JPH06167902A - Cleaning web for fixing roll and cleaning device as well as cleaning method for fixing roll - Google Patents
Cleaning web for fixing roll and cleaning device as well as cleaning method for fixing rollInfo
- Publication number
- JPH06167902A JPH06167902A JP4343404A JP34340492A JPH06167902A JP H06167902 A JPH06167902 A JP H06167902A JP 4343404 A JP4343404 A JP 4343404A JP 34340492 A JP34340492 A JP 34340492A JP H06167902 A JPH06167902 A JP H06167902A
- Authority
- JP
- Japan
- Prior art keywords
- web
- fixing roll
- oil
- cleaning
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、電子写真複写機などの
定着ロール表面に残留したトナーの除去、及びオイルの
塗布を行なう定着ロール用クリーニングウエブ、並びに
そのウエブを含んでなるクリーニング装置、更には、そ
のウエブを用いる定着ロールのクリーニング方法に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fixing roll cleaning web for removing the toner remaining on the surface of the fixing roll of an electrophotographic copying machine and applying oil, and a cleaning device including the web. Relates to a method for cleaning a fixing roll using the web.
【０００２】[0002]
【従来の技術】従来から、電子写真複写機などに含まれ
る定着装置において、定着ロール表面に残留したトナー
を除去するクリーニングウエブとして、芳香族ポリアミ
ド樹脂とポリエチレンテレフタレート樹脂とからなる不
織布に、シリコーンオイルなどのオイルを含浸させたウ
エブが知られていた（特開昭５８−１９９３７１号公
報）。しかしながら、このウエブは、定着ロールへのオ
イル塗布量が少なく、しかもクリーニングウエブとして
の寿命が短いという欠点があった。また、特開平３−６
３６８３号公報には、見掛け密度が大きい一方向性パラ
レルウエブと見掛け密度が小さい二方向性クロスウエブ
との積層ウエブからなるクリーニングウエブが記載され
ている。このウエブでは、クロスウエブ側を低密度にし
て、オイルの含浸保持性能を向上させ、そのクロスウエ
ブ側を定着ロールに接触させて、クリーニングウエブと
しての寿命を長期化させることを目指したものである。
しかしながら、この積層ウエブは、２層を構成する繊維
の収縮率の差が大きいので、実際の使用には耐えられな
いものであると共に、後記のとおり、必ずしも十分な効
果が得られるものでもなかった。2. Description of the Related Art Conventionally, in a fixing device included in an electrophotographic copying machine, as a cleaning web for removing the toner remaining on the surface of the fixing roll, a nonwoven fabric made of an aromatic polyamide resin and a polyethylene terephthalate resin has been applied to a silicone oil. A web impregnated with such oils has been known (JP-A-58-199371). However, this web has the drawbacks that the amount of oil applied to the fixing roll is small and that the life of the cleaning web is short. In addition, JP-A-3-6
Japanese Patent No. 3683 discloses a cleaning web including a laminated web of a unidirectional parallel web having a large apparent density and a bidirectional cross web having a small apparent density. With this web, the cross web side is made to have a low density to improve the impregnation and holding performance of oil, and the cross web side is brought into contact with a fixing roll to prolong the life of the cleaning web. .
However, since this laminated web has a large difference in shrinkage between the fibers constituting the two layers, it cannot withstand actual use, and as described later, it is not always possible to obtain a sufficient effect. .
【０００３】[0003]
【発明が解決しようとする課題】すなわち、本発明者
は、意外にも、この特開平３−６３６８３号公報に記載
されている態様とは逆に、むしろ密度の高いウエブ層を
定着ロールに接触させる方が有効であることを見出し
た。そこで、本発明者は、更にこの点について研究を重
ねた結果、クリーニング効果は、ウエブによるオイルの
保持能力に依存するよりも、ウエブから定着ロールへの
オイル移行性に大きく依存することを見出した。すなわ
ち、オイル移行性の高い表面を定着ロールと接触させる
とクリーニング効率が向上する。そして、例えば、密度
差が存在する場合には高密度側のオイル移行性の方が、
低密度側のオイル移行性よりも高いことを見出した。こ
の結果は、前記特開平３−６３６８３号公報の開示内容
から見れば、予想外の驚くべきものである。従って、本
発明の目的は、高オイル移行性表面を有するクリーニン
グウエブを提供することにある。That is, contrary to the embodiment described in Japanese Patent Laid-Open No. 3-63683, the present inventor has surprisingly contacted the fixing roll with a rather dense web layer. It was found that it is more effective to let them do. Therefore, as a result of further research on this point, the present inventor has found that the cleaning effect depends more on the oil transferability from the web to the fixing roll than on the oil holding capacity of the web. . That is, the cleaning efficiency is improved by bringing the surface having a high oil migration property into contact with the fixing roll. And, for example, when there is a density difference, the oil migration on the high density side is
It was found to be higher than the oil migration on the low density side. This result is unexpected and surprising in view of the disclosure of Japanese Patent Laid-Open No. 3-63683. Accordingly, it is an object of the present invention to provide a cleaning web having a high oil transfer surface.
【０００４】[0004]
【課題を解決するための手段】本発明は、融点が２００
℃以上の繊維及び／又は非溶融性の繊維を主成分として
なり、繊維の融着及び／又は絡合により結合し、一方の
表面側のオイル移行性がもう一方の表面側のオイル移行
性の２倍以上であることを特徴とする、定着ロール用ク
リーニングウエブに関する。また、本発明は、前記の定
着ロール用クリーニングウエブのオイル移行性の高い表
面側を定着ロールに接触させることを特徴とする、定着
ロールのクリーニング方法にも関する。更に、本発明
は、前記の定着ロール用クリーニングウエブの巻付け用
シャフト、その巻付け用シャフトから引出されたウエブ
を定着ロールへ接触させる押圧ロール、及び定着ロール
と接触した後のウエブの巻取用シャフトを含む定着ロー
ル用クリーニング装置であって、前記のクリーニングウ
エブが、オイル移行性の高い表面側を内側にして巻付け
用シャフトに巻付けられ、オイル移行性の高い表面側を
定着ロールと接触させることを特徴とする、前記の定着
ロール用クリーニング装置にも関する。The present invention has a melting point of 200.
℃ or more fibers and / or non-melting fiber as a main component, the fibers are bonded by fusion and / or entanglement, the oil migration of one surface side of the oil migration of the other surface side It relates to a cleaning web for a fixing roll, which is more than doubled. The present invention also relates to a method for cleaning a fixing roll, wherein the surface of the fixing roll cleaning web having a high oil migration property is brought into contact with the fixing roll. Furthermore, the present invention relates to a shaft for winding the cleaning web for the fixing roll, a pressing roll for bringing the web drawn from the winding shaft into contact with the fixing roll, and a winding of the web after contact with the fixing roll. A cleaning device for a fixing roll including a shaft for use, wherein the cleaning web is wound around a winding shaft with the surface side having a high oil migration property facing inward, and the surface side having a high oil migration property serves as a fixing roll. The present invention also relates to the above-mentioned fixing roll cleaning device, which is brought into contact.
【０００５】本発明のウエブは、融点が２００℃以上の
繊維及び／又は非溶融性の繊維（以下、両者を総称して
耐熱性繊維と称することがある）を主成分とする。ここ
で主成分とするとは、耐熱性繊維が、ウエブ全体の５０
重量％を越えることを意味する。本発明で用いることの
できる耐熱性繊維としては、オルト、メタ若しくはパラ
系の芳香族ポリアミド繊維、ポリフェニレンサルファイ
ド繊維、ポリエステル繊維、又はポリアミド繊維などを
挙げることができる。これらの耐熱性繊維の繊度や繊維
長も特に限定されるものではないが、繊度が０．１〜５
デニール（ｄ）で、繊維長が５〜１５０ｍｍの繊維を用
いるのが好ましい。The web of the present invention contains fibers having a melting point of 200 ° C. or higher and / or non-melting fibers (hereinafter, both may be collectively referred to as heat resistant fibers) as a main component. Here, the main component means that the heat-resistant fiber is 50% of the whole web.
Means more than weight percent. Examples of heat resistant fibers that can be used in the present invention include ortho-, meta- or para-based aromatic polyamide fibers, polyphenylene sulfide fibers, polyester fibers, and polyamide fibers. Although the fineness and fiber length of these heat resistant fibers are not particularly limited, the fineness is 0.1 to 5
It is preferable to use fibers having a denier (d) and a fiber length of 5 to 150 mm.
【０００６】前記の耐熱性繊維として融点が２００℃以
上の繊維（以下、熱融着性繊維と称することがある）を
加えて融着固定し、ウエブの強度を向上させることがで
きる。この熱融着性繊維としては、例えば、未延伸ポリ
エステル繊維や未延伸ポリフェニレンサルファイド繊維
を挙げることができる。これらの熱融着性繊維が加熱及
び加圧されると、繊維を構成する分子が再配列して、結
晶化し、耐熱性も向上する。これらの熱融着性繊維の繊
度や繊維長も特に限定されるものではないが、繊度が１
〜２０デニール（ｄ）で、繊維長が５〜１５０ｍｍの繊
維を用いるのが好ましい。熱融着性繊維を混合させて、
融着固定する場合は、ウエブ全体の約３０重量％〜７０
重量％の量で用いる。熱融着性繊維の混合量が約３０重
量％よりも少ないと、ウエブの強度が低くなり、使用中
に破断することがある。また、約７０重量％よりも多い
と耐熱性が悪くなり、溶断することがある。As the heat resistant fiber, a fiber having a melting point of 200 ° C. or higher (hereinafter, also referred to as a heat fusible fiber) may be added and fused and fixed to improve the strength of the web. Examples of the heat-fusible fiber include unstretched polyester fiber and unstretched polyphenylene sulfide fiber. When these heat-fusible fibers are heated and pressed, molecules constituting the fibers are rearranged and crystallized, and heat resistance is also improved. Although the fineness and fiber length of these heat-fusible fibers are not particularly limited, the fineness is 1
It is preferable to use fibers having a fiber length of 5 to 150 mm with a denier (d) of -20. Mix heat-fusible fibers,
In the case of fusion fixing, about 30% by weight to 70% by weight of the whole web
Used in an amount of% by weight. When the amount of the heat-fusible fiber mixed is less than about 30% by weight, the strength of the web becomes low and the web may break during use. On the other hand, if the amount is more than about 70% by weight, the heat resistance is deteriorated and the material may be fused.
【０００７】本発明のウエブは、水流などの流体流やニ
ードルパンチによる絡合によって結合したものでもよ
い。この場合には、熱融着性繊維を混合する必要はな
い。The web of the present invention may be joined by fluid flow such as water flow or entanglement by needle punching. In this case, it is not necessary to mix the heat fusible fibers.
【０００８】本発明のウエブは、２つの各表面側におい
て、一方の表面側のオイル移行性が他方の表面側のオイ
ル移行性の２倍以上、好ましくは３倍以上になる構成を
有する。ここでオイル移行性とは、ウエブと定着ロール
とが接触した際に、ウエブに含浸されているオイルが、
ウエブから定着ロールに移行する性質を言い、以下の方
法によって測定する。すなわち、Ａ４サイズのクリーニ
ングウエブに粘度５，０００ＣＳのシリコーンオイル
（汎用の離型剤）を含浸させる。このクリーニングウエ
ブの上下に、重量を予め測定しておいたＢ４サイズのコ
ピー用紙を５枚ずつ積層した後、温度１５０℃にて、１
０ｇ／ｃｍ2 の荷重で１分間放置する。その後、上下５
枚ずつのコピー用紙の重量を測定し、その重量増加分を
移行オイル量とする。なお、後記実施例においてもこの
方法によってオイル移行性を測定した。The web of the present invention has a structure in which, on each of the two surface sides, the oil transferability on one surface side is twice or more, and preferably three times or more, the oil transferability on the other surface side. Here, the oil transferability means that the oil impregnated in the web when the web comes into contact with the fixing roll is
It refers to the property of shifting from the web to the fixing roll and is measured by the following method. That is, a A4 size cleaning web is impregnated with silicone oil having a viscosity of 5,000 CS (general-purpose release agent). Five sheets of B4 size copy paper, the weight of which has been measured in advance, are laminated on the upper and lower sides of the cleaning web, and the temperature is 150 ° C.
Leave for 1 minute under a load of 0 g / cm 2 . Then up and down 5
The weight of each copy sheet is measured, and the weight increase is taken as the amount of transferred oil. In addition, the oil migration property was measured by this method also in Examples described later.
【０００９】クリーニングウエブは、定着ロールとの接
触時に、定着ロール側にオイルを移行させると共に、定
着ロール側からトナーを受け取る。こうして、定着ロー
ルは清浄化されると共に、オイルを供給される。本発明
のウエブの２表面におけるオイル移行性の差が２倍未満
であると、本発明の効果が十分に得られない。The cleaning web transfers the oil to the fixing roll side and receives the toner from the fixing roll side at the time of contact with the fixing roll. Thus, the fixing roll is cleaned and oil is supplied. If the difference in oil migration between the two surfaces of the web of the present invention is less than twice, the effect of the present invention cannot be sufficiently obtained.
【００１０】本発明のウエブにおいては、高オイル移行
性の表面を、各種の方法によって設けることができる。
例えば、２表面をそれぞれ粗構造と密構造とにし、密構
造側を高オイル移行性の表面とすることができる。ま
た、密構造側のオイル保持性も高くなる。粗密構造を有
するウエブを形成するには、例えば、低密度ウエブと高
密度ウエブとを重ね合わせて２層ウエブとし、これを適
当な方法で絡合及び／又は融着して結合させればよい。
また、不均一な繊維構成からなるウエブに、均一又は不
均一な処理を施すことにより、或いは、均一な繊維構成
からなるウエブに、不均一な処理を施すことにより、粗
密構造を有する本発明のウエブを形成することもでき
る。従って、本発明のウエブとしては、高オイル移行性
を有する一方の表面層から低オイル移行性を有するもう
一方の表面層まで、連続的にオイル移行性が変化する構
造のもの、高オイル移行性を有する一方の表面層と低オ
イル移行性を有するもう一方の表面層との不連続な２層
（場合により更に中間層）からなる構造のもの、などの
態様がある。In the web of the present invention, the high oil migration surface can be provided by various methods.
For example, the two surfaces can be made to have a rough structure and a dense structure, and the dense structure side can be made to have a high oil migration surface. Further, the oil retaining property on the dense structure side is also enhanced. To form a web having a coarse-dense structure, for example, a low-density web and a high-density web may be superposed on each other to form a two-layer web, and the two-layer web may be entangled and / or fused by an appropriate method to be bonded. .
Further, a web having a non-uniform fiber structure is subjected to a uniform or non-uniform treatment, or a web having a uniform fiber structure is subjected to a non-uniform treatment to obtain a coarse-dense structure of the present invention. A web can also be formed. Therefore, the web of the present invention has a structure in which the oil migration property is continuously changed from one surface layer having a high oil migration property to the other surface layer having a low oil migration property, and a high oil migration property. There is an embodiment such as one having a structure comprising two discontinuous layers (one intermediate layer in some cases) of one surface layer having a low oil migration property and the other surface layer having a low oil migration property.
【００１１】本発明のウエブは、例えば、各表面の平滑
性に差を設けることによってオイル移行性の異なる表面
を形成することができる。すなわち、表面の平滑性が高
くなると、定着ロールとの接触面積が広くなるので、オ
イル移行性が高くなる。表面に平滑性を付与するには、
カレンダー処理、バインダーによるコーティングなどの
方法がある。The web of the present invention can form surfaces having different oil migration properties by providing a difference in smoothness of each surface. That is, as the surface smoothness increases, the contact area with the fixing roll increases, so that the oil transferability increases. To give the surface smoothness,
There are methods such as calendering and coating with a binder.
【００１２】更に、例えば、ウエブの片面側を細い繊維
から構成すると、密度が高くなり、しかも平滑性も高く
なるので、オイル移行性が高くなる。換言すれば、細い
繊維を使用すると、毛細管現象により、よりオイルを保
持し易くなり、しかも繊維表面積が広いので、オイルの
移行性も向上する。この場合、例えば、密構造面は、
０．１〜１．５（ｄ）の繊維を用い、粗構造面は、１．
５〜５（ｄ）の繊維を用いる。Further, for example, if one side of the web is made of fine fibers, the density is increased and the smoothness is also increased, so that the oil migration is increased. In other words, when thin fibers are used, it becomes easier to retain oil due to the capillary phenomenon, and moreover, since the fiber surface area is large, oil migration is also improved. In this case, for example, the dense structure surface is
Using 0.1 to 1.5 (d) fibers, the rough structure surface is 1.
Fibers of 5-5 (d) are used.
【００１３】また、ウエブの片面側の構成繊維において
熱融着性繊維量を多くし、熱融着性繊維を融着させる
と、熱融着性繊維の多い側は緻密で平滑になるため、緻
密な側が高オイル移行性になり、オイル保持性も向上す
る。この場合、例えば、密構造面では、熱融着性繊維７
０〜９０重量％とし、粗構造面は、熱融着性繊維３０〜
６０重量％とする。When the amount of the heat-fusible fibers is increased in the constituent fibers on one side of the web and the heat-fusible fibers are fused, the side having the most heat-fusible fibers becomes dense and smooth. The dense side has high oil transferability, and oil retention is also improved. In this case, for example, on the dense structure side, the heat-fusible fiber 7
0 to 90% by weight, and the rough structure surface is 30 to 30
60% by weight.
【００１４】カレンダー処理を行う際に、上下のカレン
ダーロールに温度差を設けると、クリーニングウエブの
一方（高温側）の表面は緻密になり、平滑になるのに対
して、他方の表面（低温側）は粗いため、緻密な側が高
オイル移行性になり、オイル保持性も向上する。この場
合、上下のカレンダーロールの温度差は１０℃以上、よ
り好ましくは２０℃以上とする。When a temperature difference is provided between the upper and lower calender rolls during calendering, one surface (high temperature side) of the cleaning web becomes dense and smooth, while the other surface (low temperature side). Since () is coarse, the dense side has a high oil migration property and the oil retention property is also improved. In this case, the temperature difference between the upper and lower calender rolls is 10 ° C. or higher, and more preferably 20 ° C. or higher.
【００１５】ウエブの片面にエンボス加工を施すと、融
着されていない部分は嵩高で粗いので、全体として、粗
な表面と密な表面を形成し、その両面のオイル保持性に
差異が生じ、オイル移行性にも差異が生じる。また、片
側に多孔質繊維、異形断面繊維、粉体を付着させた繊維
などを使用すると、オイルと接触できる表面積が広く、
オイルを保持し易いので、これら繊維を有する面はオイ
ル保持性が高くなり、これらの繊維を有さない面とで、
オイル移行性に差異が生じる。When embossing is applied to one side of the web, the unfused portion is bulky and rough, so that a rough surface and a dense surface are formed as a whole, and a difference occurs in oil retention on both sides. Differences also occur in oil migration. Also, if you use porous fiber, modified cross-section fiber, fiber with powder attached on one side, the surface area that can contact oil is large,
Since it is easy to retain oil, the surface having these fibers has high oil retention, and the surface not having these fibers,
Differences occur in oil migration.
【００１６】前記の方法によって調製されたウエブに、
オイルを常法により含浸させることによって本発明のク
リーニングウエブを調製することができる。本発明のク
リーニングウエブを巻付け用シャフトへ巻き付ける場合
には、オイル移行性の高い面を内側にするのが好まし
い。また、図１に示すように、こうしてクリーニングウ
エブ１をシャフトに巻き付けたウエブロール２から、ウ
エブを引き出す場合には、オイル移行性の高い面Ａが下
方を向くようにするのが好ましい。なぜなら、ウエブ１
の引出口部分にはオイルの漏出部３が形成され、このオ
イルが、オイル保持性の高い面Ａに吸着され、定着ロー
ルへ運ばれるからである。The web prepared by the above method,
The cleaning web of the present invention can be prepared by impregnating oil with a conventional method. When the cleaning web of the present invention is wound around the winding shaft, it is preferable that the surface having a high oil transfer property is placed inside. Further, as shown in FIG. 1, when the web is pulled out from the web roll 2 in which the cleaning web 1 is wound around the shaft in this way, it is preferable that the surface A having a high oil migration property faces downward. Because web 1
This is because an oil leakage portion 3 is formed at the outlet of the oil, and this oil is adsorbed on the surface A having a high oil retaining property and is conveyed to the fixing roll.
【００１７】続いて、図２に示すように、ウエブロール
２から引き出されたクリーニングウエブ１は、押圧ロー
ル４と定着ロール５との間に移送され、ウエブ１の高オ
イル移行性面が定着ロール５と接触する。一方、定着ロ
ール５は、コピー紙６上のトナー７を加圧ロール８と一
緒に加熱・加圧して定着する際に、トナーで汚染される
ので、クリーニングウエブ１と接触した際に、トナーは
定着ロール５からウエブ１へ、オイルはウエブ１から定
着ロール５へ移動し、トナーとオイルとの交換が起こ
る。洗浄に用いたウエブ１は、巻取用シャフト９に巻き
取られる。Subsequently, as shown in FIG. 2, the cleaning web 1 pulled out from the web roll 2 is transferred between the pressing roll 4 and the fixing roll 5, and the high oil migration surface of the web 1 is fixed to the fixing roll. Contact 5. On the other hand, the fixing roll 5 is contaminated with the toner when the toner 7 on the copy paper 6 is heated and pressed together with the pressure roll 8 to fix the toner. The oil moves from the fixing roll 5 to the web 1, and the oil moves from the web 1 to the fixing roll 5, so that the toner and the oil are exchanged. The web 1 used for cleaning is wound around the winding shaft 9.
【００１８】本発明方法では、前記クリーニングウエブ
の高オイル移行性面を、定着ロールに接触させるので、
定着ロールに多量のオイルを塗布することができる。従
って、クリーニングウエブ単位長当たりのオイル塗布量
が多くなり、クリーニングウエブ全体の寿命が長くな
り、或いは、高速複写機に用いることができる。In the method of the present invention, since the high oil migration surface of the cleaning web is brought into contact with the fixing roll,
A large amount of oil can be applied to the fixing roll. Therefore, the amount of oil applied per unit length of the cleaning web is increased, the life of the entire cleaning web is extended, or it can be used in a high speed copying machine.
【００１９】本発明によるクリーニング装置は、図２に
示すとおり、定着ロール用クリーニングウエブの巻付け
用シャフト１０、その巻付け用シャフト１０から引き出
されたウエブ１を定着ロール５へ接触させる押圧ロール
４、及び定着ロール５と接触した後のウエブ１の巻取用
シャフト９を含み、前記のクリーニングウエブ１が、オ
イル移行性の高い表面側を内側にして巻付け用シャフト
１０に巻付けられ、オイル移行性の高い表面側を定着ロ
ール５と接触させる。本発明装置に用いるクリーニング
ウエブは、単位長当たりのオイル塗布量が多くなるの
で、複写機内部の限定されたウエブ収容部に挿入される
ウエブ１本の寿命を長くすることになる。As shown in FIG. 2, the cleaning device according to the present invention comprises a shaft 10 for winding a cleaning web for a fixing roll, and a pressing roll 4 for bringing the web 1 pulled out from the winding shaft 10 into contact with the fixing roll 5. , And the winding shaft 9 of the web 1 after contact with the fixing roll 5, the cleaning web 1 is wound around the winding shaft 10 with the surface side having high oil transferability inside. The surface side having high transferability is brought into contact with the fixing roll 5. Since the amount of oil applied per unit length of the cleaning web used in the apparatus of the present invention is large, the life of one web inserted into the limited web storage portion inside the copying machine is extended.
【００２０】[0020]
【実施例】以下、実施例によって本発明を具体的に説明
するが、これらは本発明の範囲を限定するものではな
い。なお、％は重量％を示す。実施例１ 第１繊維ウエブとして、メタ系芳香族ポリアミド繊維
（２ｄ×３８ｍｍ）１００％からなり、目付が４０ｇ／
ｍ2 の繊維ウエブを用いた。また、第２繊維ウエブとし
て、メタ系芳香族ポリアミド繊維（１ｄ×３８ｍｍ）６
０％と、ポリエステル成分をポリアミド成分により接合
した断面形状が菊花型の複合繊維〔２ｄ×３８ｍｍ；カ
ネボウ（株）、ベリーマＸ〕４０％とからなり、目付が
２０ｇ／ｍ2 の混合繊維ウエブを用いた。前記の第１繊
維ウエブと第２繊維ウエブとを重ね合わせ、水圧９０ｋ
ｇ／ｃｍ2 で絡合処理した。得られた絡合体を、第２繊
維ウエブ側が１９０℃のスチールロール、第１繊維ウエ
ブ側がコットンロールのカレンダーで処理することによ
り、厚さ０．１５ｍｍのクリーニングウエブを得た。こ
のクリーニングウエブに対して、粘度５，０００ＣＳの
シリコーンオイルを１２０ｇ／ｍ2 の量で含浸させた。
このクリーニングウエブの平滑面側である第２繊維ウエ
ブ側を上にして、オイル移行性を前記の方法によって測
定したところ、下方の第１繊維ウエブ側で７．３ｇ／ｍ
2 であるのに対し、上方の第２繊維ウエブ側では５５．
４ｇ／ｍ2 になり、約７．６倍の差があった。The present invention will be described in detail below with reference to examples, but these do not limit the scope of the present invention. In addition,% shows weight%. Example 1 The first fiber web was composed of 100% meta-aromatic polyamide fiber (2d × 38 mm) and had a basis weight of 40 g /
A m 2 fiber web was used. Further, as the second fiber web, meta-aromatic polyamide fiber (1d × 38 mm) 6
A mixed fiber web consisting of 0% and 40% of a Kikubana-shaped composite fiber [2d × 38 mm; Kanebo Ltd., Berryma X] having a cross-sectional shape in which a polyester component is bonded with a polyamide component, and a basis weight is 20 g / m 2. Using. The first fiber web and the second fiber web are superposed on each other, and the water pressure is 90 k.
Entanglement treatment was performed at g / cm 2 . The entangled body thus obtained was treated with a calender of a steel roll having a second fiber web side of 190 ° C. and a cotton roll of a first fiber web side to obtain a cleaning web having a thickness of 0.15 mm. This cleaning web was impregnated with silicone oil having a viscosity of 5,000 CS in an amount of 120 g / m 2 .
When the oil migration was measured by the above method with the second fiber web side, which is the smooth surface side, of this cleaning web facing upward, it was found to be 7.3 g / m 2 on the lower first fiber web side.
2 while the upper second fiber web side is 55.
It was 4 g / m 2 , which was a difference of about 7.6 times.
【００２１】実施例２ 実施例１の水流絡合処理と同様にして得られた不織布
を、熱カレンダー処理にかけずに、エンボス機により処
理した。すなわち、第１繊維ウエブ側をエンボスロール
（１８０℃）に、そして第２繊維ウエブ側をスムースロ
ール（２１０℃）と接触させた。こうして得られたクリ
ーニングウエブの厚さ（つぶれていない部分の厚さ）は
０．３５ｍｍであった。このクリーニングウエブに対し
て、粘度５，０００ＣＳのシリコーンオイルを２５０ｇ
／ｍ2 の量で含浸させた。このクリーニングウエブの平
滑面側である第２繊維ウエブ側を上にして、オイル移行
性を前記の方法によって測定したところ、下方の第１繊
維ウエブ側で７．６ｇ／ｍ2 であるのに対し、上方の第
２繊維ウエブ側では８１．０ｇ／ｍ2 になり、約１０．
１倍の差があった。 Example 2 The non-woven fabric obtained in the same manner as the hydroentangling treatment of Example 1 was treated by an embossing machine without being subjected to a heat calendar treatment. That is, the first fiber web side was brought into contact with an embossing roll (180 ° C) and the second fiber web side was brought into contact with a smooth roll (210 ° C). The thickness of the cleaning web thus obtained (the thickness of the portion that was not crushed) was 0.35 mm. 250 g of silicone oil with a viscosity of 5,000 CS was added to this cleaning web.
Impregnated in an amount of / m 2 . The oil migration was measured by the above method with the second fiber web side, which is the smooth surface side, of this cleaning web facing up, whereas it was 7.6 g / m 2 on the lower first fiber web side. , The upper second fiber web side was 81.0 g / m 2 , and was about 10.
There was a one-fold difference.
【００２２】比較例１ 実施例１の水流絡合処理と同様にして得られた不織布を
そのままクリーニングウエブとした。このクリーニング
ウエブの厚さは０．５０ｍｍであった。このクリーニン
グウエブに対して、粘度５，０００ＣＳのシリコーンオ
イルを３２０ｇ／ｍ2 の量で含浸させた。このクリーニ
ングウエブの平滑面側である第２繊維ウエブ側を上にし
て、オイル移行性を前記の方法によって測定したとこ
ろ、下方の第１繊維ウエブ側で４６．２ｇ／ｍ2 である
のに対し、上方の第２繊維ウエブ側では３７．７ｇ／ｍ
2 になり、約０．８倍の差があった。 Comparative Example 1 The nonwoven fabric obtained in the same manner as the hydroentangling treatment of Example 1 was used as it was as a cleaning web. The thickness of this cleaning web was 0.50 mm. This cleaning web was impregnated with silicone oil having a viscosity of 5,000 CS in an amount of 320 g / m 2 . The oil migration was measured by the above method with the second fiber web side, which is the smooth surface side, of this cleaning web facing up, and was 46.2 g / m 2 on the lower first fiber web side. , 37.7 g / m on the upper second fiber web side
It was 2, which was about 0.8 times the difference.
【００２３】実施例３ 第１繊維ウエブとして、メタ系芳香族ポリアミド繊維
（２ｄ×３８ｍｍ）７０％と、未延伸ポリエステル繊維
（５ｄ×３８ｍｍ）３０％とからなり、目付２５ｇ／ｍ
2 の混合繊維ウエブを用いた。第２繊維ウエブとして、
メタ系芳香族ポリアミド繊維（２ｄ×３８ｍｍ）３０％
と、未延伸ポリエステル繊維（５ｄ×３８ｍｍ）７０％
とからなり、目付２５ｇ／ｍ2 の混合繊維ウエブを用い
た。前記の第１繊維ウエブと第２繊維ウエブとを重ね合
わせ、上下の温度が２１０℃のカレンダーロールで処理
して、厚さ０．０８ｍｍのクリーニングウエブを得た。
このクリーニングウエブに対して、粘度５，０００ＣＳ
のシリコーンオイルを５０ｇ／ｍ2 の量で含浸させた。
このクリーニングウエブの平滑面側である第２繊維ウエ
ブ側を上にして、オイル移行性を前記の方法によって測
定したところ、下方の第１繊維ウエブ側で３．８ｇ／ｍ
2 であるのに対し、上方の第２繊維ウエブ側では１３．
０ｇ／ｍ2 になり、約３．４倍の差があった。 Example 3 The first fibrous web was composed of 70% of meta-aromatic polyamide fiber (2d × 38 mm) and 30% of unstretched polyester fiber (5d × 38 mm), and had a basis weight of 25 g / m 2.
Two mixed fiber webs were used. As the second fiber web,
30% of meta aromatic polyamide fiber (2d × 38mm)
And 70% unstretched polyester fiber (5d x 38mm)
And a mixed fiber web having a basis weight of 25 g / m 2 was used. The first fiber web and the second fiber web were superposed and treated with a calender roll having an upper and lower temperature of 210 ° C. to obtain a cleaning web having a thickness of 0.08 mm.
Viscosity of 5,000 CS for this cleaning web
Of silicone oil was impregnated in an amount of 50 g / m 2 .
When the oil transfer property was measured by the above method with the second fiber web side, which is the smooth surface side, of this cleaning web facing up, 3.8 g / m 2 was measured on the lower first fiber web side.
2 while the upper second fiber web side is 13.
It was 0 g / m 2 and there was a difference of about 3.4 times.
【００２４】比較例２ メタ系芳香族ポリアミド繊維（２ｄ×３８ｍｍ）７０％
と、未延伸ポリエステル繊維（５ｄ×３８ｍｍ）３０％
とからなり、目付５０ｇ／ｍ2 の混合繊維ウエブを、上
下の温度が２１０℃のカレンダーロールで処理して、厚
さ０．１ｍｍのクリーニングウエブを得た。このクリー
ニングウエブに対して、粘度５，０００ＣＳのシリコー
ンオイルを５０ｇ／ｍ2 の量で含浸させた。このクリー
ニングウエブのオイル移行性を前記の方法によって測定
したところ、上方ウエブ側が５．２ｇ／ｍ2 で、下方ウ
エブ側が７．６ｇ／ｍ2 であり、反転させてオイル移行
性を調べると、上方ウエブ側が５．１ｇ／ｍ2 で、下方
ウエブ側が７．２ｇ／ｍ2 であった。 Comparative Example 2 70% of a meta-aromatic polyamide fiber (2d × 38 mm)
And unstretched polyester fiber (5d x 38mm) 30%
The mixed fiber web having a basis weight of 50 g / m 2 was treated with a calendar roll having an upper and lower temperature of 210 ° C. to obtain a cleaning web having a thickness of 0.1 mm. The cleaning web was impregnated with silicone oil having a viscosity of 5,000 CS in an amount of 50 g / m 2 . When the oil migration of the cleaning web were measured by the methods above web side 5.2 g / m 2, the lower web side is 7.6 g / m 2, when it is inverted examine the oil migration, the upper The web side was 5.1 g / m 2 and the lower web side was 7.2 g / m 2 .
【００２５】実施例４：クリーニング性試験 実施例１〜３及び比較例１〜２で調製した５種のクリー
ニングウエブを（オイル移行性に差がある場合には、そ
れが高い面を内側にして）、中空アルミニウム製シャフ
ト（外径約１０ｍｍ）に巻き付け、シャフトとクリーニ
ングウエブとの合計外径をすべて４０ｍｍとした。これ
は、複写機内のウエブロール収容スペースを同一である
ものとして比較を行うためである。次に、ウエブロール
を複写機に取り付け、ウエブロールからウエブを引出し
て、定着ロールと接触できるまで引出した。この際、ク
リーニングウエブの内、オイル移行性の高い面を、定着
ロールとの接触幅が４ｍｍとなるように押し付けた。ま
た、このウエブは送り出さず、停止した状態で連続コピ
ーを行ない、定着ロールにコピー紙が巻き付くまでのコ
ピー枚数を計数した。このコピー枚数に基づいて、アル
ミニウム製の巻付け用シャフトに巻き付けたクリーニン
グウエブ全体についてコピー可能な枚数を計算した。結
果を表１に示す。 Example 4 Cleaning Property Test Five types of cleaning webs prepared in Examples 1 to 3 and Comparative Examples 1 and 2 were used (when there is a difference in oil migration property, the surface having a higher oil migration is placed inside. ), And was wound around a hollow aluminum shaft (outer diameter of about 10 mm), and the total outer diameter of the shaft and the cleaning web was set to 40 mm. This is for the purpose of comparison, assuming that the web roll storage spaces in the copying machine are the same. Next, the web roll was attached to a copying machine, and the web was pulled out from the web roll until it could come into contact with the fixing roll. At this time, the surface of the cleaning web having a high oil migration property was pressed so that the contact width with the fixing roll was 4 mm. Further, this web was not sent out, continuous copying was performed in a stopped state, and the number of copies until the copy paper was wrapped around the fixing roll was counted. Based on the number of copies, the number of copies possible for the entire cleaning web wound on the aluminum winding shaft was calculated. The results are shown in Table 1.
【００２６】[0026]
【表１】 [Table 1]
【００２７】[0027]
【発明の効果】本発明のクリーニングウエブは、高オイ
ル移行性面を有しているので、定着ロールに対するオイ
ルの移行性に優れ、定着ロールを効率よく洗浄すること
ができる。また、オイル移行性が高いので、ウエブへの
含浸オイル総量を少なくすることもできる。更に、ある
程度の剛性を有しているので、トナーをかき取ることも
できる。Since the cleaning web of the present invention has a high oil migration surface, the oil migration to the fixing roll is excellent, and the fixing roll can be efficiently washed. Further, since the oil transferability is high, the total amount of impregnated oil in the web can be reduced. Further, since it has a certain degree of rigidity, the toner can be scraped off.
【図１】本発明のクリーニングウエブを巻き付けたウエ
ブロール及びそこから引き出されるウエブを模式的に示
す断面図である。FIG. 1 is a cross-sectional view schematically showing a web roll around which a cleaning web of the present invention is wound and a web pulled out from the web roll.
【図２】本発明のクリーニングウエブにより定着ロール
を洗浄する模様を模式的に示す断面図である。FIG. 2 is a cross-sectional view schematically showing a pattern of cleaning a fixing roll with a cleaning web of the present invention.
１・・クリーニングウエブ ２・・ウエブロール ４・・押圧ロール ５・・定着ロール ９・・巻取シャフト 1 ・ ・ Cleaning web 2 ・ ・ Web roll 4 ・ ・ Pressing roll 5 ・ ・ Fixing roll 9 ・ ・ Winding shaft
Claims (3)
溶融性の繊維を主成分としてなり、繊維の融着及び／又
は絡合により結合し、一方の表面側のオイル移行性がも
う一方の表面側のオイル移行性の２倍以上であることを
特徴とする、定着ロール用クリーニングウエブ。1. A fiber comprising a fiber having a melting point of 200 ° C. or higher and / or a non-melting fiber as a main component, which are bonded by fusion and / or entanglement of the fibers, and one surface has an oil migration property to the other. The cleaning web for a fixing roll is characterized in that the oil transferability on the surface side thereof is at least twice as high.
グウエブのオイル移行性の高い表面側を定着ロールに接
触させることを特徴とする、定着ロールのクリーニング
方法。2. A method for cleaning a fixing roll, wherein the surface of the fixing roll cleaning web having a high oil migration property is brought into contact with the fixing roll.
グウエブの巻付け用シャフト、その巻付け用シャフトか
ら引出されたウエブを定着ロールへ接触させる押圧ロー
ル、及び定着ロールと接触した後のウエブの巻取用シャ
フトを含む定着ロール用クリーニング装置であって、前
記のクリーニングウエブが、オイル移行性の高い表面側
を内側にして巻付け用シャフトに巻付けられ、オイル移
行性の高い表面側を定着ロールと接触させることを特徴
とする、前記の定着ロール用クリーニング装置。3. A shaft for winding the cleaning web for a fixing roll according to claim 1, a pressing roll for bringing a web drawn from the winding shaft into contact with the fixing roll, and a web after contacting the fixing roll. A cleaning device for a fixing roll including a winding shaft, wherein the cleaning web is wound around a winding shaft with the surface side having a high oil migration property facing inward to fix the surface side having a high oil migration property. The fixing roll cleaning device described above, which is brought into contact with a roll.