JPH05270947A - Production of decorative sheet - Google Patents

Production of decorative sheet

Info

Publication number
JPH05270947A
JPH05270947A JP6752292A JP6752292A JPH05270947A JP H05270947 A JPH05270947 A JP H05270947A JP 6752292 A JP6752292 A JP 6752292A JP 6752292 A JP6752292 A JP 6752292A JP H05270947 A JPH05270947 A JP H05270947A
Authority
JP
Japan
Prior art keywords
decorative sheet
polymer cement
cement mortar
decorative
base fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP6752292A
Other languages
Japanese (ja)
Inventor
Yoshiyuki Ogushi
義之 大串
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP6752292A priority Critical patent/JPH05270947A/en
Publication of JPH05270947A publication Critical patent/JPH05270947A/en
Pending legal-status Critical Current

Abstract

PURPOSE:To produce the subject decorative sheet excellent in waterproofness, weatherability, adhesion, decorative effect, etc., and suitable, e.g. for decoration of an outer wall of a building by applying a polymer cement mortar to flexible base fabric and impregnating the base fabric therewith. CONSTITUTION:A multicomponent polymer emulsion mainly composed of an acrylic acid ester copolymer is blended with the main material mainly composed of silicon oxide, calcium oxide, iron oxide, etc., and, as necessary, a pigment is further added thereto so as to prepare a polymer cement mortar 12. The obtained polymer cement mortar 12 is then applied to flexible base fabric 10 by using a sprayer 11, etc., so as to impregnate the fabric therewith. Thereby, the objective decorative sheet (A) can be produced. The obtained decorative sheet is suitable for facing the outer wall 14 of a building, etc., by bonding the decorative sheet (A) to the outer wall 14 using an adhesive 13. Due to the flexibility of the base fabric 10 and a prescribed expansibility of the polymer cement 12, the decorative sheet (A) can readily be bonded along the wall surface 14 according to the above-mentioned process even if the wall surface 14 is curved.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、ビル等の外壁等に、装
飾効果を目的として貼着される化粧シートの製造方法に
関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a decorative sheet which is attached to the outer wall of a building or the like for the purpose of decorative effect.

【0002】[0002]

【従来の技術】従来、各種ビルの外壁等の化粧作業は、
コンクリート壁面上にスプレーガンを用いて吹付塗装し
たり、鏝等を用いて化粧モルタル仕上げしたり、化粧タ
イルを貼ったり、或いは、化粧板材を貼着することによ
って行われている。
2. Description of the Related Art Conventionally, makeup work for outer walls of various buildings is
It is carried out by spray-coating on a concrete wall surface with a spray gun, using a trowel or the like to make a decorative mortar, applying a decorative tile, or applying a decorative board material.

【0003】[0003]

【発明が解決しようとする課題】しかし、かかる従来の
外装等の化粧作業は、未だ、以下の解決すべき課題を有
していた。
However, the conventional makeup work for the exterior or the like still has the following problems to be solved.

【0004】即ち、コンクリート壁面上にスプレーガン
を用いて吹付塗装する場合は、経時的に塗装表面が褪色
し、鏝等を用いた化粧モルタルの鏝塗り作業は重労働で
あり、化粧タイルや化粧板材を貼着する作業も、タイル
や化粧板材の大きさに限界があることから、それらを多
数貼着しなければならず、同様に重労働となっていた。
また、化粧タイルや化粧板材を貼着する作業は、タイル
や化粧板材は陶器や木材からなるので、コンクリート壁
面への接着強度が弱く、コンクリート壁面から剥離する
おそれがあった。
That is, in the case of spray coating on a concrete wall surface with a spray gun, the coating surface fades over time, and the work of troweling a decorative mortar with a trowel or the like is a heavy labor, and a decorative tile or a decorative board material. Since the size of tiles and decorative board materials is also limited in the work of sticking, a large number of them must be stuck, which was also a heavy labor.
Further, in the work of attaching the decorative tiles and the decorative board materials, since the tiles and the decorative board materials are made of pottery or wood, the adhesive strength to the concrete wall surface is weak and there is a risk of peeling from the concrete wall surface.

【0005】さらに、ビルのコンクリート壁面が曲面を
なしている場合、硬質素材からなるタイルや化粧板材の
同壁面の貼着作業は極めて困難であった。
Furthermore, when the concrete wall surface of the building has a curved surface, it is extremely difficult to attach the tile wall made of a hard material or the decorative wall material to the wall surface.

【0006】本発明は、上記した課題を解決することが
できる化粧シートの製造方法を提供することを目的とす
る。
It is an object of the present invention to provide a method for manufacturing a decorative sheet which can solve the above problems.

【0007】[0007]

【課題を解決するための手段】本発明は、可撓性を有す
る基布に、ポリマーセメントモルタルを塗布・含浸して
製造することを特徴とする化粧シートの製造方法に係る
ものである。
SUMMARY OF THE INVENTION The present invention relates to a method for producing a decorative sheet, which comprises applying and impregnating a polymer base mortar on a flexible base cloth.

【0008】本発明は、また、顔料を混入したポリマー
セメントモルタルを塗布・含浸して製造することを特徴
とする化粧シートの製造方法に係るものである。
The present invention also relates to a method for producing a decorative sheet, characterized by applying and impregnating a polymer cement mortar mixed with a pigment.

【0009】上記方法において、可撓性を有する基布と
しては、織布又は不織布を用いることができ、また、ポ
リマーセメントモルタルとしては、酸化珪素、酸化カル
シウム、酸化鉄を主成分とした主材に、少なくともアク
リル酸エステル共重合体を主成分としてなる複合ポリマ
ーエマルジョンを混和して生成したものからなるものを
用いることができる。
In the above method, a woven fabric or a non-woven fabric can be used as the flexible base cloth, and the polymer cement mortar is a main material containing silicon oxide, calcium oxide and iron oxide as main components. In addition, it is possible to use a mixture formed by mixing a composite polymer emulsion containing at least an acrylic ester copolymer as a main component.

【0010】また、上記した化粧シートの製造方法は、
化粧シートを建築現場で塗布して仕上げる方法と、予め
工場で化粧シートを製作しておき、現場に持ち込み、ビ
ル等の構造物の壁面に取付ける方法とが考えられる。
Further, the above-mentioned method for manufacturing a decorative sheet is
A method of applying a decorative sheet at a construction site to finish it, and a method of manufacturing a decorative sheet in a factory in advance, bringing it to the site, and attaching it to the wall surface of a structure such as a building can be considered.

【0011】[0011]

【実施例】以下、添付図である図1(a) 〜図1(c) に示
す実施例を参照して、本発明に係る化粧シートの製造方
法を、具体的に説明する。
EXAMPLES Hereinafter, the method for producing a decorative sheet according to the present invention will be specifically described with reference to the examples shown in the accompanying drawings, FIG. 1 (a) to FIG. 1 (c).

【0012】まず、図1(a) に示すように、可撓性を有
する基布10を用意する。かかる基布10の大きさ、形状、
厚みは、ビル等のコンクリート壁面等の基布取付面の大
きさや形状に合わせて任意に選択することができる。
First, as shown in FIG. 1A, a flexible base cloth 10 is prepared. The size and shape of the base cloth 10,
The thickness can be arbitrarily selected according to the size and shape of the base cloth mounting surface such as a concrete wall surface of a building or the like.

【0013】また、基布10は、シート状、ロール状のい
ずれでも用意しておくことができ、ロール状とした場合
は、倉庫管理や搬送に便宜である。
The base fabric 10 may be prepared in the form of a sheet or a roll, and the roll form is convenient for warehouse management and transportation.

【0014】また、好ましくは、基布10は、ガラス繊維
や、ナイロン、ポリエステル、ポリアミド等の合成樹脂
繊維等を素材とした織布や不織布を用いる。
Further, preferably, the base fabric 10 is a woven fabric or a non-woven fabric made of glass fiber, synthetic resin fiber such as nylon, polyester, polyamide or the like.

【0015】次に、図1(b) に示すように、リシンガン
等の吹付装置11を用いて、ポリマーセメントモルタル12
を、基布10の一側面、他側面、両側面に吹付ける。この
吹付によって、ポリマーセメントモルタル12は、基布10
の表面に塗膜を形成するとともに、その内部に含浸し、
一定時間経過した後に、基布10と一体をなすことにな
し、化粧シートAを形成することになる。
Next, as shown in FIG. 1 (b), a polymer cement mortar 12 is used by using a spraying device 11 such as a resin gun.
Spray on one side, the other side, and both sides of the base fabric 10. By this spraying, the polymer cement mortar 12 becomes a base cloth 10
A coating film is formed on the surface of the
After a lapse of a certain time, the base sheet 10 is not integrated and the decorative sheet A is formed.

【0016】その後、図1(c) に示すように、所望の接
着剤13、例えば、上記したポリマーセメントモルタル12
と同様な成分を有するポリマーセメントを用いた接着剤
13を用いて、ビル等の壁面14に付着することによって、
同壁面14の外装作業を完成することができる。
Thereafter, as shown in FIG. 1 (c), a desired adhesive 13, for example, the above-mentioned polymer cement mortar 12 is used.
Adhesive using polymer cement with similar components
By using 13 to adhere to the wall surface 14 of a building,
The exterior work of the wall surface 14 can be completed.

【0017】しかして、上記した化粧シートAに含浸さ
せたポリマーセメントモルタル12は、後述するような成
分・組成を有するので、化粧シートAは、防水性及び耐
候性、確実な接着性等の、外装材に不可欠な条件を、全
て十分に充足することができる。
Since the polymer cement mortar 12 with which the decorative sheet A is impregnated has the components and compositions described below, the decorative sheet A has a waterproof property, a weather resistant property, a reliable adhesive property, and the like. All the conditions essential for the exterior material can be sufficiently satisfied.

【0018】また、通常、ポリマーセメントモルタル12
は、顔料を混入した状態で使用するので、かかる化粧シ
ートAは、ビル周縁の景観に合わせて、任意の色彩とす
ることができる。
Further, usually, polymer cement mortar 12
Is used in a state of being mixed with a pigment, so that the decorative sheet A can have an arbitrary color according to the scenery of the periphery of the building.

【0019】さらに、化粧シートAは色模様を有するも
のとすることもでき、この場合は、ビル等の内外壁面の
装飾効果を一段と高めることができる。かかる化粧シー
トAは、色彩の異なる顔料を混入したポリマーセメント
モルタル12を複数用意しておき、数回に分けて基布10に
塗布することによって容易に製造することができる。
Further, the decorative sheet A may have a color pattern, and in this case, the decorative effect on the inner and outer wall surfaces of a building or the like can be further enhanced. The decorative sheet A can be easily manufactured by preparing a plurality of polymer cement mortars 12 mixed with pigments of different colors and applying the polymer cement mortar 12 to the base fabric 10 in several times.

【0020】また、基布10は可撓性を有するとともに、
ポリマーセメントモルタル12も一定の伸縮性を有するの
で、ビル等のコンクリート壁面が曲面をなしている場合
であっても、容易に、同壁面に沿って化粧シートAを貼
着することができる。
The base cloth 10 has flexibility and
Since the polymer cement mortar 12 also has a certain elasticity, even when the concrete wall surface of a building or the like has a curved surface, the decorative sheet A can be easily attached along the wall surface.

【0021】また、上記した化粧シートAの製造方法に
用いるポリマーセメントモルタル12としては、例えば、
酸化珪素、酸化カルシウム、酸化鉄を主成分とした主材
に、少なくともアクリル酸エステル共重合体を主成分と
してなる複合ポリマーエマルジョンを混和して生成した
ものを用いることができ、以下に、具体的成分及び配合
割合を示す。
The polymer cement mortar 12 used in the method for producing the decorative sheet A is, for example,
It is possible to use a material produced by mixing a composite polymer emulsion containing at least an acrylic ester copolymer as a main component with a main material containing silicon oxide, calcium oxide, and iron oxide as main components. The components and blending ratios are shown.

【0022】本実施例では、ポリマーセメントモルタル
12として、以下の組成を有する複合ポリマーエマルジョ
ンPと主剤Mとを混合して生成したものを用いている。
In this embodiment, polymer cement mortar is used.
As 12, a composite polymer emulsion P having the following composition and a main agent M are mixed and produced.

【0023】(複合ポリマーエマルジョンP) (実施例1) (実施例2) (主剤M) なお、上記白色セメントの成分重量比は、以下の通りで
あった。
(Composite Polymer Emulsion P) (Example 1) (Example 2) (Main agent M) The component weight ratio of the white cement was as follows.

【0024】 また、上記した主剤Mに代えて、砂とセメントを混合し
たモルタルを用いることができる。
[0024] Further, instead of the above-mentioned main agent M, mortar in which sand and cement are mixed can be used.

【0025】そして、複合ポリマーエマルジョンPを攪
拌容器に入れ、主剤Mを徐々に加えながらハンドミキサ
ーで攪拌し、ポリマーセメントモルタル12を製造した。
Then, the composite polymer emulsion P was put in a stirring container and stirred with a hand mixer while gradually adding the main agent M to produce a polymer cement mortar 12.

【0026】なお、ポリマーセメントモルタル12の配合
比は、複合ポリマーエマルジョンPの1重量部に対し
て、主剤Mを3〜5重量部とすることが望ましい。本実
施例では、1:4であった。
The compounding ratio of the polymer cement mortar 12 is preferably 3 to 5 parts by weight of the main agent M with respect to 1 part by weight of the composite polymer emulsion P. In this example, it was 1: 4.

【0027】また、接着剤も、上記したポリマーセメン
トモルタル12と同一組成のポリマーセメントモルタルを
用いることができる。但し、接着剤としての流動性を考
慮して、ポリマーエマルジョンPと主剤Mとの混合比
は、1:2とした。
Also, as the adhesive, a polymer cement mortar having the same composition as the above-mentioned polymer cement mortar 12 can be used. However, considering the fluidity as an adhesive, the mixing ratio of the polymer emulsion P and the main agent M was set to 1: 2.

【0028】[0028]

【発明の効果】上記したように、本発明に係る化粧シー
トは、可撓性を有する基布に、必要に応じて一種又は複
数種類の顔料を混入したポリマーセメントモルタルを含
浸・塗布することによって製造することにしている。
As described above, the decorative sheet according to the present invention is obtained by impregnating and coating a flexible base cloth with polymer cement mortar in which one or more kinds of pigments are mixed if necessary. I am going to manufacture it.

【0029】従って、以下の効果を奏する。Therefore, the following effects are obtained.

【0030】化粧シートに含浸させたポリマーセメン
トによって、防水性及び耐候性、確実な接着性等の、外
装材に不可欠な条件を、全て充足することができる。
The polymer cement with which the decorative sheet is impregnated can satisfy all the conditions essential to the exterior material, such as waterproofness, weather resistance, and reliable adhesiveness.

【0031】ポリマーセメントに混入する顔料の数と
色彩とを適宜選択することによって、ビル周縁の景観に
合わせて、任意の色彩とすることができ、また、化粧シ
ートに色模様を付与することによって、ビル等の内外壁
面の装飾効果を一段と高めることができる。
By appropriately selecting the number of pigments mixed in the polymer cement and the color thereof, it is possible to obtain an arbitrary color according to the landscape of the building periphery, and by adding a color pattern to the decorative sheet. The decorative effect on the inner and outer wall surfaces of buildings, etc. can be further enhanced.

【0032】基布は可撓性を有するとともに、ポリマ
ーセメントも一定の伸縮性を有するので、ビル等のコン
クリート壁面が曲面をなしている場合であっても、容易
に、同壁面に沿って化粧シートを貼着することができ
る。
Since the base cloth has flexibility and the polymer cement also has a certain elasticity, even when the concrete wall surface of a building or the like has a curved surface, it is easy to apply makeup along the wall surface. A sheet can be attached.

【0033】基布は可撓性を有するとともに、ポリマ
ーセメントも一定の伸縮性を有するので、ひび割れ追随
性もあり、コンクリートにある程度のひび割れが起きて
も、化粧シートは十分に伸びて、外部からの水の侵入を
防ぐことができる。
Since the base cloth has flexibility and the polymer cement also has a certain elasticity, it has a crack-following property, and even if the concrete is cracked to some extent, the decorative sheet is sufficiently stretched to prevent it from the outside. Can prevent the invasion of water.

【0034】[0034]

【図面の簡単な説明】[Brief description of drawings]

【図1】本発明に係る化粧シートの製造方法の工程説明
図である。
FIG. 1 is a process explanatory view of a method for manufacturing a decorative sheet according to the present invention.

【符号の説明】[Explanation of symbols]

A 化粧シート 10 基布 11 吹付装置 12 ポリマーセメントモルタル 13 接着剤 14 壁面 A Decorative sheet 10 Base cloth 11 Spraying device 12 Polymer cement mortar 13 Adhesive 14 Wall surface

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 FI 技術表示箇所 C04B 14:06 Z 2102−4G 14:36) 2102−4G ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI technical display location C04B 14:06 Z 2102-4G 14:36) 2102-4G

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】可撓性を有する基布に、ポリマーセメント
モルタルを塗布・含浸して製造することを特徴とする化
粧シートの製造方法。
1. A method for producing a decorative sheet, which comprises applying and impregnating a flexible base cloth with polymer cement mortar.
【請求項2】可撓性を有する基布に、顔料を混入したポ
リマーセメントモルタルを塗布・含浸して製造すること
を特徴とする化粧シートの製造方法。
2. A method for producing a decorative sheet, which comprises applying and impregnating a flexible base cloth with a polymer cement mortar mixed with a pigment.
【請求項3】可撓性を有する基布は、織布又は不織布で
あることを特徴とする請求項1又は2記載の化粧シート
の製造方法。
3. The method for producing a decorative sheet according to claim 1, wherein the flexible base cloth is a woven cloth or a non-woven cloth.
【請求項4】ポリマーセメントモルタルは、酸化珪素、
酸化カルシウム、酸化鉄を主成分とした主材に、少なく
ともアクリル酸エステル共重合体を主成分としてなる複
合ポリマーエマルジョンを混和して生成したものからな
ることを特徴とする請求項1〜3のうち、いずれかの請
求項記載の化粧シートの製造方法。
4. The polymer cement mortar comprises silicon oxide,
4. A main material containing calcium oxide and iron oxide as a main component, and a composite polymer emulsion containing at least an acrylic ester copolymer as a main component admixed with each other to form the mixture. A method for manufacturing a decorative sheet according to claim 1.
JP6752292A 1992-03-25 1992-03-25 Production of decorative sheet Pending JPH05270947A (en)