JPH05339122A - Cosmetic - Google Patents
CosmeticInfo
- Publication number
- JPH05339122A JPH05339122A JP4150592A JP15059292A JPH05339122A JP H05339122 A JPH05339122 A JP H05339122A JP 4150592 A JP4150592 A JP 4150592A JP 15059292 A JP15059292 A JP 15059292A JP H05339122 A JPH05339122 A JP H05339122A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- powder
- base
- iron oxide
- coloring pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、ファンデーション、
お白い、パック、アイシャドー、アイライナー、マスカ
ラー、口紅、ほほ紅、ネイルエナメル、ノーズシャドー
などの化粧料に関する。This invention relates to a foundation,
Cosmetics such as white, pack, eye shadow, eyeliner, mascara, lipstick, blush, nail enamel and nose shadow.
【０００２】[0002]
【従来の技術】化粧料は、顔や手などに塗布して、肌色
を変えたり、色彩を部分的に強調したり、陰影をつけて
立体感をだしたり、しみ、そばかす、傷跡、白斑などの
肌の欠点を隠したりして魅力的な容貌を作りだすために
使用される。そのため、化粧料には、人体（肌）に安全
であること、経時的な変色や変臭、分離などが起こらな
いこと、光源の種類によって色が著しく変わって見えな
いこと、塗布後に違和感を感じないこと、化粧落としが
容易であることといったことに加え、滑沢性（滑りや伸
び）がよくて塗布時の感触がソフトであること、肌への
付着力がよいこと、適度なカバー力（隠ぺい力）を有す
ることが要求され、これらの要求を満たすために各種の
成分を配合している。2. Description of the Related Art Cosmetics are applied to the face or hands to change the skin color, partially enhance the color, add a shade to give a three-dimensional effect, stains, freckles, scars, white spots, etc. It is used to hide the imperfections of the skin and create an attractive appearance. Therefore, cosmetics should be safe for the human body (skin), should not be discolored or discolored over time, should not be separated, should the color change significantly depending on the type of light source, and should not be seen. In addition to having no makeup and easy makeup removal, it has good lubricity (sliding and spreading) and a soft feel when applied, good adhesion to the skin, and moderate covering power ( It is required to have hiding power, and various components are blended to meet these requirements.
【０００３】すなわち、使用時に滑らかに拡がり、ソフ
トな感触を与えるために、タルク、マイカ、カオリンの
粉末や、合成樹脂の粉末、たとえばナイロン粉末やポリ
エチレン粉末などが配合されている。しかしながら、タ
ルクやマイカ、カオリンの粉末は、ソフトな使用感を与
えるものの隠ぺい力が小さい。また、合成樹脂の粉末
は、肌への付着力が弱い。一方、肌の欠点を隠すため
に、二酸化チタンや酸化亜鉛の粉末などが多用されてい
るが、これらは伸びを悪くするし、触媒活性を有するた
めに、他の配合成分、たとえば香料やオイルを変質させ
たり劣化させたりしやすい。結局、従来の化粧料は、い
ずれも、滑沢性と、付着力と、カバー力との総合評価に
おいて劣る。That is, powders of talc, mica, kaolin, and synthetic resin powders such as nylon powder and polyethylene powder are blended in order to spread smoothly and give a soft feel when used. However, powders of talc, mica, and kaolin give a soft feeling of use but have a small hiding power. Further, the synthetic resin powder has a weak adhesion to the skin. On the other hand, titanium dioxide and zinc oxide powders are often used to hide skin defects, but these compounds slow the elongation and have catalytic activity, so other compounding ingredients such as fragrances and oils may be added. Easy to change or deteriorate. After all, all the conventional cosmetics are inferior in the comprehensive evaluation of lubricity, adhesiveness and covering power.
【０００４】[0004]
【発明が解決しようとする課題】この発明の目的は、従
来の化粧料の上述した問題点を解決し、滑沢性と、付着
力と、カバー力との総合評価において優れた化粧料を提
供するにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems of conventional cosmetics and to provide a cosmetic excellent in comprehensive evaluation of lubricity, adhesiveness and covering power. There is
【０００５】[0005]
【課題を解決するための手段】上記目的を達成するため
に、この発明は、酸化カルシウムと、酸化チタニウムお
よび酸化ジルコニウムから選ばれた少なくとも１種との
複合体の粒子からなる粉末を配合してなる化粧料を提供
する。粉末の平均粒子径は、好ましくは０．０５〜１５
μｍの範囲にある。In order to achieve the above object, the present invention blends a powder comprising particles of a complex of calcium oxide and at least one selected from titanium oxide and zirconium oxide. Provide cosmetics. The average particle size of the powder is preferably 0.05 to 15
It is in the range of μm.
【０００６】この発明の化粧料は、粉末状、液状、ケー
ク状、ペンシル状、スティック状、クリーム状、ペース
ト状、ゼリー状、ゾル状など、いずれであってもよい。
化粧料の種類による。The cosmetic material of the present invention may be in the form of powder, liquid, cake, pencil, stick, cream, paste, jelly or sol.
Depends on the type of cosmetic.
【０００７】この発明において、１個の粒子は、単一の
成分からなるのではなく、酸化カルシウムと、酸化チタ
ニウムおよび／または酸化ジルコニウムとが化学的に結
合していたり、固溶していたりするものである。In the present invention, one particle does not consist of a single component, but calcium oxide and titanium oxide and / or zirconium oxide are chemically bonded or are in solid solution. It is a thing.
【０００８】化学的に結合しているものの例としては、
ＣａＴｉＯ3 、Ｃａ2 Ｔｉ5 Ｏ12、Ｃａ4 Ｔｉ3 Ｏ10、
Ｃａ3 Ｔｉ2 Ｏ7 、ＣａＴｉ2 Ｏ5 、ＣａＴｉ4 Ｏ9 、
ＣａＴｉ2 Ｏ4 、ＣａＺｒＯ3 、Ｃａ6 Ｚｒ19Ｏ44、Ｃ
ａＺｒ4 Ｏ9 、Ｃａ0.15Ｚｒ0.85Ｏ1.85、ＣａＺｒＴｉ
2 Ｏ7 、ＣａＴｉＺｒ3 Ｏ9 、（Ｚｒ，Ｃａ，Ｔｉ）Ｏ
2 がある。これらは、１個の粒子内に、単独で存在して
いても、共存していてもよい。また、これらのほかに、
固溶体が共存していたり、酸化カルシウム、酸化チタニ
ウムおよび／または酸化ジルコニウムが共存している場
合もある。なお、化合物や固溶体、酸化カルシウム、酸
化チタニウム、酸化ジルコニウムは、結晶質であっても
よく、非晶質であってもよい。また、含水物や水和物の
形態であってもよい。Examples of chemically bound substances are:
CaTiO 3 , Ca 2 Ti 5 O 12 , Ca 4 Ti 3 O 10 ,
Ca 3 Ti 2 O 7 , CaTi 2 O 5 , CaTi 4 O 9 ,
CaTi 2 O 4 , CaZrO 3 , Ca 6 Zr 19 O 44 , C
aZr 4 O 9 , Ca 0.15 Zr 0.85 O 1.85 , CaZrTi
2 O 7 , CaTiZr 3 O 9 , (Zr, Ca, Ti) O
There are two . These may exist alone or may coexist in one particle. In addition to these,
A solid solution may coexist, or calcium oxide, titanium oxide and / or zirconium oxide may coexist. The compound, solid solution, calcium oxide, titanium oxide, and zirconium oxide may be crystalline or amorphous. Further, it may be in the form of a hydrate or a hydrate.
【０００９】そのような複合体の粒子からなる粉末は、
平均粒子径が０．０５〜１５μｍの範囲にあり、かつ、
粒子は好ましくは等軸形状をしている。すなわち、平均
粒子径が０．０５μｍ未満であるときは、比表面積が大
きすぎて塗布時の滑沢性が悪くなり、使用感が重くな
る。また、１５μｍを超えると、肌に対する付着力が弱
まり、脱落したり、そうでなくても塗布時のざらつき感
が大きくなる。結局、滑沢性と付着性の双方を満足させ
るためには、平均粒子径が０．０５〜１５μｍの範囲に
あるのが好ましい。化粧料の種類にもよるが、より好ま
しい平均粒子径の範囲は０．１〜０．８μｍ、さらに好
ましい範囲は０．３〜０．５μｍである。なお、等軸形
状とは、粒子の顕微鏡写真をみたとき、粒子の輪郭に接
する２本の平行線間の距離ａと、それと直交する方向の
輪郭に接し、かつ、間隔が最も大きい２本の平行線間の
距離ｂとの比ａ／ｂが０．５〜１．０、好ましくは０．
８〜１．０の範囲にあるということである。等軸形状で
ないときは、粒子の種類や化粧料の種類にもよるが、滑
沢性が不十分になることがある。A powder consisting of particles of such a composite is
The average particle size is in the range of 0.05 to 15 μm, and
The particles are preferably equiaxed in shape. That is, when the average particle diameter is less than 0.05 μm, the specific surface area is too large and the lubricity at the time of application is deteriorated, resulting in a heavy feeling of use. On the other hand, if it exceeds 15 μm, the adhesive force to the skin is weakened, and it may fall off, or if not so, the feeling of roughness during application becomes large. After all, in order to satisfy both the lubricity and the adhesiveness, the average particle size is preferably in the range of 0.05 to 15 μm. Depending on the type of cosmetics, a more preferable range of average particle diameter is 0.1 to 0.8 μm, and a further preferable range is 0.3 to 0.5 μm. The equiaxed shape means that when a microscopic photograph of a particle is viewed, the distance a between two parallel lines in contact with the contour of the particle and the two parallel lines that are in contact with the contour in the direction orthogonal thereto and have the largest interval The ratio a / b to the distance b between parallel lines is 0.5 to 1.0, preferably 0.
It is in the range of 8 to 1.0. When the shape is not equiaxed, lubricity may be insufficient depending on the type of particles and the type of cosmetics.
【００１０】上記の粉末は、化粧料の種類にもよるが、
好ましくは、０．１〜９９重量％の範囲で配合される。
０．１重量％未満では、滑沢性と、付着力と、カバー力
に関して十分に大きな効果が得られないことがある。ま
た、９９重量％を超えて配合すると、たとえばスティッ
クに成型するときの成型性が悪くなる。The above powder depends on the kind of cosmetics,
Preferably, it is blended in the range of 0.1 to 99% by weight.
If it is less than 0.1% by weight, a sufficiently large effect may not be obtained with respect to lubricity, adhesive force and covering force. Further, if it is blended in an amount of more than 99% by weight, the moldability at the time of molding into a stick becomes poor.
【００１１】このように、この発明の化粧料において
は、酸化カルシウムと、酸化チタニウムおよび酸化ジル
コニウムから選ばれた少なくとも１種との複合体の粒子
からなる粉末が配合されていることを必須とするが、そ
れ以外に、化粧料において通常使用されている、たとえ
ば、黄酸化鉄、黒酸化鉄、ベンガラ、雲母などの顔料
や、アニスオイル、アセトフェノン、ベンジルアルコー
ルなどの香料や、ポリビニルアルコールなどの可塑剤
や、ジブチルヒドロキシトルエンなどの酸化防止剤や、
ヒノキチオール、チモールなどの防腐剤や、ミリスチン
酸オクシルドデシル、セスキオレイン酸ソルビタンなど
の界面活性剤や、プロピレングリコール、グリセリンな
どの保湿剤やヒドロキシエチルセルロース、ペクチンな
どの増粘剤や、水やアルコールなどの他の成分が配合さ
れることはいうまでもない。As described above, in the cosmetic of the present invention, it is essential that the powder comprising the particles of the complex of calcium oxide and at least one selected from titanium oxide and zirconium oxide is blended. However, other than that, it is usually used in cosmetics, for example, pigments such as yellow iron oxide, black iron oxide, red iron oxide, mica, fragrances such as anise oil, acetophenone and benzyl alcohol, and plasticizers such as polyvinyl alcohol. Agents, antioxidants such as dibutylhydroxytoluene,
Preservatives such as hinokitiol and thymol, surfactants such as octyldodecyl myristate and sorbitan sesquioleate, moisturizers such as propylene glycol and glycerin, thickeners such as hydroxyethyl cellulose and pectin, water and alcohols, etc. It goes without saying that the other components are mixed.
【００１２】この発明の化粧料は、化粧料の種類に応じ
て通常採られている方法によって製造することができ
る。The cosmetic of the present invention can be produced by a method usually adopted depending on the type of cosmetic.
【００１３】[0013]
実施例１（パウダーファンデーション） 処方： チタン酸ジルコン酸カルシウム粉末 ８２．０重量％ （ＣａＺｒＴｉ2 Ｏ7 、平均粒子径：０．４μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ３．０重量％ 黄酸化鉄粉末（着色顔料） ２．５重量％ 黒酸化鉄粉末（着色顔料） ０．５重量％ 流動パラフィン（基剤） ６．０重量％ ミリスチン酸オクシルドデシル（基剤） ２．５重量％ ワセリン（基剤） ３．５重量％ アセトフェノン（香料） 微量 製造法：チタン酸ジルコン酸カルシウム粉末と着色顔料
とを混合しながら、基材と香料との混合物を添加し、粉
砕し、圧縮成型してパウダーファンデーションを得た。Example 1 (powder foundation) Formulation: calcium zirconate titanate powder 82.0% by weight (CaZrTi 2 O 7 , average particle size: 0.4 μm, a / b: 0.9) Red iron oxide powder (coloring pigment) 3. 0% by weight Yellow iron oxide powder (coloring pigment) 2.5% by weight Black iron oxide powder (coloring pigment) 0.5% by weight Liquid paraffin (base) 6.0% by weight Octyldodecyl myristate (base) 2 0.5 wt% Vaseline (base) 3.5 wt% acetophenone (fragrance) Trace amount Production method: While mixing calcium zirconate titanate powder and a coloring pigment, a mixture of a base material and a flavor is added and ground. Then, compression molding was performed to obtain a powder foundation.
【００１４】比較例１（パウダーファンデーション） 実施例１において、チタン酸ジルコン酸カルシウム粉末
を、酸化チタン粉末１５．０重量％、ナイロン粉末１
５．０重量％、マイカ粉末２０重量％、タルク粉末３
２．０重量％に置き換え、同様にパウダーファンデーシ
ョンを得た。Comparative Example 1 (Powder Foundation) In Example 1, calcium zirconate titanate powder, titanium oxide powder 15.0% by weight, nylon powder 1
5.0 wt%, mica powder 20 wt%, talc powder 3
It was replaced with 2.0% by weight to obtain a powder foundation in the same manner.
【００１５】実施例２（スティック型ファンデーショ
ン） 処方： チタン酸ジルコン酸カルシウム粉末 ３５．０重量％ （ＣａＺｒＴｉ2 Ｏ7 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ５．０重量％ 黄酸化鉄粉末（着色顔料） ３．０重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 流動パラフィン（基剤） １６．０重量％ ミリスチン酸イソプロピル（基剤） １５．０重量％ 液状ラノリン（基剤） ５．５重量％ マイクロクリスタリンワックス（基剤） ５．５重量％ セレシン（基剤） １０．０重量％ カルナウバロウ（基剤） ２．０重量％ セスキオレイン酸ソルビタン（基剤） １．０重量％ アセトフェノン（香料） 微量 製造法：基剤を混合し、７５℃で加熱、融解した後、チ
タン酸ジルコン酸カルシウム粉末と着色顔料とを加え、
ロールミルで混練し、溶かし、脱泡し、さらに香料を加
えて容器に流し込み、冷却してスティック型ファンデー
ションを得た。Example 2 (stick type foundation) Formulation: calcium zirconate titanate powder 35.0% by weight (CaZrTi 2 O 7 , average particle size: 0.3 μm, a / b: 0.9) Bengal powder (colored Pigment) 5.0% by weight Yellow iron oxide powder (coloring pigment) 3.0% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Liquid paraffin (base) 16.0% by weight Isopropyl myristate (base) ) 15.0% by weight liquid lanolin (base) 5.5% by weight microcrystalline wax (base) 5.5% by weight ceresin (base) 10.0% by weight carnauba wax (base) 2.0% by weight sesqui Sorbitan oleate (base) 1.0% by weight acetophenone (fragrance) Trace amount Production method: Mix bases, heat at 75 ° C, melt, and then calcium zirconate titanate End and a coloring pigment added,
The mixture was kneaded with a roll mill, melted, defoamed, further added a fragrance, poured into a container, and cooled to obtain a stick type foundation.
【００１６】比較例２（スティック型ファンデーショ
ン） 実施例２において、チタン酸ジルコン酸カルシウム粉末
を、酸化チタン粉末１５．０重量％、カオリン粉末１
５．０重量％、タルク粉末５．０重量％に置き換え、同
様にスティック型ファンデーション得た。Comparative Example 2 (stick type foundation) In Example 2, calcium titanate zirconate powder was used, titanium oxide powder 15.0% by weight, and kaolin powder 1
Substituting 5.0% by weight and 5.0% by weight of talc powder, a stick type foundation was similarly obtained.
【００１７】実施例３（クリーム状ファンデーション） 処方： チタン酸ジルコン酸カルシウム粉末 １５．０重量％ （ＣａＺｒＴｉ2 Ｏ7 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） １．０重量％ 黄酸化鉄粉末（着色顔料） ０．８重量％ 黒酸化鉄粉末（着色顔料） ０．２重量％ ミリスチン酸イソプロピル（油相基剤） ７．８重量％ 流動パラフィン（油相基剤） ７．０重量％ モノラウリン酸プロピレングリコール（油相基剤） ３．０重量％ 親油性モノステアリン酸グリセリン（油相基剤） ２．５重量％ ステアリン酸（油相基剤） ５．０重量％ セトステアリルアルコール（油相基剤） １．０重量％ パラオキシ安息香酸ブチル（油相基剤） ０．２重量％ 精製水（水相基剤） ５２．１重量％ トリエタノールアミン（水相基剤） １．２重量％ ソルビット（水相基剤） ３．０重量％ パラオキシ安息香酸メチル（水相基剤） ０．２重量％ アセトフェノン（香料） 微量 製造法：水相基剤の混合物を調製し、これにチタン酸ジ
ルコン酸カルシウム粉末と着色顔料との混合物を加えて
分散させた。一方、油相基剤の混合物を調製し、これを
８０℃に保って撹拌しながら、７５℃に保った水相基剤
の混合物に加え、乳化し、冷却しながら、５０℃で香料
を加え、さらに撹拌しながら冷却し、クリーム状ファン
デーションを得た。Example 3 (Cream Foundation) Formulation: Calcium zirconate titanate powder 15.0% by weight (CaZrTi 2 O 7 , average particle size: 0.3 μm, a / b: 0.9) Bengal powder (colored Pigment) 1.0% by weight Yellow iron oxide powder (coloring pigment) 0.8% by weight Black iron oxide powder (coloring pigment) 0.2% by weight Isopropyl myristate (oil phase base) 7.8% by weight Liquid paraffin ( Oil phase base) 7.0 wt% Propylene glycol monolaurate (oil phase base) 3.0 wt% Lipophilic glyceryl monostearate (oil phase base) 2.5 wt% Stearic acid (oil phase base) 5.0 wt% cetostearyl alcohol (oil phase base) 1.0 wt% Butyl paraoxybenzoate (oil phase base) 0.2 wt% Purified water (water phase base) 52.1 wt% Triethanol Amine (water phase base) 1.2% by weight Sorbit (water phase base) 3.0% by weight Methyl paraoxybenzoate (water phase base) 0.2% by weight Acetophenone (fragrance) Trace amount Production method: water phase base A mixture of agents was prepared, and a mixture of calcium zirconate titanate powder and a coloring pigment was added to and dispersed in the mixture. On the other hand, a mixture of an oil phase base was prepared and added to a mixture of an aqueous phase base kept at 75 ° C. while maintaining the mixture at 80 ° C. with stirring, emulsifying and cooling, and a fragrance was added at 50 ° C. Then, it was further cooled with stirring to obtain a creamy foundation.
【００１８】比較例３（クリーム状ファンデーション） 実施例３において、チタン酸ジルコン酸カルシウム粉末
を、酸化チタン粉末８．０重量％、カオリン粉末４．０
重量％、タルク粉末３．０重量％に置き換え、同様にク
リーム状ファンデーションを得た。Comparative Example 3 (Cream Foundation) In Example 3, the calcium zirconate titanate powder was used in an amount of 8.0% by weight of titanium oxide powder and 4.0 kaolin powder.
%, And 3.0% by weight of talc powder were replaced to obtain a creamy foundation in the same manner.
【００１９】実施例４（粉お白い） 処方： チタン酸ジルコン酸カルシウム粉末 ８０．０重量％ （ＣａＺｒＴｉ2 Ｏ7 、平均粒子径：０．４μｍ、ａ／ｂ：０．８５） ベンガラ粉末（着色顔料） ４．５重量％ 黄酸化鉄粉末（着色顔料） ３．５重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 沈降炭酸カルシウム粉末（顔料） ５．０重量％ ステアリン酸マグネシウム粉末（顔料） ５．０重量％ アセトフェノン（香料） 微量 製造法：チタン酸ジルコン酸カルシウム粉末と着色顔料
とを混合し、さらに顔料を加えて混合した後、香料を噴
霧し、さらに混合し、粉砕し、２００メッシュのふるい
にかけて粉お白いを得た。Example 4 (white powder) Formulation: Calcium zirconate titanate powder 80.0% by weight (CaZrTi 2 O 7 , average particle diameter: 0.4 μm, a / b: 0.85) Bengal powder (colored Pigment) 4.5% by weight Yellow iron oxide powder (coloring pigment) 3.5% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Precipitated calcium carbonate powder (pigment) 5.0% by weight Magnesium stearate powder ( Pigment) 5.0% by weight acetophenone (fragrance) Trace amount Production method: Calcium zirconate titanate powder and a coloring pigment are mixed, and then a pigment is further added and mixed, and then a fragrance is sprayed, further mixed, and ground, A 200-mesh sieve was used to obtain a white powder.
【００２０】比較例４（粉お白い） 実施例４において、チタン酸ジルコン酸カルシウム粉末
を、タルク粉末５５．０重量％、カオリン粉末１５．０
重量％、酸化亜鉛粉末１０．０重量％に置き換え、同様
に粉お白いを得た。Comparative Example 4 (powder white) In Example 4, 55.0% by weight of calcium titanate zirconate powder, talc powder, and 15.0 kaolin powder.
% By weight and 10.0% by weight of zinc oxide powder were replaced to obtain a white powder in the same manner.
【００２１】実施例５（パウダーファンデーション） 処方： チタン酸カルシウム粉末 ８２．０重量％ （ＣａＴｉＯ3 、平均粒子径：０．４μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ３．０重量％ 黄酸化鉄粉末（着色顔料） ２．５重量％ 黒酸化鉄粉末（着色顔料） ０．５重量％ 流動パラフィン（基剤） ６．０重量％ ミリスチン酸オクシルドデシル（基剤） ２．５重量％ ワセリン（基剤） ３．５重量％ アセトフェノン（香料） 微量 製造法：チタン酸カルシウム粉末と着色顔料とを混合し
ながら、基材と香料との混合物を添加し、粉砕し、圧縮
成型してパウダーファンデーションを得た。Example 5 (Powder foundation) Formulation: Calcium titanate powder 82.0% by weight (CaTiO 3 , average particle size: 0.4 μm, a / b: 0.9) Red iron oxide powder (coloring pigment) 3.0 Weight% Yellow iron oxide powder (coloring pigment) 2.5% by weight Black iron oxide powder (coloring pigment) 0.5% by weight Liquid paraffin (base) 6.0% by weight Octyldodecyl myristate (base) 2. 5 wt% Vaseline (base) 3.5 wt% acetophenone (fragrance) Trace amount Production method: While mixing calcium titanate powder and a coloring pigment, a mixture of a base material and a fragrance is added, crushed, and compression molded. Then, a powder foundation was obtained.
【００２２】比較例５（パウダーファンデーション） 実施例５において、チタン酸カルシウム粉末を、酸化チ
タン粉末１５．０重量％、ナイロン粉末１５．０重量
％、マイカ粉末２０重量％、タルク粉末３２．０重量％
に置き換え、同様にパウダーファンデーションを得た。Comparative Example 5 (Powder Foundation) In Example 5, calcium titanate powder was used in an amount of 15.0% by weight of titanium oxide powder, 15.0% by weight of nylon powder, 20% by weight of mica powder and 32.0% by weight of talc powder. %
To obtain a powder foundation in the same manner.
【００２３】実施例６（スティック型ファンデーショ
ン） 処方： チタン酸カルシウム粉末 ３５．０重量％ （ＣａＴｉＯ3 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ５．０重量％ 黄酸化鉄粉末（着色顔料） ３．０重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 流動パラフィン（基剤） １６．０重量％ ミリスチン酸イソプロピル（基剤） １５．０重量％ 液状ラノリン（基剤） ５．５重量％ マイクロクリスタリンワックス（基剤） ５．５重量％ セレシン（基剤） １０．０重量％ カルナウバロウ（基剤） ２．０重量％ セスキオレイン酸ソルビタン（基剤） １．０重量％ アセトフェノン（香料） 微量 製造法：基剤を混合し、７５℃で加熱、融解した後、チ
タン酸カルシウム粉末と着色顔料とを加え、ロールミル
で混練し、溶かし、脱泡し、さらに香料を加えて容器に
流し込み、冷却してスティック型ファンデーションを得
た。Example 6 (stick type foundation) Formulation: calcium titanate powder 35.0% by weight (CaTiO 3 , average particle diameter: 0.3 μm, a / b: 0.9) red iron oxide powder (color pigment) 5. 0% by weight Yellow iron oxide powder (coloring pigment) 3.0% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Liquid paraffin (base) 16.0% by weight Isopropyl myristate (base) 15.0 Weight% Liquid lanolin (base) 5.5 weight% Microcrystalline wax (base) 5.5 weight% Ceresin (base) 10.0 weight% Carnauba wax (base) 2.0 weight% Sorbitan sesquioleate ( Base) 1.0 wt% acetophenone (fragrance) Trace amount Production method: After mixing the base, heating at 75 ° C. and melting, calcium titanate powder and color pigment are added, and Kneaded by a mill, dissolved, degassed, further poured into the container by adding a perfume, to obtain a stick-type foundation was cooled.
【００２４】比較例６（スティック型ファンデーショ
ン） 実施例６において、チタン酸カルシウム粉末を、酸化チ
タン粉末１５．０重量％、カオリン粉末１５．０重量
％、タルク粉末５．０重量％に置き換え、同様にスティ
ック型ファンデーションを得た。Comparative Example 6 (stick-type foundation) In Example 6, the calcium titanate powder was replaced with 15.0% by weight of titanium oxide powder, 15.0% by weight of kaolin powder, and 5.0% by weight of talc powder, and the same as above. A stick type foundation was obtained.
【００２５】実施例７（クリーム状ファンデーション） 処方： チタン酸カルシウム粉末 １５．０重量％ （ＣａＴｉＯ3 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） １．０重量％ 黄酸化鉄粉末（着色顔料） ０．８重量％ 黒酸化鉄粉末（着色顔料） ０．２重量％ ミリスチン酸イソプロピル（油相基剤） ７．８重量％ 流動パラフィン（油相基剤） ７．０重量％ モノラウリン酸プロピレングリコール（油相基剤） ３．０重量％ 親油性モノステアリン酸グリセリン（油相基剤） ２．５重量％ ステアリン酸（油相基剤） ５．０重量％ セトステアリルアルコール（油相基剤） １．０重量％ パラオキシ安息香酸ブチル（油相基剤） ０．２重量％ 精製水（水相基剤） ５２．１重量％ トリエタノールアミン（水相基剤） １．２重量％ ソルビット（水相基剤） ３．０重量％ パラオキシ安息香酸メチル（水相基剤） ０．２重量％ アセトフェノン（香料） 微量 製造法：水相基剤の混合物を調製し、これにチタン酸カ
ルシウム粉末と着色顔料との混合物を加えて分散させ
た。一方、油相基剤の混合物を調製し、これを８０℃に
保って撹拌しながら、７５℃に保った水相基剤の混合物
に加え、乳化し、冷却しながら、５０℃で香料を加え、
さらに撹拌しながら冷却し、クリーム状ファンデーショ
ンを得た。Example 7 (Cream Foundation) Formulation: Calcium titanate powder 15.0% by weight (CaTiO 3 , average particle size: 0.3 μm, a / b: 0.9) Red iron oxide powder (coloring pigment) 1. 0% by weight Yellow iron oxide powder (coloring pigment) 0.8% by weight Black iron oxide powder (coloring pigment) 0.2% by weight Isopropyl myristate (oil phase base) 7.8% by weight Liquid paraffin (oil phase base) ) 7.0 wt% Propylene glycol monolaurate (oil phase base) 3.0 wt% Lipophilic glyceryl monostearate (oil phase base) 2.5 wt% Stearic acid (oil phase base) 5.0 wt% % Cetostearyl alcohol (oil phase base) 1.0% by weight Butyl paraoxybenzoate (oil phase base) 0.2% by weight Purified water (water phase base) 52.1% by weight Triethanolamine (water phase base) ) 1.2% by weight sorbit (aqueous phase base) 3.0% by weight methyl paraoxybenzoate (aqueous phase base) 0.2% by weight acetophenone (perfume) Trace amount Production method: A mixture of aqueous phase bases is prepared. Then, a mixture of calcium titanate powder and a coloring pigment was added to and dispersed therein. On the other hand, a mixture of an oil phase base was prepared and added to a mixture of an aqueous phase base kept at 75 ° C. while maintaining the mixture at 80 ° C. with stirring, emulsifying and cooling, and a fragrance was added at 50 ° C. ,
Further, the mixture was cooled with stirring to obtain a creamy foundation.
【００２６】比較例７（クリーム状ファンデーション） 実施例７において、チタン酸カルシウム粉末を、酸化チ
タン粉末８．０重量％、カオリン粉末４．０重量％、タ
ルク粉末３．０重量％に置き換え、同様にクリーム状フ
ァンデーションを得た。Comparative Example 7 (Cream Foundation) In Example 7, the calcium titanate powder was replaced with 8.0% by weight of titanium oxide powder, 4.0% by weight of kaolin powder, and 3.0% by weight of talc powder. A creamy foundation was obtained.
【００２７】実施例８（粉お白い） 処方： チタン酸カルシウム粉末 ８０．０重量％ （ＣａＴｉＯ3 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ４．５重量％ 黄酸化鉄粉末（着色顔料） ３．５重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 沈降炭酸カルシウム粉末（基剤） ５．０重量％ ステアリン酸マグネシウム粉末（基剤） ５．０重量％ アセトフェノン（香料） 微量 製造法：チタン酸カルシウム粉末と着色顔料とを混合
し、さらに顔料を加えて混合した後、香料を噴霧し、さ
らに混合し、粉砕し、２００メッシュのふるいにかけて
粉お白いを得た。Example 8 (white powder) Formulation: calcium titanate powder 80.0% by weight (CaTiO 3 , average particle size: 0.3 μm, a / b: 0.9) red iron oxide powder (color pigment) 4. 5% by weight Yellow iron oxide powder (coloring pigment) 3.5% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Precipitated calcium carbonate powder (base) 5.0% by weight Magnesium stearate powder (base) 5.0% by weight acetophenone (perfume) Trace amount Production method: Calcium titanate powder and color pigment are mixed, and then pigment is added and mixed, then perfume is sprayed, further mixed, pulverized, and sieved with 200 mesh I got white powder.
【００２８】比較例８（粉お白い） 実施例８において、チタン酸カルシウム粉末を、タルク
粉末５５．０重量％、カオリン粉末１５．０重量％、酸
化亜鉛粉末１０．０重量％に置き換え、同様に粉お白い
を得た。Comparative Example 8 (white powder) In Example 8, the calcium titanate powder was replaced with 55.0% by weight of talc powder, 15.0% by weight of kaolin powder and 10.0% by weight of zinc oxide powder, and Got white powder.
【００２９】実施例９（パウダーファンデーション） 処方： ジルコン酸カルシウム粉末 ８２．０重量％ （ＣａＺｒＯ3 、平均粒子径：０．４μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ３．０重量％ 黄酸化鉄粉末（着色顔料） ２．５重量％ 黒酸化鉄粉末（着色顔料） ０．５重量％ 流動パラフィン（基剤） ６．０重量％ ミリスチン酸オクシルドデシル（基剤） ２．５重量％ ワセリン（基剤） ３．５重量％ アセトフェノン（香料） 微量 製造法：ジルコン酸カルシウム粉末と着色顔料とを混合
しながら、基材と香料との混合物を添加し、粉砕し、圧
縮成型してパウダーファンデーションを得た。 比較例９（パウダーファンデーション） 実施例９において、ジルコン酸カルシウム粉末を、酸化
チタン粉末１５．０重量％、ナイロン粉末１５．０重量
％、マイカ粉末２０重量％、タルク粉末３２．０重量％
に置き換え、同様にパウダーファンデーションを得た。Example 9 (Powder foundation) Formulation: Calcium zirconate powder 82.0% by weight (CaZrO 3 , average particle size: 0.4 μm, a / b: 0.9) Red iron oxide powder (coloring pigment) 3.0 Weight% Yellow iron oxide powder (coloring pigment) 2.5% by weight Black iron oxide powder (coloring pigment) 0.5% by weight Liquid paraffin (base) 6.0% by weight Octyldodecyl myristate (base) 2. 5% by weight Vaseline (base) 3.5% by weight Acetophenone (fragrance) Trace amount Production method: While mixing calcium zirconate powder and a coloring pigment, a mixture of a base material and a flavor is added, crushed, and compression molded. Then, a powder foundation was obtained. Comparative Example 9 (Powder Foundation) In Example 9, the calcium zirconate powder was replaced with titanium oxide powder 15.0% by weight, nylon powder 15.0% by weight, mica powder 20% by weight, talc powder 32.0% by weight.
To obtain a powder foundation in the same manner.
【００３０】実施例１０（スティック型ファンデーショ
ン） 処方： ジルコン酸カルシウム粉末 ３５．０重量％ （ＣａＺｒＯ3 、平均粒子径：０．４μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） ５．０重量％ 黄酸化鉄粉末（着色顔料） ３．０重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 流動パラフィン（基剤） １６．０重量％ ミリスチン酸イソプロピル（基剤） １５．０重量％ 液状ラノリン（基剤） ５．５重量％ マイクロクリスタリンワックス（基剤） ５．５重量％ セレシン（基剤） １０．０重量％ カルナウバロウ（基剤） ２．０重量％ セスキオレイン酸ソルビタン（基剤） １．０重量％ アセトフェノン（基剤） 微量 製造法：基剤を混合し、７５℃で加熱、融解した後、チ
タン酸ジルコン酸カルシウム粉末と着色顔料とを加え、
ロールミルで混練し、溶かし、脱泡し、さらに香料を加
えて容器に流し込み、冷却してスティック型ファンデー
ションを得た。Example 10 (stick type foundation) Formulation: calcium zirconate powder 35.0% by weight (CaZrO 3 , average particle size: 0.4 μm, a / b: 0.9) Red iron oxide powder (coloring pigment) 5. 0% by weight Yellow iron oxide powder (coloring pigment) 3.0% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Liquid paraffin (base) 16.0% by weight Isopropyl myristate (base) 15.0 Weight% Liquid lanolin (base) 5.5 weight% Microcrystalline wax (base) 5.5 weight% Ceresin (base) 10.0 weight% Carnauba wax (base) 2.0 weight% Sorbitan sesquioleate ( Base) 1.0 wt% acetophenone (base) Trace amount Production method: Mix bases, heat at 75 ° C., melt, and then use calcium zirconate titanate powder and colored face Doo added,
The mixture was kneaded with a roll mill, melted, defoamed, further added a fragrance, poured into a container, and cooled to obtain a stick type foundation.
【００３１】比較例１０（スティック型ファンデーショ
ン） 実施例１０において、ジルコン酸カルシウム粉末を、酸
化チタン粉末１５．０重量％、カオリン粉末１５．０重
量％、タルク粉末５．０重量％に置き換え、同様にステ
ィック型ファンデーションを得た。Comparative Example 10 (stick type foundation) In Example 10, the calcium zirconate powder was replaced with 15.0% by weight of titanium oxide powder, 15.0% by weight of kaolin powder, and 5.0% by weight of talc powder, and A stick type foundation was obtained.
【００３２】実施例１１（クリーム状ファンデーショ
ン） 処方： ジルコン酸カルシウム粉末 １５．０重量％ （ＣａＺｒＯ3 、平均粒子径：０．３μｍ、ａ／ｂ：０．９） ベンガラ粉末（着色顔料） １．０重量％ 黄酸化鉄粉末（着色顔料） ０．８重量％ 黒酸化鉄粉末（着色顔料） ０．２重量％ ミリスチン酸イソプロピル（油相基剤） ７．８重量％ 流動パラフィン（油相基剤） ７．０重量％ モノラウリン酸プロピレングリコール（油相基剤） ３．０重量％ 親油性モノステアリン酸グリセリン（油相基剤） ２．５重量％ ステアリン酸（油相基剤） ５．０重量％ セトステアリルアルコール（油相基剤） １．０重量％ パラオキシ安息香酸ブチル（油相基剤） ０．２重量％ 精製水（水相基剤） ５２．１重量％ トリエタノールアミン（水相基剤） １．２重量％ ソルビット（水相基剤） ３．０重量％ パラオキシ安息香酸メチル（水相基剤） ０．２重量％ アセトフェノン（香料） 微量 製造法：水相基剤の混合物を調製し、これにジルコン酸
カルシウム粉末と着色顔料との混合物を加えて分散させ
た。一方、油相基剤の混合物を調製し、これを８０℃に
保って撹拌しながら、７５℃に保った水相基剤の混合物
に加え、乳化し、冷却しながら、５０℃で香料を加え、
さらに撹拌しながら冷却し、クリーム状ファンデーショ
ンを得た。Example 11 (Cream foundation) Formulation: Calcium zirconate powder 15.0% by weight (CaZrO 3 , average particle diameter: 0.3 μm, a / b: 0.9) Red iron oxide powder (color pigment) 1. 0% by weight Yellow iron oxide powder (coloring pigment) 0.8% by weight Black iron oxide powder (coloring pigment) 0.2% by weight Isopropyl myristate (oil phase base) 7.8% by weight Liquid paraffin (oil phase base) ) 7.0 wt% Propylene glycol monolaurate (oil phase base) 3.0 wt% Lipophilic glyceryl monostearate (oil phase base) 2.5 wt% Stearic acid (oil phase base) 5.0 wt% % Cetostearyl alcohol (oil phase base) 1.0% by weight Butyl paraoxybenzoate (oil phase base) 0.2% by weight Purified water (water phase base) 52.1% by weight Triethanolamine (water Base) 1.2% by weight Sorbit (aqueous phase base) 3.0% by weight Methyl paraoxybenzoate (aqueous phase base) 0.2% by weight Acetophenone (perfume) Trace amount Production method: Mix a mixture of aqueous phase bases The mixture was prepared, and a mixture of calcium zirconate powder and a coloring pigment was added thereto and dispersed. On the other hand, a mixture of an oil phase base was prepared and added to a mixture of an aqueous phase base kept at 75 ° C. while maintaining the mixture at 80 ° C. with stirring, emulsifying and cooling, and a fragrance was added at 50 ° C. ,
Further, the mixture was cooled with stirring to obtain a creamy foundation.
【００３３】比較例１１（クリーム状ファンデーショ
ン） 実施例１１において、ジルコン酸カルシウム粉末を、酸
化チタン粉末８．０重量％、カオリン粉末４．０重量
％、タルク粉末３．０重量％に置き換え、同様にクリー
ム状ファンデーションを得た。Comparative Example 11 (Cream Foundation) In Example 11, the calcium zirconate powder was replaced with 8.0% by weight of titanium oxide powder, 4.0% by weight of kaolin powder, and 3.0% by weight of talc powder, and the same was applied. A creamy foundation was obtained.
【００３４】実施例１２（粉お白い） 処方： ジルコン酸カルシウム粉末 ８０．０重量％ （ＣａＺｒＯ3 、平均粒子径：０．４μｍ、ａ／ｂ：０．８５） ベンガラ粉末（着色顔料） ４．５重量％ 黄酸化鉄粉末（着色顔料） ３．５重量％ 黒酸化鉄粉末（着色顔料） ２．０重量％ 沈降炭酸カルシウム粉末（顔料） ５．０重量％ ステアリン酸マグネシウム粉末（顔料） ５．０重量％ アセトフェノン（香料） 微量 製造法：ジルコン酸カルシウム粉末と着色顔料とを混合
し、さらに顔料を加えて混合した後、香料を噴霧し、さ
らに混合し、粉砕し、２００メッシュのふるいにかけて
粉お白いを得た。Example 12 (white powder) Formulation: calcium zirconate powder 80.0% by weight (CaZrO 3 , average particle size: 0.4 μm, a / b: 0.85) red iron oxide powder (coloring pigment) 4. 5% by weight Yellow iron oxide powder (coloring pigment) 3.5% by weight Black iron oxide powder (coloring pigment) 2.0% by weight Precipitated calcium carbonate powder (pigment) 5.0% by weight Magnesium stearate powder (pigment) 5. 0% by weight acetophenone (fragrance) Trace amount Production method: Calcium zirconate powder and a coloring pigment are mixed, and then pigment is added and mixed, and then the fragrance is sprayed, further mixed, crushed, and powdered through a 200-mesh sieve. Got white
【００３５】比較例１２（粉お白い） 実施例１２において、ジルコン酸カルシウム粉末を、タ
ルク粉末５５．０重量％、カオリン粉末１５．０重量
％、酸化亜鉛粉末１０．０重量％に置き換え、同様に粉
お白いを得た。Comparative Example 12 (white powder) In Example 12, the calcium zirconate powder was replaced with 55.0% by weight of talc powder, 15.0% by weight of kaolin powder, and 10.0% by weight of zinc oxide powder. Got white powder.
【００３６】[0036]
【実施例および比較例による化粧料の評価】実施例１〜
１２および比較例１〜１２による化粧料について、滑沢
性および付着力の指標としての官能性と、カバー力とを
評価した。官能性は、化粧料を２０名の女性に２週間使
用してもらい、肌ざわり、付き、のびの３点について、
「よい」を“１”、「悪い」を“０”、とすることによ
って評価した。また、カバー力は、ＪＩＳ Ｋ５１０１
の規定される「顔料試験方法」に準拠し、同法における
調製試料として上記の化粧料を使用した。評価結果を表
１に示す。[Evaluation of Cosmetics by Examples and Comparative Examples] Examples 1 to 1
For the cosmetics of No. 12 and Comparative Examples 1 to 12, the organoleptic properties as indexes of lubricity and adhesiveness and the covering power were evaluated. As for sensuality, we asked 20 women to use the cosmetics for 2 weeks.
The evaluation was performed by setting "good" to "1" and "bad" to "0". Also, the covering power is JIS K5101.
According to the “pigment test method” defined by, the above cosmetics were used as prepared samples in the same method. The evaluation results are shown in Table 1.
【００３７】[0037]
【表１】 表１において、カバー力は、実施例によるものも比較例
によるものもそれほど大きな差はない。比較例によるも
ののほうが優れているものもある。これは、実施例、比
較例ともに、化粧料としてカバー力が発現されるように
成分およびその配合比を決めたためであるが、肌ざわ
り、付き、伸びの総合評価においては、比較例によるも
のは実施例によるものに比べてかなり劣っている。この
発明の化粧料は総合評価において優れている。[Table 1] In Table 1, the covering powers of the examples and the comparative examples are not so different. Some of the comparative examples are superior. This is because the components and their compounding ratios were determined so that the covering power was developed as a cosmetic in both Examples and Comparative Examples. However, in the comprehensive evaluation of skin feel, stickiness, and elongation, those of Comparative Examples were It is considerably inferior to that according to the embodiment. The cosmetics of this invention are excellent in overall evaluation.
【００３８】[0038]
【発明の効果】この発明の化粧料は、酸化カルシウム
と、酸化チタニウムおよび酸化ジルコニウムから選ばれ
た少なくとも１種との複合体の粒子からなる粉末を配合
してなるものであるから、実施例と比較例との対比から
も明らかなように、滑沢性と、付着力と、カバー力との
総合評価において大変優れている。しかも、上記粒子は
触媒活性を有しないから、他の成分を変質させたり劣化
させたりする心配もない。EFFECT OF THE INVENTION The cosmetic material of the present invention is prepared by blending powders of particles of a complex of calcium oxide and at least one selected from titanium oxide and zirconium oxide. As is clear from the comparison with the comparative example, it is very excellent in the comprehensive evaluation of lubricity, adhesive force, and covering force. Moreover, since the particles do not have catalytic activity, there is no fear of altering or degrading other components.
Claims (2)
酸化ジルコニウムから選ばれた少なくとも１種との複合
体の粒子からなる粉末を配合してなる化粧料。1. A cosmetic comprising a powder of composite particles of calcium oxide and at least one selected from titanium oxide and zirconium oxide.
範囲にある、請求項１の化粧料。2. The cosmetic according to claim 1, wherein the average particle size of the powder is in the range of 0.05 to 15 μm.