JPH059818A - Metallic traveler for spinning frame - Google Patents
Metallic traveler for spinning frameInfo
- Publication number
- JPH059818A JPH059818A JP16839491A JP16839491A JPH059818A JP H059818 A JPH059818 A JP H059818A JP 16839491 A JP16839491 A JP 16839491A JP 16839491 A JP16839491 A JP 16839491A JP H059818 A JPH059818 A JP H059818A
- Authority
- JP
- Japan
- Prior art keywords
- traveler
- yarn
- circle
- hardness
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、精紡機，撚糸機等に用
いるトラベラの糸通過部の耐摩耗，耐久性を向上せしめ
た紡機用金属トラベラに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a metal traveler for a spinning machine, which has improved wear resistance and durability of a yarn passing portion of a traveler used in a spinning machine, a twisting machine and the like.
【０００２】[0002]
【従来の技術】従来、紡機用金属トラベラにおいては、
糸が糸通過部を高速で通過する運転条件或は、糸に特殊
な添加剤を含む運転条件の下では糸通過部の耐摩耗性が
要求される。従ってこの耐摩耗性を向上させるために、
糸通過部の表面に硬化処理としてクロムめっきや、梨地
クロムめっきを施したトラベラが使用されている。2. Description of the Related Art Conventionally, in metal travelers for spinning machines,
Abrasion resistance of the yarn passing portion is required under operating conditions in which the yarn passes through the yarn passing portion at a high speed or under operating conditions in which the yarn contains a special additive. Therefore, in order to improve this wear resistance,
A chrome-plated or satin chrome-plated traveler is used as a hardening treatment on the surface of the thread passing portion.
【０００３】然るに、従来のクロムめっきや梨地クロム
めっきの硬さはＨｖ１０００〜１２００程度であり、操
業条件の高速化及び紡出する糸の特殊化により、従来ト
ラベラでは糸通過部の摩耗が早期に発生し、糸質の低
下、糸毛羽や糸切れを引起こして安定な紡調が得られ
ず、短寿命となり、トラベラ交換の手間が増大するとい
う問題点がある。However, the hardness of conventional chrome plating and satin chrome plating is about Hv 1000 to 1200, and due to the speeding up of operating conditions and the specialization of the spun yarn, the conventional traveler will experience early wear of the yarn passing portion. However, there is a problem in that the yarn quality is deteriorated, the yarn is fluffed or broken, and stable spinning cannot be obtained, the life is shortened, and the trouble of exchanging the traveler is increased.
【０００４】また、上記と同様にリングとの接触部分の
摩擦も過酷となり、これに伴って母材の耐摩耗性もより
高いものが要求されている。Further, similar to the above, the friction at the contact portion with the ring becomes severe, and accordingly, the base material is required to have higher wear resistance.
【０００５】[0005]
【発明が解決しようとする課題】本発明は上記従来技術
の問題点に鑑みて、操業条件の高速化及び紡出する糸の
特殊化に対応して、金属トラベラの糸通過部の耐摩耗性
を著しく向上すると共に、母材金属の耐摩耗性をも向上
せんとしたものである。SUMMARY OF THE INVENTION In view of the above problems of the prior art, the present invention responds to speeding up of operating conditions and specialization of spun yarns, and wear resistance of the yarn passage portion of a metal traveler. And the wear resistance of the base metal is also improved.
【０００６】[0006]
【課題を解決するための手段】本発明の紡機用金属トラ
ベラは、母材金属をＣ：0.７〜0.９％、Ｃr ：3.５〜4.
５％、Ｗ：１０〜２２％、Ｖ：0.８〜2.３％等の元素を
含む高速度鋼線材を用いて所定のトラベラサークルを形
成し、少なくとも糸と接触する糸通過部に、炭素を２〜
４％含むクロムめっき層を設け、熱処理を施して母材金
属の硬さがＨｖ７００以上でかつ、クロムめっき層の硬
さをＨｖ１５００以上とした紡機用金属トラベラを得る
ことによる。In the metal traveler for a spinning machine of the present invention, the base metal is C: 0.7 to 0.9%, Cr: 3.5 to 4.
5%, W: 10-22%, V: 0.8-2.3%, and the like, a predetermined traveler circle is formed using a high-speed steel wire rod, and at least in the yarn passing portion that comes into contact with the yarn, 2 to 2 carbons
By providing a chromium plating layer containing 4%, heat treatment is performed to obtain a metal traveler for a spinning machine in which the hardness of the base metal is Hv 700 or more and the hardness of the chromium plating layer is Hv 1500 or more.
【０００７】[0007]
【実施例】以下、本発明の一実施例を詳細に説明する。EXAMPLES An example of the present invention will be described in detail below.
【０００８】図１は本発明の実施の１例を示す紡機用金
属トラベラの一部破断正面図であり、図２は同部分拡大
断面組織図である。図に示す様に高速度鋼線材を用い
て、所要のサークル形状１に成形した縦形トラベラ又は
横形トラベラを形成する。FIG. 1 is a partially cutaway front view of a metal traveler for a spinning machine showing an embodiment of the present invention, and FIG. 2 is a partially enlarged sectional view of the same. As shown in the figure, a high-speed steel wire rod is used to form a vertical traveler or a horizontal traveler formed into a required circle shape 1.
【０００９】上記トラベラは１２９０℃から油焼入処理
した後、研磨を行ない、下記に示すクロム酸−シュウ酸
浴（シュウ酸浴）と電着条件によりクロムめっきを行な
い、図１及び図２に示す如く、高速度鋼母材２の表面に
厚さ３０μの炭素化合物３を含有するクロムめっき層４
を形成する。The above traveler was oil-quenched at 1290 ° C., then polished, and then chromium-plated under the following chromic acid-oxalic acid bath (oxalic acid bath) and electrodeposition conditions. As shown, a chromium plating layer 4 containing a carbon compound 3 having a thickness of 30 μm on the surface of the high speed steel base material 2
To form.
【００１０】上記クロムめっきトラベラは、引続き無酸
化雰囲気中で６００℃で１時間の熱処理を行ない、本発
明の紡機用金属トラベラを形成した。The chromium-plated traveler was subsequently subjected to heat treatment at 600 ° C. for 1 hour in a non-oxidizing atmosphere to form the metal traveler for a spinning machine of the present invention.
【００１１】 めっき条件 浴組成 クロム酸 ２００g/l シュウ酸 ６４０g/l 硫酸アンモニウム ７５g/l 電着条件 電流密度 ２０Ａ／ｄm2 浴温 ６０℃ ＰＨ ２Plating conditions Bath composition Chromic acid 200 g / l Oxalic acid 640 g / l Ammonium sulfate 75 g / l Electrodeposition conditions Current density 20 A / dm 2 Bath temperature 60 ° C. PH 2
【００１２】上記の浴組成でクロムめっきを行なった場
合、めっき上がりでの硬度はＨｖ１０００〜１２００程
度となり、従来のクロムめっき（サージェント浴）との
差がでない。然るにこれを５００〜６５０℃で熱処理を
行う事によりめっき層中の炭素が、クロム炭化物の生成
によりＨｖ１５００以上のめっき硬度が得られるが、従
来のサージェント浴によるクロムめっきでは、Ｈｖ６０
０以下に軟化する。When chrome plating is performed with the above bath composition, the hardness after plating is about Hv1000 to 1200, which is not different from the conventional chrome plating (surgent bath). However, by subjecting this to a heat treatment at 500 to 650 ° C., carbon in the plating layer can obtain a plating hardness of Hv1500 or higher due to the formation of chromium carbide, but in the conventional chromium plating using the Sargent bath, Hv60
Softens to 0 or less.
【００１３】また、通常の硬鋼線材に上記シュウ酸浴組
成でクロムめっきを行なうと、５００〜６５０℃での熱
処理により、めっき層の硬度はＨｖ１５００以上となる
が、母材の硬度は反対にＨｖ５００以下に軟化してしま
い、母材の耐摩耗性が著しく悪くなる。これに対して本
発明では高速度鋼を焼入したあと６００℃で熱処理を行
なう事により、２次硬化を利用して母材の硬度を確保し
たものである。When chromium plating is applied to an ordinary hard steel wire with the above-mentioned oxalic acid bath composition, the hardness of the plating layer becomes Hv 1500 or more by heat treatment at 500 to 650 ° C., but the hardness of the base metal is opposite. It is softened to Hv 500 or less, and the wear resistance of the base material is significantly deteriorated. On the other hand, in the present invention, the hardness of the base material is ensured by utilizing the secondary hardening by quenching the high speed steel and then performing the heat treatment at 600 ° C.
【００１４】上記実施例で得られた金属トラベラのクロ
ムめっき層に含まれる炭素の含有率は3.５％で、熱処理
後のめっき層硬度はＨｖ１８５０、母材の硬度はＨｖ８
３０であった。The content ratio of carbon contained in the chromium plating layer of the metal traveler obtained in the above example is 3.5%, the hardness of the plating layer after heat treatment is Hv1850, and the hardness of the base metal is Hv8.
It was 30.
【００１５】尚、上記クロムめっき層に含まれる炭素の
含有率は２〜４％の範囲にあることが好ましく、２％未
満では熱処理を行なっても所望の硬度が得られず、又、
４％を超えるとめっき層がもろくなり好ましくない。The content of carbon contained in the chromium plating layer is preferably in the range of 2 to 4%, and if it is less than 2%, the desired hardness cannot be obtained even if heat treatment is performed, and
If it exceeds 4%, the plating layer becomes brittle, which is not preferable.
【００１６】上記実施例で得られた本発明の紡機用金属
トラベラ（Ａ）と、従来のサージェント浴硬質クロムめ
っき処理を施した紡機用金属トラベラ（Ｂ）、また、従
来の硬鋼線材で形成した金属トラベラに本発明によるシ
ュウ酸浴クロムめっきを施し、６００℃で熱処理を施し
た比較例とする金属トラベラ（Ｃ）を用いて、以下に示
す紡出条件により紡出テストを実施した。The metal traveler for a spinning machine (A) of the present invention obtained in the above example, the metal traveler for a spinning machine (B) subjected to the conventional Sargent bath hard chrome plating treatment, and the conventional hard steel wire rod. Using the metal traveler (C) as a comparative example, which was subjected to oxalic acid bath chromium plating according to the present invention and heat-treated at 600 ° C., a spinning test was carried out under the spinning conditions shown below.
【００１７】紡出条件 糸 ：ポリエステルフイラメント ４０デニール リング ：縦形焼結リング ＳＴＳｎ １４０mmφ トラベラ：縦形 ＳＳＢ No. ３３ スピンドル回転数：１００００r.p.m.Spinning conditions Thread: Polyester filament 40 denier ring: Vertical sintered ring STSn 140 mmφ Traveler: Vertical SSB No. 33 Spindle speed: 10000 r.p.m.
【００１８】上記紡出テストの結果、従来の紡機用金属
トラベラ（Ｂ）は２〜３時間で糸通過部が摩耗し、白粉
の発生や糸毛羽が多くなり繊維が疵つき紡出が困難とな
ったのに対し、本発明の紡機用金属トラベラ（Ａ）は２
０時間の運転後でも摩耗が発生せず、またリングとの接
触部は、めっきは磨滅しているが母材の硬度が高く、摩
耗は少なくて優れた耐摩耗性を有するものである事が確
認された。As a result of the above spinning test, in the conventional metal traveler (B) for spinning machine, the yarn passing portion was worn in 2 to 3 hours, white powder was generated and yarn fluffs increased, and the fiber was flawed and spinning was difficult. In contrast, the metal traveler for spinning machine (A) of the present invention is 2
Even after 0 hours of operation, no wear occurred, and the contact area with the ring had worn plating, but the base material had a high hardness, and there was little wear and it had excellent wear resistance. confirmed.
【００１９】比較例（Ｃ）は２０時間の運転後でも糸通
過部の摩耗は発生しなかったが、リングとの接触部は母
材硬度が低いため摩耗が多くトラベラの飛散が発生し
た。In Comparative Example (C), wear of the yarn passing portion did not occur even after 20 hours of operation, but since the base material hardness at the contact portion with the ring was low, there was much wear and scattering of the traveler occurred.
【００２０】[0020]
【発明の効果】本発明品は上記の構成としたので、クロ
ムめっき層の硬度がＨｖ１５００以上と高くなり、しか
も母材硬度もＨｖ７００以上と高くすることが出来、糸
通過部分の耐摩耗性が著しく向上し、糸による摩耗も解
消され、糸毛羽や白粉の発生することもない。また、リ
ングとの耐摩耗性も改良される。そのため糸に与えるダ
メージが無くなり、安定した連続運転が長期にわたって
でき、しかも、トラベラ寿命も延長できる等の優れた効
果を有する発明である。Since the product of the present invention has the above-mentioned structure, the hardness of the chromium plating layer can be as high as Hv 1500 or more, and the base material hardness can be also as high as Hv 700 or more, and the abrasion resistance of the thread passing portion can be improved. Remarkably improved, wear due to yarn is eliminated, and no fluff or white powder is generated. Also, the wear resistance with the ring is improved. Therefore, the invention has an excellent effect that damage to the yarn is eliminated, stable continuous operation can be performed for a long time, and the life of the traveler can be extended.
【図１】本発明の紡機用金属トラベラの正面図である。FIG. 1 is a front view of a metal traveler for a spinning machine of the present invention.
【図２】本発明の紡機用金属トラベラの部分拡大断面組
織図である。FIG. 2 is a partially enlarged sectional structure diagram of the metal traveler for a spinning machine of the present invention.
１ サークル形状 ２ 高速度鋼製母材 ３ 炭素化合物 ４ クロムめっき層 1 Circle shape 2 High speed steel base material 3 Carbon compound 4 Chromium plating layer
Claims (1)
５〜4.５％、Ｗ：１０〜２２％、Ｖ：0.８〜2.３％を含
有する高速度鋼線材を用いて所定のトラベラサークルを
形成し、上記サークルの少なくとも糸と接触する糸通過
部に、炭素を２〜４％含有するクロムめっき層を設けて
なり、且つ、母材金属の硬さがＨｖ７００以上で、クロ
ムめっき層の硬さがＨｖ１５００以上であることを特徴
とする紡機用金属トラベラ。Claims: 1. The base metal is C: 0.7 to 0.9%, Cr: 3.
A predetermined traveler circle is formed by using a high-speed steel wire rod containing 5 to 4.5%, W: 10 to 22%, and V: 0.8 to 2.3%, and comes into contact with at least the thread of the circle. A chrome plating layer containing 2 to 4% of carbon is provided in the thread passing portion, the hardness of the base metal is Hv 700 or more, and the hardness of the chrome plating layer is Hv 1500 or more. Metal traveler for spinning machines.