JPH0562820U - Luminous pointer - Google Patents
Luminous pointerInfo
- Publication number
- JPH0562820U JPH0562820U JP341592U JP341592U JPH0562820U JP H0562820 U JPH0562820 U JP H0562820U JP 341592 U JP341592 U JP 341592U JP 341592 U JP341592 U JP 341592U JP H0562820 U JPH0562820 U JP H0562820U
- Authority
- JP
- Japan
- Prior art keywords
- conductive film
- light emitting
- transparent conductive
- electrode
- enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 それ自体が発光して新規かつすぐれた視認効
果を発揮する発光指針を提供する。
【構成】 直径１．５mm以下の線状金属芯材10の表面
に、ホーロー質絶縁反射層２０、ホーロー中に蛍光体を
分散させた蛍光体発光層３０、透明導電膜４０および透
明保護層５０を順次形成すると共に、前記線状金属芯材
１０と前記透明導電膜４０とを電気的に連結した棒状の
無機分散型発光素子からなることを特徴とする発光指
針。透明導電膜４０側の電極は、前記透明導電膜４０よ
りも抵抗率の小さい導体膜を、指針の基部側および／ま
たは長手方向裏側に、少なくとも前記透明導電膜４０と
接するように設けた補助電極から形成する。
(57) [Summary] [Purpose] To provide a luminescent guide that emits light by itself and exhibits a novel and excellent visual effect. [Structure] On a surface of a linear metal core material 10 having a diameter of 1.5 mm or less, an enamel insulating reflection layer 20, a phosphor light emitting layer 30 in which a phosphor is dispersed in a enamel, a transparent conductive film 40 and a transparent protective layer 50 And a wire-shaped inorganic dispersion-type light emitting element in which the linear metal core material 10 and the transparent conductive film 40 are electrically connected to each other. The electrode on the transparent conductive film 40 side is an auxiliary electrode in which a conductive film having a resistivity lower than that of the transparent conductive film 40 is provided on the base side and / or the longitudinal back side of the pointer so as to be in contact with at least the transparent conductive film 40. Formed from.
Description
【０００１】[0001]
この考案は、新規な視認効果を呈する発光指針に関するものであり、さらに詳 しくは無機分散型発光素子からなりそれ自体が発光してすぐれた視認性を発揮す る発光指針に関するものである。 The present invention relates to a light emitting guide that exhibits a novel visual effect, and more specifically to a light emitting guide that is composed of an inorganic dispersion type light emitting device and emits light by itself to exhibit excellent visibility.
【０００２】[0002]
一般に、無機分散型発光素子は、自動車用計器の文字盤やショーウィンドの装 飾用などに広く用いられており、従来の無機分散型発光素子（フラット型）は図 ７に示したような基本構造を有している。 Generally, the inorganic dispersed light emitting device is widely used for the dial of automobile instrument and the display of show windows, and the conventional inorganic dispersed light emitting device (flat type) has the basic structure as shown in FIG. It has a structure.
【０００３】 すなわち、図７に示した無機分散型発光素子（フラット型）は、金属素地１上 にホーロー（ガラス質）の絶縁反射層２、蛍光体発光層３、透明導電膜４および 透明保護層５を順次形成することにより構成されている。That is, the inorganic dispersion type light emitting device (flat type) shown in FIG. 7 has an enamel (glassy) insulating reflection layer 2, a phosphor light emitting layer 3, a transparent conductive film 4 and a transparent protective layer on a metal base 1. It is constituted by sequentially forming the layer 5.
【０００４】 そして、ホーロー質絶縁反射層２としては、蛍光体発光層３への電界の印加を 増加するために誘電率が高く、また反射層としての作用を発揮させるために白色 系のホーロー釉が通常用いられている。The enamel insulating reflective layer 2 has a high dielectric constant in order to increase the application of an electric field to the phosphor light-emitting layer 3, and a white enamel glaze to exert the function as a reflective layer. Is usually used.
【０００５】 また、蛍光体発光層３は、図８に示したように、ホーロー３ａ中に蛍光体３ｂ が分散された構造となっている。As shown in FIG. 8, the phosphor light emitting layer 3 has a structure in which the phosphor 3b is dispersed in the enamel 3a.
【０００６】 さらに、蛍光体発光層３上には、蒸着やスパッタリングなどにより透明導電膜 ４が形成されており、この透明導電膜４の表面には、外部との絶縁および素子の 保護を図るために、少なくとも発光面側が透明である透明保護層５が形成されて いる。Further, a transparent conductive film 4 is formed on the phosphor light emitting layer 3 by vapor deposition, sputtering, or the like, and the surface of the transparent conductive film 4 is provided for insulation from the outside and protection of the element. Further, a transparent protective layer 5 having a transparent at least the light emitting surface side is formed.
【０００７】 上記の構成において、透明導電膜４に設けた電極４ａと、金属素地１に設けた 電極１ａとを、リード線６により電気的に連結し、電源７から電圧を印加するこ とにより、蛍光体発光層３に電界を生じ、蛍光体３ｂが発光するようになってい る。In the above structure, the electrode 4 a provided on the transparent conductive film 4 and the electrode 1 a provided on the metal base 1 are electrically connected by the lead wire 6 and a voltage is applied from the power supply 7. An electric field is generated in the phosphor light emitting layer 3 so that the phosphor 3b emits light.
【０００８】 しかるに、上記の構造からなる従来の無機分散型発光素子は、フラット（平板 ）型が主流を占めており、これは主として自動車用計器や計測機器の文字盤とし て、例えば夜間などの視認性を高めるために使用されている。However, in the conventional inorganic dispersion type light emitting device having the above-mentioned structure, the flat (flat plate) type is predominant, and this is mainly used as a dial for automobile instruments and measuring instruments, for example, at night. It is used to improve visibility.
【０００９】 ところで、従来の自動車用計器や計測機器などにおいては、上記無機分散型発 光素子を利用して文字盤や表示文字部分を照明することは知られているもの、計 器の指針そのものは発光しないため、視認効果が劣り、とくに夜間などにおいて は計器の読取り精度を十分に満足し得ないという問題があった。By the way, in the conventional instrument and measuring instrument for automobiles, it is known to illuminate the dial and the display character portion by using the above-mentioned inorganic dispersion type light emitting element, and the indicator itself of the instrument. Since it does not emit light, the visual recognition effect is poor, and there is a problem that the reading accuracy of the instrument cannot be sufficiently satisfied, especially at night.
【００１０】[0010]
この考案は、上述した従来の問題を解決するために検討した結果、達成された ものである。 The present invention has been achieved as a result of studies for solving the above-mentioned conventional problems.
【００１１】 したがって、この考案の目的は、それ自体が発光して新規かつすぐれた視認効 果を発揮する発光指針を提供することにある。Therefore, an object of the present invention is to provide a light emitting guide which emits light itself and exhibits a new and excellent visual effect.
【００１２】[0012]
上記の目的を達成するために、この考案の発光指針は、直径１．５mm以下の線 状金属芯材の表面に、ホーロー質絶縁反射層、ホーロー中に蛍光体を分散させた 蛍光体発光層、透明導電膜および透明保護層を順次形成すると共に、前記線状金 属芯材と前記透明導電膜とを電気的に連結した棒状の無機分散型発光素子からな ることを特徴とする。 In order to achieve the above-mentioned object, the light emitting pointer of the present invention is a phosphor light emitting layer in which a hollow metal insulating material having a diameter of 1.5 mm or less is provided on a surface of an insulating reflective layer, and a phosphor is dispersed in the hollow material. A transparent conductive film and a transparent protective layer are sequentially formed, and the rod-shaped inorganic dispersion type light emitting element electrically connects the linear metal core material and the transparent conductive film.
【００１３】[0013]
この考案の発光指針は、無機分散型発光素子の構造を指針形状の棒状物に応用 したため、それ自体が発光して、とくに夜間などに新規な視認効果を発揮し、計 器の読取り精度を著しく向上することができる。 The light emitting pointer of this invention applies the structure of the inorganic dispersion type light emitting element to the pointer-shaped rod-shaped object, so that it emits light and exhibits a new visual effect, especially at night, and the reading accuracy of the instrument is significantly improved. Can be improved.
【００１４】 また、この考案の発光指針は、電極の形成手段を工夫することによって、その 輝度を維持し、輝度勾配の発生などを防止することができ、その発光信頼性をき わめてすぐれたものとすることができる。Further, the light emitting pointer of the present invention can maintain its brightness and prevent the occurrence of a brightness gradient by devising the electrode forming means, and its light emitting reliability is extremely excellent. It can be
【００１５】 したがって、この考案の発光指針は、例えば自動車用計器や計測機器などの指 針として広く用いることができる。Therefore, the light emitting pointer of the present invention can be widely used as a finger needle of, for example, measuring instruments for automobiles and measuring instruments.
【００１６】[0016]
以下、図面を参照しつつ、この考案の発光指針の実施例について詳細に説明す る。 Hereinafter, embodiments of the light emitting pointer of the present invention will be described in detail with reference to the drawings.
【００１７】 図１はこの考案の発光指針の基本構造を示す断面説明図、図２はこの考案の発 光指針における電極取出例の第１実施例を示す正面説明図、図３は同じく電極取 出例の第２実施例を示す一部切欠正面説明図、図４は同じく第２実施例における 補助電極形成過程を示す断面説明図、図５は同じく第２実施例における電極端子 の形成過程を示す正面説明図、図６は同じく第２実施例におけるエナメル線電極 形成例を示す断面説明図である。FIG. 1 is a sectional explanatory view showing a basic structure of a light emitting pointer of the present invention, FIG. 2 is a front explanatory view showing a first embodiment of an electrode lead-out example in the light emitting pointer of the present invention, and FIG. A partially cutaway front view showing a second embodiment of the present invention, FIG. 4 is a sectional view showing a process of forming an auxiliary electrode in the second embodiment, and FIG. 5 is a view showing a process of forming electrode terminals in the second embodiment. Similarly, FIG. 6 is a sectional explanatory view showing an example of forming an enamel wire electrode in the second embodiment.
【００１８】 図１において、この考案の発光指針を形成する無機分散型発光素子は、線状金 属芯材１０の表面に、ホーロー質絶縁反射層２０、ホーロー中に蛍光体を分散さ せた蛍光体発光層３０、透明導電膜４０および透明保護層５０を順次形成した基 本構造を有している。In FIG. 1, an inorganic dispersion type light emitting device forming a light emitting pointer of the present invention has a enamel insulating reflective layer 20 on the surface of a linear metal core material 10 and a phosphor dispersed in the enamel. It has a basic structure in which a phosphor light emitting layer 30, a transparent conductive film 40, and a transparent protective layer 50 are sequentially formed.
【００１９】 そして、線状金属芯材１０は、脱炭素鋼またはステンレス鋼からなる直径が１ ．５mm以下の線条物で形成されている。The linear metal core material 10 is made of decarbonized steel or stainless steel and has a diameter of 1. It is made of filaments of 5 mm or less.
【００２０】 この線状金属芯材１０として、脱炭素鋼を用いる場合には、以下に説明するホ ーロー質絶縁反射層２０との接合性がすぐれているが、とくに直径が１．５mm以 下の線条物として低コストかつ容易に入手可能なステンレス鋼を用いる場合には 、ホーロー質絶縁反射層２０の形成に先立ち、予めその表面にサンドプラスト処 理またはニッケル処理を施すことによって、ホーロー質絶縁反射層２０との密着 性を改良することが望ましい。When decarbonized steel is used as the linear metal core material 10, it has excellent bondability with the hollow insulating reflection layer 20 described below, but particularly with a diameter of 1.5 mm or less. In the case where low cost and easily available stainless steel is used as the filaments, the surface of the enamel-like insulating reflection layer 20 is subjected to sand plast treatment or nickel treatment prior to the formation thereof. It is desirable to improve the adhesion with the insulating reflection layer 20.
【００２１】 上記サンドプラスト処理またはニッケル処理によって、ステンレス鋼からなる 線状金属芯材１０とホーロー質絶縁反射層２０との密着性が向上する理由につい ては明らかではないが、おそらくステンレス鋼中に含まれるニッケル原子が、ホ ーロー質絶縁反射層２０との界面でガラス質のホーロー中に拡散し、何らかの化 学結合を行うことによるものと考えられる。The reason why the adhesion between the linear metal core 10 made of stainless steel and the enamel insulating reflective layer 20 is improved by the sand plast treatment or nickel treatment is not clear, but it is probably It is considered that the contained nickel atoms diffuse into the vitreous enamel at the interface with the hollow insulating reflection layer 20 and form some chemical bond.
【００２２】 ホーロー質絶縁反射層２０としては、蛍光体発光層３０への電界の印加を増加 するために誘電率が高く、また反射層としての作用を発揮させる白色系のホーロ ー釉が好ましく用いられる。As the enamel insulating reflection layer 20, a white enamel glaze having a high dielectric constant for increasing the application of an electric field to the phosphor light emitting layer 30 and exhibiting an action as a reflection layer is preferably used. Be done.
【００２３】 ホーローで一般に言えることは、金属とガラスが直接結合するというより、表 面に必ず存在する酸化物の膜を介して両者が結合する場合が多い。つまり、酸素 原子をＳｉとＦｅが共有し合う形で両者が結合する可能性がある。従って、この 場合、Ｎｉ等のカプリング原子の存在なしでも両者は接着する。そこで、ステン レス鋼とガラス質を接着するには、先ず表面の汚れた層（酸化層）を化学的にエ ッチングしてはがし、再度きれいな薄い酸化膜の層を例えば酸素雰囲気中で加熱 することにより形成し、その後、従来通りのプロセスでガラス質を焼成すれば密 着性の良い膜を得ることができる。Generally, in enamel, the metal and the glass are not directly bonded to each other, but they are often bonded to each other through an oxide film that is always present on the surface. That is, there is a possibility that Si and Fe share an oxygen atom so that they are bound to each other. Therefore, in this case, both are bonded even without the presence of coupling atoms such as Ni. Therefore, in order to bond the stainless steel and the glassy material, first, the dirty layer (oxide layer) on the surface is chemically etched and peeled off, and the clean thin oxide layer is heated again in, for example, an oxygen atmosphere. And then the glass material is fired by a conventional process to obtain a film with good adhesion.
【００２４】 蛍光体発光層３０としては、例えば前記図８に示したように、ホーロー３ａ中 に蛍光体３ｂが分散されたものが用いられる。As the phosphor light emitting layer 30, for example, as shown in FIG. 8, a phosphor in which the phosphor 3b is dispersed in the enamel 3a is used.
【００２５】 透明導電膜４０は、ＩＴＯ膜（酸化インジウムにスズを添加したもの）に代表 される膜を、蒸着やスパッタリングなどの方法で蛍光体発光層３０上に製膜する ことにより形成される。The transparent conductive film 40 is formed by forming a film typified by an ITO film (indium oxide with tin added) on the phosphor light emitting layer 30 by a method such as vapor deposition or sputtering. ..
【００２６】 透明保護層５０としては、外部との絶縁および素子の保護を図るために、少な くとも発光面側が透明な合成樹脂膜またはガラス質ホーロー膜が使用される。As the transparent protective layer 50, a synthetic resin film or a vitreous enamel film having a transparent light emitting surface side is used at least for the purpose of insulation from the outside and protection of the element.
【００２７】 次に、この考案の発光指針における電極の取出例について説明する。Next, an example of taking out the electrodes in the light emitting pointer of the present invention will be described.
【００２８】 まず、図２に示した第１実施例においては、一方の電極１１を線状金属芯材１ ０に設け、また他方の電極６１を透明導電膜４０にエナメル線６０を巻き付けた 簡易電極により構成している。First, in the first embodiment shown in FIG. 2, one electrode 11 is provided on the linear metal core material 10, and the other electrode 61 is wound around the transparent conductive film 40 with the enamel wire 60. It is composed of electrodes.
【００２９】 なお、図２においては、透明保護層５０の図示を省略している。It should be noted that the transparent protective layer 50 is not shown in FIG.
【００３０】 この第１実施例の態様は、線状金属芯材１０の一部に電極１１を設けると共に 、透明導電膜４０上にエナメル線６０を巻いて簡易電極６１とし、さらに前記電 極１１と簡易電極６１とを電源７０に接続することにより得られる。In the mode of the first embodiment, the electrode 11 is provided on a part of the linear metal core material 10, and the enamel wire 60 is wound on the transparent conductive film 40 to form the simple electrode 61. It is obtained by connecting the simple electrode 61 and the simple electrode 61 to the power source 70.
【００３１】 そして、上記の構成において、電源７０から電圧を印加することにより、蛍光 体発光層３０に電界を生じ、蛍光体が発光するようになっている。Then, in the above configuration, when a voltage is applied from the power source 70, an electric field is generated in the phosphor light emitting layer 30, and the phosphor emits light.
【００３２】 しかるに、上記第１実施例は、簡易的に電極を形成できるという利点を有する ものの、簡易電極６１を透明導電膜４０上に部分的に、しかもエナメル線６０を 巻くことによる点接触で形成することから、蛍光体発光層３０の蛍光体の輝度に 輝度勾配を生じ、さらには簡易電極６１の形成部で透明導電膜４０が絶縁破壊し 、輝度を十分に維持できなくなるという不具合を生じる場合がある。However, although the first embodiment has an advantage that the electrode can be easily formed, the simple electrode 61 is partially formed on the transparent conductive film 40, and moreover, by the point contact by winding the enamel wire 60. Since it is formed, a brightness gradient is generated in the brightness of the phosphor of the phosphor emission layer 30, and further, the transparent conductive film 40 is dielectrically broken down in the formation portion of the simple electrode 61, which causes a problem that the brightness cannot be sufficiently maintained. There are cases.
【００３３】 そこで、図３〜図６に示した第２実施例では、上記不具合を解消し、輝度を良 好に維持すると共に、輝度勾配の発生を効果的に防止している（図３〜図６では 透明保護層５０の図示を省略してある）。In view of this, in the second embodiment shown in FIGS. 3 to 6, the above-mentioned problems are solved, the brightness is maintained favorably, and the occurrence of a brightness gradient is effectively prevented (FIGS. 3 to 6). The transparent protective layer 50 is not shown in FIG. 6).
【００３４】 すなわち、第２実施例においては、発光が視認されない指針の基部および／ま たは指針の長手方向裏側に導体膜からなる補助電極８０を設けたことを特徴とす る。That is, the second embodiment is characterized in that the auxiliary electrode 80 made of a conductive film is provided on the base of the pointer where the light emission is not visible and / or on the back side of the pointer in the longitudinal direction.
【００３５】 図２において、視認者側からは指針の裏側の発光は視認できず、また線状金属 芯材１０の基部１０´側も指針キャップ９０がかぶされることから、その発光が 視認できない。In FIG. 2, the viewer cannot see the light emitted from the back side of the pointer, and the base 10 'side of the linear metal core 10 is also covered with the pointer cap 90, so that the emitted light cannot be seen. ..
【００３６】 したがって、この発光死角となる指針の基部側および／または長手方向裏側（ 図３では両側）に、透明導電膜４０よりも抵抗率の小さい導体膜を、少なくとも 透明導電膜４０と接するように設けた補助電極８０によって、透明導電膜４０側 の電極を形成すれば、この補助電極８０は視認者の視認の妨げとならず、しかも 輝度維持および輝度勾配の防止に好ましく寄与することになるのである。Therefore, a conductor film having a resistivity lower than that of the transparent conductive film 40 should be in contact with at least the transparent conductive film 40 on the base side and / or the back side (both sides in FIG. 3) in the longitudinal direction of the pointer that becomes the light emission blind spot. When the electrode on the transparent conductive film 40 side is formed by the auxiliary electrode 80 provided in the above, the auxiliary electrode 80 does not hinder the visual recognition of the viewer, and further contributes to the maintenance of the brightness and the prevention of the brightness gradient. Of.
【００３７】 なお、図３に示したように、補助電極８０をとくに指針の長手方向裏側の全体 に渡って形成すれば、指針先端側における電界強度の低減およびロスが少なくな り、輝度勾配が効果的に解消するばかりか、指針全体の発光効率が向上し、その 信頼性をきわめて高めることが可能である。As shown in FIG. 3, if the auxiliary electrode 80 is formed over the entire back side in the longitudinal direction of the pointer, the reduction and loss of the electric field strength on the tip side of the pointer are reduced and the brightness gradient is reduced. Not only can it be effectively eliminated, but the luminous efficiency of the entire pointer can be improved and its reliability can be greatly increased.
【００３８】 導体膜からなる補助電極８０は、透明導電膜４０上または蛍光体発光層３０上 に、銅および銀などの導電ペーストを塗布し、乾燥するか、またはニッケル、ク ロムおよび錫などを無電解メッキすることにより容易に形成することができる。 ただし、導電ペーストまたは無電解メッキに用いる金属は、透明導電膜４０より も抵抗率が十分に小さいものを選択することが重要である。The auxiliary electrode 80 made of a conductive film is formed by applying a conductive paste such as copper and silver on the transparent conductive film 40 or the phosphor light emitting layer 30 and drying it, or by using nickel, chrome and tin. It can be easily formed by electroless plating. However, it is important to select a conductive paste or a metal used for electroless plating that has a resistivity sufficiently lower than that of the transparent conductive film 40.
【００３９】 図４は、補助電極８０の形成過程の一例を示し、たとえばスパッタリングなど により透明導電膜４０を形成する際に、指針裏側の長手方向は固定用基板９１を 密着配置されるため、指針本体の裏面長手方向の部分に透明導電膜４０が形成さ れない部分のある状態となる。そこでこの部分に透明導電膜４０には接するよう 導電ペーストの塗布または無電解メッキを行うことにより、補助電極８０を容易 に形成することができる。FIG. 4 shows an example of the process of forming the auxiliary electrode 80. When the transparent conductive film 40 is formed by, for example, sputtering, the fixing substrate 91 is closely arranged in the longitudinal direction on the back side of the pointer. This results in a state in which there is a portion where the transparent conductive film 40 is not formed in the longitudinal portion of the back surface of the main body. Therefore, the auxiliary electrode 80 can be easily formed by applying a conductive paste or electroless plating so that this portion is in contact with the transparent conductive film 40.
【００４０】 図５は、指針の基部近傍に位置する補助電極８０に電極端子８１を設けた例を 示し、補助電極８０をハンダ付け可能な金属で形成すれば、この電極端子８１は 半田付けにより容易に固着することが可能である。なお、電極端子８１を設けず とも、エナメル線などを補助電極８０に直接ハンダ付けすることも勿論可能であ る。FIG. 5 shows an example in which an electrode terminal 81 is provided on the auxiliary electrode 80 located near the base of the pointer. If the auxiliary electrode 80 is made of a solderable metal, the electrode terminal 81 can be soldered. It can be easily fixed. Needless to say, the enameled wire or the like can be directly soldered to the auxiliary electrode 80 without providing the electrode terminal 81.
【００４１】 図６は、とくに指針キャップ内にあって、外部から視認されない指針の基部に 位置する補助電極８０に、エナメル線６０を巻き付けることにより電極を形成し た例を示し、この例においては、まず透明導電膜４０上に第１補助電極膜８２を 形成し、その上にエナメル線６０を巻き付け、さらにエナメル線６０上に第２補 助導電膜８３を形成することによって、補助電極８０の内層にエナメル線６０が 巻線された態様となるため、エナメル線６０は透明導電膜４０を損傷することが なく、しかも透明導電膜４０と十分な接触面積をもって接続されることになる。FIG. 6 shows an example in which an electrode is formed by winding an enamel wire 60 around an auxiliary electrode 80 located at the base of the pointer which is not visible from the outside, particularly in the pointer cap. In this example, First, the first auxiliary electrode film 82 is formed on the transparent conductive film 40, the enamel wire 60 is wound on the first auxiliary electrode film 82, and the second auxiliary auxiliary conductive film 83 is further formed on the enamel wire 60. Since the enamel wire 60 is wound on the inner layer, the enamel wire 60 does not damage the transparent conductive film 40 and is connected to the transparent conductive film 40 with a sufficient contact area.
【００４２】 以下に、上記の構成からなるこの考案の発光指針を製造する一具体例について 説明する。A specific example of manufacturing the light emitting pointer of the present invention having the above structure will be described below.
【００４３】 線状金属芯材の準備 直径１mm、長さ５０〜７０mmのステンレス線状体を準備し、この線状体にサン ドプラスト処理を行った。Preparation of Linear Metal Core Material A stainless linear body having a diameter of 1 mm and a length of 50 to 70 mm was prepared, and this linear body was subjected to sand plast treatment.
【００４４】 ホーロー質絶縁反射層の形成 白色系のホーロー釉のスリップをステンレス鋼線状体の表面に塗布し、１００ 〜１５０℃で３０分間乾燥した後、３５０〜４００℃で１０分間仮焼成し、次い で７５０℃で５〜１０分間本焼成した。Formation of Enameled Insulating Reflective Layer A white enamel glaze slip was applied to the surface of a stainless steel linear body, dried at 100 to 150 ° C. for 30 minutes, and then calcined at 350 to 400 ° C. for 10 minutes. Then, main firing was performed at 750 ° C. for 5 to 10 minutes.
【００４５】 蛍光体発光層の形成 透明なホーロー釉のスリップに蛍光体を混合し、これをホーロー質絶縁反射層 上に塗布した後、上記ホーロー質絶縁反射層の場合と同様の条件で乾燥、仮焼成 および本焼成を行った。Formation of Phosphor Emitting Layer A phosphor is mixed with a slip of transparent enamel glaze, and this is applied on an enamel insulating reflective layer, and then dried under the same conditions as in the case of the enamel insulating reflective layer, Pre-baking and main baking were performed.
【００４６】 なお、蛍光体としてはSYLVANIA（シルバニア）社製８１３（青緑）、８３０（ 白）、５２３（黄緑）および７２９（緑）の４種を用い、ホーロー釉７０重量部 に対し、蛍光体３０重量部の割合で混合した。As the phosphor, four kinds of 813 (blue-green), 830 (white), 523 (yellow-green) and 729 (green) manufactured by SYLVANIA (Sylvania) were used, and 70 parts by weight of enamel glaze was used. The phosphor was mixed at a ratio of 30 parts by weight.
【００４７】 透明導電膜の形成 下記条件のマグネトロスパッタリング法により、ＩＴＯ膜（酸化インジウムに スズを添加したもの）を形成した。Formation of Transparent Conductive Film An ITO film (indium oxide with tin added) was formed by a magnetro sputtering method under the following conditions.
【００４８】 ベーク条件：２００℃、１時間 スパッタリング時間：１０分 雰囲気（Ａｒ）流量：２０CCM 真空度：９×１０-6Toor（スパッタリング時：約１×１０-3Toor） なお、基部側および指針裏側長手方向に位置する部分に固定用基板を密着させ ることにより、指針を固定するとともに補助電極形成部分を確保した。Baking condition: 200 ° C., 1 hour Sputtering time: 10 minutes Atmosphere (Ar) flow rate: 20 CCM Vacuum degree: 9 × 10 −6 Toor (Sputtering: about 1 × 10 −3 Toor) The base side and the pointer By fixing the fixing substrate to the portion located in the longitudinal direction on the back side, the pointer was fixed and the auxiliary electrode forming portion was secured.
【００４９】 電極および透明保護層の形成 基部の金属芯材の一部に電極を設けると共に、上記補助電極形成部分に導電ペ ーストを塗布、乾燥して補助電極を形成した後、補助電極の基部側に電極端子を ハンダ付けにより固着した。Formation of Electrode and Transparent Protective Layer An electrode is provided on a part of the metal core material of the base, and a conductive paste is applied to the above-mentioned auxiliary electrode forming portion and dried to form the auxiliary electrode, and then the base of the auxiliary electrode is formed. The electrode terminals were fixed to the side by soldering.
【００５０】 また、透明導電膜上に、さらにホーロー質の透明保護層を形成することにより 、この考案の発光指針を完成した。Further, the luminescent guide of this invention was completed by further forming a enamel transparent protective layer on the transparent conductive film.
【００５１】 この発光指針について、補助電極上の電極端子と、ステンレス鋼線状体上の電 極との間に、交流電界を印加したところ、２００Ｖ、４００Ｈｚにおいて、最大 ５０cd／ｍ2 の発光輝度が得られ、この発光は指針の基部から先端にかけてきわ めて均一であった。When an AC electric field was applied between the electrode terminal on the auxiliary electrode and the electrode on the stainless steel linear member with respect to this light emitting pointer, a maximum emission luminance of 50 cd / m 2 at 200 V and 400 Hz was obtained. The light emission was extremely uniform from the base of the pointer to the tip.
【００５２】 これらのことから、この考案の発光指針は、発光輝度の勾配がなく、かつ輝度 維持がすぐれ、例えば自動車用計器の指針として応用した場合に、新規かつすぐ れた視認性を呈し、読取り精度を向上し得ることが確認された。From these facts, the luminous pointer of the present invention has no gradient of luminous brightness and is excellent in maintaining the brightness, and exhibits novel and excellent visibility when applied as a pointer of an automobile instrument, for example. It was confirmed that the reading accuracy could be improved.
【００５３】[0053]
以上説明したように、この考案の発光指針は、無機分散型発光素子の構造を指 針形状の棒状物に応用したため、それ自体が発光して、とくに夜間などに新規な 視認効果を発揮し、計器の読取り精度を著しく向上することができる。 As described above, the light emitting pointer of the present invention applies the structure of the inorganic dispersion type light emitting element to the needle-shaped rod-like object, so that it emits light by itself and exhibits a new visual effect particularly at night. The reading accuracy of the instrument can be significantly improved.
【００５４】 また、この考案の発光指針は、電極の形成手段を工夫することによって、その 輝度を維持し、輝度勾配の発生などを防止することができ、その発光信頼性をき わめてすぐれたものとすることができる。Further, the light emitting pointer of the present invention can maintain its brightness and prevent the occurrence of a brightness gradient by devising the electrode forming means, and its light emitting reliability is excellent. It can be
【００５５】 したがって、この考案の発光指針は、例えば自動車用計器や計測機器などの指 針として広く用いることができる。Therefore, the light emitting pointer of the present invention can be widely used as a finger needle of, for example, measuring instruments and measuring instruments for automobiles.
【図１】図１はこの考案の発光指針の基本構造を示す断
面説明図である。FIG. 1 is an explanatory sectional view showing a basic structure of a light emitting pointer of the present invention.
【図２】図２はこの考案の発光指針における電極取出例
の第１実施例を示す正面説明図である。FIG. 2 is a front explanatory view showing a first embodiment of an electrode extraction example in the light emitting pointer of the present invention.
【図３】図３は同じく電極取出例の第２実施例を示す一
部切欠正面説明図である。FIG. 3 is a partially cutaway front view showing a second embodiment of the same example of electrode extraction.
【図４】図４は同じく第２実施例における補助電極形成
過程を示す断面説明図である。FIG. 4 is a sectional explanatory view showing a process of forming an auxiliary electrode in the second embodiment.
【図５】図５は同じく第２実施例における電極端子の形
成過程を示す正面説明図である。FIG. 5 is a front explanatory view showing a process of forming electrode terminals in the same second embodiment.
【図６】図６は同じく第２実施例におけるエナメル線電
極形成例を示す断面説明図である。FIG. 6 is an explanatory sectional view showing an example of forming an enameled wire electrode in the same manner as the second embodiment.
【図７】図７は従来のフラット型無機分散型発光素子を
示す断面説明図である。FIG. 7 is an explanatory cross-sectional view showing a conventional flat inorganic dispersion-type light emitting device.
【図８】図８は図７におけるホーロー質絶縁反射層の拡
大断面図である。FIG. 8 is an enlarged cross-sectional view of the enamel insulating reflection layer in FIG.
１０ 線状金属芯材 １１ 電極 ２０ ホーロー質絶縁反射層 ３０ 蛍光体発光層 ４０ 透明導電膜 ４１ 電極（第１実施例） ５０ 透明保護層 ６０ エナメル線 ７０ 電源 ８０ 補助電極（第２実施例） ８１ 電極端子 ９０ 指針キャップ 10 Wire Metal Core Material 11 Electrode 20 Hollow Insulating Reflective Layer 30 Phosphor Emitting Layer 40 Transparent Conductive Film 41 Electrode (First Example) 50 Transparent Protective Layer 60 Enamel Wire 70 Power Supply 80 Auxiliary Electrode (Second Example) 81 Electrode terminal 90 Pointer cap
Claims (8)
に、ホーロー質絶縁反射層、ホーロー中に蛍光体を分散
させた蛍光体発光層、透明導電膜および透明保護層を順
次形成すると共に、前記線状金属芯材と前記透明導電膜
とを電気的に連結した棒状の無機分散型発光素子からな
ることを特徴とする発光指針。1. A enamel insulating reflective layer, a phosphor light-emitting layer having a phosphor dispersed in a enamel, a transparent conductive film, and a transparent protective layer are sequentially formed on the surface of a linear metal core having a diameter of 1.5 mm or less. In addition, the light emitting pointer comprises a rod-shaped inorganic dispersion type light emitting element in which the linear metal core material and the transparent conductive film are electrically connected.
レス鋼からなることを特徴とする請求項１に記載の発光
指針。2. The luminous pointer according to claim 1, wherein the linear metal core material is made of decarbonized steel or stainless steel.
を形成する前に、予め表面にサンドプラスト処理または
ニッケル処理が施されていることを特徴とする請求項１
または２に記載の発光指針。3. The linear metal core material is subjected to a sand plast treatment or a nickel treatment on its surface in advance before forming the enamel type insulating reflection layer.
Alternatively, the luminous pointer according to item 2.
表面にエナメル線を巻線することにより形成されている
ことを特徴とする請求項１、２または３に記載の発光指
針。4. The light emitting pointer according to claim 1, 2 or 3, wherein the electrode on the transparent conductive film side is formed by winding an enamel wire on the surface of the transparent conductive film.
よりも抵抗率の小さい導体膜を、指針の基部側および／
または長手方向裏側に、少なくとも前記透明導電膜と接
するように設けた補助電極からなることを特徴とする請
求項１、２または３に記載の発光指針。5. An electrode on the side of the transparent conductive film is a conductive film having a resistivity lower than that of the transparent conductive film, and
The light emitting pointer according to claim 1, 2 or 3, further comprising an auxiliary electrode provided on the back side in the longitudinal direction so as to be in contact with at least the transparent conductive film.
無電解メッキにより形成されていることを特徴とする請
求項１、２、３または５に記載の発光指針。6. The light emitting pointer according to claim 1, 2, 3 or 5, wherein the auxiliary electrode is formed by applying a conductive paste or electroless plating.
とを特徴とする請求項１、２、３、５または６に記載の
発光指針。7. The light emitting pointer according to claim 1, 2, 3, 5 or 6, wherein an electrode terminal is fixed to a part of the auxiliary electrode.
補助電極の内層にエナメル線が巻線されていることを特
徴とする請求項１、２、３、５または６に記載の発光指
針。8. The light emitting pointer according to claim 1, 2, 3, 5 or 6, wherein an auxiliary electrode is formed on a base portion of the pointer, and an enameled wire is wound on an inner layer of the auxiliary electrode. ..