JPH06256056A - Bleeding-reducing agent for cement-based grout - Google Patents
Bleeding-reducing agent for cement-based groutInfo
- Publication number
- JPH06256056A JPH06256056A JP6625693A JP6625693A JPH06256056A JP H06256056 A JPH06256056 A JP H06256056A JP 6625693 A JP6625693 A JP 6625693A JP 6625693 A JP6625693 A JP 6625693A JP H06256056 A JPH06256056 A JP H06256056A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- bleeding
- reducing agent
- water
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はセメント系グラウト用ブ
リージング低減剤およびその使用方法に関する。TECHNICAL FIELD The present invention relates to a bleeding reducing agent for cement-based grout and a method for using the same.
【０００２】[0002]
【従来の技術】従来、セメントと水とを含有するセメン
トスラリーを硬化材として高圧噴射工法により地盤中に
噴射し、土と攪拌混合して硬化させ地盤を安定化させる
方法において、セメントスラリーのいわゆるブリージン
グ現象を低減するために、ベントナイト等の粘土質鉱物
を配合し、さらに、ポリアルキルアリルスルホン酸高縮
合物等のセメント用減水剤やメチルセルロース等の水溶
性ポリマーを添加して、セメントスラリーの流動性を確
保する手法が知られている（特開昭６１−２６８８１２
号公報）。しかし、粘土質鉱物を配合したセメントスラ
リーに既存のセメント用減水剤等を添加した直後はセメ
ントスラリーの流動性が得られるものの、その流動性は
経時的に悪化し、長時間の使用に耐えることができな
い。2. Description of the Related Art Conventionally, a cement slurry containing cement and water is used as a hardening agent to be injected into the ground by a high-pressure injection method to stir and mix with soil to harden the ground to stabilize the ground. In order to reduce the breathing phenomenon, clay minerals such as bentonite are blended, and water-reducing agents for cement such as polyalkylallyl sulfonic acid high condensation products and water-soluble polymers such as methyl cellulose are added to make the cement slurry flow. There is known a method for ensuring the property (Japanese Patent Laid-Open No. 61-268812).
Issue). However, although the fluidity of the cement slurry can be obtained immediately after adding the existing cement water reducing agent to the cement slurry mixed with clayey minerals, the fluidity deteriorates with time and it can withstand long-term use. I can't.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、地盤
を安定化させるために高圧噴射工法により地盤中に噴射
されるセメントスラリーの経時的な流動性低下を防止
し、かつ、ブリージング現象の抑制に効果的な手段を提
供することである。そこで本発明者等は鋭意研究の結
果、不飽和ジカルボン酸塩の使用が有効であることを見
出し、この知見に基づいて本発明を完成するに至った。An object of the present invention is to prevent deterioration of fluidity of cement slurry injected into the ground by the high pressure injection method for stabilizing the ground over time, and to prevent breathing phenomenon. It is to provide an effective means for suppression. Therefore, the present inventors have conducted extensive studies and found that the use of unsaturated dicarboxylic acid salts is effective, and have completed the present invention based on this finding.
【０００４】[0004]
【課題を解決するための手段】かくして本発明によれ
ば、下記（１）ないし（６）が提供される。 （１）ベントナイトと水溶性ポリカルボン酸とを配合し
てなるセメント系グラウト用ブリージング低減剤。 （２）ベントナイト１００重量部に対して水溶性ポリカ
ルボン酸２〜４０重量部を配合してなるセメント系グラ
ウト用ブリージング低減剤。 （３）水溶性ポリカルボン酸が炭素数４〜６を有するオ
レフインと無水マレイン酸との共重合体であって数平均
分子量５００〜５００００のものの塩である前記（１）
または（２）のセメント系グラウト用ブリージング低減
剤。 （４）水溶性ポリカルボン酸がイソアミレン−無水マレ
イン酸共重合体であって数平均分子量３０００〜１００
００のもののナトリウム塩である前記（１）または
（２）のセメント系グラウト用ブリージング低減剤。 （５）前記（１）ないし（４）のセメント系グラウト用
ブリージング低減剤をセメント１００重量部に対して
０．５〜５０重量部添加することを特徴とするセメント
系グラウトのブリージング低減方法。 （６）前記（１）ないし（４）のセメント系グラウト用
ブリージング低減剤をセメント１００重量部に対して２
〜１５重量部添加することを特徴とするセメント系グラ
ウトのブリージング低減方法。Thus, according to the present invention, the following (1) to (6) are provided. (1) A breathing reducing agent for cement-based grout, which comprises a mixture of bentonite and a water-soluble polycarboxylic acid. (2) A breathing reducing agent for cement-based grout, which comprises 100 parts by weight of bentonite and 2 to 40 parts by weight of a water-soluble polycarboxylic acid. (3) The water-soluble polycarboxylic acid is a salt of a copolymer of olefin having 4 to 6 carbon atoms and maleic anhydride and having a number average molecular weight of 500 to 50,000 (1)
Alternatively, the breathing reducing agent for cement-based grout of (2). (4) The water-soluble polycarboxylic acid is an isoamylene-maleic anhydride copolymer and has a number average molecular weight of 3,000 to 100.
The cement-based bleeding reducing agent for grout of (1) or (2), which is a sodium salt of No. 00. (5) A method for reducing bleeding of cement-based grout, which comprises adding 0.5 to 50 parts by weight of the bleeding-reducing agent for cement-based grout of (1) to (4) above to 100 parts by weight of cement. (6) The breathing reducing agent for cement-based grout of the above (1) to (4) is added to 2 parts per 100 parts by weight of cement.
A method for reducing bleeding of cement-based grout, which comprises adding ˜15 parts by weight.
【０００５】本発明で使用するベントナイトは、古くか
ら天然に産する膨潤性層状粘土鉱物として知られ、モン
モリロナイトを主要鉱石として、含水ケイ酸アルミニウ
ムを基体とする超微細な粘土である。なお、合成ベント
ナイトとして市販されているものも使用することができ
る。ベントナイトの粒度および比重は特に限定されない
が、通常粒度は２５０メッシュパス分７０％以上、見か
け比重は０．７〜０．９のものが用いられる。The bentonite used in the present invention has been known as a swelling layered clay mineral that has been naturally produced for a long time, and is an ultrafine clay containing montmorillonite as a main ore and hydrous aluminum silicate as a base material. In addition, what is marketed as a synthetic bentonite can also be used. The particle size and specific gravity of bentonite are not particularly limited, but normally, those having a particle size of 70% or more for 250 mesh pass and an apparent specific gravity of 0.7 to 0.9 are used.
【０００６】本発明で用いられる水溶性ポリカルボン酸
は、α，β−不飽和カルボン酸系モノマーの重合体また
はこれと共重合可能なエチレン系不飽和モノマーとの共
重合体、ならびに、該重合体または共重合体の分子中に
存在するカルボキシル基または酸無水物基の少なくとも
一部、好ましくは５０モル％以上が塩を形成しているも
のであり、該重合体または共重合体は、通常、数平均分
子量５００〜５００００、好ましくは１０００〜２５０
００、さらに好ましくは３０００〜１００００を有する
ものである。分子量が過度に大きくなると分散性が低下
し、逆にセメントスラリーを増粘、凝集させる効果が生
ずるため好ましくない。かかる塩の具体例として、例え
ばナトリウム、カリウム、マグネシウム、カルシウム、
バリウムなどのごときアルカリ金属またはアルカリ土類
金属の塩、アンモニウム塩、アミン塩などが例示され、
なかでも経済性の面からナトリウム塩が好ましい。The water-soluble polycarboxylic acid used in the present invention is a polymer of an α, β-unsaturated carboxylic acid type monomer or a copolymer of an ethylenically unsaturated monomer copolymerizable therewith, and the polymer. At least a part of the carboxyl group or acid anhydride group present in the molecule of the polymer or copolymer forms a salt, preferably 50 mol% or more, and the polymer or copolymer is usually , Number average molecular weight 500 to 50,000, preferably 1,000 to 250
00, more preferably 3000 to 10,000. If the molecular weight becomes excessively large, the dispersibility decreases, and on the contrary, the effect of thickening and aggregating the cement slurry occurs, which is not preferable. Specific examples of such salts include sodium, potassium, magnesium, calcium,
Examples are salts of alkali metals or alkaline earth metals such as barium, ammonium salts, amine salts, etc.
Among them, sodium salt is preferable from the viewpoint of economy.
【０００７】ここでα，β−不飽和カルボン酸系モノマ
ーとはカルボキシル基または酸無水物基を有する不飽和
カルボン酸またはその無水物を指し、その具体例として
は、アクリル酸、メタクリル酸、マレイン酸、フマル
酸、イタコン酸、無水マレイン酸、無水イタコン酸、無
水シトラコン酸などが例示される。Here, the α, β-unsaturated carboxylic acid type monomer means an unsaturated carboxylic acid having a carboxyl group or an acid anhydride group or an anhydride thereof, and specific examples thereof include acrylic acid, methacrylic acid and maleic acid. Examples thereof include acids, fumaric acid, itaconic acid, maleic anhydride, itaconic anhydride, citraconic anhydride and the like.
【０００８】また、共重合可能なエチレン系不飽和モノ
マーは、前記α，β−不飽和カルボン酸系モノマーとラ
ジカル重合可能なものであればいずれでもよく、その具
体例として、例えばエチレン、プロピレン、ブテン、２
−メチル−ブテン−１、２−メチル−ブテン−２、ヘキ
セン、オクテン、イソアミレン、ジイソブチレン、デセ
ン、シクロペンテン、シクロヘキセン等のオレフイン；
スチレン、ビニルトルエン、α−メチルスチレン、クマ
ロン、インデン等の芳香族ビニル系モノマー；メチルビ
ニルエーテル等のビニルエーテル系モノマー；アクリク
酸エチル、メタアクリル酸メチル等のアクリル酸アルキ
ルエステル系モノマー；および酢酸ビニル等が挙げられ
る。なかでも炭素数４〜６を有するオレフィンと無水マ
レイン酸との共重合体、さらに、イソアミレン−無水マ
レイン酸共重合体が分散性の面から好ましい。該共重合
体中のα，β−不飽和カルボン酸系モノマーの比率は適
宜選択しうるが、通常、１０モル％以上、好ましくは２
０モル％以上、もっとも好ましいのは５０モル％であ
る。Further, the copolymerizable ethylenically unsaturated monomer may be any one as long as it can be radically polymerized with the α, β-unsaturated carboxylic acid monomer, and specific examples thereof include ethylene, propylene and Butene, 2
Olefins such as -methyl-butene-1,2-methyl-butene-2, hexene, octene, isoamylene, diisobutylene, decene, cyclopentene, cyclohexene;
Aromatic vinyl monomers such as styrene, vinyltoluene, α-methylstyrene, coumarone, and indene; vinyl ether monomers such as methyl vinyl ether; alkyl acrylate monomers such as ethyl acrylate and methyl methacrylate; and vinyl acetate. Is mentioned. Among them, a copolymer of an olefin having 4 to 6 carbon atoms and maleic anhydride, and further an isoamylene-maleic anhydride copolymer are preferable from the viewpoint of dispersibility. The ratio of the α, β-unsaturated carboxylic acid monomer in the copolymer can be appropriately selected, but is usually 10 mol% or more, preferably 2 mol% or more.
It is 0 mol% or more, and most preferably 50 mol%.
【０００９】本発明で用いられるα，β−不飽和カルボ
ン酸系モノマーの重合体またはこれと共重合可能なエチ
レン系不飽和モノマーとの共重合体はその製法によって
制限されるものではないが、通常は常法に従ってラジカ
ル重合により製造される。また、これらの重合体および
共重合体の塩の製法は格別制限されるものではなく、モ
ノマーを中和したのち重合する方法、重合体または共重
合体を合成した後に常法に従って塩基の存在下で中和す
る方法のいずれを採用してもよい。The polymer of the α, β-unsaturated carboxylic acid monomer used in the present invention or the copolymer of the α, β-unsaturated carboxylic acid monomer and the ethylenically unsaturated monomer copolymerizable therewith is not limited by the production method thereof. Usually, it is produced by radical polymerization according to a conventional method. The method for producing salts of these polymers and copolymers is not particularly limited, and a method of neutralizing a monomer and then polymerizing it, or synthesizing a polymer or a copolymer in the presence of a base according to a conventional method Any of the methods of neutralizing with may be adopted.
【００１０】本発明で使用する水溶性ポリカルボン酸の
形態は固形であっても水溶液であってもよいが、通常は
取り扱いの容易さを考えて固形分濃度１０〜５０重量％
の水溶液で使用される。この際、本発明の効果を本質的
に損わない範囲であれば減水剤、分散剤、凝結遅延剤、
空気連行剤、消泡剤等の添加剤やその他の配合剤を適宜
混合することもできる。The water-soluble polycarboxylic acid used in the present invention may be in the form of a solid or an aqueous solution, but usually the solid content concentration is 10 to 50% by weight in consideration of easy handling.
Used in aqueous solution. At this time, a water reducing agent, a dispersant, a set retarder,
Additives such as an air entraining agent and an antifoaming agent and other compounding agents can be appropriately mixed.
【００１１】本発明のセメント系グラウト用ブリージン
グ低減剤はベントナイトと水溶性ポリカルボン酸とを配
合してなるものであり、通常ベントナイト１００重量部
に対して水溶性ポリカルボン酸２〜４０重量部、好まし
くは５〜２０重量部の割合で使用される。水溶性ポリカ
ルボン酸の使用量が２重量部より少ない場合にはセメン
トスラリーの流動性が改善されないので好ましくない。
また、４０重量部以上ではブリージング現象の低減効果
が得られないので好ましくない。The bleeding reducing agent for cement-based grout of the present invention is a mixture of bentonite and water-soluble polycarboxylic acid, and usually 2-40 parts by weight of water-soluble polycarboxylic acid per 100 parts by weight of bentonite, It is preferably used in a proportion of 5 to 20 parts by weight. When the amount of the water-soluble polycarboxylic acid used is less than 2 parts by weight, the fluidity of the cement slurry is not improved, which is not preferable.
If it is 40 parts by weight or more, the effect of reducing the breathing phenomenon cannot be obtained, which is not preferable.
【００１２】本発明のセメント系グラウト用ブリージン
グ低減剤を使用してセメント系グラウトのブリージング
を低減する方法は、改良すべき土壌により適宜変量し得
るが、使用に際して通常セメント配合物中のセメント１
００重量部に対して０．５〜５０重量部、好ましくは２
〜１５重量部を添加することによって、効率よくブリー
ジングを低減することができる。The method for reducing the bleeding of the cement grout using the bleeding reducing agent for the cement grout of the present invention can be appropriately varied depending on the soil to be improved.
0.5 to 50 parts by weight, preferably 2 to 100 parts by weight
Breathing can be efficiently reduced by adding about 15 parts by weight.
【００１３】本発明のセメント系グラウト用ブリージン
グ低減剤が適用出来るセメントの種類はとくに限定され
ず、その具体例として、例えば普通ポルトランドセメン
ト、早強ポルトランドセメント、中庸熱ポルトランドセ
メント、アルミナセメント、フライアッシュセメント、
高炉セメント、シリカセメント、鉱滓セメント、各種混
合セメント等が挙げられる。またセメントミルクの用途
にも有効である。The type of cement to which the breathing reducing agent for cement-based grout of the present invention can be applied is not particularly limited, and specific examples thereof include ordinary Portland cement, early strength Portland cement, moderate heat Portland cement, alumina cement, fly ash. cement,
Examples thereof include blast furnace cement, silica cement, slag cement, and various mixed cements. It is also effective for the use of cement milk.
【００１４】[0014]
【実施例】以下に実施例を挙げて本発明をさらに具体的
に説明する。なお、実施例、比較例及び参考例中の部及
び％はとくに断りのないかぎり重量基準である。 （試験方法） １．セメントスラリー 砂地盤想定配合（配合ＡおよびＣ）、及び粘性土地盤想
定配合（配合ＢおよびＤ）の４種類を調製した。使用し
た材料および配合は次のとおりである。 セメント：普通ポルトランドセメント 水 ：水道水 砂 ：豊浦標準砂 粘土 ：カオリン（ＳＡＭクレー） なお、砂は含水比１０％、粘土は含水比８０％に予め調
整したものを使用した。また、配合Ａ、配合Ｂ、配合Ｃ
および配合Ｄは表１に示した。EXAMPLES The present invention will be described in more detail with reference to the following examples. In addition, parts and% in the examples, comparative examples and reference examples are based on weight unless otherwise specified. (Test method) 1. Cement Slurry Four types were prepared: a sand ground assumption mix (formulations A and C) and a viscous ground assumption mix (formulations B and D). The materials and formulations used are as follows. Cement: Ordinary Portland cement Water: Tap water Sand: Toyoura standard sand Clay: Kaolin (SAM clay) In addition, sand used had a water content ratio of 10% and clay had a water content ratio of 80%. In addition, combination A, combination B, combination C
And the formulation D is shown in Table 1.
【００１５】[0015]
【表１】 [Table 1]
【００１６】２．流動性試験 日本土木学会基準（ＪＳＣＥ−１９８６）に従いＰロー
トによるセメントスラリーの流下時間を測定した（単
位：秒）。 ３．ブリージング率 日本土木学会基準（ＪＳＣＥ−１９８６）に従い、ブリ
ージング試験で求めた３時間および２０時間でのブリー
ジング水量を配合物量で除した値を百分率で表した（単
位：％）。 ４．圧縮強度 ＪＩＳ Ｒ−５２０１のセメント物理試験方法に準じ
て、供試体（直径５ｃｍ，高さ１０ｃｍの円筒）を作成
し、３日間気中養生後、水中養生を行い、７日後と２８
日後の圧縮強度を求めた（単位：ｋｇ／ｃｍ2 ）。2. Flowability test The flow time of the cement slurry in the P funnel was measured according to the Japan Society of Civil Engineers standard (JSCE-1986) (unit: second). 3. Breathing rate In accordance with the Japan Society of Civil Engineers standard (JSCE-1986), the value obtained by dividing the breathing water amount at 3 hours and 20 hours obtained by the breathing test by the compounding amount was expressed as a percentage (unit:%). 4. Compressive strength A specimen (cylinder having a diameter of 5 cm and a height of 10 cm) was prepared in accordance with the cement physical test method of JIS R-5201, and after air curing for 3 days, water curing was performed for 7 days and 28 days.
The compressive strength after day was determined (unit: kg / cm 2 ).
【００１７】実施例１〜１９、比較例１〜１４ 合成ベントナイト（クニゲルＶＯ、クニミネ社製）、ラ
ジカル重合によって得られたイソアミレンと無水マレイ
ン酸との等モル共重合体（重量平均分子量６０００）の
ナトリウム塩、ポリアクリル酸（重量平均分子量５００
０）のナトリウム塩とを表２の配合で混合してセメント
系グラウト用ブリージング低減剤を調製し、表３（配合
Ａ）、表４（配合Ｂ）、表５（配合Ｃ）および表６（配
合Ｄ）に示すセメントスラリーに所定量添加して、ブリ
ージング試験、流動性試験および圧縮強度を測定した。
また、比較のため、既存のセメント用減水剤であるポリ
アルキルアリルスルホン酸高縮合物（マイテイー１５０
花王（株）社製）とベントナイトとを配合した試料も
調製し同様にセメントスラリーに添加した。結果を表
３、表４、表５および表６に示す。なお、添加量はセメ
ント１００重量部に対する重量部である。Examples 1 to 19 and Comparative Examples 1 to 14 of synthetic bentonite (Kunigel VO, manufactured by Kunimine) and an equimolar copolymer of isoamylene obtained by radical polymerization and maleic anhydride (weight average molecular weight of 6000). Sodium salt, polyacrylic acid (weight average molecular weight 500
0) Sodium salt of 0) is mixed in the formulation of Table 2 to prepare a bleeding reducing agent for cement-based grout, and Table 3 (Formulation A), Table 4 (Formulation B), Table 5 (Formulation C) and Table 6 ( A predetermined amount was added to the cement slurry shown in Formulation D), and a breathing test, a fluidity test and a compressive strength were measured.
In addition, for comparison, a polycondensed polysulfonic acid polycondensate, which is an existing water reducing agent for cement (Mighty 150
A sample prepared by mixing Kao Corp. and bentonite was also prepared and similarly added to the cement slurry. The results are shown in Table 3, Table 4, Table 5 and Table 6. The addition amount is parts by weight based on 100 parts by weight of cement.
【００１８】[0018]
【表２】 [Table 2]
【００１９】[0019]
【表３】 [Table 3]
【００２０】[0020]
【表４】 [Table 4]
【００２１】[0021]
【表５】 [Table 5]
【００２２】[0022]
【表６】 [Table 6]
【００２３】表３、表４、表５および表６の結果から、
本発明のセメント系グラウト用ブリージング低減剤を使
用することによって、セメントスラリーの流動性を低下
させることなく、ブリージング現象を抑制できることが
わかる。From the results of Table 3, Table 4, Table 5 and Table 6,
It can be seen that the use of the cement-based grout bleeding reducing agent can suppress the bleeding phenomenon without lowering the fluidity of the cement slurry.
【００２４】[0024]
【発明の効果】かくして本発明によれば、セメントスラ
リーの流動性を低下させることなく、効率良くブリージ
ング現象を抑制することができる。As described above, according to the present invention, the breathing phenomenon can be efficiently suppressed without lowering the fluidity of the cement slurry.
【手続補正書】[Procedure amendment]
【提出日】平成５年１２月２８日[Submission date] December 28, 1993
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１９[Correction target item name] 0019
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１９】[0019]
【表３】 [Table 3]
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２０[Correction target item name] 0020
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２０】[0020]
【表４】 [Table 4]
【手続補正３】[Procedure 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２１[Correction target item name] 0021
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２１】[0021]
【表５】 [Table 5]
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２２[Name of item to be corrected] 0022
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２２】[0022]
【表６】 [Table 6]
───────────────────────────────────────────────────── フロントページの続き (72)発明者 斉藤 誠 東京都千代田区丸の内二丁目６番１号 古 河総合ビル内 日本ゼオン株式会社内 (72)発明者 古田 茂 東京都千代田区丸の内二丁目６番１号 古 河総合ビル内 日本ゼオン株式会社内 (72)発明者 岸川 豊 東京都千代田区丸の内二丁目６番１号 古 河総合ビル内 日本ゼオン株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Makoto Saito 2-6-1, Marunouchi, Chiyoda-ku, Tokyo Inside Furukawa General Building Zeon Co., Ltd. (72) Inventor Shigeru Furuta 2-6, Marunouchi, Chiyoda-ku, Tokyo No. 1 Inside Furukawa Building Inside Zeon Corporation (72) Inventor Yutaka Kishikawa 2-6-1, Marunouchi, Chiyoda-ku, Tokyo Inside Furukawa Building Inside Zeon Corporation
Claims (6)
を配合してなるセメント系グラウト用ブリージング低減
剤。1. A bleeding reducing agent for cement-based grout, which comprises blending bentonite and a water-soluble polycarboxylic acid.
性ポリカルボン酸２〜４０重量部を配合してなるセメン
ト系グラウト用ブリージング低減剤。2. A breathing reducing agent for cement-based grout, which comprises 100 parts by weight of bentonite and 2 to 40 parts by weight of a water-soluble polycarboxylic acid.
有するオレフインと無水マレイン酸との共重合体であっ
て数平均分子量が５００〜５００００のものの塩である
請求項１または２のセメント系グラウト用ブリージング
低減剤。3. The cement according to claim 1, wherein the water-soluble polycarboxylic acid is a salt of an olefin having 4 to 6 carbon atoms and maleic anhydride and having a number average molecular weight of 500 to 50,000. Breathing reducer for system grout.
無水マレイン酸共重合体であって数平均分子量が３００
０〜１００００のもののナトリウム塩である請求項１ま
たは２のセメント系グラウト用ブリージング低減剤。4. The water-soluble polycarboxylic acid is isoamylene-
Maleic anhydride copolymer having a number average molecular weight of 300
The cement-based bleeding reducing agent for grout according to claim 1 or 2, which is a sodium salt of 0 to 10,000.
用ブリージング低減剤をセメント１００重量部に対して
０．５〜５０重量部添加することを特徴とするセメント
系グラウトのブリージング低減方法。5. A method for reducing bleeding of cement-based grout, which comprises adding 0.5 to 50 parts by weight of the bleeding reducing agent for cement-based grout according to claim 1 to 100 parts by weight of cement.
用ブリージング低減剤をセメント１００重量部に対して
２〜１５重量部添加することを特徴とするセメント系グ
ラウトのブリージング低減方法。6. A method for reducing bleeding of cement-based grout, comprising adding 2 to 15 parts by weight of the bleeding-reducing agent for cement-based grout according to claim 1 to 100 parts by weight of cement.