JPH061947A - Facing two-pack chipping-resistant coating composition - Google Patents

Abstract

PURPOSE:To provide the subject composition causing no maladhesion and the deterioration of surfaces coated therewith due to acidic rain, excellent in scratch resistance, thus useful for e.g. the side seals of automotive bodies, comprising a polyol resin, talc and a specific curing agent at specified proportion. CONSTITUTION:The objective composition can be obtained by incorporating (A) a primary agent comprising (1) 100 pts.wt. of a polyol resin (e.g. polyether polyol) and (2) 5-100 pts.wt. of talc with (B) a curing agent consisting of a buret-modified hexamethylene diisocyanate resin at the equivalent ratio of the active isocyanate group in the component B to the hydroxyl group in the component A of (300:100) to (150:100) and also (C) 60-70wt.%, based on the solid content of the mixed coating, of a pigment.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は自動車の外板、特に自動
車車体のサイドシル部、ロッカーパネル部、フェンダー
部などに石跳ね傷防止（耐チッピング）を目的で塗装さ
れる上塗り２液型耐チッピング塗料組成物に関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a two-component topcoating chipping resistant coating for the purpose of preventing stone bruising (chipping resistance) on the outer panels of automobiles, particularly on the side sills, rocker panels and fenders of automobile bodies. The present invention relates to a coating composition.

【０００２】[0002]

【従来の技術】従来から、車両走行中に路面から跳ね上
がる小石、砂利などが原因で起こる車両外板の塗膜剥離
は、発錆や外観不良を引き起こすために問題になってお
り、車両外板を保護する目的で衝撃吸収性を持った塗料
が塗装されている。特に自動車車体のサイドシル部、ロ
ッカーパネル部、フェンダー部などの、石跳ねによる衝
撃の大きい部位には上塗り塗料塗装後に耐チッピング塗
料が塗装されている。このような塗装を完成車体に行う
場合には大型乾燥設備が不必要な２液型の耐チッピング
塗料が塗装されている。また塗装部位が耐候性の必要性
が少ない部位である場合には、塗装される耐チッピング
塗料はトルエンジイソシアネート樹脂系が利用されてい
る。2. Description of the Related Art Conventionally, peeling of a coating film on a vehicle outer plate caused by pebbles, gravel, etc. that jumps up from the road surface while the vehicle is running has been a problem because it causes rusting and poor appearance. A paint with impact absorption is applied for the purpose of protecting the. Particularly, the chipping-resistant paint is applied after the topcoat paint has been applied to the parts such as the side sill part, the rocker panel part, and the fender part of the automobile body where the impact of stone bounce is large. When such a coating is applied to a completed vehicle body, a two-pack type chipping-resistant paint which does not require a large-scale drying facility is applied. Further, when the painted part is a part that is less required to have weather resistance, a toluene diisocyanate resin system is used for the chipping resistant paint to be painted.

【０００３】[0003]

【発明が解決しようとする課題】最近社会問題化してい
る酸性雨（ｐＨ４以下）による表面劣化や、洗車時のす
り傷対策を目的とし、耐候性や機械的物性に優れた種々
の上塗り塗料の開発が近年増加している。それらの塗料
による塗膜の多くは、シリコーン系樹脂やフッソ系樹脂
を用いた複合架橋を取り入れている。たとえば、特開平
２−２４８４７７にある塗料組成物などがあげられる
が、これらは撥水性、耐溶剤性、機械的物性に優れてい
る反面、上塗り塗料塗装後に塗装する上塗り型耐チッピ
ング塗料の塗膜が付着不良を起こし、本来の性能を発揮
できないという問題が発生している。また自動車のデザ
インも多種多様化する中、耐チッピング塗料の塗装部位
にも耐候性が必要となってきた。このような現状から付
着性と耐候性に優れた上塗り２液型耐チッピング塗料の
開発が要望されている。[Problems to be Solved by the Invention] For the purpose of countermeasures against surface deterioration due to acid rain (pH 4 or less), which has become a social problem recently, and scratches during car washing, various topcoat paints excellent in weather resistance and mechanical properties have been prepared. Development has increased in recent years. Many of the coating films made from these paints incorporate composite cross-links using silicone-based resins or fluorine-based resins. For example, there are coating compositions and the like described in JP-A-2-248477. These are excellent in water repellency, solvent resistance, and mechanical properties, but on the other hand, the coating film of a top-coating type chipping-resistant coating to be applied after the top-coating coating is applied. However, there is a problem in that the original performance cannot be exhibited due to poor adhesion. In addition, as automobile designs are diversified, weather resistance is also required for the parts coated with chipping-resistant paint. Under these circumstances, there has been a demand for the development of a two-component topcoating chipping-resistant coating composition having excellent adhesion and weather resistance.

【０００４】[0004]

【課題を解決するための手段】本発明者らは、前記上塗
り塗装面において耐チッピング性はもちろんのこと、付
着性と耐候性に優れた塗膜を形成する上塗り２液型耐チ
ッピング塗料の開発を目的として研究を鋭意行った。そ
の結果、ポリオール樹脂と特定のイソシアネート樹脂を
主成分として特定量のタルクを含有する塗料であって、
ポリオール樹脂中のヒドロキシル基に対するイソシアネ
ート樹脂の有効イソシアネート基を当量比で３００：１
００〜１５０：１００の割合で配合し、かつ混合塗料固
形分あたりの顔料重量％濃度（以下ＰＷＣと略記する）
を６０〜７０に配合してなる塗料組成物を、前記上塗り
塗装がなされた自動車のサイドシル部、ロッカーパネル
部、フェンダー部などに塗装することにより耐チッピン
グ性はもちろんのこと、付着性と耐候性に優れた塗膜を
形成することを見いだし、本発明を完成した。The inventors of the present invention have developed a two-component topcoating chipping-resistant coating composition that forms a coating film having excellent adhesion and weather resistance as well as chipping resistance on the above-mentioned topcoating surface. For the purpose of As a result, a paint containing a specific amount of talc with a polyol resin and a specific isocyanate resin as main components,
Equivalent ratio of effective isocyanate group of isocyanate resin to hydroxyl group in polyol resin is 300: 1.
It is blended in a ratio of 00 to 150: 100, and the pigment weight% concentration per the mixed coating solid content (hereinafter abbreviated as PWC).
By coating a coating composition containing 60 to 70 on the side sill portion, rocker panel portion, fender portion, etc. of the above-mentioned top-coated automobile, not only chipping resistance but also adhesion and weather resistance The present invention has been completed by finding that an excellent coating film is formed.

【０００５】すなわち本発明は、ポリオール樹脂（Ａ）
１００重量部、タルク５〜１００重量部からなる主剤
に、ビウレット変性ヘキサメチレンジイソシアネート樹
脂（Ｂ）からなる硬化剤を、ポリオール樹脂（Ａ）中の
ヒドロキシル基に対するビウレット変性ヘキサメチレン
ジイソシアネート樹脂（Ｂ）の有効イソシアネート基を
当量比で３００：１００〜１５０：１００の割合で混合
し、かつ混合塗料固形分あたりの顔料重量％濃度（ＰＷ
Ｃ）を６０〜７０に配合してなることを特徴とする上塗
り２液型耐チッピング塗料組成物に関するものである。That is, the present invention relates to a polyol resin (A)
100 parts by weight of talc and 5 to 100 parts by weight of talc as a main agent, a curing agent of biuret-modified hexamethylene diisocyanate resin (B), and a biuret-modified hexamethylene diisocyanate resin (B) of hydroxyl group in polyol resin (A). Effective isocyanate groups are mixed in an equivalent ratio of 300: 100 to 150: 100, and the pigment weight% concentration (PW
The present invention relates to a two-pack topcoating anti-chip coating composition for top coating, which comprises 60 to 70 of C).

【０００６】本発明者らは、前記上塗り塗装面において
耐チッピング性はもちろんのこと、付着性に優れた塗膜
を形成する上塗り型耐チッピング塗料を開発するに当た
り、従来の２液型耐チッピング塗料の組成について、イ
ソシアネート樹脂のＮＣＯ当量、構造、硬化触媒量など
が付着性に与える影響を研究した結果、ＮＣＯ／ＯＨ当
量比を高めて塗膜中にウレタン結合以外に適当量の尿素
結合を生成させることにより前記上塗り塗装面への付着
性が向上することを見出した。これは、塗膜中の架橋密
度を高くすると付着に寄与する官能基の数が増加し、結
果として付着性が向上されるものと推定できる。また、
過剰のＮＣＯが前記上塗り塗装表面のＯＨと架橋反応し
て付着性の向上に寄与したとも推定できる。さらにＰＷ
Ｃを高くすることも付着性の向上に寄与することが判明
した。これは、顔料の凝集破壊による耐チッピング性能
の向上と擬似架橋密度の向上によると推定できる。特に
適当量のタルク充填は凝集破壊による耐チッピング性の
向上に大きく貢献し、塗膜収縮による付着性の低下も緩
和していると考えられる。本発明は、このような知見に
基づいて、完成されたものである。The inventors of the present invention developed a top-coating type chipping-resistant paint which forms not only chipping resistance on the above-mentioned top-coating coated surface but also excellent adhesiveness, in order to develop a conventional two-pack type chipping-resistant coating material. As a result of studying the influence of the NCO equivalent, structure, and curing catalyst amount of the isocyanate resin on the adhesiveness of the composition, the NCO / OH equivalent ratio was increased and a proper amount of urea bond other than urethane bond was generated in the coating film. It was found that the adhesion to the above-mentioned top-coating surface is improved by doing so. It can be presumed that this is because when the crosslink density in the coating film is increased, the number of functional groups contributing to the adhesion is increased, and as a result, the adhesion is improved. Also,
It can also be presumed that excess NCO contributed to the improvement of adhesion by cross-linking reaction with OH on the surface of the top coating. Further PW
It was found that increasing C also contributes to the improvement of adhesion. It can be presumed that this is due to improvement in chipping resistance performance due to cohesive failure of the pigment and improvement in pseudo-crosslink density. In particular, it is considered that the appropriate amount of talc filling greatly contributes to the improvement of chipping resistance due to cohesive failure, and alleviates the decrease in adhesion due to shrinkage of the coating film. The present invention has been completed based on such findings.

【０００７】以下に本発明の塗料組成物について詳細に
説明する。The coating composition of the present invention will be described in detail below.

【０００８】本発明で使用するビウレット変性ヘキサメ
チレンジイソシアネート樹脂（Ｂ）は、下記一般式で表
される。The biuret-modified hexamethylene diisocyanate resin (B) used in the present invention is represented by the following general formula.

【０００９】 [0009]

【００１０】かかる樹脂の例としてはスミジュールＮ−
１００（住友バイエルウレタン株式会社製商品名）、デ
ュラネート２４Ａ−１００（旭化成工業株式会社製商品
名）などがある。Examples of such resins include Sumidule N-
100 (Sumitomo Bayer Urethane Co., Ltd. product name), Duranate 24A-100 (Asahi Kasei Co., Ltd. product name), and the like.

【００１１】本発明で使用するポリオール樹脂（Ａ）
は、ポリエーテルポリオール、ポリエステルポリオール
などが使用できる。また上記ポリオール樹脂を必要によ
り２種類以上併用しても差し支えない。Polyol resin (A) used in the present invention
Polyether polyol, polyester polyol and the like can be used as the material. If necessary, two or more of the above polyol resins may be used in combination.

【００１２】本発明の塗料組成物は、ポリオール樹脂
（Ａ）中のヒドロキシル基に対するビウレット変性ヘキ
サメチレンジイソシアネート樹脂（Ｂ）の有効イソシア
ネート基を当量比で３００：１００〜１５０：１００の
割合で混合する必要がある。有効イソシアネート基の当
量比が３００：１００を上回る場合は、前記イソシアネ
ート樹脂の使用割合を増加する必要があり、結果として
コストが極端に増大するので好ましくない。また１５
０：１００を下回る場合は、付着に寄与する官能基数が
不足するために結果として付着性が向上しないので好ま
しくない。In the coating composition of the present invention, the effective isocyanate groups of the biuret-modified hexamethylene diisocyanate resin (B) are mixed with the hydroxyl groups in the polyol resin (A) at an equivalent ratio of 300: 100 to 150: 100. There is a need. If the equivalent ratio of the effective isocyanate group exceeds 300: 100, it is necessary to increase the use ratio of the isocyanate resin, resulting in an extremely high cost, which is not preferable. Again 15
When it is less than 0: 100, the number of functional groups that contribute to adhesion is insufficient, and as a result, the adhesion is not improved, which is not preferable.

【００１３】本発明で使用するタルクは、一般式 4SiO₂ ・3MgO・H₂O で表される。かかるタルクは一般塗料用に使用されるタ
ルクであれば全て使用できる。The talc used in the present invention is represented by the general formula 4SiO ₂ .3MgO.H ₂ O. Any talc used for general paints can be used as such talc.

【００１４】本発明の塗料組成物は、ポリオール樹脂
（Ａ）が１００重量部含まれる主剤に対し前記タルクを
５〜１００重量部配合する必要がある。配合割合が５重
量部を下回るか１００重量部を上回る場合は、耐チッピ
ング性が低下するので好ましくない。In the coating composition of the present invention, it is necessary to mix 5 to 100 parts by weight of the above talc with the main component containing 100 parts by weight of the polyol resin (A). If the blending ratio is less than 5 parts by weight or more than 100 parts by weight, the chipping resistance decreases, which is not preferable.

【００１５】本発明の塗料組成物は、一般塗料用に使用
される顔料を使用してＰＷＣを６０〜７０に調整する必
要がある。ＰＷＣが６０を下回る場合は、付着性が向上
しないので好ましくない。またＰＷＣが７０を上回る場
合は、塗膜がもろくなり結果として耐チッピング性が低
下するので好ましくない。In the coating composition of the present invention, it is necessary to adjust the PWC to 60 to 70 by using the pigment used for general coating materials. If the PWC is less than 60, the adhesion is not improved, which is not preferable. Further, if the PWC exceeds 70, the coating film becomes brittle and, as a result, the chipping resistance decreases, which is not preferable.

【００１６】前記顔料の主なものは体質顔料、着色顔料
などであり、体質顔料は炭酸カルシウム、シリカ、カオ
リン、バライト、クレーなどの一般塗料用に使用される
体質顔料が使用できる。着色顔料はカーボン、酸化チタ
ンなどの一般塗料用に使用される着色顔料が使用でき
る。その他、必要に応じて一般塗料用に使用される防錆
顔料が使用できる。The main pigments are extender pigments and coloring pigments, and extender pigments such as calcium carbonate, silica, kaolin, barite and clay which are used for general paints can be used. As the color pigment, a color pigment such as carbon or titanium oxide used for general paints can be used. In addition, a rust preventive pigment used for general paints can be used if necessary.

【００１７】本発明の塗料組成物には前述した各成分の
他に、必要により通常の溶剤系塗料組成物に使用される
その他の成分が使用できる。たとえば、反応促進剤であ
るスズ系化合物、コバルト系化合物などが使用できるが
作業性を考慮した場合、これらは塗料に対して０．０１
〜１重量％の範囲で使用するのが望ましい。界面調整剤
であるシリコーン系、非シリコーン系、フッソ系、アク
リル系共重合体などが使用できるが多量に使用すると付
着性が低下する恐れがあるので、塗料に対して０．０１
〜１重量％の範囲で使用するのが望ましい。さらに粘性
改質剤である有機系、無機系共重合体および希釈剤であ
るトルエン、キシレン、ミネラルスピリットなどの炭化
水素系溶剤、酢酸エチル、酢酸ブチルなどのエステル系
溶剤、メチルエチルケトンなどのケトン系溶剤、エタノ
ール、ブタノールなどのアルコール系溶剤、ブチルエー
テル、エチレングリコールモノメチルエーテルなどのエ
ーテル系溶剤などを単独または適宜併用して使用でき
る。In the coating composition of the present invention, in addition to the above-mentioned components, if necessary, other components used in ordinary solvent-based coating compositions can be used. For example, a tin-based compound or a cobalt-based compound which is a reaction accelerator can be used.
It is desirable to use in the range of ˜1% by weight. Interface modifiers such as silicone-based, non-silicone-based, fluorine-based, and acrylic-based copolymers can be used, but if used in a large amount, the adhesiveness may decrease.
It is desirable to use in the range of ˜1% by weight. In addition, viscosity modifiers such as organic and inorganic copolymers and diluents such as toluene, xylene, mineral spirits and other hydrocarbon solvents, ethyl acetate, butyl acetate and other ester solvents, and methyl ethyl ketone and other ketone solvents. , Alcohol solvents such as ethanol and butanol, and ether solvents such as butyl ether and ethylene glycol monomethyl ether can be used alone or in combination.

【００１８】本発明塗料組成物は、前記主剤と前記のイ
ソシアネート樹脂を用いてなる組成物（硬化剤）との２
液塗料組成物であり、各成分を混合分散して調整する。
塗膜の形成は、塗装直前にこの２液を所定比率にて混合
し、たとえばエアスプレー塗装、エアレススプレー塗装
（２液混合型の塗装機の使用が好ましい）などの従来使
用されている塗装機、塗装設備によって塗装することが
でき、室温で約１〜５時間乾燥して形成されるが、３０
〜５０℃で１０分程度乾燥することによりさらに短時間
で形成される。また、反応促進剤の配合量を調整するこ
とによっても任意の乾燥時間を選択することができる。The coating composition of the present invention comprises the above-mentioned base material and a composition (curing agent) using the above-mentioned isocyanate resin.
It is a liquid coating composition and is prepared by mixing and dispersing each component.
The coating film is formed by mixing these two liquids at a predetermined ratio immediately before coating, and for example, conventionally used coating machines such as air spray coating and airless spray coating (preferably using a two liquid mixing type coating machine). It can be painted by painting equipment and is formed by drying at room temperature for about 1-5 hours.
It is formed in a shorter time by drying at -50 ° C for about 10 minutes. Further, an arbitrary drying time can be selected also by adjusting the compounding amount of the reaction accelerator.

【００１９】[0019]

【実施例】次に、本発明の実施例について説明する。文
中の部および％はいずれも重量による。EXAMPLES Next, examples of the present invention will be described. All parts and% in the text are by weight.

【００２０】硬化剤Ａ：ビウレット変性ヘキサメチレン
ジイソシアネート樹脂であるデュラネート２５Ａ−１０
０（旭化成工業株式会社製商品名）と酢酸イソブチルか
らなる固形分７５％、ＮＣＯ％１８のビウレット変性ヘ
キサメチレンイソシアネート樹脂液を得た。Curing agent A: Duranate 25A-10, a biuret-modified hexamethylene diisocyanate resin
A biuret-modified hexamethylene isocyanate resin liquid having a solid content of 75% and an NCO% of 18 consisting of 0 (trade name of Asahi Kasei Co., Ltd.) and isobutyl acetate was obtained.

【００２１】硬化剤Ｂ：アダクト変性トルエンジイソシ
アネート樹脂であるスミジュールＬ（住友バイエルウレ
タン株式会社製商品名）と酢酸ブチルからなる固形分７
５％、ＮＣＯ％１３のアダクト変性トルエンジイソシア
ネート樹脂液を得た。Curing agent B: Solid content 7 consisting of butyl acetate and Sumidule L (trade name of Sumitomo Bayer Urethane Co., Ltd.), which is an adduct-modified toluene diisocyanate resin
An adduct-modified toluene diisocyanate resin solution containing 5% and NCO% 13 was obtained.

【００２２】主剤Ａ：ポリエステルポリエーテルポリオ
ール樹脂（ＯＨ価１６５）であるディスモヘン１１５０
（住友バイエルウレタン株式会社製商品名）１００部、
炭酸カルシウム３１０部、カーボン５部、タルク５０
部、アミン変性ベントナイト５部、ジブチルスズジラウ
レート０．１部、変性ポリシロキサン０．１部、酢酸イ
ソブチル４２部の混合物を６０分高速撹拌し分散させ、
塗料組成物を得た。Main agent A: Dismohen 1150 which is a polyester polyether polyol resin (OH value 165)
(Sumitomo Bayer Urethane Co., Ltd. product name) 100 copies,
310 parts calcium carbonate, 5 parts carbon, 50 talc
Part, 5 parts of amine-modified bentonite, 0.1 part of dibutyltin dilaurate, 0.1 part of modified polysiloxane and 42 parts of isobutyl acetate are stirred for 60 minutes at high speed to disperse,
A coating composition was obtained.

【００２３】主剤Ｂ：ポリエステルポリエーテルポリオ
ール樹脂（ＯＨ価１６５）であるディスモヘン１１５０
（住友バイエルウレタン株式会社製商品名）１００部、
炭酸カルシウム１８０部、カーボン１５部、アミン変性
ベントナイト５部、ジブチルスズジラウレート０．７
部、酢酸イソブチル５６部、トルエン１５部の混合物を
６０分高速撹拌し分散させ、塗料組成物を得た。Main agent B: Dismohen 1150 which is a polyester polyether polyol resin (OH value 165)
(Sumitomo Bayer Urethane Co., Ltd. product name) 100 copies,
180 parts of calcium carbonate, 15 parts of carbon, 5 parts of amine-modified bentonite, 0.7 parts of dibutyltin dilaurate
Part, 56 parts of isobutyl acetate, and 15 parts of toluene were stirred at high speed for 60 minutes to disperse the mixture to obtain a coating composition.

【００２４】主剤Ｃ：ポリエステルポリエーテルポリオ
ール樹脂（ＯＨ価１６５）であるディスモヘン１１５０
（住友バイエルウレタン株式会社製商品名）１００部、
炭酸カルシウム３５８部、カーボン５部、タルク２部、
アミン変性ベントナイト５部、ジブチルスズジラウレー
ト０．１部、変性ポリシロキサン０．１部、酢酸イソブ
チル４２部の混合物を６０分高速撹拌し分散させ、塗料
組成物を得た。Main agent C: Dismohen 1150 which is a polyester polyether polyol resin (OH value 165)
(Sumitomo Bayer Urethane Co., Ltd. product name) 100 copies,
358 parts calcium carbonate, 5 parts carbon, 2 parts talc,
A mixture of 5 parts of amine-modified bentonite, 0.1 part of dibutyltin dilaurate, 0.1 part of modified polysiloxane, and 42 parts of isobutyl acetate was rapidly stirred for 60 minutes to disperse the mixture to obtain a coating composition.

【００２５】主剤Ｄ：ポリエステルポリエーテルポリオ
ール樹脂（ＯＨ価１６５）であるディスモヘン１１５０
（住友バイエルウレタン株式会社製商品名）１００部、
炭酸カルシウム２００部、カーボン５部、タルク１６０
部、アミン変性ベントナイト５部、ジブチルスズジラウ
レート０．１部、変性ポリシロキサン０．１部、酢酸イ
ソブチル４２部の混合物を６０分高速撹拌し分散させ、
塗料組成物を得た。Main agent D: Dismohen 1150 which is a polyester polyether polyol resin (OH value 165)
(Sumitomo Bayer Urethane Co., Ltd. product name) 100 copies,
200 parts calcium carbonate, 5 parts carbon, 160 talc
Part, 5 parts of amine-modified bentonite, 0.1 part of dibutyltin dilaurate, 0.1 part of modified polysiloxane and 42 parts of isobutyl acetate are stirred for 60 minutes at high speed to disperse,
A coating composition was obtained.

【００２６】実施例 １：主剤Ａ５１２．２部、硬化剤
Ａ１７４．８部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で２５４：１００、ＰＷＣ６１．６の塗料組
成物を得た。Example 1 A coating composition comprising 512.2 parts of a main agent A and 174.8 parts of a curing agent, and having an equivalent ratio of isocyanate groups in an isocyanate resin to hydroxyl groups in a polyol resin of 254: 100 and PWC61.6. Got

【００２７】実施例 ２：主剤Ａ５１２．２部、硬化剤
Ａ１３１．３部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で１９２：１００、ＰＷＣ６５．１の塗料組
成物を得た。Example 2: A coating composition of PWC65.1, which is composed of 512.2 parts of the main agent A and 131.3 parts of a curing agent A, and the equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin is 192: 100. Got

【００２８】実施例 ３：主剤Ａ５１２．２部、硬化剤
Ａ１０５．４部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で１５３：１００、ＰＷＣ６７．４の塗料組
成物を得た。Example 3: A coating composition of PWC 67.4, which comprises 512.2 parts of the main agent A and 105.4 parts of the curing agent A, and the equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin is 153: 100. Got

【００２９】比較例 １：主剤Ａ５１２．２部、硬化剤
Ａ２２４．６部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で３２７：１００、ＰＷＣ５８．０の塗料組
成物を得た。Comparative Example 1: A coating composition consisting of 512.2 parts of the main agent A and 224.6 parts of the curing agent, and having an equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin of 327: 100 and PWC of 58.0. Got

【００３０】比較例 ２：主剤Ａ５１２．２部、硬化剤
Ａ７２．０部からなり、ポリオール樹脂中のヒドロキシ
ル基に対するイソシアネート樹脂中のイソシアネート基
を当量比で１０５：１００、ＰＷＣ７０．６の塗料組成
物を得た。Comparative Example 2: A coating composition consisting of 512.2 parts of the main agent A and 72.0 parts of the curing agent, and having an equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin of 105: 100 and PWC of 70.6. Got

【００３１】比較例 ３：主剤Ｂ３７１．７部、硬化剤
Ｂ１２３．９部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で１３０：１００、ＰＷＣ５０．９の塗料組
成物を得た。Comparative Example 3: A coating composition consisting of 371.7 parts of the main agent B and 123.9 parts of a curing agent, and having an equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin of 130: 100 and PWC of 50.9. Got

【００３２】比較例 ４：主剤Ｃ５１２．２部、硬化剤
Ａ１３１．３部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で１９２：１００、ＰＷＣ６５．１の塗料組
成物を得た。COMPARATIVE EXAMPLE 4 A coating composition of PWC65.1, consisting of 512.2 parts of the main agent C and 131.3 parts of the curing agent A, in which the equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin was 192: 100. Got

【００３３】比較例 ５：主剤Ｄ５１２．２部、硬化剤
Ａ１３１．３部からなり、ポリオール樹脂中のヒドロキ
シル基に対するイソシアネート樹脂中のイソシアネート
基を当量比で１９２：１００、ＰＷＣ６５．１の塗料組
成物を得た。Comparative Example 5: A coating composition consisting of 512.2 parts of a main agent D and 131.3 parts of a curing agent A, and having an equivalent ratio of the isocyanate group in the isocyanate resin to the hydroxyl group in the polyol resin of 192: 100, PWC 65.1. Got

【００３４】試験例 １：リン酸亜鉛処理軟綱板状に電
着塗膜、中塗り塗膜、上塗り塗膜、および特開平２−２
４８４７７にもとづくクリヤー塗膜であるＵＣＸ−３０
０Ｋ（関西ペイント株式会社製商品名）を１４０℃にて
形成した工程塗装板上に、上記各実施例１〜３および比
較例１〜５の塗料組成物を乾燥膜厚２００μとなるよう
に塗装し、５０℃で１０分間乾燥したのちに室温で５日
間放置した。得られた塗膜の付着性を確認するために付
着性試験を実施した。また、耐チッピング性を確認する
ためにグラベロ試験を実施した。それらの試験結果を表
１に示す。Test Example 1: Zinc phosphate-treated soft steel plate-like electrodeposition coating film, intermediate coating film, top coating film, and JP-A-2-2
UCX-30, a clear coating film based on 48477
0K (trade name of Kansai Paint Co., Ltd.) was formed at 140 ° C. on the process coated plate so that the coating compositions of Examples 1 to 3 and Comparative Examples 1 to 5 were coated to a dry film thickness of 200 μ. Then, it was dried at 50 ° C. for 10 minutes and then left at room temperature for 5 days. An adhesion test was conducted to confirm the adhesion of the obtained coating film. In addition, a gravure test was carried out to confirm the chipping resistance. The test results are shown in Table 1.

【００３５】 [0035]

【００３６】付着性試験評価：ます目間隔２ｍｍの碁盤
目１００個を素地に到達するように刃を入れた後にセロ
テープにて剥離させた。評価は剥離個数にて行った。Evaluation of Adhesion Test: 100 cross-cuts having 2 mm intervals were put on a blade so as to reach the base material and then peeled off with a cellophane tape. The evaluation was performed by the number of peeled pieces.

【００３７】グラベロ試験評価：スガ試験機株式会社製
ＪＡ−４００ＬＡ型飛石試験機を使用し、以下の試験条
件にて実施した。 飛石種類 ：玄武岩（標準ふるいＪＩＳＺ８８０１−１
９６５による７．９３〜１１．１ｍｍのもの） 飛石量 ：１Ｋｇ 空気圧力 ：５Ｋｇｆ／ｃｍ² 吹付距離 ：３００ｍｍ 試料温度 ：室温（２０℃） 試料保持角：吹付方向に対して垂直 試験板面積：１４０ｍｍ×７０ｍｍ ５は素地に到達するキズがなく、剥離がないもの。４は
素地に到達するキズがなく、０．５ｍｍ角以上の剥離が
ないもの。３は素地に到達するキズがなく、１ｍｍ角以
上の剥離がないもの。２は素地に到達するキズがなく、
２ｍｍ角以上の剥離がないもの。１は前記以外のもの、
素地に到達するキズや剥離の著しいもの。Gravel test evaluation: A JA-400LA stepping stone tester manufactured by Suga Test Instruments Co., Ltd. was used under the following test conditions. Stepping stone type: Basalt (standard sieve JISZ8801-1
795 to 7.93 to 11.1 mm) Stepping stone amount: 1 kg Air pressure: 5 kgf / cm ² Spraying distance: 300 mm Sample temperature: Room temperature (20 ° C) Sample holding angle: Vertical to spraying direction Test plate area: 140 mm × 70 mm 5 has no scratches that reach the substrate and does not peel off. No. 4 does not have scratches that reach the substrate and does not peel off more than 0.5 mm square. No. 3 does not have scratches that reach the substrate, and there is no peeling of 1 mm square or more. 2 has no scratches that reach the base,
No peeling of 2 mm square or more. 1 is other than the above,
Scratches or significant peeling that reaches the substrate.

【００３８】[0038]

【発明の効果】本発明の塗料組成物に寄れば、最近社会
問題化している酸性雨による表面劣化や、洗車時のすり
傷対策を目的に開発されている上塗り塗膜に対して付着
不良を起こすことなく、耐チッピング性に優れた塗膜を
得ることができるので、上塗り２液型耐チッピング塗料
組成物として好適である。EFFECTS OF THE INVENTION According to the coating composition of the present invention, the surface deterioration due to acid rain, which has become a social problem lately, and the poor adhesion to the top coating film, which has been developed for the purpose of preventing scratches during car washing, can be performed. Since a coating film having excellent chipping resistance can be obtained without causing this, it is suitable as a topcoat two-pack type chipping resistant coating composition.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 広田 哲也 兵庫県尼崎市南塚口町６丁目10番73号 神 東塗料株式会社内 (72)発明者 丸岡 宏彰 兵庫県尼崎市南塚口町６丁目10番73号 神 東塗料株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Tetsuya Hirota 6-1073 Minamitsukaguchi-cho, Amagasaki City, Hyogo Prefecture Shinto Paint Co., Ltd. (72) Inventor Hiroaki Maruoka 6-10 Minamitsukaguchi-cho, Amagasaki City, Hyogo Prefecture No. 73 Shinto Paint Co., Ltd.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 ポリオール樹脂（Ａ）１００重量部、タ
ルク５〜１００重量部からなる主剤に、ビウレット変性
ヘキサメチレンジイソシアネート樹脂（Ｂ）からなる硬
化剤を、ポリオール樹脂（Ａ）中のヒドロキシル基に対
するビウレット変性ヘキサメチレンジイソシアネート樹
脂（Ｂ）の有効イソシアネート基を当量比で３００：１
００〜１５０：１００の割合で混合し、かつ混合塗料固
形分あたりの顔料重量％濃度を６０〜７０に配合してな
ることを特徴とする上塗り２液型耐チッピング塗料組成
物。1. A base material consisting of 100 parts by weight of a polyol resin (A) and 5 to 100 parts by weight of talc, a curing agent consisting of a biuret-modified hexamethylene diisocyanate resin (B) and a hydroxyl group in the polyol resin (A). The effective isocyanate group of the biuret-modified hexamethylene diisocyanate resin (B) is 300: 1 in an equivalent ratio.
A topcoat two-pack type chipping resistant coating composition, characterized in that it is mixed at a ratio of 0 to 150: 100, and the pigment weight% concentration per mixed coating solid content is blended to 60 to 70.