickness of the base material sheet 21 and a cross shape may be formed at a portion corresponding to the concave portion as shown in FIG. 2B. The depth may be such that the membrane 2 can be easily cut.

【００１４】[0014]

【発明の効果】本発明は上記の如き構成であり、破封膜
として基材フィルムに無機酸化物を蒸着したものを使用
し従来のアルミニュウム箔と同等のバリヤー性を有し内
容物保護性に優れ、かつ前記基材フィルムに切り込みを
設けてあるので、指で押して固形物品を大人の力で、簡
単に取り出せるばかりでなく、破封膜全体が透明にする
ことも可能であり、破封膜２側から内容物を確認でき、
しかも従来のようにアルミニュウム箔等の金属をを使用
していないので、焼却が容易で廃棄性にも優れている。EFFECTS OF THE INVENTION The present invention has the above-mentioned constitution and uses a base film obtained by vapor-depositing an inorganic oxide as a rupturing film and has a barrier property equivalent to that of a conventional aluminum foil to protect contents. It is excellent, and since the notch is provided in the base film, it is possible not only to easily remove the solid article with the force of an adult by pushing with a finger, but also to make the entire rupturable membrane transparent. You can check the contents from the 2 side,
Moreover, unlike the conventional case, since no metal such as aluminum foil is used, it is easy to incinerate and is excellent in disposability.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明のＰＴＰ包装体の実施例の一部断面説明
図である。FIG. 1 is a partial cross-sectional explanatory view of an example of a PTP package of the present invention.

【図２】本発明のＰＴＰ包装体の実施例の一平面説明図
であり、（ａ）は切り込みがミシン目状の実施例を示す
ものであり、（ｂ）は切り込みが十字の実施例を示すも
のである。FIG. 2 is a plan view of one embodiment of the PTP package of the present invention, in which (a) shows an example in which the cut is a perforation, and (b) shows an example in which the cut is a cross. It is shown.

【符号の説明】[Explanation of symbols]

１ 成形シート ２ 破封膜 １１ 凹部 ２１ 基材シート ２２ 金属酸化物層 ２３ ヒートシール樹脂 Ａ 固形物品 ｐ 切り込み 1 Molded Sheet 2 Sealing Film 11 Recess 21 Base Material Sheet 22 Metal Oxide Layer 23 Heat Seal Resin A Solid Article p Notch

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】成形シートの裏面に形成した凹部に固形物
品を収納し、破封膜でこの凹部を封止したＰＴＰ包装体
において、前記破封膜が基材フィルムに無機酸化物層を
形成したものであり、かつ前記基材フィルムの上記凹部
に対応する部分の少なくとも一部に切り込みが形成され
ていることを特徴とするＰＴＰ包装体。1. A PTP package in which a solid article is housed in a recess formed on the back surface of a molded sheet and the recess is sealed with a sealing film, the sealing film forming an inorganic oxide layer on a base film. A PTP package, characterized in that a cut is formed in at least a part of a portion of the base film corresponding to the recess.