JPH0551870A - Flavored plush and pile cloth - Google Patents
Flavored plush and pile clothInfo
- Publication number
- JPH0551870A JPH0551870A JP3229481A JP22948191A JPH0551870A JP H0551870 A JPH0551870 A JP H0551870A JP 3229481 A JP3229481 A JP 3229481A JP 22948191 A JP22948191 A JP 22948191A JP H0551870 A JPH0551870 A JP H0551870A
- Authority
- JP
- Japan
- Prior art keywords
- pile
- cloth
- resin binder
- plush
- fragrance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は立毛・パイル製品に香料
を付着した製品に関するものであって、詳しくは立毛・
パイル製品の基布のみに香料を内包するマイクロカプセ
ルを含有する樹脂バインダーを塗布した付香加工立毛・
パイル製品に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a napped / pile product in which a fragrance is attached.
Perfumed nap with resin binder containing microcapsules containing perfume only applied to pile fabric base cloth.
It concerns pile products.
【０００２】[0002]
【従来の技術】繊維製品に香りを付与する方法について
は、香料を直接付与したり、繊維に香りを移す等の方法
があったが、繊維に付与された香りの持続性、特に洗濯
した時の耐久性に問題があった。2. Description of the Related Art As a method for imparting a scent to a textile product, there have been methods such as directly applying a fragrance or transferring the scent to the fiber. However, the persistence of the scent imparted to the fiber, especially when washed There was a problem with the durability of.
【０００３】そこでこの問題を解決するために様々な方
法が検討されている。例えば、香料を繊維ポリマー中
に入れて混合紡糸する方法、香り成分を担持させた多
孔質粉末等を布帛に付与する方法、香料を接着剤や樹
脂バインダーと共に付与する方法、香料含有マイクロ
カプセルを糊剤やバインダーを利用して付着させる方法
（特開平 1−260066号、特開平2-6672号公報）等が開示
されている。Therefore, various methods have been studied to solve this problem. For example, a method in which a fragrance is put into a fiber polymer and mixed and spun, a method in which a scent component-supporting porous powder or the like is applied to a cloth, a method in which a fragrance is applied together with an adhesive or a resin binder, and a fragrance-containing microcapsule is glued. A method of adhering using an agent or a binder (Japanese Patent Laid-Open Nos. 1-260066 and 2-6672) is disclosed.
【０００４】しかしながら、上記のの方法では、加工
プロセスで高温環境下に置かれた時点で香料が変質して
しまい、あるいはの方法では、繊維に付着した後の
香りの徐放性、持続性および洗濯耐久性等の特性が充分
でなく、流通過程で移香してしまうといった欠点があっ
た。またの方法では、香料をマイクロカプセルに内包
させることによって、徐放性や持続性はおおむね満足で
きるものが得られているが、バインダー樹脂と共に繊維
全体に付与するために、得られる付香繊維製品の外観、
風合い、肌ざわり等が悪化してしまうといった問題が残
っている。However, in the above method, the fragrance is deteriorated when it is placed in a high temperature environment in the processing process, or in the above method, the fragrance is gradually released after being attached to the fiber, and the fragrance is maintained. There was a defect that the characteristics such as washing durability were not sufficient, and the fragrance was transferred during the distribution process. In the other method, by encapsulating the perfume in microcapsules, sustained release and sustainability can be generally satisfied, but since it is added to the entire fiber together with the binder resin, the obtained perfume fiber product is obtained. The appearance of
There remains a problem that the texture and feel of the skin deteriorate.
【０００５】特に、マイヤー毛布やボア、ハイパイル等
の起毛仕上げされる繊維製品や、外観が重要視されるマ
ット類、カーペット類、椅子張り地等の立毛・パイル製
品においては、繊維の肌ざわり、風合い、および外観を
変化させずに付香することは非常に困難であった。[0005] In particular, in the case of raised fiber products such as Meyer blankets, bores, and high piles, and mats, carpets, and upholstered pile products such as upholstered fabrics, where appearance is important, the texture of the fibers, It was very difficult to perfume without changing the texture and appearance.
【０００６】[0006]
【発明が解決しようとする課題】上記事情を考慮した本
発明の目的は、立毛・パイル製品の風合い、外観を損な
うことなく、かつ徐放性、持続性に優れた付香加工製品
を提供することである。SUMMARY OF THE INVENTION In consideration of the above circumstances, an object of the present invention is to provide a perfumed product which is excellent in sustained release and sustainability without impairing the texture and appearance of napped and pile products. That is.
【０００７】[0007]
【課題を解決するための手段】上記目的を解決するため
の本発明の構成は、立毛部もしくはパイル部および基布
からなる立毛もしくはパイル布帛において、香料を内包
するマイクロカプセルを樹脂バインダーと共に前記基布
にのみ付与し、前記樹脂バインダーの使用量を前記マイ
クロカプセルの６〜３０倍とし、樹脂バインダーとマイ
クロカプセルの総付与量を２〜１５０g/m2とすることを
要旨とするものである。Means for Solving the Problems The constitution of the present invention for solving the above-mentioned object is to provide a napped or pile cloth comprising a napped portion or a pile portion and a base cloth with microcapsules containing a perfume together with a resin binder. The gist of the present invention is to apply only to the cloth, the amount of the resin binder used is 6 to 30 times that of the microcapsules, and the total amount of the resin binder and the microcapsules applied is 2 to 150 g / m 2 .
【０００８】[0008]
【作用】本発明の対象となる立毛・パイル布帛とは、織
ボア、ニットボア、マイヤー毛布（ダブルラッセル毛布
とも言う）、モケット、カットパイルカーペット、カッ
トパイルマット、ハイパイル等の起毛および／またはシ
ャーリング等の仕上げ加工がなされる繊維製品や、ルー
プパイルフック、マット類、ループカーペット織、ニッ
ト椅子張り地等の基布あるいは明確な裏面を有する製品
を包含するものである。本発明では、上記製品の基布も
しくは裏面に付香加工を行なうことによって、表側の立
毛・パイル部分の風合い低下を防ぐものである。このた
めこれらの製品の中で、製織後の毛抜けを防止するため
に裏面バッキング処理をするものには本発明の付香加工
処理が施し易く好ましいが、織毛布や、ニューマイヤー
毛布、タフト毛布等の両面（表裏）起毛加工されている
製品には適していない。The napped / pile cloth to which the present invention is applied includes woven boa, knit boa, Meyer blanket (also called double Russell blanket), moquette, cut pile carpet, cut pile mat, raised pile and / or shirring, etc. The present invention includes textile products that are finished by the above, base fabrics such as loop pile hooks, mats, loop carpet woven fabrics, and knit upholstery fabrics or products having a clear back surface. In the present invention, the texture of the napped / pile portion on the front side is prevented from being deteriorated by performing the scenting process on the base fabric or the back surface of the above product. For this reason, among these products, those with a backing treatment for preventing hair loss after weaving are preferable because they can be easily subjected to the scenting treatment of the present invention, but woven blankets, New Meyer blankets, and tuft blankets are preferred. It is not suitable for products that have been brushed on both sides (front and back).
【０００９】本発明において用いられる香料内包マイク
ロカプセルは、使用時の摩擦や圧迫等の外力によって破
壊されて香りを発散させるものであればその組成、構造
等は限定されないが、人体に接する製品に使用する場合
は皮膚刺激の少ない低ホルマリン系のものが好ましい。
マイクロカプセルの形状等も特に限定はされないが、粒
径が５〜２０μｍ、膜厚が０．３〜３０μｍ、香料の内
包率が３０〜８０重量％程度のものを利用することがで
きる。The fragrance-encapsulating microcapsules used in the present invention are not limited in composition, structure, etc. as long as they can be destroyed by external force such as friction and pressure during use and emit scent. When used, a low formalin type that causes less skin irritation is preferable.
The shape and the like of the microcapsules are not particularly limited, but those having a particle size of 5 to 20 μm, a film thickness of 0.3 to 30 μm, and a fragrance inclusion rate of about 30 to 80% by weight can be used.
【００１０】マイクロカプセルに内包される香料は、天
然香料および合成香料等の芳香性物質であればよく、液
状物質が好ましい。製品の用途によって香料内包マイク
ロカプセルの付着量は適宜変えられるが、０．３〜５g/
m2の範囲が好ましい。該マイクロカプセルの付着量が
０．３g/m2より少ない場合には芳香が少な過ぎるために
香りの持続性という面で不充分となりやすく、５g/m2を
超えて使用した場合には、香りが強過ぎて使用者に不快
感を与える可能性が出てくることと、コスト面でも不経
済であるため好ましくない。The fragrance contained in the microcapsules may be an aromatic substance such as a natural fragrance and a synthetic fragrance, and a liquid substance is preferable. The amount of the microcapsules containing the perfume can be appropriately changed depending on the use of the product, but 0.3 to 5 g /
A range of m 2 is preferred. The adhesion amount of the microcapsule tends to be insufficient in terms of fragrance durability because aroma is too small if less than 0.3 g / m 2, when used in excess of 5 g / m 2, the fragrance Is too strong and may cause discomfort to the user, and is uneconomical in terms of cost, which is not preferable.
【００１１】香料内包マイクロカプセルを付与するため
に必要な樹脂バインダーは、繊維加工に一般的に用いら
れている公知の樹脂を利用することができる。このよう
な樹脂バインダーとしては、酢酸ビニル系、アクリル
系、ウレタン系、シリコーン系およびゴム系ラテックス
もしくはエマルジョンが挙げられるが、本発明において
は汎用の酢酸ビニル系エマルジョン、アクリル系エマル
ジョンが、処方の簡便さおよび低コスト等の理由から好
ましく、その中でも低温架橋性のものが好ましく用いら
れる。As the resin binder necessary for providing the perfume-containing microcapsules, known resins generally used for fiber processing can be used. Examples of such a resin binder include vinyl acetate-based, acrylic-based, urethane-based, silicone-based, and rubber-based latexes or emulsions. In the present invention, general-purpose vinyl acetate-based emulsions and acrylic-based emulsions have a simple formulation. It is preferable because of its low cost and low cost, and among them, a low temperature crosslinkable one is preferably used.
【００１２】本発明における上記樹脂バインダーの使用
量は香料内包マイクロカプセルに対して重量比で６〜３
０倍が適している。樹脂バインダーの量がマイクロカプ
セルの量の６倍より少ない場合には、付香加工処理後の
樹脂層の厚みが少な過ぎて耐久性が悪く、３０倍より多
くなると樹脂層が厚過ぎてマイクロカプセルが破壊され
にくくなるので好ましくない。The amount of the above resin binder used in the present invention is 6 to 3 in weight ratio with respect to the perfume-containing microcapsules.
0 times is suitable. When the amount of the resin binder is less than 6 times the amount of the microcapsules, the resin layer after the perfuming process is too thin and the durability is poor. When the amount is more than 30 times, the resin layer is too thick and the microcapsules are too large. Is less likely to be destroyed, which is not preferable.
【００１３】前記香料内包マイクロカプセルは樹脂バイ
ンダー中に混合分散され（以下、樹脂バインダー中に香
料内包マイクロカプセルが混合されたものをカプセル含
有樹脂液と言う）、公知の方法によって立毛・パイル布
帛の基布あるいは裏面に塗工される。この時の付与量は
香料の種類、製品の用途等によって適宜決められる。カ
プセル含有樹脂液の使用量は、前記香料内包マイクロカ
プセルの適正使用量と上記樹脂バインダーの適性使用量
から明らかなように、２〜１５０g/m2が好ましく、さら
に好ましくは、５〜５０g/m2である。カプセル含有樹脂
液が１５０g/m2を超えると、芳香の発散性が低下するた
め好ましくない。The perfume-encapsulating microcapsules are mixed and dispersed in a resin binder (hereinafter, a mixture of the perfume-encapsulating microcapsules in the resin binder is referred to as a capsule-containing resin liquid), and a napped / pile fabric is formed by a known method. It is applied to the base cloth or the back surface. The applied amount at this time is appropriately determined depending on the kind of the fragrance, the use of the product, and the like. The amount of the capsule-containing resin liquid is, as is clear from the appropriate amount of the perfume-containing microcapsules and the appropriate amount of the resin binder, preferably 2 to 150 g / m 2 , more preferably 5 to 50 g / m 2. Is 2 . When the amount of the capsule-containing resin liquid exceeds 150 g / m 2 , it is not preferable because the fragrance emission is reduced.
【００１４】上記公知の塗工方法としては、パッディン
グ法、スプレイ法、プリント法、コーティング法、浸漬
脱水法等が挙げられるが、裏面を含むパイル面全体をカ
プセル含有樹脂液で加工するようなパッディング法や浸
漬脱水法は、表面の立毛・パイル部の繊維まで集束して
しまい、外観および風合いが著しく低下してしまうため
好ましくない。付香加工を起毛あるいはシャーリング工
程の前に行なった場合には、これらの工程中に香料内包
マイクロカプセルが大量に脱落するために好ましくな
い。Examples of the above-mentioned known coating methods include a padding method, a spray method, a printing method, a coating method, an immersion dehydration method, and the like. The entire pile surface including the back surface is processed with a resin solution containing capsules. The padding method and the immersion dehydration method are not preferable because the fibers on the naps and piles on the surface are also bundled and the appearance and texture are significantly deteriorated. If the perfuming process is performed before the raising or shirring process, a large amount of the perfume-containing microcapsules fall off during these processes, which is not preferable.
【００１５】従って、本発明において最も好ましい付香
加工方法は、プリント法、コーティング法、スプレイ法
のいずれかによって、立毛・パイル製品の基布あるいは
裏面にカプセル含有樹脂液を付着させる方法である。こ
の方法を用いれば、立毛・パイル製品の表面繊維の風合
い、外観はまったく変化せずに付香加工処理を行なうこ
とができる。また、織ボア、ニットボア、モケット、ハ
イパイル、編およびニット椅子張り地等の製品化の過程
でバッキング工程のあるものは、バッキング樹脂液中に
香料内包マイクロカプセルを混合し、従来通りの条件で
加工を行なうだけで付香することができる。Therefore, the most preferable perfuming processing method in the present invention is a method of adhering the capsule-containing resin liquid to the base cloth or the back surface of the napped / pile product by any one of the printing method, the coating method and the spray method. By using this method, the scenting process can be performed without changing the texture and appearance of the surface fibers of the napped / pile product. Also, woven bores, knit bores, moquettes, high piles, knits, and knit upholstery fabrics that have a backing process in the process of production are mixed with perfume-containing microcapsules in a backing resin liquid and processed under conventional conditions. You can perfume just by doing.
【００１６】マット類あるいはカーペット類のように多
量のゴム系ラテックス等でバッキングされる製品は、バ
ッキング樹脂層が厚過ぎて香料の発散が妨げられるた
め、バッキング処理工程の前に付香処理を行なって、香
料がマットあるいはカーペット表面の方へ発散しやすい
ようにすることが好ましい。Products such as mats and carpets that are backed with a large amount of rubber latex or the like have a backing resin layer that is too thick to prevent the perfume from being diffused. Therefore, a perfume treatment is performed before the backing treatment step. Therefore, it is preferable that the fragrance is easily diffused toward the mat or the carpet surface.
【００１７】[0017]
【発明の効果】香料を内包するマイクロカプセルを樹脂
バインダーと共に立毛・パイル製品の基布あるいは裏面
に付与する付香方法によって、立毛・パイル部分の外
観、風合い、肌ざわりを低下させることなく、香りの持
続性、徐放性、洗濯耐久性等に優れた立毛・パイル付香
製品を提供できた。[Effects of the Invention] By the perfuming method in which the microcapsules containing a fragrance are applied to the base fabric or the back surface of the napped / pile product together with the resin binder, the fragrance can be obtained without deteriorating the appearance, texture and texture of the napped / pile part. It was possible to provide a napped and piled scented product with excellent durability, sustained release, and washing durability.
【００１８】また香料内包マイクロカプセルを含有する
樹脂バインダー層は、立毛・パイル部分の根元付近に形
成されることから毛抜け、パイル抜けの防止および洗濯
時等の寸法安定性にも有用であった。The resin binder layer containing the perfume-containing microcapsules is formed near the roots of the naps and piles, and is therefore useful for preventing hair loss and pile loss, and for dimensional stability during washing and the like. ..
【００１９】[0019]
【実施例】以下に実施例を挙げて、本発明を具体的に説
明する。本発明はこれらの実施例に限定されるものでは
ない。実施例Ｂ〜Ｄおよび比較例Ａ アクリル 100％梳毛紡糸（メートル番手32番双糸、熱水
収縮率25.5％）を常法で綛染めし、ニットボア原反を作
成した。次に、松本油脂製薬製マイクロスフェア K−30
1(セル組成：ホルマリン重縮合系、香料：レモン系，80
％内包、粒径：5〜20μｍ、固形分濃度30重量％）を 1.
5重量％となるように水で希釈したものと、大日本イン
キ化学工業社製の樹脂ボンコート2835（酢酸ビニル系エ
マルジョン、固形分濃度50％）を、表１に示したような
配合比で混合し４種類のカプセル含有樹脂液を得た。各
濃度の水分散体をスプレイ法で100g/m2 塗布加工し、乾
燥、ベーキング（80〜 140℃×３分）処理を行なった。
その後に起毛、ポリッシャー、シャーリング工程を通
し、ニットボア付香処理製品を得た。EXAMPLES The present invention will be specifically described with reference to the following examples. The invention is not limited to these examples. Examples B to D and Comparative Example A A 100% acrylic worsted spinning yarn (metric number 32 twin yarn, hot water shrinkage rate 25.5%) was dyed by a conventional method to prepare a knit bore raw fabric. Next, Matsumoto Yushi-Seiyaku Microsphere K-30
1 (cell composition: formalin polycondensation system, fragrance: lemon system, 80
% Inclusion, particle size: 5-20 μm, solid content concentration 30% by weight) 1.
A mixture of 5% by weight diluted with water and Dainippon Ink and Chemicals Co., Ltd. resin Boncoat 2835 (vinyl acetate emulsion, solid content concentration 50%) was mixed at the mixing ratio shown in Table 1. Then, four types of capsule-containing resin liquids were obtained. The aqueous dispersion of each concentration was coated by a spray method at 100 g / m 2 , and dried and baked (80 to 140 ° C. × 3 minutes).
Then, a brushing, polishing, and shirring process was performed to obtain an aroma-treated product with a knit bore.
【００２０】得られたニットボア製品を洗濯し、洗濯前
後の香りを官能５段階評価（複数パネラーによるテス
ト）で判定し、洗濯耐久性をみた。なお、洗濯はJIS-L-
0217に準じて行なった。また、評価基準は最も香りの強
いものを５級、香りを感じないものを１級とし、パネラ
ーの評価平均値の最も近い等級を結果として表１に併記
した。The knit bore product obtained was washed, and the scent before and after washing was judged by a sensory five-level evaluation (test by a plurality of panelists) to check the washing durability. In addition, washing is JIS-L-
Performed according to 0217. In addition, as the evaluation criteria, the one with the strongest scent was grade 5, and the one without the scent was grade 1, and the grade closest to the average evaluation value of the panelists is also shown in Table 1 as a result.
【００２１】[0021]
【表１】 [Table 1]
【００２２】実施例Ｅ〜Ｆおよび比較例Ｇ〜Ｈ パイル糸として扁平断面アクリル繊維（日本エクスラン
工業製）を含むアクリル 100％紡績糸（メートル番手36
番双糸、熱水収縮率30％）を使用し、インレイ糸および
チェーン糸としてポリエステル繊維(100d ／24fil)を使
用して、カールマイヤー社製ダブルラッセル機を用いて
編立て（18Ｇ、釜間30mm、14.1c/in）、パイル糸をセン
ターカットした後、パッドスチーム染色機を用いて常法
で染色、柔軟加工を行なった。 Examples E to F and Comparative Examples G to H 100% acrylic spun yarn ( meal count 36) containing flat cross section acrylic fiber (manufactured by Japan Exlan Industrial Co., Ltd.) as pile yarn.
Weaving (18G, between the kettles) using a double Raschel machine made by KARL MAYER, using No. Futaba yarn, hot water shrinkage ratio 30%) and polyester fiber (100d / 24fil) as inlay yarn and chain yarn After 30 mm, 14.1 c / in) and the pile yarn were center cut, they were dyed and softened by a conventional method using a pad steam dyeing machine.
【００２３】この染色反に松本油脂製薬製マイクロスフ
ェア K−501(セル組成：ホルマリン重縮合系、香料：ラ
ベンダー系、80％内包、粒径： 5〜20μｍ、固形分濃度
30重量％）を 1.5重量％に水で希釈したものと、大日本
インキ化学工業社製の樹脂ボンコートR3020 （アクリル
系エマルジョン、固形分濃度50％）を、表２に示したよ
うな配合比でスプレイ法により付与し、常法の乾燥工程
（100 〜 150℃×２分）を通した後、ブラッシング、シ
ャーリング、ポリッシング処理を行ない、張り合せマイ
ヤー毛布を作成した。ここで、実施例Ｅおよび実施例Ｆ
は裏面側へ塗布し、比較例Ｇはパイル面へ塗布し、比較
例Ｈはカプセル含有樹脂液を塗布しなかった。実施例Ｂ
と同様に洗濯し、香りの洗濯耐久性および寸法安定性を
評価し、表２に併記した。寸法安定性は、洗濯１０回後
の１ｍ角のマイヤー毛布の縦および横の長さの収縮率
（％）を測定した。In addition to this dyeing, Matsumoto Yushi-Seiyaku Microsphere K-501 (cell composition: formalin polycondensation system, perfume: lavender system, 80% inclusion, particle size: 5 to 20 μm, solid content concentration)
(30% by weight) diluted with water to 1.5% by weight, and Dainippon Ink and Chemicals Co., Ltd. resin Boncoat R3020 (acrylic emulsion, solid content concentration 50%) at the compounding ratios shown in Table 2. After applying by a spray method and passing through a usual drying step (100 to 150 ° C. × 2 minutes), brushing, shirring and polishing treatments were performed to prepare a laminated Meyer blanket. Here, Example E and Example F
Was applied to the back side, Comparative Example G was applied to the pile surface, and Comparative Example H was not applied with the capsule-containing resin liquid. Example B
Washing was carried out in the same manner as above, the washing durability of the scent and the dimensional stability were evaluated, and the results are shown in Table 2. The dimensional stability was measured by measuring the shrinkage rate (%) in the length and width of a 1 m square Meyer blanket after washing 10 times.
【００２４】[0024]
【表２】 [Table 2]
【００２５】実施例Ｉ〜Ｊおよび比較例Ｋ〜Ｌ 実施例Ｅと同様にしてマイヤー毛布を作成した。ただ
し、表３に示した量のカプセル含有樹脂液を裏面へスプ
レイ法にて付香を行なった。実施例Ｂと同様にして洗濯
および香りの官能試験を行ない結果を表３に併記した。Meyer blankets were prepared in the same manner as in Examples I to J and Comparative Examples KL to Example E. However, the amount of the resin solution containing capsules shown in Table 3 was applied to the back surface by the spray method. The laundry and the scent sensory test were conducted in the same manner as in Example B, and the results are also shown in Table 3.
【００２６】[0026]
【表３】 [Table 3]
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０４Ｈ 11/08 7199−3Ｂ Ｄ０６Ｍ 23/12 7199−3Ｂ Ｄ０６Ｍ 21/00 Ｂ ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 5 Identification code Internal reference number FI Technical display location D04H 11/08 7199-3B D06M 23/12 7199-3B D06M 21/00 B
Claims (1)
なる立毛もしくはパイル布帛において、香料を内包する
マイクロカプセルを樹脂バインダーと共に前記基布にの
み付与し、前記樹脂バインダーの使用量を前記マイクロ
カプセルの６〜３０倍とし、樹脂バインダーとマイクロ
カプセルの総付与量を２〜１５０g/m2とすることを特徴
とする付香加工された立毛およびパイル製品。1. A napped or pile cloth comprising a napped portion or pile portion and a base cloth, wherein microcapsules containing a fragrance are applied together with the resin binder only to the base cloth, and the amount of the resin binder used is adjusted to A perfume-processed napped and pile product, which is 6 to 30 times and the total amount of the resin binder and the microcapsules applied is 2 to 150 g / m 2 .